Patent Grant
7791561
The entire disclosures of the above 5 U.S. patent applications are incorporated by reference as part of the specification of this application.
This application relates to display systems that use screens with fluorescent materials to emit colored light under optical excitation, such as laser-based image and video displays and screen designs for such displays.
Many image and video displays are designed to directly produce color images in different colors, such as red, green and blue and then project the color images on a screen. Such systems are often referred to as “projection displays” where the screen is simply a surface to make the color images visible to a viewer. Such projection displays may use white light sources where white beams are filtered and modulated to produce images in red, green and blue colors. Alternatively, three light sources in red, green and blue may be used to directly produce three beams in red, green and blue colors and the three beams are modulated to produce images in red, green and blue. Examples of such projection displays include digital light processing (DLP) displays, liquid crystal on silicon (LCoS) displays, and grating light valve (GLV) displays. Notably, GLV displays use three grating light valves to modulate red, green and blue laser beams, respectively, and use a beam scanner to produce the color images on a screen. Another example of laser-based projection displays is described in U.S. Pat. No. 5,920,361 entitled “Methods and apparatus for image projection.” Projection displays use optical lens systems to image and project the color images on the screen.
Some other image and video displays use a “direct” configuration where the screen itself includes light-producing color pixels to directly form color images in the screen. Such direct displays eliminate the optical lens systems for projecting the images and therefore can be made relatively smaller than projection displays with the same screen sizes. Examples of direct display systems include plasma displays, liquid crystal displays (LCDs), light-emitting-diode (LED) displays (e.g., organic LED displays), and field-emission displays (FEDs). Each color pixel in such direct displays includes three adjacent color pixels which produce light in red, green and blue, respectively, by either directly emit colored light as in LED displays and FEDs or by filtering white light such as the LCDs.
These and other displays are replacing cathode-ray tube (CRT) displays which dominated the display markets for decades since its inception. CRT displays use scanning electron beams in a vacuum tube to excite color phosphors in red, green and blue colors on the screen to emit colored light to produce color images. Although CRT displays can produce vivid colors and bright images with high resolutions, the use of cathode-ray tubes places severe technical limitations on the CRT displays and leads to dramatic decline in demand for CRT displays in recent years.
The display systems and techniques described in this application include fluorescent screens using at least one excitation optical beam to excite one or more fluorescent materials on a screen to emit light to form images. The fluorescent materials may include phosphor materials and non-phosphor materials. The excitation light may be a laser beam or a non-laser beam.
Examples of display systems described here use at least one screen with a fluorescent material to receive a laser beam and to produce at least one monochromatic image. A screen with three or more different fluorescent materials that absorb laser light to emit colored light at different wavelengths may be used as the screen to produce the final images for viewing. Alternatively, a screen with only one fluorescent material may be used as a monochromatic projector to produce only one of monochromatic images of different colors and this one monochromatic image is combined with other monochromatic images to produce the final images for viewing at a final viewing screen. Such a laser excitable fluorescent material absorbs the laser light, e.g., UV laser light, to emit a color which is determined by the composition of the fluorescent material.
Screens with laser-excitable fluorescent materials may be used in various laser displays. One example is a laser vector scanner which scans one or more excitation laser beams on the screen to trace out texts, graphics, and images. Hence, an image of the letter “O” can be formed on the screen by scanning a laser beam along an “O” shaped path on the screen. The excitation laser beam may be a UV beam to excite the fluorescent material which emits colored light to form the image. Two or more scanning laser beams of different colors may be used to trace the same pattern to produce color mixing effects. Other complex and moving patterns can be generated by using complex scanning patterns.
Lasers may also be used in laser TV systems to form still and moving images, graphics, videos or motion pictures by raster scanning similar to the raster scanning of electron beams in CRT TVs. Such laser TVs may use scan one or more multiple excitation laser beams and a screen with one or more fluorescent materials. A scanning laser beam excites the fluorescent material on the screen to produce colored light which forms the image.
In some implementations, a display screen may include a fluorescent layer that absorbs UV light to emit visible light, a first layer on a first side of the fluorescent layer to transmit the UV light and to reflect the visible light. A Fresnel lens may be formed on the first side of the fluorescent layer to direct the UV light incident to the screen at different angles to be approximately normal to the fluorescent layer. The Fresnel lens may be in a telecentric configuration for the incident UV light. The first layer can be a dichroic layer. In addition, the screen may also include a second layer on a second side of the fluorescent layer to transmit visible light and to block the UV light. The second layer may be, e.g., a dichroic layer. In other implementations, the first layer may include a lens having a first surface to receive the UV light and a second opposing surface facing the fluorescent layer and coated with a reflective layer to reflect the UV and the visible light, wherein the reflective layer has an aperture in a center of the second surface to allow for the UV light to transmit through.
Other laser display systems are described.
For example, a laser display system is described to include a screen comprising a substrate on which a plurality of parallel phosphor stripes are formed, wherein at least three adjacent phosphor stripes are made of three different phosphors: a first phosphor to absorb light at an excitation wavelength to emit light of a first color, a second phosphor to absorb light at the excitation wavelength to emit light of a second color, and a third phosphor to absorb light at the excitation wavelength to emit light of a third color. The system also includes a laser module to project and scan a laser beam at the excitation wavelength onto the screen to convert an image carried by the laser beam via an optical modulation into a color image produced by the phosphor stripes on the screen.
In one implementation, the screen in the above system may include phosphor stripes that comprise a fourth phosphor to absorb light at the excitation wavelength to emit light of a fourth color.
In another implementation, the display system may include optical sensors positioned to receive and detect light from the phosphor stripes, where one optical sensor receives only one of colors emitted by the phosphor stripes on the screen. A feedback mechanism is included to direct outputs of the phosphor sensors to the laser module and an alignment control mechanism in the laser module is further included to control a timing of image data modulated on the laser beam to correct an alignment of the laser beam respect to the phosphor stripes.
In yet another implementation, the laser module may include a modulation control which combines a pulse code modulation and a pulse width modulation in the optical modulation of the laser beam to produce image grey scales.
In yet another implementation, the laser module may be configured to project and scan at least a second laser beam on the screen simultaneously with the scanning of the laser beam to produce two different spatial parts of an image on different locations of the screen.
In yet another implementation, the laser module may be configured to include a mechanism to monitor image data bits to be modulated on the laser beam to produce a black pixel monitor signal, at least a diode laser to produce the laser beam, and a laser control coupled to receive the black pixel monitor signal and to operate the diode laser at a driving current below a laser threshold current without turning off the driving current to produce a virtual black color on the screen when the black pixel monitor signal indicates a length of black pixels is less than a threshold and turn off the driving current to produce a true black color on the screen when the black pixel monitor signal indicates a length of black pixels is greater than a threshold.
Laser display systems with three or more monochromatic laser display projection modules are also described. In one example, such a system includes first, second, and third laser display modules to produce first, second and third monochromatic image components of a final image in first, second, and third different colors, respectively, and to project the first, second and third monochromatic image components on a display screen to produce the final image. In this example, the first laser display module includes: (1) a first screen comprising a first phosphor to absorb light at an excitation wavelength to emit light at a first wavelength different from the excitation wavelength; (2) a first laser module to project and scan at least one laser beam at the excitation wavelength onto the first screen to convert an image in the first color carried by the laser beam into the first monochromatic image component produced by the first phosphor on the first screen; and (3) a first projection optical unit to project the first monochromatic image component from the first screen to the display screen.
In one implementation, the third laser display module may include (1) a third screen which does not have a phosphor; (2) a third laser module to project and scan at least one laser beam of the third color onto the third screen to directly produce the third monochromatic image component on the third screen; and (3) a third projection optical unit to project the third monochromatic image component from the third screen to the display screen.
In another implementation, the third laser display module directly projects and scans at least one laser beam of the third color onto the display screen to directly produce the third monochromatic image component on the display screen.
Another example for laser display systems with three or more monochromatic laser display projection modules uses a first laser display module which comprises: (1) a first screen comprising a first phosphor to absorb light at an excitation wavelength to emit light at a first wavelength different from the excitation wavelength; (2) a first laser module to project and scan at least one laser beam at the excitation wavelength onto the first screen to convert an image carried by the laser beam into a first image produced by the first phosphor on the first screen. A second laser display module is also used in this system and includes: (1) a second screen comprising a second phosphor to absorb light at an excitation wavelength to emit light at a second wavelength different from the excitation wavelength; (2) a second laser module to project and scan at least one laser beam at the excitation wavelength onto the second screen to convert an image carried by the laser beam into a second image produced by the second phosphor on the second screen. In addition, a third laser display module is used and includes: (1) a third screen which does not have a phosphor; (2) a third laser module to project and scan at least one laser beam at a third wavelength different from the first and second wavelengths onto the third screen to directly produce a third image on the third screen in a color of the third wavelength. Furthermore, first, second and third projection optical units are used to respectively project the first image, second image and third image on a display screen to produce a final image.
A further example for laser display systems is a system with at least three monochromatic laser display projection modules each with a phosphor projection screen. The first laser display module includes (1) a first screen comprising a first phosphor to absorb light at an excitation wavelength to emit light at a first wavelength different from the excitation wavelength; and (2) a first laser module to project and scan at least one laser beam at the excitation wavelength onto the first screen to convert an image carried by the laser beam into a first image produced by the first phosphor on the first screen. The second laser display module includes (1) a second screen comprising a second phosphor to absorb light at an excitation wavelength to emit light at a second wavelength different from the excitation wavelength; and (2) a second laser module to project and scan at least one laser beam at the excitation wavelength onto the second screen to convert an image carried by the laser beam into a second image produced by the second phosphor on the second screen. The third laser display module includes (1) a third screen comprising a third phosphor to absorb light at an excitation wavelength to emit light at a third wavelength different from the excitation wavelength; and (2) a third laser module to project and scan at least one laser beam at the excitation wavelength onto the third screen to convert an image carried by the laser beam into a third image produced by the third phosphor on the third screen. In addition, this system includes first, second and third projection optical units to project the first image, second image and third image to spatially overlap on a display screen to produce a final image.
The above and other laser display systems may use various phosphor materials on the screen. Suitable phosphor materials may include the following:
an Eu-doped photoluminescent metal sulfide in form of MS:Eu where M is at least one of Ca, Sr, Ba, Mg and Zn;
a metal thiometallate photoluminescent material in form of M*N*2S4:Eu,Ce where M* is at least one of Ca, Sr, Ba, Mg and Zn, and N* is at least one of Al, Ga, In, Y, La and Gd;
Sr1-u-v-xMguCavBax)(Ga2-y-zAlyInzS4):Eu2+ or (Sr1-u-v-xMguCavBax)(Ga.sub.2-y-zAlyInzS4):Eu2+;
(Y,Gd)3Al5O12:Ce;
a rare earth doped CaS, SrS or a thiogallates;
one of SrS:Eu2+;CaS:Eu2+;CaS:Eu2+,Mn2+;(Zn,Cd)S:Ag+; Mg4GeO5.5F:Mn4+;Y2O2S:Eu2+, ZnS:Mn2+, SrGa2S4:Eu2+;ZnS:Cu,Al; BaMg2Al16O27:Eu2+,Mg; and (Y,Gd)3Al5O12:Ce,Pr;
at least one of Ba2MgSi207:Eu2+;Ba2SiO4:Eu2+; and (Sr,Ca,Ba)(Al,Ga)2S4:Eu2+;
AEu(1-x)LnxB2O8 where A is an element selected from the group consisting of Li, K, Na and Ag; Ln is an element selected from a group consisting of Y, La and Gd; and B is W or Mo; and x is number equal to or larger than 0, but smaller than 1;
at least one of YBO3:Ce3+,Tb3+;BaMgAl10O17:Eu2+,Mn2+;(Sr,Ca,Ba)(Al,Ga)2S4:Eu2+;Y3Al5O12:Ce3+;Y2O2S:Eu2+,Bi3+;YVO4:Eu3+,Bi3+;SrS:Eu2+;SrY2S4:Eu2+;SrS:Eu2+,Ce3+,K+;(Ca,Sr)S:Eu2+; and CaLa2S4:Ce3+;
a host material selected from Yttrium-Aluminum-Garnet, monoklinic YalO and YalO-perovskite, Y,Ln)AlO, and (Y,Ln)(Al,Ga)O, wherein the host is doped with at least one of Cerium (Ce), Praseodymium (Pr), Holmium (Ho), Ytterbium (Yb), and Europium (Eu);
MexSi12-(m+n)Al(m+n)OnN16-n:Re1yRe2z, where Me is one or more of Li, Ca, Mg, Y and lanthanide metals except for La and Ce, Re1 and Re2 are lanthanide metals;
an oxide nitride phosphor that includes α-sialon and is doped with a rare-earth element;
a cerium ion doped lanthanum silicon nitride phosphor: La1-XSi3N5:xCe (0<x<1);
a garnet fluorescent material comprising 1) at least one element selected from the group consisting of Y, Lu, Sc, La, Gd and Sm, and 2) at least one element selected from the group consisting of Al, Ga and In, and being activated with cerium;
a phosphor blend comprising BaMg2Al16O27:Eu2+(BAM) and (Tb1-x-yAxREy)3DzO12(TAG), where A is a member selected from the group consisting of Y, La, Gd, and Sm; RE is a member selected from the group consisting of Ce, Pr, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, and Lu; D is a member selected from the group consisting of Al, Ga, and In; x, y and z are positive numbers;
a phosphor blend comprising Tb3Al4.9O12:Ce and at least one of BaMg2Al16O27:Eu2+(BAM) and (Sr,Ba,Ca,Mg)5(PO4)3Cl:Eu2+;
BaF2.aBaX2.bMgF2.cBeF2.dMeIIF2:eLn, where X is at least one halogen selected from the group consisting of chlorine, bromine and iodine; MeII is at least one divalent metal selected from the group consisting of: calcium and strontium; Ln is at least one rare earth element selected from the group consisting of: divalent europium (Eu2+), cerium (Ce3+) and terbium (Tb3+), and a, b, c, and d are positive numbers;
a cerium activated rare earth halophosphate phosphor: LnPO4.aLnX3:xCe3+ in which Ln is at least one rare earth element selected from the group consisting of Y, La, Gd and Lu; X is at least one halogen selected from the group consisting of F, Cl, Br and I; and a and x are positive numbers;
SrxLn1y1Ln2y2Ln3y3MzAaBbO19-k(I), where Ln1 represents at least one trivalent element selected from lanthanum, gadolinium and yttrium; Ln2 represents at least one trivalent element selected from neodymium, praseodymium, erbium, holmium and thulium; Ln3 represents an element selected from bivalent europium or trivalent cerium with retention of electric neutrality by virtue of oxygen holes; M represents at least one bivalent metal selected from magnesium, manganese, and zinc; A represents at least one trivalent metal selected from aluminum and gallium; B represents at least one trivalent transition metal selected from chromium and titanium; x, y1, y2, y3, z, a, b and k are positive numbers;
MIIX2.aMIIX′2.bSiO:xEu2+, where MII is at least one alkaline earth metal selected from the group consisting of Ba, Sr and Ca; each of X and X′ is at least one halogen selected from the group consisting of Cl, Br and I, and X is not the same as X′; a, b and x are positive numbers;
an alkaline-based halide as a host material and a rare earth as a dopant;
(Ba1-qMq)(Hf1-z-eZrzMge): yT wherein M is selected from the group consisting of Ca and Sr and combinations thereof; T is Cu; and q is, z, e and y are positive numbers;
A3B5X12:M, where A is an element selected from the group consisting of Y, Ca, Sr; B is an element selected from the group consisting of Al, Ga, Si; X is an element selected from the group consisting of O and S; and M is an element selected from the group consisting of Ce and Tb;
Ba2 (Mg, Zn)Si2O7: Eu2+ or (Ba1-X-Y-Z, CaX, SrY, EuZ)2(Mg1-w,Znw)Si2O7;
SrxBayCazSiO4:Eu2+ in which x, y, and z are each independently any value between and including 0 and 2;
ZnSxSey:Cu,A in which x and y are each independently any value between 0 and 1 and A is at least one of Ag, Al, Ce, Tb, Cl, I, Mg, and Mn;
MA2(SxSey)4:B in which x and y are each independently any value between about 0.01 and about 1; M is at least one of Be, Mg, Ca, Sr, Ba, Zn; and A is at least one of Al, Ga, In, Y, La, and Gd; and the activator B is at least one of Eu, Ce, Cu, Ag, Al, Tb, Cl, F, Br, I, Pr, Na, K, Mg, and Mn;
M2A4(SxSey)7:B in which x and y are each independently any value between about 0.01 and about 1, M is at least one of Be, Mg, Ca, Sr, Ba, Zn; and A is at least one of Al, Ga, In, Y, La, and Gd; and B is at least one of Eu, Ce, Cu, Ag, Al, Tb, Cl, Br, F, I, Pr, K, Na, Mg, and Mn;
(M1)m(M2)nA2(SxSey)4:B in which: M1 comprises an element selected from the group consisting of: Be, Mg, Ca, Sr, Ba, Zn; M2 comprises an element selected from the group consisting of: Be, Mg, Ca, Sr, Ba, Zn; A comprises one or more elements selected from the group consisting of: Al, Ga, In, Y, La, and Gd; and B comprises one or more elements selected from the group consisting of: Eu, Ce, Cu, Ag, Al, Tb, Cl, Br, F, I, Mg, Pr, K, Na, and Mn;
(M1)m(M2)nA4(SxSey)7:B in which M1 comprises an element selected from the group consisting of: Be, Mg, Ca, Sr, Ba, Zn; M2 comprises an element selected from the group consisting of: Be, Mg, Ca, Sr, Ba, Zn; A comprises one or more elements selected from the group consisting of: Al, Ga, In, Y, La, and Gd; and B comprises one or more elements selected from the group consisting of: Eu, Ce, Cu, Ag, Al, Th, Cl, Br, F, I, Mg, Pr, K, Na, and Mn;
These and other laser display systems, display techniques, and fluorescent materials are described in greater detail in the attached drawings, the textual description, and the claims.
