Patent Application
20140166921
The present invention relates to ionic liquid, particularly to a double-center bipyridyl cationic ion liquid, preparation method thereof, an electrolyte comprising the same, and preparation method thereof.
Ionic liquids are in the liquid state at room temperature range (generally below 100° C.), which consist of organic cations and inorganic anions (or organic anions). Ionic liquids which are regulable have been recognized as designer solvents, because ionic structure may be changed as needed by designer. The first ionic liquid, ethylamine nitrate was discovered as early as 1914. However, development in this field has been slowing down after the first discovery. Until 1992, when Wikes's team successfully synthesized 1-ethyl-3-methyl imidazolium tetrafluoroborates ionic liquid ([EMIM]BF4) having low melting point, resistance to hydrolyzation, and good stability, studies on ionic liquids were developed rapidly. Since then a series of ionic liquids systems have been developed. Ionic liquids are primarily used for electrochemical investigation purpose. Recently, ionic liquids have drawn more public attention because ionic liquids can be used as green solvents for organic and macromolecular synthesis.
Compared to conventional organic solvent and electrolyte, ionic liquids exhibit a range of advantageous properties such as (1) having a melting point below or near room temperature, being liquid in a wide temperature range; (2) having a low vapor pressure, being non-volatile, colorless and odorless; (3) having a wide and stable temperature range, good chemical stability and wide electrochemical potential window range; (4) having a excellent solubility, can dissolve lots of inorganics and organics (5) having no ignition point, and being nonflammable; (6) can be recycled, environmentally friendly. So ionic liquids are promising electrolytes for double-layer capacitors.
Traditional electrolytes are prone to decompose at high voltage, causing a sharp rise of internal resistance and a rapid fall of capacitance. Therefore stability of electrolyte has always been the critical factor in specific energy of capacitor.
In view of this, it is necessary to provide double-center bipyridyl cationic ion liquid of resistance to decomposition at high voltage.
In addition, it is also necessary to provide a method for preparing the double-center bipyridyl cationic ion liquid.
In addition, it is also necessary to provide a method for preparing organic electrolyte comprising the double-center bipyridyl cationic ion liquid, and preparation method thereof.
A double-center bipyridyl cationic ion liquid having the following structural formula:
wherein Y− is BF4−, PF6−, (CF3SO2)2N− or (FSO2)2N−.
A method for preparing double-center bipyridyl cationic ion liquid, comprising:
step 1: in atmosphere of protective gas, mixing bipyridine with haloalkane according to molar ratio of 1:2˜1:2.5, heating to 60˜80° C.; reacting while stirring to obtain dialkyl bipyridyl halide; wherein said haloalkane is methoxyethoxymethyl chloride or methoxyethoxymethyl bromide;
step 2: mixing the dialkyl bipyridyl halide prepared in step 1 with salt having a formula of M+Y− in a molar ratio of 1:2, then adding into deionized water; carrying out an ion exchange reaction while stirring; then obtaining a double-center bipyridyl cationic ion liquid having the following structural formula:
wherein M+ is Na+, K+ or NH4+, Y− is BF4−, PF6−, (CF3SO2)2N− or (FSO2)2N−.
Preferably, in step 1, the step of reacting bipyridine with haloalkane is carried out for 24˜72 h; reaction liquid is cooled and then washed with ethyl acetate to get washed matter; the washed matter is dried under vacuum to obtain purified dialkyl bipyridyl halide.
Preferably, in step 1, atmosphere of protective gas is nitrogen or argon.
Preferably, the ion exchange reaction of step 2 is carried out at room temperature for 8˜24 h.
Preferably, step 2 further comprises purification of double-center bipyridyl cationic ion liquid, comprising:
subjecting mixed liquid obtained after the reaction of dialkyl bipyridyl halide with salt having a formula of M+Y− to extraction with dichloromethane to get aqueous phase, until no precipitation occurs in the aqueous phase when saturated aqueous solution of AgNO3 is added;
evaporating and concentrating extracts in dichloromethane then drying under vacuum to obtain purified double-center bipyridyl cationic ion liquid.
