Disk Drive Suspension Baseplate Having Enhanced Torque Retention And Method Of Manufacture

Information

  • Patent Application
  • 20180068684
  • Publication Number
    20180068684
  • Date Filed
    August 30, 2017
    7 years ago
  • Date Published
    March 08, 2018
    6 years ago
Abstract
A system and methods for manufacturing disk drive suspension baseplates are described. Disk drive suspension baseplates having boss outer surfaces characterized by roughness parameters Ra≧0.15 μm.
Description
FIELD

The invention relates to baseplates of the type incorporated into disk drive suspensions, and methods for manufacturing such baseplates.


BACKGROUND

Disk drive suspension baseplates and methods for manufacturing the baseplates are disclosed in the Yabu U.S. Pat. No. 8,339,745 which is incorporated herein by reference in its entirety and for all purposes. As described in the Yabu patent, baseplates are attached (e.g., by welding) to the proximal end portions of the suspensions and have tubular bosses or boss towers. Baseplates are commonly manufactured by a stamping process from metal such as stainless steel, and can be subjected to various chemical polishing or etching processes in connection with their manufacture. The suspension is attached to an actuator arm of the disk drive by a swaging process. During the swaging process the boss is located in an opening in the actuator arm, and a ball is forced through the boss to deform the boss and engage the outer surface of the boss (sometimes known as the outer diameter or OD) with the inner surface of the actuator arm opening. The strength of the mechanical connection between the boss and actuator arm is characterized by a property and measurement known as torque retention. Torque retention is affected by the normal force between the baseplate and the actuator arm after swage, the amount of area in contact after swage, and the static coefficient of friction between these two surfaces. The static coefficient of friction can be improved by changing the surface roughness of the baseplate. There remains a continuing need for improved baseplates and methods of manufacture.


SUMMARY

A system and methods for manufacturing disk drive suspension baseplates are described. Disk drive suspension baseplates having boss outer surfaces characterized by roughness parameters Ra≧0.15 μm.


Other features and advantages of embodiments of the present invention will be apparent from the accompanying drawings and from the detailed description that follows.





BRIEF DESCRIPTION OF THE DRAWINGS

Embodiments of the present invention are illustrated by way of example and not limitation in the figures of the accompanying drawings, in which like references indicate similar elements and in which:



FIG. 1 illustrates a baseplate including a boss according to an embodiment;



FIG. 2 illustrates a baseplate including a boss according to embodiment as part of a dual-stage actuation suspension assembly;



FIG. 3 illustrates a baseplate including a boss according to an embodiment as part of a suspension assembly;



FIG. 4 illustrates a flow chart of a process for manufacturing baseplates to have a surface characterized by roughness according to an embodiment;



FIG. 5 illustrates a boss outer surface not using the process for manufacturing baseplates as describe herein;



FIG. 6 illustrates a boss outer surface manufactured using a process for manufacturing baseplates to have a surface characterized by roughness according to an embodiment.





DETAILED DESCRIPTION

Embodiments of the invention include lower swage force baseplates having boss surface roughness characteristics that provide enhanced torque retention, and methods for manufacturing the baseplates. Current baseplates have boss outer surfaces characterized, for example, by roughness parameters: Ra, which is typically 0.04 μm to 0.14 μm; Rq, which is typically 0.07 μm to 0.18 μm; and H, which is typically 0.16 μm to 0.50 μm. FIG. 1 illustrates a baseplate 10 including a boss 20 according to an embodiment. As illustrated, the baseplate 10 includes openings 16 for motors, such as piezoelectric motor. FIG. 2 illustrates a baseplate 10 including a boss 20 according to embodiment as part of a dual-stage actuator suspension assembly. The suspension assembly 22 including motors 24, a load beam 30, and a gimbaled flexure 26. FIG. 3 illustrates a baseplate 10 including a boss 20 according to an embodiment as part of a suspension assembly 22 including a load beam 30 and a gimbaled flexure 26. According to embodiments, the gimbaled flexure 26 may include one or two motors mounted on the gimbaled flexure 26.


In embodiments, baseplates 10 have boss outer surfaces 14 characterized by roughness parameters Ra≧0.15 μm. Other embodiments have boss outer surfaces 14 characterized by roughness parameters Ra≧0.20 μm. Yet other embodiments have boss outer surfaces 14 characterized by roughness parameters Ra≧0.25 μm, including 0.40 μm. Boss outer surfaces 14 in accordance with embodiments can be characterized by roughness parameters Ra≧0.70 μm.


