Display Panel Structure and Manufacture Method Thereof

Abstract

A display panel structure having a circuit element disposed thereon and method of manufacture are provided. The display panel includes a substrate and the circuit element disposed on the substrate. The circuit element has a first interface layer and a first conductive layer. Both the first interface layer and the first conductive layer have copper materials. The material which makes the first interface layer includes a reactant or a compound of the material which makes the first conductive layer. The method for manufacturing includes the following steps: forming a first interface layer on the substrate; forming a first conductive layer on the first interface layer; and etching the first conductive and interface layers to form a pattern. The existence of the first interface reduces the penetration of the first conductive layer on the substrate and improves the adhesive force between the first conductive layer and the substrate.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a conventional display panel and a thin-film-transistor (TFT).

FIG. 2 illustrates an embodiment of a display panel in the present invention.

FIG. 3 a illustrates an embodiment of the present invention applied in a-Si TFT.

FIG. 3 b shows another embodiment of the present invention applied in a-Si TFT.

FIG. 4 a is a view of an embodiment of the top gate design applied in a-Si TFT.

FIG. 4 b is a view of another embodiment of the top gate design applied in a-Si TFT.

FIG. 4 c illustrates of another embodiment applied in a-Si TFT.

FIG. 5 shows a flowchart of an embodiment used in a manufacture method of the display panel in the present invention.

FIG. 6 shows a flowchart of another embodiment used in a manufacture method of the display panel in the present invention.

FIG. 7 illustrates a device applied in the manufacture method of the display panel in the present invention.

FIG. 8 illustrates another embodiment of a-Si TFT made of the bottom gate design in the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

A structure and manufacture method of display panel is disclosed in the present invention. In the preferred embodiment, the structure of the display panel presented here is a liquid crystal display (LCD) panel. However, in a different embodiment, the structure of the display panel is an organic light emitting diode (OLED) LCD panel or other display device.

FIG. 2 illustrates an embodiment of the present invention showing a display panel structure. In the embodiment, the display panel structure includes a substrate 100 and a circuit element 300. The substrate 100 is a substrate preferably made of glass. In a different embodiment, the substrate 100 is a substrate made of polymer, such as plastic substrate. Besides, the circuit element 300 includes transistor, such as a-Si thin-film-transistor (a-Si TFT) or p-Si TFT. In a different embodiment, the circuit element 300 is a metal-insulator-metal thin-film-diode (MIM-TFD).

The circuit element 300 includes a first interface layer 310 and a first conductive layer 330. As shown in FIG. 2, the first interface layer 310 is directly formed over the internal surface 110 of the substrate 100. In a different embodiment, the first interface layer 310 is formed over a metal layer or a nonmetal layer of the internal surface of the substrate 100. Besides, in the preferred embodiment, the first interface layer 310 is formed over the substrate 100 by physical vapor deposition (PVD), such as sputtering process. In a different embodiment, the first interface layer 310 is formed over the substrate 100 by chemical vapor deposition (CVD) or other methods.

In the preferred embodiment, the first interface layer 310 is about 1 nm to 100 nm thick. In a different embodiment, the first interface layer 310 is about 3 nm to 50 nm thick. The materials of the first interface layer 310 include copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy oxygen-nitrogen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture and/or copper alloy nitrogen-oxygen mixture. The first interface layer 310 is made of the combination of the materials described above. Besides, the material of the copper alloy includes magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium and/or iron. In the preferred embodiment, the percentage of copper included in copper alloy is more than 50 mol %. In a different embodiment, the percentage of copper included in copper alloy is more than 90 mol %. The first interface layer 310 is electrically conducted or electrically insulated according to different materials and the percentages of the copper.

As shown in FIG. 2, the first conductive layer 330 is directly formed over the first interface layer 310. The first interface layer 310 and the conductive layer 330 are together formed an etching pattern. In the preferred embodiment, the first conductive layer 330 is formed over the interface layer 310 by physical vapor deposition (PVD), such as sputtering process. In a different embodiment, the first conductive layer 330 is formed over the first interface layer 310 by chemical vapor deposition (CVD) or other method.