This application describes display systems and devices that use screens with fluorescent materials to emit light under optical excitation to produce images, including laser vector scanner display devices and laser video display devices that use laser excitable fluorescent screens to produce images by absorbing excitation laser light and emitting colored light. Various examples of screen designs with fluorescent materials are described. Screens with phosphor materials under excitation of one or more scanning excitation laser beams are described in details and are used as specific implementation examples of optically excited fluorescent materials in various system and device examples in this application. In one implementation, for example, three different color phosphors that are optically excitable by the laser beam to respectively produce light in red, green, and blue colors suitable for forming color images may be formed on the screen as pixel dots or repetitive red, green and blue phosphor stripes in parallel. Various examples described in this application use screens with parallel color phosphor stripes for emitting light in red, green, and blue to illustrate various features of the laser-based displays. Phosphor materials are one type of fluorescent materials. Various described systems, devices and features in the examples that use phosphors as the fluorescent materials are applicable to displays with screens made of other optically excitable, light-emitting, non-phosphor fluorescent materials.
For example, quantum dot materials emit light under proper optical excitation and thus can be used as the fluorescent materials for systems and devices in this application. More specifically, semiconductor compounds such as, among others, CdSe and PbS can be fabricated in form of particles with a diameter on the order of the exciton Bohr radius of the compounds as quantum dot materials to emit light. To produce light of different colors, different quantum dot materials with different energy band gap structures may be used to emit different colors under the same excitation light. Some quantum dots are between 2 and 10 nanometers in size and include approximately tens of atoms such between 10 to 50 atoms. Quantum dots may be dispersed and mixed in various materials to form liquid solutions, powders, jelly-like matrix materials and solids (e.g., solid solutions). Quantum dot films or film stripes may be formed on a substrate as a screen for a system or device in this application. In one implementation, for example, three different quantum dot materials can be designed and engineered to be optically excited by the scanning laser beam as the optical pump to produce light in red, green, and blue colors suitable for forming color images. Such quantum dots may be formed on the screen as pixel dots arranged in parallel lines (e.g., repetitive sequential red pixel dot line, green pixel dot line and blue pixel dot line).
Some implementations of laser-based display techniques and systems described here use at least one scanning laser beam to excite color light-emitting materials deposited on a screen to produce color images. The scanning laser beam is modulated to carry images in red, green and blue colors or in other visible colors and is controlled in such a way that the laser beam excites the color light-emitting materials in red, green and blue colors with images in red, green and blue colors, respectively. Hence, the scanning laser beam carries the images but does not directly produce the visible light seen by a viewer. Instead, the color light-emitting fluorescent materials on the screen absorb the energy of the scanning laser beam and emit visible light in red, green and blue or other colors to generate actual color images seen by the viewer.
Laser excitation of the fluorescent materials using one or more laser beams with energy sufficient to cause the fluorescent materials to emit light or to luminesce is one of various forms of optical excitation. is In other implementations, the optical excitation may be generated by a non-laser light source that is sufficient energetic to excite the fluorescent materials used in the screen. Examples of non-laser excitation light sources include various light-emitting diodes (LEDs), light lamps and other light sources that produce light at a wavelength or a spectral band to excite a fluorescent material that converts the light of a higher energy into light of lower energy in the visible range. The excitation optical beam that excites a fluorescent material on the screen can be at a frequency or in a spectral range that is higher in frequency than the frequency of the emitted visible light by the fluorescent material. Accordingly, the excitation optical beam may be in the violet spectral range and the ultra violet (UV) spectral range, e.g., wavelengths under 420 nm. In the examples described blow, UV light or a UV laser beam is used as an example of the excitation light for a phosphor material or other fluorescent material and may be light at other wavelength.
The optical modulation in the laser module 110 may be achieved in two different configurations.
The laser beam 120 is scanned spatially across the screen 101 to hit different color pixels at different times. Accordingly, the modulated beam 120 carries the image signals for the red, green and blue for each pixel at different times and for different pixels at different times. Hence, the modulation of the beam 120 is coded with image information for different pixels at different times to map the timely coded image signals in the beam 120 to the spatial pixels on the screen 101 via the beam scanning.
One important technical parameter for displays is the contrast ratio. The light level of the black color is usually the dominating factor for the contrast ratio. For a given system, the lower the light level of the black color the better the contrast of the display system. Many display systems can achieve a virtual black color by reducing the light levels in all three color sub pixels of a color pixel to their minimum levels without being able to completely shut off the light. The laser-based display systems described here, however, can be designed to completely shut off light in each color sub pixel to produce the true black color. This technique is now described with a specific reference to a diode laser as the light source as an example and it is understood that the technique can also be used in other laser sources.
A diode laser has a threshold behavior where the laser action starts when the forward driving current is greater than a threshold value and the diode laser emits spontaneously without lasing when the driving current is below the threshold.
When an image frame does not have contiguous black pixels in time less than the delay time of the diode laser, the diode laser is controlled to operate at a bias current just below the threshold current to produce a virtual black in these black pixels. When an image frame has contiguous black pixels in time greater than the delay time of the diode laser, the diode laser is turned off by shutting off the driving current at the beginning of the black pixels to produce the true black in these pixels. At the end of the this block of contiguous black pixels, the driving current of the diode laser is turned back on to a value just below the threshold current to produce the virtual black for the remaining black pixels so that the first non-black pixel following the block of the contiguous pixels can be timely generated. In this example, a part of the black pixels is true black and a part of the black pixels is virtual black. On average, the light level for the black pixels is better than the virtual black. For a diode laser with a delay time in tens of nanoseconds, two or more sequential black pixels with a pixel duration of 50 nsec would be sufficient to operate the diode laser to generate the true black.
In operation, the display processor monitors the pixels in each image frame to be displayed. This monitoring process can be achieved in the digital domain where the data bits for the pixels in a memory buffer of the processor are monitored. Depending on the length of the contiguous black pixels in time to be displayed, the display processor operates to keep the switch open to produce the virtue black to close the switch to produce the true black.
Referring back to
To mitigate this horizontal misalignment, a sensing mechanism may be built in the screen 101 as a pixel sensor unit to detect the horizontal misalignment and a feedback control may be used to correct the misalignment.
The on-screen pixel sensor unit 1401 may include three optical detectors PD1, PD2 and PD3 that are located on the screen 101 and are respectively configured to respond to red, green and blue light. Each optical detector is only responsive to its designated color and not to other colors. Hence, as an example, the red optical detector PD1 responds to the red light but is not responsive to green and blue light. This may be achieved by, e.g., using red, green and blue optical bandpass filters in front of the optical detectors PD1, PD2 and PD3, respectively. Assume the adjacent color phosphor strips are arranged in the order of red, green and blue from the left to the right in the horizontal direction of the screen 101. If a red image is generated by the display processor in the laser module 110 but the red detector PD1 does not respond while either the blue detector PD3 or the green detector PD2 produces an output, the horizontal alignment is out of order by one sub pixel.
One way to correct this horizontal misalignment is to program the display processor in the laser module 110 to delay the modulated image signal carried by the modulated laser beam 120 by one sub color pixel time slot if the green detector PD2 has an output and red and blue detectors PD1 and PD3 have no output, or by two sub color pixel time slots if the blue detector PD3 has an output and red and green detectors PD1 and PD2 have no output. This correction by time delay may be achieved digitally within the display processor in the laser module 110. No physical adjustment in the optical scanning and imaging units in the laser module 110 is needed. Alternatively, the imaging unit in the laser module 110 may be adjusted to shift the laser position on the screen 101 horizontally to the left or right by, e.g., one sub pixel, to correct the horizontal misalignment as indicated by the sensor feedback signal 1402.
The above red, green and blue optical detectors PD1, PD2 and PD3 may be positioned to receive light from multiple pixels on the screen 101. A test pattern may be used to check the alignment. For example, a frame of one of the red, green and blue colors may be used as a test pattern to test the alignment. Alternatively, the red, green and blue optical detectors PD1, PD2 and PD3 may be embedded in the screen 101 to receive color light from different color sub pixels.
The present display systems may use a single scanning laser beam 120 to scan one horizontal line at a time to scan through the entire screen 101. Alternatively, multiple lasers may be used to produce multiple parallel scanning beams 120 to divide the screen 101 into N segments along the vertical direction so that one scanning beam 120 is designated to scan one segment and N scanning beams 120 are scanning N different segments at the same time.
As an example, the horizontal scanning may be achieved with a rotating polygon mirror with M facets and the vertical scanning may be achieved with a galvo mirror. For a screen for HDTV 16:9 aspect ratio, the angular ranges for horizontal and vertical scans are similar. For 16 degrees horizontal scan or +/−8 degrees, a mirror on the polygon needs to have a minimum subtended angle of 8 degrees. Therefore, the maximum number M of mirrors per 360 degrees is M=360/8=45 mirrors per revolution. Assuming 1080 interlaced lines or 540 odd lines followed by 540 even lines in 1/60 of a second, the number N of the scanning beams is equal to 540/M=12. Each beam scans 1/12 of the screen using a galvo mirror moving 9 degrees/12=0.75 degrees or 13 mrad. The segment of 1/12 of a screen is a sub-screen or a screen segment. Under this design, each sub-screen is traced in 1/60 of a second. The RPM of the disk is 3600 RPM with each mirror scan time equal to 1/60/45=370 usecs (ignoring retrace time). Each M facet moves at a speed of 370 usec. In each 370 usec slot the galvo mirror steps by increments of 0.75 degrees/45=0.3 mrad. Each subscreen is scanned twice, one for odd lines and one for even lines in 1/60th second each, this means the galvo mirror moves by discrete steps of 0.3 mrad as shown below:
In this particular example, the video bandwidth can be determined as follows. Each horizontal scan takes 370 usec to complete. Time for each pixel=370 usec/1920=192 nsec or 5.2 Mhz. Typically one needs 3× the pixel time for proper video BW which means about 15 MHz 3 dB point. This type of modulation frequency is easily attained by AO modulation. A total of 12×3 UV diode lasers each at about 50-100 mW each may be used to generate the scanning beams.
In implementing the above and other display designs, there can be a vertical misalignment between the multiple segments comprising the full screen. This misalignment can be digitally corrected with a means similar to that of the horizontal correction. Each segment of the screen can be driven with a scan engine capable of generating more horizontal lines than actually required for display in that segment (e.g., 4 extra lines). In perfectly aligned situation, there are an equal number of extra (unused) lines above and below the segment image. If vertical misalignment exists, the control electronics may shift the segment image upwards or downwards by utilizing these extra lines in place of normal lines. For example, if the image needs to be moved upwards one line, the controller moves each line upwards to the previous one, utilizing one of the extra lines above the normal image and adding an extra unused line at the bottom. If this adjustment is desired to take place automatically during startup or normal operation, a sensor is required to provide feedback in real time. Such a sensor could be a position sensing diode located to either side of the viewable area of the segment to be controlled. The line would over scan onto this sensor when required. Alternatively a beam splitter could be used to provide feedback during the viewable portion of the scan.
One of the advantages of the above method is to reduce or simplify the requirement for accurate optical alignment because the electronic adjustment, when properly implemented, is simpler to implement and can reduce cost of the device.
The above described method allows adjustment with a resolution of only one line. To accomplish sub-line (sub-pixel) adjustment, the scan engine can be rotated slightly. This produces slightly diagonal horizontal scan lines. The adjacent screen segments would have scan engines slightly rotated on the opposite direction. Under this condition, to create a straight horizontal line, portions of at least two scan lines are used depending on the amount of rotation. This may provide a less noticeable junction between the screen segments.
Another method to reduce the visible junction artifact between two adjacent screen segments is to overlap the colors from each segment at the junction. For example the last blue line of segment #1 might be painted by one of the extra lines from the top of segment #2. Likewise, the first red line of segment #2 might be painted to be one of the extra lines at the bottom of segment #1. This could further visually spread any junction artifacts.
In the above display systems with color phosphor screens, the same scanning beam is used to address all three color sub pixels within each pixel on the screen. Alternatively, three different scanning beams may be used to respectively address the three color sub pixels in each color pixel.
More specifically,
As illustrated in
In an alternative implementation, a single stationary actuator 2240 may be used to control tilting of different reflecting facets 2210. As each facet 2210 rotates around the axis 2230 and passes by the stationary actuator 2240, the facet is tilted by the operation of the actuator 2240 to perform the vertical scanning of the beam. Similarly, two or more stationary actuators may be used and placed at different heights of the facets.
The above scanning-laser display systems with screens having laser-excitable light-emitting materials may be used to form a monochromatic display module by having only one phosphor material on the screen. Hence, a red monochromatic display module based on this design can be implemented by replacing the green and blue phosphor stripes with red phosphor stripes on the screen 101 in
The above design of mixing phosphor-generated colors with direct laser colors can be applied to other color arrangements.
In addition, a monochromatic laser display module in the above color mixing designs may alternatively directly project its scanning laser beam at a desired color to the common display screen without the projection screen with the phosphor material. Accordingly, each projection screen without the phosphor material in
In the above designs, the final, common screen for displaying the final images produced from mixing a fluorescence-generated monochromatic image and a monochromatic image at a different color directly formed by a scanning colored beam is an optically “passive” screen in that the screen does not have any fluorescent material that emits light. A fluorescence-generated monochromatic image is generated by a phosphor projection screen which is excited by an excitation beam and the image is projected from the phosphor projection screen to the final optically “passive” screen where the mixing with images in other colors occurs. In some implementations, the separate projection screens and the final “passive” screen can be replaced by a single screen that generates one or more fluorescence-generated monochromatic images and mixes a fluorescence-generated monochromatic image and a monochromatic image directly formed on the screen by a scanning beam. Because at least one of monochromatic images that form the final image is directly formed on the screen by a scanning beam, the screen in such a design is “partially optically active” in that the screen has a fluorescent material that is excited by an optical excitation beam to produce one or more monochromatic images but does not generate all of the monochromatic images that form the final images on the screen. The screen may be designed to include parallel fluorescent stripes and non-fluorescent stripes on a substrate where each non-fluorescent stripe is to display a monochromatic image that is directly formed by light of a scanning beam without emitting fluorescent light.
