Patent Application
20140034257
The present invention relates to a disk roll which comprises a rotating shaft and ring-shaped disks fitted thereon by insertion, whereby the peripheral surface of the disks serves as a conveying surface. More particularly, the invention relates to a disk roll suitable for use in producing a high-quality glass plate. The invention further relates to a base material for disk rolls which is for use in producing therefrom disks for the disk roll.
In the production of a glass plate, a conveying mechanism is necessary for glass plate formation from a molten-state glass or for annealing the glass plate formed. This conveying mechanism generally comprises conveying rolls, and disk rolls are being used as one species of such conveying rolls.
Such disk rolls 10 are mounted in a glass plate production apparatus 100 as shown in
Alumina fibers and aluminosilicate fibers are extensively used as the inorganic fibers from the standpoint of heat resistance. Alumina fibers and aluminosilicate fibers crystallize upon heating or the crystallization thereof proceeds with heating, whereby these fibrous materials increase in hardness. Although alumina fibers and aluminosilicate fibers can contribute to an improvement in wearing resistance through the hardening thereof, neither the alumina fibers nor the aluminosilicate fibers crystallize at the surface temperature of the molten glass 110 (about 800° C.).
A disk roll containing mica particles which are incorporated in order to impart heat resistance and wearing resistance has been proposed (see, for example, patent document 1). However, with the formulations using alumina fibers or aluminosilicate fibers, the contribution of these fibers to wearing resistance is not great as stated above.
An object of the invention, which has been achieved under those circumstances, is to provide a disk roll which has a well balanced combination of heat resistance, wearing resistance and flexibility, and which is satisfactory in these properties.
Other objects and effects of the invention will become apparent from the following description.
In order to accomplish the object, the invention provides the base material for disk rolls and the disk roll shown below.
(1) A base material for disk rolls which is a platy molded article for obtaining ring-shaped disks for use in a disk roll comprising a rotating shaft and ring-shaped disks fitted thereon by insertion, whereby the peripheral surface of the disks serves as a conveying surface,
the base material comprising inorganic fibers having a crystallization temperature of 800-900° C., a filler, and a clay.
(2) The base material for disk rolls according to (1) above, wherein the inorganic fibers are biosoluble fibers.
(3) The base material for disk rolls according to (2) above, wherein the biosoluble fibers are coated with a phosphoric acid salt, a molybdenum compound, a zinc compound, a polyamidine compound, or an ethyleneimine compound.
(4) The base material for disk rolls according to any one of (1) to (3) above wherein the content of the inorganic fibers is 5-40% by mass based on the whole amount of the base material.
(5) A disk roll which comprises a rotating shaft and, fitted thereon by insertion, ring-shaped disks cut out of the base material for disk rolls according to any one of (1) to (4) above, whereby the peripheral surface of the disks serves as a conveying surface.
(6) The disk roll according to (5) above which has a compression deformation of 0.05-0.3 mm when a load of 10 kgf/cm is imposed on the roll surface at 800° C.
In the disk roll of the invention, the inorganic fibers contained in the disks crystallize at the surface temperature of a molten glass. Consequently, upon contact with a molten glass, the inorganic fibers crystallize simultaneously with sintering of the clay to form a surface layer having higher hardness and thereby impart excellent heat resistance and wearing resistance. In addition, due to the heat-insulating properties inherently possessed by the disks, heat transfer to inner parts of the disks during repetitions of contact with a molten glass is inhibited and, hence, the inner parts do not harden excessively and can retain moderate flexibility. Because of this, the disk roll of the invention has a well balanced combination of heat resistance, wearing resistance and flexibility, and has a long life and high performance.
The reference numerals used in the drawings denote the followings, respectively.
The invention will be explained below in detail.
The base material for disk rolls of the invention is a platy molded article of a mixture of a clay, a filler, and inorganic fibers having a crystallization temperature of 800-900° C. (hereinafter also referred to simply as “inorganic fibers”).
As the clay, use can be made of one which, when mixed with water, shows viscosity and plasticity and which has the property of sintering upon heating. With respect to the kind thereof, examples include Kibushi clay, Gairome clay, and fire clay. Of these, Kibushi clay is preferred because it has a high binding effect in sintering and has a low impurity content. Two or more clays can be used in combination according to need.
