The present disclosure is directed to the area of dispensing alkali metals. The present disclosure is also directed to the generation of alkali metals in the zero oxidation state, as well as applications that include the dispensed alkali metal.
The manufacture of vapor cells, used in optical magnetometry and atomic clocks, and alkali metal batteries typically includes the dispensing of alkali metals. In at least some of these products, the alkali metal is present in the zero oxidation state. For example, an alkali metal vapor cell can have a vapor of alkali metal atoms in the zero oxidation state. The reactivity of alkali metals to water, oxygen, and other reactants hinders the dispensing of the alkali metals in the zero oxidation state.
A variety of conventional arrangements are used for the dispensing of alkali metals. The following are a few examples. In one conventional method, an alkali dispenser (such as the arrangement commercialized by SAES Getters) is placed inside a double cavity cell. The dispenser is activated after sealing by local laser heating. This reaction creates cesium and non-reactive side reacting products: 2Cs2CrO4+ZrAl2→2Cs+Cr2O3+Al2O3+3ZrO2. A similar reaction can be used for rubidium. Drawbacks for this arrangement include the SAES pill being relatively large compared to the size of the cell and the zirconium getter nitrogen complicating cell filing. In a paste version, Cs2CrO4 is replaced by Cs2MoO4. The paste contains a stabilizer and a binder.
Another conventional arrangement uses wax packets. In this method, rubidium is enclosed into wax micropacket produced at wafer scale in a glove box. Vapor cells are then produced with only the desired buffer gas pressure. The cells are sealed at the bottom by only a small SiN layer. The micropacket is then attached to the cells by heating. Finally, a laser removes the SiN layer from the inside of the cell releasing the rubidium inside the cell.
Another conventional arrangement utilizes enriched glass electrolysis. A cesium enriched glass is placed in an electric field inside the cell. This results in the cesium diffusing out of the glass.
One embodiment is a method for generating alkali metal in a zero oxidation state that includes reacting an alkali metal compound having a —S-M substituent, where M is an alkali metal and S is sulfur, with gold in a zero oxidation state to release the alkali metal in the zero oxidation state.
In at least some embodiments, the alkali metal compound is an alkali metal alkylthiolate. In at least some embodiments, the method further includes reacting an alkyl thiol with an alkali metal hydroxide or alkali metal amide to form the alkali metal alkylthiolate. In at least some embodiments, the alkali metal compound is an alkali metal sulfide, M2S.
In at least some embodiments, the alkali metal is selected from lithium, sodium, potassium, rubidium, or cesium. In at least some embodiments, the gold is part of a gold surface. In at least some embodiments, the gold surface is a gold(111) surface. In at least some embodiments, the gold surface comprises a gold layer disposed on a substrate.
In at least some embodiments, the alkali metal compound with the gold comprises reacting the alkali metal compound with the gold in an aprotic solvent. In at least some embodiments, the method further includes removing the solvent leaving the zero oxidation state alkali metal.
In at least some embodiments, reacting the alkali metal compound with the gold comprises herein reacting the alkali metal compound with the gold in a vapor cell. In at least some embodiments, the method further includes removing the gold from the vapor cell.
Another embodiments is a method of making an alkali metal vapor cell that includes reacting an alkali metal compound having a —S-M substituent, where M is an alkali metal and S is sulfur, with gold in a zero oxidation state to release the alkali metal in the zero oxidation state; and disposing the alkali metal in the zero oxidation state into a vessel of an alkali metal vapor cell.
In at least some embodiments, the disposing step comprises performing the reacting step in the vessel of the alkali metal vapor cell. In at least some embodiments, the method further includes removing the gold from the vessel of the alkali metal vapor cell.
In at least some embodiments, the reacting step is performed in a solvent in a reaction vessel, wherein disposing the alkali metal comprises transferring the solvent and the alkali metal in the zero oxidation state from the reaction vessel to the vessel of the alkali metal vapor cell and the method further comprises removing the solvent.
In at least some embodiments, the alkali metal compound is an alkali metal alkylthiolate and the method further includes reacting an alkyl thiol with an alkali metal hydroxide or alkali metal amide to form the alkali metal alkylthiolate.