For example, a display system based on this design may include a screen with at least two different florescent materials that absorb an excitation beam at an excitation wavelength and emit fluorescent light at two different colors. The excitation beam is at a visible color that is different from the colors of the light emitted by the fluorescent materials. In some implementations, the screen include an array of color pixels where each pixel includes subpixels for different colors: a non-fluorescent sub pixel without a fluorescent material to directly display the color and image of the excitation beam, and spatially separated fluorescent subpixels respectively with different fluorescent materials to emit different colors in response to the illumination of the excitation beam. In other implementations, the screen can have parallel stripe patterns in a period pattern where each period includes a non-fluorescent stripe that does not have a fluorescent material and directly displays the color and image of the excitation beam and adjacent different stripes formed of the different florescent materials for different colors. The visible monochromatic excitation beam scans through the screen in a direction perpendicular to the stripes to produce different monochromatic images at different colors that form the final colored images on the screen.
UV-excitable phosphors suitable of color or monochromatic screens described in this application may be implemented with various material compositions. Typically, such phosphors absorb excitation light such as UV light to emit photons in the visible range at wavelengths longer than the excitation light wavelength. For example, red, green, and blue fluorescent materials may be ZnCdS:Ag, ZnS:Cu, and ZnS:Ag, respectively.
TABLE 1 lists some examples of phosphors that emit visible color light when excited by excitation light in the wavelength range from 380 nm to 415 nm described in various published patent documents. Various phosphors listed in TABLE 1 can also be excited by light from 450 nm to 470 nm. These and other phosphors can be used to implement the phosphor-based laser displays described in this application.
The examples of phosphors described in the published PCT application No. WO 02/11173 A1 are “Type I” phosphors with compositions of Eu-doped photoluminescent metal sulfides in form of MS:Eu where M is at least one of Ca, Sr, Ba, Mg and Zn, and “Type II” phosphors with compositions of metal thiometallate photoluminescent materials in form of M*N*2S4:Eu,Ce where M* is at least one of Ca, Sr, Ba, Mg and Zn, and N* is at least one of Al, Ga, In, Y, La and Gd. A photoluminescent metal sulfide MS (Type I phosphor) may include at least one of Ba, Mg, and Zn alone or in combination with at least one of Sr and Ca. A metal thiometallate photoluminescent material M*N*2S4 (type II phosphor) may include at least one element selected from the group M*=Mg and Zn alone for M* or in combination with at least one of Ba, Sr and Ca and the element N* may be Al or Ga alone or in further combination with In, Y, La, Gd. A metal thiometallate photoluminescent material may be activated with at least one of europium (Eu) and cerium (Ce). Two or more of type I and type II phosphors may be combined, or one or more phosphors of type I and type II phosphors may be combined with other phosphors different from phosphors of type I and type II to form a phosphor blend to generate a color that may not be available from individual type I and type II phosphors.
Specific examples of the phosphor compositions for the type I phosphors for emitting red colors include (Sr1-x-yMxEuy)S with M is at least one of Ba, Mg, Zn alone or in combination with Ca and 0<x≦=0.5 and 0<y≦=0.10, (Sr1-x-yBaxEuy)S with x≦0.25, (Sr1-x-z-yCaxBazEuy)S with x+y+z≦=0.35 which exhibit a high quantum efficiency of 65-80%, high absorbance in the range from 370 nm to 470 nm of 60-80% and low loss, below 10%, of the luminescent lumen output from room temperature to 100° C. due to thermal quenching. Specific examples of type II phosphor compositions are M*N*2S4:Eu,Ce (type II phosphor) where M* is at least one of M*=Mg, Zn alone or together with at least one of Ba, Sr, Ca, and N* is at least one of N*=Al, Ga, alone or together with small amounts (below 20%) of In, Y, La, Gd. Such type II phosphors emit light in the blue, green or green-yellow spectral range of the visible spectrum. Specific compositions for the type II phosphors include (M**1-uMgu) (Ga1-vN*v)2S4:Ce with u≦0.75 and v≦0.10, and M** is at least one of M**=Ba, Sr, Ca, Zn, (M**1-s-tEusCet)(Ga1-vN*v)2S4 with M** is at least one of ═Mg, Zn alone or in combination with Sr, Ba, Ca, and N*=Al, In, Y, La, Gd and 0≦s<=0.10 and 0≦t:s<0.2 with v≦0.10, ((Ba1-uMgu)1-s-tEusCet)(Ga1-vN*v)2S4 with u≦0.75 and v≦0.10 and 0<s≦0.10 and 0s≦t:s<0.2, (Ba1-wCaw)1-uMgu)1-s-tEusCet)(Ga1-vN*v)2S4 with u<0.75 and w≧0.10 and v<0.10 and 0<s≦0.10 and 0≦t:s<0.2, (((Ba1-rSrr)1-uMgu)1-s-tEusCet)(Ga1-vN*v)2S4 with u<0.75 and r≧0.10 and v≦0.10 and 0<s≦0.10 and 0≦t:s<0.2, (((Sr1-wCaw)1-uMgu)1-s-tEusCet)(Ga1-vN*v)2S4 with u≦0.75 and w≧0.10 and v≦0.10 and 0<s≦0.10 and t:s<0.2, and (((Sr1-pZnp)1-uMgu)1-s-tEusCet)(Ga1-vN*v)2S4 with u<0.75 and p≦0.35 and v≦0.10 and 0<s≦0.10 and 0≦t:s<0.2.
The examples of phosphors described in U.S. Pat. No. 6,417,019 include (Sr1-u-vMguCavBax)(Ga2-y-zAlInz S4):Eu2+, (Sr1-u-v-xMguCavBax)(Ga.sub.2-y-zAlyInzS4):Eu2+. The phosphor particles may be dispersed in a host material which is selected from, for example, materials including but not limited to epoxies, acrylic polymers, polycarbonates, silicone polymers, optical glasses, and chalcogenide glasses. Alternatively, such phosphors may be deposited on substrate surfaces as phosphor films.
The examples of phosphors described in U.S. Patent Application Publication No. 2002/0185965 include the phosphor powder mixed with the conventional curable silicone composition is a powder of (Y,Gd)3Al5O12:Ce (gadolinium and cerium doped yttrium aluminum garnet) particles available as product number QUMK58/F from Phosphor Technology Ltd., Nazeing, Essex, England. Particles of this phosphor material have a typical diameter of about 5 microns (μm), range from 1 to 10 μm, absorb light of wavelengths from about 430 nm to about 490 nm, and emit light in a broad band from about 510 nm to about 610 nm. The color of light emitted by an LED having a stenciled phosphor layer is determined, in part, by the concentration of phosphor particles in the luminescent stenciling composition. The phosphor particles may be mixed with the curable silicone polymer composition at concentrations ranging from about 20 grams of phosphor particles per 100 grams of silicone polymer composition to about 120 grams of phosphor particles per 100 grams of silicone polymer composition. In some implementations, the titanium dioxide particles may also be used as additives and dispersed in the silicone polymer composition at a concentration of about 1.5 grams of titanium dioxide per 100 grams of silicone polymer composition to about 5.0 grams of titanium dioxide per 100 grams of silicone polymer composition. The titanium dioxide particles, which are approximately the same size as the phosphor particles, increase the scattering of excitation light and thus increase the absorption of that light by the phosphor particles. Next, after the phosphor particles and optional titanium dioxide particles are mixed with the curable silicone composition, finely divided silica particles are dispersed in the mixture to form a thixotropic gel. A thixotropic gel exhibits thixotropy, i.e., an apparent drop in viscosity when subjected to shear and a return to the original viscosity level when the shear force is removed. Consequently, a thixotropic gel behaves as a fluid when shaken, stirred, or otherwise disturbed and sets again to a gel when allowed to stand. The silica particles may be, e.g., particles of fumed silica, a colloidal form of silica made by combustion of chlorosilanes in a hydrogen-oxygen furnace. Fumed silica is chemically and physically stable at temperatures exceeding 120° C., transparent to visible light, and will impart satisfactory thixotropic properties to the luminescent stenciling composition at comparatively low concentrations. The grade of fumed silica used is chosen to be compatible with non-polar materials. In one implementation, the fumed silica is M-5P grade CAB-O-SIL®. untreated amorphous fumed silica obtained from Cabot Corporation of Boston, Mass. This grade of fumed silica is hydrophobic and has an average surface area per unit mass of 200±15 m2/g. The M-5P grade fumed silica particles are dispersed in the mixture of phosphor particles and silicone polymer composition with a conventional three roll mill at concentrations of about 1.5 grams of fumed silica per 100 grams of silicone polymer composition to about 4.5 grams of fumed silica per 100 grams of silicone polymer composition. As the concentration of fumed silica is increased, the stenciling composition becomes more thixotropic, i.e., more solid-like as an undisturbed gel.
Other implementations use fumed silica having a surface area per unit mass either greater than or less than 200±15 m2/g. For fixed concentrations of fumed silica, stenciling compositions become more thixotropic as the surface area per unit mass of the fumed silica is increased. Thus, fumed silicas having lower surface area per unit mass must be used at higher concentrations. The required high concentrations of low surface area per unit mass fumed silicas can result in stenciling compositions having viscosities that are too high to be easily stenciled. Consequently, the fumed silica preferably has a surface area per unit mass greater than about 90 m2/g. In contrast, as the surface area per unit mass of the fumed silica is increased, the required concentration of fumed silica decreases, but the fumed silica becomes more difficult to disperse in the silicone polymer composition.
The examples of phosphors described in the PCT Patent Application Publication No. WO 01/24229 include host materials and dopant ions. The host material may have an inorganic, ionic lattice structure (a “host lattice”) in which the dopant ion replaces a lattice ion. The dopant is capable of emitting light upon absorbing excitation radiation. Suitable dopants strongly absorb excitation radiation and efficiently convert this energy into emitted radiation. As an example, the dopant may be a rare earth ion which absorbs and emits radiation via 4f-4f transitions, i.e. electronic transitions involving f-orbital energy levels. While f-f transitions are quantum-mechanically forbidden, resulting in weak emission intensities, it is known that certain rare earth ions, such as Eu2+ or Ce3+, strongly absorb radiation through allowed 4f-5df transitions (via d-orbital/f-orbital mixing) and consequently produce high emission intensities. The emissions of certain dopants can be shifted in energy depending on the host lattice in which the dopant ion resides. Certain rare earth dopants efficiently convert blue light to visible light when incorporated into an appropriate host material. In some implementations, the first and second phosphors comprise a host sulfide material, i.e. a lattice which includes sulfide ions. Examples of suitable host sulfide materials include CaS, SrS and a thiogallates such as SrGa2S4. A phosphor mixture may be formed by different rare earth ions that are excitable by one common blue energy source of a relatively narrow linewidth to emit light at two different energy ranges (e.g. red and green). As an example for such a phosphor mixture, the dopant is the same in the first and second phosphors with different host materials. The red and green emissions of the two phosphors can be tuned by selecting an appropriate host material. In one embodiment, the green phosphor is SrGa2S4:Eu. In another embodiment, the red phosphor is selected from the group consisting of SrS:Eu and CaS:Eu.
The examples of phosphors described in U.S. Patent Application Publication No. 2004/0263074 include particles which are characterized as being capable of down-conversion, that is, after being stimulated (excitation) by relatively shorter wavelength light, they produce longer wavelength light (emission). The phosphor composition comprises at least one, typically at least two (or three, or four) types of phosphor particles, which each have their own emission characteristics. In an embodiment having at least two different types of phosphor particles, the first type of phosphor particle emits red light upon excitation, and the second type of phosphor particle emits green light upon excitation. For red emission, typical phosphor particles suitable for use in the phosphor composition may comprise a material selected from SrS:Eu2+; CaS:Eu2+; CaS:Eu2+,Mn2+; (Zn,Cd)S:Ag+; Mg4GeO5.5F:Mn4+; Y2O2S:Eu2+, ZnS:Mn2+, and other phosphor materials having emission spectra in the red region of the visible spectrum upon excitation. For green emission, typical phosphor particles suitable for use in the phosphor composition may comprise a material selected from SrGa2S4:Eu2+; ZnS:Cu,Al and other phosphor materials having emission spectra in the green region of the visible spectrum upon excitation. In some implementations, blue emitting phosphor particles may be included in the phosphor composition in addition to the red- and green-emitting phosphors; suitable blue emitting phosphor particles may comprise, e.g. BaMg2Al16O27:Eu2+,Mg or other phosphor materials having emission spectra in the blue region of the visible spectrum upon excitation. In other implementations, the phosphor composition may comprise a type of phosphor particles that is selected to produce yellow light upon excitation. For yellow emission, phosphor particles suitable for use in the phosphor composition may include a material selected from (Y,Gd)3Al5O12:Ce,Pr and other phosphor materials having emission spectra in the yellow region of the visible spectrum upon excitation.
Some suitable red-emitting phosphor particles may have a peak emission wavelength in the range of about 590 nm to about 650 nm. In particular embodiments, the phosphor particles have a peak emission wavelength in the range of about 620 nm to about 650 nm, typically in the range of about 625 nm to about 645 nm, more typically in the range of about 630 nm to about 640 nm. In other embodiments, the phosphor particles have a peak emission wavelength in the range of about 590 nm to about 625 nm, typically in the range of about 600 nm to about 620 nm. In yet other embodiments, the phosphor particles may emit light having a wavelength in the range of about 600 nm to about 650 nm, typically in the range of about 610 nm to about 640 nm, more typically in the range of about 610 nm to about 630 nm.
Some suitable green-emitting phosphor particles may have a peak emission wavelength in the range of about 520 nm to about 550 nm. In particular embodiments, the phosphor particles have a peak emission wavelength in the range of about 530 nm to about 550 nm, typically in the range of about 535 nm to about 545 nm. In other embodiments, the phosphor particles have a peak emission wavelength in the range of about 520 nm to about 535 nm. In yet other embodiments, the phosphor particles emit light having a wavelength in the range of about 520 nm to about 550 nm, typically in the range of about 535 nm to about 550 nm, or in the range of about 520 nm to about 535 nm.
Some suitable blue-emitting phosphor particles typically have a peak emission wavelength in the range of about 440 nm to about 490 nm. In particular embodiments, the phosphor particles have a peak emission wavelength in the range of about 450 nm to about 470 nm, typically in the range of about 455 nm to about 465 nm. In other embodiments, the phosphor particles have a peak emission wavelength in the range of about 440 nm to about 45.0 nm, typically in the range of about 435 nm to about 445 nm. In yet other embodiments, the phosphor particles emit light having a wavelength in the range of about 440 nm to about 480 nm, typically in the range of about 450 nm to about 470 nm.
Some suitable yellow-emitting phosphor particles typically have a peak emission wavelength in the range of about 560 nm to about 580 nm. In particular embodiments, the phosphor particles have a peak emission wavelength in the range of about 565 nm to about 575 nm. In other embodiments, the phosphor particles have a peak emission wavelength in the range of about 575 nm to about 585 nm. In yet other embodiments, the phosphor particles emit light having a wavelength in the range of about 560 nm to about 580 nm, typically in the range of about 565 nm to about 575 nm.
