Patent Grant
7229598
The present invention relates to a diffusion bonded metallic catalyst carrier used for purifying exhaust gas discharged from an automobile engine. Also, the present invention relates to a method of manufacturing the diffusion bonded metallic catalyst carrier.
Ceramic carrier have been conventionally used for catalytic converters used for purifying exhaust gas discharged from automobile engines. However, recently, the use of metallic catalyst carrier is increasing because the resistance to heat of the catalyst carrier is high and, further, the pressure loss caused by the catalyst carrier is low and furthermore catalytic converters into which the catalyst carrier are incorporated can be easily mounted on automobiles.
As shown in
High durability is required of the catalytic converter because it must stand the severe heat cycle given off by the exhaust gas at a high temperature discharged from an engine and further it must stand the intense vibration from the engine. Therefore, in the conventional catalyst carrier 1, the flat foil 5 and the corrugated foil 6 of the metallic honeycomb body 2 are joined to each other at the contact section, and further an outer circumference of the metallic honeycomb body 2 and an inner circumference of the outer cylinder 3 are joined to each other.
Concerning the joining means, there are provided various means such as soldering, diffusion bonding, resistance welding, laser welding and so forth. Diffusion bonding is advantageous because no solder is required and further no specific welding jig is required and, furthermore, diffusion bonding can be appropriately used for mass production.
In general, when diffusion bonding is conducted, members to be joined to each other are made to come close to each other and are heated to high temperature in a high vacuum. In diffusion bonding of the metallic honeycomb body 2 in which pieces of foil are spirally wound, it is impossible to apply surface pressure to the metallic honeycomb body 2 from the outside. Therefore, when back tension is given to the flat foil 5 in the direction of arrow A in the process of winding as shown in
However, as shown in
Due to the foregoing, the following are required in order to obtain a metallic honeycomb body of high quality.
(1) Aluminum, the quantity of which is not less than a predetermined value for obtaining a section of diffusion bonding, is vaporized.
(2) Vaporization of aluminum is suppressed to a value not more than a predetermined value so that resistance to oxidation is impaired, that is, it is necessary to control vaporization of aluminum in the process of diffusion bonding.
As a method of controlling vaporization of aluminum in the process of diffusion bonding of the metallic honeycomb body 2, Japanese Unexamined Patent Publication No. 9-215930 discloses the following means. According to the above method, the metallic honeycomb body 2 is covered with a cover having holes and subjected to diffusion bonding. Due to the foregoing, residual oxygen is discharged outside from the holes, and generated aluminum vapor is made to stay close to the metallic honeycomb body 2. According to the above proposal, vaporization of aluminum can be surely suppressed, however, it is necessary to attach the covers to all honeycomb bodies 2, which remarkably deteriorates the productivity. According to this proposal, heat treatment of diffusion bonding is conducted at 1300° C. in a vacuum. When heat treatment is conducted at such a high temperature in a vacuum, aluminum is intensely vaporized, and diffusion bonding cannot be sufficiently done. Therefore, in order to ensure resistance to heat, it is necessary to provide another means instead of the cover described above.
In the same manner, Japanese Unexamined Patent Publication No. 5-168945 discloses another means for controlling vaporization of aluminum in the process of diffusion bonding of the metallic honeycomb body 2. According to this method, a cover is set on the metallic honeycomb body 2, and a clearance is provided between the cover and the outer cylinder. Under the above condition, diffusion bonding is conducted. Due to the foregoing, residual oxygen is discharged outside from the clearance, so that generated aluminum vapor is made to stay close to the metallic honeycomb body 2. According to the above proposal, vaporization of aluminum can be surely suppressed, however, it is necessary to attach the covers to all honeycomb bodies 2, which remarkably deteriorates the productivity.
The applicant filed a patent, by Japanese Unexamined Patent Publication No. 8-38912, in which the following method is proposed. The average roughness (Ra) of a surface of the flat foil and that of a surface of the corrugated foil before diffusion bonding are kept to be not less than 0.001 μm and not more than 0.2 μm, and further the contact width of the flat foil with the corrugated foil is kept to be not less than 30 μm. Due to the foregoing, diffusion bonding can be excellently conducted in all regions of the honeycomb body from the center to the outer circumferential section by giving a back tension, the intensity of which is not higher than a value at which buckling is caused in the vent hole of the honeycomb body, and also by reducing the diameter of the outer cylinder. Also, the applicant filed Japanese Unexamined Patent Publication No. 10-309472 in which the following method is proposed. The contact width of the flat foil with the corrugated foil is kept at a value not less than 5 times of the thickness t of the flat foil and the corrugated foil. The flat foil and the corrugated foil are wound while a back tension, the intensity of which is 0.2 to 1.5 kgf/cm, is being given to the honeycomb body, and diffusion bonding is conducted in a temperature range from 1100 to 1250° C., and it is preferable that diffusion bonding is conducted in a temperature range of vacuum heat treatment corresponding to the average roughness Rac (μm) in the width direction of the plane foil.
It is an object of the present invention to provide a diffusion bonded metallic catalyst carrier of a catalytic converter used for purifying exhaust gas discharged from an automobile engine. It is another object of the present invention to provide a method of manufacturing the diffusion bonded metallic catalyst carrier of the catalytic converter. According to the present invention, when a metallic honeycomb body made of heat-resistant stainless steel containing aluminum is subjected to diffusion bonding, a quantity of vaporization of aluminum is minimized while a necessary mechanical strength of diffusion bonding is ensured. Due to the foregoing, it is possible to provide diffusion bonded metallic catalyst carrier, the resistance to oxidation and the durability of which are high. Also, it is possible to provide a method of manufacturing the diffusion bonded metallic catalyst carrier. A summary of the present invention is described below.
