Direct-flame fuel cell

Abstract

A direct-flame fuel cell according to the invention has a cell in which a solid electrolyte 1 is sandwiched between an anode 2 and a cathode 3. The anode 2 contains one or more kinds of alkaline metal compounds or alkaline earth metal compounds which are effective in suppressing soot generation due to exposure to a flame. Where the anode 2 includes two or more layers 2a and 2b, the one or more kinds of alkaline metal compounds or alkaline earth metal compounds are contained in the outermost layer 2b.

Description

BACKGROUND OF THE INVENTION

The present invention relates to a direct-flame fuel cell which uses a cell that is configured in such a manner that a solid electrolyte is sandwiched between an anode and a cathode.

Among various types of fuel cells is a direct-flame fuel cell in which power is generated by placing a cell inside or in the vicinity of a flame and thereby exposing the anode side to the flame, the cell being configured in such a manner that a solid electrolyte is sandwiched between an anode and a cathode. This type of direct-flame fuel cell is disclosed in JP-A-2004-139936.

Since the anode is directly exposed to a flame, the direct-flame fuel cell can generate power in a simple and easy way and enables miniaturization of a fuel cell module in which cells are combined as desired. Furthermore, with a high degree of freedom of fuel selection, it is expected that the direct-flame fuel cell will be applied to various uses.

In the direct-flame fuel cell, since the surface of the anode of the cell is directly exposed to a flame during power generation, a large amount of soot is attached to the anode depending on the time of exposure to the flame. The soot that is attached to the anode is a cause of deteriorating the power generation performance of the cell to a large extent over time.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a direct-flame fuel cell which suppresses deterioration of the power generation performance of a cell by lowering the degree of attachment of soot to the anode.

According to the present invention, there is provided with a direct-flame fuel cell including:

a cell in which a solid electrolyte is sandwiched between an anode and a cathode, wherein

the anode contains one or more kinds of alkaline metal compounds or alkaline earth metal compounds.

According to the invention, the attachment of soot to the anode is suppressed by the function of the one or more kinds of alkaline metal compounds or alkaline earth metal compounds, whereby the deterioration of the power generation performance of the cell can be suppressed. The invention can thus provide a direct-flame fuel cell having a long life.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a schematic diagram showing an exemplary direct-flame fuel cell according to the present invention.

FIG. 2 is a graph showing output power reduction of a fuel cell using a cell having an anode in which no component that is effective in suppressing soot generation is added.

FIG. 3 is a graph showing output power reduction of a fuel cell using a cell having an anode in which Rh₂O₃ is added at 5 wt %.

FIG. 4 is a graph showing output power reduction of a fuel cell using a cell having an anode in which CaCO₃ and Rh₂O₃ are added at 3 wt % and 5 wt %, respectively.

FIGS. 5A to 5C are photographs, taken after power generation of 15 hours, of the anode surfaces of a sample using an outer anode layer in which neither Rh₂O₃ nor CaCO₃ is added, a sample using an outer anode layer in which only Rh₂O₃ is added, and a sample using an outer anode layer in which both of Rh₂O₃ and CaCO₃ are added.

FIG. 6 is a graph showing a relationship between the amount of CaCO₃ added in the outer anode layer and the time taken until the output power of the fuel cell decreases to 50% of an initial value.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

