Patent Application
20070122930
The present invention relates to an electrochemical cell structure and a method of fabrication.
The International Energy Agency's “World Energy Outlook” predicts that global primary energy demand will increase by 1.7% per year from 2000 to 2030. It also predicts that 90% of this demand will be met by fossil fuels. Consequently, there will be a 1.8% per year increase in carbon dioxide from 2000 to 2030, reaching 38 billion tonnes in 2030. Cleaner, renewable energy sources, including solar cells, have long been heralded as counters to this increased pollution trend. While advanced silicon based solar cells are now widely commercially available, their uptake has been slow due to high production costs, a lack of robustness and associated visual pollution resulting from the large surface exposure requirements.
Dye Sensitised Solar Cells (DSSC) are an alternative to crystalline solar cells that are cheaper than crystalline solar cells to produce. However, DSSC's are less efficient than crystalline solar cells. Therefore DSSC's require significant area coverage to be effective power generators.
U.S. Pat. No. 4,927,721 entitled “Photo-Electrochemical Cell”, by M Gratzel et al. discloses a typical DSSC. As illustrated in
A DSSC generates charge by the direct absorption of visible light. Since most metal oxides absorb light predominantly in the ultra-violet region of the electromagnetic spectrum, a sensitiser (dye) 4 is absorbed onto the surface of metal oxide layer 3 to extend the light absorption range of the solar cell into the visible light region.
In order to increase the amount of light that the metal oxide layer 3 and the sensitiser (dye) layer 4 can absorb, at least some portion of the metal oxide layer 3 is made porous, increasing the surface area of the metal oxide layer 3. This increased surface area can support an increased quantity of sensitiser (dye) 4 resulting in increased light absorption and improving the energy conversion efficiency of the DSSC to more than 10%.
An electrochromic display (ECD) is a relatively new electrochemical, bi-stable display. While the application is different to the DSSC, these devices share many physical attributes, illustrated in
When a sufficient negative potential is applied to the first transparent conductive oxide (TCO) electrode layer 2, whilst the second transparent conductive electrode oxide (TCO) layer 6 is held at ground potential, electrons are injected into the conduction band of the metal oxide semiconductor layer 3 and reduce the adsorbed molecules (the coloration process). The reverse process occurs when a positive potential is applied to the first transparent conductive oxide (TCO) electrode layer 2 and the molecules become bleached (transparent).
A single electrochromic molecular monolayer on a planar substrate would not absorb sufficient light to provide a strong colour contrast between the bleached and unbleached states. Therefore a highly porous, large surface area, nanocrystalline metal oxide layer 3 is used to promote light absorption in the unbleached state by providing a larger effective surface area for the electrochromophore to bind onto. As light passes through the thick metal oxide layer 3, it crosses several hundreds of monolayers of molecules coloured by the sensitiser (dye) 4, giving strong absorption.
Since the structure of both electrochemical devices is similar, we describe only the method of DSSC manufacture as an example. Equally, this process could be applied with little modification to the ECD manufacture.
In order to manufacture the DSSC 10 illustrated in
After drying and cooling, the porous metal oxide layer 3 is coated with sensitiser (dye) 4 by immersion in a low concentration (≦1 mM) sensitiser (dye) solution for an extended period, typically 24 hours, to allow absorption of the sensitiser (dye) 4 onto the metal oxide layer 3 through a functional ligand structure, that often comprises a carboxylic acid derivative. Typical solvents used in this process are acetonitrile or ethanol, since aqueous solutions would inhibit the absorption of the sensitiser (dye) 4 onto the surface of the metal oxide layer 3.
The first transparent conductive oxide (TCO) electrode layer 2, having the porous metal oxide layer 3 and sensitiser (dye) layer 4 formed thereon, is then assembled with the second transparent conductive oxide (TCO) electrode layer 6. Both electrode layers 2, 6 are sandwiched together with a perimeter spacer dielectric encapsulant to create an electrode-to-electrode gap of at least 10 μm, before filling with the electrolyte layer 5. The spacer material is most commonly a thermoplastic that provides an encapsulation seal. Once the electrolyte layer 5, which is most commonly an iodide/triiodide salt in organic solvent, is introduced, the DSSC is completed by sealing any remaining aperture with either a thermoplastic gasket, epoxy resin or a UV-curable resin to prevent the ingress of water and hence device degradation.