(1) A diffusion bonded metallic catalyst carrier comprising: a honeycomb body composed of a piece of corrugated foil made of heat-resistant stainless steel containing aluminum and a piece of flat foil or corrugated foil made of stainless steel, the piece of corrugated foil and the piece of flat foil or corrugated foil being alternately wound or laminated on each other; and an outer cylinder made of metal into which the honeycomb body is incorporated, the honeycomb body and the outer cylinder being integrated into one body by means of diffusion bonding, wherein the surface roughness of the pieces of foil after diffusion bonding is kept so that the center line average height Ra can be 0.001 to 2.0 μm, and no sintered bridges are formed at both end portions of the bond sections of the two pieces of foil of the flat foil and the flat foil or corrugated foil in the longitudinal direction of the pieces of foil.
(2) A diffusion bonded metallic catalyst carrier according to item (1), wherein the surface roughness of the pieces of foil in the foil width direction after diffusion bonding is kept so that the center line average height Ra can be 0.001 to 2.0 μm.
(3) A diffusion bonded metallic catalyst carrier according to item (1) or (2), wherein solder bonding is conducted on a contact section of the piece of flat foil with the piece of corrugated foil on the entry side of exhaust gas and diffusion bonding is conducted on the delivery side of exhaust gas.
(4) A diffusion bonded metallic catalyst carrier according to one of items (1) to (3), wherein the corrugated-form of the piece of corrugated foil on the entry side of exhaust gas of the catalyst carrier is formed into a trapezoid in which an area of the contact section of the piece of flat foil with the piece of corrugated foil is large, and the corrugated-form of the piece of corrugated foil on the delivery side of exhaust gas of the catalyst carrier is formed into a configuration in which an area of the contact section of the piece of flat foil with the piece of corrugated foil is not large.
(5) A diffusion bonded metallic catalyst carrier according to one of items (1) to (4), wherein the thickness of the piece of flat foil is not uniform, so that the thickness of the piece of flat foil on the entry side of exhaust gas of the metallic support is large, and the thickness of the piece of flat foil on the delivery side of exhaust gas of the catalyst carrier is small.
(6) A method of manufacturing a diffusion bonded metallic catalyst carrier, the diffusion bonded metallic catalyst carrier comprising: a honeycomb body composed of a piece of corrugated foil made of heat-resistant stainless steel containing aluminum and a piece of flat foil or corrugated foil made of stainless steel, the piece of corrugated foil and the piece of flat foil or corrugated foil being alternately wound or laminated on each other; and an outer cylinder made of metal into which the honeycomb body is incorporated, the honeycomb body and the outer cylinder being integrated into one body by means of diffusion bonding, the method of manufacturing the diffusion bonded metallic catalyst carrier comprising the step of selecting parameters so that λb, which is defined by
λb=C×δf−1×F1/2×Ra−1/2×T1/4×exp(15000/T)×b1/2
under the condition where 7.52×109×exp(−35000/T)≧8 Pout is satisfied, can be in a range from 8 to 20 where thickness of the strip of foil is δf (m), center line average height of the foil surface before diffusion bonding is Ra (m), back tension in the case of winding is F (kgf), contact width of the piece of flat foil with the piece of corrugated foil or contact width of the piece of a first corrugated foil with the piece of a second corrugated foil is b (m), heat treatment temperature is T (K), degree of vacuum is Pout (Pa), and the constant of proportion is C.
(7) A method of manufacturing a diffusion bonded metallic catalyst carrier according to item (6), wherein surface roughness Rac (m) of the strip of foil in the foil width direction is used for the center line average height Ra (m).
(8) A method of manufacturing a diffusion bonded metallic catalyst carrier according to item (6) or (7), wherein a strip of foil is used, the surface roughness of which is 0.001 to 0.30 μm when it is expressed by the center line average height Ra.
(9) A method of manufacturing a diffusion bonded metallic catalyst carrier according to item (6) or (7), wherein a strip of foil is used, the surface roughness in the foil width direction of which is 0.001 to 0.30 μm when it is expressed by the center line average height Ra.
(10) A method of manufacturing a diffusion bonded metallic catalyst carrier according to one of items (6) to (9), wherein the parameters are selected so that λb can be in a range from 14 to 18.
(11) A method of manufacturing a diffusion bonded metallic catalyst carrier according to one of items (6) to (9), wherein the constant of proportion is C=6.8×10−12.
a) and 5(b) are partial enlarged views of a metallic honeycomb body.
a) and 7(b) are cross-sectional views showing a catalyst carrier of the present invention.
