Electric insulating prepreg applied to fuel cell

Abstract

A prepreg for fuel cell obtained by soaking reinforcing glass fiber cloth in resin mixture and having the soaked cloth pre-dried to form incompletely cured prepreg which can be press-cured under temperature range of 60□˜200□ to provide good mechanical and electrical property and high bonding strength, and when applied to fuel cell for bonding together the parts and components of the fuel cell the prepreg can also provide the effect of preventing crossover of fuel of the fuel cell and helping to the normal operation of the fuel cell.

Description

BRIEF DESCRIPTION OF THE DRAWING FIGURES

FIG. 1 is an enlarged sectional view of the structure of Fuel cell which employs the prepreg of the invention; it shows that the prepreg of the invention can be employed to bond together the parts and components, and can effectively prevent crossover of fuel of fuel cell.

Claims

1. A prepreg applied for fuel cell obtained by soaking a reinforcing glass fiber cloth in resin mixture and pre-drying the soaked cloth to form incompletely cured bonding material which shall be press-cured under temperature range of 60˜200□ with an amount of the resin mixture used making up 30˜95% of the total weight of the prepreg and the major components of the resin mixture comprises: (a) epoxy resin makes up 20˜99 wt % of the total solid of the resin mixture with an equivalent epoxy weight of 150˜10000 g/eq approximately;(b) curing agent makes up 1˜60 wt % of the total solid of the resin mixture;(c) accelerator makes up 0˜30 wt % of the total solid of the resin mixture; and(d) additives makes up 0˜80 wt % of the total solid of the resin mixture.

2. The prepreg as described in claim 1, wherein the fiber glass cloth comprises the cloth made of continuous glass fiber by weaving process or the non-woven glass fiber mat or paper or synthetic fiber.

3. The prepreg as described in claim 1, wherein the epoxy resin (a) is Bisphenol A type epoxy resin, Bisphenol F type epoxy resin, Tetra-function epoxy resin, Multi-function epoxy resin, Brominated epoxy resin or Phosphureted epoxy resin; or more than one of the above.

4. The prepreg as described in claim 1, wherein the curing agent (b) of the resin mixture are Amine compounds of MDA or DDS or Benzyl dimethyl amine (BDMA) and the Imidazole compounds such as 2MI, or Acid anhydrides or Phenol novolak or DICY or BF3MEA or more than one of the above.

5. The prepreg as described in claim 1, wherein the accelerator (c) is Imidazole compounds including 2MI, 2PI, 2E4MZ or BF3MEA; or Amine compounds including benzyl dimethyl amine (BDMA); or more than one of the above.

6. The prepreg as described in claim 1, wherein the additives (d) are organic additives, inorganic additives, engineering plastics, defoamer or flattening agent; or more than one of the above.

7. The prepreg as described in claim 6, wherein the inorganic additives are clay, SiO2, CaCO3, TiO2, Al(OH)3 or more than one of the above.

8. The prepreg as described in claim 6, wherein the organic additives are brominated additives or phosphureted additives or modified engineering plastics or non-modified engineering plastics or more than one of the above.