This application claims priority to and the benefit of Korean Patent Application No. 10-2019-0051701 filed in the Korean Intellectual Property Office on May 2, 2019, the entire contents of which are incorporated herein by reference.
The present invention relates to a dip-coating method and apparatus. More particularly, the present invention relates to a dip-coating method of dipping a coating target in a liquid including a coating material to be coated and a dip-coating apparatus therefor. Also, the present invention relates to a method for fabricating a hollow tube by using the dip-coating method and apparatus.
Coating is a technology for covering a surface of a solid mold with a material of a liquid or semi-liquid state and is used in aesthetic or functional aspects, and various coating technologies have been developed depending on a purpose and material. For example, methods for forming a liquid coating layer include dip-coating, roller coating, spray coating, and flow coating.
The dip-coating method is a method in which a target is immersed in a coating liquid and is pulled up and then dried after preventing the excess coating liquid from flowing, and this is also called dipping. This method is simple to operate and may be applied to coat the entire surface of a target having a complex shape, small parts, and parts having a three-dimensional design. However, as a drawback, the thickness of the coating film is not uniform, and the coating material is easily aggregated in the lower part.
In a typical dip-coating method performed in air, the thickness and uniformity of the coated film are determined according to characteristics (curing rate, surface tension, viscosity, etc.) of the coating solution. When coating to form a film with a macroscopic thickness, in a case in which the curing rate is slow, the uncured solution flows in the direction of gravity, which may cause a difference in the thickness between the upper and lower ends of the film. In addition, in the case of the three-dimensional mold, a phenomenon in which the coating solution is formed in a portion where a curve is severe may occur.
Therefore, there is a need for a method of uniformly coating the film having the macroscopic thickness regardless of the shape of the mold.
The above information disclosed in this Background section is only for enhancement of understanding of the background of the invention, and therefore it may contain information that does not form the prior art that is already known in this country to a person of ordinary skill in the art.
One aspect of the present invention is to provide a dip-coating method capable of forming a coating film of a uniform thickness by offsetting the effect of gravity acting on a coating liquid applied to a target mold by using a supporting liquid.
Another aspect of the present invention is to provide a dip-coating apparatus capable of performing the dip-coating method described above.
A further aspect of the present invention is to provide a method for fabricating a hollow tube by utilizing the dip-coating method using the supporting liquid.
A dip-coating method as a method for coating an outer surface of a target mold according to an exemplary embodiment of the present invention includes steps of: preparing and putting a supporting liquid in a container; applying a coating material to the target mold; dipping the target mold in the supporting liquid; shaking the target mold surrounded by the coating material in the supporting liquid; curing the coating material surrounding the target mold in the supporting liquid; and taking out the coated target mold from the supporting liquid.
The preparing and putting the supporting liquid in the container may further include pouring the coating material onto the supporting liquid, and the dipping the target mold in the supporting liquid may further include immersing the target mold in the supporting liquid through the coating material.
The applying the coating material to the target mold may further include preparing and putting the coating material in a separate container from the supporting liquid, immersing the target mold in the coating material and taking the target mold out, and then again immersing the target mold in the supporting liquid.
The supporting liquid may be formed of a material that does not react with or is not mixed with the coating material.
A density of the supporting liquid may be equal to or larger than a density of the coating material.
An interface tension between the supporting liquid and the coating material may be 5 mN/m or more and 30 mN/m or less.
The supporting liquid includes water, glycerol, and a surfactant.
The dip-coating method of the present exemplary embodiment may further include vibrating the target mold by using a 3-axis linear stage to remove the coating material formed at a portion.
The dip-coating method of the present exemplary embodiment may further include rotating the target mold to remove the coating material formed at the portion.
The curing the coating material surrounding the target mold in the supporting liquid may include applying heat to the coating material to be cured.
The curing the coating material surrounding the target mold in the supporting liquid may include irradiating light to the coating material to be cured.
A fabricating method of a hollow tube according to another exemplary embodiment of the present invention includes steps of: preparing the coated target mold by using the dip-coating method described above; removing the target mold in the coating film; and manufacturing a hollow tube with the remaining coating film.
According to the dip-coating method according to an exemplary embodiment of the present invention, the effect of gravity acting on the coating liquid applied to the target mold may be offset by using the supporting liquid, thereby forming a coating film of a uniform thickness. According to the fabricating method of the hollow tube according to another exemplary embodiment of the present invention, the hollow tube having the uniform thickness may be manufactured by utilizing the dip-coating method using the supporting liquid.
Hereinafter, the present invention will be described more fully with reference to the accompanying drawings, in which exemplary embodiments of the invention are shown. The drawings and description are to be regarded as illustrative in nature and not restrictive. Like reference numerals designate like elements throughout the specification.
Referring to
Referring to
In the step of preparing and putting the supporting liquid 20 in the container 23, the coating material 25 may be poured onto the supporting liquid 20 to be prepared. The supporting liquid 20 may be made of a material that does not mix with the coating material 25, and its density is equal to or at least slightly larger than the density of the coating material 25. Therefore, the supporting liquid 20 is disposed under the coating material 25 in the container 23 (See
The coating material 25 should not mix or react with the supporting liquid 20, and should have the same density as or at least slightly lower than that of the supporting liquid 20. As the coating material 25, for example, polydimethylsiloxane (PDMS), Ecoflex™, DragonSkin™, etc. may be used.
The coating material may be a thermally curable material or a photocurable material. Therefore, when curing the coating material made of the thermally curable material, heat is applied, while when curing the coating material made of the photo curable material, light is irradiated. As the thermally curable coating material, for example, polydimethylsiloxane (PDMS), Ecoflex™, Dragon Skin™, etc. may be used, and as the photocurable coating material, photocurable polydimethylsiloxane may be used, and for example, in the case of the photocurable polydimethylsiloxane, the curing is possible by using light of an ultraviolet ray region (e.g., a 365 nm wavelength).
