1. Field of the Invention
The present invention relates to a dispersion compensating optical fiber and to a dispersion compensating optical fiber module. Specifically, the present invention relates to a dispersion compensating optical fiber compensating for wavelength dispersion and the dispersion slope caused by transmitting optical signals in an employed wavelength band selected from the wavelength region from 1.52 μm to 1.63 μm by means of a standard single mode optical fiber with a dispersion zero at 1.3 μm, and relates to a dispersion compensating optical fiber module including the dispersion compensating optical fiber.
2. Description of Related Art
Systems including optical amplifiers such as very-long-distance non-repeating relays for wavelengths of 1.52 to 1.63 μm are already commercially available as erbium-doped optical fiber amplifiers and are in practical use. Furthermore, the development of wavelength division multiplexing transmission has rapidly progressed with the increase in transmission capacity. Wavelength division multiplexing transmission system is already commercially available in a number of transmission lines. It is anticipated that the expansion of the wavelength band and the increase in the number of times wavelengths are multiplexed will rapidly progress in the future.
In order to perform high-speed transmission, the wavelength dispersion in transmission lines of optical fibers are preferably as small as possible in the transmission band, but are not zero. Moreover, in order to perform wavelength division multiplexing in a transmission system, it is important that the ratio of dispersion change relative to wavelength change in the entire length of the transmission path (which is referred to as “dispersion slope”, hereinafter) is small in order to decrease the difference in the dispersion between each wavelength in an employed wavelength band, in addition to decreasing amplification differences caused by the erbium-doped optical fiber amplifier in the employed wavelength band and decreasing the wavelength dispersion.
Moreover, recent long-distance systems require techniques for suppressing effects of nonlinearity which may cause deterioration, such as transmission characteristics, because the number of wavelengths multiplexed and the optical power propagating through the optical fiber rapidly increase.
The magnitude of the nonlinearity is expressed as n2/Aeff, where n2 represents the nonlinear refractive index for the optical fiber, and Aeff represents the effective area of the optical fiber. In order to suppress the effects of the nonlinearity, n2 is required to be small or Aeff is required to be large. However, it is difficult to significantly decrease n2 in an optical fiber composed of silica glass material, because n2 is a constant value of a material for the optical fiber. Therefore, it is important to increase Aeff in order to suppress the effect of nonlinearity.
Recently, single mode optical fiber networks for a wavelength of 1.3 μm are being used worldwide. When the transmission for a wavelength of 1.55 μm band is performed by using the optical fiber network, about +17 ps/nm/km of wavelength dispersion is caused. Therefore, when optical signals are transmitted through the optical fiber, the transmission characteristics are worsened by the wavelength dispersion.
A dispersion compensating optical fiber for compensating the wavelength dispersion has been developed and is commercially available. The dispersion compensating optical fiber has a large negative dispersion in the 1.55 μm wavelength band. By connecting the dispersion compensating optical fiber to a transmitting single mode optical fiber at a suitable length, accumulated positive dispersion caused by the transmitting single mode optical fiber can be compensated for, which actualizes high-speed communication.
Moreover, the wavelength division multiplexing system has recently progressed accompanying the increase in the transmission capacity. For example, in the case of compensating for the wavelength dispersion of the transmitting optical fiber for the wavelength of 1.3 μm by using a dispersion compensating optical fiber having a large negative wavelength dispersion and a positive dispersion slope, although the dispersion of one wavelength among wavelengths can be compensated for, the dispersions of other wavelengths are not sufficiently compensated for, and the transmission characteristics of the wavelengths far from the compensated wavelength are worsened.
Accordingly, a dispersion-slope-compensating and dispersion-compensating optical fiber having a W-type refractive index profile with a negative dispersion slope as shown in
The dispersion-slope-compensating and dispersion-compensating optical fiber can compensate for the wavelength dispersion and the dispersion slope by rendering it into a cable for a transmission line or by inserting it as a small module into the receiving side or the transmitting side of an existing transmission line.