The exact wavelength range for each of the above described type of phosphor particles may be determined by selection from available sources of phosphors, desired color attributes of the light emitting device (e.g. the ‘correlated color temperature’ of the emitted white light), choice of the excitation light such as the excitation wavelength, and the like. Useful phosphor materials and other information may be found in Mueller-Mach et al., “High Power Phosphor-Converted Light Emitting Diodes Based on III-Nitrides”, IEEE J. Sel. Top. Quant. Elec. 8(2):339 (2002).
The examples of phosphors described in the published PCT Application No. PCT/US99/28279 include Ba2MgSi2O7:Eu2+; Ba2SiO4:Eu2+; and (Sr,Ca,Ba) (Al,Ga)2S4:Eu2+, where the element following the colon represents an activator. The notation (A,B,C) signifies (Ax,By,Cz) where o≦x≦1 and o≦y≦1 and O≦z≦1 and x+y+z=1. For example, (Sr,Ca,Ba) signifies (Srx,Cay,Baz) where o≦x≦1 and o≦y≦1 and O≦z≦1 and x+y+z=1. Typically, x, y, and z are all nonzero. The notation (A,B) signifies (Ax,By) where o≦x≦1 and o≦y≦1 x+y=1. Typically, x and y are both nonzero. Examples of green emitting phosphors may have peak emissions between about 500 nm and about 555 nm. For example, Ba2MgSi2O7:Eu2+ has a peak emission at about 495-505 nm, typically about 500 nm, Ba2SiO4: Eu2+ has a peak emission at about 500-510 nm, typically about 505 nm, and (Sr,Ca,Ba) (Al,Ga)2S4:Eu2+ has a peak emission at about 535-545 nm, typically about 540 nm.
The examples of phosphors described in U.S. Patent Application Publication No. 2001/0050371 include fluorescent materials that include a CaS phosphor activated by Eu, phosphors represented by AEu(1-x)LnxB2O8 where A is an element selected from the group consisting of Li, K, Na and Ag; Ln is an element selected from the group consisting of Y, La and Gd; and B is W or Mo; and x is number equal to or larger than 0, but smaller than 1. A CaS phosphor activated by Eu or a phorsphor of AEu(1-x)LnxB2O8 may be mixed with a base polymer to form a transparent resin. As an example, a red phosphor that emits red light may be CaS activated by Eu or a compound expressed by a general formula AEu(1-x)LnxB2O8. CaS activated by Eu is excited by light of 420 to 600 nm and emits light of 570 to 690 nm which peaks at 630 nm. AEu(1-x)LnxB2O8 is a phosphor which emits light near 614 nm by 5D0□7F2 transition of Eu3+ ions. Although an excitation wavelength and an emission wavelength differ depending on the kinds of elements A and B of the phosphor, the red phosphors can be excited by light near 470 nm (blue) and or 540 nm (green) and can emit light near 620 nm (red). When x is zero, the phosphor AEuB2O8 is formed and exhibits the highest emission intensity near 615 nm (red). AEu(1-x)LnxB2O8 (A=Li, K, Na, Ag; Ln=Y, La, Gd; B=W, Mo) may be obtained by mixing oxides, carbonate and the like of elements which constitute the phosphor at a desired stoichiometric ratio. In addition to the above red phosphors, a yttrium aluminate phosphor (so-called YAG) can be a stable oxide having a garnet structure in which Y-atoms of Y3Al5O12 are substituted by Gd at part of their positions, particularly a phosphor which is excited by blue light (400 to 530 nm) to emit light of yellow to green region centering 550 nm. Activating elements to be added to the yttrium aluminate phosphor include, for example, cerium, europium, manganese, samarium, terbium, tin, chromium, etc. For example, YxGd3-xAl5O12 activated by Ce may be used. In implementations, one, two or more kinds of such YAG phosphors may be mixed together to form a desired phosphor material.
The examples of phosphors described in U.S. Pat. No. 6,252,254 include YBO3:Ce3+,Tb3+; BaMgAl10O17:Eu2+,Mn2+; (Sr,Ca,Ba)(Al,Ga)2S4:Eu2+; and Y3Al5O12:Ce3+; and at least one of: Y2O2S:Eu3+,Bi3+; YVO4:Eu3+,Bi3+; SrS:Eu2+; SrY2S4:Eu2+; SrS:Eu2+,Ce3+,K+; (Ca,Sr)S:Eu2+; and CaLa2S4:Ce3+, where the element following the colon represents an activator. As an example, the SrS:Eu2+,Ce3+,K+ phosphor, when excited by blue light, emits a broadband spectrum including red light and green light. These phosphor compositions can be used to produce white light with pleasing characteristics, such as a color temperature of 3000-4100° K, a color rendering index of greater than 70, typically greater than 80, for example about 83-87, and a device luminous efficacy of about 10-20 lumens per watt of input electric power when blue LED is used as the excitation source.
The examples of phosphors described in U.S. Patent Application Publication No. 2002/0003233 include a single crystal Cerium-doped Yttrium-Aluminum-Garnet (Y3Al5O12:Ce3+) compound as a yellowish-light-emitting phosphor. Yttrium-Aluminum-Oxides which do not have garnet structures, such as monoklinic YalO and YalO-perovskite, may also be used as the host materials for the phosphors. Several lanthanides (Ln) may partly replace the Yttrium, such as in (Y,Ln)AlO, (Y,Ln)(Al,Ga)O. The lanthanide may be, for example Lutethium (Lu). These host materials may be doped with single dopants such as Cerium (Ce), Praseodymium (Pr), Holmium (Ho), Ytterbium (Yb), and Europium (Eu), or with double dopants such as (Ce,Pr), (Ce, Ho), and (Eu,Pr) to form various phosphors. Y3Al5O12:Ho3+, and Y3Al5O12:Pr3+ are examples of single crystal phosphor materials. In one embodiment, a phosphor listed above emits yellowish light by absorbing either bluish light or ultraviolet light having a wavelength that is shorter than or equal to about 460 nm. In one example, a YAG substrate doped with 4 mol % Cerium (Ce3+) can absorb light having a wavelength of about 410-460 nm and emit yellowish light having a peak wavelength of about 550-570 μm. any. Part of the Yttrium in YAG may be substituted by a lanthanide element such as Gadolinium (Gd). For example, a phosphor may be (Y0.75Gd0.25) AG:Ce.
The examples of phosphors described in European Patent Application No. 1,150,361 include a resin comprising a phosphor selected from the phosphor family chemically identified as (Sr,Ca,Ba)S:Eu2+. One phosphor selected from this family is strontium sulfide doped with europium, which is chemically defined as SrS:Eu2+ and has a peak emission at 610 nm. Rather than using phosphor-converting resins, dyes or epoxies, other types of phosphor converting elements may also be used, including phosphor-converting thin films, phosphor-converting substrates, or various combinations of these elements.
The examples of phosphors described in U.S. Patent Application Publication No. 2002/0145685 include a red phosphor SrS:Eu2+ and a green phosphor SrGa2S4:Eu2+. These phosphors are excitable by the 460 nm blue light.
The examples of phosphors described in U.S. Patent Application Publication No. 2005/0001225 include rare-earth element doped oxide nitride phosphor or cerium ion doped lanthanum silicon nitride phosphor. A rare-earth element doped oxide nitride in the following examples is a crystalline material, not including a glass material such as oxynitride glass. However, it may include a small amount of glass phase (e.g., less than 5%). A cerium ion doped lanthanum silicon nitride in the following examples is a crystalline material, not including a glass material.
One example of a first phosphor is single-phase α-sialon phosphor that is represented by: MexSi12-(m+n)Al(m+n)OnN16-n:Re1yRe2z. Part or all of metal (Me) (Me is one or more of Li, Ca, Mg, Y and lanthanide metals except for La and Ce) dissolved into the α-sialon is replaced by lanthanide metal (Re1) (Re1 is one or more of Ce, Pr, Eu, Tb, Yb and Er) as luminescence center or lanthanide metal (Re1) and lanthanide metal (Re2) (Re2 is Dy) co-activator. In this case, Me may be one or more of Ca, Y and lanthanide metals except for La and Ce. In some implementations, Me may be Ca or Nd. The lanthanide metal (Re1) used for replacing may be Ce, Eu or Yb. In case of using two kinds of metals for replacing, for example, a combination of Eu and Er may be used. In case of using three kinds of metals for replacing, for example, a combination of Eu, Er and Yb may be used.
Also, the metal (Me) may be replaced by lanthanide metal Re1 and lanthanide metal Re2 as co-activator. The lanthanide metal Re2 is dysprosium (Dy). In this case, the lanthanide metal Re1 may be Eu. Meanwhile, if part or all of metal (Me) replaced by one or more of Ce, Pr, Eu, Tb. Yb and Er (lanthanide metal (Re1)), or one or more of Ce, Pr, Eu, Tb, Yb and Er (lanthanide metal (Me) (Re1)) and Dy (lanthanide metal (Re2)), then the metal is not necessarily added and may be replaced by another metal.
A-sialon (α-sialon) has a higher nitrogen content than oxynitride glass and is represented by: NxSi12-(m−n)Al(m+n−)OnN16-n where x is a value obtained dividing (m) by a valence of metal (M). Meanwhile, oxynitride glass is as described in prior art 3, such a phosphor that serves to shift the position of excitation/emission peak of conventional oxide system phosphors to the longer wavelength side by replacing oxygen atom surrounding the rare-metal element as luminescence center by nitrogen atom to relax the influence of surrounding atoms to electron of rare-metal element, and that has an excitation spectrum extending until visible region (≦500 μm).
Also, in the single-phase α-sialon phosphor, the metal (Me) is dissolved in the range of, at the minimum, one per three unit cells of α-sialon including four mass weights of (Si, Al)3(N,O)4 to, at the maximum, one per one unit cell thereof. The solid solubility limit is generally, in case of bivalent metal (Me), 0.6<m<3.0 and 0≦n<1.5 in the above formula and, in case of trivalent metal (Me), 0.9<m<4.5 and 0≦n<1.5. It is estimated that, in a region except for those regions, single-phase α-sialon phosphor is not obtained.
The interionic distance of lanthanide metal Re1 as luminescence center to replace part or all of metal (Me) and to serve as activator is about 5 angstroms at the minimum. It is significantly greater than 3 to 4 angstroms in phosphor known thus far. Therefore, it can prevent a significant reduction in emission intensity due to concentration quenching generated when a high concentration of lanthanide metal as luminescence center is included in matrix material.
Further in the single-phase α-sialon phosphor, the metal (Me) is replaced by lanthanide metal (Re2) as α-activator as well as lanthanide metal (Re1) as luminescence center. It is assumed that lanthanide metal (Re2) has two co-activation effects. One is sensitizer function and the other is to newly generate a carrier trap level to develop or improve the long persistence or to improve the thermal luminescence. Since the lanthanide metal Re2 is co-activator, it is suitable that the replacement amount thereof is generally 0.0≦z<0.1 in the earlier formula.
The single-phase α-sialon phosphor has α-sialon as a matrix material, and is essentially different in composition and crystal structure from a phosphor having β-sialon as matrix material.
Namely, β-sialon is represented by: Si6-zAlzOzN8-z (0<z<0.2), and it is solid solution of β-type silicon nitride where part of Si sites is replaced by Al and part of N sites is replaced by O. In contrast, α-sialon is represented by: MexSi12-(m+n)Al(m+n)OnN16-n, and it is a solid solution of α-type silicon nitride, where part of Si—N bonds is replaced by Al—N bond and a specific metal (Me) (Me is one or more of Li, Ca, Mg, Y and lanthanide metals except for La and Ce) invades between lattices and is dissolved therein. Thus, both are different in state of solid solution and, therefore, the β-sialon has a high oxygen content and the α-sialon has a high nitrogen content. So, if a phosphor is synthesized using β-sialon as matrix material and adding one or more of rare-earth oxides of Ce, Pr, Eu, Tb, Yb and Er as luminescence center, it becomes a mixed material that has a compound including a rare-earth metal between β-sialon particles since the β-sialon does not dissolve metal.
In contrast, if α-sialon is used as matrix material, the metal (Me) (Me is one or more of Li, Ca, Mg, Y and lanthanide metals except for La and Ce) is taken and dissolved in the crystal structure and the metal (Me) is replaced by rare-earth metal, Ce, Pr, Eu, Tb, Yb and Er as luminescence center. Therefore, the oxide nitride phosphor composed of single-phase α-sialon structure can be obtained.
Accordingly, the composition and crystal structure of phosphor drastically changes by whether to use β-sialon or α-sialon as matrix material. This is reflected in emission characteristics of phosphor.
In case of using β-sialon as matrix material, for example, a phosphor that is synthesized adding Er oxide to β-sialon radiates a blue luminescent light (410-440 nm). In α-sialon, as described later, rare-earth element doped oxide nitride phosphor radiates orange to red light (570-590 nm) due to the activation of Er. Viewing from this phenomenon it is assumed that Er is taken in the crystal structure of α-sialon and, thereby, Er is influenced by nitrogen atom composing the crystal and, therefore, the elongation of light source wavelength, which is very difficult to realize in phosphor with oxide as matrix material, can be easily generated.
In case of using α-sialon as matrix material, the rare-earth element doped oxide nitride phosphor also has the advantages of matrix material, α-sialon. Namely, α-sialon has excellent thermal and mechanical properties and can prevent the thermal relaxation phenomenon that causes a loss in excitation energy. Therefore, in the rare-earth element doped oxide nitride phosphor, a ratio of reduction in emission intensity according to rise of temperature becomes small. Thus, the temperature range available can be broadened as compared to the conventional phosphor.
Furthermore, α-sialon has an excellent chemical stability. Therefore, the phosphor has an excellent heat resistance. The rare-earth element doped oxide nitride phosphor can be excited by ultraviolet rays to X-rays further electron beam, according to O/N ratio in its composition, selection of lanthanide metal Re1 to replace metal (Me), and existence of lanthanide metal Re2 as α-activator.
Especially, of rare-earth element doped oxide nitride phosphor, in MexSi9.75Al2.25O0.75N15.25:Re1yRe2z (m=1.5, n=0.75), one that satisfies 0.3<x+y<0.75 and 0.01<y+z<0.7 (where y>0.01, 0.0≦z<0.1) or 0.3<x+y+z<1.5, 0.01<y<0.7 and 0.0≦z<0.1, and metal (Me) is Ca offers an excellent emission characteristic and can have great potential in applications not only as ultraviolet-visible light excitation phosphor but also as electron beam excitation phosphor.
Different from the above first phosphor, an example of a second phosphor is a rare-earth element doped oxide nitride phosphor that contains α-sialon as main component (hereinafter referred to as mixture α-sialon phosphor). This second phosphor includes α-sialon, which dissolves a rare-earth element allowing an increase in brightness of a white LED using blue LED chip as light source, β-sialon, and unreacted silicon nitride. As the result of researching a composition with high emission efficiency, a mixture material with a property equal to single-phase α-sialon phosphor is found that is composed of α-sialon that part of Ca site in α-sialon stabilized by Ca is replaced by one or more of rare-earth metal (M) (where M is Ce, Pr, Eu, Tb, Yb or Er), β-sialon and unreacted silicon nitride. In some implementations, M is preferably Ce, Eu or Yb and further preferably Ce or Eu.
The mixture α-sialon phosphor can be produced adding less rare-earth element than the single-phase α-sialon phosphor. Thus, the material cost can be reduced. Further, since the mixture α-sialon phosphor also has α-sialon as matrix material like the single-phase α-sialon phosphor, it can have the advantages of matrix material α-sialon, i.e. good chemical, mechanical and thermal properties. Thus, it offers a stable and long-lifetime phosphor material. Due to these properties, it can suppress thermal relaxation phenomenon causing a loss in excitation energy. Therefore, in α-sialon with dissolved rare-earth element as well as Ca in this embodiment, a ratio of reduction in emission intensity according to rise of temperature becomes small. Thus, the temperature range available can be broadened as compared to the conventional phosphor.