In a process of developing a technique for suppressing generation of soot that is attached to the anode of a direct-flame fuel cell, the present inventors have found that Rh₂O₃ which is added as an oxidation catalyst exhibits an effect of suppressing soot generation. Specifically, a cell is prepared in which, as shown in FIG. 1, an anode 2 having a two-layer structure (formed by an inner anode layer 2a made of samaria-doped ceria (SDC) (60 wt %)-Ni_0.9Co_0.1O and an outer anode layer 2b which is made of SDC (30 wt %)-Ni_0.9Co_0.1O added with Rh₂O₃ (5 wt %)) is provided on one side of a solid electrolyte 1 made of samaria-doped ceria (SDC) and a cathode 3 having a two-layer structure (formed by an inner cathode layer 3a made of SDC (50 wt %)-samarium strontium cobaltite (SSC) and an outer cathode layer 3b made of a cathode material of SDC (30 wt %)-SSC added with a pore-forming material (55 vol %)) is provided on the other side of the solid electrolyte 1. To transfer generated power to the outside, collectors 4 and 5 each of which is a platinum mesh are connected to the outer anode layer 2b and the outer cathode layer 3b, respectively of the cell of FIG. 1. For comparison, a comparative cell is prepared which had the same two-layer anode and cathode as the cell of FIG. 1 except that the outer anode layer does not contain Rh₂O₃. Each of the above cells is caused to generate power at a constant current (400 mA/cm²) while being exposed to a flame of a Bunsen burner to which a fuel-air mixture gas containing n-butane (6.5%), and a variation of the output power with time is observed.

FIGS. 2 and 3 show results of the comparative cell and the cell using the outer anode layer 2b that is added with Rh₂O₃, respectively. In the comparative cell, soot is generated remarkably immediately after the start of power generation and the output power decreased steeply. In the cell using the outer anode layer 2b that is added with Rh₂O₃, output power reduction due to soot generation is observed after a lapse of about 20 hours. However, even in this case, it is difficult to suppress soot generation in the long-term power generation experiment.

The inventors have found that compounds of alkaline earth metals such as calcium, barium, and strontium and compounds of alkaline metals such as sodium, potassium, and cesium are effective in suppressing soot generation by studying the soot generation suppressing effect (like the one Rh2O3 exhibits) of various substances, and have completed the invention on the basis of this fact.

Typical examples of such alkaline earth metal compounds are carbonates, oxides, hydroxides, nitrates, and sulfates of calcium, barium, and strontium. Typical examples of such alkaline metal compounds are carbonates, oxides, hydroxides, nitrates, and sulfates of sodium, potassium, and cesium. A mixture of alkaline metal compounds, a mixture of alkaline earth metal compounds, or a mixture of an alkaline metal compound and an alkaline earth metal compound may also be used.

For example, it has been found that if CaCO₃ is added at 3 wt % in the outer anode layer 2b (containing Rh₂O₃ at 5 wt %) of the above-described cell, soot generation can be suppressed satisfactorily and output power reduction is delayed as shown in FIG. 4.

FIGS. 5A to 5C are photographs, taken after power Generation of 15 hours, of the anode surfaces of sample 1 using an outer anode layer in which neither Rh₂O₃ nor CaCO₃ is added, sample 2 using an outer anode layer in which only Rh₂O₃ is added, and sample 3 using an outer anode layer in which both of Rh₂O₃ and CaCO₃ are added. It is seen that soot is attached to the entire surface of the anode in sample 1 (FIG. 5A; neither Rh₂O₃ nor CaCO₃ is added) and the degree of attachment of soot is lower in sample 2 (FIG. 5B; only Rh₂O₃ is added) than in sample 1. Almost no soot is attached to the anode in sample 3 (FIG. 5C; both of Rh₂O₃ and CaCO₃ are added). The same test is performed on a sample in which only CaCO₃ is added to produce a result that is the same as of sample 3.

The anode of the fuel cell according to the invention is not limited to the above-described one having a two-layer structure, and may have a multilayer structure of three or more layers or a single-layer structure (described below). In each case, it is important that the alkaline metal compound or the alkaline earth metal compound (essentially a non-conductive substance) which is effective in suppressing soot generation cue to exposure to a flame be added in the outermost layer of the cell that is directly exposed to a flame.

In practice, it is preferable that CaCO₃ be added at 1 to 10 wt % with respect to the amount of the anode materials irrespective of whether the anode contains Rh₂O₃. If the addition amount of CaCO₃ is smaller than 1 wt %, the effect of suppressing soot generation is slight. If it is larger than 10 wt %, output power reduction starts earlier contrary to the intention. In the case of a multi-layered anode, the amount of the compound such as CaCO₃ that is effective in suppressing soot generation is that in the outermost anode layer which is directly exposed to a flame.

