Electrochromic device and method for manufacturing electrochromic device

Information

  • Patent Grant
  • 11698565
  • Patent Number
    11,698,565
  • Date Filed
    Monday, June 29, 2020
    4 years ago
  • Date Issued
    Tuesday, July 11, 2023
    a year ago
  • CPC
  • Field of Search
    • US
    • 359 266000
    • 359 242000
    • 359 265000
    • 359 273000
    • 252 583000
    • CPC
    • G02F1/161
    • G02F1/155
    • G02F2001/1512
    • G02F2001/1515
    • G02F1/15
    • B29D11/00634
    • B29D11/0074
    • B29D99/0053
    • C09K9/02
    • C09K2211/1018
    • C09K2211/14
    • C09K2211/187
  • International Classifications
    • G02F1/15
    • B29D11/00
    • G02F1/1516
    • Disclaimer
      This patent is subject to a terminal disclaimer.
      Term Extension
      227
Abstract
The invention relates to devices that provide a color change under the influence of an electric voltage, in particular to an electrochromic device and a method for manufacturing such a device. Disclosed is the method for manufacturing an electrochromic device comprising at least two electrodes that are flexible and optically transparent with a hermetically closed space between the electrodes filled with an electrochromic composition that may contain transparent and insoluble microparticles that function as spacers.
Description
BACKGROUND OF THE INVENTION
Field of the Invention

The disclosed embodiments relate in general to the field of applied electrochemistry, and in particular to methods for manufacturing electrochromic compositions used in devices with electrically controlled absorption of light such as light filters of variable optical density, light emission modulators, and information image displays.


Description of the Related Art

Electrochromism is the physical phenomenon found in certain compositions of reversibly changing predetermined optical properties such as color or light transmittance with an application of an electrical voltage called a control voltage. Electrochromism provides the basis for operation of various electrochromic devices, such as smart glass well known to persons of ordinary skill in the art. Various types of optical materials and structures can be used to construct the aforesaid compounds with electrochromic properties, with the specific structures being dependent on the specific purpose of the electrochromic device.


Known in the art is a method of manufacturing an electrochromic device (U.S. Pat. No. 4,902,108 issued on Feb. 20, 1990, incorporated herein by reference) wherein an electrically conductive coating of one of two optically transparent electrodes is coated with a thickened solution of polymethylmethacrylate in a low-boiling-point solvent, the solvent then evaporating to yield a layer of polymethylmethacrylate. Following this step, both optically transparent electrodes bond to each other on the perimeter while the electrodes are spaced at a predetermined distance from one another, and the thus-formed space is filled through an opening (openings) in the adhesive with an electrochromic solution that contains cathodic and anodic components; the filled space is then sealed. The layer of polymethylmethacrylate is dissolved, and, as a result, the electrochromic solution thickens, and this significantly reduces the negative effect of gravitational “delamination” of the composition in the electrically colored state. Thus, actually the electrochromic composition is prepared only after completing the assembly of the aforementioned electrochromic device, and this limits the manufacturability of the device as a whole. In addition, the electrochromic composition is a liquid phase having viscosity defined by the amount of polymeric thickener, and the indifferent electrolyte solution introduced into the electrochromic solution provides electroconductivity of the latter if the cathodic and anodic components are not soluble in the ionic state. An indifferent electrolyte is introduced into compositions based on quaternary salts of bipyridine.


Also known in the art is a method for manufacturing an electrochromic device (U.S. Pat. No. 5,471,337 issued on Nov. 28, 1995, incorporated herein by reference) wherein the space between the electrodes is filled with an electrochromic dispersion system comprising the following: a dispersion medium in the form of a solvent that is thickened, preferably, with polymethylmethacrylate or is plasticized with a polymer solvent; a dispersion phase in the form of polyoxometalate as the cathodic component; and an anodic component.


