Doped, pyrogenically prepared oxides

Abstract

Doped, pyrogenically prepared oxides of metals and/or non-metals which are doped with one or more doping components in an amount of 0.00001 to 20 wt. %. The doping component may be a metal and/or non-metal or an oxide and/or a salt of a metal and/or a non-metal. The BET surface area of the doped oxide may be between 5 and 600 m2/g. The doped pyrogenically prepared oxides of metals and/or non-metals are prepared by adding an aerosol which contains an aqueous solution of a metal and/or non-metal to the gas mixture during the flame hydrolysis of vaporizable compounds of metals and/or non-metals.

Description

INTRODUCTION AND BACKGROUND

[0001] The present invention relates to doped, pyrogenically prepared oxides, a process for their preparation and their use.

[0002] It is known that pyrogenically prepared oxides can be coated with metal salts or metal oxides by mixing the pyrogenically prepared oxides with aqueous solutions of metal salts and then drying and/or calcining.

[0003] Products prepared in this way have the disadvantages a) that the doping substance is not homogeneously distributed in the entire primary particle or b) that, depending on the type of doping, inhomogeneities may occur during mixing. Thus, after doping and calcining, the primary particles of the doping substance may separate out and be present with much larger diameters than the primary particles of pyrogenic oxides.

[0004] It is therefore an object of the invention to achieve homogeneous doping of pyrogenically prepared oxides with another substance while at the same time avoiding problems of the prior art, and more particularly, to avoid the presence of separate primary particles of the doping substance or oxides of the doping substance alongside primary particles of the pyrogenically prepared oxide.

SUMMARY OF THE INVENTION

[0005] The above as well as other objects are obtained by the present invention in the form of doped, pyrogenically prepared oxides of metals and/or non-metals wherein the basic components are pyrogenically prepared oxides of metals and/or non-metals, prepared using flame hydrolysis techniques, which are doped with at least one doping component at 0.00001 to 20 wt. %, wherein the doping amount may preferably be in the range 1 to 10,000 ppm, and the doping component is a non-metal and/or a metal or a non-metal salt and/or a metal salt or an oxide of a metal and/or a non-metal, and the BET surface area of the doped oxides is between 5 and 600 m2/g.

[0006] Another feature of the invention is a process for preparing doped, pyrogenically prepared oxides of metals and/or non-metals. In carrying out the process, an aerosol is fed into a flame, such as is used in a known manner to prepare pyrogenic oxides by flame hydrolysis and wherein this aerosol is homogeneously mixed with the gas mixture for flame oxidation or flame hydrolysis prior to reaction. The aerosol/gas mixture is allowed to react in the flame and the resulting doped pyrogenically prepared oxides are separated from the gas stream in a known manner. A salt solution or suspension which contains the components of the substance to be doped, which may be a metal salt or a non-metal salt (metalloid salt) or mixtures of both or a suspension of an insoluble metal compound or non-metal (metalloid) compound, is used as the starting material for the aerosol. The aerosol is prepared by nebulization using a two-fluid nozzle or using an aerosol generator, preferably by the ultrasonic method.

BRIEF DESCRIPTION OF THE DRAWINGS

[0007] The invention will be further understood with reference to the drawings, wherein:

[0008] FIG. 1 is a schematic diagram of an apparatus suitable for practicing the present invention;

[0009] FIG. 2 is an EM photograph of pyrogenic silicon made without doping; and

[0010] FIG. 3 is an EM photograph of pyrogenic silicon made with doping in accordance with the present invention.

DETAILED DESCRIPTION OF THE DRAWINGS

[0011] In carrying out the present invention, aerosol technology is used to feed into a flame in order to prepare pyrogenic oxides by flame hydrolysis.

[0012] The aerosol may be introduced in a preferred embodiment of the invention by means of a device such as the one shown in FIG. 1. According to FIG. 1, the main part of the apparatus is a burner 1 of known construction, such as is conventionally used for preparing pyrogenic oxides. In this case, the pipes for gas and aerosol introduction may also be interchanged.