First, a diffusion bonded metallic catalyst carrier of the present invention is characterized in that: because of diffusion bonding, the surface roughness of pieces of flat foil and corrugated foil is 0.001 to 2.0 μm after heat treatment in a vacuum when it is expressed by the center line average height Ra, and it is preferable that surface roughness of pieces of flat foil and corrugated foil is 0.2 to 1.0 μm after heat treatment in a vacuum when it is expressed by the center line average height Ra. When surface roughness before heat treatment in a vacuum for diffusion bonding of stainless steel used for material of a diffusion bonded metallic catalyst carrier of the present invention is smooth or a little rough so that the center line average height Ra is 0.001 to 0.30 μm, the mechanical strength of diffusion bonding can be more enhanced. This can be seen from the following. As shown in
In the case where the center line average height is not more than 0.001 μm, a swell is caused in the piece of foil and it becomes difficult for alumina to adhere to the piece of foil. On the other hand, in the case where the center line average height is not less than 2.0 μm, the thickness of wash-coat (Al2O3) becomes not uniform.
Next, the diffusion bonded metallic catalyst carrier of the present invention is also characterized in that: no sintered bridges are formed at both end portions of the bond of two pieces of foil of the corrugated foil and the flat foil in the longitudinal direction of the piece of foil of a product obtained by means of diffusion bonding conducted by heat treatment in a vacuum. Usually, when a catalyst carrier made of stainless steel containing aluminum is subjected to heat treatment in a vacuum at high temperature of not lower than 1300° C., sintered bridges are formed at the bonding. When these sintered bridges are formed, the following problems may be encountered. When the catalyst carrier is used in a converter for exhaust gas, and vibration is given to the catalyst carrier at high temperature at all times, aluminum is vaporized from these sintered bridges, so that a quantity of aluminum contained in stainless steel is reduced. Therefore, the catalyst carrier becomes fragile. As a result, sintered bridges S shown in
Next, when the diffusion bonded metallic catalyst carrier is manufactured, the primary manufacturing particulars are foil thickness, surface roughness of foil, configuration of corrugated foil, temperature of heat treatment and degree of vacuum. Since a relation of relative dependency of these manufacturing particulars is unknown and a general solution has not been found until now, a particular solution is found according to data obtained by an experiment. In the diffusion bonded metallic catalyst carrier, (1) the mechanical strength of a diffusion bonded joints and (2) the resistance to oxidation must be compatible with each other. However, these two factors depend upon a phenomenon of vaporization of aluminum. Therefore, it is impossible to control these two factors by the conventional technique, that is, it is difficult to make these two factors (1) and (2) compatible with each other.
First, the reason why vaporization of aluminum is required for guaranteeing the mechanical strength of a diffusion bonded joint will be described below. The present applicant made experiments and confirmed that a strong oxide film was formed on a surface of heat-resistant stainless steel containing aluminum by residual oxygen in a furnace in the process of heat treatment in a vacuum. As long as this oxide film exists, the diffusion bonding cannot proceed. However, when aluminum is vaporized below this oxide film, the oxide film comes off like scales and coagulates. After the oxide film has come off, fresh surfaces of base metal come into contact with each other, and the diffusion bonding can proceed. In other words, it was found that vaporization of aluminum is essential in order to remove the oxide film. It was also found that vapor of aluminum covers a surface of metal after the oxide film has come off and that the vapor of aluminum is combined with residual oxygen so that oxidation can be prevented.
However, there is an upper limit of a quantity of aluminum to be vaporized, that is, when an excessively large quantity of aluminum is vaporized, the quantity of remaining aluminum is reduced. Accordingly, the resistance to oxidation of the base metal is remarkably impaired. Consequently, the quantity of aluminum to be vaporized is limited. The most powerful parameter to control the vaporization of aluminum is temperature T of heat treatment, and the next powerful parameter to control the vaporization of aluminum is degree of vacuum Pout.
As described before, when heat treatment in a vacuum is conducted at a high temperature of not lower than 1300° C. in a vacuum of 10−2 Pa, the vaporization of aluminum does not occurred. For example, when the temperature is decreased to 1200° C., the quantity of vaporized aluminum is considerably decreased. If it is possible to conduct diffusion bonding in this temperature range, it is unnecessary to use the cover described in Japanese Unexamined Patent Publication Nos. 5-168945 and 9-215930, and the productivity is not impaired.
In order to make (1) the mechanical strength of the diffusion bonded joint and (2) the resistance to oxidation compatible with each other, the inventors made investigation into an interaction between the manufacturing, condition of catalyst carrier of diffusion bonding and aluminum. As a result of the investigation, in order to express a state of vaporization of aluminum, the following λb, which is a dimensionless number, was newly introduced, wherein b is the contact width of the pieces of flat foil and corrugated foil in meters (m).
λb=√{(2kT×K1×√(1/T))/(δg×D0×exp(−Qp/RT))}×b (1)
However, the inventors made experiments and found that the following relation can be established between pressure of saturated vapor Ps of aluminum and degree of vacuum Pout.
Ps=K2×exp(−Q/RT)≧8×Pout (2)
Each constant can be expressed as follows.
K1=6.69×1024 (s−1Pa−1 m−2K−1/2)
K2=7.52×109 (Pa)
Q=291.0 (kJ·mol−1)
Qp=250 (kJ·mol−1)
D0=1.905×1011 (m2s−1)
R=8.31J·K−1mol−1
k=1.38×10−23 (J·K−1)
The average gap δg between the pieces of flat foil and corrugated foil is in proportion to moment of inertia of area of the piece of foil and also in proportion to average roughness of a surface of the piece of foil. Further, the average gap δg between the pieces of flat foil and corrugated foil is in inverse proportion to surface pressure. Therefore, it can be expressed by the following expression.