The clay may be one which has been regulated, through separation/purification, so that the content of components having a particle diameter of 5 μm or larger therein is 30% by mass or lower, preferably 15% by mass or lower, more preferably 10% by mass or lower. With respect to the lower limit thereof, a clay containing entirely no component having a particle diameter of 5 μm or larger is optimal. Such clay particles which are fine and uniform in particle diameter exhibit higher binding ability and tenaciously bind other disk-constituting materials.
Through the separation/purification, impurities also are simultaneously removed. In general, the particle diameters of a clay, which is a natural mineral, can be regulated in some degree by pulverization/classification. However, clay products contain a large amount of impurities and the impurities, in many cases, include ones which do not have susceptibility to sintering, such as, e.g., silica. In disk rolls, sintering and resultant hardening proceed during use as a result of contact with the material being conveyed, such as a molten glass. However, the impurities not having susceptibility to sintering can be a factor which inhibits the hardening function. In addition, the impurities include many hard substances and there is a possibility that the hard substances might mar the material being transferred, in particular, a glass plate. The content of impurities is preferably as close to zero as possible. However, in view of the actual circumstances including labor and cost, the content of impurities is preferably 10% by mass or lower, especially 5% by mass or lower, more preferably 1% by mass or lower, based on the whole clay.
In regulating the particle diameters so as to be small and within the given range as described above and in removing impurities, it is effective to employ wet-process classification as a method of separation/purification. By conducting wet-process classification, not only impurities differing in specific gravity or size can be removed, but also a raw-material clay having smaller particle diameters and a narrower particle size distribution than in dry classification can generally be obtained while utilizing the phenomenon in which sedimentation velocities vary with the particle diameter.
As the filler, use can be made of one which has heat resistance, does not show unnecessary reactivity with other compounding materials, and does not contain hard large particles. Examples thereof include talc, alumina powder, silica powder, highly purified wollastonite, and non-plastic kaolinite. However, particles of a mica or vermiculite are suitable. Micas are known to have high elasticity and be excellent in slip properties, wearing resistance, heat resistance, etc., and are materials which have been industrially utilized from long ago in various fields. In the invention, a mica may be added for the purpose of enabling the disks to conform to the thermal expansion of the shaft. In a disk roll, since the shaft 11 onto which the disks 12 are fitted as shown in
As the mica, use can be made of muscovite (K2Al4(Si3Al)2O20(OH)4), biotite, phlogopite (K2Mg6(SiAl)2O20(OH)4) paragonite, lepidolite, or a synthetic fluoromica. However, muscovite, which releases crystal water at about 600° C., i.e., a temperature lower than the surface temperature of a molten glass, is preferred from the standpoint of the function of enhancing conformability.
The average particle diameter of the mica may be 5-500 μm, and is preferably 100-300 μm, more preferably 200-300 μm. When the mica has an average particle diameter within that range, it is highly elastic and hence effectively functions as plate springs to store the stress generated by compression with other compounding materials, in particular, the inorganic fibers. Thus, conformability to the thermal expansion of the shaft can be further enhanced.
Vermiculite generally contains crystal water and dehydrates upon exposure to high temperatures. Namely, it functions like a blowing agent. It is therefore preferred to use vermiculite which has been burned beforehand at, e.g., 600-900° C. The average particle diameter of the vermiculite is preferably 5-500 μm as in the mica.
The mica and vermiculite may be used alone or in combination.
The inorganic fibers are not limited as long as they have a crystallization temperature of 800-900° C. Examples thereof include the inorganic fibers described in JP-A-2000-220037, JP-A-2002-68777, JP-A-2003-73926, and JP-A-2003-212596. Specific examples thereof include: inorganic fibers in which the total content of SiO2 and CaO is 85% by mass or higher and which contain 0.5-3.0% by mass MgO and 2.0-8.0% by mass P2O5 and have a carcinogenicity index (KI value) as determined in accordance with German Hazardous Substances Regulations of 40 or higher; inorganic fibers comprising SiO2, MgO, and TiO2 as essential components; inorganic fibers comprising SiO2, MgO, and manganese oxide as essential components; inorganic fibers comprising 52-72% by mass SiO2, less than 3% by mass Al2O3, 0-7% by mass MgO, 7.5-9.5% by mass CaO, 0-12% by mass B2O3, 0-4% by mass BaO, 0-3.5% by mass SrO, 10-20.5% by mass Na2O, 0.5-4.0% by mass K2O, and 0-5% by mass P2O5; and inorganic fibers comprising 75-80% by mass SiO2, 19-25% by mass CaO+MgO, and 1-3% by mass Al2O3. Such inorganic fibrous materials may be used alone or as a mixture of two or more thereof. The crystallization temperature of inorganic fibers can be ascertained by examining the fibers with a differential thermal analyzer (DTG-50, manufactured by Shimadzu Corp.) for exothermic peak attributable to crystallization.