Another embodiment is a vapor cell that includes a vessel; and alkali metal disposed in the vessel, wherein the alkali metal is disposed in the vessel by reacting an alkali metal compound having a —S-M substituent, wherein M is an alkali metal and S is sulfur, with gold in a zero oxidation state to release the alkali metal in the zero oxidation state.
In at least some embodiments, the alkali metal compound is an alkali metal alkylthiolate. In at least some embodiments, the alkali metal compound is an alkali metal sulfide.
Non-limiting and non-exhaustive embodiments of the present invention are described with reference to the following drawings. In the drawings, like reference numerals refer to like parts throughout the various figures unless otherwise specified.
For a better understanding of the present invention, reference will be made to the following Detailed Description, which is to be read in association with the accompanying drawings, wherein:
The present disclosure is directed to the area of dispensing alkali metals. The present disclosure is also directed to the generation of alkali metals in the zero oxidation state, as well as applications that include the dispensed alkali metal.
Conventional methods for generating and dispensing alkali metals in the zero oxidation state may not be suitable or amenable to particular applications. For example, the reaction arrangement may not be suitable for a relatively small vapor cell, the kinetics and equilibrium may not be known, and some of the compounds (e.g., reactants) may be highly toxic.
As described herein, alkali metals in the zero oxidation state can be generated and dispensed through the mediation of a gold surface with zero oxidation state gold atoms. The methods described herein present new chemistry for generating or dispensing alkali metals and can have a number of different features or advantages as described herein. An alkali metal compound having a —S-M substituent (wherein M is an alkali metal and S is sulfur) can react with gold in the zero oxidation state to substitute the gold for the alkali metal (forming a —S—Au linkage) and free the alkali metal in the zero oxidation state. The alkali metal compound can be an organometallic or inorganic compound including, but not limited to, an alkali metal alkylthiolate or an alkali metal sulfide.
At least some embodiments include providing a gold surface presenting zero oxidation state gold (e.g., a gold(111) surface or monolayer). At least some embodiments include providing an organic solvent, with little or no water or water vapor content, for performing a reaction. At least some embodiments include providing an inert gas environment (for example, argon, nitrogen, or any combination thereof) for performing the reaction in a dry environment (for example, a water or water vapor free environment). At least some embodiments include submersing the gold surface and reagents in the solvent so that a reaction releases zero oxidation state alkali metal in the solvent solution.
In at least some embodiments, the methods and schemes described herein can include a reaction arrangement that is compatible with a vapor cell having a small form factor. In at least some embodiments, the methods and schemes can be compatible with fabrication (for example, micro-electro-mechanical systems (MEMS) fabrication) of a vapor cell. In at least some embodiments, the methods and schemes (or at least a portion of the methods and schemes) can be performed in a target vessel, such as a vapor cell, prior to final assembly of the vapor cell (for example, prior to closure of the vapor cell.)
In at least some embodiments, the methods and schemes can include a dispensed amount of alkali metal that is directly proportional to the surface area of the gold surface. In at least some embodiments, these schemes and methods can provide for accurate and repeatable dispensing of alkali metal.
In at least some embodiments, the schemes and methods can include precursors that are inexpensive and safe (for example, the precursors do not react violently with water or oxygen). In at least some embodiments, the methods and schemes do not require getter gases. In at least some embodiments, the methods and schemes do not require heat or UV light for activation. In at least some embodiments, the reactions can be performed at room temperature. In at least some embodiments, undesired reaction products can be eliminated, reduced, or minimized through the stoichiometry of the reaction.
As indicated above, the methods and schemes described herein include the reaction of an alkali metal compound with a —S-M substitute (where M is an alkali metal and S is sulfur) with gold in the zero oxidation state (such as a gold surface) to substitute the gold for the alkali metal and release the alkali metal in a zero oxidation state. The following Scheme 1 (using an alkali metal alkylthiolate) and Scheme 2 (using an alkali metal sulfide) illustrate example embodiments for the generating or dispensing of alkali metals in the zero oxidation state using a reaction of the indicated alkali metal compounds with gold in the zero oxidation state.
