Electrical insulating paper

Information

  • Patent Grant
  • 9922750
  • Patent Number
    9,922,750
  • Date Filed
    Thursday, November 14, 2013
    11 years ago
  • Date Issued
    Tuesday, March 20, 2018
    6 years ago
Abstract
An electrical insulating paper having 40-80 wt % of aramid fibrid, 10-50 wt % of aramid pulp, and 10-50 wt % of aramid short-cut. The aramid pulp is para-aramid pulp with a length of 0.5-6 mm and has a Schopper Riegler value of 15-85; the aramid fibrid is para-aramid fibrid; and the aramid short-cut is para-aramid short-cut. The paper shows a high dielectric strength and tensile index. A method for manufacturing the paper and an insulated conductor that includes the paper.
Description

The invention pertains to electrical insulating paper, to an insulated conductor comprising said paper, to a transformer, generator or electric motor comprising said insulated conductor, and to a method of preparing said paper.


WO2012093048 describes an electrical insulating paper comprising 40-100 wt. % of a para-aramid fibrid, and up to 60 wt. % of at least one of aramid pulp, aramid floc, aramid staple fiber, aramid fibril, meta-aramid fibrid, meta-para-aramid fibrid, thermal conductive fillers, and common paper additives such as fillers such as kaolin, binders, fibers, tackifiers, and adhesives. The paper can be used in insulated conductors and transformers, generators and electric motors made thereof. The papers described in the examples of this application show a high dielectric strength. However, dielectric strength is but one of the parameters which a high-quality El-paper should satisfy. More specifically, El paper should combine a high dielectric strength with a high tensile index, which can be expressed as the product of the dielectric strength and the tensile index. Further, the ease of manufacture of the paper is also an important feature, and especially papers with high fibrid contents may be difficult to manufacture.


There is therefore need for El papers with improved properties and improved ease of manufacture. The present invention provides such a paper. Further advantages of the present invention will become evident from the further specification.


The present invention pertains to an electrical insulating paper comprising

    • 40-80 wt. % of aramid fibrid,
    • 10-50 wt. % of aramid pulp, and
    • 10-50 wt. % of aramid short-cut,


      the aramid pulp being para-aramid pulp with a length of 0.5-6 mm and a Schopper Riegler of 15-85.


It has been found that a paper meeting the above requirements shows an increased value for the product of the dielectric strength (expressed in kV/mm) and the tensile index (expressed in Nm/g), as compared to systems comprising only two of the cited components, or less than 40 wt. % of aramid fibrid. A paper comprising 100% aramid fibrid shows a higher value for the product of the dielectric strength (expressed in kV/mm) and the tensile index (expressed in Nm/g) than the papers according to the invention, but this paper may be less attractive because it is difficult to manufacture. Additionally, the tear strength of all-fibrid-papers may be insufficient for certain applications.


It is noted that U.S. Pat. No. 5,026,456 describes a high-porosity paper comprising 10-40 wt. % of aramid fibrid, 5-30 wt. % of high temperature resistant floc, and 30-85 wt. % of aramid paper pulp. The aramid paper pulp is pulp obtained from dried aramid paper comprising floc and fibrid, e.g., by wet refining. The aramid fibrid, the floc, and the pulp are all obtained from meta-aramid. It will be evident to the skilled person that high-porosity papers are not suitable for use as electrical insulating paper, because a high porosity is accompanied by a low electric resistance.


In the context of the present specification aramid refers to an aromatic polyamide which is a condensation polymer of aromatic diamine and aromatic dicarboxylic acid halide. Aramids may exist in the meta- and para-form, both of which may be used in the present invention. The use of aramid wherein at least 85% of the bonds between the aromatic moieties are para-aramid bonds is considered preferred. As typical members of this group are mentioned poly(paraphenylene terephthalamide), poly(4,4′-benzanilide terephthalamide), poly(paraphenylene-4,4′-biphenylenedicarboxylic acid amide) and poly(paraphenylene-2,6-naphthalenedicarboxylic acid amide or copoly(para-phenylene/3,4′-dioxydiphenylene terephthalamide). The use of aramid wherein at least 90%, more in particular at least 95%, of the bonds between the aromatic moieties are para-aramid bonds is considered preferred. The use of poly(paraphenylene terephthalamide), also indicated as PPTA is particularly preferred. This applies to all aramid components present in the paper according to the invention.