An organic electrolyte, comprising double-center bipyridyl cationic ion liquid, organic solvent and lithium salt, wherein said double-center bipyridyl cationic ion liquid has the following structural formula:
wherein Y− is BF4−, PF6−, (CF3SO2)2N− or (FSO2)2N−, mass ratio of said organic solvent to said double-center bipyridyl cationic ion liquid is in the range of 0˜100, concentration of said lithium salt is in the range of 0.3 mol/L˜1.2 mol/L.
Preferably, lithium salt is at least one of lithium tetrafluoroborate, lithium hexafluorophosphate, lithium bis(trifluoromethanesulphonyl)imide and lithium bis(fluorosulfonyl)imide.
Preferably, organic solvent is at least one of ethylene carbonate, methyl ethyl carbonate, dimethyl carbonate and ethyl propionate.
A method for preparing organic electrolyte, comprising:
step 1: in atmosphere of protective gas, mixing bipyridine with haloalkane according to molar ratio of 1:2˜1:2.5, heating to 60˜80° C.; reacting while stirring to obtain dialkyl bipyridyl halide; wherein said haloalkane is methoxyethoxymethyl chloride or methoxyethoxymethyl bromide;
step 2: mixing the dialkyl bipyridyl halide prepared in step 1 with salt having a formula of M+Y− in a molar ratio of 1:2, then adding into deionized water; carrying out an ion exchange reaction while stirring; then obtaining a double-center bipyridyl cationic ion liquid having the following structural formula:
wherein M+ is Na+, K+ or NH4+, Y− is BF4−, PF6−, (CF3SO2)2N− or (FSO2)2N−;
step 3: providing organic solvent, adding said double-center bipyridyl cationic ion liquid into said organic solvent while stirring uniformly; wherein mass ratio of said organic solvent to said double-center bipyridyl cationic ion liquid is in the range of 0˜100;
step 4: adding lithium salt into mixed liquid of organic solvent and double-center bipyridyl cationic ion liquid; stirring to dissolve lithium salt then obtaining said organic electrolyte; wherein concentration of said lithium salt in organic electrolyte is in the range of 0.3˜1.2 mol/L.
Electrochemical potential window range of such double-center bipyridyl cationic ion liquid is out of 4V, indicating good electrochemical stability, and resistance to decomposition at high voltage. Thus, organic electrolyte comprising such double-center bipyridyl cationic ion liquid has good stability at high charging voltage.
The FIGURE is standard charge-discharge curve obtained by conducting conventional test on super capacitor comprising organic electrolyte prepared in Example 6 and electrode material.
Further description of double-center bipyridyl cationic ion liquid, preparation method thereof and use thereof will be illustrated, which combined with preferred embodiments and the drawings
In one embodiment, double-center bipyridyl cationic ion liquid has the following structural formula:
wherein Y− is BF4−, PF6−, (CF3SO2)2N− or (FSO2)2N−.
Electrochemical potential window range of such double-center bipyridyl cationic ion liquid is out of 4V, indicating good electrochemical stability, and resistance to decomposition at high voltage.
Alkoxyl structure is introduced into side chain of such double-center bipyridyl cationic ion liquid. Viscosity of ionic liquids is reduced. Besides, such oxygen-containing functional groups are beneficial for complexing with lithium ions in electrolyte and improvement of solubility of lithium salts.
Provided is a method for preparing the double-center bipyridyl cationic ion liquid, comprising:
step S11: in protective atmosphere of nitrogen or argon, mixing bipyridine with haloalkane according to molar ratio of 1:2˜1:2.5, heating to 60˜80° C.; reacting while stirring to obtain dialkyl bipyridyl halide;
The reaction equation is:
Purified dialkyl bipyridyl halide is obtained by drying washed matter under vacuum at 80° C. for 48 h.
Haloalkane can be methoxyethoxymethyl chloride
Reaction can be conducted and stirred for 24˜72 h. Generally, double-center bipyridyl cationic ion liquid should react with haloalkane completely.
The reaction between bipyridine and haloalkane is not limited to conduct in protective atmosphere of nitrogen or argon, any inert gas may also be employed.
