Patent Application
20200319417
The present disclosure is generally directed to downhole strain sensing cables, and more particularly to downhole strain sensing cables having relatively small profiles and operable at extreme temperatures.
In industries such as the oil and gas industry, wells are utilized to provide access to raw materials. A variety of cables may be utilized in the wells, and various of these cables may perform specified functions. One type of cable that is utilized in well settings is a downhole strain sensing cable. These cables are provided in the well to determine the strain that the well casing is exposed to during installation and operation processes. This strain can be correlated to earth movements, shifts and well wall movements. Typically, these cables are sealed to the well casings to monitor the movement of the well casing via resulting cable movement and strain determination.
One issue with known downhole strain sensing cables is vulnerability to loading at extreme temperature ranges. The exposure to extreme temperatures can cause the optical characteristics of the cables to be damaged and potentially cause cable failure. Further, cables which are designed to withstand such temperatures have relatively large profiles, making the cables heavy and intrusive.
Accordingly, improved downhole sensing cables are desired in the art. In particular, downhole sensing cables which can withstand extreme temperatures while maintaining proper optical characteristics, and which have relatively small profiles, would be advantageous.
Aspects and advantages of the invention will be set forth in part in the following description, or may be obvious from the description, or may be learned through practice of the invention.
In accordance with one embodiment of the present disclosure, a downhole strain sensing cable is provided. The cable includes a core optical unit which includes a plurality of optical fibers. A fiber-reinforced polymer matrix layer surrounds and contacts the core optical unit. An extrusion layer surrounds and contacts the fiber-reinforced polymer matrix layer. An outer metal tube surrounds and contacts the extrusion layer.
These and other features, aspects and advantages of the present invention will become better understood with reference to the following description and appended claims. The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention.
A full and enabling disclosure of the present invention, including the best mode thereof, directed to one of ordinary skill in the art, is set forth in the specification, which makes reference to the appended figures, in which:
Reference now will be made in detail to embodiments of the invention, one or more examples of which are illustrated in the drawings. Each example is provided by way of explanation of the invention, not limitation of the invention. In fact, it will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope or spirit of the invention. For instance, features illustrated or described as part of one embodiment can be used with another embodiment to yield a still further embodiment. Thus, it is intended that the present invention covers such modifications and variations as come within the scope of the appended claims and their equivalents.
The present disclosure generally provides an improved downhole strain sensing cable. The cable includes a core optical unit which includes a plurality of optical fibers. A fiber-reinforced polymer matrix layer surrounds and contacts the core optical unit. An extrusion layer surrounds and contacts the fiber-reinforced polymer matrix layer. An outer metal tube surrounds and contacts the extrusion layer. In exemplary embodiments, a maximum outer diameter of the outer metal tube is less than 0.3 inches, such as between approximately 0.28 and approximately 0.22 inches, such as approximately 0.25 inches. Downhole strain sensing cables in accordance with the present disclosure advantageously can withstand extreme temperatures, such as at least up to between 150 degree Celsius and 165 degrees Celsius, while maintaining proper optical characteristics. Additionally, such cables in accordance with the present disclosure can advantageously have relatively small profiles.
Referring now to
A cladding 24 may surround and encase the optical fibers 22. The cladding in exemplary embodiments may be formed from silicone. A jacket 26 may surround and contact the cladding 24. The jacket 26 may be formed from a suitable fluoropolymer, such as a polymethylpentene (i.e. TPX® manufactured by Mitsui Chemicals, Inc.).
Notably, the cladding 24 and jacket 26 may be free from reinforcing fibers (or any fibers other than optical fibers 22).
The core optical unit 20 (such as the jacket 26 thereof) may have a relatively small maximum outer diameter 21. For example, the maximum outer diameter 21 may be between 0.6 millimeters and 1.09 millimeters, such as between 0.7 millimeters and 1 millimeter, such as between 0.8 millimeters and 0.9 millimeters, such as approximately 0.84 millimeters.
A fiber-reinforced polymer matrix layer 30 may surround and contact the core optical unit 20 (such as the jacket 26 thereof). The layer 30 advantageously protects the unit 20 from sudden impacts and reduces the risk of damage to the optical fibers 22. The layer 30 may include a plurality of fibers embedded in a polymer matrix. The fiber may, for example, be glass fibers or alternatively carbon fibers or other suitable reinforcing fibers. The polymer matrix may be formed from a suitable thermoplastic or thermoset, such as in exemplary embodiments a polyester (such as an unsaturated polyester) resin, an acrylic-based resin, a terephthalic resin, or a vinyl ester resin.
The layer 30 may have a relatively small maximum outer diameter 31. For example, the maximum outer diameter 31 may be between 3 millimeters and 3.3 millimeters, such as between 3.1 millimeters and 3.3 millimeters, such as approximately 3.2 millimeters.