Most, if not all, of the materials used to fabricate the DSSC can be handled in air and also under atmospheric pressure conditions, removing the necessity for expensive vacuum processes associated with crystalline solar cell fabrication. As a result, a DSSC can be manufactured at a lower cost than a crystalline solar cell.
The ECD fabrication process is very similar to that for the DSSC, with several exceptions. The porous metal oxide layer 3 is often patterned by screen printing to provide a desired electrode image, allowing the device to convey information by colouring or bleaching selected regions. Additionally, the sensitiser (dye) layer 4 is replaced with an absorbed electrochromophore material layer. Furthermore, a permeable diffuse reflector layer, typically large particles of sintered metal oxide, can be positioned between the first and second electrode layers 2, 6 to increase the viewed image contrast.
U.S. Pat. No. 5,830,597, entitled “Method and Equipment for Producing a Photochemical Cell”, by H Hoffmann also discloses a DSSC 100. As illustrated in
An individual cell 110 formed between the insulating web 108 and the insulating web 109 is different from the adjoining individual cell 110 formed between the insulating web 109 and the insulating web 108. This is because the TiO2 layer 103 and the electrolyte layer 105 are interchanged in each adjoining individual cell 110. Thus, the electrical polarity of the adjoining individual cells 110 is opposite. This alternate division of different layers results in the formation of conducting layers 111 from the electrically conductive layers 102 and 106, each conducting layer 111 connecting a positive (negative) pole of one individual cell 110 to the negative (positive) pole of an adjacent individual cell 110. The resultant structure provides a method of increasing the overall DSSC output voltage, without the necessity of incorporating a multi-layered structure.
U.S. Pat. No. 6,310,282B1, entitled “Photovoltaic Conversion Element and a Dye-Sensitising Photovoltaic Cell”, by Sakurai et al. discloses a multi-colour DSSC 200. As illustrated in
The multi-colour DSSC 200 is manufactured by covering the transparent semiconductor layer 202 with a mask having openings that coincide only with the red sensitising dye absorption portions 203, dipping the transparent semiconductor layer 202 in red sensitising dye for a predetermined period of time, removing the transparent semiconductor layer 202 from the red sensitising dye and removing the mask. Then the transparent semiconductor layer 202 is covered with a mask having openings that coincide only with the green sensitising dye absorption portions 204, the transparent semiconductor layer 202 is dipped in green sensitising dye for a predetermined period of time, the transparent semiconductor layer 202 is removed from the green sensitising dye and the mask is removed. Next the transparent semiconductor layer 202 is covered with a mask having openings that coincide only with the blue sensitising dye absorption portions 205, the transparent semiconductor layer 202 is dipped in blue sensitising dye for a predetermined period of time, the transparent semiconductor layer 202 is removed from the blue sensitising dye and the mask is removed. Finally, the transparent semiconductor layer 202 is dipped in black sensitising dye for a predetermined period of time and the transparent semiconductor layer 202 is removed from the black sensitising dye.
The multi-colour DSSC 200 would have poor picture quality with respect to dye bleeding through the transparent semiconductor layer 202 from the separate dye absorption portions 203, 204, 205, 206 and the lack of greyscale (contrast) control.
In order to improve the incident photon to current conversion efficiency and control the stability/reproducibility of the DSSC performance, it is important to precisely control the physical properties of the metal oxide layer, and hence the absorption of the sensitiser (dye) molecule. However, metal oxide layer fabrication using screen-printing often results in a ±5% film thickness variation caused by residual blocked or dirty screen cells, adhesion to the screen during separation from the substrate surface and trapped bubble expansion during drying, caused by the inability to completely outgas a viscous paste. Other methods, such as doctor-blading, also suffer from an inability to provide a well defined thick metal oxide layer without significant spatial deviations. Subsequent porosity and film quality deviations are therefore likely to occur throughout such metal oxide layers, resulting in a degradation of efficiency and image quality for the DSSC and ECD, respectively.
In the case of the ECD, screen-printing demands are further exacerbated by the requirement to create ever finer metal oxide layer features for higher quality images, i.e. increase the dots-per-inch (dpi) for a pixelated display. As the dpi increases, the smallest feature size becomes limited as the screen mesh size approaches the mesh partition width.