[0013] The burner 1 consists of a central tube 2 which discharges into a nozzle 3, out of which the main gas stream flows into the combustion chamber 8 and is there burned off. The inner nozzle is surrounded by the further annular nozzle 4 (mantle nozzle), out of which flows mantle- or secondary-hydrogen to prevent caking.

[0014] According to the invention, a centrally located axial tube 5 is located inside central tube 2 and terminates a few centimeters upstream of the nozzle 3 of the central tube 2. The aerosol is fed into the axial tube 5, whereby the aerosol gas stream from the axial tube 5 is homogeneously mixed with the gas stream from the central tube 2 over the last section of the central tube 2. The central tube conveys air, hydrogen and, for example, silicon tetrachloride for the pyrolysis reaction.

[0015] The aerosol is produced in an aerosol generator 6 (ultrasonic nebulizer). An aqueous salt solution 9 located in the generator 6 contains the metal or non-metal as a salt in dissolved or dispersed/suspended form and is used as the aerosol starting material. The aerosol produced by the aerosol generator 6 is passed through the heating zone 7 by means of a carrier gas stream 10, whereupon the water evaporates and small, finely distributed salt crystals remain in the gas phase. The flame pipe 11 can be cooled with cooling water 12. Secondary air can be introduced through part 13 into the chamber 8.

[0016] In a further embodiment of the invention, the aerosol may be introduced using an annular nozzle, which may be arranged at any angle, preferably at right angles, to the main gas stream.

[0017] The basic components which may be used are the non-metals/metals aluminum, niobium, titanium, tungsten, zirconium, germanium, boron and/or silicon.

[0018] The doping components which are used may be metals and/or non-metals and their compounds, provided they are soluble in or can be suspended in a liquid solution. In a preferred embodiment, compounds of transition metals and/or noble metals may be used for this purpose. The term “transition metals” is used herein in its art-recognized meaning.

[0019] By way of example, cerium and potassium salts may be used as doping components.

[0020] The flame hydrolysis process for preparing pyrogenic oxides is known from Ullmann's Encyclopedia of Industrial Chemistry, 4th ed., vol. 21, page 464, the disclosure of which is relied on and incorporated herein by reference.

[0021] Due to the fine distribution of the doping component in the aerosol, and also the high temperatures (1,000 to 2,400° C.) during subsequent flame hydrolysis, during which the doping components are possibly further reduced in size and/or melted, the doping medium is finely distributed in the gas phase during the initial stages of production of the pyrogenic oxide, so that homogeneous incorporation of the doping component in the pyrogenically prepared oxide is possible.

[0022] Using the process according to the invention, it is possible to dope all known pyrogenically prepared oxides (e.g., SiO2, TiO2, Al2O3, B2O3, ZrO2, GeO2, WO3, Nb2O5) with other metal or metal oxides or non metal or non metal (metalloid) oxides or mixtures thereof.

[0023] The process according to the invention has several advantages: The aggregate or agglomerate structure of the pyrogenic oxide can be influenced by the choice of doping components. Furthermore, the pH of the pyrogenic oxide can be affected.

[0024] Catalytically active substances (e.g., cerium or noble metals) which are used as doping components can be distributed almost homogeneously in the pyrogenically prepared oxide.

[0025] Phase conversion of pyrogenically prepared oxides, for example from rutile to anatase in pyrogenically prepared titanium oxide, can be affected by doping.

[0026] Using the process according to the invention, combinations of properties of pyrogenically prepared oxides which have hitherto not been available, or available only with great difficulty, i.e. for example in processes requiring several steps, can be achieved.

[0027] Pyrogenically prepared oxides of metals and/or non-metals, doped according to the invention, can be used as fillers, as support materials, as catalytically active substances, as starting materials for preparing dispersions, as polishing materials for polishing metal or silicon wafers in the electrical industry, as ceramic substrates, in the electronics industry (CMP applications), in the cosmetics industry, as additives in the silicone and rubber industry, to adjust the rheology of liquid systems, for heat-resistant stabilization purposes, in the lacquer industry, as a heat insulation material, and the like.

[0028] The invention also provides a device for performing the process according to the invention which is characterized in that an additional tube for introducing the aerosol is arranged, preferably axially, in a burner of the structure known for preparing pyrogenic oxides, wherein the tube terminates upstream of the burner nozzle.