The paper according to the invention comprises aramid fibrid. Aramid fibrids are known in the art. Within the context of the present specification the term aramid fibrid refers to small, non-granular, non-rigid film-like particles. The film-like fibrid particles have two of their three dimensions in the order of microns, and have one dimension less than 1 micron. In one embodiment, the fibrids used in the present invention have an average length in the range of 0.2-2 mm, and average width in the range of 10-500 microns, and an average thickness in the range of 0.001-1 microns.


In one embodiment, the aramid fibrid comprises less than 40%, preferably less than 30%, of fines, wherein fines are defined as particles having a length weighted length (LL) of less than 250 micron.


Meta-aramid fibrids may be prepared by shear precipitation of polymer solutions into coagulating liquids as is well known from U.S. Pat. No. 2,999,788. Fibrids of wholly aromatic polyamides (aramids) are also known from U.S. Pat. No. 3,756,908, which discloses a process for preparing poly(meta-phenylene isophthalamide) (MPD-I) fibrids. Para-aramid fibrids are made via much later developed high shear processes such as for example described in WO2005/059247, which fibrids are also called jet-spun fibrids.


It is preferred for the aramid fibrid to be para-aramid fibrid. The most suitable papers have been made from para-aramid fibrid with a Schopper-Riegler (SR) value between 50 and 90, preferably between 75 and 85. These fibrids preferably have a specific surface area (SSA) of less than 10 m2/g, more preferably between 0.5 and 10 m2/g, most preferably between 1 and 4 m2/g.


In one embodiment, fibrids are used with a LL0.25 of at least 0.3 mm, in particular of at least 0.5 mm, more in particular at least 0.7 mm. In one embodiment the LL0.25 is at most 2 mm, more in particular at most 1.5 mm, still more in particular at most 1.2 mm. LL0.25 stands for the length weighted length of the fibrid particles wherein particles with a length below 0.25 mm are not taken into account.


The paper according to the invention comprises aramid pulp. Aramid pulp is well known in the art. The pulp is para-aramid pulp.


Aramid pulp may be derived from aramid fibres which are cut to a length of, e.g., 0.5-6 mm, and then subjected to a fibrillation step, wherein the fibers are pulled apart to form the fibrils, whether or not attached to a thicker stem. Pulp of this type may be characterized by a length of, e.g., 0.5-6 mm, and a Schopper-Riegler of 15-85. In some embodiments, the pulp may have a surface area of 4-20 m2/g.


Within the context of the present specification, the term pulp also encompasses fibrils, i.e., “pulp” which predominantly contains the fibrillated part and little or no fiber stems. This pulp, which is sometimes also indicated as aramid fibril, can, e.g., be obtained by direct spinning from solution, e.g. as described in WO2004/099476. In one embodiment the pulp has a structural irregularity expressed as the difference in CSF (Canadian Standard Freeness) of never dried pulp and dried pulp of at least 100, preferably of at least 150. In one embodiment fibrils are used having in the wet phase a Canadian Standard Freeness (CSF) value less than 300 ml and after drying a specific surface area (SSA) less than 7 m2/g, and preferably a weight weighted length for particles having a length>250 micron (WL 0.25) of less than 1.2 mm, more preferably less than 1.0 mm. Suitable fibrils and their preparation method are described, e.g., in WO2005/059211.


The paper according to the invention comprises aramid shortcut. In one embodiment aramid shortcut is used, which in the present invention are aramid fibres cut to a length of, e.g., 0.5-15 mm, in particular a length of 2 to 10 mm, more in particular 3-8 mm. The aramid shortcut preferably is para-aramid shortcut.


The paper according to the invention comprises 40-80 wt. % of a aramid fibrid, 10-50 wt. % of aramid pulp, and 10-50 wt. % of aramid short-cut. It has been found that it is the presence of all three components which yields a paper with good properties, as is evidenced by an increased value for the product of the dielectric strength (expressed in kV/mm) and the tensile index (expressed in Nm/g).