However, a conventional dispersion compensating optical fiber has a structure in which the specific refractive index difference Δ1 of the center core portion increases and the specific refractive index difference Δ2 of the side core portion around the core portion decreases, and has a small core diameter, in order to increase the absolute value of the wavelength dispersion per unit length while having a refractive index distribution profile as shown in FIG. 6.
In
Although examples in which the dispersion slopes are compensated for by means of the dispersion compensating optical fibers each having a W-type profile are reported in TuG3 of OFC 2000 (Optical Fiber Communication Conference) and in C3-3-38 of the Institute of Electronics, Information and Communication Engineers in 2000, for example, effective areas (Aeff) of both of the dispersion compensating optical fibers are 18.4 μm2, which are not sufficiently large.
Moreover, in order to improve the bending loss and the dispersion slope characteristics, a dispersion-slope-compensating and dispersion-compensating optical fiber having segment-attached a W-type refractive index profile as shown in
Although the present inventors reported, at 14C4-4 at the OECC 2000 (Optoelectronics and Communications Conference), one embodiment of this dispersion compensating optical fiber compensating the dispersion slope, which has an effective area (Aeff) enlarged to 21.0 μm2, the absolute value of the wavelength dispersion is 61.5 ps/nm/km, which is small. Therefore, it is required to increase the length of the fiber for producing a dispersion compensating optical fiber module by winding the fiber into a small coil. However, it is difficult to wind the fiber into the small coil and to miniaturize the module. When the length of the fiber used becomes longer, the cost required for producing the module increases.
The present inventors, Shimizu et al., reported, at C3-3-33 of the Institute of Electronics, Information and Communication Engineers in 2001, a dispersion compensating optical fiber module having low nonlinear properties, low losses, and superior dispersion slope compensating functions, which are not provided conventionally.
However, the dispersion compensating optical fiber has characteristics in which the microbending loss increases as the dispersion slope compensation ratio increases from low values to 100%. Moreover, the microbending loss tends to be caused by decreasing the dispersion values or increasing the effective area. In order to prevent the microbending loss, a method in which an optical fiber is fixed by a resin without using a reel (NFOEC (National Fiber Optic Engineers Conference) 2000, pp. 420 to 429).
An optical fiber generally includes a coating layer which is made from at least one ultraviolet light curable resin such as ultraviolet light curable urethane acrylate resin, and which is formed onto the surface of glass. Since the surface of the coating layer has a slight adhesive property (which is referred to as “surface tackiness”), which causes adhesion of portions of the optical fiber to other portions thereof, a dispersion compensating optical fiber module produced by winding a long optical fiber into a small coil has problems in that temperature characteristics are increased.
The adhesive property (surface tackiness) is defined as the degree to which optical fibers stick together. A specific example of a method for measuring the adhesive property is disclosed in Japanese Patent Application, First Publication No. Hei 10-62301, in which the tensile change of an optical fiber which is wound many times around a delivery roll so as to be overlapped is measured by rewinding the optical fiber with a constant tension.
Specifically, various situations are anticipated for environments in which a dispersion compensating optical fiber module is employed, and suitable operations of the dispersion compensating optical fiber module may be required from the low temperature region (down to −40° C.) to the high temperature region (up to +80° C.). A dispersion compensating optical fiber used for the dispersion compensating optical fiber module has a short fiber length, a large absolute value of the wavelength dispersion, and a large effective area, which enable miniaturization of the module. Therefore, the microbending loss of the dispersion compensating optical fiber is larger than those of conventional dispersion compensating optical fibers. As a result, problems are caused in which the loss at the low temperature region is increased by the microbending loss and the surface tackiness, when the module is produced by using the dispersion compensating optical fiber. Although the aforementioned problems are caused depending on characteristics of the dispersion compensating optical fiber, the problems are significant when the module is formed into a small coil in which portions of the optical fibers are adhered to other portions thereof.
The present invention has been accomplished in view of the aforementioned circumstance, and aims at providing a dispersion compensating optical fiber module in which the loss change is suppressed over a broad temperature range even if the dispersion compensating optical fiber is wound around a small reel.