As a result, fabrication of an electrochemical device based on a functionally sensitised thick porous metal oxide layer, as for the DSSC and ECD, using the aforementioned fabrication techniques are inappropriate from the view points of device reproducibility and adaptability to large size device production.
The present invention aims to address the above mentioned problems of manufacturing electrochemical cells (DSSC's and ECD's) of the prior art, to improve the efficiency with which they are made and thus further decrease the cost of electrochemical cells. Additionally, the present invention aims to produce a multi-coloured and/or a grayscale electrochemical cell having improved picture quality with respect to bluring (bleeding) and greyscale (contrast) over that of the prior art.
In a first embodiment of the present invention an electrochemical cell is provided comprising: a first conductive layer; a metal oxide layer formed on the first conductive layer, the metal oxide layer comprising a plurality of adjacent metal oxide cells, spaced from one another; a functional dye layer formed on the metal oxide layer; a second conductive layer; and an electrolyte between the functional dye layer and the second conductive layer, wherein at least one of the first and second conductive layers is transparent; and the functional dye layer comprises at least two different coloured functional dyes each having a depth of colour, such that at least some of the plurality of adjacent metal oxide cells have different colours.
In a second embodiment of the present invention an electrochemical cell is provided. The electrochemical cell comprising: a first conductive layer; a metal oxide layer formed on the first conductive layer, the metal oxide layer comprising a plurality of adjacent metal oxide cells, spaced from one another; a functional dye layer formed on the metal oxide layer; a second conductive layer; and an electrolyte between the functional dye layer and the second conductive layer, wherein at least one of the first and second conductive layers is transparent; and the functional dye layer comprises at least two different depths of colour, such that at least some of the plurality of adjacent metal oxide cells have different depths of colour.
In one embodiment at least one of the at least two different coloured functional dyes contributes to the electrochemical cell power generation. In another embodiment the depth of colour of the functional dye layer in at least one metal oxide cell is altered by altering a thickness of the metal oxide layer. In another embodiment the depth of colour of the functional dye layer in at least one metal oxide cell is altered by altering a size of droplets of functional dye formed thereon. In another embodiment the depth of colour of the functional dye layer in at least one metal oxide cell is altered by altering a number of droplets of functional dye formed thereon. In another embodiment the depth of colour of the functional dye layer in at least one metal oxide cell is altered by altering a concentration of functional dye formed thereon.
In a further embodiment the electrochemical cell further comprises: separating means formed on the first conductive layer and surrounding each of the plurality of adjacent metal oxide cells. In another embodiment the separating means is a polymer pattern or a polyimide pattern. In another embodiment at least part of the separating means is hydro- and/or oleophobic and wherein the first conductive layer is hydro- and/or oleophilic.
In a further embodiment the separating means forms a matrix of cells on the first conductive layer. In another embodiment each of the metal oxide cells is substantially square shaped, substantially circular shaped, substantially hexagonal shaped or substantially rectangular shaped. In another embodiment the separating means are banks.
In one embodiment the first conductive layer is transparent, and the electrochemical cell further comprises: a reflector layer provided on the opposite side of the functional dye layer to the at least one transparent conductive layer. In another embodiment the electrochemical cell further comprises: an electrocatalytic layer formed between the electrolyte and the second conductive layer. In another embodiment the electrocatalytic layer is any one of platinum, ruthenium, rhodium, palladium, iridium or osmium.
In a further embodiment the electrochemical cell further comprises: a first insulating substrate on a side of the first conductive layer opposite to the metal oxide layer. In another embodiment the electrochemical cell further comprises: a second insulating substrate on a side of the second conductive layer opposite to the electrolyte. In another embodiment the first insulating substrate is glass or plastic. In another embodiment the metal oxide layer is a titanium dioxide layer. In another embodiment the metal oxide layer comprises particles of metal oxide, and wherein the functional dye layer is formed on surface of the particles of the metal oxide layer.
In one embodiment the first and second conductive layers are continuous layers. In another embodiment the first conductive layer is a transparent conductive oxide layer. In another embodiment the second conductive layer is a transparent conductive oxide layer. In a further embodiment the electrochemical cell is a dye sensitised solar cell. In another embodiment the electrochemical cell is an electrochromic display. In another embodiment the functional dye layer is an electrochromophore layer.