In the preferred embodiment, the material of first conductive layer 330 is copper or copper alloy. The material of the first conductive layer 330 at least comprises reactant or compound formed the first interface layer 310. In other words, the material formed the first interface layer 310 is formed by reacting or compounding the materials of first conductive layer 330 with other elements. For example, when the first conductive layer 330 is formed by copper, the first interface layer 310 is made of reacting or compounding copper with oxygen ion, nitrogen ion or mixture of oxygen ion and/or nitrogen ion. Because the materials of the first interface layer 310 and the first conductive layer 330 have common compositions, the etching step can etch the first interface layer 310 and the first conductive layer 330 at the same time. Besides, in the preferred embodiment, the copper alloy is composed of copper and the metal includes magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium and/or iron. In the preferred embodiment, the percentage of the copper included in the copper alloy is more than 50 mol %. In a different embodiment, the percentage of the copper included in the copper alloy is more than 90 mol %.

As the embodiment shown in FIG. 3a, the circuit element 300 is a-Si TFT and used in a bottom gate electrode design. In this embodiment, the etching pattern formed together by the first interface layer 310 and the first conductive layer 330 is used to be the gate electrode of the circuit element 300. The circuit element 300 further comprises an isolated layer 340, a semiconductor layer 350, an ohm contacted layer 360, a source electrode 370 and a drain electrode 380. The isolated layer 340 covers the gate electrode by forming the first conductive layer 330 and the first interface layer 310 and covers the internal surface 110 of the substrate 100 exposed at the two ends of the first interface layer 310. In the preferred embodiment, the isolated layer 340 is made of oxygen silicon compound or nitrogen silicon compound.

The semiconductor layer 350 covers the isolated layer 340. After the etching process, the etching pattern of the semiconductor layer 350 is opposite to the gate electrode formed by the first conductive layer 330 and the first interface layer 310. In this preferred embodiment, the semiconductor layer 350 is a-Si layer. The ohm contacted layer 360 includes a source ohm contacted layer 361 and a drain ohm contacted layer 363. The source ohm contacted layer 361 and the drain ohm contacted layer 363 are respectively connected to two ends of the semiconductor layer 350. In other words, the source ohm contacted layer 361 and the drain ohm contacted layer 363 are respectively opposite to two ends of the gate electrode formed by the first conductive layer 330 and the first interface layer 310. In the preferred embodiment, the ohm contacted layer 360 is n+a-Si layer. The source electrode 370 covers the source ohm contacted layer 361. The drain electrode 380 covers the drain ohm contacted layer 363. The source electrode 370 and the drain electrode 380 are metal layers deposited after etching.

Because of disposing the first interface layer 310, the problem of the first conductive layer 330 diffusing into the substrate 100 can be improved when the first conductive layer 330 is formed over the substrate 100. Besides, the existence of the first interface layer 310 can enhance the strength of the adhesive force between the first conductive layer 330 and the substrate 100. The problem of the first conductive layer 330 peeling off from the substrate 100 can be improved.

FIG. 3 b is another embodiment of a-Si TFT made of the bottom gate design. In this embodiment, the source electrode 370 and the drain electrode 380 respectively include a second interface layer 410 and a second conductive layer 430. The second interface layer 410 is in the bottom of the source electrode 370 and the drain electrode 380 and formed over the ohm contacted layer 360. The material of the second interface layer 410 includes copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy nitrogen solid solution, copper alloy nitrogen-oxygen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture and/or copper alloy nitrogen-oxygen mixture. Besides, in the preferred embodiment, the copper alloy is composed of copper and the metal includes magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium and/or iron. In the preferred embodiment, the percentage of copper included in copper alloy is more than 50 mol %. In a different embodiment, the percentage of copper included in copper alloy is more than 90 mol %. The second interface layer 410 is electrically conducted or electrically insulated according to different materials and the percentages of the copper. The limitation of the thickness of the second interface layer 410 is close to the thickness of the first interface layer 310.

