Abstract
Ultra low haze, co-extruded, thermoplastic polymer film prepared by co-extrusion of a blend of polyethyleneterephthalate with organic and inorganic fillers in at least one skin layer on a virtually particle-free polyethyleneterephthalate core layer; the inorganic fillers are aluminum oxide particles and/or silicon oxide of average particle size of about 0.035 μm to about 0.3 μm, and wherein particles of the organic filler have a particle size of less than or equal to about 0.8 μm and are present in an amount less than about 0.04% by weight, based on the weight of the polyethyleneterephthalate, the skin layer being less than about 3 μm in thickness.
Description
FIELD OF THE INVENTION
[0001] This invention relates to thermoplastic polyester film, particularly to ultralow haze polyethyleneterephthalate film having a wide variety of applications.
BACKGROUND
[0002] Polyethyleneterephthalate films are used for a host of converting, printing, coating and metallizing applications. The thermal stability, dimensional stability, chemical resistance and relative high surface energy of polyethyleneterephthalate films are beneficial for typical enduse applications. For instance, polyethyleneterephthalate films are often used as coating bases for magnetic tape, thermal transfer ribbon, packaging materials, thermal lamination and many other web converted products.
[0003] Low film haze is often a key requirement for a range of applications of polyethyleneterephthalate films, herein sometimes referred to as “polyester films”. Labels, solar control films and other optical applications require films with very low film haze in order to satisfy enduser expectations. Films with high haze typically limit the enduser acceptance of such products. However, many solutions to film haze requirements render the polyester films difficult to handle and process. Clear polyester films are typically produced by coating or surface treating a plain almost particle free film base. This method produces clear film, but due to the surface treatment the film's chemical resistance and scratch resistance may be compromised rendering it unsuitable for specific applications.
[0004] Found within the art are many examples of low haze, easy handling polyester films. However, these prior art materials do not meet the requirements of ultra low haze, herein defined as about 0.6% haze. Such low haze numbers are required for highest performance in the optical requirements described above. Furthermore, traditional solutions to low haze polyester film formulations render the film handling properties extremely poor, often leading to converter yield losses and a host of other commercial issues. Therefore, there is a need for an ultra low haze polyester film with improved handling characteristics.
DESCRIPTION OF THE PRIOR ART
[0005] U.S. Pat. No. 6,180,209 describes a biaxially oriented polyester film containing inorganic and organic particle fillers. The particle size distribution of the particles are particularly specified within tight ranges. Our invention advantageously creates a co-extruded film structure with aluminum oxide particles and organic fillers of minimum sizes without the requirements for specific particle size distributions. Such particle size distributions are practically difficult to achieve.
[0006] U.S. Pat. No. 5,096,773 describes a biaxially oriented polyester film containing from 0.05 to 3 wt. % of primary aluminum oxide particles of about 5 to 40 nm in size. Furthermore, these primary particles are specified to aggregate to an average particle size of from 50 to 400 nm. Furthermore, this patent teaches the requirement of an F-5 value (force required for 5% extension) in either the machine or transverse direction of not less than about 12.0 kg/mm2. Our invention differs sharply from this prior art in that we achieve a co-extruded structure, and the minimum sizes of aluminum oxide and organic fillers required to produce a high clarity, easy handling film.
[0007] U.S. Pat. No. 5,023,291 describes a polyester composition of >80 mol % of ethylene terephthalate units or 2,6-napthalenedicarboxylate units having 40-80 equivalents/10ˆ 6 g of terminal carboxyl groups. Further specified are the requirements of from 0.01 to 5% of aluminum oxide particles of 0.005 to 5 μm particle diameter, and also having a melt resistivity of 6E10ˆ A6 to 5E10ˆ A9 ohm-cm. Our invention uses low particle size aluminum oxide fillers in conjunction with organic particle fillers in a co-extruded film structure without particle requirements of melt resistivity.
[0008] U.S. Pat. No. 4,820,583 describes a metallized, composite polyester film with specific requirements for surface roughness. Our invention differentiates in that we have discovered specific particle type, concentration and layer thickness ranges that produce an ultra clear and easy handling polyester film.