Furthermore, the mixture α-sialon phosphor can be excited by ultraviolet rays to X-rays further electron beam, according to O/N ratio in its composition and selection of metal (M).
The mixture α-sialon phosphor offers a material that has an emission property equal to the single-phase α-sialon phosphor even when reducing the amount of rare-earth metal added. In order to stabilize the α-sialon structure, it is necessary to dissolve more than a certain amount of element. When amounts of Ca and trivalent metal dissolved are given x and y, respectively, a value of (x+y) is needed to be greater than 0.3 in thermodynamic equilibrium.
The mixture α-sialon phosphor includes an organ with β-sialon and unreacted silicon nitride remained other than single-phase α-sialon phosphor because of less addition amount and not reaching the thermodynamic equilibrium.
The amount of added metal in the mixture α-sialon phosphor is in the range of 0.05<(x+y)<0.3, 0.02<x<0.27 and 0.03<y<0.3 in chemical composition of powder. If the amount of added metal is less than the lower limit, the amount of α-sialon lowers and the emission intensity lowers. If the amount of added metal is greater than the upper limit, only α-sialon remains. Therefore, the object of high brightness can be completed. In the range defined above, the mixture α-sialon phosphor can be obtained that is composed of: α-sialon of 40 weight % or more and 90 weight % or less; β-sialon of 5 weight % or more and 40 weight % or less; and unreacted silicon nitride of 5 weight % or more and 30 weight % or less. The reason why the emission intensity is high even with the unreacted silicon nitride included is that α-sialon epitaxially grows on unreacted silicon nitride and its surface portion mainly responds to excitation light to offer an emission property substantially equal to only α-sialon.
The range may be 0.15<(x+y)<0.3, 0.10<x<0.25 and 0.05<y<0.15. In this range, the mixture α-sialon phosphor can be obtained that is composed of: α-sialon of 50 weight % or more and 90 weight % or less; β-sialon of 5 weight % or more and 30 weight % or less; and unreacted silicon nitride of 5 weight % or more and 20 weight % or less.
The mixture α-sialon phosphor can be obtained by, e.g., heating Si3N4—M2O3—CaO—AlN—Al2O3 system mixed powder at 1650 to 1900° C. in inert gas atmosphere to get a sintered body, then powdering it. Since CaO is so instable that it easily reacts with moisture vapor in the air, it is generally obtained by adding in the form of calcium carbonate or calcium hydroxide, then making it CaO in the process of heating at high temperature.
The chemical composition of mixture α-sialon phosphor can be defined using the composition range of M-α-sialon, Ca-α-sialon and β-sialon. Namely, in the range of three composition lines of Si3N4-a(M2O3.9AlN), Si3N4-b(CaO.3AlN) and Si3N4-c(AlN.Al2O3), it is defined 4×10−3<a<4×10−2, 8×10−3<b<8×10−2 and 10−2<c<8×10−1.
An example of a third phosphor is a cerium ion doped lanthanum silicon nitride phosphor: La1-xSi3N5:xCe (doping amount x is 0<x<1), where lanthanum site is replaced in solid dissolution by cerium ion activator. If the doping amount is 0.1<x<0.5, it is ultraviolet light excitation phosphor and, if the doping amount is 0.0<x<0.2, it is electron beam excitation phosphor.
Lanthanum silicon nitride (LaSi3N5) has an excellent thermal stability and serves to suppress the thermal relaxation phenomenon in the process of phosphor emission. Therefore, a loss in excitation energy can be reduced and a ratio of reduction in emission intensity according to rise of temperature becomes small. Thus, in the cerium ion doped lanthanum silicon nitride phosphor, the temperature range available can be broadened as compared to the conventional phosphor. Also, the lanthanum silicon nitride (Lasi3N5) has excellent chemical stability and is light resistance.
The cerium ion doped lanthanum silicon nitride phosphor satisfies a blue chromaticity value and has excellent thermal stability, mechanical property and chemical stability. Therefore, it can have great potential in applications for fluorescent character display tube (VFD), field emission display (FED) etc. that may be used in severe environment.
The examples of phosphors described in U.S. Pat. No. 5,998,925 include a garnet fluorescent material comprising 1) at least one element selected from the group consisting of Y, Lu, Sc, La, Gd and Sm, and 2) at least one element selected from the group consisting of Al, Ga and In, and being activated with cerium. Y3Al5O12:Ce and Gd3In5O12:Ce are two examples. The presence of Y and Al enables a phosphoer to increase the luminance. For example, in a yttrium-aluminum-garnet fluorescent material, part of Al may be substituted by Ga so that the proportion of Ga:Al is within the range from 1:1 to 4:6 and part of Y is substituted by Gd so that the proportion of Y:Gd is within the range from 4:1 to 2:3. Other examples of phosphor include (Re1-rSmr)3(Al1-sGas)5O12:Ce, where 0≦r<1 and 0≦s≦1 and Re is at least one selected from Y and Gd, (Y1-p-q-rGdpCeqSmr)3(Al1-sGas)tO12 as the phosphor, where 0≦p≦0.8, 0.003≦q≦0.2, 0.0003≦r≦0.08 and 0≦s≦1. In some implementations, a phosphor may include two or more yttrium-aluminum-garnet fluorescent materials, activated with cerium, of different compositions including Y and Al to control the emission spectrum of the phosphor. In other implementations, a phosphor may include a first fluorescent material represented by general formula Y3(Al1-sGas)5O12:Ce and a second fluorescent material represented by the formula Re3Al5O12:Ce, where 0≦s≦1 and Re is at least one selected from Y, Ga and La. In addition, two or more fluorescent materials of different compositions represented by a general formula (Re1-rSmr)3(Al1-sGas)5O12:Ce, where 0≦r<1 and 0≦s≦1 and Re is at least one selected from Y and Gd may be used as the phosphor in order to control the emitted light to a desired wavelength.
The examples of phosphors described in U.S. Pat. No. 6,765,237 include phosphors that absorb UV light from about 380 to about 420 nm and emit visible light of different colors. For example, a phosphor blend may include a first phosphor comprising BaMg2Al16O27:Eu2+(BAM) and a second phosphor comprising (Tb.1-x-yAxREy)3DzO12(TAG), where A is a member selected from the group consisting of Y, La, Gd, and Sm; RE is a member selected from the group consisting of Ce, Pr, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, and Lu; D is a member selected from the group consisting of Al, Ga, and In; x is in the range from 0 to about 0.5, y is in the range from about 0 to about 0.2, and z is in the range from about 4 to about 5. As another example, a phosphor blend may include a first phosphor comprising Tb3Al4.9O12:Ce and a second phosphor selected from the group consisting of BaMg2Al16O27:Eu2+ (BAM) and (Sr,Ba,Ca,Mg)5(PO4)3Cl:Eu2+.
The phosphors described in U.S. Patent Application Publication No. 2004/0227465 include various phosphor compositions as follows.
1. A rare earth element activated complex halide phosphor represented by the formula: BaF2.a BaX2.bMgF2.cBeF2.dMeIIF2:eLn, where X is at least one halogen selected from the group consisting of chlorine, bromine and iodine; MeII is at least one divalent metal selected from the group consisting of: calcium and strontium; Ln is at least one rare earth element selected from the group consisting of: divalent europium (Eu2+), cerium (Ce3+) and terbium (Tb3+), and a is in the range between 0.90 and 1.05, b is in the range of 0 to 1.2; c is in the range of between 0 and 1.2, and d is defined by the sum of c+d being in the range of between 0 and 1.2, and BeF2 is present in an amount sufficient to effect a phosphor exhibiting a higher luminance than said phosphor absent BeF2 when stimulated by light of a wavelength ranging from 450 to 800 nm after exposure to X-rays. See U.S. Pat. No. 4,512,911 for additional details.
2. A cerium activated rare earth halophosphate phosphor having the formula: LnPO4.aLnX3:xCe3+ in which Ln is at least one rare earth element selected from the group consisting of Y, La, Gd and Lu; X is at least one halogen selected from the group consisting of F, Cl, Br and I; and a and x are numbers satisfying the conditions of 0.1<a<10.0 and 0<x<0.2, respectively and exhibiting a higher stimulated emission upon excitation with a He—Ne laser of a wavelength 632.8 nm after exposure to X-rays at 80 KVp, than the phosphor wherein a is less than 0.1. See U.S. Pat. No. 4,661,419 for additional details.
3. A mixed single-phase strontium and lanthanide oxide with a magnetolead type crystalline structure having the formula (I): SrxLn1y1Ln2y2Ln3y3MzAaBbO19-k(I) in which Ln1 represents at least one trivalent element selected from lanthanum, gadolinium and yttrium; Ln2 represents at least one trivalent element selected from neodymium, praseodymium, erbium, holmium and thulium; Ln3 represents an element selected from bivalent europium or trivalent cerium with retention of electric neutrality by virtue of oxygen holes; M represents at least one bivalent metal selected from magnesium, manganese, and zinc; A represents at least one trivalent metal selected from aluminum and gallium; B represents at least one trivalent transition metal selected from chromium and titanium; x, y1, y2, y3, z, a, b and k represent numbers so that 0<x<1, 0<y1<1, 0<y2<1, 0<y3<1, 0<z<1, 10.5<a<12, 0<b<0.5 and 0<k<1 provided that 0<x+y1+y2+y3<1 and that 11<z+a+b<12. See U.S. Pat. No. 5,140,604 for additional details.
4. A divalent europium activated alkaline earth metal halide phosphor having the formula: MIIX2.aMIIX′2.bSiO:xEu2+ in which MII is at least one alkaline earth metal selected from the group consisting of Ba, Sr and Ca; each of X and X′ is at least one halogen selected from the group consisting of Cl, Br and I, and X is not the same as X′; a and x are numbers satisfying the conditions of 0.1<a<10.0 and 0<x<0.2, respectively; and b is a number satisfying the condition of 0<b<3 X10−2. See U.S. Pat. No. 5,198,679 for additional details.
5. A bright, short wavelength blue-violet phosphor for electro luminescent displays comprising an alkaline-based halide as a host material and a rare earth as a dopant. See U.S. Pat. No. 5,602,445. The host alkaline chloride can be chosen from the group II alkaline elements, particularly SrCl2 or CaCl2, which, with a europium or cerium rare earth dopant, electroluminesces at a peak wavelength of 404 and 367 nanometers respectively. The resulting emissions have CIE chromaticity coordinates which lie at the boundary of the visible range for the human eye thereby allowing a greater range of colors for full color flat panel electroluminescent displays.
6. An inorganic thin film electroluminescent device, comprising an inorganic light emission layer, a pair of electrodes and a pair of insulating layers, at least one of the electrodes being optically transparent, the light emission layer being positioned between the pair of insulating layers, each insulating layer being formed on an opposite side of the light emission layer, the pair of insulating layers being positioned between a light emission layer and the pair of electrodes, the light emission layer consisting essentially of inorganic material comprising a matrix of lanthanum fluoride doped with at least one member selected from the group consisting of: rare earth element metals and compounds thereof. See U.S. Pat. No. 5,648,181 for additional details.
7. A radiographic phosphor screen comprising a support and, coated on the support, at least one layer forming a luminescent portion and an overcoat layer, the luminescent portion and overcoat layer including a binder that is transparent to X-radiation and emitted light and said luminescent portion including phosphor particles in a weight ratio of phosphor particles to binder of 7:1 to 25:1. The phosphor comprises oxygen and a combination of species characterized by the relationship: (Ba1-qMq)(Hf1-z-eZrzMge): yT wherein M is selected from the group consisting of Ca and Sr and combinations thereof; T is Cu; q is from 0 to 0.15; z is from 0 to 1; e is from 0 to 0.10; z+e is from 0 to 1; an y is from 1×10−6 to 0.02. See U.S. Pat. No. 5,698,857 for additional details.
8. A garnet fluorescent material comprising: 1) at least one element selected from the group consisting of Y, Lu, Se, La, Gd and Sm; and 2) at least one element selected from the group consisting of Al, Ga and In, and being activated with cerium. One example is cerium-doped yttrium aluminum garnet Y3Al5O12:Ce (YAG:Ce) and its derivative phosphors. See U.S. Pat. No. 5,998,925 for additional details.
9. A wavelength-converting casting composition, for converting a wavelength of ultraviolet, blue or green light emitted by an electroluminescent component, comprising: a) a transparent epoxy casting resin; b) an inorganic luminous substance pigment powder dispersed in the transparent epoxy resin, the pigment powder comprising luminous substance pigments from a phosphorus group having the general formula: A3B5X12:M, where A is an element selected from the group consisting of Y, Ca, Sr; B is an element selected from the group consisting of Al, Ga, Si; X is an element selected from the group consisting of O and S; and M is an element selected from the group consisting of Ce and Tb. The luminous substance pigments have grain sizes <20 μm and a mean grain diameter d50<5 μm. See U.S. Pat. No. 6,066,861 for additional details.
10. Phosphors Ba2(Mg,Zn)Si2O7:Eu2+ and (Ba1-X-Y-Z,CaX,SrY,EuZ)2(Mg1-w,Znw)Si2O7, where X+Y+Z=1; Z>0; and 0.05<W<0.50 in some implementations. In other implementations, X+Y+Z=1; 0.01≦Z≦0.1; and 0.1≦W<0.50. X and Y can be zero or a non-zero number. Examples of UV-excitable phosphors for emitting green, red, and blue colors are Ca8Mg(SiO4)4Cl2:Eu2+, Mn2+; Y2O3:Eu3+, Bi3+; and Ba2(Sr,Ba,Ca)5(PO4)3Cl: Eu2+ (or BaMg2Al16O27: Eu2+); respectively. See U.S. Pat. No. 6,255,670 for additional details.
The U.S. Patent Application Publication No. 2004/0227465 also discloses phosphors represented by SrxBayCazSiO4:Eu2+ in which x, y, and z are each independently any value between 0 and 2, including 0 and 2. In some implementations, divalent Eu, which serves as an activator, is present in any amount between 0.0001% and about 5% in mole percent based on the total molar weight of said composition. Thus, the activator, Eu, may be present in any amount between 0.0001% and 5.00% in mole percent based on the total molar weight of the composition, including every thousandth percentage therebetween. In other implementations, the parameters x, y and z are 0.5≦x≦1.5; 0≦y≦0.5; and 0.5≦z≦1.5 in the above formula. In yet other implementations, the parameters x, y and z are 1.5≦x≦2.5; 0≦y≦0.5; and 0≦z≦0.5 in the above formula. The parameters x, y and z may also be 1.0≦x≦2.0; 0≦y≦1.0; and 0≦z≦0.5 in the above formula.
The above phosphor SrxBayCazSiO4:Eu2+ may further include at least one additional element selected from the group consisting of: Ce, Mn, Ti, Pb, and Sn. In some implementations, such an additional element is present in the phosphor in any amount between 0.0001% and 5.00% in mole percent based upon the total molar weight of the phosphor.
The examples of phosphors described in U.S. Patent Application Publication No. 2005/0023962 include ZnSxSey:Cu,A in which x and y are each independently any value between 0 and 1 and A is at least one of Ag, Al, Ce, Tb, Cl, I, Mg, Mn. The monovalent Cu, which serves as the main activator, may be present in any amount between 0.0001% and about 5% in mole percent based on the total molar weight of said composition. Thus, the activator, Cu, may be present in any amount between 0.0001% and 5.00% in mole percent based on the total molar weight of the composition, including every thousandth percentage therebetween. In some implementations, the parameters x, y and z are 0.5≦x≦1 and 0≦y≦0.5 in the above formula. In other implementations, the parameters x, y and z are 0≦x≦0.5 and 0≦y≦0.5 in the above formula. The parameters x, y and z may also be 0≦x≦0.5 and 0.5≦y≦1.0 in the above formula.