The present invention provides a dispersion compensating optical fiber comprising: an uncovered dispersion compensating optical fiber containing a core and a cladding; and a resin coating which is disposed around the uncovered dispersion compensating optical fiber and which has an adhesive property of 10 g/mm or less.
The resin coating may hves an adhesive property of 1 g/mm or less. The outer diameter of the uncovered dispersion compensating optical fiber may be in a range from 90 to 125 μm, and the outer diameter of the dispersion compensating optical fiber may be in a range from 180 to 250 μm.
The resin coating may include an outer coating layer. The outer coating layer may contain silicone in an amount of 1% by weight or more. The outer coating layer may include an ultraviolet light curable urethane acrylate resin containing a coloring agent. The outer coating layer may be formed to have a thickness of 3 μm or more. The outer coating layer may be formed by a step different from an optical fiber drawing step.
The resin coating may further include a single or double coating layer formed between the cladding and the outer coating layer. The outer diameter of the uncovered dispersion compensating optical fiber may be in a range from 90 to 125 μm, and the diameter coated by the single or double coating layer may be in a range from 180 to 250 μm.
The optical fiber may have a bending loss of 20 dB/m or less at the bending diameter of 20 mm in an employed wavelength band selected from the range of 1.52 to 1.63 μm.
The dispersion compensating optical fiber may have an effective area of 19 μm2 or more, a wavelength dispersion of −70 ps/nm/km or less, and a cut-off wavelength which is capable of substantially single mode propagation, in an employed wavelength band selected from the range of 1.52 to 1.63 μm, and the compensation ratio of the dispersion slope may be 80 to 120% when the wavelength dispersion of a single mode optical fiber having a zero dispersion wavelength shorter than the employed wavelength band is compensated for by using the dispersion compensating optical fiber having a length enough to compensate for the wavelength dispersion of the single mode optical fiber to zero or nearly zero.
The uncovered dispersion compensating optical fiber may have a refractive index profile including a center core portion; a core portion provided around the outer periphery of the center core portion and having a lower refractive index than that of the center core portion; a ring core portion provided around the outer periphery of the core portion and having a lower refractive index than that of the center core portion and a higher refractive index than that of the core portion; and a cladding portion provided around the periphery of the ring core portion and having a higher refractive index than the core portion and a lower refractive index than the ring core portion; in which the radius of the ring core portion is 6 to 10 μm; the ratio of the radius of the core portion relative to the radius of the center core portion is 2.5 to 4.0; and the ratio of the radius of the ring core portion relative to the radius of the core portion is 1.1 to 2.0; and when the refractive index of the cladding portion is taken as the standard, the relative refractive index of the center core portion is 1.2 to 1.7%; the relative refractive index of the core portion is −0.20 to −0.45%; and the relative refractive index of the ring core portion is 0.2 to 1.1%.
Moreover, the present invention provides a dispersion compensating optical fiber module, wherein the aforementioned dispersion compensating optical fiber is wound into a coil. The dispersion compensating optical fiber may be wound by the winding tension of 20 to 70 gf around a reel having a minimum diameter of 200 mm or less.
In the following, although preferred embodiments of the present invention will be explained, the present invention is not limited by the preferred embodiments, and components and concepts of the embodiments may be freely combined.
A dispersion compensating optical fiber according to a first embodiment of the present invention includes an uncovered dispersion compensating optical fiber and a resin coating. In
The center core portion 1 has a refractive index higher than that of the cladding portion 4. The core portion 2 has a refractive index lower than that of the cladding portion 4. The ring core portion 3 has a refractive index higher than that of the cladding portion 4.
As shown in
When the relative refractive index differences for the central core portion 1 is represented as Δ1, the relative refractive index differences for the core portion 2 is represented as Δ2, and the relative refractive index differences for the ring core portion 3 is represented as Δ3, where the refractive index of the cladding portion 4 is taken as the standard, Δ1 is 1.2 to 1.7%, Δ2 is −0.20 to −0.45%, and Δ3 is 0.2 to 1.1%.