Scheme 1:
In this scheme, an alkali metal alkylthiolate reacts with a gold surface to release the alkali metal in the zero oxidation state. The thioalkyl may be bound to the gold surface as a result of the reaction. In at least some embodiments, the alkali metal alkylthiolate is generated by reaction of an alkyl thiol with an alkali metal hydroxide. Other methods for generating the alkali metal alkylthiolate may also be used.
One embodiment of this set of reactions can be represented by the following reaction equations:
R-SH+MOH→R—S-M
RSM+Auo (surface)→Au—S-R+Mo
R is an alkyl group (for example, a C4 to C30 branched or unbranched alkyl chain, such as C18H37) which may be substituted with one or more substituents that do not interfere with the reaction steps including, for example, ethers, polyethylene glycol (—CH2CH2O—)n, carboxylic esters, tertiary amines, and amides;
SH is a thiol group;
R—SH is an alkyl thiol, for example C18H37SH;
MOH is an alkali metal hydroxide;
M is an alkali metal (for example, lithium, sodium, potassium, rubidium, cesium, or francium);
Auo is zero oxidation state gold (e.g., an atom on a Au(111) surface); and
Mo is a zero oxidation state alkali metal.
One embodiment of the set of reactions is provided as follows:
As an embodiment of the set of reactions, in a first step, an alkyl thiol is reacted with an alkali metal hydroxide in an organic solvent such as, for example, acetonitrile, tetrahydrofuran, acetone, N,N-dimethlyformamide (DMF), N,N-dimethylacetamide (DMA), or the like. The product of this reaction is an alkali metal alkylthiolate. Preferably, the solvent contains little (for example, no more than 0.1%) or no water. In at least some embodiments, the solvent is an aprotic solvent. In at least some embodiments, the solvent is a polar aprotic solvent. As an alternative to alkali metal hydroxide, an alkali metal amide can react with the alkyl thiol.
In at least some embodiments, this first reaction is performed in a vessel, such as a gas or vapor cell, into which the zero oxidation state alkali metal, Mo, is to be dispensed. In at least some embodiments, this first reaction is performed in an open gas or vapor cell which can be sealed after dispensing the alkali metal (and adding any other suitable components, such as a buffer gas or the like). In other embodiments, the first reaction may be performed in vessel other than the final vessel in which the alkali metal is to be dispensed.
In at least some embodiments, the alkali metal alkylthiolate produced in the first step is isolated or otherwise separated from at least a portion of the reactants prior to proceeding to the next step.
Next, in a second step, a gold surface, presenting zero oxidation state gold, Auo, (such as a Au(111) surface), is brought into contact with the alkali metal alkylthiolate of the first step. In at least some embodiments, this occurs in the original solvent. In other embodiments, the second reaction may be performed using a new or different solvent, such as, for example, acetonitrile, tetrahydrofuran, acetone, N,N-dimethlyformamide (DMF), N,N-dimethylacetamide (DMA), or the like. Preferably, the solvent contains little (for example, no more than 0.01% or 100 ppm) or no water. In at least some embodiments, the solvent is an aprotic solvent.
The gold surface (for example, a Au(111) surface) can be, for example, a thin gold layer formed on a substrate, such as glass, silicon, a ceramic material, plastic, other metal, or the like, including micropipette tips with an inner coating of gold. For example, gold can be deposited (using any suitable deposition technique, such as e-beam evaporation, thermal evaporation, or the like) on the substrate. In at least some embodiments, the substrate may be structured (for example, with peaks and valleys, holes, dimples, pyramidal structures, or any regular or irregular structure, or the like) to increase the surface area of the gold surface. The gold surface can also be gold microsphere beads of various sizes.
In the presence of the zero oxidation state gold, Auo, the alkali metal alkylthiolate decomposes linking the alkyl group to the gold via a thio (sulfur) linkage and releasing the zero oxidation state alkali metal Mo in solution.