The examples of phosphors described in U.S. Patent Application Publication No. 2005/023963 include thioselenide and/or selenide-based fluorescent materials which are capable of absorbing with high efficiency blue, violet, or ultraviolet (UV) light and emitting light of a wavelength longer than that absorbed from the light source. Such phosphor materials may be manufactured to emit broad color spectra that can be tuned from blue to green to yellow and red emissions. Two or more phosphors may be mixed in order to achieve a specific, desired white color performance. One example is. MA2(SxSey)4:B in which x and y are each independently any value between about 0.01 and about 1; M is at least one of Be, Mg, Ca, Sr, Ba, Zn; and A is at least one of Al, Ga, In, Y, La, and Gd; and the activator B is at least one of Eu, Ce, Cu, Ag, Al, Tb, Cl, F, Br, I, Pr, Na, K, Mg, and Mn. The divalent Eu, which can serve as the main activator, may be present in any amount between 0.0001% and about 10% in mole percent based on the total molar weight of said composition. Thus, the activator, Eu, may be present in any amount between 0.0001% and 10.00% in mole percent based on the total molar weight of the composition, including every thousandth percentage therebetween. In some implementations, the parameters x, y, and z are 0.5≦x≦1 and 0≦y≦0.5 in the above formula. In other implementations, the parameter x, y and z are 0≦x≦0.5 and 0.5≦y≦1.0 in the above formula. In yet other implementations, x is about 0 and y is about 1 in the above formula, or x is about 1 and y is about 0 in the above formula.
Another example is M2A4(SxSey)7:B in which x and y are each independently any value between about 0.01 and about 1, M is at least one of Be, Mg, Ca, Sr, Ba, Zn; and A is at least one of Al, Ga, In, Y, La, and Gd; and B is at least one of Eu, Ce, Cu, Ag, Al, Tb, Cl, Br, F, I, Pr, K, Na, Mg, and Mn. The divalent Eu, which can serve as the main activator, may be present in any amount between 0.0001% and about 10% in mole percent based on the total molar weight of said composition. Thus, the activator, Eu, may be present in any amount between 0.0001% and 10.00% in mole percent based on the total molar weight of the composition, including every thousandth percentage there between. In some implementations, the parameters x and y are 0.5≦x≦1 and 0≦y≦0.5 in the above formula. In other implementations, the parameters x and y are 0≦x≦0.5 and 0≦y≦0.5 in the above formula. In yet other implementations, x is about 1 and y is about 0 in the above formula, or x is about 0 and y=1 in the above formula, or 0≦x≦0.5 and 0.5≦y≦1.0 in the above formula, or x is about 0.75 and y is about 0.25 in the above formula.
Yet another example described in U.S. Patent Application Publication No. 2005/023963 is (M1)m(M2)nA2(SxSey)4:B in which: M1 comprises an element selected from the group consisting of: Be, Mg, Ca, Sr, Ba, Zn; M2 comprises an element selected from the group consisting of: Be, Mg, Ca, Sr, Ba, Zn; A comprises one or more elements selected from the group consisting of: Al, Ga, In, Y, La, and Gd; and B comprises one or more elements selected from the group consisting of: Eu, Ce, Cu, Ag, Al, Tb, Cl, Br, F, I, Mg, Pr, K, Na, and Mn. B may be present in any amount between 0.0001% and about 10% in mole percent based on the total molar weight of said composition, and wherein x and y are each independently any value between 0 and 1, subject to the provisos that the sum of x and y is equal to any number in the range of between about 0.75 and about 1.25, the sum of m and n is about 1, and M1 is different than M2. In some implementations, the parameters x and y are 0.5≦x≦1 and 0≦y≦0.5 in the above formula. In other implementations, the parameters x and y are 0≦x≦0.5 and 0≦y≦0.5, or 0≦x≦0.5 and 0.5≦y≦1.0, or x is about 0.75 and y is about 0.25, or x is about 0 and y is about 1, or x is about 1 and y is about 0 in the above formula.
Yet another example described in U.S. Patent Application Publication No. 2005/023963 is: (M1)m(M2)nA4(SxSey)7:B in which M1 comprises an element selected from the group consisting of: Be, Mg, Ca, Sr, Ba, Zn; M2 comprises an element selected from the group consisting of: Be, Mg, Ca, Sr, Ba, Zn; A comprises one or more elements selected from the group consisting of: Al, Ga, In, Y, La, and Gd; and B comprises one or more elements selected from the group consisting of: Eu, Ce, Cu, Ag, Al, Th, Cl, Br, F, I, Mg, Pr, K, Na, and Mn. B may be present in any amount between 0.0001% and about 10% in mole percent based on the total molar weight of said composition, and wherein x and y are each independently any value between 0 and 1, subject to the provisos that the sum of x and y is equal to any number in the range of between about 0.75 and about 1.25, the sum of m and n is about 2, and M1 is different than M2. In some implementations, the parameters x and y are 0.5≦x≦1 and 0≦y≦0.5 in the above formula. In other implementations, the parameters are 0≦x≦0.5 and 0≦y≦0.5, or 0≦x≦0.5 and 0.5≦y≦1.0, or x is about 0.75 and y is about 0.25, or x is about 0 and y is about 1, or x is about 1 and y is about 0 in the above formula.
In the above examples, the color generation is based on mixing of three primary colors of red, green, and blue. The described devices, systems, and techniques, however, may use mixing of four or more colors to generate the desired colors. For example, four different colors may be used. Accordingly, the screens shown in
A phosphor screen, which may be used as either a projection screen as shown in
1. Painting
The painting techniques apply luminescent paints on a substrate, such as fluorescent, phosphorescent and self-luminous painting materials. Paints can be organic or inorganic in nature and are used with a vehicle such as lacquers or oils. Paints can be applied with a brush, roller or a spraying device. Stencils may be used to obtain detailed spatial patterns. Paints can also be applied via off-set printing methods. These fluorescence and phosphorescent paints can be excited via IR, visible or UV radiation. In the self luminous paints the source of the excitation is a radioactive material (ex. Radium) mixed with the paint.
2. Settling by Gravity
Settling is a well known method and is documented in the literature. See, e.g., Pringsheim & Vogel, Luminescence of Liquids and Solids, Interscience Publishers, 1946, NY, pp 144 & 145; Hopkinson R. G., An Examination of Cathode Ray tube characteristics, Journal of the Institute of Electrical Engineers, Vol. 13, Part IIIa, No. 5 1946, pp. 779-794; Donofrio & Rehkopf, Screen Weight Optimization, Journal of the Electrochemical Society, Vol. 126, No. 9, September 1979, pp. 1563-1567; and Technical Information Booklet CM-9045, Method of Settling Phosphor Slides, GTE Sylvania, 3/82. For example, settling of phosphor slides may be achieved with a mixture of phosphor, a 1% barium acetate solution (in water), PS-6 potassium silicate and deionized water in a settling chamber. One recipe is to add 34 ml of the 1% barium acetate to the settling chamber. N. Yocom in the 1996 SID Seminar on Phosphor Screening discussed nine steps for settling and aluminizing a phosphor screen which are 1. settle phosphor on a face plate, 2. a liquid cushion is decanted and siphoned off, 3. dry the settled screen, 4. bake the screen, 5. rewet the screen, 6. apply a filming material on top of water, 7. remove water, 8. evacuate and evaporate the aluminum layer, 9. bake the screen.
3. Slurry
The slurry methods use a phosphor-containing slurry to form a phosphor layer over a screen surface. See, e.g., Tatayama, Yamazaki, Kato & Tashima, European Patent Application #86302192.9, filed Mar. 25, 1986 by Sony. One of his recipes is to use 100 g of phosphor, 0.6 g of Aerosil, with 5 g of PVA and 0.5 g of ADC (ammonium dichromate) and 100 g of water to form the slurry. This slurry is then deposited near the center of the face of a CRT screen panel and the panel is rotated and tilted to spread the slurry over the inside of the face plate. A cascaded slurry system may be used an aging effect where the silicate concentration is set to be higher on the glass substrate side than that on the electron gun side.
4. Dusting
Various dusting methods are known for forming phosphor screens. Hopkinson R. G. in “An Examination of Cathode Ray tube characteristics,” Journal of the Institute of Electrical Engineers, Vol. 13, Part IIIa, No. 5 1946, pp. 779-794 describes a dusting method where the phosphor is sprayed into a wet or dry binder. In another implementation, dusting can be done by allowing the phosphor to fall on or to be projected on a prepared surface. In yet another implementation of the dusting approach, the phosphor material may be agitated through a sieve or muslin gauze upon the screen plate coated with a suitable binder such as sodium silicate. The U.S. Pat. No. 3,025,161 entitled “Method of Forming Patterns” and issued Mar. 13, 1962 discloses a dusting method where the phosphor is dusted more vigorously via a dry powder spray system onto a wet photo-resist prior to exposure. In addition, phosphors are dusted on photo-tacky, coated dry surface and are exposed UV to allow the coating to become tacky. This tacky nature of the surface coating causes the phosphor in the exposed areas to be attached to the surface. See, Nonogaki, Tomita, Nishizawa, Akagi & Kohasji, “Dry Process for Phosphor Screen Fabrication of Multicolored Cathode Ray Tubes,” Research & Development in Japan, 1984, pp. 50-55.
5. Settling with Compression
Phosphor screens can also be made by settling the phosphors with compression. See, e.g., Oki K. & Ozawa L., A phosphor screen for high-resolution CRTs, Journal of the SID, Vol. 3, No. 2, September 1995, pp. 51-57 which describes settling with normal sedimentation techniques and a use of a mechanical press machine to reduce the voids in the screen for high resolution uses.
6. Thin Film Screens Evaporation or Sputtering
High resolution screens can be made by evaporating or sputtering the phosphor on the substrate. For example, magnetron sputtering of ZnGa2O4 onto BaTiO3 ceramic sheets have been used in thin film Electro-luminescent devices. Vacuum evaporation methods have been used to deposit a thin layer of phosphor on a substrate such as a SrS:Ce, Cl, Ag, Mn layer.
7. Screen Printing
Phosphor screens can also be made by screen printing techniques. In some implementations, a tight but spring-like cloth or metal mesh is used with areas blocked by a lacquer and aligned above a substrate to be coated. The slurry mix is then mechanically pressed through the selected areas of the mesh on to the substrate and the mesh springs back to its original position after the phosphor paste is applied. By photographic printing of patterns on a mesh, very fine patterns can be screen printed. In 1992 Morikawa et al discussed a method to achieve a smoother and better aging screen using a printing method plus screen compression. This compression method allows the manufacturer to achieve higher packing densities. See, Morikawa, Seko, Kamogawa & Shimojo, Study to Improve Flood Beam CRT for Giant Screen Display, Japan Display '92, pp 385-388.
8. Pulsed Laser Deposition
Laser pulses can be directed to target materials and deposit the target materials on a screen. Greer et al in 1994 reported a Pulsed Laser Deposition (PLD) of phosphor screens used in helmet mounted displays (HMD). See, Greer, J. A. et al., P-53 Thin Film Phosphors Prepared by Pulsed—Laser Deposition, SID 94 Digest, pp. 827-830. A rastered laser with a wavelength of 248 nm was used to scan targets of Yttrium Aluminum Gallium Garnet phosphors and to deposit these materials on to sapphire substrates by ablation. A screen growth rate of one micron per hour and screens of a thickness up to 8 microns were reported.
9. Centrifugal Deposition
A phosphor suspension in a solution can be deposited on a screen by using a centrifugal action. See, e.g., Mezner, L. Z., Zumer, M., Nemanic, V., Centrifugal Settling of High Resolution 1-in CRT Screens, SID Digest 1994, pp 520-522. CRT screens have been made by this method where a stable phosphor suspension is made with a fine grain (less than 5 micron particle size) phosphor, a binder, electrolyte and in some cases a dispersing agent. In some implementations, the settling in the centrifuge may be set at 3000 rpm for 2 minutes to 4000 rpm for 3 minutes. Screens of optimum screen weight of about 0.6 mg/cm2 for 5 KV electrons was found using P20 phosphor with an average particle size of 1.9 microns. In a publication entitled “Preparation of P43 Suspension and Screen-Quality Evaluation in CRTs” (SID '97 vol 28, pp 440-443), it is reported that a suspension containing (1.8 micron) P43 phosphor, Barium Acetate, Potassium silicate and a surfactant was used in a centrifugal deposition process to achieve good electron aging with a screen weight of 1.0 mg/cm2 at a screen thickness of approximately five particle diameters and an anode voltage of 5 KV.
10. Electrophoretic and Cataphoretic Coating
Electrophoretic or Cataphoretic phosphor coatings can be used to make high resolution phosphor screens. Schesinger described an electrophoretic coating process where a conductive coated glass face plate is put in a solution of a phosphor and electrolyte and a metallic anode (situated about two inches from the face plate). Sclesinger et al., Design Development and Fabrication of Ultra High-Resolution Cathode Ray tube. Technical Report ECOM-00476-February 1969, pp 64-72. When a DC electric current of 20 ma is passed through the solution the phosphor screen is deposited on the cathode. In May 1997, Schermerhorn, Sweeney & Wang from Electro Plasma and Park, Park and Kim from Samsung discussed the use of electrophoretic deposition of color phosphors for Plasma Display screens through the use of metalized recessed regions or cavities. J. M. Kim et al. Development of 4-in. Full Color FED, Devices SID97 Digest, pp 56-59; J. D. Schemerhorn et al. A Groved Structure for a Large High, Resolution Color ACPDP SID97 Digest, pp 229-232.
11. Spraying
Wet or dry phosphors can be sprayed on a substrate to form a phosphor screen. The nozzle of the spray gun can be changed to spray at various spray angles depending on the distance from the substrate and other constraints. A pressure pot is used as in various spray systems to keep the pressure constant to the spray gun. In the dry system, the dry phosphor is sprayed on the screen face whose surface is coated with an adhesive binder. wet binders and dry binders can be used. In wet spraying, an organic binder such as nitrocellulose or PVA may be used. A binder which becomes tacky under UV radiation bombardment may also be used.
11. Electrostatic Spray/Dust
Phosphor screens can also be made by using a phosphor spray or dusting process in which the phosphor is charged and blown against a charged screen surface. The phosphors are then fixed to allow further processing. The U.S. Pat. No. 5,477,285 entitled “CRT developing apparatus” and issued Dec. 19, 1995 describes a process where a tribo-electric gun is used to charge the phosphor, and the phosphor is fed to the panel using a hopper, an auger to transfer the material from the hopper to the venturi chamber. The venturi chamber dispenses the charged phosphor to the latent image on the panel.
12. Transfer Tape
In a transfer tape method, the phosphor is coated on a tape base with a layer to contain phosphor. Under the phosphor layer is a release layer and the phosphor and binder are pressed onto a substrate. The base tape is removed leaving the phosphor and binder. See, N. Yocom—1996 SID Seminar on Phosphor Screening.
13. Reactive Deposition
Vapor reaction processes can be used for fabricating phosphor layers such as ZnS phosphor layers. See, e.g., D. A. Cusano, Cathodo-, Photo-, and D.C-, Electro-luminescence in Zinc Sulfide Layers. Luminescence of Organic and Inorganic Materials Edited by Kallman & Spruch Wiley & Sons 1962, pp 494-522. The substrate to be coated can be heated to temperatures from 400-700 deg C. For example, in making the phosphor screen based on ZnS:Mn, materials Zn, ZnCl2, MnC12H2S are continuously present during the formation of the phosphor layer. This process can also be used for fabricating electroluminescent screens.
14. Reactive Evaporation
Reactive evaporation methods have been reported for making screens. Transparent thin films of Y2O2S:Eu have been formed by a reactive evaporation process where the Yttrium metal is evaporated onto a substrate using an electron beam gun and excited SO2 is introduced while simultaneously heating a crucible of EuCl2 powder. Daud, Futaki, Ohmi, Tanaki & Kobayashi, Transparent Y2020S:Eu 3+ phosphor thin films grown by reactive evaporation and their luminescent properties, Journal of the Society for Information Display (SID), Vol 4, No 3 1996, pp 193-196.