Additionally known are methods for making an electrochromic device by obtaining a solid-like film of an electrochromic composition directly in the device itself by polymerization alone and/or polymerization with crosslinking of monomer chains with the use of initiators of different types (see EP 0612826 A1 of Aug. 31, 1994; WO 97/34186 of Sep. 18, 1997; and WO 98/42796 of Oct. 1, 1998, incorporated herein by reference). However, such polymerization reactions are accompanied by volume shrinkage adversely affecting the quality of the electrochromic device. This negative effect can be particularly manifested in electrochromic devices with large interelectrode spaces (1 to 2 mm) usually provided in electrochromic devices having large work surfaces (more than 0.5 m2).


Therefore, new and improved methods for manufacturing of electrochromic devices are needed that would not be subject to the above deficiencies of the prior art technology.


SUMMARY OF THE INVENTION

The inventive methodology is directed to methods and systems that substantially obviate one or more of the above and other problems associated with conventional methods for manufacturing electrochromic devices.


In accordance with one aspect of the embodiments described herein, there is provided a method for manufacturing an electrochromic device comprising at least two flexible electrodes and a hermetically closed space between the at least two flexible electrodes, at least one of the at least two flexible electrodes being optically transparent, wherein the hermetically closed space between the at least two flexible electrodes is filled with an electrochromic composition, the method comprising: preparing an initial deaerated electrochromic composition in the form of an electrochromic dispersion system containing at least one of a suspension and a colloid, wherein a dispersion medium of the electrochromic dispersion system comprises an electrochromic solution comprising a liquid solvent, a cathodic component, an anodic component, a polymerizable low-shrinkage monomer or a monomer mixture, and a polymerization thermal activator, wherein the dispersion phase consists of a highly dispersible polymer, and wherein the initial electrochromic composition is deaerated to remove the dissolved oxygen of air that were introduced with the highly dispersible polymer; (2) filling the hermetically closed space between the at least two flexible electrodes with the deaerated initial electrochromic composition, and (3) sealing the hermetically closed space between the at least two flexible electrodes.


In accordance with another aspect of the embodiments described herein, there is provided an electrochromic device comprising at least two flexible electrodes and a hermetically closed space between the at least two flexible electrodes, at least one of the at least two flexible electrodes being optically transparent, wherein the hermetically closed space between the at least two flexible electrodes is filled with an electrochromic composition, the electrochromic device being manufactured by a method comprising: (1) preparing an initial deaerated electrochromic composition in the form of an electrochromic dispersion system containing at least one of a suspension and a colloid, wherein a dispersion medium of the electrochromic dispersion system comprises an electrochromic solution comprising a liquid solvent, a cathodic component, an anodic component, a polymerizable low-shrinkage monomer or a monomer mixture, and a polymerization thermal activator, wherein the dispersion phase consists of a highly dispersible polymer, and wherein the initial electrochromic composition is deaerated to remove the dissolved oxygen of air that were introduced with the highly dispersible polymer; (2) filling the hermetically closed space between the at least two flexible electrodes with the deaerated initial electrochromic composition, and (3) sealing the hermetically closed space between the at least two flexible electrodes.


Additional aspects related to the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of the invention. Aspects of the invention may be realized and attained by means of the elements and combinations of various elements and aspects particularly pointed out in the following detailed description and the appended claims.


It is to be understood that both the foregoing and the following descriptions are exemplary and explanatory only and are not intended to limit the claimed invention or application thereof in any manner whatsoever.





BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are incorporated in and constitute a part of this specification exemplify the embodiments of the present invention and, together with the description, serve to explain and illustrate principles of the inventive technique. Specifically:



FIG. 1 shows the embodiment of an electrochromic device with two optically transparent electrodes.



FIG. 2 shows the projection of a set of layers that forms the electrochromic device.





DETAILED DESCRIPTION

In the following detailed description, reference will be made to the accompanying drawing(s), in which identical functional elements are designated with like numerals. The aforementioned accompanying drawings show by way of illustration, and not by way of limitation, specific embodiments and implementations consistent with principles of the present invention. These implementations are described in sufficient detail to enable those skilled in the art to practice the invention and it is to be understood that other implementations may be utilized and that structural changes and/or substitutions of various elements may be made without departing from the scope and spirit of present invention. The following detailed description is, therefore, not to be construed in a limited sense.


