Patent Grant
10689545
The invention relates to a dispersion and also to a method for coating objects, in particular heat exchanger structures, in which this dispersion is applied on a carrier structure and is crosslinked and/or made into a film with formation of a layer. Likewise, the invention relates to heat exchanger structures coated in this way. The dispersions according to the invention can likewise be used for coatings in the construction of chemical plants and also in medical technology.
Exploitation of the physical process of adsorption of gases on microporous surfaces and hence the use in thermally actuated heat pumps and refrigeration machines has various advantages:
Disadvantages result due to the equipment which to date is still very large and the poor power density associated therewith, in comparison with conventional mechanical systems.
Heat pumps or adsorption refrigeration plants constructed at present have low power densities, which results in a very large construction in order to achieve corresponding cooling or heating outputs. Important approaches for making the construction more compact and increasing the power density reside in constructing the sorption chamber to be smaller. For this purpose, a large surface of the heat exchanger must be ensured and good adhesion of the sorption material thereon.
Adsorption refrigeration machines and -heat pumps and also thermal stores based on the adsorption of gases on microporous solid materials are known from the state of the art, mainly water and also silica gels, zeolites and zeolite-like materials being used as operating media. Generally beds or loose adhesions are hereby used.
In addition, coating technology has been developed in recent years, which is distinguished however frequently by inadequate coupling and also by a lack of adequate thermal and mechanical stability. The possible systems of binder and active sorption material and also the carrier structure have to date been very restricted.
If the sorption material in the form of a granular bed or as a moulded article is used in the sorption heat pumps or sorption refrigeration pumps, heat- and material transport limit the output of the plant. Whilst the material transport is limited naturally by macroscopic granulates, the heat transport is restricted by the mainly present point contacts, e.g. spherical granulates on a carrier metal sheet.
If in contrast the sorption material is used in a thin layer on the heat exchanger due to a planar composite, the material transport and above all the heat transport can be significantly improved.
An adsorber element is known from DE 10 2008 050 926 A1, which consists of a carrier material on which sorbent particles with a binder material are disposed as adsorber layer. As binder, colloidal binders based on silicon oxide or aluminium oxide are used here.
Starting herefrom, it was the object of the present invention to provide a stable dispersion for coating substrates, in particular metallic and ceramic substrates, which allow more simple handling during coating.
This object is achieved by the features of the dispersion described herein, by the method for coating substrates and the coated heat exchanger structure also described herein, and the advantageous developments thereof. Uses according to the invention are also described.
According to the invention, a dispersion for coating substrates which has the following components is provided:
There is understood by sorbent, within the scope of the present invention, in particular an adsorbent. However, it can also be materials which exhibit absorption in addition.
According to the invention, a dispersion of a binder and a porous solid material in an organic solvent was therewith provided, which surprisingly is stable over at least 6 h, preferably 12 h, particularly preferred 24 h and in particular 48 h. With the dispersion according to the invention, for example ceramic and metallic substrates can hence be coated with a porous solid material. The preparation of binder, sorption material and organic solvent is applied on the substrate and solidified by evaporation of the organic solvent or crosslinked in addition in the case of reactive end groups.
In contrast to the aqueous dispersion, the dispersion according to the invention in an organic solvent has the following advantages:
The polysiloxane binder or the precursor thereof emerges from production already in the form of an organic solution/dispersion, the preparation of an aqueous dispersion and the complexity associated therewith are dispensed with. In addition, the solution comprises no dispersion aids and fewer further processing aids.
Numerous sorption materials, e.g. MOFs, such as copper(II)-trimesate “HKUST-1” or zinc terephthalate MOF-5, are produced by solvothermal synthesis and are produced from this in the form of a dispersion in an organic solvent. If likewise the binder is present in an organic phase, the suspension for the coating can be produced directly by blending the two components. Purification of the material can be effected significantly more easily on the coated heat exchanger, complex and expensive separation steps (centrifugation) can be avoided.
Many sorption materials react sensitively to water. When using organic suspensions, successful coatings of these materials were able to be produced. The possibility of producing coatings also from water-sensitive materials opens up numerous further application possibilities, for instance in the field of sensory technology or heterogeneous catalysis. With skilled process control, also open handling of particularly sensitive substances, even those requiring protective gas, in the form of an organic dispersion is conceivable.
By the choice of the organic solvent, the evaporation rate can be controlled very well, which enables a more efficient drying process.
Organic solvents generally have a lower surface tension, as a result of which wetting is improved relative to the undercoat and to the adsorption material and thus improved distribution of the binder on the surfaces is obtained. Liquids with low surface tensions have in addition more homogeneous surfaces after drying.
Suspensions of sorption materials in organic liquids are shown to be significantly more stable with respect to demixing and sedimentation, which substantially simplifies implementation on a large industrial scale.