δg=f(δf2, F/b, Ra) (3)
As a result of the experiments made by the inventors, it was found that the above expression (3) can be approximated by the following expression.
δg=C1×δf2×1/(F/b)×Ra (4)
In this case, C1 is a proportional constant, δf (m) is foil thickness, Ra (m) is average roughness of the surface of foil, F (kgf) is back tension in the case of winding the pieces of foil, and b (m) is contact width of the pieces of flat foil and corrugated foil.
The following expression can be obtained from the above constants and expressions (1) and (4).
λb=C×δf−1×F1/2×Ra−1/2×T1/4×exp(15000/T)×b1/2 (5)
In the above expression, C is a proportional constant.
When the constant is substituted into the expression (2), the following expression can be obtained.
7.52×109×exp(−35000/T)≧8×Pout (6)
In this connection, in the above expressions (3) to (5), it is more preferable to use Rac (average roughness in the width direction) instead of Ra.
In this connection, several methods of measuring parameters will be explained as follows.
A geometrical configuration of a piece of foil has a great influence on the diffusion bonding. This geometrical configuration of a piece of foil could be represented by average roughness Ra of the piece of foil. This Ra is based on the arithmetic means stipulated by JIS B0601-1994, and the measurement of Ra was made by a tracer method type roughness measuring device stipulated by JIS B0651-1976.
In this connection, in order to take measurements precisely while an influence caused by deformation of a piece of foil is eliminated, a sample to be measured was made to come into close contact with a surface plate. In the measurement, a tracer needle was used, the radius of curvature of the tip of which was 1 μm, and the measurement was made under the condition that the cut-off value was 0.8 mm, the scanning speed of the tracer needle was 0.3 mm/sec, and the gauge length was 4 mm.
Surface configurations of some pieces of foil made of stainless steel have an orientation. For example, when a piece of foil is rolled by a pair of finishing rollers having flaws in the circumferential direction, these flaws are transferred onto a surface of the piece of foil. Therefore, flaws are caused on the piece of foil in the longitudinal direction. When a piece of corrugated foil is made from the above piece of foil having flaws when it is made to pass through a pair of corrugating gears 9 as shown in
When the contact portions of the pieces of flat foil 5 and corrugated foil 6 are subjected to diffusion bonding, it is necessary to fill the flaws in the foil width direction by means of surface diffusion. Accordingly, when the flaws are caused on the piece of foil in the longitudinal direction by the finishing rollers in the process of rolling, average roughness Rac in the foil width direction, which is one of the geometrical configurations of the piece of foil, controls a phenomenon of diffusion bonding. Of course, the tracer needle conducts scanning in the foil width direction (direction C in
Concerning contact width b of the piece of flat foil with the piece of corrugated foil, after the pieces of flat foil and the corrugated foil were alternately wound, they were inserted into an outer cylinder, and contact width b of the piece of flat foil with the piece of corrugated foil was measured by a microscope before conducting heat treatment in a vacuum.
Table 1 shows a relation between λb and the result of a thermal durability test of an engine conducted on the metallic honeycomb body. In this test, the temperature of the exhaust gas discharged from the engine was 950° C., and one cycle was determined in such a manner that ON was kept for 10 minutes and then OFF was kept for 10 minutes. In this case, when λb is calculated, a proportional constant C=6.8×10−12 was adopted.
According to the result of the above experiment, the following can be understood. When λb is not less than 8 and not more than 20, it is possible to make the bond strength of the metallic honeycomb body and the resistance to oxidation compatible with each other, and also it is possible to succeed in passing the thermal durability test of 900 cycles in which an actual automobile engine is used. Further, when λb is not less than 14 and not more than 18, it was possible to succeed in passing the thermal durability test of 1800 cycles.
A honeycomb body, in which a piece of flat foil made of stainless steel containing aluminum and a piece of corrugated foil obtained by corrugating the piece of flat foil are alternately wound, is incorporated into an outer cylinder made of metal, and then the honeycomb body is integrated into one body by diffusion bonding. In diffusion bonded metallic catalyst carrier, manufacturing is conducted under the condition that λb is not less than 8 and not more than 20, wherein λb is defined by the following expression.
λb=6.8×10−12×δf−1×F1/2×Ra−1/2×T1/4×exp(15000/T)×b1/2
In this case, the condition of 7.52×109×exp(−35000/T)≧8×Pout is satisfied
where δf (m) is foil thickness, Ra (m) is average roughness of a surface of foil, F (kgf) is back tension given in the process of winding, b(m) is contact width of a piece of flat foil with a piece of corrugated foil, T(K) is temperature of heat treatment, and Pout (Pa) is degree of vacuum. Due to the foregoing, When a quantity of aluminum to be vaporized necessary for diffusion bonding is ensured, it is possible to guarantee the bond strength of diffusion bonding, and further when a quantity of aluminum to be vaporized is made a minimum, the resistance to oxidation can be maximized. In this way, it is possible to obtain a diffusion bonded metallic catalyst carrier of high quality in which the bond strength of diffusion bonding is guaranteed and the resistance to oxidation can be maximized.
When exhaust gas is discharged from an engine in the form of a drift current, the catalyst reaction on the exhaust gas entry side of the catalyst carrier and that on the exhaust gas delivery side are different from each other. In the present invention, the designing of the catalyst carrier was studied while consideration was given to this difference of catalyst reaction.