The second conductive layer 430 is directly formed over the second interface layer 410. The second interface layer 410 and the second conductive layer 430 are together formed an etching pattern. In the preferred embodiment, the second conductive layer 430 is formed over the second interface layer 410 by physical vapor deposition (PVD), such as sputtering process. In a different embodiment, the second conductive layer 430 is formed over the second interface layer 410 by chemical vapor deposition (CVD) or other method.

In the preferred embodiment, the material of the second conductive layer 430 is copper or copper alloy. The material of the second interface layer 410 at least comprises reactant or compound forms the second conductive layer 430. In other words, the material of the second interface layer 410 is formed by reacting or compounding the material of second conductive layer 430 with other elements. For example, as the second conductive layer 430 is made of copper, the second interface layer 410 is made of reacting or compounding copper with oxygen, nitrogen or mixture of oxygen and nitrogen. Because of the commonness of the materials of the second interface layer 410 and the second conductive layer 430, the etching step can etch the second interface layer 410 and the second conductive layer 430 at the same time. Besides, in the preferred embodiment, the material of the copper alloy is composed of copper and the metal includes magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium and/or iron. In the preferred embodiment, the percentage of copper included in copper alloy is more than 50 mol %. In a different embodiment, the percentage of copper included in copper alloy is more than 90 mol %.

FIG. 3 c is another embodiment of a-Si TFT made of the bottom gate design. In this embodiment, the third interface layer 450 is formed between the first conductive layer 330 and the isolated layer 340. The third interface layer 450 is directly formed over the first conductive layer 330. The method to form the third interface layer 450 is used by PVD, CVD and so on. The isolated layer 340 is directly formed over the third interface layer 450. The top end and the bottom end of the third interface layer 450 are respectively connected to the isolated layer 340 and the first conductive layer 330. Because of disposing the third interface layer 450, the adhesive force between the first conductive layer 330 and the isolated layer 340 is increased.

The material of the third interface layer 450 includes copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy nitrogen solid solution, copper alloy nitrogen-oxygen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture and/or copper alloy nitrogen-oxygen mixture. It should be noted that the material of the third interface layer 450 at least comprises reactant or compound formed the first conductive layer 330. In other words, the material of the third interface layer 450 is formed by reacting or compounding the material of the first conductive layer 330 with other elements.

FIG. 4 a is another embodiment of the present invention. The a-Si TFT is made of the top gate electrode design. As shown in FIG. 4a, the first interface layer 310 and the first conductive layer 330 are directly formed over the internal surface 110 of the substrate 100 to be the source electrode 370 and the drain electrode 380. After the etching process, there is a gap formed between the source electrode 370 and the drain electrode 380. The ohm contacted layer 360 includes a source ohm contacted layer 361 and a drain ohm contacted layer 363 and partially covers the source electrode 370 and the drain electrode 380. In the preferred embodiment, the ohm contacted layer is n+a-Si layer. The semiconductor layer 350 covers the source ohm contacted layer 361 and the drain ohm contacted layer 363. Furthermore, the semiconductor layer 350 covers the internal surface 110 of the substrate 100 exposed between the source ohm contacted layer 370 and the drain ohm contacted layer 380. In this preferred embodiment, the semiconductor layer 350 is a-Si layer and the isolated layer 340 covers the semiconductor layer 350. The isolated layer 340 is formed by oxygen silicon compound or nitrogen silicon compound. The gate electrode 390 is directly formed over the isolated layer 340 and is a deposited metal layer formed after etching.

FIG. 4 b is another embodiment of a-Si TFT made of the top gate design. In this embodiment, the gate electrode 390 includes the second interface layer 410 and the second conductive layer 430. The second interface layer 410 is formed over the isolated layer 340. The material of the second interface layer 410 includes copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy nitrogen solid solution, copper alloy nitrogen-oxygen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture and/or copper alloy nitrogen-oxygen mixture. The second conductive layer 430 is directly formed over the second interface layer 410. The material of the second conductive layer 430 is copper or copper alloy.