In accordance with one aspect of the embodiments described herein, there is provided an electrochromic device with an electrochromic composition in the form of a solid polymer layer that has an increased rate of discoloration in a wide temperature range and that imparts stability to the electrochromic device operating under conditions that maintain a long-term colored state and allow for high-voltage control and change of electrode polarity, which result in long-term uniformity of coloration and discoloration, especially for electrochromic devices having large work surface areas.


In accordance with another aspect of the embodiments described herein, there is provided an electrochromic device comprising at least two electrodes, wherein the electrodes are flexible and optically transparent and the interelectrode space is sealed and filled with the prepared electrochromic composition, as described above. The described device achieves long-term stability of a colored state and may operate under conditions that allow for high-voltage control and reversal of electrode polarity, resulting in uniformity of coloration and discoloration. In addition, the described electrochromic device may be manufactured to have a large surface area.


In one or more embodiments, there is provided a method for manufacturing an electrochromic device comprising at least two electrodes that are flexible and optically transparent with a hermetically closed space between the electrodes filled with an electrochromic composition that may contain transparent and insoluble microparticles that function as spacers. In one or more embodiments, the aforesaid method comprises the following steps: preparing an initial electrochromic composition in the form of an electrochromic dispersion system consisting of at least a suspension and/or a colloid, wherein the dispersion medium of said system is an electrochromic solution comprising a liquid solvent, a cathodic component, an anodic component, a polymerizable low-shrinkage monomer, and a polymerization thermal activator. The dispersion phase comprises a highly dispersible polymer. The initial electrochromic composition is deaerated to remove the dissolved oxygen of air that were introduced with the highly dispersible polymer and the hermetically closed space between the at least two flexible electrodes is filled with the initial deaerated electrochromic composition, and the enclosed space between the at least two flexible electrodes is then hermetically sealed.


In one or more embodiments, the method for manufacturing the electrochromic device comprises filling the electrochromic device with an electrochromic composition, which, in general, is an electrochromic dispersion system comprising at least a suspension and/or a colloid, wherein the dispersion medium of the system is an electrochromic solution containing a liquid solvent, a cathodic component, an anodic component, a polymerizable low-shrinkage monomer or monomers, and a polymerization thermal activator. The dispersion phase comprises a highly dispersible polymer. The initial electrochromic composition is deaerated to remove the dissolved oxygen of air that were introduced with the highly dispersible polymer and the hermetically closed space between the at least two flexible electrodes is filled with the initial deaerated electrochromic composition, and the enclosed space between the at least two flexible electrodes is then hermetically sealed.


In one or more embodiments, the aforesaid electrochromic solution may additionally contain an indifferent electrolyte. Provision of an indifferent electrolyte additionally introduced into the dispersion medium accelerates discoloration of the electrically activated electrochromic device and prevents violation of uniformity in coloration and discoloration after operation of the electrochromic device under conditions of long-term polarization with application of DC voltage and/or after application of high voltages.


In one or more embodiments, it is preferable to use the highly dispersed polymer in an amount sufficient to form a solid layer of the electrochromic composition, which is characterized by the lack of volumetric shrinkage during dissolution of the polymer in the above-described electrochromic solution over a wide temperature range.


In one or more embodiments, the low-shrinkage monomer is used in an amount sufficient to provide formation of a solid layer, which is formed after polymerization of the monomer/monomers in the presence of a high dispersible polymer. The monomer/monomers are selected based on their minimal shrinkage during polymerization. The thermal activator of polymerization is used in an amount necessary for the thermal activation of the used monomer or monomers.


In one or more embodiments, the aforesaid liquid solvent is an individual chemical compound or mixture of chemical compounds.


In one or more embodiments, the cathodic component is an individual organic electrochromic compound having at polarograms at least one reversible reduction wave or a mixture of such organic electrochromic compounds. The anodic component is an individual organic electrochromic compound having at polarograms at least one reversible oxidation wave or a mixture of organic electrochromic compounds.


In one or more embodiments, the composition may further comprise transparent insoluble microparticles that function as spacers. These spacers provide a predetermined distance between the transparent, conductive, flexible electrodes.


In one or more embodiments, deaeration of the initial electrochromic composition for removing dissolved oxygen and air introduced with the highly dispersed polymer can be carried out by evacuation.