Although it is not desirable, a drift current, in which a flow velocity of gas is partially increased, exists on the exhaust gas entry side of the catalyst carrier in some cases. In this case, in a portion of the catalyst carrier into which the drift current flows, the catalyst reaction proceeds. Therefore, a large amount of combustion heat is generated and the temperature is raised higher than other portions, that is, the temperature distribution becomes non-uniform.
Concerning the combustion caused by the catalyst reaction in the catalyst carrier, the combustion is most intensely conducted in a portion right after an entrance of the catalyst carrier from which exhaust gas is fed, and a quantity of combustion heat is decreased in a portion located on the downstream side of the exhaust gas flow. On the other hand, heat is emitted outside via a metallic portion composing the catalyst carrier. Therefore, as shown in
In the present invention, as shown in
In the present invention, a corrugate-form of the piece of corrugated foil on the entry side of exhaust gas is determined to be a trapezoid as shown in
Further, in the present invention, the thickness of the piece of flat foil on the entry side of exhaust gas is different from the thickness of the piece of flat foil on the delivery side of exhaust gas. It is preferable that the thickness of the piece of flat foil on the entry side of exhaust gas is not less than twice as large as the thickness of the piece of flat foil on the delivery side of exhaust gas. The reason is described as follows. In the same manner as that of an increase in the rigidity by improvement in the shape of the trapezoidal corrugation, when the thickness of the piece of flat foil on the entry side of exhaust gas is increased with respect to the thickness of the piece of flat foil on the delivery side of exhaust gas, the rigidity of the honeycomb body in the radial direction can be increased. The thickness of the piece of foil may be changed by a constant taper from the entry side of exhaust gas to the delivery side of exhaust gas, however, it is possible to adopt an arrangement in which the thickness is changed stepwise.
1. A catalyst carrier, the outer diameter of which is 100 mm, the length of which is 100 mm, was made of the following material, and a durability test was made.
Flat Foil:
Foil is made of 20Cr-5Al ferritic stainless steel, width is 100 mm, and surface is finished without orientation.
A piece of foil, the surface of which is finished without orientation, is rolled by finish rolling. Surface roughness of a piece of foil in direction L is the same as that in direction C.
Corrugated Foil:
The above piece of foil is corrugated.
Outer Cylinder:
Outer cylinder is composed of a heat-resistant stainless steel pipe made of 18Cr-8Ni, the wall thickness is 1.5 mm, the length is 100 mm, and the outer diameter is 102 mm.
Thickness of pieces of flat foil and corrugated foil is 50 μm, and Ra is 0.40 μm.
Corrugation is a sine wave form.
Width of a contact portion of a piece of flat foil with a piece of corrugated foil is 10 μm.
While a piece of flat foil was being given a back tension of 10 kgf, it was wound together with a piece of corrugated foil, so that a metallic honeycomb, the outer diameter of which was 100 mm, was made. After solder was coated on an inner face of an outer cylinder, the outer cylinder was inserted into the metallic honeycomb body. Then, the metallic honeycomb body was heated to 1200° C. for 90 minutes in a vacuum of 10−2 Pa.
In this catalyst carrier, λb was 3.6 as shown in the following expression.
λb=6.8×10−12×1/(50×10−6)×√10/√(0.40×10−6)×4√1473×exp(15000/1473)×√(10×10−6)=3.6
In this connection,
7.52×109×exp(−35000/1473)=0.36≧8×10−2
Thickness of pieces of flat foil and corrugated foil is 50 μm, and Ra is 0.18 μm.
Corrugation is a trapezoid.
Width of a contact portion of a piece of flat foil with a piece of corrugated foil is 100 μm.
While a piece of flat foil was being given a back tension of 10 kgf, it was wound together with a piece of corrugated foil, so that a metallic honeycomb, the outer diameter of which was 100 mm, was made. After solder was coated on an inner face of an outer cylinder, the outer cylinder was inserted into the metallic honeycomb body. Then, the metallic honeycomb body was heated to 1200° C. for 90 minutes in a vacuum of 10−2 Pa.
In this catalyst carrier, λb was 16.7 as shown in the following expression.
λb=6.8×10−12×1/(50×10−6)×√10/√(0.18×10−6)×4√1523×exp(15000/1523)×√(100×10−6)=16.7
In this connection,
7.52×109×exp(−35000/1523)=0.36≧8×10−2
Thickness of pieces of flat foil and corrugated foil is 20 μn, and Ra is 0.18 μm.
Corrugation is a sine wave form.
Width of a contact portion of a piece of flat foil with a piece of corrugated foil is 10 μm.
While a piece of flat foil was being given a back tension of 10 kgf, it was wound together with a piece of corrugated foil, so that a metallic honeycomb, the outer diameter of which was 100 mm, was made. After solder was coated on an inner face of an outer cylinder, the outer cylinder was inserted into the metallic honeycomb body. Then, the metallic honeycomb body was heated to 1200° C. for 90 minutes in a vacuum of 10−2 Pa.
In this catalyst carrier, λb was 8.4 as shown in the following expression.
λb=6.8×10−12×1/(20×10−6)×√2/√(0.18×10−6)×4√1473×exp(15000/1473)×√(10×10−6)=8.4
In this connection,
7.52×109×exp(−35000/1473)=0.36≧8×10−2
Thickness of pieces of flat foil and corrugated foil is 20 μm, and Ra is 0.18 μm.
Corrugation is a trapezoid.