The purification of dialkyl bipyridyl halide is carried out by washing cooled reaction liquid with ethyl acetate for three times, but not limited to, other methods in the art may also be employed to purify dialkyl bipyridyl halide.
Step S12: mixing the dialkyl bipyridyl halide prepared in S11 with salt having a formula of M+Y− in a molar ratio of 1:2, then adding into deionized water; reacting at room temperature for 8˜24 h; subjecting mixed liquid obtained after the ion exchange reaction of dialkyl bipyridyl halide with salt having a formula of M+Y− to extraction with dichloromethane to get aqueous phase, until no precipitation occurs in the aqueous phase when saturated aqueous solution of AgNO3 is added; evaporating and concentrating extracts in dichloromethane then drying under vacuum at 80° C. for 48 h to obtain purified double-center bipyridyl cationic ion liquid;
wherein M+ is Na+, K+ or NH4+, Y− is BF4−, PF6−, (CF3SO2)2N− or (FSO2)2N−.
The reaction equation is:
It will be understood that, the time of ion exchange reaction is not limited to 8˜24 h, but dialkyl bipyridyl halide should react with salt having a formula of M+Y− completely; other commonly encountered solvents or methods in the art may also be employed to separate and purify double-center bipyridyl cationic ion liquid.
Preparation method of the double-center bipyridyl cationic ion liquid is simple, and solvent of low toxicity is used during the process. So the preparation is low-cost, a large scale preparation can be easily achieved.
In one embodiment, organic electrolyte comprises double-center bipyridyl cationic ion liquid, organic solvent and lithium salt.
Double-center bipyridyl cationic ion liquid having the following structural formula:
wherein Y− is BF4−, PF6−, (CF3SO2)2N− or (FSO2)2N−.
Mass ratio of organic solvent to double-center bipyridyl cationic ion liquid is greater than or equal to 0 and less than or equal to 100. Organic solvent can be at least one of ethylene carbonate, ethyl methyl carbonate, dimethyl carbonate and ethyl propionate (EP).
Concentration of lithium salt in organic electrolyte is in the range of 0.3˜1.2 mol/L.
In some preferred embodiments, concentration of lithium salt in organic electrolyte is 1 mol/L.
Lithium salt can be at least one of lithium tetrafluoroborate (LiBF4), lithium hexafluorophosphate (LiPF6), lithium bis(trifluoromethanesulphonyl)imide (LiTFSI) and lithium bis(fluorosulfonyl)imide (LiFSI).
Provided is a method for preparing the electrolyte, comprising:
S21: in protective atmosphere of nitrogen or argon, mixing bipyridine with haloalkane according to molar ratio of 1:2˜1:2.5, heating to 60˜80° C.; reacting while stirring to obtain dialkyl bipyridyl halide;
Purified dialkyl bipyridyl halide is obtained by drying washed matter under vacuum at 80° C. for 48 h.
Haloalkane can be methoxyethoxymethyl chloride
Reaction can be conducted and stirred for 24˜72 h. Generally, double-center bipyridyl cationic ion liquid should react with haloalkane completely.
The reaction between bipyridine and haloalkane is not limited to conduct in protective atmosphere of nitrogen or argon, any inert gas may also be employed.
The purification of dialkyl bipyridyl halide is carried out by washing cooled reaction liquid with ethyl acetate for three times, but not limited to, other methods in the art may also be employed to purify dialkyl bipyridyl halide.
S22: mixing the dialkyl bipyridyl halide prepared in step S21 with salt having a formula of M+YΔ in a molar ratio of 1:2, then adding into deionized water; reacting at room temperature for 8∞24 h; subjecting mixed liquid obtained after the ion exchange reaction of dialkyl bipyridyl halide with salt having a formula of M+Y− to extraction with dichloromethane to get aqueous phase, until no precipitation occurs in the aqueous phase when saturated aqueous solution of AgNO3 is added; evaporating and concentrating extracts in dichloromethane then drying under vacuum at 80° C. for 48 h to obtain purified double-center bipyridyl cationic ion liquid;
wherein M+ is Na+, K+ or NH4+, Y− is BF4−, PF6−, (CF3SO2)2N− or (FSO2)2N−.