An extrusion layer 40 may surround and contact the fiber-reinforced polymer matrix layer 30. The extrusion layer 40 generally seals the fiber-reinforced polymer matrix layer 30 within an outer metal tube 50. The extrusion layer 40 may be formed from an extrusion of a foamed polymer, such as in exemplary embodiments a polypropylene. Notably, the extrusion layer 40 may be free from reinforcing fibers.
The layer 40 may have a relatively small maximum outer diameter 41. For example, the maximum outer diameter 41 may be between 4 millimeters and 4.8 millimeters, such as between 4.2 millimeters and 4.6 millimeters, such as between 4.5 millimeters and 4.6 millimeters, such as approximately 4.57 millimeters.
An outer metal tube 50 may surround and contact the extrusion layer 40. The outer metal tube 50 protects the various interior components 20, 30, 40, thus acting as a protective layer for the cable 10 generally. The outer metal tube 50 may be the outermost layer defining an exterior surface of the cable 10. In exemplary embodiments, the outer metal tube 50 is formed from a steel, such as a stainless steel. 825, 316 or 625 grade steels are suitable for use as outer metal tube 50.
The outer metal tube 50 may have a relatively small maximum outer diameter 51. For example, the maximum outer diameter 51 may be less than 0.3 inches, such as between approximately 0.28 and approximately 0.22 inches, such as approximately 0.25 inches.
In general, due to the contact therebetween as discussed above, the layers 20, 30, 40, 50 of the cable 10 advantageously behave and move as a single unit when strain-inducing events are encountered, such as earth movements, shifts and well wall movements. Further, as discussed herein, cables 10 having layers 20, 30, 40, 50 as discussed herein can advantageously withstand relatively high temperatures, such as at least up to between 150 degree Celsius and 165 degrees Celsius, while maintaining proper optical characteristics.
Cables 10 in accordance with the present disclosure may advantageously be rated to 150 degrees Celsius, such as in some embodiments to 165 degrees Celsius. Such rating may be based on BOTDA and tensile tests after ageing at 150 degrees Celsius or 165 degrees Celsius. A cable is considered rated to 150 degrees Celsius or 165 degrees Celsius in accordance with the present disclosure if a sample of the cable aged to 150 degrees Celsius or 165 degrees Celsius as discussed herein has test results that are equal to or better than those of a comparative room temperature aged-sample.
Ageing and tensile testing performed on cables 10 in accordance with the present disclosure were performed in accordance IEC-60794-1-2 standards. Cables being qualified to 150 degree Celsius or 165 degree Celsius ratings were constructed in 1300 meter sections having four optical fibers as follows: one VERRILLON® FBR00190 multi-mode optical fiber, one VERRILLON® FBR00248 multi-mode optical fiber, one VERRILLON® FBR00270 single mode fiber, and one VERRILLON® FBR00293 single mode fiber. A silicone cladding and TPX jacket surround the optical fibers. A fiber-reinforced polymer matrix layer which includes glass fibers embedded in an unsaturated polyester-based resin surrounds the jacket, and a foamed polypropylene extrusion layer surrounds the fiber-reinforced polymer matrix layer. A stainless steel outer tube surrounds the extrusion layer. A maximum outer diameter of the stainless steel outer tube is approximately 0.25 inches, and a maximum outer diameter of the jacket is approximately 0.84 millimeters.
Ageing was performed by exposing cables to 150 degree Celsius temperature and 165 degree Celsius temperature, respectively, for 30 days. For tensile testing, samples were tested in increments of 50 pounds and held at each load for a period of 5 minutes. Test results for 150 degree Celsius- and 165 degree Celsius-rated samples were equal to or better than those of a comparative room temperature aged-sample. For example, all cables began to yield at 2200 lbf and at 0.48% strain, indicating no degradation in performance for the 150 degree Celsius- and 165 degree Celsius-rated samples. In addition, the breaking strengths of the room temperature aged-sample and the 150 degree Celsius-rated sample were the same, and the breaking strength of the 165 degree Celsius-rated sample was approximately 1000 lbf higher.
BOTDA testing was performed concurrently with ageing. Test results for 150 degree Celsius- and 165 degree Celsius-rated samples were equal to or better than those of a comparative room temperature aged-sample. For example, BOTDA strain levels indicated no changes in the 150 degree Celsius- and 165 degree Celsius-rated samples as compared to the room temperature aged-sample.
This written description uses examples to disclose the invention, including the best mode, and also to enable any person skilled in the art to practice the invention, including making and using any devices or systems and performing any incorporated methods. The patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they include structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal languages of the claims.
This application is based upon and claims the benefit of priority from U.S. Provisional Patent Application No. 62/345,402, filed Jun. 3, 2016, the disclosure of which is incorporated by reference herein in its entirety.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2017/035656 | 6/2/2017 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62345402 | Jun 2016 | US |