Width of a contact portion of a piece of flat foil with a piece of corrugated foil is 100 μm.
While a piece of flat foil was being given a back tension of 10 kgf, it was wound together with a piece of corrugated foil, so that a metallic honeycomb, the outer diameter of which was 100 mm, was made. After solder was coated on an inner face of an outer cylinder, the outer cylinder was inserted into the metallic honeycomb body. Then, the metallic honeycomb body was heated to 1200° C. for 90 minutes in a vacuum of 10−2 Pa.
In this catalyst carrier, λb was 18.6 as shown in the following expression.
λb=6.8×10−12×1/(20×10−6)×√2/√(0.18×10−6)×4√1473×exp(15000/1473)×√(100×10−6)=18.6
In this connection,
7.52×109×exp(−35000/1473)=0.36≧8×10−2
Thickness of pieces of flat foil and corrugated foil is 20 μm, and Ra is 0.40 μm.
Corrugation is a sine wave form.
Width of a contact portion of a piece of flat foil with a piece of corrugated foil is 10 μm.
While a piece of flat foil was being given a back tension of 2 kgf, it was wound together with a piece of corrugated foil, so that a metallic honeycomb, the outer diameter of which was 100 mm, was made. After solder was coated on an inner face of an outer cylinder, the outer cylinder was inserted into the metallic honeycomb body. Then, the metallic honeycomb body was heated to 1250° C. for 90 minutes in a vacuum of 10−2 Pa.
In this catalyst carrier, λb was 28.6 as shown in the following expression.
λb=6.8×10−12×1/(20×10−6)×√/2/√(0.40×10−6)×4√1523×exp(15000/1523)×√(10×10−6)=28.6
In this connection,
7.52×109×exp(−35000/1523)=0.75≧8×10−2
1. With respect to Conventional Examples 1 and 2 and Examples 1 to 3 of the present invention, a thermal durability test of engine was conducted, in which the temperature of gas on the entry side was 950° C. and it was turned on for 10 minutes and turned off for 10 minutes, which was determined to be one cycle. The results of evaluation are shown on Table 2.
According to the results of the above experiments, the following can be concluded. The present invention can provide a diffusion bonded metallic catalyst carrier, comprising: a honeycomb body composed of a piece of plane foil made of heat-resistant stainless steel containing aluminum and a piece of corrugated foil made of stainless steel, the piece of corrugated foil and the piece of flat foil being alternately wound; and an outer cylinder made of metal into which the honeycomb body is incorporated, the honeycomb body and the outer cylinder being integrated into one body by means of diffusion bonding,
the diffusion bonded metallic catalyst carrier being manufactured in a condition so that λb, which is defined by
λb=6.8×10−12×δf−1×F1/2×Ra−1/2×T1/4×exp(15000/T)×b1/2,
can be in a range from 8 to 20 where thickness of the strip of foil is δf (m), average roughness of the foil surface in the width direction is Ra (m), back tension in the case of winding is F (kgf), contact width of the piece of flat foil with the piece of corrugated foil is b (m), heat treatment temperature is T (K), and degree of vacuum is Pout (Pa). In this case, 7.52×109×exp(−35000/T)≧8×Pout is satisfied.
When the diffusion bonded metallic catalyst carrier is manufactured as described above, it is possible to ensure a quantity of vaporized aluminum necessary for diffusion bonding, so that the mechanical strength of the diffusion bonded joint can be guaranteed. When a quantity of vaporized aluminum is minimized, the resistance to oxidation can be maximized. In this way, it is possible to provide a high quality of diffusion bonded metallic catalyst carrier.
2. A catalyst carrier, the outer diameter of which is 100 mm and the length of which is 100 mm, was made of the following material, and a durability test was made.
Flat Foil:
Foil is made of 20Cr-5Al ferritic stainless steel, and width is 100 mm.
Corrugated Foil:
The above piece of foil is corrugated.
Outer Cylinder:
Outer cylinder is composed of a heat-resistant stainless steel pipe made of 18Cr-8Ni, the wall the thickness is 1.5 mm, the length is 100 mm, and the outer diameter is 102 mm.
Thickness of pieces of flat foil and corrugated foil is 50 μm, and Ra is 0.35 μm.
Corrugation is a sine wave form.
Width of a contact portion of a piece of flat foil with a piece of corrugated foil is 10 μm.
While a piece of flat foil was being given a back tension of 10 kgf, it was wound together with a piece of corrugated foil, so that a metallic honeycomb, the outer diameter of which was 100 mm, was made. After solder was coated on an inner face of an outer cylinder, the outer cylinder was inserted into the metallic honeycomb body. Then, the metallic honeycomb body was heated to 1200° C. for 90 minutes in a vacuum of 10−2 Pa.
In this catalyst carrier, λb was 3.8 as shown in the following expression.
λb=6.8×10−12×1/(50×10−6)×√10/√(0.35×10−6)×4√1473×exp(15000/1473)×√(10×10−6)=3.8
In this connection,
7.52×109×exp(−35000/1473)=0.36≧8×10−2 is satisfied.
Thickness of pieces of flat foil and corrugated foil is 50 μm, and Ra is 0.15 μm.
Corrugation is a trapezoid.
Width of a contact portion of a piece of flat foil with a piece of corrugated foil is 100 μm.