In one or more embodiments, the described electrochromic device is manufactured by using flexible, optically transparent electrodes that comprise polymeric substrates (particularly, polyethylene terephthalate substrates) coated on one side thereof with a transparent electrically conductive layer of doped indium oxide (In2O3) or doped tin oxide (SnO2). The electrodes are hermetically bonded around the perimeter so that the conductive coating is located within the closed space defined between the electrodes to prevent contact between the electrodes. The sealing bond may comprise an adhesive joint that usually contains a spacer or spacers to provide a predetermined distance between electrodes. Since the polymeric substrate with the electrodes deposited on it is flexible and does not provide a gap between the surfaces of the conductive layers, the electrochromic composition may be combined with transparent insoluble microparticles that function as additional spacers. These spacers are evenly distributed over the volume occupied by the electrochromic composition. The spacers are comprised of glass or insoluble polymeric microparticles of a predetermined size, wherein the material of the spacers is selected so that it has a refractive index as close as possible to the refractive index of the electrochromic composition. Dimensions of the spacers can range from 20 μm to 200 μm, and determine the volume to be filled with the electrochromic composition.


In one or more embodiments, arranged along the outer perimeter of the adhesive joint or along the longest sides of the electrodes are busbars. The busbars can be located inside the adhesive connection with the withdrawal of conductors outside. One or several holes are left in the adhesive joint for filling the interelectrode space between the source electrodes with the electrochromic composition. After completion of the filling operation, the holes are closed with an inert sealant.


In one or more embodiments, to increase the viscosity of the electrochromic layer and to prevent the phenomenon of gravitational separation, the electrochromic composition can be additionally combined with a highly dispersible polymer. To further increase viscosity [of the composition] after filling the device, the composition can contain some amount of a polymerizable monomer or monomers. Such a monomer (or a monomer mixture) should possess low shrinkage during polymerization. This monomer belongs to the class of monomers polymerizable by a cationic mechanism; an example is a cationic ring-openable polymerization (CROP) monomer. Use of these monomers makes it possible practically to avoid shrinkage during the manufacture of the electrochromic devices. Such an electrochromic layer increases overvoltage of irreversible electrode reactions that are accompanied by gas evolution, which ensures the stability of the electrochromic device against the effects of elevated voltages (more than 2 V).


In one or more embodiments, a space between the electrodes is filled with the initial electrochromic composition through the hole or several holes left in the adhesive joint.



FIG. 1 shows an embodiment of an electrochromic device with two optically transparent electrodes. FIG. 2 shows the projection of an exemplary set of layers that forms the embodiment of the electrochromic device. The illustrated electrochromic device contains two flexible, optically transparent electrodes 1 and 2, which are deposited on substrates 3 and 4, respectively. The substrates 3 and 4 are polymer films, the surface areas of which depend on the specific use of the electrochromic device.


In one or more embodiments, the optically transparent electrodes 1 and 2 are provided with busbars 5 and 6, which are arranged over the entire perimeter on surfaces of the electrodes. The substrates 3 and 4 and their respective electrodes are bonded together along their perimeter by a sealant 7. Sealing may be done either by adhesive bonding or by thermally fusing the polymer substrates 3 and 4. To ensure a predetermined distance between the conductive, optically transparent electrodes 1 and 2, the cavity formed between electrodes is filled with spacers 8. The spacers can be made of glass or insoluble polymer microparticles. The spacers 8 are added to the electrochromic composition in the required amount during composition preparation and are uniformly distributed over the volume of the composition during the stage of device filling. After the device is filled with the electrochromic composition, it is finally sealed. If the polymerizable monomers contained in the electrochromic composition need thermal activation, then the device is heated after sealing. By means of respective wires 10 and 11, the busbars 5 and 6 are connected to a control device 12. When the device is exposed to intensive luminous fluxes, a part of the absorbed energy can be reflected as heat. To prevent the passage of heat radiation (e.g., into the room), the device may be provided with an additional thermally reflective layer 13, which promotes reflection of infrared radiation in the outward direction (e.g., to the street).