By varying the molecule size in the case of different solvents, it can be controlled specifically whether the solvent penetrates into the micro- and/or micropores of the adsorption material. As a result, it can be specifically ensured for example that a dissolved binder does not penetrate into the pores at all and this can no longer adhere or cause a blockage.
As a result of the low vapour pressures of many solvents, drying at high temperatures can become superfluous. Thus the drying process no longer requires further use of energy.
Relative to aqueous dispersions, the dispersion according to the invention has the advantage in addition that, by the choice of a suitable organic solvent with a low boiling point in comparison to water, the evaporation rate and hence the drying process during the coating can be significantly accelerated.
The dispersion according to the invention thereby has the additional advantages, with respect to the coating, that mechanically and thermally highly-loadable surfaces can herewith be produced, which enable good heat- and material transport, the technical and equipment outlay during the coating being able to be kept low.
It is preferred that the at least one sorbent has nano-, meso- and/or macropores and hence is porous and has a BET surface of at least 300 m2/g, in particular of 300 to 5,000 m2/g. There should be understood here by nanopores, pores with a diameter of 0.1 to 2 nm. Mesopores have a diameter of 2 to 50 nm, whilst macropores have a diameter of at least 50 nm, in particular of 50 nm to 950 μm.
A further preferred embodiment provides that the mesoporous alumino- and/or silicon compounds are selected from the group consisting of silica gels, zeolites and zeolite-like materials, aluminophosphates, silica aluminophosphates and metal aluminium phosphates and also mixtures hereof.
Preferably, the at least one sorbent is water-sensitive. There are included herein, for example MOF-5 or HKUST-1. However, also water-sensitive activated carbons or mesoporous molecular sieves (MCM) exist.
The at least one sorbent is preferably present as a powder, in particular with an average crystallite size of 50 nm to 20 μm and in particular with an average particle size of 200 nm to 200 μm.
It is further preferred that the at least one binder is selected from the group consisting of aliphatic, olefinic and aromatic mono-, di- and triorganosiloxanes which can be crosslinked via a crosslinker, in particular silanes, silicates, such as soda water glass or silicic acids. Aliphatic and/or aromatic diorganosiloxanes, such as for example methylsilicone resins or phenylsilicone resins or combinations hereof, are suitable in particular for this purpose. These can be present dissolved as monomers or even be polymerised. A crosslinker can be added in order to vary the strength and the flexibility. This can be introduced as supplement, such as for example tri- or tertiary silanes (for example octyltriethoxysilane or beta-(3,4-epoxycyclohexyl)ethyltriethoxysilane) or can even be contained as active end group of the polymers.
Preferably, the at least one solvent is selected from the group consisting of hydrocarbons, in particular aliphatic and aromatic hydrocarbons, preferably benzene and alkyl-substituted benzene derivatives, such as toluene, xylenes or ethylbenzene, or from the group consisting of aliphatic or aromatic alcohols, esters, ketones such as methanol, 2-methylpropan-1-ol or 2-methoxy-1-methylethylacetate.
Furthermore, it is preferred that, in the dispersion, in addition stabilisers, emulsifiers, low-molecular functional additives for improving the processability, for example organic and inorganic rheological additives, in particular polyurethane resins or pyrogenic silicic acid, components increasing heat conductivity, in particular graphite, expanded graphite, carbon fibres, carbon tubes, glass fibres, metallic nanoparticles and also mixtures hereof, are contained.
A further preferred variant provides that the suspension, relative to the dry mass without a proportion of solvent, has the following composition:
60% to 99% by weight, in particular of 80 to 95% by weight, of the sorbent,
1 to 40% by weight, in particular of 5 to 15% by weight, of the binder,
0 to 10% by weight of additives, selected from the group of stabilisers, emulsifiers, low-molecular functional additives for improving the processability and also mixtures hereof.
The suspensions according to the invention have surprisingly good stability which enables a coating with the dispersion in a time period of at least 6 h, preferably 12 h, particularly preferred 24 h and in particular 48 h.
According to the invention, a method for coating substrates, in particular heat exchanger structures, is likewise provided, in which
a) the dispersion is formed on the substrate or is applied on the substrate after production,
b) film formation and/or crosslinking with formation of a layer is effected at temperatures of 0° C. to 300° C., in particular at temperatures of 50 to 250° C.
Firstly film formation can hereby take place on the surface and the material subsequently can be thoroughly dried. By introducing active end groups and/or crosslinker molecules, additionally a molecular crosslinking of the binder can be produced during the drying process.
Preferably, the film formation and/or—crosslinking can be accelerated by applying a vacuum or by heating.
It is further preferred that the dispersion is formed on the substrate by firstly the binder being applied on the substrate and subsequently the sorbent being scattered on in dry or moist form and subsequently being dried.
Handling of the materials under a water-free or even inert gas atmosphere can hereby be required.