In a third embodiment of the present invention a method of forming an electrochemical cell is provided. The method comprising: forming a first conductive layer; forming a metal oxide layer on the first conductive layer, the metal oxide layer comprising a plurality of adjacent metal oxide cells, spaced from one another; forming a functional dye layer on the metal oxide layer by depositing at least two different coloured functional dyes each having a depth of colour on the metal oxide layer, such that at least some of the adjacent metal oxide cells have different coloured functional dyes; forming a second conductive layer; and providing an electrolyte between the second conductive layer and the functional dye layer, wherein at least one of the first and second conductive layers is transparent.
In a fourth embodiment of the present invention a method of forming an electrochemical cell is provided. The method comprising: forming a first conductive layer; forming a metal oxide layer on the first conductive layer, the metal oxide layer comprising a plurality of adjacent metal oxide cells, spaced from one another; forming a functional dye layer on the metal oxide layer, the functional dye layer comprising at least two different depths of colour, such that at least some of the plurality of adjacent metal oxide cells have different depths of colour; forming a second conductive layer on the electrolyte; and providing an electrolyte between the functional dye layer and the second conductive layer, wherein at least one of the first and second conductive layers is transparent.
In one embodiment the method further comprises: forming separating means on the first conductive layer surrounding each of the plurality of adjacent metal oxide cells. In another embodiment the metal oxide layer is inkjet printed onto the first conductive layer. In another embodiment the metal oxide layer is inkjet printed onto the first conductive layer in one step. In another embodiment the functional dye is inkjet printed onto the adjacent metal oxide cells of the metal oxide layer.
In one embodiment the method further comprises: providing a reflector layer on the opposite side of the functional dye layer to said at least one transparent conductive layer. In another embodiment the method further comprises: providing an electrocatalytic layer between the electrolyte and the second conductive layer. In another embodiment the method further comprises: forming the first conductive layer on a first insulating substrate, whereby the first insulating substrate and the metal oxide layer are on opposite sides of the first conductive layer. In another embodiment the method further comprises: forming the second conductive layer on a second insulating substrate, whereby the second insulating substrate and the electrolyte are on opposite sides of the first conductive layer.
In a fifth embodiment of the present invention an electrochemical cell structure is provided. The electrochemical cell structure comprises: a plurality of adjacent micro-electrochemical cells, spaced from one another, and wherein the micro-electrochemical cells have different functional dyes, transmissivity, reflectivity or chromaticity from one another. In one embodiment the electrochemical cell structure further comprises: separating means surrounding each of the plurality of adjacent micro-electrochemical cells. In another embodiment the separating means are banks.
In a sixth embodiment of the present invention an electrochemical cell structure is provided. The electrochemical cell structure comprises: a dye sensitised solar cell and an electrochromic display formed on a substrate.
The method of fabrication of the electrochemical cell of the present invention, using inkjet printing, is advantageous over screen printing fabrication as format scaling (up or down) does not require re-investment in machine hardware. This is because inkjet fabrication is software controlled and the software can be reconfigured without the expense of commissioning new screens. Additionally, inkjet heads are significantly more durable, than patterned screens, as patterned screens last only approximately 100 uses.
Furthermore, the drop on demand placement enabled by inkjet fabrication is less wasteful than screen printing. Unlike conventional inkjet overwriting, where each deposited layer is dried and then printed over to produce a thick deposition, the inkjet flood filling technique, which doses a confined region with a large volume of liquid to provide the required deposit thickness, has been shown to produce fracture-free metal oxide layers. Moreover, the surface confinement used to enable flood filling, through the use of a bank structure, ensures long range uniform material distribution and therefore uniform and repeatable performance. Additionally, surface confinement through the use of a bank structure ensures enhanced picture quality and contrast by colour separation between the different coloured cells.
Embodiments of the present invention will now be described by way of further example only and with reference to the accompanying drawings, in which:
The present invention relates to an electrochemical cell such as a Dye Sensitised Solar Cell (DSSC) or an electrochromic display (ECD). One electrochemical cell 400 of the present invention comprises, with reference to
The first and second transparent insulating substrate layers 401, 407 are preferably glass or plastic. The metal oxide layer 403 is preferably titanium dioxide (TiO2) and is a semiconductor.
The metal oxide layer 403 should preferably be a material which promotes intimate adhesion of the sensitiser (dye)/electrochromic material layer 404 on its surface. Additionally, the particles of the metal oxide layer 403 must be reasonably light transmissible. Particles greater then 500 nm are expected to be opaque and are not generally considered appropriate for use in the present invention. Such large particles would also tend to cause inkjet nozzle blocking.