EXAMPLE 1

A first exemplary electrochromic device was manufactured to comprise two flexible, optically transparent SnO2 electrodes with a surface electric resistance of 35 Ohm/cm2 and with a polymeric substrate having a thickness of 200 μm. The size of the electrodes was (5×6) cm2. The electrodes were shifted against one another to provide a current supply and were glued along the perimeter by means of double-sided adhesive tape having a thickness of 100 μm. A hole was left in the adhesive joint having a width of 3 mm for filling the device with the initial electrochromic composition that comprised a dispersion system in the form of a suspension containing the following components: a dispersion medium (electrochromic solution), i.e., a solution of 0.01 M 1,1′-dibenzyl-4,4′-bipyridinium diperchlorate and 0.01 M 1,1′-diethylferrocene in propylene carbonate; and a dispersion phase (33 mass %), i.e., a copolymer of polymethylmethacrylate and methacrylic acid. Filling of the internal volume of the device by the initial electrochromic composition was performed with heating to a temperature of 70 to 80° C. After completion of the filling operation, the hole in the adhesive seam was sealed.


In this exemplary electrochromic device, the device transmittance in the visible range of the spectrum was 75%. Application to the device of 2 VDC caused uniform and intense coloring into a blue color in the direction from the busbars toward the center. At the wavelength of 610 nm, the time of shading to the minimal transmittance of 8% was 30 sec. When the voltage reached a steady state and short-circuiting of the electrodes, the application of voltage was discontinued, and the device returned to its initial (transparent) state. The time to complete discoloration was 30 sec.


EXAMPLE 2

A second exemplary electrochromic device was manufactured as the device in Example 1, but prior to filling, the initial electrochromic composition was evacuated for 15 minutes.


In this exemplary electrochromic device, in the visible range of the spectrum, device transmittance was 78%. Application to the device of 2 VDC caused uniform and intense coloring into a blue color. At the wavelength of 610 nm, the time of shading to minimal transmittance of 8% was 25 sec. When the voltage reached a steady state and short-circuiting of the electrodes, the application of voltage was discontinued, and the device returned to its initial (transparent) state. The time to complete discoloration was 20 sec.


EXAMPLE 3

A third exemplary electrochromic device was manufactured as the device in Example 1, but the initial electrochromic composition contained 3 mass % of glass microspheres having a size of 60 μm. The thickness of the sealing adhesive layer also was equal to 60 μm.


In this exemplary electrochromic device, the device transmittance in the visible range of the spectrum was 70%. Application to the device of 2 VDC caused uniform and intense coloring into a blue color in the direction from the busbars toward the center. At the wavelength of 610 nm, the time of shading to minimal transmittance of 8% was 30 sec. When the voltage reached a steady state and short-circuiting of the electrodes, the application of voltage was discontinued, and the device returned to its initial (transparent) state. The time to complete discoloration was 30 sec.


In this exemplary electrochromic device, on application of compressive mechanical stress perpendicular to the plane of the device, there was no significant change in color uniformity of the device.


Finally, it should be understood that processes and techniques described herein are not inherently related to any particular apparatus and may be implemented by any suitable combination of components. Further, various types of general purpose devices may be used in accordance with the teachings described herein. It may also prove advantageous to construct specialized apparatus to perform the method steps described herein. The present invention has been described in relation to particular examples, which are intended in all respects to be illustrative rather than restrictive.


Moreover, other implementations of the invention will be apparent to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. Various aspects and/or components of the described embodiments may be used singly or in any combination in methods for manufacturing electrochromic compositions for use in devices with electrically controlled absorption of light. It is intended that the specification and examples be considered as exemplary only, with a true scope and spirit of the invention being indicated by the following claims.