The dispersion compensating optical fiber has an effective area of 19 μm2 or more, a wavelength dispersion of −70 ps/nm/km or less, and a cut-off wavelength which is capable of substantially single mode propagation, in an employed wavelength band selected from the range of 1.52 to 1.63 μm. The compensation ratio of the dispersion slope is 80 to 120% when the wavelength dispersion of a single mode optical fiber having a zero dispersion wavelength shorter than the employed wavelength band is compensated for by using the dispersion compensating optical fiber having a length sufficient to compensate for the wavelength dispersion of the single mode optical fiber to zero, or nearly zero.
The dispersion compensating optical fiber includes the uncovered dispersion compensating optical fiber having an outer diameter of 90 to 125 μm and the resin coating formed around the uncovered dispersion compensating optical fiber and having an adhesive property of 10 g/mm or less, preferably 1 g/mm or less. When the adhesive property of the dispersion compensating optical fiber is more than 10 g/mm, since portions of the dispersion compensating optical fiber tend to adhere to other portions thereof by winding the dispersion compensating optical fiber into a coil in accordance with the temperature change, the loss change tends to increase.
The adhesive property is measured by the following method. First, the optical fiber is wound on a winding roll a number of times, and is introduced into a transmitting side dancer roll. Then, it is introduced into a receiving roll through a first fixed roll, a moving roll and a second fixed roll, and is set to a tension pickup between the moving roll and the second fixed roll. The optical fiber passed through the receiving roll is mounted on a winding roll through a winding side dancer roll similar to the transmitting side dancer roll. Then, the winding roll is rotated to impart a fixed tension to the optical fiber. The tension pickup detects the moving quantity of a detecting roll by the tension of the optical fiber to detect the tension, and displays and records it on a monitor. In this case, since the tension change added to the optical fiber becomes a value according to the surface tackiness, the surface tackiness of the optical fiber can be easily and quantitatively measured and evaluated.
The resin coating includes a single or double coating layer and an outer coating layer disposed around the single or double coating layer. The diameter coated by the single or double coating layer is in a range from 180 to 250 μm. The outer coating layer has a thickness of 3 μm or more, and preferably 3 to 7 μm. The resin coating preferably contains at least one ultraviolet light curable resin such as ultraviolet light curable urethane acrylate resin. The outer coating layer may further contain silicone in an amount of 1% by weight or more, preferably 1 to 5% by weight, more preferably 2 to 3% by weight, relative to the total weight of the outer coating layer. By adding silicone into the outer coating layer in an amount of 1% by weight or more, the value of the adhesive property can be further reduced.
The dispersion compensating optical fiber can be produced by drawing an optical fiber preform (an uncovered dispersion compensating optical fiber) together with a resin composition containing silicone and the ultraviolet light curable resin. The optical fiber preform can be produced by a VAD method, an MCVD method, a PCVD method, or the like. The optical fiber drawing step for forming around the uncovered dispersion compensating optical fiber the resin coating having an adhesive property of 10 g/mm or less is preferably carried out under the conditions in which the resin composition is applied onto the uncovered dispersion compensating optical fiber to have a thickness of 3 μm or more, and in which the atmospheric oxygen concentration during curing of the ultraviolet light curable resins is set to 2% or less, more preferably 0%. Moreover, the drawing speed is preferably set to 300 to 1,000 m/min, more preferably 300 to 600 m/min, so as to prevent winding disarrangement.
Next, a dispersion compensating optical fiber according to a second embodiment of the present invention will be explained.
In the dispersion compensating optical fiber of this embodiment, the uncovered dispersion compensating optical fiber disclosed in the first embodiment is coated by a resin coating comprising an outer coating layer formed by an ultraviolet light curable urethane acrylate resin including silicone and a coloring agent. Preferably, the content of silicone in the ultraviolet light curable urethane acrylate resin is 1 to 5% by weight, and more preferably 2 to 3% by weight, relative to the total weight of the ultraviolet light curable urethane acrylate resin. The diameter coated by the resin coating is in a range from 180 to 250 μm. The adhesive property of the dispersion compensating optical fiber is 1 g/mm or less. The ultraviolet light curable resin containing a coloring agent may be a UV curable ink or the like. Instead of the coloring agent, other materials which can decrease the adhesive property of the resin coating can be mixed with the ultraviolet light curable resin.