[0009] U.S. Pat. No. 5,718,971 describes the formulation of a low haze polyester film prepared from alumina particles treated with a silane coupling agent. Our invention differentiates from this patent in avoiding the necessity of using treated alumina particles in order to obtain sufficient polymer wetting.
[0010] U.S. Pat. No. 5,475,046 describes the use of alumina particles of specific sizes added to a reactor blend to produce PET chip. This chip, when extruded, cast into sheets and biaxially oriented produces films of haze <2.0% and μs/μd of <0.7/0.6. Our invention sharply distinguishes from this patent in that we utilize much smaller particles and achieve the advantage of lower friction as well.
[0011] U.S. Pat. No. 4,828,918 describes a co-extruded film structure with low haze and low surface roughness required for the production of easy handling ultraclear films. Our invention covers the discovery of specific requirements for particle size, concentration and layer thickness necessary to produce easy handling, ultraclear polyester films.
[0012] U.S. Pat. No. 4,092,289 describes a monolayer PET film comprising particles of a mixture of pyrogenic alumina and pyrogenic silica. Our invention has specific requirements for particle size, concentration and co-extruded layer thickness necessary to produce easy handling, ultraclear polyester films.
SUMMARY OF THE INVENTION
[0013] This invention relates to an ultralow haze thermoplastic polyester film prepared by co-extrusion of a blend of polyethyleneterephthalate with inorganic and organic fillers in at least one skin layer on a substantially particle free polyethyleneterephthalate core layer, wherein the inorganic fillers are selected from the group consisting of aluminum oxide particles, silicon dioxide, zirconium oxide, titanium dioxide, tin oxide, calcium carbonate, barium sulfate, calcium phosphate, zeolite, hydroxy apatite, aluminum silicate and mixtures thereof, of average particle size of about 0.035 μm to about 0.3 μm, and wherein particles of the organic filler have a particle size of less than or equal to about 0.8 μm and are present in an amount less than about 0.04% by weight, based on the weight of the polyethyleneterephthalate, the skin layer being less than about 3 μm in thickness.
[0014] This invention also relates to a solar control film comprising an ultralow haze thermoplastic polyester film prepared by co-extrusion of a blend of polyethylene-terephthalate with inorganic and organic fillers in at least one skin layer on a substantially particle-free polyethyleneterephthalate core layer, wherein said inorganic fillers are selected from the group consisting of aluminum oxide particles, silicon dioxide, zirconium oxide, titanium dioxide, tin oxide, calcium carbonate, barium sulfate, calcium phosphate, zeolite, hydroxy apatite, aluminum silicate and mixtures thereof of average particle size about 0.035 μm to about 0.3 μm, and wherein particles of the organic filler have a particle size of less than or equal to about 0.8 μm and are present in an amount less than about 0.04% by weight, based on the weight of the polyethyleneterephthalate, the skin layer being less than about 3 μm in thickness.
[0015] Further, this invention relates to a label film including a polystyrene acrylate coating laminated with an ultralow haze thermoplastic polyester film prepared by co-extrusion of a layer of a blend of polyethyleneterephthalate with inorganic fillers including aluminum oxide particles of average particle size of between about 0.035 μm and about 0.3 μm, and said inorganic particles including one or more polymers having an average particle sizes of less than about 0.8 and are present in an amount less than about 0.04% by weight, based on the weight of the polyethyleneterephthalate, said co-extruded layer being less than about 3 μm thickness.
DETAILED DESCRIPTION
[0016] This invention is based upon results of exhaustive tests we have conducted. The following disclosure, in describing specific test methods and results, is not intended to define or limit the scope of the invention, which is defined in the appended claims.
[0017] “Organic particles” are defined herein as materials roughly spherical in shape prepared from free radical polymerization or polycondensation polymerization to produce stable high polymer. In the context of this invention, these particles have high thermal stability, high melting or no melting temperature and good wet-out in a polyester film matrix. Many such methods exist to prepare these organic particles and include, but are not limited to, suspension polymerization, dispersion polymerization, emulsion polymerization, melt polymerization and solution polymerization. Optionally, these particles may be reduced in size through grinding and classification to produce size ranges used in the invention.