Of those inorganic fibrous materials, ones which have a solubility in physiological saline, as determined by the method shown below, of 1% or higher are called “biosoluble fibers” and are especially preferred in the invention.
A method of determining the solubility of inorganic fibers in physiological saline is explained. First, 1 g of a sample prepared by pulverizing the inorganic fibers to a 200-mesh powder and 150 mL of physiological saline are introduced into an Erlenmeyer flask (300 mL). This flask is placed in a 40° C. incubator. Subsequently, the Erlenmeyer flask is continuously shaken horizontally at a rotation speed of 120 rpm for 50 hours. After the shaking, the mixture is filtered, and the resultant filtrate is analyzed by ICP emission spectroscopy to determine the concentrations of silicon, magnesium, calcium, and aluminum elements (mg/L) contained therein. The solubility in physiological saline C (%) is calculated from the concentrations of the elements and from the contents of the elements in the inorganic fibers before the dissolution (% by mass), using the following equation (1). With respect to the element concentrations obtained by the ICP emission spectroscopy, the concentration of silicon element is expressed as a1 (mg/L), concentration of magnesium element as a2 (mg/L), concentration of calcium element as a3 (mg/L), and concentration of aluminum element as a4 (mg/L). With respect to the element contents in the inorganic fibers before dissolution, the content of silicon element is expressed as b1 (% by mass), content of magnesium element as b2 (% by mass), content of calcium element as b3 (% by mass), and content of aluminum element as b4 (% by mass).
C(%)={(filtrate amount (L))×(a1+a2+a3+a4)×100}/{(amount of inorganic fibers before dissolution (mg))×(b1+b2+b3+b4)/100} (1)
The size of the inorganic fibers is not particularly limited. However, from the standpoint of the strength of the disk roll to be produced, the inorganic fibers preferably are ones having an average fiber diameter of 1-5 μm, preferably 3-5 μm, and a fiber length of 0.5-200 mm, preferably 1-20 mm.
The clay, filler, and inorganic fibers may be mixed in the following proportions. The proportion of the clay is 5-55% by mass, preferably 20-40% by mass, based on the total amount of the base material. The proportion of the filler is 5-60% by mass, preferably 20-55% by mass, based on the total amount of the base material. The proportion of the inorganic fibers is 5-40% by mass, preferably 20-30% by mass, based on the total amount of the base material. When the ingredients are mixed in such proportions, a disk roll retaining a well balanced combination of heat resistance, wearing resistance, and flexibility is obtained.
For producing the base material for disk rolls, use can be made of a method in which an aqueous slurry containing the clay, filler, and inorganic fibers is formed into a plate shape by a papermaking method and this plate is dried. This method is preferred because it is efficient. In this operation, ingredients such as a coagulant aid, organic fibers, and organic binder may be incorporated into the aqueous slurry in a given amount. The coagulant aid, organic fibers, and organic binder each may be known one.
In the case where biosoluble fibers are used as the inorganic fibers, it is preferred that a substance which forms a coating layer, such as, e.g., a phosphoric acid salt, a molybdenum compound, a zinc compound, a polyamidine compound, or an ethyleneimine compound, be incorporated into the aqueous slurry in order to inhibit the fibers from dissolving in the water. The amount of the coating-forming substance to be incorporated is preferably 0.1-10% by mass, more preferably 0.3-6% by mass, based on the sum of the clay, filler, and biosoluble fibers from the standpoint of satisfactorily coating the whole biosoluble fibers.