EXAMPLES

[0029] The burner arrangement used in examples 1 to 4 is shown schematically in FIG. 1.

Example 1

No Doping

[0030] 4.44 kg/h of SiCl4 are evaporated at about 130° C. and introduced into the central tube of the burner. 3 Nm3/h of primary hydrogen and 8.0 Nm3/h of air are also fed to the central tube. The gas mixture flows out of the inner nozzle of the burner and burns in the combustion chamber and the water-cooled flame tube connected in series therewith. 0.5 Nm3/h of mantle or secondary hydrogen are fed to the mantle nozzle which surrounds the central nozzle, in order to prevent caking of the nozzle. An additional 12 Nm3/h of secondary air are fed to the combustion chamber.

[0031] The aerosol flows out of the axial tube into the central tube. The aerosol consists of water vapor which has been produced in an amount of 195 g/h by ultrasonic nebulization of pure distilled water in the aerosol generator.

[0032] The nebulized water vapor is passed through a heated pipe with the assistance of a carrier gas of about 0.5 Nm3/h of air, wherein the aerosol is converted into gas at a temperature of about 180° C.

[0033] At the mouth of the burner (nozzle 3), the temperature of the gas mixture (SiCl4/air/hydrogen, water vapor and water aerosol) is 150° C.

[0034] The reaction gases and the resulting pyrogenic silica are passed under suction through a cooling system, by applying a reduced pressure to the flame tube, and thus cooled to about 100 to 160° C. The solid is separated from the vent gas stream in a filter or a cyclone.

[0035] The silica is produced as a white, finely divided powder. In a further step, adhering residues of hydrochloric acid are removed from the silica by treating it with water vapor-containing air at elevated temperature.

[0036] The BET surface area of the pyrogenic silica is 150 m2/g.

[0037] The production parameters are given in Table 1. Further analytical data relating to the pyrogenic silica obtained are given in Table 2.

Example 2

Doping With Cerium

[0038] The same procedure is used as described in Example 1: 4.44 kg/h of SiCl4 are evaporated at about 130° C. and introduced into the central tube of the burner. 3 Nm3/h of primary hydrogen and 8.0 Nm3/h of air are also supplied to the central tube. The gas mixture flows out of the inner burner nozzle and burns in the combustion chamber and the water-cooled flame tube connected in series therewith. In the mantle nozzle which surrounds the central nozzle, 0.5 Nm3/h of mantle or secondary hydrogen are supplied in order to prevent caking. An additional 12 Nm3/h of secondary air are supplied to the combustion chamber.

[0039] The aerosol flows out of the axial tube into the central tube. The aerosol is a cerium salt aerosol which is produced in an amount of 210 g/h by ultrasonic nebulization of a 5% aqueous cerium(III) chloride solution in the aerosol generator.

[0040] The cerium salt aerosol is passed through a heated pipe with the assistance of 0.5 Nm3/h of air as carrier gas, wherein the aerosol is converted into a gas and a salt crystal aerosol at temperatures around 180° C.

[0041] At the mouth of the burner, the temperature of the gas mixture (SiCl4/air/hydrogen, aerosol) is 180° C.

[0042] The reaction gases and the resulting pyrogenically prepared silica, doped with cerium, are removed under suction via a cooling system by applying a reduced pressure and thus cooled to about 100 to 160° C. The solid is separated from the gas stream in a filter or cyclone.

[0043] The doped, pyrogenically prepared silica is produced as a white, finely divided powder. In a further step, adhering hydrochloric acid residues are removed from the silica by treatment with water vapor-containing air at elevated temperatures.

[0044] The BET surface area of the doped, pyrogenically prepared silica is 143 m2/g.

[0045] The production parameters are given in Table 1. Further analytical data for the pyrogenic silica obtained are given in Table 2.

Example 3

No Doping

[0046] 4.44 kg/h of SiCl4 are evaporated at about 130° C. and transferred to the central tube in the burner. 3 Nm3/h of primary hydrogen and 8.7 Nm3/h of air are also fed through the central tube. The gas mixture flows out of the inner nozzle of the burner and burns in the combustion chamber and the water-cooled flame tube connected in series therewith. In the mantle nozzle which surrounds the central nozzle, 0.5 Nm3/h of mantle or secondary hydrogen are supplied in order to prevent caking. An additional 12 Nm3/h of secondary air are supplied to the combustion chamber.