In one embodiment, the paper comprises at most 70 wt. % of fibrid, or even at most 60 wt. % of fibrid, on the one hand to allow for the presence of larger amount of other components, and on the other hand to increase the manufacturability of the paper. The presence of large amount of fibrid is associated with the a lower manufacturing velocity, because the removal of water from fibrid-containing paper during manufacture is difficult. Further, the tear strength of paper containing a very high amount of fibrid may be insufficient.


In one embodiment, the paper contains at least 15 wt. % of aramid shortcut, more in particular at least 20 wt. %, because this makes for a paper with increased strength. It may be preferred for the paper to contain at most 40 wt. % of shortcut. If the amount of shortcut is too high, the insulating properties may be detrimentally affected. If the amount of shortcut is too low, the properties of the invention will not be obtained.


In one embodiment, the paper contains at least 15 wt. % of pulp. It may be preferred for the paper to contain at most 40 wt. % of pulp, more in particular at most 30 wt. % of pulp. If the amount of pulp is too high, the insulating properties may be detrimentally affected. If the amount of pulp is too low, the properties of the invention will not be obtained.


In one embodiment, the paper comprises 40-60 wt. % of aramid fibrid as described above, 20-40 wt. % of para-aramid shortcut as described above, and 15-30 wt. % of para-aramid pulp as described above.


If so desired, the paper can comprise one or more common papermaking components, such as fillers including mica, clay such as kaolin and bentonite, thermally conductive electrically insulating fillers, minerals, binders, fibers, tackifiers, adhesives, and the like. It may be preferred for the paper to comprise kaolin as additive. It is further preferred to introduce kaolin into the paper by way of the fibrid, e.g., by using kaolin-containing fibrids manufactured by incorporating kaolin into the fibrid during the spinning process, for instance as has been described in WO 2008/122374.


Thermally conductive electrically insulating fillers are known in the art. They are commonly applied in electrical power generators, switching mode power suppliers and signal amplifiers. Examples of such materials can be found in U.S. Pat. No. 4,869,954, and include aluminum nitride, aluminum oxide, boron nitride, magnesium oxide and zinc oxide.


In one embodiment, the paper of this invention has a bulk density of at least 0.7 g/cm3, preferably 0.9 g/cm3 or higher. Papers with bulk densities less than 0.7 g/cm3 were found to have lower dielectrical strength. As a maximum, a value of 1.4 g/cm3 may be mentioned.


In one embodiment, the paper according to the invention has an electric resistance of at least 1013 Ωcm according to the volume resistivity method of ASTM D-257. Preferably, the resistance is at least 1015 Ωcm.


In one embodiment, the paper according to the invention has a grammage in the range of 20 to 1000 g/m2, more in particular in the range of 30 to 300 g/m2.


In one embodiment, the paper according to the invention has a thickness in the range of 20 micron to 1 mm, more in particular in the range of 30 to 300 micron.


The invention also relates to a method of making the above electrical insulating papers. In the process according to the invention, a suspension, generally an aqueous suspension, is prepared comprising aramid fibrid, pulp, and shortcut as described above. The suspension is applied onto a porous screen, so as to lay down a mat of randomly interwoven material onto the screen. Water is removed from this mat, e.g., by pressing and/or applying vacuum, followed by drying to make paper. It has appeared that papers with improved properties can be obtained is the dried paper is subjected to a calendering step. Calendering steps are known in the art. They generally involve passing the paper through a set of rolls. It was also found that a further improvement could be obtained if the calendering was performed at elevated temperature, particularly at 100° C. or higher, preferably between 150° C. to 300° C., more preferably between 180 and 220° C., and most preferably between 180 and 200° C.


It may be beneficial for the electrical properties of the paper to subject the fibrid to shear forces, such as in a Waring blender, prior to using it in the papermaking process.