Examples of the substance for forming a coating layer include inorganic compounds such as phosphoric acid salts, molybdenum compounds, and zinc compounds and organic compounds such as polyamidine compounds and ethyleneimine compounds. Examples of the phosphoric acid salts include aluminum tripolyphosphate, aluminum dihydrogen tripolyphosphate, aluminum metaphosphate, zinc phosphate, and calcium phosphate. Examples of the molybdenum compounds include zinc molybdate, aluminum molybdate, calcium molybdate, calcium phosphomolybdate, and aluminum phosphomolybdate. Examples of the zinc compounds include zinc oxide. Examples of the polyamidine compounds include acrylamide, acrylonitrile, N-vinylacrylamidine hydrochloride, N-vinylacrylamide, vinylamine hydrochloride, and N-vinylformamide copolymers. Examples of the ethyleneimine compounds include aminoethylene and dimethyleneimine.
The thickness of the base material for disk rolls can be suitably regulated, and may be the same as those heretofore in use. In general, the thickness thereof is 2-10 mm.
The invention further provides a disk roll employing disks cut out of the base material for disk rolls described above. The disk roll may have the constitution shown in
In the disk roll 10 of the invention, the inorganic fibers in a surface layer part crystallize simultaneously with the sintering of the clay upon contact with a molten glass. As a result, the surface layer part comes to have a higher hardness and better wearing resistance than those in which clay sintering only has occurred. In addition, the surface layer comes to have enhanced heat-insulating properties and, hence, the heat of the molten glass is less apt to be transferred to inner parts, whereby moderate flexibility is retained. Specifically, the disk roll has a compression deformation of 0.05-0.3 mm when a load of 10 kgf/cm is imposed on the roll surface at 800° C.
The invention will be explained below in greater detail with reference to Examples and Comparative Examples, but the invention should not be construed as being limited to the Examples.
Aqueous slurries containing the raw materials shown in Table 1 were prepared. Each slurry was formed into sheets by an ordinary papermaking method to produce a disk-roll base material in sheets which had dimensions of 100 mm×100 mm×6 mm on a dry basis. The inorganic fibers A are aluminosilicate fibers (SiO2:Al2O3=(54-55% by weight):(45-55% by weight)), while the inorganic fibers B are biosoluble fibers comprising 75-80% by mass SiO2, 19-25% by mass CaO+MgO, and 1-3% by mass Al2O3 and having a crystallization temperature of 860° C. and a solubility in physiological saline at 40° C. of 5.9%.
Disks having an outer diameter of 80 mm and an inner diameter of 30 mm were punched out of each of the base materials for disk rolls, and fitted onto an iron shaft having a diameter of 30 mm and a length of 100 mm by insertion. Both ends of each disk stack were fixed with nuts to produce a cylindrical disk roll which had the constitution shown in
Disk rolls produced in the same manner were evaluated for wearing resistance in the following manner. Each disk roll was held in an 800° C. heating furnace for 180 minutes. Thereafter, the roll was rotated at 10 rpm and rubbed against a friction material made of SUS. The amount by which the radius of the roll had decreased due to the rubbing was measured as an index to wearing resistance.
Furthermore, disk rolls produced in the same manner were mounted in a glass plate production apparatus having the constitution shown in
The results of those examinations are also shown in Table 1.
Table 1 shows the following. By incorporating the inorganic fibers having a crystallization temperature of 800-900° C., disk rolls can be obtained which have practically satisfactory heat resistance and wearing resistance and have moderate flexibility which prevents the disk rolls from marring the glass surfaces.
While the present invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.
This application is based on Japanese Patent Application No. 2006-100490 filed Mar. 31, 2006, and the contents thereof are herein incorporated by reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| P. 2006-100490 | Mar 2006 | JP | national |
This application is a divisional of application Ser. No. 12/801,166 filed May 26, 2010, now allowed, which in turn is a continuation application based on application Ser. No. 11/727,447 filed Mar. 27, 2007, now U.S. Pat. No. 7,781,043, which in turn is based on and claims priority to JP 2006-100490 filed 31 Mar. 2006, the entire contents of which is hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12801166 | May 2010 | US |
| Child | 14060685 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11727447 | Mar 2007 | US |
| Child | 12801166 | US |