In the cell of the direct-flame fuel cell according to the invention, each of the solid electrolyte, the anode, and the cathode can be produced by a general method by using materials of a member of cells of ordinary solid electrolyte fuel cells except that the alkaline metal compound or the alkaline earth metal compound is added in the anode which is directly exposed to a flame at a sufficient amount to suppress soot generation.

The material of the solid electrolyte may be one of the following materials (a), (b), and (c):

(a) Ceria-based ceramics such as SDC (samaria-doped ceria) or GDC (gadolia-doped ceria).

(b) Zirconia-based ceramics such as YSZ (yttria-stabilized zirconia), ScSZ (scandia-stabilized zirconia), or YSZ or ScSZ doped with Ce, Al, or the like.

(c) LSGM (lanthangallate) or bismuth-oxide-based ceramics.

The material of the anode may be one of the following materials (a), (b), (c), and (d):

(a) A cermet of nickel, cobalt, and yttria-stabilized-zirconia-based ceramics, scandia-stabilized-zirconia-based ceramics, or ceria-based ceramics (SDC, GDC, or YDC).

(b) A cermet of nickel and yttria-stabilized-zirconia-based ceramics, scandia-stabilized zirconia-based ceramics, or ceria-based ceramics (SDC, GDC, YDC, or the like).

(c) A sintered body having a conductive oxide as the main component (50 to 99 wt %). For example, the conductive oxide may be a solid solution of nickel oxide and lithium.

(d) A material obtained by adding a platinum-group metal or its oxide to one of the materials (a)-(d) at 1 to 10 wt %.

In the invention, a preferable anode electrode material is one containing a cermet of nickel oxide and cobalt oxide.

The material of the cathode may be a strontium (Sr)-added cobalate compound of a rare earth element such as lanthanum or samarium (e.g., samarium strontium cobaltite or lanthanum strontium cobaltite), a strontium-added manga-nate compound of lanthanum (e.g., lanthanum strontium manganite), a strontium-added gallate compound of lanthanum, or a strontium-added ferrite compound (e.g., lanthanum strontium cobalt ferrite). If necessary, a carbon-based pore-forming material or the like may be added in the cathode.

Each of the anode and the cathode may have either a single-layer structure or a multilayer structure. In the case of the multilayer structure, it is appropriate that the compound that contributes to suppression of soot generation, which is an important element of the invention, be added in the outermost portion (layer) of the anode that is directly exposed to a flame. In the case of the multilayer structure, the number of layers of the anode or cathode may be two or more.

The direct-flame fuel cell according to the invention is useful as a single-cell fuel cell which generates power in an atmosphere that is a mixture of a fuel component and an oxidizing agent component, and is particularly useful as an open-to-air fuel cell which generates power in a state that the cell is exposed to a flame in an open-to-air atmosphere rather than in a state that the cell is placed in a closed space.

EXAMPLES

Although Examples of the invention will be described below, the invention is not limited to them.

Example 1

A cell is produced according to the following procedure.

An SDC (samaria-doped ceria, Sm_0.2Ge_0.8O_1.9) ceramic substrate to be used as a solid electrolyte is prepared. This SDC ceramic substrate which is a circular plate of 180 (μm in thickness and 15 mm in diameter is produced in the following manner. A green sheet is shaped by a doctor blade method. Fibrous cloths are applied to both surfaces of the green sheet and the green sheet is pressed at about 15 MPa (150 kg/cm²) by hydraulic pressing, whereby the surfaces of the green sheet is roughened. The thus-processed green sheet is punched into a circular plate and then fired at 1,300° C.

