The present invention relates to display technology, more particularly, to a display substrate, a display apparatus, and a method of fabricating a display substrate.
A liquid crystal display apparatus includes an array substrate and a color filter substrate assembled together, and a liquid crystal layer between the array substrate and the color filter substrate. The liquid crystal layer includes liquid crystal molecules. A liquid crystal display device produces an image by applying an electric field to a liquid crystal layer between the array substrate and the color filter substrate. In response to the electric field applied to the liquid crystal layer, the liquid crystal molecules in the liquid crystal layer rotate. Thus, the electric field changes an alignment direction of the liquid crystal molecules in the liquid crystal layer. Light transmittance of the liquid crystal layer is adjusted when the alignment direction of the liquid crystal molecules changes.
In one aspect, the present invention provides a display substrate comprising a base substrate; a color filter on the base substrate; and an overcoat layer on a side of the color filter distal to the base substrate; wherein the overcoat layer comprises a first sublayer and a second sublayer, the second sublayer on a side of the first sublayer distal to the base substrate; the first sublayer comprises a first polymer material; and the second sublayer comprises a second polymer material different from the first polymer material.
Optionally, the display substrate further comprises an alignment film on a side of the second sublayer distal to the first sublayer.
Optionally, the first polymer material comprises an acrylic polymer; and the second sublayer comprises a polyimide.
Optionally, the overcoat layer further comprises a third sublayer between the first sublayer and the second sublayer, and the third sublayer comprises a third polymer material different from the first polymer material and the second polymer material.
Optionally, the third polymer material comprises a co-polymer of the first polymer material and the second polymer material.
Optionally, the third polymer material comprises a poly-(acrylic-imide) co-polymer.
Optionally, the poly-(acrylic-imide) co-polymer comprises
Optionally, the display substrate further comprises a spacer layer on a side of the second sublayer distal to the base substrate.
Optionally, the first sublayer has a thickness in a range of approximately 0.6 μm to approximately 1.5 μm; the second sublayer has a thickness in a range of approximately 0.6 μm to approximately 1.5 μm; and the overcoat layer has a thickness in a range of approximately 1.2 μm to approximately 3.0 μm.
In another aspect, the present invention provides a display apparatus comprising the display substrate described herein or fabricated by a method described herein.
In another aspect, the present invention provides a method of fabricating a display substrate comprising forming a color filter on a base substrate; and forming an overcoat layer on a side of the color filter distal to the base substrate; wherein forming the overcoat layer comprises forming a first sublayer and forming a second sublayer subsequent to forming the first sublayer, the second sublayer formed on a side of the first sublayer distal to the base substrate; the first sublayer is formed to comprise a first polymer material; and the second sublayer is formed to comprise a second polymer material different from the first polymer material.
Optionally, subsequent to forming the second sublayer, further comprising forming an alignment film on a side of the second sublayer distal to the first sublayer.
Optionally, forming the overcoat layer comprises forming a first polymer material layer comprising a first polymer material on a side of the color filter distal to the base substrate; drying the first polymer material layer, forming a second polymer material layer comprising a second polymer material on a side of the first polymer material layer distal to the base substrate; drying the second polymer material layer; and curing the first polymer material layer and the second polymer material layer thereby forming the first sublayer and the second sublayer.
Optionally, curing the first polymer material layer and the second polymer material layer comprises pre-curing the first polymer material layer and the second polymer material layer at a temperature in a range of approximately 50 degrees to approximately 80 degrees for a duration in a range of approximately 50 seconds to approximately 150 seconds; and subsequent to pre-curing the first polymer material layer and the second polymer material layer, curing the first polymer material layer and the second polymer material layer at a temperature in a range of approximately 200 degrees to approximately 250 degrees for a duration in a range of approximately 15 minutes to approximately 30 minutes.
Optionally, the first polymer material layer comprises an acrylic polymer and the second polymer material layer comprises a polyimide.
Optionally, the first polymer material layer further comprises an epoxy resin and the second polymer material layer further comprises an epoxy resin.
Optionally, forming the overcoat layer further comprises forming a third sublayer between the first sublayer and the second sublayer; and the third sublayer is formed to comprise a third polymer material different from the first polymer material and the second polymer material.
Optionally, forming the third sublayer comprises co-polymerizing the first polymer material and the second polymer material at an interface between the first polymer material layer and the second polymer material layer during curing the overcoat layer; and the third polymer material comprises a co-polymer of the first polymer material and the second polymer material.