It is common practice in the manufacture of insulated electrical windings, such as those used in electrical motors or in power transformers, to insulate the respective turns of the windings from one another by placing insulating sheet material between the winding turns. Such sheet material insulation is normally only required on high voltage windings or windings having relatively large turns which inherently develop relatively high voltages between the adjacent turns of the winding. The present papers are suitable for insulating conductors and for making transformers, generators, and electric motors. The present invention therefore also pertains to the use of the paper according to the invention in insulated conductors, and to the use of such insulated conductors in transformers, generators, and electric motors. The present invention also pertains to an insulated conductor comprising the paper as described herein or as obtained by the manufacturing method described herein, and to a transformer, generator or electric motor comprising said insulated conductor. In one embodiment, the paper according to the invention is used in rotating electrical equipment, e.g., for lead wire, coil, slot, phase, wedge, and end insulation. In another embodiment the paper according to the invention is used in transformers for turn, layer, barrier, and tap insulation.


It is noted that the embodiments of the paper described herein may be combined with each other in manners clear to the skilled person. All embodiments and properties described for the paper are also applicable to the method for manufacturing the paper, individually or in combination. All embodiments and properties described for the paper are also applicable to the use thereof in any application, individually or in combination.


Experimental


Papermaking Process (General Procedure)


All paper recipes have been made on the Rapid Koethe (RK) handsheet former according to the method of ISO 5269-2. Drying was done using the RK-dryer under vacuum at 95° C. Calendering of the dried papers was done at 10 μm gap control at 200° C. For calendering two steel rollers were used.


The dielectric strength measurements were done according to ASTM D149 97A 920040. The thickness of the papers was measured according to TAPPI 411 om-05 at the position of the dielectric breakdown. This thickness was used in the calculation of the dielectric strength. At least 5 breakdowns for each type of paper were measured to give the average dielectric strength (which is denoted in the Table). Tensile index (TI) and elongation at break (EAB) were determined in accordance with ISO 1924-2. Gurley was determined in accordance with IS05636-5.


Starting materials were as follows:

    • PPTA fibrid: Twaron® D8016, ex Teijin Aramid, The Netherlands
    • Short cut PPTA fiber: Twaron® T1000, 6 mm, ex Teijin Aramid, The Netherlands
    • PPTA pulp: Twaron® 1094, ex Teijin Aramid, The Netherlands







EXAMPLES

Papers were made according to the method of ISO 5269-2 and thereafter calendered according to the general procedure, unless indicated differently. The ingredients for making paper amounted to 1.6 g of material (based on dry weight), resulting in sheets of 50 g/m2. The compositions, grammage, and thickness of the various papers are presented in table 1 below. Ex 1 is a paper according to the invention. Papers A through E are comparative.









TABLE 1







Composition













Fibrids
Short Cut
Pulp
Grammage
Thickness


Ex
[%]
[%]
[%]
[g/m2]
[um]















Ex 1
50
30
20
50
49.5


A
20
30
50
50
52.3


B
50
50

50
55.0


C
100


50
48.7


D
50

50
50
49.0


E

50
50
50
55.6









Various properties of these papers were determined, and the results thereof are presented in Table 2 below.









TABLE 2







Results













Dielectric







Strength
TI
EAB
Gurley


Ex
[kV/mm]
[Nm/g]
[%]
[Gs]
TI*DiS















Ex 1
36.2
50.6
1.5
91400
1832


A
19.6
37.8
1.1
1230
741


B
23.4
54.4
1.9
7150
1273


C
67.1
69.5
3.2
1986096
4663


D
44.3
31.2
2.2
30000
1382


E
12.0
6.5
0.7
12
78









From the results in Table 2 it can be seen that the paper of Example 1, which is according to the invention, shows a high value for the product of the tensile index and the dielectric strength, which makes it suitable for use in various applications. The paper containing fibrids only has a very high value for this parameter, but water removal during manufacture was difficult, and tear strength was low.