Application of the dispersion in step b) is effected preferably by means of manual application, immersion coating, spray coating, rotational coating or various knife-coating methods.
It is further preferred that the coating is produced with a layer thickness in the range of 100 nm to 10 mm, in particular of 100 μm to 1 mm.
A further preferred embodiment provides that the substrate consists of a metal or a metal alloy, in particular aluminum and the alloys thereof, copper and the alloys thereof or stainless steel, a glass, a polymer, a ceramic or combinations of these or essentially comprises these.
According to the invention, likewise coated heat exchanger structures which are producible according to the previously described method are provided.
The dispersions according to the invention are used for the production of
There should be understood here by sterile layers, sterile coatings, e.g. of operation instruments. Since the sorbent keeps the water content on the surface of such layers to a minimum because of the water absorbency, the formation of germs, the formation of which is possible only in an aqueous media, can be suppressed outstandingly because of these dry conditions.
The subject according to the invention is intended to be explained in more detail with reference to the subsequent examples without wishing to restrict said subject to the specific embodiments shown here.
Coating of an aluminum sheet with a xylene-containing suspension of a water-sensitive adsorption material and a polyorganosiloxane as binder
The aluminum sheets (alloy AlMg3) were washed with isopropanol and dried. Subsequently, the sheets were etched for 60 s in freshly prepared 2-molar NaOH solution. Subsequently immersed in water and washed under running distilled water, dried with a paper towel and weighed.
1.9290 g adsorption material (HKUST-1, Basolite®-C300, BASF) was made up to 6.9213 g with xylene (isomer mixture, technical). Subsequently, the suspension was treated for 5 min. in the ultrasound bath. Shortly before the processing, with constant agitation, 0.9492 g of a phenylmethylsilicone resin solution (55% by weight in xylene) (Silikophen® P50/300, Evonik Industries) was added to the suspension. Between 0.8 and 1.5 ml of the dispersion was applied on the sample sheets with a Pasteur pipette.
The coated sheets were heated on a heating plate to 55° C. and hence dried. Subsequently, all the samples were heated for the duration of 5 h to 200° C.
The addition of a substrate network additive, for example 0.032 g Tego® Twin 4100, can improve the homogeneity of the layer.
Coating of an aluminum sheet with a solvent-containing dispersion of an adsorption material and a polyorganosiloxane as binder
The aluminum sheets (alloy AlMg3) were pretreated in a mechanical-abrasive manner, washed with distilled H2O and isopropanol and dried. Subsequently, the sheets were etched for 60 s in sodium hydroxide solution (150 g NaOH/1) at 65° C. Thereafter immersed in water and washed under running distilled water, dried with a paper towel and weighed.
1.9699 g adsorption material (activated carbon, CarboTech A35/1) was made up to 6.9528 g with xylene (isomer mixture, technical). Subsequently, the solid material dispersion was treated for 5 min. in the ultrasound bath. Shortly before processing, with agitation, 0.6457 g of a phenylmethylsilicone resin solution (55% by weight in xylene) (Silikophen P50/300, Evonik) was added to the dispersion. 0.8-1.5 ml of the dispersion was applied on the sample sheets with a Pasteur pipette.
The coated sheets were heated on a heating plate to 60° C. and consequently dried. Subsequently, all of the samples were heated once again at 250° C. on the heating plate for 45 min.
Variant:
Instead of xylene as solvent, also methanol can be used. For this purpose, 1.9778 g adsorption material (activated carbon, CarboTech A35/1) was made up to 6.6042 g with methanol. Subsequently, the solid material dispersion was treated for 5 min. in the ultrasound bath. Shortly before processing, with agitation, 0.6434 g of a phenylmethylsilicone resin solution (55% by weight in xylene) (Silikophen P50/300, Evonik) was added to the dispersion.
If water is taken as the basis for the dispersion and if the phenylmethylsilicone resin dissolved in xylene is replaced with an aqueous system (for example SILRES® MP50, Wacker), the dispersion agglomerates immediately after addition of the silicone resin. Processing by application is no longer possible here.
Coating of an aluminum sheet with a xylene-containing dispersion of a zeolite-like hydrophilic adsorption material and a polyorganosiloxane as binder
The aluminum sheets (AlMg3 alloy) were pretreated in advance in a mechanical-abrasive manner and washed with distilled H2O. Thereafter washed with isopropanol and dried. Subsequently, the sheets were etched for 60 s in NaOH (150 g/l) at 65°, immersed in water and washed under running distilled water, dried with a paper towel and weighed.