In at least some embodiments, subsequent to the second reaction, the gold surface, and accompanying substrate, is removed from the solution. The solvent containing the zero oxidation state alkali metal Mo is evaporated, leaving the zero oxidation state alkali metal Mo in the vessel. In at least some embodiments, this second reaction is performed in a vessel, such as a gas or vapor cell, into which the zero oxidation state alkali metal, Mo, is to be dispensed. In at least some embodiments, this second reaction is performed in an open vapor cell vessel. In other embodiments, the second reaction may be performed in a vessel other than the final vessel in which the alkali metal is to be dispensed with the alkali metal (optionally, in solvent) being disposed to the final vessel after the reaction is complete. For example, the solvent with the zero state alkali metal can be aliquoted and transferred to the target vessel, such as a vapor cell, and then evaporated in the target vessel.
In at least some embodiments, the number of alkali metal alkylthiolate molecules is smaller than the capacity of the gold surface. This arrangement may eliminate or reduce the possibility of unreacted contaminants (e.g., alkali metal alkylthiolate) left in the solvent. In at least some embodiments, the gold surface area can be controlled to dispense a relatively precise amount of zero oxidation state alkali metal Mo. For example, a 1 cm2 of gold surface may release up to 2.7×1014 zero oxidation state alkali metal, Mo, atoms.
In at least some embodiments, this scheme may be advantageous over conventional alkali metal dispensing methods as many alkane thiols have good solubility in organic solvents because they are surfactants. Selection of a suitable solvent may also enable good solubility for the alkali metal hydroxide.
The gold surface is oxidized during the reaction. In at least some embodiments, the gold surface may be regenerated into a zero oxidation state gold, Auo, surface by exposing the surface to a suitable reducing agent. In at least some embodiments, once regenerated, the gold surface may be reused.
In step 1, dodecanethiol was reacted with CsOH (50% aqueous solution) in acetonitrile to produce cesium dodecylthiolate. This reaction product was lyophilized (freeze dried) to remove all water content. The structure of the product was verified using proton NMR.
In step 2, the cesium dodecylthiolate was then exposed to a gold 111 surface. In particular, gold coated glass slides (25 mm×76 mm with 200 nm thickness of gold) were used for the gold 111 surface. The gold coated glass slides were dipped into a solution (1 mM) of the cesium dodecylthiolate in dry acetonitrile for approximately 24 hours at room temperature under an argon atmosphere. The gold 111 surface reacted with the cesium dodecylthiolate to bind the sulfur atom to the gold surface releasing zero oxidation state cesium into the acetonitrile solution.
The gold surface was then removed from the reaction vessel leaving the zero oxidation state cesium in acetonitrile. The solution was centrifuged and the residue was transferred into a container (15 mm×5 mm), dried, and sealed. In at least some embodiments, no unreacted cesium dodecylthiolate should remain in the solution as long as the gold surface capacity exceeds the amount of cesium dodecylthiolate.
The solution with the zero-oxidation state cesium was transferred to a target vessel (a glass ampule). The target vessel was in an inert gas environment. The acetonitrile was evaporated, leaving the zero oxidation state Cs in the target vessel.
Scheme 2:
In this scheme, an alkali metal sulfide (M2S) reacts with a gold surface to release one of the alkali metal atoms in the zero oxidation and form a gold-sulfur-alkali metal sulfide attached to the gold surface.
One embodiment of this reaction can be represented by the following reaction equation:
M2S+Auo (surface)→Au—S-M+Mo
M is an alkali metal (for example, lithium, sodium, potassium, rubidium, cesium, or francium);
Auo is zero oxidation state gold (e.g., an atom on a Au(111) surface);
M2S is an alkali metal sulfide (for example, lithium sulfide, sodium sulfide, rubidium sulfide, cesium sulfide, or francium sulfide); and
Mo is a zero oxidation state alkali metal.
One embodiment of the reaction is provided as follows:
Rubidium sulfide (Rb2S) is reacted with a gold(111) surface so that a mixed gold-sulfur-rubidium sulfide is formed on the gold surface releasing one mole equivalent of rubidium metal in the reaction solution.
In general, an alkali metal sulfide, M2S, is disposed in a solvent and is presented to a surface containing zero oxidation state gold, Auo, such as a Au(111) surface. The solvent can be, for example, acetonitrile, tetrahydrofuran, acetone, N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMA), or the like. Preferably, the solvent contains little (for example, no more than 0.01% or 100 ppm) or no water. In at least some embodiments, the solvent is an aprotic solvent. The products of this reaction are zero oxidation state alkali metal in solution, Mo, and a mixed metal-gold sulfide which may be attached onto the gold surface.
