Ductile brazing alloy of copper-nickel-silicon-titanium

Information

  • Patent Grant
  • 4897243
  • Patent Number
    4,897,243
  • Date Filed
    Monday, November 7, 1988
    36 years ago
  • Date Issued
    Tuesday, January 30, 1990
    35 years ago
Abstract
A brazing alloy useful for brazing ceramics having the following composition, in weight percent: 0.3 to 5% titanium; 2 to 15% nickel; 0.25 to 4% silicon; balance copper.
Description

This invention concerns a ductile brazing alloy of copper-nickel-silicon-titanium which can be used for brazing ceramics. Such an alloy is disclosed in U.S. Pat. No. 4,426,033, which discloses alloys within the broad compositional range of 50 to 98.75 wt. % copper, 0.25 to 5 wt. % titanium, vanadium or zirconium, 1 to 45 wt. % silicon, tin, germanium, manganese, nickel or cobalt.
I have found that in order to have a brazing alloy which does not grey upon cooling, but remains metallic shiny, the composition of the alloy must be controlled within narrower limits, and especially the amounts of nickel and silicon. An alloy as per this invention has the following composition, in weight percent: 0.3 to 5% titanium; 2 to 15% nickel; 0.25 to 4% silicon; balance copper.
In the following examples, the compositions are expressed in weight percent.