While a piece of flat foil was being given a back tension of 10 kgf, it was wound together with a piece of corrugated foil, so that a metallic honeycomb, the outer diameter of which was 100 mm, was made. After solder was coated on an inner face of an outer cylinder, the outer cylinder was inserted into the metallic honeycomb body. Then, the metallic honeycomb body was heated to 1200° C. for 90 minutes in a vacuum of 10−2 Pa.
In this catalyst carrier, λb was 18.0 as shown in the following expression.
λb=6.8×10−12×1/(50×10−6)×√10/√(0.15×10−6)×4√1473×exp(15000/1473)×√(100×10−6)=18.0
In this connection,
7.52×109×exp(−35000/1473)=0.36≧8×10−2 is satisfied.
Thickness of pieces of flat foil and corrugated foil is 20 μm, and Ra is 0.15 μm.
Corrugated is a sine wave form.
Width of a contact portion of a piece of flat foil with a piece of corrugated foil is 10 μm.
While a piece of flat foil was being given a back tension of 10 kgf, it was wound together with a piece of corrugated foil, so that a metallic honeycomb, the outer diameter of which was 100 mm, was made. After solder was coated on an inner face of an outer cylinder, the outer cylinder was inserted into the metallic honeycomb body. Then, the metallic honeycomb body was heated to 1200° C. for 90 minutes in a vacuum of 10−2 Pa.
In this catalyst carrier, λb was 9.0 as shown in the following expression.
λb=6.8×10−12×1/(20×10−6)×√2/√(0.15×10−6)×4√1473×exp(15000/1473)×√(10×10−6)=9.0
In this connection,
7.52×109×exp(−35000/1473)=0.36≧8×10−2 is satisfied.
Thickness of pieces of flat foil and corrugated foil is 20 μm, and Ra is 0.15 μm.
Corrugation is a trapezoid.
Width of a contact portion of a piece of flat foil with a piece of corrugated foil is 100 μm.
While a piece of flat foil was being given a back tension of 10 kgf, it was wound together with a piece of corrugated foil, so that a metallic honeycomb, the outer diameter of which was 100 mm, was made. After solder was coated on an inner face of an outer cylinder, the outer cylinder was inserted into the metallic honeycomb body. Then, the metallic honeycomb body was heated to 1200° C. for 90 minutes in a vacuum of 10−2 Pa.
In this catalyst carrier, λb was 20.0 as shown in the following expression.
λb=6.8×10−12×1/(20×10−6)×√2/√(0.15×10−6)×4√1473×exp(15000/1473)×√(100×10−6)=20.0
In this connection,
7.52×109×exp(−35000/1473)=0.36≧8×10−2 is satisfied.
Thickness of pieces of flat foil and corrugated foil is 20 μm, and Ra is 0.35 μm.
Corrugation is a sine wave form.
Width of a contact portion of a piece of flat foil with a piece of corrugated foil is 10 μm.
While a piece of flat foil was being given back tension of 2 kgf, it was wound together with a piece of corrugated foil, so that a metallic honeycomb, the outer diameter of which was 100 mm, was made. After solder was coated on an inner face of an outer cylinder, the outer cylinder was inserted into the metallic honeycomb body. Then, the metallic honeycomb body was heated to 1250° C. for 90 minutes in a vacuum of 10−2 Pa.
In this catalyst carrier, λb was 30.5 as shown in the following expression.
λb=6.8×10−12×1/(20×10−6)×√2/√(0.35×10−6)×4√1523×exp(15000/1523)×√(10×10−6)=30.5
In this connection,
7.52×109×exp(−35000/1523)=0.75≧8×10−2 is satisfied.
In this connection,
With respect to Conventional Examples 1 and 2 and Examples 1 to 3 of the present invention, a thermal durability test of engine was conducted, in which the temperature of entry gas was 950° C. and it was turned on for 10 minutes and turned off for 10 minutes, which was determined to be one cycle. The results of evaluation are shown on Table 2.
According to the results of the above experiments, the following can be concluded. The present invention can provide a diffusion bonded metallic catalyst carrier, comprising: a honeycomb body composed of a piece of flat foil made of heat-resistant stainless steel containing aluminum and a piece of corrugated foil made of stainless steel, the piece of corrugated foil and the piece of flat foil being alternately wound; and an outer cylinder made of metal into which the honeycomb body is incorporated, the honeycomb body and the outer cylinder being integrated into one body by means of diffusion bonding,
the diffusion bonded metallic catalyst carrier being manufactured in a condition so that λb, which is defined by
λb=6.8×10−12×δf−1×F1/2×Rac−1/2×T1/4×exp(15000/T)×b1/2,
can be in a range from 8 to 20 where thickness of the strip of foil is δf (m), average roughness of the foil surface in the width direction is Ra (m), back tension in the case of winding is F (kgf), contact width of the piece of flat foil with the piece of corrugated foil is b (m), heat treatment temperature is T (K), and degree of vacuum is Pout (Pa). When the diffusion bonded metallic catalyst carrier is manufactured as described above, it is possible to ensure a quantity of vaporized aluminum necessary for diffusion bonding, so that the mechanical strength of the diffusion bonded joint can be guaranteed. When a quantity of vaporized aluminum is minimized, the resistance to oxidation can be maximized. In this way, it is possible to provide a high quality diffusion bonded metallic catalyst carrier.