[0047] The aerosol flows out of the axial tube into the central tube. The aerosol consists of water vapor which is produced in an amount of 210 g/h by ultrasonic nebulization of pure distilled water in the aerosol generator.

[0048] The aerosol is passed through a heated pipe with the assistance of about 0.5 Nm3/h of air as carrier gas, wherein the aerosol is converted into a gas at temperatures around 180° C.

[0049] At the mouth of the burner, the temperature of the gas mixture (SiCl4/air/hydrogen, water vapor or water aerosol) is 180° C.

[0050] The reaction gases and the resulting pyrogenic silica are removed under suction via a cooling system by applying a reduced pressure and thus cooled to about 100 to 160° C. The solid is separated from the gas stream in a filter or cyclone.

[0051] The silica is produced as a white, finely divided powder. In a further step, adhering hydrochloric acid residues are removed from the silica by treatment with water vapor-containing air at elevated temperature.

[0052] The BET surface area of the pyrogenic silica is 215 m2/g.

[0053] The production parameters are given in Table 1. Further analytical data for the pyrogenic silica obtained are given in Table 2.

Example 4

Doping With Cerium

[0054] The same procedure is used as described in Example 1: 4.44 kg/h of SiCl4 are evaporated at about 130° C. and introduced into the central tube of the burner. 3 Nm3/h of primary hydrogen and 8.7 Nm3/h of air are also supplied to the central tube. The gas mixture flows out of the inner burner nozzle and burns in the combustion chamber and the water-cooled flame tube connected in series therewith.

[0055] In the mantle nozzle which surrounds the central nozzle, 0.5 Nm3/h of mantle or secondary hydrogen are supplied in order to prevent caking.

[0056] An additional 12 Nm3/h of secondary air are supplied to the combustion chamber.

[0057] The aerosol flows out of the axial tube into the central tube. The aerosol is a cerium salt aerosol which has been produced in an amount of 205 g/h by ultrasonic nebulization of a 5% aqueous cerium(III) chloride solution in the aerosol generator.

[0058] The cerium salt aerosol is passed through a heated pipe with the assistance of 0.5 Nm3/h of air as carrier gas, wherein the aerosol is converted into a gas and a salt crystal aerosol at temperatures around 180° C.

[0059] At the mouth of the burner, the temperature of the gas mixture (SiCl4/air/hydrogen, aerosol) is 180° C.

[0060] The reaction gases and the resulting pyrogenically prepared silica, doped with cerium, are removed under suction via a cooling system by applying a reduced pressure and thus cooled to about 100 to 160° C. The solid is separated from the gas stream in a filter or cyclone.

[0061] The doped, pyrogenic silica is produced as a white, finely divided powder. In a further step, adhering hydrochloric acid residues are removed from the pyrogenic silica by treatment with water vapor-containing air at elevated temperatures.

[0062] The BET surface area of the doped, pyrogenic silica is 217 m2/g.

[0063] The production parameters are given in Table 1. Further analytical data for the pyrogenic silica obtained are given in Table 2.

Example 5

Doping With Potassium Salts

[0064] The same procedure is used as described in Example 1, wherein a 0.5% aqueous potassium chloride solution is used as salt solution.

[0065] 4.44 kg/h of SiCl4 are evaporated at about 130° C. and introduced into the central tube of the burner. 3 Nm3/h of primary hydrogen and 8.7 Nm3/h of air are also supplied to the central tube. The gas mixture flows out of the inner burner nozzle and burns in the combustion chamber and the water-cooled flame tube connected in series therewith.

[0066] In the mantle nozzle which surrounds the central nozzle, 0.5 Nm3/h of mantle or secondary hydrogen are supplied in order to prevent caking.

[0067] The aerosol flows out of the axial tube into the central tube. The aerosol is a potassium salt aerosol which has been produced in an amount of 215 g/h by ultrasonic nebulization of a 0.5% aqueous potassium chloride solution in the aerosol generator.