In another embodiment, as shown in FIG. 4c, a semiconductor layer 350 is formed between the substrate 100 and the first interface layer 310. The semiconductor layer 350 is formed over the substrate 100. The semiconductor layer 350 is a-Si layer. The source ohm contacted layer 361 and the drain ohm contacted layer 363 are formed over the semiconductor layer 350. The source ohm contacted layer 361 is disposed between the semiconductor layer 350 and the source electrode 370. The drain ohm contacted layer 363 is disposed between the semiconductor layer 350 and the drain electrode 380. In the preferred embodiment, the source ohm contacted layer 361 and the drain ohm contacted layer 363 are n+a-Si layer. The isolated layer 340 partially covers the first conductive layer 330. In other words, the isolated layer 340 partially covers the top surface of the source electrode 370 and the drain electrode 380. The gate electrode 390 is formed over the isolated layer 340 and disposed between the source electrode 370 and the drain electrode 380.

FIG. 5 is a flow chart showing the method for manufacturing the display panel structure and the circuit element. As shown in FIG. 5, the step 501 is to form a first interface layer 310 on the substrate 100. In this step, the PVD method, such as sputtering process, is used to form the first interface layer 310 on the substrate 100. In a different embodiment, the first interface layer 310 is formed by using CVD method or other methods. Besides, the first interface layer 310 is maintained within a thickness of 1 nm to 100 nm in step 501. In a different embodiment, the first interface 310 is further maintained within a thickness of 3 nm to 50 nm.

The material of the first interface layer 310 includes copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy oxygen-nitrogen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture and/or copper alloy nitrogen-oxygen mixture. Besides, in the preferred embodiment, the copper alloy is composed of copper and the metal includes magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium and/or iron. The percentage of copper included in copper alloy is more than 50 mol %. In the specific embodiment, the percentage of copper included in copper alloy is more than 90 mol %.

The step 503 is to form a first conductive layer 330 on the first interface layer 310. In this step, the PVD method, such as sputtering process, is used to form the first conductive layer 330 on the first interface layer 310. In a different embodiment, the first conductive layer 330 is formed over the first interface layer 310 by the CVD method or other method. Besides, the process method used in step 503 is the same as the method used in the step 501 to simplify the process procedure.

The material of the first conductive layer 330 is copper or copper alloy. The material formed the first interface layer 310 at least includes reactant or compound forming the material of the first conductive layer 330. In other words, the material formed the first interface layer 310 is made of reacting or compounding the material of the first conductive layer 330 with other elements. For example, when the first conductive layer 330 is made of copper, the first interface layer 310 is made of reacting or compounding copper with oxygen, nitrogen ion or mixture of oxygen and nitrogen Besides, in the preferred embodiment, the copper alloy described above is composed of copper and the metal includes magnesium, chromium, titanium calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium and/or iron. The percentage of copper included in copper alloy is more than 50 mol %. In the specific embodiment, the percentage of copper included in copper alloy is more than 90 mol %.

Step 505 is to etch the first conductive layer 330 and the first interface layer 310 to form the etching pattern. Because the material of the first interface layer 310 includes reactant or compound formed the first conductive layer 330, step 505 is to etch the first interface layer 310 and the conductive layer 330 at the same time.

FIG. 6 is a flowchart of another embodiment of the manufacture method in the present invention. In this embodiment, the step 501 is to form the first interface layer 310, which includes several steps: step 5011 is to stimulate the substrate material to produce the extricated substrate material in the chamber. The substrate material is made of copper or copper alloy. In the preferred embodiment, the copper alloy includes copper, magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium and/or iron. The percentage of copper included in copper alloy is more than 50 mol %. In the specific embodiment, the percentage of copper included in copper alloy is more than 90 mol %.

In the sputtering process, as shown in FIG. 7, the ions with high energy are used to hit the substrate material 710 to generate the extricated material. The argon is inputted in the chamber and is ionized to generate high energy ions in the embodiment shown in FIG. 7. In order to successfully proceed with the reaction, the mechanism bumper 751 and the diffused bumper 753 are used in the chamber 700 to generate a vacuum status. However, in the different embodiment, the thermal energy or electrical energy is used in the step 5011 to stimulate the substrate material to produce ion substrate material when the CVD method process or the plasma enhanced CVD method process is used.