In a first embodiment of the present invention, a bank structure 410 is formed on the first TCO layer 402, prior to the application of the metal oxide layer 403, so that a metal oxide layer 403 is formed of isolated cells. In one embodiment the bank structure 410 may be formed from a polymer or a polyimide.
Preferably, the bank structure is hydro- and/or oleophobic in some part while the TCO layer 402 is hydro- and/or oleophilic, depending on the nature of the metal oxide ink used to form the metal oxide layer 403.
The bank structure 410 can take on any desired shape forming a matrix of individual pixel cells on the first TCO layer 402, within which the isolated metal oxide cells are formed; such that no metal oxide bridges the bank structure 410 to cause short circuiting.
When the electrochemical cell is an ECD, it is essential that all the metal oxide cells (pixels) are electrically isolated from one another to control the image formation. While the metal oxide cell electrical isolation is not essential when the electrochemical cell is a DSSC, it is preferable to maintain a uniform metal oxide distribution throughout the active device area.
The ECD electrochemical cell can be considered as being composed of a plurality of micro-electrochemical cells, and different micro-electrochemical cells may have different coloured eletrochromophore layers 404. The eletrochromophore layers 404 may also have different transmissivity, reflectivity or chromaticity from one another. Each micro-electrochemical cell is separated from the other micro-electrochemical cells, which together form the ECD, by the bank structure 410. Additionally, an ECD electrochemical cell can be composed of a combination of one or more dye sensitised solar cells and one or more electrochromic display cells formed on a substrate. Each micro-electrochemical cell is preferably between 20 μm to 500 μm across.
In a further embodiment of the present invention an electrocatalytic layer can be formed between the electrolyte layer 405 and the second TCO layer 406. The electrocatalytic layer is preferably greater than 2 nm thick and is selected to enhance the electrolyte regeneration. In the case of the DSSC, effective electrocatalytic metals can be selected from the platinum group metals; platinum, ruthenium, rhodium, palladium, iridium or osmium. The use of an electrocatalytic layer improves the overall performance of the electrochemical cell of the present invention.
The present invention also relates to a method of fabricating the electrochemical cell 400 of the present invention.
The TCO layer 402 is formed on the first transparent insulating substrate layer 401,
The bank structure 410 is then fabricated on the TCO layer 402,
The TCO layer 402 having a bank structure 410 is then treated by oxygen or oxygen plus carbon tetrafluoride plasma to remove residual polyimide in the exposed regions. A carbon tetrafluoride (CF4) plasma treatment is then applied to cause the polyimide bank structure 410 to become hydrophobic, while preserving the hydrophilic nature of the TCO layer 402.
The metal oxide layer 403 is then inkjet printed onto the TCO layer 402 having the bank structure 410 formed thereon. The metal oxide ink is jetted into each of the isolated pixel cells to form the metal oxide layer 403,
Precise control of the metal oxide layer 403 thickness throughout the device area is essential to provide a uniform canvas on which the DSSC or ECD image can be formed. The thickness of the metal oxide layer 403 is controlled by the concentration of the aqueous colloidal TiO2 ink, and the deposition volume. The resultant deviation in the peak thickness of the metal oxide layer 403 is less than 1.5% between pixel cells over a 50 cm2 substrate area.
Sensitiser (dye) 404 is then inkjet printed into each of the pixel cells, onto the metal oxide layer 403 formed therein. This method of fabrication allows for the formation of different coloured pixel cells, by enabling the different application of sensitiser(s) (dye(s)) 404 to different pixel cells, in order to create a coloured and/or gray-scale image, with each pixel cell of the bank structure 410 corresponding to a pixel of a picture. Therefore, a high image quality electrochemical cell, with a resolution of 200 dots per inch (dpi) or greater, can be created. The sensitiser (dye) 404 is absorbed by the metal oxide layer 403,
The first TCO layer 402, having the porous metal oxide layer 403 and sensitiser (dye) layer 404 formed thereon, is then assembled with the second TCO layer 406. Both electrode layers 402, 406 are sandwiched together with a perimeter spacer to create an electrode-to-electrode gap, before filling with the electrolyte layer 405. Once the electrolyte layer 405 is introduced, the DSSC is completed by sealing the remaining aperture.