Next, the coating material 25 is coated on a target mold 10 (S120). Then, the target mold 10 is immersed in the supporting liquid 20 (S130).
When the coating material 25 and the supporting liquid 20 are contained in one container 23, the coating material 25 may be coated by dipping the target mold 10 into the supporting liquid 20.
Alternatively, when preparing the coating material 25 in a separate container from that of the supporting liquid 20, the target mold 10 may be immersed in the coating material 25 to be coated. That is, the target mold 10 may be immersed in the coating material 25 contained in the separate container, be taken out at a constant speed, and then be immersed again in the supporting liquid 20.
The target mold 10 may be a mold of a three-dimensional shape. The target mold 10 of the three-dimensional shape, for example, may be an artificial blood vessel model mold. The target mold 10 of the three-dimensional shape may be made by using a 3D printer for example. The material forming the target mold 10, for example, acrylonitrile butadiene styrene (ABS) polymer, polylactic acid (PLA), etc. may be used. Also, the coating material 25 may have higher wettability with the target mold 10 than the supporting liquid 20. That is, a contact angle of the coating material 25 for the target mold 10 may be relatively lower than the contact angle of the supporting liquid 20 thereto.
As shown in
Referring to
Next, the target mold 10 surrounded by the coating material 25 is gently shaken in the supporting liquid 20 (S140).
The 3-axis linear stage 40 is provided on the top of the target mold 10 to generate a vibration. The 3-axis linear stage 40 may be connected to an end of a stainless steel post extending to one axis of the clamp 15. If the target mold 10 is vibrated in the 3 axes by using this 3-axis linear stage 40, the coating material formed on the part in which the bending is severe may be removed to form a uniform coating film (See
Next, the coating material 25 surrounding the target mold 10 is cured in the supporting liquid 20 (S150).
When the target mold 10 is surrounded by a thermally curable coating material, the thermally curable coating material may be cured by applying heat. When the target mold 10 is surrounded by a photocurable coating material, the photocurable coating material may be cured by irradiating light.
Next, the target mold 10 on which a coating film 25a is formed is taken out from the supporting liquid 20 (S160).
After taking it out, if the supporting liquid 20 is removed from the target mold 10 on which the coating film 25a is formed, the dip-coating process is completed.
Capillary pressure, adherence, and gravity act on the uncured coating material 25 applied to the target mold 10. At this time, while the force of gravity acts larger than the other two forces, the net force is directed toward the direction of gravity, and as a result, as shown in
Since the supporting liquid 20 is used in the dip-coating method according to the present exemplary embodiment, in addition to the capillary pressure, the adherence, and gravity, buoyancy acts on the uncured coating material 25 applied to the target mold 10. In other words, as the buoyancy force acts in the opposite direction of gravity, the net force becomes close to zero while forming an approximate equilibrium with gravity. Therefore, the uncured coating material 25 may form the coating film 25a of a uniform thickness on the surface of the target mold 10 without sagging.
Referring to
Referring to
Referring to
Then, the target mold 10 surrounded by the coating material 25 and is gently shaken in the supporting liquid 20 (S240), the coating material 25 surrounding the target mold 10 is cured in the supporting liquid 20 (S250, See
Next, the target mold 10 inside the coating film 25a is removed (S270). For example, when the target mold 10 is acrylonitrile butadiene styrene, acetone may be used, and in the case of polylactic acid, the target mold 10 may be removed through chloroform, benzene, and other chlorinated organic solvents.
When the target mold 10 is removed in this way, and a hollow tube is manufactured with the remaining coating film 25a (S280, See
While this invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments. On the contrary, it is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims.
Number | Date | Country | Kind |
---|---|---|---|
10-2019-0051701 | May 2019 | KR | national |
Number | Name | Date | Kind |
---|---|---|---|
1831212 | Voss et al. | Nov 1931 | A |
5725667 | Petropoulos et al. | Mar 1998 | A |
6497916 | Taylor et al. | Dec 2002 | B1 |
6569375 | McGlothlin et al. | May 2003 | B1 |
8227016 | Thornton et al. | Jul 2012 | B2 |
20080040835 | Miyamoto et al. | Feb 2008 | A1 |
20160130690 | Winn et al. | May 2016 | A1 |
20170148356 | Black et al. | May 2017 | A1 |
20180333902 | McGlothlin et al. | Nov 2018 | A1 |
Number | Date | Country |
---|---|---|
H10-407 | Jan 1998 | JP |
2008-012396 | Jan 2008 | JP |
4330557 | Sep 2009 | JP |
2011-525137 | Sep 2011 | JP |
2017-527322 | Sep 2017 | JP |
10-2018-0083919 | Jul 2018 | KR |
Entry |
---|
Rajasubramanian, Ganesh, et al. “Fabrication of resorbable microporous intravascular stents for gene therapy applications.” ASAIO journal 40.3 (Jul. 1994): M584-M589. (Year: 1994). |
Ceratti, Davide R., et al. “A new dip coating method to obtain large-surface coatings with a minimum of solution.” Advanced Materials 27.34 (Jul. 21, 2015): 4958-4962. (Year: 2015). |
Lim, Jongkyeong, et al. “A new dip coating method using supporting liquid for forming uniformly thick layers on serpentine 3D substrates.” Advanced Materials Interfaces 6.24 (Nov. 12, 2019): 1901485. (Year: 2019). |
Jaewook Nam, “Roll-To Roll Coating Process Overview and Future Tasks”, News & Information for Chemical Engineers, vol. 28, No. 5, 2010. |
Number | Date | Country | |
---|---|---|---|
20200346375 A1 | Nov 2020 | US |