It will be understood that, the time of ion exchange reaction is not limited to 8˜24 h, but dialkyl bipyridyl halide should react with salt having a formula of M+Y− completely; other commonly encountered solvents or methods in the art may also be employed to separate and purify double-center bipyridyl cationic ion liquid.
S23: providing organic solvent, adding double-center bipyridyl cationic ion liquid into organic solvent while stirring uniformly; wherein mass ratio of organic solvent to double-center bipyridyl cationic ion liquid is in the range of 0˜100;
Organic solvent is at least one of ethylene carbonate, methyl ethyl carbonate, dimethyl carbonate and ethyl propionate (EP).
Preferably, Step S23 is carried out under the protection of inert gas, the inert gas can be nitrogen or argon.
S24: adding lithium salt into mixed liquid of organic solvent and double-center bipyridyl cationic ion liquid; stirring to dissolve lithium salt then obtaining organic electrolyte.
Concentration of lithium salt in organic electrolyte is in the range of 0.3˜1.2 mol/L.
In some preferred embodiments, concentration of lithium salt is 1 mol/L.
Lithium salt can be at least one of lithium tetrafluoroborate (LiBF4), lithium hexafluorophosphate (LiPF6), lithium bis(trifluoromethanesulphonyl)imide (LiTFSI) and lithium bis(fluorosulfonyl)imide (LiFSI).
Electrochemical potential window range of such double-center bipyridyl cationic ion liquid is out of 4V, indicating good electrochemical stability, and resistance to decomposition at high voltage, thus, organic electrolyte comprising such double-center bipyridyl cationic ion liquid has good stability at high charging voltage. Lithium salt provides lithium ions when employed in lithium ion batteries or lithium ion capacitors, while organic solvent could reduce viscosity of electrolyte.
The present invention will be described below in detail referring to preferred embodiments.
Synthesis of double-center bipyridyl tetrafluoroborate.
To a 250-mL flask, 1 mol of bipyridine and 2.1 mol of methoxyethoxymethyl chloride were added separately. In the protective atmosphere of N2, temperature was elevated to 70° C. The reaction was started and stirred for 36 h. After being allowed to stand and cool down, the reaction mixture was washed with ethyl acetate for three times. Drying under vacuum at 80° C., light yellow solid, i.e. dialkyl bipyridyl chloride was obtained in a yield of 78%.
To a 500-mL flask, 0.5 mol of dialkyl bipyridyl chloride, 1 mol of NaBF4 and 120 mL of deionized water were added at room temperature while stirring for 16-24 h. After the reaction, mixed liquid was subjected to extraction with 250 mL of dichloromethane for three times, liquid extracts were combined. Then back-extracted with 60 mL of deionized water each time to get aqueous phase, until no further precipitation occurs in the aqueous phase when saturated aqueous solution of AgNO3 was added. Dichloromethane phase was evaporated and concentrated by rotary evaporator then dried under vacuum at 80° C. for 48 h to give light yellow solid, i.e. double-center bipyridyl tetrafluoroborate.
Hydrogen-1 nuclear magnetic resonance (NMR) spectrum of double-center bipyridyl tetrafluoroborate of this embodiment shows: 1H NMR ((CD3)2CO, 400 MHz, ppm): 8.69 (d, 4H), 7.63 (d, 4H), 5.92 (s, 4H), 3.64 (m, 8H), 3.24 (s, 6H).
Synthesis of double-center bipyridyl hexafluorophosphate.
To a 250-mL flask, 1 mol of bipyridine and 2.1 mol of methoxyethoxymethyl bromide were added separately. In the protective atmosphere of Are, temperature was elevated to 70° C. The reaction was started and stirred for 36 h. After being allowed to stand and cool down, the reaction mixture was washed with ethyl acetate for three times. Drying under vacuum at 80° C., light yellow solid, i.e. dialkyl bipyridyl bromide was obtained in a yield of 80%.
