DIGITALLY RECEPTIVE COATING METHOD

Abstract

A digitally receptive coating method includes the steps of applying a digitally receptive coating to a first side of a film, metalizing the first side of the film and bonding the metallized first side of the film to a substrate to produce a laminate having a digitally receptive coating.

Description

FIELD OF THE INVENTION

The present invention relates generally to a digitally receptive coating method and, more particularly, to a digitally receptive coating method using transfer lamination.

BACKGROUND OF THE INVENTION

Currently, a laminate is manufactured using a paper stock that has a clay coating on both the face and the back sides. The clays coating imparts certain desirable qualities to the paper such as surface gloss, smoothness and reduced ink absorbency. Such double coated papers are utilized in the packaging industry, for postcards, for advertising materials and in magazines.

As is currently known in the art, such a clay-coated laminate may be made using transfer lamination. Transfer lamination is a process by which a layer of material is applied to a substrate. Generally, transfer lamination involves bonding a transfer film having a application layer, e.g., a metallized layer, to a paper substrate, stripping the film from the substrate leaving the application layer, and then applying a coating to the layer to facilitate printing. As will be appreciated, this process typically involves multiple, separate steps.

In particular, an untreated film, such as a polyester film, that has a micro-embossable coating that has been micro-embossed and metallized is laminated to the face side of a clay-coated paper substrate using a water-based adhesive. The film layer is then stripped away, leaving the micro-embossable coating and metalizing on the face side surface. A digitally receptive coating is then applied to the laminated sheet.

A drawback to this method is that when the digitally receptive coating is applied to the front side of the laminate, the clay coating on the back side can “offset” or transfer to the front side of the laminate during storage. This is due in part to the paper laminate being wound up tightly in a roll after the digitally receptive coating is applied. In particular, as the finished laminate is being wound up into a roll, inter-layer slippage and/or rubbing between the front and back sides of the laminate may cause the clay coating on the back of the laminate to transfer to front of the laminate and adhere to the digitally receptive coating. Moreover, the digitally receptive coating on the front of the laminate is generally soft and acts like a quasi-adhesive under the tension of being wound in a roll, causing specs of the clay coating to pull from the back side of the laminate and stick to the digitally receptive coating on the front side. As a result, the digitally receptive coating may have specs of clay adhered thereto which can result in the finished laminate being “milky” or “hazy” in appearance.

In view of the above, it is desirable to produce a laminate wherein clay transfer and marring is minimized. Moreover, a need exists for a digitally receptive coating method which eliminates or reduces clay transfer. As discussed in detail herein, the present invention addresses these needs.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide a digitally receptive coating method.

It is another object of the present invention to provide a digitally receptive coating method that utilizes transfer lamination.

It is another object of the present invention to provide a digitally receptive coating method whereby clay transfer is eliminated or reduced.

It is another object of the present invention to provide a digitally receptive coating method whereby a produced laminate may be stored in roll form without substantial clay transfer.

It is another object of the present invention to provide a digitally receptive coating method whereby the digitally receptive coating is substantially smooth as compared to existing methods.

It is another object of the present invention to provide a digitally receptive coating method in which a digitally receptive coating is applied to a transfer film.

These and other objects, features and advantages of the present invention will become apparent in light of the detailed description of the best mode embodiment thereof, as illustrated in the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flowchart illustrating a prior art method for transfer lamination.

FIG. 2 is an illustration of a prior art transfer film construction.

FIG. 3 is an illustration of a prior art laminate construction at a point prior to removing the transfer film.

FIG. 4 is an illustration of a prior art laminate construction after the film has been removed and a digitally receptive coating applied.

FIG. 5 is a flowchart illustrating a digitally receptive coating method in accordance with an embodiment of the present invention.

FIG. 6 is an illustration of a transfer film construction in accordance with an embodiment of the present invention.

FIG. 7 is an illustration of a laminate construction in accordance with an embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

Referring to FIGS. 1 and 2, known processes for producing a clay-coated laminate having a digitally receptive coating for digital printing involve the following general steps. The first of these steps, labeled with reference numeral 10, is to coat an untreated polyester film 12 with a micro-embossable coating layer 14. The film 12 is then either metallized, as shown at step 20, or micro-embossed and then metallized. The step of metallization involves placing the film 12 in a large metallizer where metals, such as aluminum 16, are vacuum deposited or deposited by other means known in the art, on the film 12. The construction of the transfer film after metallization is shown in FIG. 2. As shown therein, subsequent to metallization, the transfer film includes an untreated polyester film 12, a micro-embossable coating layer 14, and a metal layer 16.

Once the film has been metallized, it is bonded to a paperboard substrate 18 in a third step, represented by reference numeral 30. In this step, a water-based adhesive 22 is applied to the film and the film is laminated to the face side of a paperboard substrate 18 (having a clay coating on both sides). Alternatively, the adhesive 22 may be a solvent-based adhesive, energy curable adhesive, or other type of adhesive known in the art, without departing from the broader aspects of the present invention.