Optionally, the third polymer material comprises a poly-(acrylic-imide) co-polymer.
Optionally, the poly-(acrylic-imide) co-polymer comprises
Optionally, curing the first polymer material layer is performed using one or a combination of an epoxy curing agent, a silane coupling agent, and a surfactant; and curing the second polymer material layer is performed using one or a combination of an epoxy curing agent, a silane coupling agent, and a surfactant.
The following drawings are merely examples for illustrative purposes according to various disclosed embodiments and are not intended to limit the scope of the present invention.
The disclosure will now be described more specifically with reference to the following embodiments. It is to be noted that the following descriptions of some embodiments are presented herein for purpose of illustration and description only. It is not intended to be exhaustive or to be limited to the precise form disclosed.
In a process of fabricating a conventional display substrate (e.g., a color filter substrate), a black matrix and a color filter is formed on a base substrate, an overcoat layer is formed on a side of the color filter distal to the base substrate, a spacer layer and an alignment film is then formed on a side of the overcoat layer distal to the base substrate. Typically, the alignment film is made of polyimide. The step of forming the alignment film typically includes coating the polyimide dissolved in an organic solvent such as 1-Methyl-2-pyrrolidone. The organic solvent in the alignment film may permeate through the overcoat layer and dissolve the pigments contained in the color filter. The dissolved pigments then permeate out of the overcoat layer. When the display substrate is assembled with an array substrate in a cell, the permeated pigments will contaminate the liquid crystal molecule layer in the assembled display apparatus, resulting in spackle defects in the display apparatus. The contamination process becomes more severe in the subsequent fabricating processes, some of which are performed at an elevated temperature.
Accordingly, the present disclosure provides, inter alia, a display substrate, a display apparatus, and a fabricating method thereof that substantially obviate one or more of the problems due to limitations and disadvantages of the related art. In one aspect, the present disclosure provides a display substrate. In some embodiments, the display substrate includes a base substrate; a color filter on the base substrate; and an overcoat layer on a side of the color filter distal to the base substrate. Optionally, the overcoat layer includes a first sublayer and a second sublayer, the second sublayer on a side of the first sublayer distal to the base substrate. Optionally, the first sublayer comprises a first polymer material; and the second sublayer comprises a second polymer material different from the first polymer material.
The overcoat layer 3 is on a side of the color filter 2 distal to the base substrate 1. In some embodiments, the overcoat layer 3 includes a first sublayer 31 and a second sublayer 32, the second sublayer 32 on a side of the first sublayer 21 distal to the base substrate 1.
In some embodiments, the display substrate further includes an alignment film 5 on a side of the second sublayer 32 distal to the first sublayer 31. In a liquid crystal display apparatus assembled using the display substrate, the alignment film 5 is used to pre-align the liquid crystal molecules in the liquid crystal display apparatus. For example, a plurality of microgrooves may be formed in the alignment film 5 to induce the liquid crystal molecules in the liquid crystal display apparatus to align in a certain direction.
In some embodiments, the first sublayer 31 is in contact with the color filter 2, and the second sublayer 32 is in contact with the alignment film 5. Optionally, the first sublayer 31 is configured to prevent pigments in the color filter 2 from permeating out of the overcoat layer 3. Optionally, the second sublayer 32 is configured to achieve an enhanced adhesion between the overcoat layer 3 and the alignment film 5.
In the present display substrate, the overcoat layer 3 includes at least two sublayers, a first sublayer 31 and a second sublayer 32. The first sublayer 31 includes a first material capable of effectively preventing pigments in the color filter 2 from permeating out of the overcoat layer 3, thereby avoiding defects in the liquid crystal display apparatus having the display substrate caused by leakage of the color filter pigments into the liquid crystal molecule layer in the liquid crystal display apparatus. The second sublayer 32 includes a second material having an enhanced adhesivity with the alignment film 5. By having the second sublayer 32, various layers including the first sublayer 31, the second sublayer 32, and the alignment film 5 can be adhered together tightly, achieving an enhanced hermeticity of the liquid crystal display apparatus, enhanced reliability under high-temperature and high-humidity environment, and enhance moist-resistance and oxygen-resistance.