If an electrocatalytic layer is desired in the electrochemical cell of the present invention, then the electrocatalytic layer is formed on the second TCO layer 406 prior to the electrode layers 402, 406 being sandwiched together.
An inkjet head is capable of providing a well defined aqueous colloidal metal oxide ink droplet, with volume deviation less than ±1.5%, to a precise location on the TCO layer 402. Moreover, this volumetric accuracy of ≦1.5% represents that for a commercial printer head. Several industrial heads and complementary techniques are available which can reduce this figure to ≦1%.
Inkjet deposition enables accurate positioning of the metal oxide on the TCO layer 402, within each pixel cell of the bank structure 410 as required. Thus, the thickness of the metal oxide layer 403 can be controlled precisely and a uniform porous metal oxide layer 403 can be obtained. Additionally, inkjet deposition enables accurate positioning of the sensitiser (dye) on the metal oxide layer 403, within each pixel cell of the bank structure 410.
When at least part of the bank structure 410 is hydro- and/or oleophobic, and at least part of the TCO layer 402 is hydro- and/or oleophilic, the bank structure 410 repels the deposited ink, thus correcting the final position of the deposited material on the target surface and compensating for the inherent ±15 μm droplet lateral divergence from the inkjet nozzle axis. This repulsion is especially beneficial in the case of the ECD to prevent pixel short-circuits caused by printed metal oxide 403 bridging the bank structure 410. The bank structure 410 also enables the formation of a narrower gap between ECD pixels than otherwise permitted by the 30 μm spacing necessary for bank-less free-printing, enabling a higher active area ratio to be obtained in the ECD and increased image quality. Furthermore, the bank acts to confine the printed sensitiser ink to a specific device region, preserving the resultant image definition.
Only a portion of the bank structure 410 needs to be hydro- and/or oleophobic. For example, if the bank wall is hydrophilic and its top hydrophobic, then for an aqueous metal oxide ink the resultant deposit profile will be modified compared to the fully hydrophobic case, as illustrated in
The metal oxide layer 403 should be several microns thick to function effectively. In traditional inkjet printing the thickness of the deposit is built up to the desired profile by using an overwriting technique, wherein each deposited layer is dried and sintered and then overwritten with another layer of ink, and so on, until the desired thickness is reached.
However, the method of the present invention uses a flood filling technique, whereby a large volume of metal oxide ink is introduced into each pixel cell of the bank structure 410 in one pass. The bank structure 410 prevents the metal oxide ink from spreading into neighbouring pixel cells. Using this process, only a single drying and sintering stage is required to produce the desired thickness of the metal oxide layer 403. The bank structure 410 also prevents the sensitiser (dye) 404 from spreading into neighbouring pixel cells, thus preventing colour bleeding, and improving the contrast of any image formed on the electrochemical cell.
The sensitiser (dye) ink solution is absorbed into the porous metal oxide layer 403 through capailary action. If the bank structure 410 was not used to separate the metal oxide layer 403 into isolated pixel cells, then upon jetting from an ink jet head the sensitiser (dye) 404 would spread throughout the metal oxide layer 403 and picture quality would be reduced.
Using a continuous metal oxide layer 403 makes control of image colour depth difficult by inkjet dye overwriting, as the deposited ink merely spreads throughout the porous metal oxide layer 403. To increase the resolution and contrast between the colours and to enable control of sensitiser (dye) 404 colour depth, the metal oxide layer 403 is separated into isolated pixel cells, so that sensitiser (dye) 404 introduced into one cell remains within that cell. Thus, the bank structure 410 is used to prevent lateral liquid diffusion.
Additionally, the use of the bank structure 410 enables the metal oxide layer 403 to have a uniform and repeatable cross-sectional profile throughout, assisting uniformity of colour depth across the image. To provide the required image quality, the pixel cells defined by the bank structure 410 should be as small as practicable.
In the case of the DSSC, not all of the coloured pixel cells are required to be coloured using sensitiser (dye) 404, however, at least some of the colours used in the image should preferably be coloured using sensitiser (dye) 404. The remainder pixel cells of the image can be fabricated using ‘inert’ dye that contributes to the image but not the electrochemical cell power generation. Though described as ‘inert’ dyes, they should chemically bond to the metal oxide layer 403 to provide good image stability. If only one coloured sensitiser (dye) 404 is used, black is preferable. This is because black sensitiser (dye) 404 has a high energy conversion efficiency.