The gold surface (for example, a Au(111) surface) can be, for example, a thin gold layer formed on a substrate, such as glass, silicon, a ceramic material, plastic, other metal, or the like, including micropipette tips with an inner coating of gold. For example, gold can be deposited (using any suitable deposition technique, such as e-beam evaporation, thermal evaporation, or the like) on the substrate. In at least some embodiments, the substrate may be structured (for example, with peaks and valleys, holes, dimples, pyramidal structures, or any regular or irregular structure, or the like) to increase the surface area of the gold surface. The gold surface can also be gold microsphere beads of various sizes.
Subsequent to the reaction, the gold surface, and accompanying substrate, is removed from the solution. The solvent containing the zero oxidation state alkali metal Mo is evaporated, leaving the zero oxidation state alkali metal Mo in the vessel.
In at least some embodiments, this reaction is performed in a vessel, such as a gas or vapor cell, into which the zero oxidation state alkali metal, Mo, is to be finally dispensed. In at least some embodiments, this reaction is performed in an open vapor cell vessel. In other embodiments, the reaction may be performed in a vessel other than the final vessel in which the alkali metal is to be dispensed with the alkali metal (optionally, in solvent) being disposed to the final vessel after the reaction is complete. For example, the solvent with the zero state alkali metal can be aliquoted and transferred to the target vessel, such as a vapor cell, and then evaporated in the target vessel.
In at least some embodiments, the gold surface area can be controlled to dispense a relatively precise amount of zero oxidation state alkali metal Mo. For example, a 1 cm2 of gold surface may release up to 2.7×1014 zero oxidation state alkali metal, Mo, atoms. In at least some embodiments, each alkali sulfide molecule, M2S, yields one zero oxidation state alkali metal Mo in the vessel as long as the number of alkali sulfide molecule, M2S, used in the reaction does not exceed the binding capacity of the zero oxidation state gold, Auo, surface.
The gold surface is oxidized during the reaction. In at least some embodiments, the gold surface may be regenerated into a zero oxidation state gold, Auo, surface by exposing the surface to a suitable reducing agent. In at least some embodiments, once regenerated, the gold surface may be reused.
In at least some embodiments of Scheme 1 and Scheme 2, the reactions may be performed in an inert atmosphere, such as argon, nitrogen, or any combination thereof. In at least some embodiments of Scheme 1 and Scheme 2, the reactions can be performed at ambient (e.g., room) temperature or in a temperature range from 15° C. to 50° C.
The alkali metal obtained using either of the schemes described above can be utilized in a number of different applications. For example, the alkali metal can be dispensed into a vapor cell (or gas cell). One application of such a vapor cell is in an optically pumped magnetometer.
A magnetometer can be used as part of a magnetic field measurement system.
The computing device 150 can be a computer, tablet, mobile device, or any other suitable device for processing information. The computing device 150 can be local to the user or can include components that are non-local to the user including one or both of the processor 152 or memory 154 (or portions thereof). For example, in at least some embodiments, the user may operate a terminal that is connected to a non-local computing device. In other embodiments, the memory 154 can be non-local to the user.
The computing device 150 can utilize any suitable processor 152 including one or more hardware processors that may be local to the user or non-local to the user or other components of the computing device. The processor 152 is configured to execute instructions provided to the processor 152, as described below.
Any suitable memory 154 can be used for the computing device 150. The memory 154 illustrates a type of computer-readable media, namely computer-readable storage media. Computer-readable storage media may include, but is not limited to, nonvolatile, non-transitory, removable, and non-removable media implemented in any method or technology for storage of information, such as computer readable instructions, data structures, program modules, or other data. Examples of computer-readable storage media include RAM, ROM, EEPROM, flash memory, or other memory technology, CD-ROM, digital versatile disks (“DVD”) or other optical storage, magnetic cassettes, magnetic tape, magnetic disk storage or other magnetic storage devices, or any other medium which can be used to store the desired information and which can be accessed by a computing device.