[0018] Test Methods
[0019] Friction was measured with the use of a Testing Machine, Inc. slip tester (TMI-Model #32-06) using ASTM D1894-95. Polyester film samples were cut to specified sizes. One sheet of polyester was clamped, “A” surface up, onto an 18″ MD (machine direction)×6″ TD (transverse direction) glass plate. Another piece of polyester film was mounted using double-sided tape to a 2.5″×2.5″ 200 g sled, with the “B” surface down. The sled was placed on top of the glass plate and attached to the load sensing device. The sled was then dragged over the film on the glass plate at 6 in/min. The only contact during the testing was polyester film surface “A” rubbing against polyester film surface “B”. The measuring distance used to calculate the value of μs was 1″ and 4″ for μd.
[0020] Average surface roughness (Ra) was measured using Kosaka Laboratory Limited Model #SE-30AK and #Ay-3 1. The average value of the data of 10 times measurements was taken as the surface roughness of the film according to the present invention. All measurements were run at 50,000× magnification and in the transverse direction of the film. The length of the measurement was 4 mm and the cut-off value was 0.08 mm.
[0021] Haze was measured using Suga Test Instruments Co. Model #HGM-2DP, using the methods of ASTM Standard D1003.
[0022] Total luminous transmission, herein referred to as TLT, was measured on a Suga Test Instruments Co. Model #HGM-2DP, using method described in ASTM Standard D1003.
[0023] Clarity was measured on a Byk Garner Hazeguard-Plus equipment, using methods described in ASTM Standard D1003.
[0024] Cloudiness was assessed by visual inspection as follows: single sheet samples of film were viewed at a distance of approximately 1 ft. in bright sunlight or under intense light at a slight glancing angle, typically less than 15 degress. Cloudiness is the milkiness or translucence that appears from such a viewer angle. From this assessment a rating system was established for the film samples. A rating value of “poor” (Grade 10) indicates that the sample looks visibly cloudy to the viewer. The samples were then further ranked according to the perceived cloudiness.
[0025] Laminate layer and main layer thicknesses were determined based on a ratio of extruder outputs.
[0026] Average Particle Size Measurement
[0027] Organic Particles
[0028] The particles were placed on the object stage of an electron microscope without overlapping them as far as possible, and observed at a magnification of 10,000 to 100,000 times using a scanning electron microscope or transmission electron microscope. In the case of a scanning electron microscope, on the surface of a sample, a platinum film of about 200 angstroms was vapor deposited using a sputtering apparatus beforehand. From the screen or photographed image, the areas of at least 200 particles were measured to calculate the equivalent diameters, and from the area equivalent diameters the volumes of the individual particles were calculated. Based on the volumes, the volume average particle diameter was calculated in accordance with U.S. Pat. No. 5,912,074.
[0029] Inorganic Particles
[0030] A sample slurry was added to solvent (methanol) such that the concentration of the slurry/solvent was adequate to show adequate light transmission. This solution was pipetted into the Honeywell Microtrac X100 machine. The average particle size and distribution was then measured via this machine.
EXAMPLE 1
[0031] The unagglomerated alumina particles having a A(delta) type crystal form and having an average primary particle diameter of 20 nm, a Mohs' hardness of 7.5 are dispersed substantially uniformly in ethylene glycol by a media dispersion method using glass beads having a particle diameter of 50 μm (rotational speed: 3000 rpm, dispersion time: 4 hours), and the ethylene glycol including the alumina particles was polymerized with dimethylterephthalate to make pellets of polyethylene terephthalate. The content of alumina particles in the polyester was 1.5 wt. %. (U.S. Pat. No. 5,284,699) During polymerization the alumina particles agglomerated into particles with an average particle size 0.1 μm. The average particle size was found to be approximately 0.1 μm, with a range of about 0.035 μm to about 0.3 μm. This particle type is herein defined as “particle (A)” and this pellet type is herein defined as “pellet (A).”
[0032] Polyethyleneterephthalate chips having an intrinsic viscosity of 0.62 were melted using a vent type 2-screw extruder, and a water slurry of the polymer particles prepared above (styrene/bisphenol A diglycidyl ether dimethacrylate copolymer particles) was added, to obtain a polyethylene terephthalate containing organic polymer particles. (U.S. Pat. No. 5,912,074) The content of particle (B) in the polyester pellet (B) was 1.0% with an average particle size of 0.8 μm.