However, it is preferable that all the pixel cells are coloured using sensitiser (dye) 404 that contributes to the electrochemical cell power generation to maximise power output. This is because the use of a plurality of isolated pixel cells reduces the energy conversion efficiency of the electrochemical cell of the present invention by area. Additionally, if only some of the pixel cells are coloured using sensitiser (dye) 404 that contributes to the electrochemical cell power generation, then the energy conversion efficiency of the electrochemical cell of the present invention is further reduced.
The depth of colour of the sensitiser (dye) 404 can be controlled through adjustment of the size and number of droplets printed into each pixel cell of the bank structure 410. Additionally, the depth of colour of the sensitiser (dye) 404 can be controlled through adjustment of the thickness of the metal oxide layer 403.
At least four inks are necessary to provide photographic quality images; cyan, magenta, yellow and black or red, green, blue and black depending on the image construction. Many of these coloured sensitisers (dyes) 404 already exist, i.e. Ru11(dmbpy)2(dcbpy)Cl2 is a known yellow dye, N719 is a known purple/red dye and Fell complexes are known blue dyes. To create a colour mix within one pixel cell, a predefined dose of one colour can be jetted into that pixel cell before being overwritten with a different dose of another colour.
In a further embodiment of the present invention an inert, diffuse, white reflector layer 412 can be provided between the sensitiser (dye) layer 404 and the second TCO layer 406, as illustrated in
In another embodiment, only one coloured sensitiser (dye) 404 is used in the electrochemical cell of the present invention. Black is preferred as the colour for the sensitiser (dye) as black sensitiser (dye) has a high energy conversion efficiency. In order to improve the aesthetic appearance of the electrochemical cell, a gray-scale coloured image can be created on the metal oxide layer 403, using only one coloured sensitiser (dye) 404 with each pixel cell of the bank structure 410 corresponding to a pixel of the image.
To create a gray-scale coloured image the depth of “colour” of the sensitiser (dye) 404 in each pixel cell can be controlled through adjustment of the size and number of droplets printed into each pixel cell of the bank structure 410. The greater the number of droplets printed into each pixel cell, the darker that pixel cell appears. Additionally, the depth of colour of the sensitiser (dye) 404 can be controlled through adjustment of the thickness of the metal oxide layer 403.
Employing the latter method of creating the image contrast, varying the metal oxide layer 403 thickness by inkjet printing, it is not necessary to inkjet print the sensitizer (dye) 404. Rather the final metal oxide layer 403 film can be simply immersed in a standard sensitiser (dye) 404 solution. The image contrast is then revealed by the capacity of different regions to absorb the sensitiser (dye), as shown in
Control of the depth of colour of the sensitiser (dye) 404, within each pixel cell enables the electrochemical cell to comprise a high quality image, with a resolution of 200 dots per inch (dpi) or greater. The image quality of a gray-scale coloured image can be further enhanced by providing an inert, diffuse, white reflector layer 412 between the sensitiser (dye) layer 404 and the second TCO layer 406, as discussed above.
A bank structure 410 having a matrix of square pixel cells produces a pyramidal metal oxide topography as illustrated in
The bank structure 410 of the present invention increases the metal oxide layer's 403 ability to accommodate bending stress without fracturing, compared to a continuous metal oxide layer 403. This enables a flexible substrate 401 to be utilised, such as a plastic first insulating substrate 401.
In the first embodiment of the present invention, the bank structure 410 comprises a matrix of square pixel cells as illustrated in
It has been determined that the pixel cell shape has little influence on the peak or average metal oxide ink thickness across the TCO layer 402. However, if the volume of the deposited metal oxide ink exceeds the advancing contact angle of the bank material at the bank/ink/air interface, it is likely that the bank structure 410 will be breached and that the metal oxide ink contained in adjacent pixel cells will coalesce. Therefore, a pixel cell shape that minimises the metal oxide ink contact angle at the bank/ink/air interface for a fixed deposition volume is preferable. Additionally, a pixel cell shape that minimises the constriction of the ink on the surface, lowering the minimum surface energy liquid gradient at its periphery is preferable.