Communication methods provide another type of computer readable media; namely communication media. Communication media typically embodies computer-readable instructions, data structures, program modules, or other data in a modulated data signal such as a carrier wave, data signal, or other transport mechanism and include any information delivery media. The terms “modulated data signal,” and “carrier-wave signal” includes a signal that has one or more of its characteristics set or changed in such a manner as to encode information, instructions, data, and the like, in the signal. By way of example, communication media includes wired media such as twisted pair, coaxial cable, fiber optics, wave guides, and other wired media and wireless media such as acoustic, RF, infrared, and other wireless media.
The display 156 can be any suitable display device, such as a monitor, screen, or the like, and can include a printer. In some embodiments, the display is optional. In some embodiments, the display 156 may be integrated into a single unit with the computing device 150, such as a tablet, smart phone, or smart watch. The input device 158 can be, for example, a keyboard, mouse, touch screen, track ball, joystick, voice recognition system, or any combination thereof, or the like.
The magnetometers 160 can be any suitable magnetometers including any suitable optically pumped magnetometers. An optically pumped magnetometer (OPM) is a basic component used in optical magnetometry to measure magnetic fields. While there are many types of OPMs, in general magnetometers operate in two modalities: vector mode and scalar mode. In vector mode, the OPM can measure one, two, or all three vector components of the magnetic field; while in scalar mode the OPM can measure the total magnitude of the magnetic field.
Vector mode magnetometers measure a specific component of the magnetic field, such as the radial and tangential components of magnetic fields with respect the scalp of the human head. Vector mode OPMs often operate at zero-field and may utilize a spin exchange relaxation free (SERF) mode to reach femto-Tesla sensitivities. A SERF mode OPM is one example of a vector mode OPM, but other vector mode OPMs can be used at higher magnetic fields. These SERF mode magnetometers can have high sensitivity but may not function in the presence of magnetic fields higher than the linewidth of the magnetic resonance of the atoms of about 10 nT, which is much smaller than the magnetic field strength generated by the Earth. As a result, conventional SERF mode magnetometers often operate inside magnetically shielded rooms that isolate the sensor from ambient magnetic fields including Earth's.
Magnetometers operating in the scalar mode can measure the total magnitude of the magnetic field. (Magnetometers in the vector mode can also be used for magnitude measurements.) Scalar mode OPMs often have lower sensitivity than SERF mode OPMs and are capable of operating in higher magnetic field environments.
The magnetic field measurement systems described herein can be used to measure or observe electromagnetic signals generated by one or more sources (for example, biological sources). The system can measure biologically generated magnetic fields and, at least in some embodiments, can measure biologically generated magnetic fields in an unshielded or partially shielded environment. Aspects of a magnetic field measurement system will be exemplified below using magnetic signals from the brain of a user; however, biological signals from other areas of the body, as well as non-biological signals, can be measured using the system. Uses for this technology outside biomedical sensing include, but are not limited to, navigation, mineral exploration, non-destructive testing, detection of underground devices, asteroid mining, and space applications. In at least some embodiments, the system can be a non-invasive wearable MEG system that can be used outside a magnetically shielded room. Examples of non-invasive magnetic field measurement applications systems or methods are described in U.S. patent application Ser. No. 16/364,338 and U.S. Provisional Patent Application Ser. Nos. 62/829,124 and 62/839,405, all of which are incorporated herein by reference.
The magnetic field generator(s) 162 can be, for example, Helmholtz coils, solenoid coils, planar coils, saddle coils, electromagnets, permanent magnets, or any other suitable arrangement for generating a magnetic field. The optional sensor(s) 164 can include, but are not limited to, one or more magnetic field sensors, position sensors, orientation sensors, accelerometers, image recorders, or the like or any combination thereof.
The above specification provides a description of the invention and its manufacture and use. Since many embodiments of the invention can be made without departing from the spirit and scope of the invention, the invention also resides in the claims hereinafter appended.
This application is related to U.S. Provisional Patent Application Ser. Nos. 62/719,475, filed Aug. 17, 2018; 62/745,144, filed Oct. 12, 2018; and 62/776,895, filed Dec. 7, 2018, all of which are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62776895 | Dec 2018 | US | |
| 62745144 | Oct 2018 | US | |
| 62719475 | Aug 2018 | US |