To a 500-mL flask, 0.5 mol of dialkyl bipyridyl bromide, 1 mol of KPF6 and 120 mL of deionized water were added at room temperature while stirring for 16 h. After the reaction, mixed liquid was subjected to extraction with 250 mL of dichloromethane for three times, liquid extracts were combined. Then back-extracted with 60 mL of deionized water each time to get aqueous phase, until no further precipitation occurs in the aqueous phase when saturated aqueous solution of AgNO3 was added. Dichloromethane phase was evaporated and concentrated by rotary evaporator then dried under vacuum at 80 ° C. for 48 h to give light yellow solid, i.e. double-center bipyridyl hexafluorophosphate.
Hydrogen-1 nuclear magnetic resonance (NMR) spectrum of double-center bipyridyl hexafluorophosphate of this embodiment shows: 1H NMR ((CD3)2CO, 400 MHz, ppm): 8.70 (d, 4H), 7.63 (d, 4H), 5.93 (s, 4H), 3.64 (m, 8H), 3.25 (s, 6H).
Synthesis of double-center bipyridyl trifluoromethylsulfonyl imide.
To a 500-mL flask, 0.5 mol of dialkyl bipyridyl chloride (prepared in Example 1), 1 mol of potassium trifluoromethanesulfonyl imide (KTFSI), and 120 mL of deionized water were added at room temperature while stirring for 16 h. After the reaction, mixed liquid was subjected to extraction with 250 mL of dichloromethane for three times, liquid extracts were combined. Then back-extracted with 60 mL of deionized water each time to get aqueous phase, until no further precipitation occurs in the aqueous phase when saturated aqueous solution of AgNO3 was added. Dichloromethane phase was evaporated and concentrated by rotary evaporator then dried under vacuum at 80° C. for 48 h to give light yellow solid, i.e. double-center bipyridyl trifluoromethylsulfonyl imide.
Hydrogen-1 nuclear magnetic resonance (NMR) spectrum of double-center bipyridyl trifluoromethylsulfonyl imide of this embodiment shows: 1H NMR ((CD3)2CO, 400 MHz, ppm): 8.71 (d, 4H), 7.65 (d, 4H), 5.95 (s, 4H), 3.66 (m, 8H), 3.26 (s, 6H).
Synthesis of double-center bipyridyl trifluoromethansulphonate.
To a 500-mL flask, 0.5 mol of dialkyl bipyridyl bromide (prepared in Example 2), 1 mol of CF3SO3Na and 120 mL of deionized water were added at room temperature while stirring for 16 h. After the reaction, mixed liquid was subjected to extraction with 250 mL of dichloromethane for three times, liquid extracts were combined. Then back-extracted with 60 mL of deionized water each time to get aqueous phase, until no further precipitation occurs in the aqueous phase when saturated aqueous solution of AgNO3 was added. Dichloromethane phase was evaporated and concentrated by rotary evaporator then dried under vacuum at 80 ° C. for 48 h to give light yellow solid, i.e. double-center bipyridyl trifluoromethansulphonate.
Hydrogen-1 nuclear magnetic resonance (NMR) spectrum of double-center bipyridyl trifluoromethansulphonate of this embodiment shows: 1H NMR ((CD3)2CO, 400 MHz, ppm): 8.70 (d, 4H), 7.63 (d, 4H), 5.93 (s, 4H), 3.65 (m, 8H), 3.23 (s, 6H).
Synthesis of double-center bipyridyl bis(fluorosulfonyl)imide.
See Example 1 for preparation details. 1 mol of NaBF4 was replaced with 1 mol of potassium bis(fluorosulfonyl)imide ((FSO2)2NK).
Hydrogen-1 nuclear magnetic resonance (NMR) spectrum of double-center bipyridyl bis(fluorosulfonyl)imide of this embodiment shows: 1H NMR ((CD3)2CO, 400 MHz, ppm): 8.70 (d, 4H), 7.64 (d, 4H), 5.92 (s, 4H), 3.66 (m, 8H), 3.25 (s, 6H).