[0068] The potassium salt aerosol is passed through a heated pipe with the assistance of 0.5 Nm3/h of air as carrier gas, wherein the aerosol is converted into a gas and a salt crystal aerosol at temperatures around 180° C.

[0069] At the mouth of the burner, the temperature of the gas mixture (SiCl4/air/hydrogen, aerosol) is 180° C.

[0070] The reaction gases and the resulting pyrogenically prepared silica, doped with potassium, are removed under suction via a cooling system by applying a reduced pressure and the particle/gas stream is thus cooled to about 100 to 160° C. The solid is separated from the gas stream in a filter or cyclone.

[0071] The doped, pyrogenically prepared silica is produced as a white, finely divided powder. In a further step, adhering hydrochloric acid residues are removed from the silica by treatment with water vapor-containing air at elevated temperatures.

[0072] The BET surface area of the doped, pyrogenically prepared silica is 199 m2/g.

[0073] The production parameters are given in Table 1.

[0074] Further analytical data for the pyrogenic silica obtained are given in Table 2.

TABLE 1
EXPERIMENTAL CONDITIONS DURING THE PREPARATION OF DOPED PYROGENIC SILICAS
		Prim.	Sec.		H2	N2	Gas		Aerosol	Air
	SiCl4	air	air	H2 core	mantle	mantle	temp.	Salt	amount	aeros.	BET
No.	kg/h	Nm3/h	Nm3/h	Nm3/h	Nm3/h	Nm3/h	° C.	soln.	kg/h	Nm3/h	m2/g
Doping with cerium salt and comparison examples
1	4.44	8.0	12	3	0.5	0.3	150	only	0.195	0.5	150
								H2O
2	4.44	8.0	12	3	0.5	0.3	180	5% CeCl3	0.210	0.5	143
3	4.44	8.7	12	3	0.5	0.3	180	only	0.210	0.5	215
								H2O
4	4.44	8.7	12	3	0.5	0.3	180	5% CeCl3	0.205	0.5	217
Doping with potassium salt and comparison example
3	4.44	8.7	12	3	0.5	0.3	180	only	0.210	0.5	215
								H2O
5	4.44	8.7	12	3	0.5	0.3	180	0.5% KCl	0.215	0.5	199
Notes:
Prim. air = amount of air in central tube; sec. air = secondary air; H2 core = hydrogen in central tube; Gas temp. = gas temperature at the nozzle in the central tube; Aerosol amount = mass flow of salt solution converted into aerosol form; Air aerosol = carrier gas (air) in the aerosol.

[0075]

TABLE 2
ANALYTICAL DATA FOR SAMPLES OBTAINED ACCORDING TO EXAMPLES 1 TO 5
													Thick.
		Ce	K	Cl				Grindo	Sedi-		pH	Comp.	Lupoda
	BET	wt.	wt.	conc.	LOD	LOI	Cl	meter	vol.	Effic-	4%	b. d.	1
No.	[m2/g]	μg/g	μg/g	ppm	wt. %	wt. %	ppm	μm	vol %	iency	sus.	g/l	[mPas]
Doping with cerium salt and comparison examples
1	150	—			0.19	1.29		18	0	697	3.98	27	1745
2	143	1860	<5		0.09	1.33		20	0	690	3.93	26	1990
3	215	84	<5	45	0.27	1.87	45	18	11	422	4.00	25	3390
4	217	2350	<5	112	0.22	2.23	112	40	50	548	3.67	29	3680
Doping with potassium salt and comparison example
3	215		<5	45	0.27	1.87	45	18	11	422	4.00	25	3390
5	199		300	55	0.32	1.86	55	60	50	451	4.83	32	2575
Notes:
Cerium content as Ce in μg/g (ppm); Potassium content as K in μg/g; LOD = loss on drying (2 h at 105° C., based on DIN/ISO 787/II, ASTM D 280, JIS K 5101/21); LOI = loss on ignition (2 h at 1000° C., based on DIN 55921, ASTM D 1208, JIS K 5101/23, with ref. to substance dried for 2 h at 105° C.); Grindometer = Grindometer value; Sedi-vol. = sediment volume;
# Efficiency = turbidity measurement: the method of effciency determination (turbidity measurement) is described in Patent DE 44 00 170; the suspension prepared by the same method is used for determining sediment volume after standing for a further 5 minutes; Compacted bulk density based on DIN/ISO 787/IX, JIS K 5101/18 (no sieved). Thickening in polyester reference system: described in EP-A 0 015 315.