Claims
  • 1. An electrical insulating paper comprising: 40-80 wt % of aramid fibrid,10-50 wt % of aramid pulp, and10-50 wt % of aramid short-cut,wherein the aramid of the aramid pulp consists of para-aramid and wherein the aramid pulp has a length of 0.5-6 mm and has a Schopper Riegler (SR) value of 15-85, andwherein the aramid fibrid has a SR value of 50-90, and/or a specific surface area (SSA) of less than 10 m2/g.
  • 2. The electrical insulating paper according to claim 1, wherein the aramid fibrid is para-aramid fibrid, and/or the aramid short-cut is para-aramid short-cut.
  • 3. The electrical insulating paper according to claim 1, wherein the paper comprises at most 70 wt % of the aramid fibrid.
  • 4. The electrical insulating paper according to claim 1, wherein the paper contains at least 15 wt % of the aramid short-cut.
  • 5. The electrical insulating paper according to claim 1, wherein the paper contains at least 15 wt % of the aramid pulp.
  • 6. The electrical insulating paper according to claim 1, wherein the paper has a bulk density of at least 0.7 g/cm3.
  • 7. The electrical insulating paper according to claim 1, wherein the paper has an electric resistance of at least 1013 Ωcm according to the volume resistivity method of ASTM D-257.
  • 8. A method for manufacturing the electrical insulating paper according to claim 1, comprising: preparing a suspension comprising the aramid fibrid, the aramid pulp, and the aramid shortcut,applying the suspension onto a porous screen, so as to lay down a mat of randomly interwoven material onto the porous screen,removing water from the mat by pressing and/or application of a vacuum, andsubjecting the mat from which water is removed to a drying step.
  • 9. The method according to claim 8, further comprising subjecting the dried paper to a calendering step.
  • 10. The method according to claim 9, wherein the calendering step is performed at 100° C. or higher.
  • 11. An insulated conductor comprising the paper according to claim 1.
  • 12. A transformer, generator, or electric motor comprising the insulated conductor of claim 11.
Priority Claims (1)
Number Date Country Kind
12193957 Nov 2012 EP regional
PCT Information
Filing Document Filing Date Country Kind
PCT/EP2013/073782 11/14/2013 WO 00
Publishing Document Publishing Date Country Kind
WO2014/079761 5/30/2014 WO A
US Referenced Citations (22)
Number Name Date Kind
4698267 Tokarsky Oct 1987 A
4729921 Tokarsky Mar 1988 A
4888091 Nollen et al. Dec 1989 A
5026456 Hesler et al. Jun 1991 A
8168039 Levit May 2012 B2
8211272 Levit Jul 2012 B2
9073290 Levit Jul 2015 B2
9194061 Hendriks Nov 2015 B2
20040089432 Levit May 2004 A1
20050230072 Levit Oct 2005 A1
20070087178 Hendriks Apr 2007 A1
20070137818 Levit Jun 2007 A1
20080107959 Ishino May 2008 A1
20100212851 Levit Aug 2010 A1
20130277089 Rolink Oct 2013 A1
20140184371 Harmer Jul 2014 A1
20150056429 Kawka Feb 2015 A1
20150318078 Rolink Nov 2015 A1
20160060461 David Mar 2016 A1
20160076201 Wodetzki Mar 2016 A1
20160160444 Tiecken Jun 2016 A1
20170030020 Adjei Feb 2017 A1
Foreign Referenced Citations (13)
Number Date Country
101872852 Oct 2010 CN
102517976 Jun 2012 CN
S59228059 Dec 1984 JP
04228696 Aug 1992 JP
2000034693 Feb 2000 JP
20140040096 Apr 2014 KR
20150087248 Jul 2015 KR
2005103376 Nov 2005 WO
2012093048 Jul 2012 WO
WO 2012093048 Jul 2012 WO
WO 2013033044 Mar 2013 WO
WO 2014079761 May 2014 WO
WO 2016103966 Jun 2016 WO
Non-Patent Literature Citations (6)
Entry
Research Disclosure of Jun. 1992, anonymously disclosed.
Jan. 13, 2014 International Search Report issued in International Patent application No. PCT/EP2013/073782.
Jan. 13, 2014 International Written Opinion issued in International Patent Application No. PCT/EP2013/073782.
Jun. 28, 2016 Office Action issued in Chinese Patent Application No. 2013-80061049.1.
Sep. 30, 2017 Office Action issued in Chinese Application No. 201380061049.1.
Gailun, Zhijiang Zaozhi. “Introduction to Pulping and Papermaking”. Jan. 2012; pp. 143-147.
Related Publications (1)
Number Date Country
20150318078 A1 Nov 2015 US