The resin coating is formed by a step different from an optical fiber drawing step. The step of forming the resin coating is carried out under the conditions in which the atmospheric oxygen concentration during curing of the ultraviolet light curable urethane acrylate resin is set to 2% or less, more preferably 0%.
The dispersion compensating optical fiber has a bending loss of 20 dB/m or less at a bending diameter of 20 mm in an employed wavelength band selected from the range of 1.52 to 1.63 μm.
Next, one embodiment of a dispersion compensating optical fiber module according to the present invention will be explained.
The dispersion compensating optical fiber module is produced by winding the dispersion compensating optical fiber into a coil to suppress the loss change caused by the temperature change. The dispersion compensating optical fiber is wound by the winding tension of 20 to 70 gf, more preferably 30 to 50 gf, around a reel having a minimum diameter of 200 mm or less.
The aforementioned dispersion compensating optical fiber module is used by being disposed between a light source and a transmitting single mode optical fiber, or disposed to the side of the transmitting single mode optical fiber at which the optical signal is emitted.
Since the dispersion compensating optical fiber has a low adhesive property which can prevent portions of the wavelength dispersion compensating optical fiber from adhering to other portions thereof when the wavelength dispersion compensating optical fiber is wound into a small coil, the wavelength dispersion compensating optical fiber module has a low loss change in accordance with the temperature change over a broad temperature range. Therefore, the dispersion compensating optical fiber module can have a low loss and can be miniaturized.
In the following, specific examples will be explained.
Five dispersion compensating optical fiber preforms were produced by an MCVD method or a PCVD method. Then, dispersion compensating optical fibers (A to E) were produced by drawing the dispersion compensating optical fiber preforms together with an ultraviolet light curable resin. The drawing step of each of the dispersion compensating optical fiber preforms was carried out while controlling drawing conditions so that the produced resin coating had an adhesive property of 5 to 6 g/mm. Specifically, the atmospheric oxygen concentration during curing of the ultraviolet light curable resin was set to 2% or less, and the drawing speed was set to be 300 m/min so as to prevent winding irregularities.
Each of the dispersion compensating optical fibers (A to E) has a profile as shown in FIG. 1. The specific refractive index difference Δ1 of the center core portion 1, the specific refractive index difference Δ2 of the core portion 2, the specific refractive index difference Δ3 of the ring core portion 3, the ratio b/a of the core radius relative to the center core radius, the ratio c/b of the ring core radius relative to the core radius, and other optical properties, of each of the uncovered dispersion compensating optical fibers (A to E) are shown in Table 1. As shown in Table 1, each of the dispersion compensating optical fibers has a low transmission loss in a range from 0.25 to 0.32 dB/km and has a large effective area Aeff of 20 μm2 or more.
By using the dispersion compensating optical fibers A and B shown in Table 1, three dispersion compensating optical fiber modules (A to C) each of which has a dispersion compensation value different from the others were produced. Characteristics of the dispersion compensating optical fiber modules are shown in Table 2. As shown in Table 2, results of the characteristics required for the dispersion compensating optical fiber modules, such as dispersion slope compensation ratio, insertion loss, PMD, and the like are satisfactory.
It is possible to increase transmission capacity and to increase transmission length by inserting the dispersion compensating optical fiber module and an amplifier module into the terminal of a transmission line of a conventional single mode optical fiber. Moreover, it is possible to miniaturize the module by using the dispersion compensating optical fiber having a low bending loss and a large absolute value of the wavelength dispersion.