1.9699 g of a strongly hydrophilic adsorption material (Y-zeolite, CBV100, Zeolyst) was made up to 10.194 g with xylene (technical). Subsequently, the solid material dispersion was treated for 5 min in the ultrasound bath. Shortly before processing, 0.4288 g of a phenylmethylsilicone resin solution (55% by weight in xylene) (Silikophen® P50/300, Evonik Industries) was added to the dispersion and agitated once again with the magnetic agitator. 1.5 ml of the dispersion was applied on the sample sheets with a glass pipette.
The coated sheets were heated on a heating plate to 60° C. and dried. Subsequently, all of the samples were heated once again at 250° C. on the heating plate for 45 min.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2012 014 335 | Jul 2012 | DE | national |
This patent application is the divisional of co-pending U.S. patent application Ser. No. 14/413,190, filed Jan. 6, 2015, now abandoned which is the U.S. national phase of International Application No. PCT/EP2013/065123, filed on Jul. 17, 2013, which claims the benefit of German Patent Application No. 10 2012 014 335.4, filed Jul. 19, 2012, the disclosures of which are incorporated by reference in their entireties for all purposes.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3031366 | Bueche et al. | Apr 1962 | A |
| 5599445 | Betz et al. | Feb 1997 | A |
| 6508860 | Kulkarni et al. | Jan 2003 | B1 |
| 7820592 | Cattaneo et al. | Oct 2010 | B2 |
| 20030089228 | Kulprathipanja et al. | May 2003 | A1 |
| 20030175533 | McGarry | Sep 2003 | A1 |
| 20050045031 | Rajagopalan | Mar 2005 | A1 |
| 20050272601 | Cattaneo et al. | Dec 2005 | A1 |
| 20060189775 | Takahashi | Aug 2006 | A1 |
| 20080093059 | Nishida | Apr 2008 | A1 |
| 20080128941 | Lopez | Jun 2008 | A1 |
| 20080308262 | Sauer et al. | Dec 2008 | A1 |
| 20090075060 | Miller | Mar 2009 | A1 |
| 20090092776 | Betz et al. | Apr 2009 | A1 |
| 20090155464 | Liu et al. | Jun 2009 | A1 |
| 20100132559 | Ishida et al. | Mar 2010 | A1 |
| 20100140638 | Kotani | Jun 2010 | A1 |
| 20110183835 | Sauer et al. | Jul 2011 | A1 |
| 20110232493 | Yeganeh | Sep 2011 | A1 |
| 20110319673 | Dunne | Dec 2011 | A1 |
| 20130068101 | Knapp et al. | Mar 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 1751085 | Mar 2006 | CN |
| 101079489 | Nov 2007 | CN |
| 101107494 | Jan 2008 | CN |
| 102005003543 | Aug 2006 | DE |
| 102008050926 | Apr 2010 | DE |
| 102011011688 | Aug 2012 | DE |
| 03244996 | Nov 1991 | JP |
| 2001-321425 | Nov 2001 | JP |
| 2004-148274 | May 2004 | JP |
| 2009-091208 | Apr 2009 | JP |
| 1020090039179 | Apr 2009 | KR |
| Entry |
|---|
| English language translation JP 03/244996 Nov. 1991 (Year: 1991). |
| English language translation KR 1020090039179 Apr. 2009 (Year: 2009). |
| Basu et al., “Solvent resistant nanofiltration (SRNF) membranes based on metal-organic frameworks,” J. Membr. Sci 344(1): 190-198 (2009). |
| Takamizawa et al., “Alcohol-Vapor Inclusion in Single-Crystal Adsorbents [MII2(bza)4(pyz)]n (M=Rh, Cu): Structural Study and Application to Separation Membranes,” Chem. Asian J. 2(7): 837-848 (2007). |
| German Patent Office, Office Action in German Patent Application No. 10 2012 014 335.4 (dated Mar. 11, 2013). |
| European Patent Office, International Search Report in International Application No. PCT/EP2013/065123 (dated Sep. 20, 2013). |
| European Patent Office, Written Opinion in International Application No. PCT/EP2013/065123 (dated Sep. 20, 2013). |
| European Patent Office, International Preliminary Report on Patentability in International Application No. PCT/EP2013/065123 (dated Jan. 29, 2015). |
| State Intellectual Property Office of the People's Republic of China, Notification of First Office Action in Chinese Patent Application No. 201380038159.6 (dated Dec. 9, 2015). |
| State Intellectual Property Office of the People's Republic of China, Second Office Action in Chinese Patent Application No. 201380038159.6 (dated Jul. 5, 2016). |
| State Intellectual Property Office of the People's Republic of China, Third Office Action in Chinese Patent Application No. 201380038159.6 (dated Mar. 22, 2017). |
| Korean Intellectual Property Office, Notification of Reason for Refusal in Korean Patent Application No. 10-2015-7001240 (dated Sep. 11, 2019). |
| Number | Date | Country | |
|---|---|---|---|
| 20180118974 A1 | May 2018 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14413190 | US | |
| Child | 15855885 | US |