In embodiments, baseplates 10 have boss outer surfaces 14 characterized by roughness parameters Rq≧0.2 μm. Other embodiments have boss outer surfaces 14 characterized by roughness parameters Rq≧0.3 μm. Yet other embodiments have boss outer surfaces 14 characterized by roughness parameters Rq≧0.5 μm, including 0.7 μm. Boss outer surfaces 14 in accordance with embodiments can be characterized by roughness parameters Rq≧0.7 μm. Measurements of these surface roughness characteristics, for example, can be performed using instruments such as a white laser interferometer.


In embodiments, baseplates 10 have boss outer surfaces 14 characterized by roughness parameters H≧0.5 μm. Other embodiments have boss outer surfaces 14 characterized by roughness parameters H≧0.6 μm. Yet other embodiments have boss outer surfaces 14 characterized by roughness parameters H≧0.8 μm, including 1.4 μm. Boss outer surfaces 14 in accordance with embodiments can be characterized by roughness parameters H≧2.0 μm. Measurements of these surface roughness characteristics, for example, can be performed using instruments such as a white laser interferometer.


In embodiments, baseplates having surface roughness characteristics providing enhanced torque retention can be manufactured by a multi-step (e.g. two-step) process including passivation of the baseplate (including the boss outer surface)(401), followed by a chemical etch (404) as illustrated in FIG. 4. The passivated baseplates can be rinsed (e.g., using deionized water) and dried before the chemical etch step (402). Following the passivation (401), and any rinse and dry steps (402), and before the chemical etch step (404), the baseplates can be subjected to alkaline clean and rinse steps (403). The baseplates can also be rinsed and dried following the chemical etch step (405).


In embodiments, the passivation is performed by exposing the baseplates to a bath of acid such as citric or nitric acid. Embodiments of citric acid passivation include exposing the baseplates to a bath of citric acid having (1) a concentration of 3%-15% (w/w), (2) at a temperature of 70°−200° F., and (3) for an immersion time of 10-120 minutes. Other embodiments of a citric acid passivation include exposing the baseplates to a bath of citric acid having (1) a concentration of 8%-12% (w/w), (2) at a temperature of 160°−180° F., and (3) for an immersion time of 20-75 minutes. Embodiments of nitric acid passivation include exposing the baseplates to a bath of nitric acid having (1) a concentration of 15%-70% (v/v), (2) at a temperature of 100°−200° F., and (3) for an immersion time of 10-60 minutes. Other embodiments of a nitric acid passivation include exposing the baseplates to a bath of nitric acid having (1) a concentration of 40%-60% (v/v), (2) at a temperature of 160°−180° F., and (3) for an immersion time of 20-75 minutes. The acid used in these embodiments can include other additives such as accelerants, inhibitors, and/or solutions capable of producing parts that pass specified test requirements for passivation (e.g., per 7.1.1.5 of ASTM standard A967) to enhance passivation and cleaning.


In embodiments, the chemical etch following the passivation is performed by methods described in the above-identified and incorporated Yabu patent. For example, embodiments of the chemical etch include exposing the baseplates to a bath component including (1) 0%-50% (w/w) hydrochloric acid, (2) 0%-50% (w/w) nitric acid, (3) 0%-50% (w/w) phosphoric acid, (4) 0-20 g/l iron (Fe+3 and Fe+2), and (5) 0%-10% surfactant, inhibitor, leveler and stabilizer. Other embodiments of the chemical etch include exposing the baseplates to a bath component including (1) 1%-10% (w/w) hydrochloric acid, (2) 1%-10% (w/w) nitric acid, (3) 10%-30% (w/w) phosphoric acid, (4) 6-15 g/l iron (Fe+3 and Fe+2), and (5) 0.1%-5% surfactant, inhibitor, leveler and stabilizer.


In other embodiments, baseplates having surface roughness characteristics providing enhanced torque retention can be manufactured by performing chemical etch steps of the type described above two or more times. In embodiments, the baseplates can be subjected to rinse and dry steps, and/or to alkaline clean and rinse steps, before one or more of the chemical etch steps. FIG. 5 illustrates a boss outer surface not using the process for manufacturing baseplates as describe herein, such as the passivation and chemical etch methods described herein. FIG. 6 illustrates a boss outer surface manufactured using a process for manufacturing baseplates to have a surface characterized by roughness according to an embodiment described herein, such as subjected to the passivation and chemical etch methods described herein. As illustrated, the boss outer surface illustrated in FIG. 6 has a rougher surface than the boss outer surface illustrated in FIG. 5.