Moreover, temperature characteristics of the insertion loss of the dispersion compensating optical fiber modules are shown in FIG. 2. As shown in
Five dispersion compensating optical fiber preforms were produced by an MCVD method or a PCVD method. Then, dispersion compensating optical fibers each of which had the same profile as shown in
Each of the produced dispersion compensating optical fibers includes an uncovered dispersion compensating optical fiber having an outer diameter of 125 μm, the double coating layer by which the coated diameter was 230 μm, and the outer coating layer by which the coated diameter was 240 μm. That is, the thickness of the outer diameter was 5 μm.
Each of the produced dispersion compensating optical fibers has a low transmission loss in a range from 0.25 to 0.32 dB/km and has a large effective area (Aeff) of 20 μm2 or more.
By using the dispersion compensating optical fibers each having the same profile as that of the aforementioned dispersion compensating optical fiber A or B, three dispersion compensating optical fiber modules (D to F), each of which has a dispersion compensation value different from the others, were produced. Characteristics of the dispersion compensating optical fiber modules are shown in Table 3. As shown in Table 3, results of the characteristics required for the dispersion compensating optical fiber modules, such as dispersion slope compensation ratio, insertion loss, PMD, and the like are satisfactory.
Moreover, temperature characteristics of the insertion loss of the dispersion compensating optical fiber modules are shown in FIG. 3. As shown in
Two dispersion compensating optical fiber preforms were produced by an MCVD method or a PCVD method. Then, dispersion compensating optical fibers (F and G) were produced by drawing the dispersion compensating optical fiber preforms with ultraviolet light curable resin to form a double coating layer, and then by coating a resin composition including silicone and an ultraviolet light curable urethane acrylate resin containing a coloring agent to form an outer coating layer around the double coating layer, while controlling coating conditions so that the produced resin had an adhesive property of 1 g/mm or less.
Each of the dispersion compensating optical fibers (F and G) has a profile as shown in FIG. 1 and properties shown in Table 4. Each of the produced dispersion compensating optical fibers includes an uncovered dispersion compensating optical fiber having an outer diameter of 125 μm, the double coating layer by which coated diameter was 230 μm, and the outer coating layer by which coated diameter was 240 μm. That is, the outer coating layer had a thickness of 5 μm.
Each of the produced dispersion compensating optical fibers can compensate, in an employed wavelength band selected from a range of 1565 nm to 1625 nm, a single mode optical fiber having a wavelength dispersion of +19.0 ps/nm/km and a wavelength dispersion slope of +0.054 ps/nm2/km, at a wavelength of 1590 nm.
Each of the produced dispersion compensating optical fibers has a low transmission loss in a range from 0.25 to 0.32 dB/km and has a large effective area (Aeff) of 20 μm2 or more.
By using the dispersion compensating optical fibers F and G shown in Table 4, three dispersion compensating optical fiber modules (G to I) each of which has a dispersion compensation value different from the others were produced. Characteristics of the dispersion compensating optical fiber modules are shown in Table 5. As shown in Table 5, results of the characteristics required for the dispersion compensating optical fiber modules, such as dispersion slope compensation ratio, insertion loss, PMD, and the like are satisfactory.
Moreover, temperature characteristics of the insertion loss of the dispersion compensating optical fiber modules were measured at a wavelength of 1625 nm which is the longest wavelength in the employed wavelength band. Obtained results are shown in FIG. 4. As shown in
Next, comparative examples will be shown so as to compare them with the aforementioned examples.
Five dispersion compensating optical fiber preforms were produced by an MCVD method or a PCVD method. Then, dispersion compensating optical fibers were produced by drawing the dispersion compensating optical fiber preforms. The drawing step of each of the dispersion compensating optical fiber preforms was carried out by using ultraviolet light curable resin under the conditions in which the atmospheric oxygen concentration during curing the ultraviolet light resin was not controlled.
Each of the dispersion compensating optical fibers has the same profile as shown in FIG. 1 and properties shown in Table 1. The adhesive property of each of the produced dispersion compensating optical fibers was 15 g/mm.
By using the dispersion compensating optical fibers each having the same profile as that of the dispersion compensating optical fibers A or B, five dispersion compensating optical fiber modules (J to N) each of which has a dispersion compensation value different from the others were produced.