15. RF Sputtering and Ion Implantation
In RF sputtering and ion implantation for forming phosphor screens, the activator ion is implanted. In N.M. Kalkhoran et al., Luminescence Study of Ion-Implanted, ZnGa2O4 Thin Films on Flexible Organic Substrates, SID '97 Digest, pp 623-626, RF sputtering was used to form thin film electroluminescent screens where ZnGa2O4 thin films were implanted on a flexible polyimide substrate with Mn, Eu to get green and red phosphor screens. The un-doped host material was used for the blue screen.
16. Metal Organic Chemical Vapor Deposition
Metal Organic Chemical Vapor Deposition (MOCVD) can be used to fabricate phosphor screens. As an example, a MOCVD process for fabricating screens with the CaGa2S4:Ce phosphor was reported by Smith et. Al., in “Crystalline-As-Deposited CaGa2S4:Ce via Low Temperature Metal Organic Chemical Vapor Deposition”:SID Digest 1995, Vol. XXVI pp 728-731. Calcium metal-organics were used in the form of Ca(2,2,6,6-tetramethyl-3,5-heptanedionate)2 called Ca(thd)2. The CaS was deposited using Ca(thd)2 in an argon carrier gas and H2S. with reactor pressures from 1 to 10 Torr. Substrates were glass, silicon and coated EL substrates at temperatures from 400-600 deg C. The Ga2S3 and CaS formation was combined with the use of Ce(thd)4 to obtain the CaGa2S4:Ce phosphor.
17. Atomic Layer Epitaxy
Atomic layer epitaxy has been used to form luminescent screens for alternating current thin film electroluminescent displays. See, Lindsay McDonald and Anthony Lowe, Display Systems, Publisher John Wiley & Sons 1997 pp. 195 & 196. A substrate was heated to a high temperature (500° C.) and was exposed to low pressure chemical precursors for forming the screen layers. As an example, Zn and Mn can be used as part of the precursors for forming a ZnS:Mn layer. The reactor is evacuated and Sulfur is introduced. The epitaxy cycle is then started to form the layers.
The phosphor materials used for screens described in this application may be prepared as phosphor nanoscale powders where in the phosphor materials are nanoscale particles or grains of 500 nm or less to produce enhanced optical conversion efficiency. Such phosphor nanoscale powders may be prepared by forming a solution or slurry which comprises phosphor precursors and then firing the solid residue of the solution or slurry which comprises the phosphor precursors. The phosphor precursors in the form of nano-sized particles or grains have a dimension less than 500 nm, preferably 200 nm or less, more preferably 100 nm or less, even more preferably 50 nm or less, and most preferably 10 nm or less. Thus, the nano-sized particles may have an average particle size of in the range from 1 nm to 500 nm, preferably 2 nm to 200 nm, more preferably 2 nm to 100 nm, even more preferably 2 nm to 50 nm, most preferably 3 nm to 10 nm. The nano-sized particles of the precursor will also preferably have a uniform size distribution with a variation within a range, e.g., 10% or less. U.S. Pat. No. 6,576,156, which is incorporated by reference in its entirety as part of this application, describes examples of phosphor nanoscale powders and fabrication techniques. In one implementation, phosphor nanoscale powders may be prepared by (1) forming a solution or slurry which contains nanosized particles of the phosphor precursors, (2) drying the solution or slurry to obtain a residue; and (3) firing the residue to form a phosphor nanoscale powder.
A screen suitable for use in the devices of this application may include one or more fluorescent materials to form a fluorescent layer sandwiched between two dichroic layers D1 and D2 to receive excitation laser light through the first dichroic layer D1 and the emitted colored light from the fluorescent layer exits the screen via the second dichroic layer D2. The first dichroic layer D1 transmits the excitation laser light, e.g., UV light, and reflects visible light. The second dichroic layer D2 is complementary to the layer D1: transmits visible light and reflects the excitation laser light, e.g., UV light. This screen design with the two dichroic layers D1 and D2 can effectively confine the excitation light such as UV light in the fluorescent layer and allows the emitted visible light, which originally tends to be in all directions, to be directed towards the other side the screen to be viewed by a viewer.
TABLE 2 shows the examples of 6-layer screens where S represents the substrate, one or more phosphors are used to form the fluorescent layer and a lacquer layer (L) or other capsulation layer is used to protect the overall screen structure from handling and environmental conditions. The substrate may be made out of plastic or glass and is capable of transmitting light in the spectral range of, e.g., 400-800 nm.
In
The excitation laser light in the above described systems, such as a laser vector scanner display and a laser video display, may enter the fluorescent layer of the screen at an angle due to the scanning action of a beam scanning module to scan the beam across the screen. This incident angle varies with the entry position of the laser light. The direction of the laser light should be as close to the normal direction to the fluorescent layer as possible to improve the image quality. Hence, an optical mechanism may be implemented at the entry to the screen to direct the incident laser beam to be normal or approximately normal to the screen. One exemplary way to implement this optical mechanism is to use a Fresnel lens, which is constructed as a layer of the screen, to make the incident laser light approximately normal to the screen.
Each of the above dichroic layers used in the screens may be implemented in various configurations. For large format displays, it may be desirable that such a dichroic layer be made of relatively inexpensive materials and be relatively easy to manufacture. Multiple dielectric layers can be designed to construct various wavelength-selective optical filters by controlling the refractive indices and the physical thickness values of the layers. For example, multiple layers of alternating high and low index dielectric layers may be designed to achieve desired wavelength-selective reflection and transmission spectra. In implementations, two different multi-layer sheet materials may be used as the D1 and D2 dichroic layers for the UV-phosphor color screens described in this application, e.g., the designs in
More specifically, multiple sheets of films with different refractive indices may be laminated or fused together to construct a composite sheet as the D1 or D2 dichroic layer. In some implementations, multiple layers of two different materials with different indices may be used to form a composite film stack as D1 or D2 by placing the two materials in an alternating manner. In other implementations, three or more different materials with different indices may be stacked together to form the composite film stack as D1 or D2. Such a composite sheet for the D1 layer is essentially an optical interference reflector that transmits the excitation light (e.g., UV light) that excites the phosphor materials which emit colored visible light and reflects the colored visible light. A composite sheet for the D2 layer may be complementary to the D1 layer: transmitting the colored visible light emitted by the phosphors and reflecting the excitation light (e.g., UV light). Such composite sheets may be formed of organic, inorganic or a combination of organic and inorganic materials. The multiple-layer composite sheet may be rigid or flexible. A flexible multi-layer composite sheet may be formed from polymeric, non-polymeric materials, or polymeric and non-polymeric materials. Exemplary films including a polymeric and non-polymeric material are disclosed in U.S. Pat. Nos. 6,010,751 and 6,172,810 which are incorporated by reference in their entirety as part of the specification of this application. An all-polymer construction for such composite sheets may offer manufacturing and cost benefits. If high temperature polymers with high optical transmission and large index differentials are utilized in the of an interference filter, then an environmentally stable filter that is both thin and very flexible can be manufactured to meet the optical needs of short-pass (SP) and (LP) filters. In particular, coextruded multilayer interference filters as taught in U.S. Pat. No. 6,531,230 can provide precise wavelength selection as well as large area, cost effective manufacturing. The entire disclosure of U.S. Pat. No. 6,531,230 is incorporated by reference as part of the specification of this application. The use of polymer pairs having high index differentials allows the construction of very thin, highly reflective mirrors that are freestanding, i.e. have no substrate but are still easily processed for constructing large screens. Such a composite sheet is functionally a piece of multi-layer optical film (MOF) and includes, e.g., alternating layers of PET and co-PMMA to exhibit a normal-incidence reflection band suitable for the screen applications of this application. As an example, an enhanced specular reflector (ESR) made out of a multilayer polyester-based film from 3M Corporation may be configured to produce the desired dichroic reflection and transmission bands for the present application. Examples for various features of multi-layer films are described in U.S. Pat. No. 5,976,424, U.S. Pat. No. 5,080,467 and U.S. Pat. No. 6,905,220, all of which are incorporated by reference as part of the specification of this application.
The dichroic layer D1 on the laser entry side of the screen in
The above combination of the lens array, the slit apertures and the reflective surfaces may be implemented in various configurations via different fabrication processes. Examples of some implementations are now described.
In other implementations, the designated carrier layer may be eliminated from the screen structure. For example, a substrate or sheet may be processed to monolithically fabricate optical elements such as the lens array on one side and the reflector array on the opposite side without separate the lens array layer, the carrier layer and the reflector array layer. Such a monolithic structure may be formed by embossing or pressing a substrate or sheet to form the optical structures, or by an extruding process through a die.
The geometries of the convex lens surfaces and the concave reflective surfaces may be different in some implementations and may be the same in other implementations. To simplify the fabrication tooling and the fabrication process, the convex lens surfaces and the concave reflective surfaces can be the identical curved surfaces and thus can be generated from the same diamond-turn master pattern using an embossing or extrusion fabrication process. The convex lens surface or the concave reflective surface may be designed in any suitable surface geometry that produces a sufficiently narrow focal spot at the slit aperture. Examples for surface shapes include, but are not limited to, a spherical surface, a hyperbolic surface, a parabolic surface, an elliptical surface, and an ellipsoidal surface. Simple spherical surfaces may be sufficient for many applications.
The materials for the lens array layer and the reflector array layer may be the same in some implementations and different in others. Various plastic materials, polymer materials and glass materials may be used for the lens and reflector array layers. The carrier layer may be a flexible layer or a rigid layer. Examples of materials suitable for a flexible carrier layer include, polyethylene terephthalate (PET), polycarbonate (PC), acrylic, polyvinyl chloride (PVC) and other plastic and polymer materials. During fabrication, the materials for the lens and reflector array layers are applied on the carrier layer and are shaped to their desired geometries. As an example, a radiation-curable resin, e.g., a UV-curable polymer, may be used for both the lens and reflector array layers. As the resin is applied on the carrier layer, the resin is exposed to the UV radiation beam and thus is cured.
One technical challenge to the design in
In mass production of the screens shown in
After the structure in
Next shown in
An alternative process for forming the optical slit apertures is laser ablation where a sufficiently powerful laser beam is used to ablate the reflective material such as a metal material of the reflector layer to form each slit aperture. Similar to the photo exposure process in the above photolithography process where the lens array is used to focus the exposure light beams to the desired focus locations on the photoresist layer, the lenses in the lens array layer can be used to focus the ablation laser beams in a self aligned manner. Referring to
The screen structure in
Phosphor stripes may be deposited by various methods. Examples include techniques such as screen printing of the “phosphor ink” in registration with the lens array and reflector array layers, selective UV tack with a distributed UV source to selectively pick up the phosphor as powder, and the electrostatic pickup. The inkjet printing for phosphor deposition may be implemented in various ways. In one implementation of the inkjet printing, a phosphor “ink” is produced by mixing a UV curable binder and a phosphor material, and is jetted through an inkjet nozzle orifice of a selected size, e.g., approximately 80 μm to print the phosphor ink on a surface. To properly position the inkjet nozzle for printing the phosphor ink at a reflector in the reflector layer, the screen may be illuminated from the side with the lens array layer and an optical detector is placed on the reflector layer side to track the bright transmission line emerging through the optical slit in each reflector. A servo mechanism tied to the inkjet nozzle can be used to position the nozzle in the proper location according to the detected transmission light by the optical detector as the nozzle sprays the phosphor ink into each reflector cavity. This method of depositing the phosphor can be used to achieve flexibility in volume control and contour shape of the phosphor layer in each reflector of the reflector layer. In this process, the inkjet nozzle does not directly contact the reflector surface. Such non-contact phosphor deposition is advantageous for manufacturing a screen that may be prone to damage via direct contact, such as the case when the inject nozzle moves at a high speed relative to the reflector layer in a high speed web process. This inkjet printing process may also be used to apply the optical filler material in the reflector layer and achieve flexibility in volume control and contour shape of the optical filler layer.
In some implementations, the phosphor layer may be further covered with a protection layer to isolate the phosphor stripes from external elements such as contaminants. The protection layer may be a polymer coating or other materials. In addition, a final rigid layer may be used to stiffen and protect the screen on the viewing side. The final layer would likely be a hard coating to prevent scratching of the screen.
Referring back to
In the above examples, the reflective surfaces of the reflectors in the reflector array layer are concave in shape. In other implementations, other geometries for the reflective surfaces may also be used. For example, two or more reflective facets may be used as a combination in each reflector.
Referring to
In the above screens with phosphor stripes, adjacent regions in the same stripe used for different subpixels of the same color for different color pixels may be better optically separated by having an optical divider between two adjacent sub-pixel areas within a phosphor stripe. The optical divider may be optically reflective or optically absorbent.
The above techniques for providing optical separation of different subpixels can enhance the image contrast by reducing crosstalk between different pixels due to the internal structure of the screen. Various external factors may also adversely affect the contrast of the display systems described in this application. For example, a portion of the ambient light reflected off the screen may enter a viewer's eye along with the image signal and thus reduce the contrast of the image perceived by the viewer.
In operation, the UV excitation light enters the phosphor layer 4520 to excite different phosphors to emit visible light of different colors. The emitted visible light transmits through the contrast enhancement layer 4510 to reach the viewer. The ambient light incident to the screen enters the contrast enhancement layer 4510 and a portion of the ambient light is reflected towards the viewer by passing through the contrast enhancement layer 4510 for the second time. Hence, the reflected ambient light towards the viewer has transmitted the contrast enhancement layer 4510 and thus has been filtered twice. The filtering of the contrast enhancement layer 4510 reduces the intensity of the reflected ambient light by two thirds. As an example, the green and blue portions comprise approximately two thirds of the flux of the ambient light entering a red subpixel. The green and blue are blocked by the contrast enhancement layer 4510. Only the red portion of the ambient light within the transmission band of the red filter material in the contrast enhancement layer 4510 is reflected back to the viewer. This reflected ambient light is essentially the same color for the subpixel generated by the underlying color phosphor stripe and thus the color contrast is not adversely affected.
In the above screen designs, the emitted colored light from the phosphor layer passes through various interfaces between two different layers or materials in the path towards the viewer. At each of such interfaces, a difference in the refractive indices at the two sides of the interface cause undesired reflection. In particular, the total internal reflection may occur at an interface when the emitted colored light propagates from a layer with an index higher than the next layer when the incident angle is greater than the critical angle of that interface. Therefore, the optical materials may be selected to have refractive indices as close as possible to minimize the reflection. The optical filler used in the concave space of the reflector array layer, for example, may be selected to match the index of the phosphor layer in order to get as much as possible the emitted visible light reflected from the reflector array layer through the phosphor layer to the viewer.
Only a few implementations are disclosed. However, it is understood that variations and enhancements may be made.