Step 5013 is to input and stimulate the reactive gas to generate the extricated gas in the chamber 700. In the preferred embodiment, the reactive gas is nitrogen, oxygen or nitrogen-oxygen mixture. The sputtering process method shown in FIG. 7, the reactive gas inputted in the chamber is the mixture of nitrogen and oxygen gas. The reactive gas is stimulated to be extricated gas ion in the chamber 700 by the voltage inputted by the voltage generator 730. In the preferred embodiment, when the oxygen is used to be the reactive gas, the oxygen input pressure is about 1.3 mTorr. When the nitrogen is used to be the reactive gas, the nitrogen input pressure is about 3 mTorr.

Step 5015 is to attract the composition of the extricated substrate material and the extricated gas to be deposited onto the substrate 100 and form the first interface layer 310. In the preferred embodiment, the composition described above includes solid solution or compound formed by the extricated substrate material and the extricated gas, such as copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy nitrogen solid solution, copper alloy nitrogen-oxygen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture and/or copper alloy nitrogen-oxygen mixture. In the embodiment shown in FIG. 7, because the substrate 100 is disposed in the anodic position of the electric field of the chamber, the composition of the extricated substrate material and the extricated gas is attracted by the electric field to be deposited onto the substrate 100 and form the first interface layer 310.

In the embodiment shown in FIG. 6, the step to form the first conductive layer 330 includes two steps. The step 5031 is to stop inputting the reactive gas into the chamber 700. In the preferred embodiment, the step 5031 is used in the moment when the requested thickness of the deposition of the first interface layer 310 is achieved. The step 5033 is to attract the composition of the extricated substrate material to be deposited onto the first interface layer 310 and form the first conductive layer 330. In the step 5033, the extricated substrate material stimulated in the chamber 700 cannot react or compound with the reactive gas because the reactive gas is stopped inputting into the chamber 700. Therefore, the extricated substrate material will only be attracted to the electric field to be deposited onto the substrate 100 and form the first conductive layer 330.

Besides, when the adhesive force between the first conductive layer 330 and any other upper layers is needed to enhance, a sub interface layer is formed over the first conductive layer 330. For example, in the embodiment shown in FIG. 6, when the requested thickness of the first conductive layer 330 is formed in the step 5033, the reactive gas is inputted again to stimulate in the chamber 700. At this time, the reactive gas stimulated in the chamber 700 is reacting or compounding with the extricated substrate material. The composition of the extricated substrate material and the reactive gas is attracted to be deposited onto the first conductive layer 330 to form the sub interface layer.

As known in the flowchart of the embodiment of FIG. 6, only one substrate material 710 is used in the chamber 700 to form the first interface layer 310 or form the first conductive layer 330. Therefore, the complication of the manufacture process and the processed time can be improved because only one substrate material 710 is used to form the first interface layer 310 and the first conductive layer 330. Besides, when the oxygen input pressure is about 1.3 mTorr or the nitrogen input pressure is about 3 mTorr, the adhesive force between the first conductive layer 330 and the substrate 100 is about 220 Newton force.

FIG. 8 is another embodiment of a-Si TFT made of the bottom gate design. In this embodiment, the etching pattern formed by the first conductive layer 330 is used to be the gate electrode of the circuit element 300. The source electrode 370 and the drain electrode 380 respectively include a second interface layer 410 and a second conductive layer 430. The second interface layer 410 is in the bottom of the source electrode 370 and the drain electrode 380 and formed over the ohm contacted layer 360. The material of the second interface layer 410 includes copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy nitrogen solid solution, copper alloy nitrogen-oxygen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture and/or copper alloy nitrogen-oxygen mixture. Besides, in the preferred embodiment, the copper alloy is composed of copper and the metal includes magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium and/or iron. In the preferred embodiment, the percentage of copper included in copper alloy is more than 50 mol %. In a different embodiment, the percentage of copper included in copper alloy is more than 90 mol %. The second interface layer 410 is electrically conducted or electrically insulated according to different materials and the percentages of the copper. The limitation of the thickness of the second interface layer 410 is close to the thickness of the first interface layer 310.