The construction of the laminate following step 30 is shown in FIG. 3. As shown therein, the construction includes a paperboard substrate 18 with a clay coating on both the face and back sides, a water-based adhesive layer 22, a metal layer 16, a micro-embossable coating layer 14 and the untreated polyester film 12 forming the top layer.

As shown in step 40, the film is then stripped off, leaving the thin metal layer 16 bonded to the paper substrate 18. At step 50, a digitally receptive coating 24 is then applied to the face side of the laminate. This digitally receptive coating allows for digital printing, such as text, designs, pictures or the like, on the laminate. This process is described in further detail in U.S. Patent Application Publication No. 2010/0314036, which is hereby incorporated by reference herein in its entirety.

As shown in FIG. 4, once the film 12 is stripped off and the digitally receptive coating applied, the finished laminate construction includes a paperboard substrate 18 with a clay coating on both the face and back sides, a water-based adhesive layer 22, a metal layer 16, a micro-embossable coating layer 14 and a digitally receptive coating 24 on top.

As discussed above, however, this process may be problematic, especially when the laminate is wound into a roll for storage and the like. In particular, the digitally receptive coating 24 may be sensitive to excessive pressure such that when the finished laminate is would up tightly in a roll, the digitally receptive coating 24 may adhere slightly to the clay coated back of the laminate and cause an effect known as “offsetting,” where part of the clay coating transfers to the digitally receptive coating 24, causing an unsightly, “hazy” look. Rolls of laminate produced by this method, therefore, must be sheeted immediately to minimize this effect.

Turning now to FIG. 5, the inventive digitally receptive coating method 100 of the present invention substantially eliminates offsetting, leaving the digitally receptive coating 24 with a smooth and mirror-like finish. The method 100 includes first coating an untreated polyester film 12 with a digitally receptive coating layer 24. This step is represented by reference numeral 110. In the preferred embodiment, the digital coating 24 is applied at a coat weight of approximately 0.15 to 0.40 dry pounds per 3000 square feet. Next, a micro-embossable coating layer 14 is applied to the digitally receptive coating 24, as shown at step 120. In the preferred embodiment, the micro-embossable coating layer 14 is applied at a coat weight of 0.7-1.5 dry pounds per 3000 square feet, although other coat weights are certainly possible without departing from the broader aspects of the present invention. The film 12 is then either metallized, as shown at step 130, or micro-embossed and then metallized. In an embodiment, metallization involves depositing a thin layer of aluminum on the micro-embossable coating layer 14.

At this point in the process, the transfer film construction includes the untreated polyester film 12, a digitally receptive coating layer 24, a micro embossable coating layer 14 and a metal layer 16. Importantly, the digitally receptive coating layer is actually applied to the transfer film 12, not the finished laminate, and is intermediate the metal layer and the film 12. This construction is illustrated in FIG. 6.

Once the film has been metallized, it is bonded to a paperboard substrate 18 in a fourth step, represented by reference numeral 140. In this step, a water-based adhesive 22 is applied to the transfer film 12 and then the film 12 is then laminated to the face side of a paperboard substrate 18 (having a clay coating on both sides). Importantly, the resulting laminate remains in this state until it is ready to be sheeted, at which time the film 12 is stripped/removed. After laminating the transfer film to the paper substrate 18, the laminate, including the film 12, can be wound into a roll for storage, as shown at step 150.

As will be readily appreciated, after adhering the transfer film to the paperboard substrate 18, the laminate construction includes a paperboard substrate 18 with a clay coating on both the face and back sides, a water-based adhesive layer 22, a metal layer 16, a micro-embossable coating layer 14, a digitally receptive coating layer 24 and the untreated polyester film 12 forming the top layer. This construction is shown in FIG. 7. Importantly, the untreated polyester film 12 is left on top of the laminate and serves to protect the digitally receptive coating 24. In particular, when the finished laminate is would into a roll, the film 12 serves as a buffer between the “soft” and “sticky” digitally receptive coating layer 24 and the clay-coated back side of the paperboard 18. In this manner, the film 12 prevents the digitally receptive coating 24 from contacting the clay-coated back side of the paperboard substrate 18 while in roll form.

Moreover, because the digitally receptive coating 24 is applied to the film 12 prior to laminating the film to the paperboard 18 (rather than applying it to the laminate as a final step), the film may be left on the laminate, rather than stripped off, until just prior to sheeting. As noted above, the laminate may then be wound tightly in a roll and stored without the clay transfer issue that has hampered prior methods.

When the finished laminate is sheeted, the film 12 is finally stripped off. The laminate is then sheeted and stacked. As will be readily appreciated, the interlay pressure is less in sheeted form than in roll form, so the offsetting or clay transfer is minimized or eliminated.