In some embodiments, the first polymer material includes an acrylic polymer. Optionally, the first sublayer 31 further includes an epoxy resin. Optionally, the acrylic polymer is a polymer or copolymer of acrylic monomers such as acrylate, acrylic acid, and acrylic anhydride. Examples of the acrylic monomer for making the acrylic polymer include, but are not limited to, methylmethacrylate, ethylmethacrylate, propylmethacrylate, butylmethacrylate, pentylmethacrylate, hexylmethacrylate, cyclohexylmethacrylate, heptylmethacrylate, octylmethacrylate, nonylmethacrylate, decylmethacrylate, laurylmethacrylate, dodecylmethacrylate, tetradecylmethacrylate, hexadecylmethacrylate, isobornylmethacrylate, adamantylmethacrylate, dicyclopentanylmethacrylate, dicyclopeutenylmethacrylate, benzylmethacrylate, 2-methoxyethylmethacrylate, 2-ethoxyethylmethacryate, acrylic acid, methacrylic acid, itaconic acid, maleic acid, maleic anhydride, maleic acid monoalkyl ester, monoalkyl itaconate, monoalkyl fumarate, glycidylacrylate, glycidyl methacrylate, 3,4-epoxybutylmethacrylate, 2,3-epoxycyclohexyl methacrylate, 3,4-epoxycyclohexyhnethylmethacrylate, 3-methyl oxetane-3-methylmethacrylate, and 3-ethyloxetane-3-methylmethacrylate. Optionally, the acrylic polymer may be a copolymer obtained by polymerization of the above-mentioned acrylic monomers with one or more monomers of styrene, α-methylstyrene, acetoxystyrene, N-methylmaleimide, N-ethylmaleimide, N-propylmaleimide, N-butylmaleimide, N-cyclohexylmaleimide, methacrylamide, and N-methyl methacrylamide. Polymerization of the acrylic monomers can be performed by, e.g., heat, irradiation, and cross-linking.
In some embodiments, the second polymer material includes a polyimide. Examples of polyimides include polyimides composed of acid anhydrides such as pyromellitic dianhydride, biphenyltetracarboxylic dianhydride or 2,2′-4,4′-di(dicarboxyphenyloxy)phenyl] propane dianhydride, and diamines such as oxydiamine, paraphenylenediamine, metaphenylenediamine or benzophenonediamine. Further examples of polyimides include pyromellitic dianhydride, oxydianiline, polymers of benzophenonetetracarboxylic dianhydride and oxydianiline and/or 1,3-phenylenediamine and the polymer of 3,3′-biphenylenetetracarboxylic acid and 1,4-phenyleuediamice, Kapton and Vespel resins sold by Du Pont, Matrimide 5218 sold by Ciba-Geigy, LaRC-TPI sold by Mitsui Toatsu or Upilex® sold by Ube Industries, Apical® sold by Allied Corporation, and PIQ-L100 sold by Hitachi Chemical Company. Polyimides have an enhanced adhesivity with the alignment film 5. Optionally, the second sublayer 32 further includes an epoxy resin. By including the epoxy resin in the second sublayer 32, the adhesion between the second sublayer 32 and the first sublayer 31, and between the second sublayer 32 and the alignment film 5, can be further enhanced.
Referring to
Optionally, at an interface between the first sublayer 31 and the second sublayer 32, the first polymer material (e.g., an acrylic polymer), the second polymer material (e.g., a polyimide), and optionally the epoxy resin, co-polymerize to form the third polymer material. By having the third sublayer 33, the adhesion between the first sublayer 31 and the second sublayer 32 can be further enhanced.
Optionally, the first sublayer 31 further includes one or a combination of an epoxy curing agent, a silane coupling agent, and a surfactant. Optionally, the second sublayer 32 further includes one or a combination of an epoxy curing agent, a silane coupling agent, and a surfactant.
In some embodiments, the first sublayer 31 has a thickness in a range such that permeation of pigments through the overcoat layer 3 can be effectively prevented and at the same time light transmittance and a total thickness of the display substrate is not significantly compromised. Optionally, the first sublayer 31 has a thickness in a range of approximately 0.6 μm to approximately 1.5 μm, e.g., approximately 0.8 μm to approximately 1.2 μm, approximately 0.9 μm to approximately 1.1 μm, and approximately 1.0 μm.
In some embodiments, the second sublayer 32 has a thickness in a range such that sufficient adhesion between the second sublayer 32 and the adjacent layers (e.g., the alignment film 5) can be achieved and at the same time light transmittance and a total thickness of the display substrate is not significantly compromised. Optionally, the second sublayer 32 has a thickness in a range of approximately 0.6 μm to approximately 1.5 μm, e.g., approximately 0.8 μm to approximately 1.2 μm, approximately 0.9 μm to approximately 1.1 μm, and approximately 1.0 μm.