[0033] Polyethyleneterephthalate chips having an intrinsic viscosity of 0.62 were melted using a vent type 2-screw extruder, and a water slurry of the polymer particles prepared above (styrene/bisphenol A diglycidyl ether dimethacrylate copolymer particles) was added, to obtain a polyethyleneterephthalate containing organic polymer particles. (U.S. Pat. No. 5,912,074) The content of particle (C) in the polyester pellet (C) was 1.0% with an average particle size of 0.5 μm.
[0034] Next, 49.2 parts by weight of pellets (A), 0.7 parts by weight of pellets (B), 0.9 parts by weight of pellets (C), and 49.2 parts by weight of pellets (D) which did not substantially include any particles, were mixed. The mixed pellets were extruded using a vent-type two-screw extruder and filtered using high accuracy filters. This melt stream (I) was fed through a rectangular joining zone where it was laminated to a melt stream of polyester (II), which contained substantially no particles. The laminate produced a three layer co-extruded I/Il/I structure. The resulting melt curtain was quenched on a casting drum, and then biaxially oriented via subsequent stretching steps on a roller train and chain driven transverse stretcher. The biaxially oriented film had a total thickness of 23 μm. Both laminate layers (I) were 1.4 μm in thickness.
[0035] The resulting film had an exceptionally low haze value of 0.5% and excellent handling and cloudiness properties as shown in Table 1.
EXAMPLES 2 AND 3
[0036] Film was produced as described in Example 1, except that the pellet content of the laminate layer (I) was varied. As shown in Table 1, the products also had exceptionally low haze of less than or equal to 0.6% and excellent handling and cloudiness properties.
EXAMPLES 4, 5 AND 6
[0037] Film was produced as described in Example 1, except that the pellet content varied, the thickness of both laminate layers (I) were 0.6 μm and the total film thickness was 12 μm. All samples exhibited excellent handling and clarity as shown in Table 1.
EXAMPLE 7
[0038] Polyethylene terephthalate was polymerized by a known method. In particular, a melt slurry of ethylenegycol and purified terephthalic acid was heated, in the presence of esterification catalyst, and water and excess ethylene glycol were removed under vacuum leaving residual melt of polyester. This melt was discharged via strand die into a cooling trough, pelletized, and then further dried to remove residual moisture to less than 500 ppm to complete the polymerization. Particles (F), being SiO2 particles of an average particle size of 0.2 μm, were admixed into the polyethyleneterephthalate, antimony trioxide of 0.030 wt. %, calcium acetate of 0.090 wt. %, phosphorous acid of 0.030 wt. %, and dimethyl phenylphophonite of 0.080 wt. % was prepared as polyester pellet (F). The content of particles (F) in the polyester pellet (F) was 1.0 wt %.
[0039] Film was produced as described in Example 1, except that pellet content varied, the thickness of both laminate layers (I) were 0.6 μm and the total thickness was 12 μm. The example exhibited excellent handling and haze. See Table 2 for results.
EXAMPLE 8
[0040] Film was produced as described in Example 1, except that the pellet content varied, the thickness of both laminate layers (I) were 0.6 μm and the total thickness was 12 μm. The example exhibited excellent handling and haze.
Comparative Examples 1, 2 and 3
[0041] Film was produced as described in Example 1, except that the pellet content and thickness of the laminate layer (I) was varied. As shown in Table 3, while these polyester films exhibited good handling, low haze or good cloudiness, they were deficient in at least one of these properties. Comparative Example 1 exhibited good handling but haze and cloudiness levels were not adequate. Desired cloudiness levels were at least of a Grade B level and ultra clear film is defined as a haze level of about 0.6%. Comparative Example 2 did not handle well or have the desired cloudiness. Its static coefficient of friction was in excess of 0.55 and its dynamic coefficient of friction was greater than 0.45. Comparative Example 3 exhibited low haze but was extremely hard to handle with a μs/μd value of 0.683/0.582.
Comparative Example 4
[0042] Calcium carbonate particles having a Mohs' hardness of 3 were dispersed in ethylene glycol by a media dispersion method after adding ammonium phosphate as a dispersant, and the ethylene glycol including the particles of CaCO3 was polymerized with dimethylterephthalate to make pellets (E) of polyethylene terephthalate. The average particle diameter of the CaCO3 was 0.8 μm and the content thereof in the polyester was 3.0 wt. %.