In protective atmosphere of N2, organic solvent was prepared by mixing ethylene carbonate (EC), ethyl methyl carbonate (EMC), dimethyl carbonate (DMC) and ethyl propionate (EP) in a molar ratio of 2:5:2:3 (abbr. mixed solventEC+EMC+DMC+EP). Double-center bipyridyl tetrafluoroborate (prepared in Example 1) ionic liquid was added according to the mass ratio of mixed solventEC+EMC+DMC+EP: double-center bipyridyl ionic liquid=10:1. The mixture was heated to 40° C. and stirred to get uniform organic phase. At last, a certain amount of lithium salt (LiBF4 in this embodiment) was added, the molar concentration of lithium salt was 1 mol/L (amount of lithium salt was determined by volume of organic phase VEC+EMC+DMC+EP+double-center bipyridyl ionic liquid). Lithium salt was completely dissolved by stirring constantly. The desired organic electrolyte was obtained.
The FIGURE is charge-discharge curve of button cell comprising graphene as electrode material and organic electrolyte prepared in this embodiment. The charge-discharge test was performed on a CHI660A electrochemical workstation at a constant current 0.25 A/g. The electrochemical potential window ranges from 0 to 3.2V.
It can be seen from the FIGURE that electrolyte as prepared in this embodiment is suitable for super capacitors, and electrolyte has good stability at a charging voltage of 3.2 V.
In protective atmosphere of Ar2, 100 mL of double-center bipyridyl hexafluorophosphate (prepared in Example 2) ionic liquid was added and heated to 40° C. while stirring. A certain amount of lithium salt (LiPF6 in this embodiment) was added, the molar concentration of lithium salt was 0.3 mol/L. Lithium salt was completely dissolved by stirring constantly. The desired organic electrolyte was obtained.
In protective atmosphere of N2, organic solvent was prepared by mixing ethylene carbonate (EC), ethyl methyl carbonate (EMC), dimethyl carbonate (DMC) and ethyl propionate (EP) in a molar ratio of 2:5:2:3 (abbr. mixed solventEC+EMC+DMC+EP). Double-center bipyridyl bis(trifluoromethylsulfonyl)imide (prepared in Example 3) ionic liquid was added according to the mass ratio of mixed solventEC+EMC+DMC+EP: double-center bipyridyl ionic liquid=1:100. The mixture was heated to 40° C. and stirred to get uniform organic phase. At last, a certain amount of lithium salt (LiTFSI in this embodiment) was added, the molar concentration of lithium salt was 0.5 mol/L (amount of lithium salt was determined by volume of organic phase VEC+EMC+DMC+EP+double-center bipyridyl ionic liquid). Lithium salt was completely dissolved by stirring constantly. The desired organic electrolyte was obtained.
In protective atmosphere of Ar2, organic solvent was prepared by mixing ethylene carbonate (EC), ethyl methyl carbonate (EMC), dimethyl carbonate (DMC) and ethyl propionate (EP) in a molar ratio of 2:5:2:3 (abbr. mixed solventEC+EMC+DMC+EP). Double-center bipyridyl bis(fluorosulfonyl)imide (prepared in Example 4) ionic liquid was added according to the mass ratio of mixed solventEC+EMC+DMC+EP: double-center bipyridyl ionic liquid=1:10. The mixture was heated to 40° C. and stirred to get uniform organic phase. At last, a certain amount of lithium salt (LiFSI in this embodiment) was added, the molar concentration of lithium salt was 0.7 mol/L (amount of lithium salt was determined by volume of organic phase VEC+EMC+DMC+EP+double-center bipyridyl ionic liquid). Lithium salt was completely dissolved by stirring constantly. The desired organic electrolyte was obtained.
In protective atmosphere of N2, organic solvent was prepared by mixing ethylene carbonate (EC), ethyl methyl carbonate (EMC), dimethyl carbonate (DMC) and ethyl propionate (EP) in a molar ratio of 2:5:2:3 (abbr. mixed solventEC+EMC+DMC+EP). Double-center bipyridyl tetrafluoroborate ionic liquid was added according to the mass ratio of mixed solventEC+EMC+DMC+EP: double-center bipyridyl ionic liquid=1:1. The mixture was heated to 40° C. and stirred to get uniform organic phase. At last, a certain amount of lithium salt (in this embodiment, mixture of LiBF4 and LiPF6 in a molar ratio of 1:1) was added, the molar concentration of lithium salt was 0.9 mol/L (amount of lithium salt was determined by volume of organic phase VEC+EMC+DMC+EP+double-center bipyridyl ionic liquid). Lithium salt was completely dissolved by stirring constantly. The desired organic electrolyte was obtained.