Baseplates having surface roughness characteristics in accordance with embodiments of the invention offer significant advantages. For example, they provide improved torque retention when swaged to a drive actuator arm. Tests of baseplates manufactured in accordance with embodiments of the invention have demonstrated significant torque retention increases (e.g., from about 10 oz.-in. using prior art processes to about 15 oz.-in.). Additional torque retention in the same design allows the swaging process to be modified to their advantage. For example, a smaller swage ball can be used to swage the baseplate manufactured with the above-described manufacturing methods. Thus, a lower swage force baseplate results using the manufacturing methods described herein. While still achieving satisfactory torque, the smaller ball will lead to fewer detrimental effects such as warping of the flange portion of the baseplate during the swaging process. This in turn results in less change to the gram load, or vertical placement of the read-write head relative to the disk. Alternatively, a baseplate manufactured with the above-described methods can be designed with a smaller boss height, allowing thinner actuator arms, which allows closer spacing of the disks, leading to a smaller overall drive height. The above-described baseplate manufacturing methods are efficient, repeatable and effective.


Although the invention has been described with reference to preferred embodiments, those of skill in the art will recognize that changes can be made in form and detail without departing from the spirit and scope of the invention. For example, other chemical methods involving other chemical etchants, polishes, pickling solutions in single process can be employed to create the surface roughness. In addition, other methods such as those involving thermal (e.g., heat treating), electrochemical (e.g., anodic current flow in combination with a chemical solution) and mechanical (e.g., shot peen or tumbling with media) can also be used to manufacture baseplates in accordance with embodiments of the invention.

Claims
  • 1. Disk drive suspension baseplate having boss outer surfaces characterized by roughness parameters Ra≧0.15 μm.
  • 2. The disk drive suspension baseplate of claim 1 having boss outer surfaces characterized by roughness parameters Ra≧0.20 μm.
  • 3. The disk drive suspension baseplate of claim 1 having boss outer surfaces characterized by roughness parameters Ra≧0.25 μm
  • 4. The disk drive suspension baseplate of claim 3 having boss outer surfaces characterized by roughness parameters including 0.40 μm.
  • 5. The disk drive suspension baseplate of claim 1 having boss outer surfaces characterized by roughness parameters Ra≧0.70 μm.
  • 6. Disk drive suspension baseplate having boss outer surfaces characterized by roughness parameters Rq≧0.2 μm.
  • 7. Disk drive suspension baseplate of claim 6 having boss outer surfaces characterized by roughness parameters Rq≧0.3 μm.
  • 8. Disk drive suspension baseplate of claim 6 having boss outer surfaces characterized by roughness parameters Rq≧0.5 μm
  • 9. Disk drive suspension baseplate of claim 8 having boss outer surfaces characterized by roughness parameters including 0.7 μm.
  • 10. Disk drive suspension baseplate of claim 6 having boss outer surfaces characterized by roughness parameters Rq≧0.7 μm.
  • 11. Disk drive suspension baseplate having boss outer surfaces characterized by roughness parameters H≧0.5 μm.
  • 12. Disk drive suspension baseplate of claim 11 having boss outer surfaces characterized by roughness parameters H≧0.6 μm.
  • 13. Disk drive suspension baseplate of claim 11 having boss outer surfaces characterized by roughness parameters H≧0.8 μm
  • 14. Disk drive suspension baseplate of claim 13 having boss outer surfaces characterized by roughness parameters including 1.4 μm.
  • 15. Disk drive suspension baseplate of claim 11 having boss outer surfaces characterized by roughness parameters H≧2.0 μm.
  • 16. A method for manufacturing a lower swage force baseplate comprising passivation of the baseplate followed by a chemical etch.
  • 17. The method of claim 16, wherein the passivation includes a citric acid passivation.
  • 18. The method of claim 16, wherein the passivation includes a nitric acid passivation.
  • 19. The method of claim 16, wherein the chemical etch includes using hydrochloric acid.
  • 20. The method of claim 16 further comprises subjecting the baseplate to a chemical etch two or more times.
  • 21. The method of claim 20 wherein the chemical etch includes nitric acid.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority from U.S. Provisional Patent Application No. 62/383,053, filed on Sep. 2, 2016, which is hereby incorporated by reference in its entirety.

Provisional Applications (1)
Number Date Country
62383053 Sep 2016 US