In addition to eliminating the clay transfer issue, waste associated with known processes is reduced. Furthermore, the finished surface of the digitally receptive coating 24 is much smoother as compared to the finished surface of the laminate manufactured utilizing known processes. This is a result the fact that the polyester film 12 to which the digitally receptive coating 24 is applied during the inventive method 100 is much smoother than micro-embossable coating layer 14 to which the digitally receptive coating 24 has been applied in existing processes. The method of the present invention also is more environmentally friendly than existing methods, as once the film 12 is finally stripped, the produced laminate is easier to recycle.

Although this invention has been shown and described with respect to the detailed embodiments thereof, it will be understood by those of skill in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiments disclosed in the above detailed description, but that the invention will include all embodiments falling within the scope of this disclosure.

Claims

1. A method of forming a laminate construction, comprising the steps of: applying a print receptive coating to a first side of a film;applying at least one of a micro-embossable coating and a metallized layer to said print receptive coating; andbonding said film with said at least one of said micro-embossable coating and said metallized layer to a substrate to form a laminate construction.

2. The method according to claim 1, further comprising the step of: removing said film from said laminate construction to expose said print receptive coating.

3. The method according to claim 2, wherein: said step of removing said film from said laminate construction is carried out utilizing a transfer lamination stripping process.

4. The method according to claim 1, wherein: said substrate is a paperboard substrate having a clay coating on a face side of said paperboard substrate and a back side of said paperboard substrate.

5. The method according to claim 1, further comprising the step of: winding said laminate construction into a roll such that said film serves as a buffer between said substrate and said print receptive coating.

6. The method according to claim 5, further comprising the steps of: unwinding said roll;removing said film from said laminate construction to expose said print receptive coating; andsheeting said laminate construction.

7. The method according to claim 1, wherein: said step of applying said print receptive coating to said first side of said film imparts a smoothness to said print receptive coating that corresponds to a smoothness of said first side of said film.

8. The method according to claim 1, wherein: said step of bonding said film with said at least one of said micro-embossable coating and said metallized layer to said substrate includes applying an adhesive to at least one of said substrate and/or said at least one of said micro-embossable coating and said metallized layer.

9. The method according to claim 1, wherein: said film is a polyester transfer film.

10. A digitally receptive coating method, comprising the steps of: applying a digitally receptive coating layer to a first side of a transfer film to impart a smoothness to said digitally receptive coating layer that corresponds to a smoothness of said first side of said transfer film;applying at least one of a micro-embossable coating layer and a metallized layer to said digitally receptive coating layer; andbonding said transfer film with said at least one of said micro-embossable coating layer and said metallized layer to a substrate to form a laminate construction, and in a manner such that said transfer film is removable from said laminate construction.

11. The digitally receptive coating method according to claim 10, further comprising the step of: stripping said transfer film from said laminate construction to expose said digitally receptive coating layer.

12. The digitally receptive coating method according to claim 10, wherein: said substrate is a paperboard substrate having a clay coating on a face side of said paperboard substrate and a back side of said paperboard substrate.

13. The digitally receptive coating method according to claim 12, further comprising the step of: winding said laminate construction into a roll such that said transfer film serves as a buffer between said substrate and said digitally receptive coating layer to prevent clay transfer from said back side of said paperboard substrate onto said digitally receptive coating layer.

14. The digitally receptive coating method according to claim 13, further comprising the steps of: unwinding said roll;removing said transfer film from said laminate construction to expose said digitally receptive coating layer; andsheeting said laminate construction.

15. The digitally receptive coating method according to claim 10, wherein: said step of bonding said transfer film with said at least one of said micro-embossable coating layer and said metallized layer to said substrate includes applying an adhesive to at least one of said substrate and/or said at least one of said micro-embossable coating layer and said metallized layer.

16. The digitally receptive coating method according to claim 10, wherein: the transfer film is a polyester transfer film.

17. A digitally receptive coating method, comprising the steps of: applying a digitally receptive coating layer to a first side of a polyester transfer film to impart a smoothness to said digitally receptive coating layer that corresponds to a smoothness of said first side of said polyester transfer film;applying at least one of a micro-embossable coating layer and a metallized layer to said digitally receptive coating layer;applying an adhesive to at least one of a paperboard substrate and/or said at least one of said micro-embossable coating layer and said metallized layer and bonding, via said adhesive, said polyester transfer film to said substrate to form a laminate construction; andstripping said polyester transfer film from said laminate construction to expose said digitally receptive coating layer having a smooth surface.

18. The digitally receptive coating method according to claim 17, wherein: said substrate is a paperboard substrate having a clay coating on a face side of said paperboard substrate and a back side of said paperboard substrate; andwherein said method further includes the step of winding said laminate construction into a roll such that said polyester transfer film serves as a buffer between said paperboard substrate and said digitally receptive coating layer.