In protective atmosphere of Ar2, organic solvent was prepared by mixing ethylene carbonate (EC), ethyl methyl carbonate (EMC), dimethyl carbonate (DMC) and ethyl propionate (EP) in a molar ratio of 2:5:2:3 (abbr. mixed solventEC+EMC+DMC+EP). Double-center bipyridyl ionic liquid (in this embodiment, mixture of double-center bipyridyl tetrafluoroborate and double-center bipyridyl hexafluorophosphate in a molar ratio of 1:1) was added according to the mass ratio of mixed solventEC+EMC+DMC+EP: double-center bipyridyl ionic liquid=40:1. The mixture was heated to 40° C. and stirred to get uniform organic phase. At last, a certain amount of lithium salt (in this embodiment, mixture of LiTFSI and LiFSI in a molar ratio of 1:1) was added, the molar concentration of lithium salt was 1 mol/L (amount of lithium salt was determined by volume of organic phase VEC+EMC+DMC+EP+double-center bipyridyl ionic liquid). Lithium salt was completely dissolved by stirring constantly. The desired organic electrolyte was obtained.
In protective atmosphere of Ar2, organic solvent was prepared by mixing ethylene carbonate (EC), ethyl methyl carbonate (EMC), dimethyl carbonate (DMC) and ethyl propionate (EP) in a molar ratio of 2:5:2:3 (abbr. mixed solventEC+EMC+DMC+EP). Double-center bipyridyl ionic liquid (in this embodiment, mixture of double-center bipyridyl bis(trifluoromethylsulfonyl)imide and double-center bipyridyl bis(fluorosulfonyl)imide in a molar ratio of 1:1) was added according to the mass ratio of mixed solventEC+EMC+DMC+EP: double-center bipyridyl ionic liquid=70:1. The mixture was heated to 40° C. and stirred to get uniform organic phase. At last, a certain amount of lithium salt (in this embodiment, mixture of LiPF6 and LiTFSI in a molar ratio of 1:1) was added, the molar concentration of lithium salt was 1.1 mol/L (amount of lithium salt was determined by volume of organic phase VEC+EMC+DMC+EP+double-center bipyridyl ionic liquid). Lithium salt was completely dissolved by stirring constantly. The desired organic electrolyte was obtained.
In protective atmosphere of N2, organic solvent was prepared by mixing ethylene carbonate (EC), ethyl methyl carbonate (EMC), dimethyl carbonate (DMC) and ethyl propionate (EP) in a molar ratio of 2:5:2:3 (abbr. mixed solventEC+EMC+DMC+EP). Double-center bipyridyl bis(trifluoromethylsulfonyl)imid ionic liquid was added according to the mass ratio of mixed solventEC+EMC+DMC+EP: double-center bipyridyl ionic liquid=100:1. The mixture was heated to 40° C. and stirred to get uniform organic phase. At last, a certain amount of lithium salt (LiTFSI in this embodiment) was added, the molar concentration of lithium salt was 1.2 mol/L (amount of lithium salt was determined by volume of organic phase VEC+EMC+DMC+EP+double-center bipyridyl ionic liquid). Lithium salt was completely dissolved by stirring constantly. The desired organic electrolyte was obtained.
While the present invention has been described with reference to particular embodiments, it will be understood that the embodiments are illustrative and that the invention scope is not so limited. Alternative embodiments of the present invention will become apparent to those having ordinary skill in the art to which the present invention pertains. Such alternate embodiments are considered to be encompassed within the spirit and scope of the present invention. Accordingly, the scope of the present invention is described by the appended claims and is supported by the foregoing description.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/CN2011/079118 | 8/30/2011 | WO | 00 | 1/22/2014 |