Optionally, the overcoat layer 3 has a total thickness in a range of approximately 1.2 μm to approximately 3.0 μm, e.g., approximately 1.6 μm to approximately 2.4 μm, approximately 1.8 μm to approximately 2.2 μm, and approximately 2.0 μm.
In some embodiments, the display substrate further includes a spacer layer 4 on a side of the second sublayer 32 distal to the base substrate 1. The spacer layer 4 is configured to spaced apart the display substrate and another substrate (e.g., an array substrate) facing the display substrate by a distance. Optionally, an orthographic projection of the spacer layer 4 on the base substrate 1 is covered by an orthographic projection of the black matrix 6.
In another aspect, the present disclosure provides a method of fabricating a display substrate.
Optionally, the first sublayer is formed to be in contact with the color filter, and the second sublayer is formed to be in contact with the alignment film. Optionally, the alignment film is formed to be in contact with the second sublayer. Optionally, the first sublayer is formed to prevent pigments in the color filter from permeating out of the overcoat layer. Optionally, the second sublayer is formed to achieve an enhanced adhesion between the overcoat layer and the alignment film. Optionally, the second sublayer is formed using a same material as that of the alignment film.
Optionally, the step of forming the alignment film includes coating the display substrate with an alignment material layer, curing the alignment material layer, and aligning the alignment material layer thereby forming the alignment film. Optionally, the step of aligning the alignment material layer is performed by rubbing the alignment material layer. Optionally, the step of aligning the alignment material layer is performed by a photo-alignment process.
In a display substrate fabricated by the present method, the overcoat layer is formed to include at least two sublayers, a first sublayer and a second sublayer. The first sublayer includes a first material capable of effectively preventing pigments in the color filter from permeating out of the overcoat layer, thereby avoiding defects in the liquid crystal display apparatus having the display substrate caused by leakage of the color filter pigments into the liquid crystal molecule layer in the liquid crystal display apparatus. The second sublayer includes a second material having an enhanced adhesivity with the alignment film. By forming the second sublayer, various layers including the first sublayer, the second sublayer, and the alignment film can be adhered together tightly, achieving an enhanced hermeticity of the liquid crystal display apparatus, enhanced reliability under high-temperature and high-humidity environment, and enhance moist-resistance and oxygen-resistance.
Referring to
Referring to
Referring to
Referring to
Referring to
In some embodiments, the step of forming the overcoat layer further includes forming a third sublayer 33 between the first sublayer 31 and the second sublayer 32. The third sublayer 33 is formed to include a third polymer material different from the first polymer material and the second polymer material. Referring to
Referring to
Referring to
In another aspect, the present disclosure provides a display apparatus having the display substrate described herein or fabricated by a method described herein. Examples of appropriate display apparatuses includes, but are not limited to, an electronic paper, a mobile phone, a tablet computer, a television, a monitor, a notebook computer, a digital album, a GPS, etc. Optionally, the display apparatus is a liquid crystal display apparatus. Optionally, the display apparatus is an organic light emitting diode display apparatus.
The foregoing description of the embodiments of the invention has been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form or to exemplary embodiments disclosed. Accordingly, the foregoing description should be regarded as illustrative rather than restrictive. Obviously, many modifications and variations will be apparent to practitioners skilled in this art. The embodiments are chosen and described in order to explain the principles of the invention and its best mode practical application, thereby to enable persons skilled in the art to understand the invention for various embodiments and with various modifications as are suited to the particular use or implementation contemplated. It is intended that the scope of the invention be defined by the claims appended hereto and their equivalents in which all terms are meant in their broadest reasonable sense unless otherwise indicated. Therefore, the term “the invention”. “the present invention” or the like does not necessarily limit the claim scope to a specific embodiment, and the reference to exemplary embodiments of the invention does not imply a limitation on the invention, and no such limitation is to be inferred. The invention is limited only by the spirit and scope of the appended claims. Moreover, these claims may refer to use “first”, “second”, etc. following with noun or element. Such terms should be understood as a nomenclature and should not be construed as giving the limitation on the number of the elements modified by such nomenclature unless specific number has been given. Any advantages and benefits described may not apply to all embodiments of the invention. It should be appreciated that variations may be made in the embodiments described by persons skilled in the art without departing from the scope of the present invention as defined by the following claims. Moreover, no element and component in the present disclosure is intended to be dedicated to the public regardless of whether the element or component is explicitly recited in the following claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201710406158.2 | Jun 2017 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2017/111291 | 11/16/2017 | WO | 00 |