Where the contact angle is less than 90°, the predicted ratios of maximum contact angle are 2.3:1.9:1.0 for the triangle, square and hexagonal pixel cell structures respectively, each having the same unit area. The contact angle is reduced as the number of pixel edges increases. Thus, a circular pixel cell provides the minimal contact angle at the bank/ink/air interface, thereby accepting the most metal oxide ink before breaching the bank structure 410. However, circular pixel cells inhibit the effective device area due to poor tessellation, reducing device performance compared to pixel cells having a higher packing density. While the triangular pixel cell shape has a better active area foot-print, it is disadvantageous due to the large contact angle of constrained inkjet printed metal oxide ink. Therefore, a hexagonal pixel cell shape or a square pixel cell shape is preferable for use in a DSSC of the present invention.
DSSC's of the present invention have been made with an energy conversion efficiency (η), an open circuit voltage (Voc), a short circuit current (Isc) and a fill factor (FF) of 5.0%, 0.48 V, 15 mA/cm2 and 57%, respectively. The variation in energy conversion efficiency of a electrochemical cell of the present invention over a 50 cm2 substrate area is less than 1.5%. This is due to the process stability of the inkjet fabrication method of the present invention.
Wider bank structures 410 are deleterious to both ECD operation, by a reduction in image quality, and DSSC operation, by a reduction in efficiency; resulting from a decrease in active area. Therefore, the bank structure 410 has a preferable width from 0.2 μm to 20 μm. 0.2 μm is the resolution limit for cost effective fabrication of the bank structure 410 by photolithography. 20 μm is considered the maximum effective bank structure 410 width before serious degradation of the image and performance becomes inhibitive, compared to the lowest common display resolutions of 72 dpi. Using inkjet technology hydrophilic pixel cell sizes less than 1 mm2 are readily achievable, though lengths less than several hundred microns are preferred.
In the case of DSSC, absorption of light is proportional to the thickness of the porous metal oxide layer 403. If too thin, a fraction of the incident light will pass unhindered through the metal oxide layer 403, with a loss of potential efficiency. If too thick, once all of the useful light has been completely absorbed, any remaining metal oxide layer 403 thickness will be redundant. Therefore, preferably the thickness of the deposited metal oxide layer 403 should be between from 0.5 μm to 20 μm.
Moreover, due to the uniformity of the thickness of the metal oxide layer 403 produced by inkjet printing over screen printing, the optimal metal oxide layer 403 thickness can be thinner when using inkjet printing.
Furthermore, in the case of screen printing, the ink viscosity must be much higher than that preferred for inkjet printing. Therefore, the material added to increase viscosity must be removed during the sintering process. Consequently, the as-deposited, pre-sintered metal oxide layer 403 thickness must be greater for screen-printing than for inkjet printing.
Although a bank structure 410 is used to form a matrix of isolated pixel cells on the TCO layer 402, prior to application of the metal oxide ink, the present invention is not limited to banks. Any method of forming isolated pixel cells on the TCO layer 402 may be used, such by creating troughs in the TCO layer 402.
Additionally, it is not essential for the first transparent conductive oxide layer 402 to be formed of an oxide material for the electrochemical cell of the present invention to function. Moreover, it is not essential for the second transparent conductive oxide layer 406 to be transparent or formed of an oxide material for the electrochemical cell of the present invention to function. Indeed, it is not essential to provide the second substrate (or either substrate in the finished device).
Any suitable material can be used for the bank structures. However, it is preferred to deposit them as a polymer, and more preferably as a polyimide, pattern.
Although liquid electrolytes have been discussed above, solid or gel electrolytes are also suitable for use in the present invention and, in this context, any reference in this specification to providing an electrolyte between an electrode/conductive layer and another element includes forming the electrode/conductive layer and/or the other element on the electrolyte.
For the avoidance of doubt, the term gray-scale in this specification may refer to different shades or depths of any one or more colours, which may include black. For example, a gray-scale display may comprise different shades of blue; or different shades of red, different shades of green, and different shades of blue.
In summary, the present invention has the advantage of being able to provide a display of one colour, with pixels having different depths of colour; a display of two or more colours, with each pixel of a particular colour having the same depth of colour; and a display of two or more colours, with pixels of a particular colour having different depths of colour.
The foregoing description has been given by way of example only and it will be appreciated by a person skilled in the art that modifications can be made without departing from the scope of the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0524068.4 | Nov 2005 | GB | national |