The second conductive layer 430 is directly formed over the second interface layer 410. The second interface layer 410 and the second conductive layer 430 are together formed an etching pattern. In the preferred embodiment, the second conductive layer 430 is formed over the second interface layer 410 by physical vapor deposition (PVD), such as sputtering process. In a different embodiment, the second conductive layer 430 is formed over the second interface layer 410 by chemical vapor deposition (CVD) or other method.

In the preferred embodiment, the material of the second conductive layer 430 is copper or copper alloy. The material of the second interface layer 410 at least comprises reactant or compound forms the second conductive layer 430. In other words, the material of the second interface layer 410 is formed by reacting or compounding the material of second conductive layer 430 with other elements. For example, as the second conductive layer 430 is made of copper, the second interface layer 410 is made of reacting or compounding copper with oxygen, nitrogen or mixture of oxygen and nitrogen. Because of the commonness of the materials of the second interface layer 410 and the second conductive layer 430, the etching step can etch the second interface layer 410 and the second conductive layer 430 at the same time. Besides, in the preferred embodiment, the material of the copper alloy is composed of copper and the metal includes magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium and/or iron. In the preferred embodiment, the percentage of copper included in copper alloy is more than 50 mol %. In a different embodiment, the percentage of copper included in copper alloy is more than 90 mol %.

Although the preferred embodiments of the present invention have been described herein, the above description is merely illustrative. Further modification of the invention herein disclosed will occur to those skilled in the respective arts and all such modifications are deemed to be within the scope of the invention as defined by the appended claims.

Claims

1. A display panel structure comprising: a substrate;a first interface layer disposed on the substrate, wherein the materials of the first interface layer comprise copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy nitrogen solid solution, copper alloy nitrogen-oxygen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture or copper alloy nitrogen-oxygen mixture; anda first conductive layer formed over the first interface layer and the materials of the first conductive layer including copper or copper alloy.

2. The display panel structure of claim 1, wherein the first interface layer and the first conductive layer together form a gate electrode.

3. The display panel structure of claim 2 further comprising: an isolated layer covering the gate electrode;a semiconductor layer covering the isolated layer and corresponding to the gate electrode;an ohm contacted layer including a source ohm contacted layer and a drain ohm contacted layer, and the source ohm contacted layer and the drain ohm contacted layer are respectively connected to two end1s of the semiconductor layer;a source electrode covering the source ohm contacted layer; anda drain electrode covering the drain ohm contacted layer.

4. The display panel structure of claim 3, wherein the source electrode and the drain electrode respectively include: a second interface layer formed over the ohm contacted layer and the materials of the second interface layer comprising copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy nitrogen solid solution, copper alloy nitrogen-oxygen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture or copper alloy nitrogen-oxygen mixture; anda second conductive layer formed over the second interface layer and the materials of the second conductive layer including copper or copper alloy.

5. The display panel structure of claim 3 further comprising a third interface layer, wherein the third interface layer is disposed between the first conductive layer and the isolated layer and connected to the first conductive layer and the isolated layer; the materials of the third interface layer include copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy nitrogen solid solution, copper alloy nitrogen-oxygen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture or copper alloy nitrogen-oxygen mixture.

6. The display panel structure of claim 3, wherein the first interface layer and the first conductive layer together form a source electrode and a drain electrode.

7. The display panel structure of claim 6 further comprising: a source ohm contacted layer partially covering the source electrode;a drain ohm contacted layer partially covering the drain electrode;a semiconductor layer covering the source ohm contacted layer and the drain ohm contacted layer;an isolated layer covering the semiconductor layer; anda gate electrode formed over the isolated layer.

8. The display panel structure of claim 7, wherein the gate electrode comprises: a second interface layer formed over the isolated layer and the materials of the second interface layer including copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy nitrogen solid solution, copper alloy nitrogen-oxygen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture or copper alloy nitrogen-oxygen mixture; anda second conductive layer formed over the second interface layer and the materials of the second conductive layer including copper or copper alloy.