In this case, a proportion constant C is determined to be C=6.8×10−12. That is, it is determined that C=6.8×10−12 when the thermal durability test of an engine is conducted wherein one cycle is set in such a manner that the catalyst carrier is turned on for 10 minutes and turned off of 10 minutes at the entry gas temperature of 950° C. When the test condition is changed, C is also changed. Therefore, C can be found as a dependent variable of the condition of the thermal durability test of an engine by experiments.
In this example, pieces of flat foil and corrugated foil were made of stainless steel containing aluminum at 5 weight %. In Examples 1 and 2 of the present invention and also in Comparative Example, thickness T of pieces of foil is 30 μm. In Example 3 of the present invention, thickness of a piece of flat foil on the entry side of exhaust gas is 60 μm and thickness of a piece of flat foil on the delivery side of exhaust gas is 30 μm, and thickness is linearly changed. Thickness of a piece of corrugated foil is uniformly 30 μm.
In Examples 1 and 2 of the present invention and also in Comparative Example, the configuration of a piece of corrugation-form was a sine wave, and the height of a wave was 1.25 mm and the pitch of a wave was 2.5 mm. In Example 2 of the present invention, the corrugation on the entry side of exhaust gas was a trapezoid, the corrugation on the delivery side of exhaust gas was a sine wave, the length of a trapezoidal portion was 20 mm, and a configuration of the transition portion between the trapezoid and the sine wave-form is gradually changed. The height of the wave was 1.25 mm, the pitch was 2.5 mm, and width W of the contact portion of the piece of flat foil with the piece of corrugated foil was 0.3 mm. A configuration of the corrugation of the piece of corrugated foil can be changed by changing a configuration of a die used for making the piece of corrugated foil when the piece of flat foil is corrugated.
The thus corrugated piece of corrugated foil and the piece of flat foil were wound so that a honeycomb body, the diameter of which was 88 mm and the length of which was 120 mm, was made. This honeycomb body was inserted into an outer cylinder made of stainless steel, the inner diameter of which was 87 mm, the thickness of which was 1.5 mm and the length of which was 125 mm. In this way, a metallic support was made.
In Example 1 of the present invention, before the pieces of flat foil and corrugated foil were wound, portions on both sides of the piece of flat foil on the entry side of exhaust gas, the width of which was 20 mm, were coated with adhesive. After that, the pieces of flat foil and corrugated foil were wound and press-fitted into the outer cylinder, so that the catalyst carrier was made. Before the coated adhesive was dried, powder of solder was scattered in a range from a gas passage of the catalyst carrier to the inside of the catalyst carrier. Due to the foregoing, powder of solder was made to adhere to the portion coated with adhesive. Under the above condition, the catalyst carrier was put into a vacuum treatment furnace so as to conduct diffusion bonding. In the furnace, the catalyst carrier was heated to 1150° C. and kept at the temperature for 60 minutes. In this way, diffusion bonding was carried out. When the catalyst carrier was heated to high temperature as described above, powder of solder was melted and solidified after the completion of vacuum treatment. In this way, the soldered section was completed. In Examples 2 and 3 of the present invention and also in Comparative Example, vacuum treatment was carried out in the same manner as that of Example 1 of the present invention, and all joined portions of the catalyst carrier were subjected to diffusion bonding.
The thus manufactured catalyst carrier was arranged right after the exhaust manifold of a gasoline engine of 4 cylinders, and a thermal repetition test of 900° C.×20 minutes→150° C.×30 minutes was conducted for 600 cycles, and damage of the catalyst carrier was investigated. As a result of the investigation, a defect was found in one portion of the catalyst carrier on the entry side of exhaust gas in Comparative Example, however, no defects were found in the catalyst carrier of Examples of the present invention.
According to the present invention, it is possible to propose a manufacturing condition by which the bond strength of diffusion bonded joint and the resistance to oxidation can be made to be compatible with each other. Therefore, when a diffusion bonded metallic catalyst carrier is manufactured according to the condition proposed by the present invention, it is possible to manufacture a high quality diffusion bonded metallic catalyst carrier.
According to the present invention, the rigidity of a piece of foil on the entry side of exhaust gas of the catalyst carrier is high. Therefore, even if a drift current of exhaust gas exists, there is no possibility of damage to the catalyst carrier. On the delivery side of exhaust gas, diffusion bonding is conducted by the most appropriate foil thickness and the most appropriate foil configuration. Accordingly, advantages of the diffusion bonded metallic catalyst carrier can be fully utilized.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-65088 | Mar 1998 | JP | national |
This application is a continuation application under 35 U.S.C. §120 of prior application Ser. No. 09/423,944 filed Feb. 22, 2000, now U.S. Pat. No. 6,761,857, which is a 35 U.S.C. §371 of PCT/JP99/01297 filed Mar. 16, 1999, wherein PCT/JP99/01297 was filed and published in the Japanese language. The entire disclosure of prior application Ser. No. 09/423,944, which is a 35 U.S.C. §371 of PCT/JP99/01297, is considered part of this continuation application and is hereby incorporated by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4752599 | Nakamura et al. | Jun 1988 | A |
| 4870046 | Yamanaka et al. | Sep 1989 | A |
| 6689328 | Otani et al. | Feb 2004 | B1 |
| 6761857 | Takahashi et al. | Jul 2004 | B1 |
| Number | Date | Country |
|---|---|---|
| 08-038912 | Feb 1996 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20040258943 A1 | Dec 2004 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09423944 | US | |
| Child | 10830885 | US |