[0043] Next, 49.7 parts by weight of pellets (A), 0.5 parts by weight of pellets (E), and 49.8 parts by weight of pellets (D) which did not substantially include any particles, were mixed. The mixed pellets were extruded using a vent-type two-screw extruder and filtered using high accuracy filters. This melt stream (I) was fed through a rectangular joining zone where it was laminated to a melt stream of polyester (II), which contained substantially no particles. The laminate produced a three layer co-extruded I/II/I structure. The resulting melt curtain was quenched on a casting drum, and then biaxially oriented via subsequent stretching steps on a roller train and chain driven transverse stretcher. The biaxially oriented film had a total thickness of 23 μm. Both laminate layers (I) were 1.4 μm in thickness.
[0044] As shown in Table 3, while this polyester film exhibited low haze and good cloudiness, its handling characteristics were significantly worse than those of the invention.
Comparative Example 5
[0045] Dupont 23 μm Mylar® Type D. Mylar D is an ultra high clarity polyester film used in solar and photo proofing applications. This film consists of a plain polyester substrate, with essentially no particles, that is, surface treated on either one or two sides. While the optical properties of the film were excellent, the film's handling properties were only moderate. Because of inadequate handling, rolls of Mylar D contain knurl impressions to improve winding, which is undesirable.
Comparative Examples 6a and 6b
[0046] 12 μm and 23 μm Mitsubishi Hostophan® 5000 series. Hostophan® 5000 series is a clear polyester film used widely throughout the solar control window industry. This film is a mono-layer film that contains both small and moderate size particle additives. The particle distribution and the fact that this film is single layer caused it to have a combination of poor handling, poor cloudiness and moderate haze as shown in Table 4.
Comparative Example 7
[0047] 23 μm Melinex 453. Melinex 453 polyester film consists of a plain polyester substrate, with essentially no particles, that is, one side adherable coated. This film, while having desirable haze values as shown in Table 4, has less than desirable handling. Another problem with the nature of this film is that slip additives in the coating can migrate out of the film and cause scratching.
Comparative Example 8
[0048] Film was produced as described in Example 1, except that the pellet content varied, the thickness of both laminate layers (I) were 0.35 μm and the total thickness was 12 μm. The example exhibited excellent handling but had poor haze values. See Table 4 for results.
1TABLE 1
|
|
Example123456
|
|
Laminate (I)Composition (%)
Particles (A)0.1 μm Alumina0.740.740.740.750.750.75
Particles (B)0.8 μm Organic0.00740.00740.00740.01720.00500.0100
Particles (C)0.5 μm Organic0.0091—0.00180.02110.02110.0211
Particles (E)0.8 μm CaCO3——————
Particles (F)0.2 μm SiO2——————
Film Thickness (I/II/I) μm1.4/20.2/1.41.4/20.2/1.41.4/20.2/1.40.6/10.7/0.60.6/10.7/0.60.6/10.7/0.6
Frictionμs0.5360.5120.5180.4200.4900.478
μd0.4150.4330.4310.3450.3900.383
Ra (nm)5.0———7.0—
Haze0.50.30.30.60.40.5
TLT89.189.889.789.489.189.5
Clarity99.899.899.899.799.799.8
Cloudiness222322
|
[0049]
2
TABLE 2
|
|
|
Example
7
8
|
|
|
+UZ,1/14 Laminate (I)
Composition (%)
|
Particles (A)
0.1 μm Alumina
0.34
0.35
|
Particles (B)
0.8 μm Organic
0.005
0.005
|
Particles (C)
0.5 μm Organic
0.021
0.021
|
Particles (E)
0.8 μm CaCO3
—
—
|
Particles (F)
0.2 μm SiO2
0.017
—
|
Film Thickness (I/II/I) μm
0.6/10.7/0.6
0.6/10.7/0.6
|
Friction
μs
0.455
0.440
|
μd
0.380
0.355
|