9. The display panel structure of claim 6 further comprising: a semiconductor layer formed over the substrate and disposed between the substrate and the first interface layer;a source ohm contacted layer formed over the semiconductor layer and disposed between the semiconductor layer and the source electrode;a drain ohm contacted layer formed the semiconductor layer and disposed between the semiconductor layer and the drain electrode;an isolated layer partially formed over the first conductive layer; anda gate electrode formed over the isolated layer.

10. The display panel structure of claim 1, wherein the first interface layer is electric conductive.

11. The display panel structure of claim 1, wherein the first interface layer is an isolated layer.

12. The display panel structure of claim 1, wherein the substrate includes a glass substrate or a polymer substrate.

13. The display panel structure of claim 1, wherein the first interface layer is about 1 nm to 100 nm thick.

14. The display panel structure of claim 13, wherein the first interface layer is about 3 nm to 50 nm thick.

15. The display panel structure of claim 1, wherein the materials of the copper alloy comprise copper, magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium or iron.

16. The display panel structure of claim 1, wherein the percentage of copper included in the copper alloy is more than 50 molar ratios.

17. The display panel structure of claim 16, wherein the percentage of copper included in the copper alloy is more than 90 molar ratios.

18. The display panel structure of claim 1, wherein the display panel structure further comprises a semiconductor layer disposed between the substrate and the first interface layer, and the substrate and the semiconductor layer are together formed a gate electrode and the first interface layer and the first conductive layer are together formed a source electrode and a drain electrode.

19. A method for manufacturing a display panel structure comprising: forming an interface layer on a substrate, wherein the materials of the interface layer include copper oxygen solid solution, copper nitrogen solid solution, copper nitrogen-oxygen solid solution, copper alloy oxygen solid solution, copper alloy nitrogen solid solution, copper alloy nitrogen-oxygen solid solution, copper oxygen compound, copper alloy oxygen compound, copper nitrogen compound, copper alloy nitrogen compound, copper nitrogen-oxygen mixture or copper alloy nitrogen-oxygen mixture;forming a conductive layer on the interface layer, wherein the materials of the conductive layer include copper or copper alloy, and the materials of the interface layer include one of reactant or compound of the conductive layer; andetching the conductive layer and the interface layer to form an etching pattern.

20. The method of claim 19, wherein the interface layer forming step further comprises: stimulating a substrate material in a chamber to generate an extricated material with copper or copper alloy;inputting and stimulating a reactive gas in the chamber to generate an extricated gas, wherein the reactive gas includes nitrogen, oxygen and nitrogen-oxygen mixture; andattracting a composition of the extricated material and the extricated gas to deposit on the substrate and form the interface layer; wherein the composition includes a solid solution or a compound formed by the extricated material and the extricated gas.

21. The method of claim 20, wherein the oxygen input pressure is more than 1.3 mTorr in the step of stimulating the reactive gas.

22. The method of claim 20, wherein the nitrogen input pressure is more than 3 mTorr in the step of stimulating the reactive gas.

23. The method of the display panel structure of claim 19, wherein the interface layer forming step further comprises using a physical vapor deposition (PVD) or a chemical vapor deposition (CVD) to form the interface layer on the substrate.

24. The method of the display panel structure of claim 19, wherein the conductive layer forming step further comprises using a PVD or CVD to form the conductive layer on the substrate.

25. The method of the display panel structure of claim 19, wherein the interface layer forming step further comprises controlling the interface layer with 1 nm to 100 nm thick.

26. The method of the display panel structure of claim 25, wherein the interface layer forming step further comprises controlling the interface layer with 3 nm to 50 nm thick.

27. The method of the display panel structure of claim 19, wherein the materials of the copper alloy comprises copper, magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium or iron.

28. The method of the display panel structure of claim 20, wherein the substrate material comprises copper, magnesium, chromium, titanium, calcium, niobium, manganese, tantalum, nickel, vanadium, hafnium, boron, aluminum, gallium, germanium, tin, molybdenum, tungsten, palladium, zinc, indium, silver, cobalt, iridium or iron.