Characteristics of the dispersion compensating optical fiber modules were shown in Table 6. As shown in Table 6, results of the characteristics required for the dispersion compensating optical fiber modules, such as dispersion slope compensation ratio, insertion loss, PMD, and the like are satisfactory.
Temperature characteristics of the insertion loss of the dispersion compensating optical fiber modules are shown in FIG. 5. As shown in
As described above, since the dispersion compensating optical fiber according to the present invention has a low adhesive property, the dispersion compensating optical fiber module produced from the dispersion compensating optical fiber can satisfactorily compensate for the wavelength dispersion and the dispersion slope while suppressing the loss increase in accordance with the broad temperature change, which is caused by adhering portions of the dispersion compensating optical fiber to other portions thereof when winding the dispersion compensating optical fiber into a coil to form the dispersion compensating optical fiber module. Thus, according to the present invention, it is possible to prevent the loss increase of the dispersion compensating optical fiber module and to miniaturize the dispersion compensating optical fiber module.
Number | Date | Country | Kind |
---|---|---|---|
P2001-193546 | Jun 2001 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
3980390 | Yamamoto et al. | Sep 1976 | A |
4482204 | Blyler et al. | Nov 1984 | A |
4715679 | Bhagavatula | Dec 1987 | A |
4801186 | Wagatsuma et al. | Jan 1989 | A |
4877304 | Bhagavatula | Oct 1989 | A |
5259060 | Edward et al. | Nov 1993 | A |
5261016 | Poole | Nov 1993 | A |
5361319 | Antos et al. | Nov 1994 | A |
5381504 | Novack et al. | Jan 1995 | A |
5416880 | Edwards et al. | May 1995 | A |
5448674 | Vengsarkar et al. | Sep 1995 | A |
5555340 | Onishi et al. | Sep 1996 | A |
5568583 | Akasaka et al. | Oct 1996 | A |
5644670 | Fukuda et al. | Jul 1997 | A |
5673354 | Akasaka et al. | Sep 1997 | A |
5680491 | Shigematsu et al. | Oct 1997 | A |
5684909 | Liu | Nov 1997 | A |
5701188 | Shigematsu et al. | Dec 1997 | A |
5740297 | Onishi et al. | Apr 1998 | A |
5742723 | Onishi et al. | Apr 1998 | A |
5781673 | Reed et al. | Jul 1998 | A |
5799123 | Oyobe et al. | Aug 1998 | A |
5802234 | Vengsarkar et al. | Sep 1998 | A |
5802235 | Akasaka | Sep 1998 | A |
5838867 | Onishi et al. | Nov 1998 | A |
5887093 | Hansen et al. | Mar 1999 | A |
5887104 | Sugizaki et al. | Mar 1999 | A |
5933561 | Sugizaki | Aug 1999 | A |
5995694 | Akasaka et al. | Nov 1999 | A |
5999679 | Antos et al. | Dec 1999 | A |
6009221 | Tsuda | Dec 1999 | A |
6021245 | Berger et al. | Feb 2000 | A |
6031955 | Mukasa et al. | Feb 2000 | A |
6048911 | Shustack et al. | Apr 2000 | A |
6055081 | Koyano et al. | Apr 2000 | A |
6173102 | Suzuki et al. | Jan 2001 | B1 |
6744959 | Takahashi | Jun 2004 | B2 |
Number | Date | Country |
---|---|---|
1 083 446 | Mar 2001 | EP |
1 107 027 | Jun 2001 | EP |
56149351 | Nov 1981 | JP |
0294229 | Jul 1990 | JP |
04006125 | Jan 1992 | JP |
04310547 | Nov 1992 | JP |
04342445 | Nov 1992 | JP |
05203847 | Aug 1993 | JP |
08036123 | Feb 1996 | JP |
10-62301 | Mar 1998 | JP |
10115727 | May 1998 | JP |
WO 0050935 | Aug 2000 | JP |
WO 0111402 | Feb 2001 | WO |
Number | Date | Country | |
---|---|---|---|
20030049006 A1 | Mar 2003 | US |