Claims
  • 1. A method for manufacturing an electrochromic device comprising at least two flexible electrodes and a hermetically closed space between the at least two flexible electrodes, at least one of the at least two flexible electrodes being optically transparent, wherein the hermetically closed space between the at least two flexible electrodes is filled with an electrochromic composition, the method comprising: (1) preparing an initial deaerated electrochromic composition in the form of an electrochromic dispersion system containing a colloid,wherein a continuous phase of the electrochromic dispersion system comprises, an electrochromic solution comprising a liquid solvent,a cathodic component,an anodic component,a polymerizable low-shrinkage monomer or a monomer mixture comprising a cationic ring-openable polymerization monomer, anda polymerization thermal activator,wherein a non-continuous phase, of said electrochromic dispersion system, consists of a dispersible polymer, wherein said non-continuous phase is said colloid, andwherein the initial electrochromic composition is deaerated to remove the dissolved oxygen of air that were introduced with the dispersible polymer;(2) filling the hermetically closed space between the at least two flexible electrodes with the deaerated initial electrochromic composition; and(3) sealing the hermetically closed space between the at least two flexible electrodes.
INCORPORATION BY REFERENCE TO ANY PRIORITY APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 16/436,731, filed on Jun. 10, 2019, entitled “ELECTROCHROMIC DEVICE AND METHOD FOR MANUFACTURING ELECTROCHROMIC DEVICE,” which is a continuation of U.S. patent application Ser. No. 14/300,220, filed Jun. 9, 2014, now U.S. Pat. No. 10,344,208, entitled “ELECTROCHROMIC DEVICE AND METHOD FOR MANUFACTURING ELECTROCHROMIC DEVICE”. This application is related to U.S. patent application Ser. No. 14/300,216, filed Jun. 9, 2014, now U.S. Pat. No. 10,294,415, entitled “ELECTROCHROMIC COMPOSITION AND ELECTROCHROMIC DEVICE USING SAME.” Each of the above applications is incorporated herein by reference in its entirety.