[0076] FIG. 2 shows an EM photograph of pyrogenic silica prepared in accordance with Example 3 (no doping).

[0077] FIG. 3 shows an EM photograph of pyrogenic silica prepared in accordance with Example 4 (doped with cerium salt).

[0078] It can be seen that the aggregate and agglomerate structure is modified when doped with cerium salt. Larger cohesive structures are produced with doping.

[0079] The analytical data for silica in accordance with Example 4, as compared with that for silica in accordance with Example 3, shows an increased sediment volume and a greatly increased efficiency value. This also indicates enlargement of the aggregate or agglomerate structure.

[0080] It should be noted that comparable results are obtained in accordance with the present invention when a noble metal is used in place of cerium in Example 4. Similarly, when silica is replaced with aluminum oxide, niobium oxide, germanium oxide or boron oxide, comparable results would be obtained.

[0081] Furthermore, using silica doped with cerium in accordance with the invention, a clear improvement in thickening effect is produced in unsaturated polyester resins.

[0082] Further variations and modifications will be apparent to those skilled in the art from the foregoing and are intended to be encompassed by the claims appended hereto.

[0083] German priority application 195 50 500.3 is relied on and incorporated herein by reference.

Claims

1. A doped pyrogenically prepared oxide of a metal and/or a non-metal, comprising an oxide of a metal and/or non-metal prepared by flame hydrolysis, which is doped with at least one doping component at 0.00001 to 20 wt. % and the doping component is a non-metal and/or metal or a salt or an oxide of a metal or non-metal, and the BET surface area of the doped oxide is between 5 and 600 m2/g.

2. The doped pyrogenically prepared oxide according to claim 1 wherein the doping amount is in the range 1 to 10,000 ppm.

3. The doped pyrogenically prepared oxide according to claim 1 wherein silica is said oxide.

4. The doped pyrogenically prepared oxide according to claim 1 wherein said oxide is an oxide of a member selected from the group consisting of aluminum, niobium, titanium, tungsten, zirconium, germanium, boron, silicon and mixtures thereof.

5. The doped pyrogenically prepared oxide according to claim 1 wherein said doping component is cerium.

6. The doped pyrogenically prepared oxide according to claim 1 wherein said doping component is a noble metal.

7. The doped pyrogenically prepared oxide according to claim 1 wherein said doping component is a transition series element soluble in water or capable of forming a liquid suspension.

8. A process for preparing a pyrogenically prepared oxide of a metal and/or non-metal comprising feeding an aerosol to a flame for preparing a pyrogenic oxide by flame hydrolysis, this aerosol being homogeneously mixed with a gas stream for flame oxidation or flame hydrolysis prior to reaction, allowing the aerosol/gas mixture to react in a flame and separating resulting doped pyrogenically prepared oxide from the gas stream, wherein a salt solution or suspension which contains the component of a substance to be doped, which can be a metal salt, non-metal salt, or metalloid salt or mixtures or a suspension of an insoluble metal compound or non-metal or metalloid compound or mixture, is used as a starting material for the aerosol.

9. The process according to claim 8 wherein the aerosol is produced by an aerosol generation system.

10. The process according to claim 8 wherein the aerosol is produced by nebulization.

11. The process according to claim 8 wherein the aerosol is produced by ultrasonic nebulization.

12. A device for preparing a doped pyrogenically produced oxide of a metal and/or a non-metal, comprising a pyrolysis reactor including a heater, a source of aerosol, a conduit to convey said aerosol to said heater, said conduit being jacketed by a mantel downstream from said heater and projecting into a combustion chamber, said mantel terminating in a nozzle for producing a flame for flame pyrolysis wherein the additional conduit for introducing the aerosol into the chamber is axially in a burner chamber for preparing said pyrogenic oxide, wherein the conduit terminates upstream of the burner nozzle.