N_0.9Co_0.1O_x paste added with SDC at 60 wt % is printed on one surface (area: 1.8 cm²) of the ceramic substrate in an area of 1.3 cm² as an inner anode layer, and Ni_0.9Co_0.1O_x paste added with CaCO₃, Rh₂O₃ and SDC at 3 wt %, 5 wt % and 30 wt %, respectively, is printed thereon in an area of 1.3 cm² as an outer anode layer. SSC (samarium strontium cobaltite, Sm_0.5Sr_0.5CoO₃) paste added with SDC at 50 wt % is printed on the other surface in an area of 1.3 cm² as an inner cathode layer, and SSC paste added with SDC and a carbon powder (pore-forming material) at 30 wt % and 55 vol %, respectively, is printed thereon as an outer cathode layer.

Then, an assembly in which platinum meshes formed by welding platinum wires are buried in the printed pastes of the cuter anode layer and the outer cathode layer is fired in the air at 1,200° C. for one hour, whereby a cell of a solid oxide fuel cell (i.e., a cell whose anode and cathode had a two-layer structure as shown in FIG. 1) is produced.

For comparison, a cell of a solid oxide fuel cell is produced according to the same procedure except that a paste that is not added with CaCO₃ is used for forming an outer anode layer.

The generation of soot on the anode surface is evaluated by exposing the cell to the flame of a Bunsen burner to which a fuel-air mixture gas containing n-butane (6.5%) is supplied at a total flow rate of 400 seem. Power is generated for a long time with such a load that a constant current (400 mA/cm²) flows and the generation of soot on the anode surface is checked in a state that the anode of the cell is exposed to the flame. FIGS. 5B and 5C, which are referred to above, are photographs of the anode surfaces of the cells taken after power generation of 15 hours. It is clearly seen that the amount of generated soot is smaller in the anode that is added with CaCO₃ (FIG. 5C) than in the anode that is not added with CaCO₃ (FIG. 5B). The durability of the cell whose anode is added with CaCO₃ is improved accordingly.

Example 2

Experiments are conducted in the same manner as in Example 1 while the amount of CaCO₃ added to the paste for the outer anode layer is varied, and the time taken until the output power of the fuel cell decreased to 50% of an initial value is measured. FIG. 6 shows results. It is seen from the results that the practical amount of CaCO₃ added in the outer anode layer is about 1 to 10 wt %, preferably, 2 to 7 wt %.

As is understood from the above, the practical amount of a calcium compound that is added in the anode can be determined easily on the basis of the kinds of anode material and calcium compound used, flame conditions, etc. by conducting simple experiments. Likewise, the amount of a compound added other than calcium compounds that is effective in suppressing soot generation can be determined easily on the basis of the kinds of anode material and compound used, flame conditions, etc. by conducting simple experiments.

Claims

1. A direct-flame fuel cell comprising: a cell in which a solid electrolyte is sandwiched between an anode and a cathode, wherein:the cell is adapted to generate power when the anode is exposed to a flame,the anode comprises a material selected from the group consisting of:(a) a cermet of nickel, cobalt and (i) yttria-stablized-zirconia-based ceramics,(ii) scandia-stabilized-zirconia-based ceramics, or(iii) ceria-based ceramics; and(b) a cermet of nickel and (i) yttria-stablized-zirconia-based ceramics,(ii) scandia-stabilized-zirconia-based ceramics, or(iii) ceria-based ceramics; andthe anode further comprises calcium carbonate in addition to the material.

2. The direct-flame fuel cell according to claim 1, wherein the content of the calcium carbonate is 1 to 10 wt %.

3. The direct-flame fuel cell according to claim 1, wherein the anode comprises a multilayer structure, and an outermost layer of the anode comprises calcium carbonate.

4. The direct-flame fuel cell according to claim 1, wherein the direct-flame fuel cell is a single-cell fuel cell adapted to generate power in an atmosphere that is a mixture of a fuel component and an oxidizing agent component.

5. The direct-flame fuel cell according to claim 1, wherein the direct-flame fuel cell is an open-to-air fuel cell adapted to generate power when the cell is exposed to a flame in an open-to-air atmosphere.