US Referenced Citations (144)
Number Name Date Kind
5774255 Howard Jun 1998 A
6067184 Bonhote et al. May 2000 A
6509999 Shelepin et al. Jan 2003 B1
6853472 Warner et al. Feb 2005 B2
7106489 Berneth et al. Sep 2006 B2
7256925 Noh et al. Aug 2007 B2
7295361 Gavrilov et al. Nov 2007 B2
7428091 Baumann et al. Sep 2008 B2
7638632 French et al. Dec 2009 B2
7667043 Getty et al. Feb 2010 B2
7988885 Percec et al. Aug 2011 B2
8323534 Percec et al. Dec 2012 B2
8736943 Guarr et al. May 2014 B2
8867116 Kloeppner et al. Oct 2014 B1
8902486 Chandrasekhar Dec 2014 B1
8947758 Agrawal et al. Feb 2015 B2
9057925 Veenman et al. Jun 2015 B2
9069222 Naijo et al. Jun 2015 B2
9145090 Barksdale et al. Sep 2015 B2
9159890 Moosburger et al. Oct 2015 B2
9170466 Marcel et al. Oct 2015 B2
9207515 Chandrasekhar Dec 2015 B2
9304368 Yashiro et al. Apr 2016 B2
9440588 Nelson et al. Sep 2016 B2
9482880 Chandrasekhar et al. Nov 2016 B1
9500888 Schwartz et al. Nov 2016 B2
9500926 Fujimura et al. Nov 2016 B2
9529240 Paolini et al. Dec 2016 B2
9547213 Lee et al. Jan 2017 B2
9738140 Ash et al. Aug 2017 B2
9766496 Cammenga et al. Sep 2017 B2
9778534 Tran et al. Oct 2017 B2
9785030 Biver et al. Oct 2017 B2
9807847 Wang et al. Oct 2017 B2
9810963 Gauthier et al. Nov 2017 B2
9823796 Wang Nov 2017 B2
9829762 Takahashi et al. Nov 2017 B2
9841652 Biver et al. Dec 2017 B2
9857656 Seo et al. Jan 2018 B2
9869918 Matsumoto et al. Jan 2018 B2
9880441 Osterhout Jan 2018 B1
9897497 Yashiro et al. Feb 2018 B2
9933680 Taya et al. Apr 2018 B2
9939703 Nguyen Apr 2018 B1
9955577 Cho et al. Apr 2018 B2
10344208 Vasiliev Jul 2019 B2
20020021481 Lin et al. Feb 2002 A1
20030161025 Asano Aug 2003 A1
20040257633 Agrawal et al. Dec 2004 A1
20060050357 Gavrilov et al. Mar 2006 A1
20090027757 Kokeguchi Jan 2009 A1
20090279160 Percec et al. Nov 2009 A1
20100018578 Yu Jan 2010 A1
20100110523 Varaprasad May 2010 A1
20110147680 Percec et al. Jun 2011 A1
20110149366 Percec et al. Jun 2011 A1
20110216389 Piroux et al. Sep 2011 A1
20110222138 Piroux et al. Sep 2011 A1
20110317243 Piroux et al. Dec 2011 A1
20120139824 Takahashi Jun 2012 A1
20120242614 Ferreira et al. Sep 2012 A1
20130251943 Pei Sep 2013 A1
20140198370 Trajkovska-Broach et al. Jul 2014 A1
20150077832 Berland et al. Mar 2015 A1
20150153624 Yamada et al. Jun 2015 A1
20150160525 Shi Jun 2015 A1
20150212382 Miyazaki Jul 2015 A1
20150219974 Trajkovska-Broach et al. Jul 2015 A1
20150227016 Yamada et al. Jul 2015 A1
20150261009 Boulton Sep 2015 A1
20150261056 Kumar et al. Sep 2015 A1
20150286107 Chen et al. Oct 2015 A1
20150322296 Keite-Telgenbuscher et al. Nov 2015 A1
20150338714 Li Nov 2015 A1
20150346573 Theiste et al. Dec 2015 A1
20150378396 Park et al. Dec 2015 A1
20160005375 Naijo et al. Jan 2016 A1
20160011428 Li et al. Jan 2016 A1
20160033836 Chen Feb 2016 A1
20160033839 Lee et al. Feb 2016 A1
20160033842 Shi et al. Feb 2016 A1
20160041447 Yamamoto et al. Feb 2016 A1
20160079560 Guimard Mar 2016 A1
20160167339 Dollase et al. Jun 2016 A1
20160167584 Chan et al. Jun 2016 A1
20160170277 Lu et al. Jun 2016 A1
20160203399 Cox Jul 2016 A1
20160223877 Magdassi et al. Aug 2016 A1
20160229803 Lin et al. Aug 2016 A1
20160231635 Aiken et al. Aug 2016 A1
20160243773 Wang Aug 2016 A1
20160246152 Igawa et al. Aug 2016 A1
20160259224 Ozyilmaz et al. Sep 2016 A1
20160266461 Yamamoto Sep 2016 A1
20160282978 Wang Sep 2016 A1
20160299401 Kubo et al. Oct 2016 A1
20160306251 Yamamoto et al. Oct 2016 A1
20170003562 Kubo et al. Jan 2017 A1
20170018370 Segawa et al. Jan 2017 A1
20170031224 Gil et al. Feb 2017 A1
20170031226 Gauthier et al. Feb 2017 A1
20170059957 Garcia et al. Feb 2017 A1
20170082864 Zhao et al. Mar 2017 A1