This application claims the benefits of the following four U.S. provisional applications: 1. U.S. provisional application No. 60/667,839 entitled “Laser Displays” and filed Apr. 1, 2005, 2. U.S. provisional application No. 60/683,381 entitled “Display Screen Having UV-Excitable Phosphors” and filed May 20, 2005, 3. U.S. provisional application No. 60/690,760 entitled “Display Screen Having Lens Array, Transmitting Slit Array and UV-Excitable Phosphors” and filed Jun. 14, 2005, and 4. U.S. provisional application No. 60/733,342 entitled “Display Screens Having Multi-Layer Dichroic Layer and UV-Excitable Phosphors” and filed Nov. 2, 2005. In addition, this application claims the benefit of and is a continuation-in-part application of U.S. patent application Ser. No. 11/116,998 entitled “Laser Displays Using UV-Excitable Phosphors Emitting Visible Colored Light” and filed Apr. 27, 2005 now U.S. Pat. No. 7,474,286.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2439181 | Nicoll | May 1946 | A |
| 3025161 | Thaddeus | Mar 1962 | A |
| 3556637 | Palmquist | Jan 1971 | A |
| 3652956 | Pinnow et al. | Mar 1972 | A |
| 3691482 | Pinnow et al. | Sep 1972 | A |
| 3750189 | Fleischer | Jul 1973 | A |
| 4165154 | Takahashi | Aug 1979 | A |
| 4166233 | Stanley | Aug 1979 | A |
| 4307320 | Kotera et al. | Dec 1981 | A |
| 4401362 | Maeda | Aug 1983 | A |
| 4512911 | Kotera et al. | Apr 1985 | A |
| 4613201 | Shortle et al. | Sep 1986 | A |
| 4624528 | Brueggemann | Nov 1986 | A |
| 4661419 | Nakamura | Apr 1987 | A |
| 4707093 | Testa | Nov 1987 | A |
| 4737840 | Morishita | Apr 1988 | A |
| 4816920 | Paulsen | Mar 1989 | A |
| 4923262 | Clay | May 1990 | A |
| 4978202 | Yang | Dec 1990 | A |
| 4979030 | Murata | Dec 1990 | A |
| 5054866 | Tomita et al. | Oct 1991 | A |
| 5080467 | Kahn et al. | Jan 1992 | A |
| 5089907 | Yoshikawa et al. | Feb 1992 | A |
| 5094788 | Schrenk et al. | Mar 1992 | A |
| 5122905 | Wheatley et al. | Jun 1992 | A |
| 5136426 | Linden et al. | Aug 1992 | A |
| 5138441 | Tanaka | Aug 1992 | A |
| 5140604 | Alablanche et al. | Aug 1992 | A |
| 5146355 | Prince et al. | Sep 1992 | A |
| 5166944 | Conemac | Nov 1992 | A |
| 5175637 | Jones et al. | Dec 1992 | A |
| 5182659 | Clay et al. | Jan 1993 | A |
| 5198679 | Katoh et al. | Mar 1993 | A |
| 5255113 | Yoshikawa et al. | Oct 1993 | A |
| 5269995 | Ramanathan et al. | Dec 1993 | A |
| 5270842 | Clay et al. | Dec 1993 | A |
| 5296922 | Mitani et al. | Mar 1994 | A |
| 5365288 | Dewald et al. | Nov 1994 | A |
| 5389324 | Lewis et al. | Feb 1995 | A |
| 5414521 | Ansley | May 1995 | A |
| 5442254 | Jaskie | Aug 1995 | A |
| 5473396 | Okajima et al. | Dec 1995 | A |
| 5475524 | Harris | Dec 1995 | A |
| 5477285 | Riddle et al. | Dec 1995 | A |
| 5477330 | Dorr | Dec 1995 | A |
| 5491578 | Harris | Feb 1996 | A |
| 5526166 | Genovese | Jun 1996 | A |
| 5541731 | Freedenberg et al. | Jul 1996 | A |
| 5550667 | Krimmel et al. | Aug 1996 | A |
| 5587818 | Lee | Dec 1996 | A |
| 5594556 | Vronsky et al. | Jan 1997 | A |
| 5598292 | Yoshikawa et al. | Jan 1997 | A |
| 5602445 | Solanki et al. | Feb 1997 | A |
| 5614961 | Gibeau et al. | Mar 1997 | A |
| 5633736 | Griffith et al. | May 1997 | A |
| 5646766 | Conemac | Jul 1997 | A |
| 5648181 | Watanabe | Jul 1997 | A |
| 5666174 | Cupolo, III | Sep 1997 | A |
| 5668662 | Magocs et al. | Sep 1997 | A |
| 5670209 | Wyckoff | Sep 1997 | A |
| 5684552 | Miyamoto et al. | Nov 1997 | A |
| 5698857 | Lambert et al. | Dec 1997 | A |
| 5715021 | Gibeau et al. | Feb 1998 | A |
| 5716118 | Sato et al. | Feb 1998 | A |
| 5870224 | Saitoh et al. | Feb 1999 | A |
| 5882774 | Jonza et al. | Mar 1999 | A |
| 5907312 | Sato et al. | May 1999 | A |
| 5920361 | Gibeau et al. | Jul 1999 | A |
| 5959296 | Cyr et al. | Sep 1999 | A |
| 5973813 | Takeuchi | Oct 1999 | A |
| 5976424 | Weber et al. | Nov 1999 | A |
| 5978142 | Blackham et al. | Nov 1999 | A |
| 5994722 | Averbeck et al. | Nov 1999 | A |
| 5998918 | Do et al. | Dec 1999 | A |
| 5998925 | Shimizu et al. | Dec 1999 | A |
| 6008925 | Conemac | Dec 1999 | A |
| 6010751 | Shaw et al. | Jan 2000 | A |
| 6057953 | Ang | May 2000 | A |
| 6064417 | Harrigan et al. | May 2000 | A |
| 6066861 | Hohn et al. | May 2000 | A |
| 6069599 | Py et al. | May 2000 | A |
| 6080467 | Weber et al. | Jun 2000 | A |
| 6088163 | Gilbert et al. | Jul 2000 | A |
| 6101032 | Wortman et al. | Aug 2000 | A |
| 6117530 | Jonza et al. | Sep 2000 | A |
| 6118516 | Irie et al. | Sep 2000 | A |
| 6128131 | Tang | Oct 2000 | A |
| 6134050 | Conemac | Oct 2000 | A |
| 6154259 | Hargis et al. | Nov 2000 | A |
| 6157486 | Benson et al. | Dec 2000 | A |
| 6157490 | Wheatley et al. | Dec 2000 | A |
| 6172810 | Fleming et al. | Jan 2001 | B1 |
| 6175440 | Conemac | Jan 2001 | B1 |
| 6219168 | Wang | Apr 2001 | B1 |
| 6224216 | Parker | May 2001 | B1 |
| 6226126 | Conemac | May 2001 | B1 |
| 6252254 | Soules et al. | Jun 2001 | B1 |
| 6255670 | Srivastava et al. | Jul 2001 | B1 |
| 6288817 | Rowe | Sep 2001 | B2 |
| 6329966 | Someya et al. | Dec 2001 | B1 |
| 6333724 | Taira et al. | Dec 2001 | B1 |
| 6417019 | Mueller et al. | Jul 2002 | B1 |
| 6429583 | Levinson et al. | Aug 2002 | B1 |
| 6429584 | Kubota | Aug 2002 | B2 |
| 6463585 | Hendricks et al. | Oct 2002 | B1 |
| 6531230 | Weber et al. | Mar 2003 | B1 |
| 6576156 | Ratna et al. | Jun 2003 | B1 |
| 6621593 | Wang et al. | Sep 2003 | B1 |
| 6621609 | Conemac | Sep 2003 | B1 |
| 6628248 | Masumoto et al. | Sep 2003 | B2 |
| 6678081 | Nishihata et al. | Jan 2004 | B2 |
| 6717704 | Nakai | Apr 2004 | B2 |
| 6765237 | Doxsee et al. | Jul 2004 | B1 |
| 6777861 | Russ et al. | Aug 2004 | B2 |
| 6809347 | Tasch et al. | Oct 2004 | B2 |
| 6809781 | Setlur et al. | Oct 2004 | B2 |
| 6839042 | Conemac et al. | Jan 2005 | B2 |
| 6853131 | Srivastava et al. | Feb 2005 | B2 |
| 6900916 | Okazaki et al. | May 2005 | B2 |
| 6905220 | Wortman et al. | Jun 2005 | B2 |
| 6937221 | Lippert et al. | Aug 2005 | B2 |
| 6937383 | Morikawa et al. | Aug 2005 | B2 |
| 6947198 | Morikawa et al. | Sep 2005 | B2 |
| 6986581 | Sun et al. | Jan 2006 | B2 |
| 6987610 | Piehl | Jan 2006 | B2 |
| 7068406 | Shimomura | Jun 2006 | B2 |
| 7088335 | Hunter et al. | Aug 2006 | B2 |
| 7090355 | Liu et al. | Aug 2006 | B2 |
| 7147802 | Sugimoto et al. | Dec 2006 | B2 |
| 7181417 | Langseth et al. | Feb 2007 | B1 |
| 7213923 | Liu et al. | May 2007 | B2 |
| 7230767 | Walck et al. | Jun 2007 | B2 |
| 7239436 | Orttinger et al. | Jul 2007 | B2 |
| 7283301 | Peeters et al. | Oct 2007 | B2 |
| 7302174 | Tan et al. | Nov 2007 | B2 |
| 7474286 | Hajjar et al. | Jan 2009 | B2 |
| 20010019240 | Takahashi | Sep 2001 | A1 |
| 20010024086 | Fox et al. | Sep 2001 | A1 |
| 20010050371 | Odaki et al. | Dec 2001 | A1 |
| 20020003233 | Mueller-Mach et al. | Jan 2002 | A1 |
| 20020008854 | Leigh Travis | Jan 2002 | A1 |
| 20020024495 | Lippert et al. | Feb 2002 | A1 |
| 20020050963 | Conemac et al. | May 2002 | A1 |
| 20020122260 | Okazaki et al. | Sep 2002 | A1 |
| 20020124250 | Proehl et al. | Sep 2002 | A1 |
| 20020145685 | Mueller-Mach et al. | Oct 2002 | A1 |
| 20020163702 | Hori et al. | Nov 2002 | A1 |
| 20020185965 | Collins et al. | Dec 2002 | A1 |
| 20030015692 | Teng et al. | Jan 2003 | A1 |
| 20030094893 | Ellens et al. | May 2003 | A1 |
| 20030184209 | Russ et al. | Oct 2003 | A1 |
| 20030184531 | Morikawa et al. | Oct 2003 | A1 |
| 20030184613 | Nakamura et al. | Oct 2003 | A1 |
| 20030184842 | Morikawa et al. | Oct 2003 | A1 |
| 20040027465 | Smith et al. | Feb 2004 | A1 |
| 20040070551 | Walck et al. | Apr 2004 | A1 |
| 20040141220 | Hama et al. | Jul 2004 | A1 |
| 20040145312 | Ouderkirk et al. | Jul 2004 | A1 |
| 20040156079 | Marshall et al. | Aug 2004 | A1 |
| 20040160516 | Ford | Aug 2004 | A1 |
| 20040165642 | Lamont | Aug 2004 | A1 |
| 20040184123 | Morikawa et al. | Sep 2004 | A1 |
| 20040223100 | Kotchick et al. | Nov 2004 | A1 |
| 20040227465 | Menkara et al. | Nov 2004 | A1 |
| 20040263074 | Baroky et al. | Dec 2004 | A1 |
| 20050001225 | Yoshimura et al. | Jan 2005 | A1 |
| 20050012446 | Jermann et al. | Jan 2005 | A1 |
| 20050023962 | Menkara et al. | Feb 2005 | A1 |
| 20050023963 | Menkara et al. | Feb 2005 | A1 |
| 20050051790 | Ueda | Mar 2005 | A1 |
| 20050093818 | Hatam-Tabrizi et al. | May 2005 | A1 |
| 20050094266 | Liu et al. | May 2005 | A1 |
| 20050280785 | Beeson et al. | Dec 2005 | A1 |
| 20060050015 | Kusunoki et al. | Mar 2006 | A1 |
| 20060066508 | Walck et al. | Mar 2006 | A1 |
| 20060081793 | Nestorovic et al. | Apr 2006 | A1 |
| 20060082873 | Allen et al. | Apr 2006 | A1 |
| 20060088951 | Hayashi et al. | Apr 2006 | A1 |
| 20060132021 | Naberhuis et al. | Jun 2006 | A1 |
| 20060139580 | Conner | Jun 2006 | A1 |
| 20060197922 | Liu et al. | Sep 2006 | A1 |
| 20060221022 | Hajjar | Oct 2006 | A1 |
| 20060227087 | Hajjar et al. | Oct 2006 | A1 |
| 20060262243 | Lester et al. | Nov 2006 | A1 |
| 20060266958 | Shimizu et al. | Nov 2006 | A1 |
| 20060290898 | Liu et al. | Dec 2006 | A1 |
| 20070014318 | Hajjar et al. | Jan 2007 | A1 |
| 20070183466 | Son et al. | Aug 2007 | A1 |
| 20070187580 | Kykta et al. | Aug 2007 | A1 |
| 20070187616 | Burroughs et al. | Aug 2007 | A1 |
| 20070188417 | Hajjar et al. | Aug 2007 | A1 |
| 20070206258 | Malyak et al. | Sep 2007 | A1 |
| 20070228927 | Kindler et al. | Oct 2007 | A1 |
| 20070229946 | Okada et al. | Oct 2007 | A1 |
| 20080018558 | Kykta et al. | Jan 2008 | A1 |
| 20080066107 | Moonka et al. | Mar 2008 | A1 |
| 20080068295 | Hajjar | Mar 2008 | A1 |
| 20080235749 | Jain et al. | Sep 2008 | A1 |
| 20080247020 | Malyak et al. | Oct 2008 | A1 |
| 20080291140 | Kent et al. | Nov 2008 | A1 |
| 20090001272 | Hajjar | Jan 2009 | A1 |
| 20090116107 | Kindler et al. | May 2009 | A1 |
| 20090153582 | Hajjar et al. | Jun 2009 | A1 |
| 20090174632 | Hajjar et al. | Jul 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 10044603 | Apr 2001 | DE |
| 0196862 | Oct 1986 | EP |
| 0271650 | Jun 1988 | EP |
| 1150361 | Oct 2001 | EP |
| 56164826 | Dec 1981 | JP |
| 59-155826 | Sep 1984 | JP |
| 02-157790 | Jun 1990 | JP |
| 2-199975 | Aug 1990 | JP |
| 5232583 | Sep 1993 | JP |
| 06046461 | Feb 1994 | JP |
| 2000-49380 | Feb 2000 | JP |
| 2001-210122 | Aug 2001 | JP |
| 2001-316664 | Nov 2001 | JP |
| 2002-83549 | Mar 2002 | JP |
| 2006-323391 | Nov 2006 | JP |
| 10-2001-0097415 | Nov 2001 | KR |
| 2002-0024425 | Mar 2002 | KR |
| 2003-0068589 | Aug 2003 | KR |
| WO 9012387 | Oct 1990 | WO |
| WO 9222109 | Dec 1992 | WO |
| WO 0020912 | Apr 2000 | WO |
| WO 0033389 | Jun 2000 | WO |
| WO 0124229 | Apr 2001 | WO |
| WO 0188609 | Nov 2001 | WO |
| WO 0211173 | Feb 2002 | WO |
| WO 0223962 | Mar 2002 | WO |
| WO 0233970 | Apr 2002 | WO |
| WO 02057838 | Jul 2002 | WO |
| WO 2002071148 | Sep 2002 | WO |
| WO 2005119797 | Dec 2005 | WO |
| WO 2006097876 | Sep 2006 | WO |
| WO 2006107720 | Oct 2006 | WO |
| WO 2007050662 | May 2007 | WO |
| WO 2007095329 | Aug 2007 | WO |
| WO 2007114918 | Oct 2007 | WO |
| WO 2007131195 | Nov 2007 | WO |
| WO 2007134329 | Nov 2007 | WO |
| WO 2008116123 | Sep 2008 | WO |
| WO 2008124707 | Oct 2008 | WO |
| WO 2008144673 | Nov 2008 | WO |
| WO 2009003192 | Dec 2008 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20060221021 A1 | Oct 2006 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60667839 | Apr 2005 | US | |
| 60683381 | May 2005 | US | |
| 60690760 | Jun 2005 | US | |
| 60733342 | Nov 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11116998 | Apr 2005 | US |
| Child | 11335813 | US |