Ra (nm)
—
—
|
Haze
0.4
0.4
|
TLT
—
—
|
Clarity
99.8
99.8
|
Cloudiness
—
—
|
|
[0050]
3
TABLE 3
|
|
|
Example
Comp 1
Comp 2
Comp 3
Comp 4
Comp 5
|
|
|
Laminate (I)
Composition (%)
|
Particles (A)
0.1 μm Alumina
0.74
1.49
0.75
0.75
|
Particles (B)
0.8 μm Organic
0.014
0.0074
—
—
|
Particles (C)
0.5 μm Organic
—
—
—
—
|
Particles (E)
0.8 μm CaCO3
—
—
—
0.015
|
Particles (F)
0.2 μm SiO2
—
—
—
—
|
Film Thickness (I/II/I) μm
1.4/20.2/1.4
1.4/20.2/1.4
1.5/20/1.5
1.4/20.2/1.4
Total 23 μm
|
Friction
μs
0.420
0.593
0.683
0.639
0.647
|
μd
0.345
0.474
0.582
0.526
0.523
|
Ra (nm)
—
—
—
—
2.5
|
Haze
0.7
0.6
0.1
0.2
0.2
|
TLT
89.6
89.2
89.6
89.6
87.5
|
Clarity
99.7
99.8
100
99.8
100
|
Cloudiness
5
4
1
3
1
|
|
[0051]
4
TABLE 4
|
|
|
Example
Comp 6a
Comp 6b
Comp 7
Comp 8
|
|
|
Laminate (I)
Composition (%)
|
Particles (A)
0.1 μm Alumina
1.42
|
Particles (B)
0.8 μm Organic
0.010
|
Particles (C)
0.5 μm Organic
0.0411
|
Particles (E)
0.8 μm CaCO3
—
|
Particles (F)
0.2 μm SiO2
—
|
Film Thickness (I/II/I) μm
Total 12 μm
Total 23 μm
Total 23 μm
0.35/11.2/0.35
|
Friction
μs
1.00
0.587
0.596
0.355
|
μd
0.75
0.486
0.517
0.320
|
Ra (nm)
14.3
10.5
3.0
—
|
Haze
1.1
1.7
0.2
0.8
|
TLT
89.1
87.4
89.5
89.4
|
Clarity
99.4
99.3
100
99.8
|
Cloudiness
10
10
2
|
|
[0052] Ultra-low haze and easy handling in polyester film are desirable attributes. Such attributes are useful for use in optically clear products such as solar control films, safety films, labels, graphics and other film uses. However, previous solutions to these issues were either deficient in clarity, film handling properties, or more often both.
[0053] In our experience, film handling properties are directly related to the friction properties of the film. A high coefficient of friction tends to lead to difficult converting of the film due to difficulties in unwinding the film and in subsequent re-winding of the film due to the possibility of increased static and the requirements for higher load tensions to pull the film through the typical roller train used in converting processes. High coefficients of friction can also lead to end user roll formation issues such as pimples and high edges. For easy converting of the film it is desired to create a static coefficient of friction of less than or equal to about 0.55 together with a dynamic coefficient of friction of less than or equal to about 0.45.
Claims
- 1. An ultralow haze thermoplastic polyester film prepared by co-extrusion of a blend of polyethyleneterephthalate with inorganic and organic fillers in at least one skin layer on a substantially particle free polyethyleneterephthalate core layer, wherein said inorganic fillers are selected from the group consisting of aluminum oxide particles, silicon dioxide, zirconium oxide, titanium dioxide, tin oxide, calcium carbonate, barium sulfate, calcium phosphate, zeolite, hydroxy apatite, aluminum silicate and mixtures thereof, of particle size of about 0.035 μm to about 0.30 μm, and wherein particles of said organic filler have a particle size of less than or equal to about 0.8 μm and are present in an amount less than about 0.04% by weight, based on the weight of the polyethyleneterephthalate, said skin layer being less than about 3 μm in thickness.
- 2. The film of claim 1, wherein the organic particles are prepared from free radical polymerization of styrene and one or more unsaturated ester and, optionally, a multifunctional unsaturated crosslinking monomer.
- 3. The film of claim 1, wherein the organic particles are prepared from a polyesterification reaction between a diacid and diol or a diester and a diol or a combination of a diacid and a diester and a diol.