20170100991 Cammenga et al. Apr 2017 A1
20170108754 Ali Apr 2017 A1
20170114274 Yamada et al. Apr 2017 A1
20170117505 Kwon Apr 2017 A1
20170131609 Okada et al. May 2017 A1
20170146882 Bass et al. May 2017 A1
20170158139 Tonar et al. Jun 2017 A1
20170168363 Kim et al. Jun 2017 A1
20170176833 Goto et al. Jun 2017 A1
20170192334 An et al. Jul 2017 A1
20170199383 Machida Jul 2017 A1
20170219900 Kim et al. Aug 2017 A1
20170229000 Law Aug 2017 A1
20170235203 Yamamoto et al. Aug 2017 A1
20170235204 Bergh et al. Aug 2017 A1
20170239931 Wolk et al. Aug 2017 A1
20170293193 Miyazaki Oct 2017 A1
20170298682 Wang et al. Oct 2017 A1
20170307952 Ash et al. Oct 2017 A1
20170313934 Yamada et al. Nov 2017 A1
20170315384 Saylor et al. Nov 2017 A1
20170329196 Timmennan et al. Nov 2017 A1
20170329197 Yashiro et al. Nov 2017 A1
20170329199 Yashiro et al. Nov 2017 A1
20170336692 Park et al. Nov 2017 A1
20170349103 Tonar et al. Dec 2017 A1
20170351126 Chu et al. Dec 2017 A1
20170355313 Park et al. Dec 2017 A1
20170355901 Branda et al. Dec 2017 A1
20180004013 Vasiliev et al. Jan 2018 A1
20180017835 Kim et al. Jan 2018 A1
20180039148 Franz et al. Feb 2018 A1
20180066132 Nair et al. Mar 2018 A1
20180074377 You et al. Mar 2018 A1
20180088426 Posset et al. Mar 2018 A1
20180095338 Ash et al. Apr 2018 A1
20180100056 Wang et al. Apr 2018 A1
20180105738 Giri Apr 2018 A1
20180112127 Franz et al. Apr 2018 A1
20180113366 Kaneko et al. Apr 2018 A1
20180121011 Vasiliev et al. May 2018 A1
Foreign Referenced Citations (55)
Number Date Country
104698717 Jun 2015 CN
104865767 Aug 2015 CN
106997134 Aug 2017 CN
107779190 Mar 2018 CN
107814493 Mar 2018 CN
102017118091 Mar 2018 DE
0725304 Apr 2003 EP
3118613 Jan 2017 EP
201617044949 Apr 2017 IN
201737006673 May 2017 IN
201737017732 Aug 2017 IN
H 10-239715 Sep 1998 JP
2009-529153 Aug 2009 JP
2011-133622 Jul 2011 JP
2012-529661 Nov 2012 JP
2015-007628 Jul 2015 KR
722219 Feb 1993 RU
860456 Feb 1993 RU
1334662 Feb 1993 RU
972815 Oct 1993 RU
2009530 Mar 1994 RU
2059974 May 1996 RU
2063644 Jul 1996 RU
2079864 May 1997 RU
2110823 May 1998 RU
2130630 May 1999 RU
2144937 Jan 2000 RU
2216757 Nov 2003 RU
2224275 Feb 2004 RU
2321113 Mar 2008 RU
2569913 Dec 2015 RU
2642558 Jan 2018 RU
0995146 Jun 2003 SI
566863 Jul 1977 SU
201537274 Apr 2016 TW
WO 2014134714 Sep 2014 WO
WO 2014143011 Sep 2014 WO
WO 2015040029 Mar 2015 WO
WO 2015130227 Sep 2015 WO
WO 2015163824 Oct 2015 WO
WO 2015179564 Nov 2015 WO
WO 2015183821 Dec 2015 WO
WO 2015193301 Dec 2015 WO
WO 2016000996 Jan 2016 WO
WO 2016028828 Feb 2016 WO
WO 2016081787 May 2016 WO
WO 2016145120 Sep 2016 WO
WO 2016196546 Dec 2016 WO
WO 2016209323 Dec 2016 WO
WO 2017094218 Jun 2017 WO
WO 2017106852 Jun 2017 WO
WO 2017109265 Jun 2017 WO
WO 2017153403 Sep 2017 WO
WO 2018007355 Jan 2018 WO
WO 2018038743 Mar 2018 WO
Non-Patent Literature Citations (5)
Entry
Alesanco, et al., “All-in-one gel-based electrochromic devices: Strengths and recent developments,” Materials, 2018, 11, 414, 27 pages.
Gusev, Technical Report (3-D Printer, Electrochrom), Dec. 2012, retrieved from https://www.researchgate.net/publication/311562920.
Percec et al., “A Single-Layer Approach to Electrochromic Materials,” Journal of Polymer Science, Part A: Polymer Chemistry, 2010, vol. 49, pp. 361-368.
International Search Report and Written Opinion from PCT/US2015/054337, dated Jan. 13, 2016.
Japanese Office Action from Japanese Application No. 2018-538517, dated Jul. 2, 2019, 3 pages.
Related Publications (1)
Number Date Country
20200333676 A1 Oct 2020 US
Continuations (2)
Number Date Country
Parent 16436731 Jun 2019 US
Child 16915896 US
Parent 14300220 Jun 2014 US
Child 16436731 US