EXAMPLE 1 (SAMPLE 95-54)
An alloy of 88% Cu, 2% Si, 7.0% Ni, 3% Ti was prepared by melting a 6 gram button on a water cooled copper crucible using tungsten electrode and arc melted under argon atmosphere. The alloy was rolled to a four mil thickness foil. The melting temperature was determined to be 1083.degree. C. liquidus/1071.degree. C. solidus. The foil was placed between Al-995 alumina ceramic and Alloy 42 (42 Ni-58 Fe) and type 410 stainless steel (Fe-Cr) and brazed at 1110.degree. C. under 10.sup.-5 torr vacuum. The brazing alloy formed a small fillet on both Alloy 42 and the stainless steel and joined both to alumina. The braze alloy after brazing showed a yellowish bright metallic color.
EXAMPLE 2 (Sample 95-55)
An alloy of 92% Cu, 1% Si, 4% Ni, 3% Ti was prepared as in Example 1 and was used to braze Alloy 42 and also type 410 stainless to Al-995 alumina substrate at 1100.degree. C. under 10.sup.-5 torr vacuum. The brazing alloy showed slight filleting on both metals. An excellent bright joint was formed between the alumina ceramic and the metals.
EXAMPLE 3 (Sample 20-49)
An alloy of 91.25% Cu, 1% Si, 1% Ti, 6.75% Ni was prepared as an ingot. The ingot was reduced to a 4 mil foil using intermediate anneal in a vacuum. The alloy was ductile with 1099.degree. C. liquidus and 1083.degree. C. solidus.
A Kovar strip 1/4" wide by 3" long by 0.10" thick was brazed to 11/4".times.11/4.times.0.100" thick Al-995 alumina substrate using the 4 mil foil at 1125.degree. C. for 2 minutes under 10.sup.-5 torr vacuum. The Kovar was peeled off at a rate of 2" per minute using an Instron Tensile Tester, which resulted in a 20 pound peeling force. This peel strength is better than that obtained by the use of the molybdenum manganese process for brazing to alumina. Kovar is Westinghouse's trademark for an FeNiCo alloy.
EXAMPLE 4 (Sample 20-47)
An alloy of 90% Cu, 1.25% Si, 1.25% Ti, 7.5% Ni was weighed, and 20 troy ounces were melted in a dense alumina crucible under 10.sup.-5 torr vacuum, and cast into a 1/2" thick.times.3" wide copper mold. The ingot was rolled to a 4 mil foil with two intermediate vacuum anneals. The above alloy was placed between Al-995 alumina and a silicon nitride ceramic and heated to 1100 .degree. C. under 10.sup.-5 torr vacuum. An excellent braze was made. A Kovar strip 1/4".times.3".times.0.010" thick was brazed to an Al-995 substrate 11/4".times.11/4".times.0.100" thick at 1105.degree. C. by 5 minute hold under 10.sup.10-5 torr vacuum. This braze yielded a 17 pound peeling force, which is an excellent peel strength.
EXAMPLE 5
An alloy of 91.1% Cu, 1.3% Si, 7.5% Ni was gas atomized to a powder and passed through a 150 mesh screen. A mixture was prepared comprising 98.5% of the minus 150 mesh alloy powder and 1.5% titanium hydride powder. This powder mixture was mixed with a screening oil to form a screenable paste consisting of 85% powder, 15% oil. The paste was screened onto a 11/4" square by 100 mils thick Al-995 alumina substrate using a 105 mesh screen. The coated substrate was oven dried at 100.degree. C. for 30 minutes and a Kovar strip (1/4".times.3".times.10 mils thick) was placed on top and brazed at 1125.degree. C. under 10.sup.-5 torr vacuum. An excellent braze resulted with an 18 pound force peel strength.
EXAMPLE 6 (Sample 20.47)
An alloy of 90% Cu, 1.25% Si, 1.25% Ti, 7.5% Ni was rolled down to a 4 mil thick foil. The foil was placed between a high density graphite cylinder, 1" diameter by 1/2" thick, and a similar cylinder of silicon nitride ceramic. The assembly was brazed at 1125.degree. C. under 10.sup.10-5 torr vacuum. An excellent sound braze joint resulted.
EXAMPLE 7 (Sample 20-51)
An alloy with a composition of 89.5% Cu, 1% si, 1% Ti, 8.5% Ni was cast and rolled to 2 mil thick foil. A 2 mil foil of this alloy was placed between silicon nitride and silicon carbide ceramic discs and brazed at 1125.degree. C. under 10.sup.10-5 torr vacuum. An excellent braze resulted.
Table 1 shows examples of brazing alloy compositions within this invention. The compositions are in weight percent. KHN means Knoop hardness number.
TABLE 1______________________________________Sample Cu Si Ti Ni Sol Liq KHN Peel Lbs______________________________________95-50 90 1 3 6 1068 1096 13495-54 88 2 3 7 1071 1083 13295-55 92 1 3 4 1054 1088 13295-58 88 3 3 6 1025 1061 15195-68 89 0.5 4 6.5 1051 1084 17420-23 95 1 1 3 1065 1081 14120-29 92.5 1 1.5 5 1074 1089 13720-45 89.25 1.5 1.75 7.5 1071 1094 139 14-1620-47 90 1.25 1.25 7.5 1078 1112 126 16-2220-49 91.25 1.0 1.0 6.75 1083 1099 117 16-2520-50 90.75 1.0 0.75 7.5 1087 1103 122 20-2520-51 89.5 1.0 1.0 8.5 1082 1110 101 18-3020-60 91.5 1.0 0.5 7.0 1074 1089 115 10-1520-64 91.75 1.0 0.25 7.0 1070 1101 117 10-1520-68 85.75 1.25 1.0 12.0 1086 1111 12120-69 82.75 1.25 1.0 15.0 1087 1121 145______________________________________
Brazing alloys having compositions within this invention may be used in powder form as in Example 5, in wire form made by drawing, or as a foil as in Examples 1, 3, 4, 6 and 7.
Claims
  • 1. A brazing alloy consisting of, in weight percent; 0.3 to 5% Ti; 2 to 15% Ni; 0.25 to 4% Si; balance copper.
  • 2. A brazing alloy wire having the composition of claim 1.
  • 3. A brazing alloy of claim 1 consisting of 88% Cu, 2% Si, 7% Ni; 3% Ti.
  • 4. A brazing alloy of claim 1 consisting of 92% Cu, 1% Si, 4% Ni; 3% Ti.
  • 5. The brazing alloy of claim 1 consisting of 91.25% Cu, 1% Si, 6.75% Ni; 1%.
  • 6. The brazing alloy of claim 1 consisting of 90% Cu, 1.25% Si, 7.5% Ni; 1.25% Ti.
  • 7. The brazing alloy of claim 1 consisting of 89.5% Cu, 1% Si, 8.5% Ni; 1% Ti.
  • 8. A brazing alloy, for brazing ceramics, which does not grey upon cooling after brazing, the brazing alloy composition consisting of, in weight percent: 0.3 to 5% Ti; 2 to 15% Ni; 0.25 to 4% Si; balance copper.
US Referenced Citations (2)
Number Name Date Kind
4426033 Mizuhara Jan 1984
4612167 Watanabe et al. Sep 1986
Foreign Referenced Citations (4)
Number Date Country
0145745 Aug 1984 JPX
0145746 Aug 1984 JPX
0145747 Aug 1984 JPX
0535921 Apr 1981 GBX