- 4. The film defined in claim 1, wherein the amount of inorganic filler is about 0.4% to 0.8% by weight, based on the weight of the polyethyleneterephthalate.
- 5. The film defined in claim 1, wherein the average particle size of the inorganic filler is about 0.1 μm.
- 6. The film defined in claim 1, wherein the skin layer has a thickness between about 0.6 μm and about 3 μm.
- 7. The film defined in claim 1, wherein the organic particles have a particle size between about 0.5 μm and about 0.8 μm.
- 8. A solar control film comprising an ultralow haze thermoplastic polyester film prepared by co-extrusion of a blend of polyethyleneterephthalate with inorganic and organic fillers in at least one skin layer on a substantially particle-free polyethyleneterephthalate core layer, wherein said inorganic fillers are selected from the group consisting of aluminum oxide particles, silicon dioxide, zirconium oxide, titanium dioxide, tin oxide, calcium carbonate, barium sulfate, calcium phosphate, zeolite, hydroxy apatite, aluminum silicate and mixtures thereof of average particle size about 0.035 μm to about 0.3 μm, and wherein particles of said organic filler have a particle size of less than or equal to about 0.8 μm and are present in an amount less than about 0.04% by weight, based on the weight of the polyethyleneterephthalate, said skin layer being less than about 3 μm in thickness.
- 9. The film of claim 8, wherein the organic particles are prepared from free radical polymerization of styrene and one or more unsaturated ester and, optionally, a multifunctional unsaturated crosslinking monomer.
- 10. The film of claim 8, wherein the organic particles are prepared from a polyesterification reaction between a diacid and diol or a diester and a diol or a combination of a diacid and a diester and a diol.
- 11. The film defined in claim 8, wherein the amount of inorganic filler is about 0.4% to 0.8% by weight, based on the weight of the polyethyleneterephthalate.
- 12. The film defined in claim 8, wherein the average particle size of the inorganic filler is about 0.1 μm.
- 13. The film defined in claim 8, wherein the skin layer has a thickness between about 0.6 μm and about 3 μm.
- 14. The film defined in claim 8, wherein the organic particles have a particle size between about 0.5 μm and about 0.8 μm.
- 15. A label film comprising a polystyrene acrylate coating laminated with an ultralow haze thermoplastic polyester film prepared by co-extrusion of a layer of a blend of polyethyleneterephthalate with inorganic fillers comprising aluminum oxide, silicon dioxide, zirconium oxide, titanium dioxide, tin oxide, calcium carbonate, barium sulfate, calcium phosphate, zeolite, hydroxy apatite, aluminum silicate and mixtures thereof, of particles of average particle size of between about 0.035 μm and about 0.3 μm, and said inorganic particles comprising one or more polymers having an average particle sizes of less than about 0.8 μm and are present in an amount less than about 0.04% by weight, based on the weight of the polyethyleneterephthalate, said co-extruded layer being less than about 3 μm thickness.
- 16. The film of claim 15, wherein the organic particles are prepared from free radical polymerization of styrene and one or more unsaturated ester and optionally a multifunctional unsaturated crosslinking monomer.
- 17. The film of claim 15, wherein the organic particles are prepared from a polyesterification reaction between a diacid and diol or a diester and a diol or a combination of a diacid and a diester and a diol.
- 18. The film of claim 15, wherein the organic particles are a mixture of organic particles prepared from the free radical polymerization of styrene and one or more unsaturated ester and, optionally, a multifunctional unsaturated crosslinking monomer prepared from a polyesterification reaction between a diacid and diol or a diester and a diol or a combination of a diacid and a diester and a diol.
- 19. The film defined in claim 15, wherein the amount of inorganic filler is about 0.4% to 0.8% by weight, based on the weight of the polyethyleneterephthalate.
- 20. The film defined in claim 15, wherein the average particle size of the inorganic filler is about 0.1 μm.
- 21. The film defined in claim 15, wherein the skin layer has a thickness between about 0.6 μm and about 3 μm.
- 22. The film defined in claim 15, wherein the organic particles have a particle size between about 0.5 μm and about 0.8 μm.
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
09931473 |
Aug 2001 |
US |
Child |
10079770 |
Feb 2002 |
US |