Patent Application
20130280604
1. Field of the Invention
The present invention relates to electrode active materials, nonaqueous secondary battery electrodes, and nonaqueous secondary batteries.
2. Description of the Related Art
Recently, the widespread use of hybrid cars, which can be driven by the energy of both gasoline and electricity, and devices requiring power supplies, such as uninterruptible power supplies, mobile communications devices, and portable electronic devices, has created an enormous need for improvements in the performance of rechargeable storage devices used therefor as power supplies. Specifically, there is a need for improved properties such as increased power, capacity, and cycle life.
To provide storage devices with such properties, research has been directed to the use of organic compounds as electrode active materials. Recently, organic compounds having a π-electron conjugated cloud have been suggested as novel active materials capable of absorbing and releasing lithium, which has the potential for high-speed charge and discharge (see, for example, Patent Documents 1 and 2). Also suggested is a lithium-dicarboxylate containing conjugated organic active material having an organic backbone composed of dilithium trans-muconate or dilithium terephthalate (see, for example, Non-Patent Document 1). This active material is characterized in that its organic backbone has a conjugated structure, which allows oxidation and reduction (absorption and release of lithium).
Also suggested are negative electrodes based on the conversion reaction of a metal oxide (e.g., MOx, where M is Fe, Co, Ni, Cu, Mn, or the like) such as manganese oxide or iron oxide (see, for example, Non-Patent Documents 2 to 4). These negative electrodes are charged and discharged by the reaction formula MOx+xe−+2xLi+→M+xLi2O.
The batteries in Patent Documents 1 and 2 described above, however, operate at a potential of 2.8 to 3.7 V with respect to lithium metal, meaning that they have insufficient energy densities. The battery in Non-Patent Document 1 has a conjugated structure that allows absorption and release of lithium, although the charge-discharge capacity thereof is insufficient, and there is a need for improved charge-discharge properties. Typical negative electrode materials used for lithium batteries are currently carbon materials such as graphite, which allow a redox reaction to occur at about 50 mV with respect to metallic lithium. This potential is close to that of metallic lithium, and there is a need for a secondary battery that has a sufficiently higher potential than lithium metal and that can itself operate at a higher voltage.
For negative electrodes based on conversion reaction, the lithium absorption reaction, which corresponds to the charge reaction at the negative electrode, occurs at a potential of 0.5 to 1.0 V with respect to metallic lithium, although the lithium release potential, which corresponds to the discharge reaction at the negative electrode, occurs at a potential of 1.5 to 2.0 V with respect to metallic lithium; thus, the negative electrode is considerably polarized. When used as a negative electrode, therefore, electrodes based on conversion reaction cause a problem in that the battery voltage drops during discharge.
In view of the foregoing problems, a primary object of the present invention is to provide electrode active materials with improved charge-discharge properties, nonaqueous secondary battery electrodes, and nonaqueous secondary batteries.
After conducting extensive research in order to achieve the above object, the inventors have found that a composition prepared using an aromatic compound that is a dicarboxylic acid anion by allowing lithium to coordinate to oxygen contained in the carboxylic acid and modifying the crystal structure thereof has improved charge-discharge properties with chemical stability, thus completing the present invention.
An electrode active material comprises a layered composition including: organic backbone layers containing an aromatic compound that is a dicarboxylic acid anion having two or more aromatic ring structures; and alkali metal element layers containing an alkali metal element coordinated to oxygen contained in the carboxylic acid anion to form a backbone, wherein the aromatic compound contained in the organic backbone layers has a naphthalene backbone, and wherein the layered composition has an interplanar spacing between (002) planes of 0.42400 to 0.42800 nm, an interplanar spacing between (102) planes of 0.37000 to 0.37600 nm, an interplanar spacing between (211) planes of 0.32250 to 0.32650 nm, and an interplanar spacing between (112) planes of 0.30400 to 0.30700 nm, as measured by X-ray diffraction.
A nonaqueous secondary battery electrode of the present invention includes the electrode active material described above.
A nonaqueous secondary battery of the present invention includes the nonaqueous secondary battery electrode described above and the ion-conducting medium that conducts alkali metal ions.
The electrode active material, nonaqueous secondary battery electrode, and nonaqueous secondary battery of the present invention provide improved charge-discharge properties. Although not fully understood, it is believed that this advantage is provided for the following reason. For example, the layered composition, serving as an active material, has four coordination bonds between the oxygen in the dicarboxylic acid and the alkali metal element (e.g., lithium), which presumably makes it insoluble in the nonaqueous electrolyte solution to maintain its crystal structure, thus improving the stability of the charge-discharge cyclability. In the layered composition, the organic backbone layers presumably function as redox sites, whereas the alkali metal element layers presumably function as alkali-metal-ion absorbing sites responsible for charge and discharge. In addition, for example, in the case of a negative electrode active material for a nonaqueous secondary battery that uses lithium ions, the electrode of the present invention has a charge-discharge potential of 0.5 to 1.0 V with respect to lithium metal, which prevents a significant decrease in energy density due to a decrease in the operating voltage of the battery and also prevents precipitation of lithium metal around 0 V with respect to lithium metal. This novel layered composition (crystalline organic-inorganic composite material) presumably improves the charge-discharge properties.
Furthermore, because the layered composition has a structure whose interplanar spacings, measured by X-ray diffraction, between planes such as (002) planes, (102) planes, (211) planes, and (112) planes fall within the preferred ranges, it probably increases the π-electron interaction of the aromatic compound, thus allowing exchange of more electrons. In addition, the layered composition presumably has fewer defects in the alkali metal element layers, which are made of an alkali metal and oxygen, and thus allows exchange of more ions, which increases the performance as an electrode active material. This presumably improves the capacity density and the charge-discharge cycling stability and thus improves the charge-discharge properties.
A nonaqueous secondary battery of the present invention includes a positive electrode containing a positive electrode active material that absorbs and releases an alkali metal, a negative electrode containing a negative electrode active material that absorbs and releases the alkali metal, and an ion-conducting medium that is disposed between the positive electrode and the negative electrode and that conducts alkali ions. At least one of the positive and negative electrodes of the nonaqueous secondary battery of the present invention contains a layered composition of the present invention as an electrode active material. The layered composition of the present invention includes organic backbone layers containing an aromatic compound that is a dicarboxylic acid anion having two or more aromatic ring structures and alkali metal element layers containing an alkali metal element coordinated to oxygen contained in the carboxylic acid anion to form a backbone. The layered composition of the present invention is preferably a negative electrode active material. In addition, the alkali metal contained in the alkali metal element layers may be, for example, one or more of Li, Na, K, and the like, preferably Li. In addition, the alkali metal that is absorbed and released during charge and discharge may be the same as or different from the alkali metal element contained in the alkali metal element layers, for example, one or more of Li, Na, K, and the like. As an electrode active material, a layered composition used as a negative electrode active material and including organic backbone layers containing an aromatic compound having a naphthalene backbone and alkali metal element layers containing Li will be mainly described. As a nonaqueous secondary battery, additionally, a nonaqueous secondary battery that uses the layered composition as a negative electrode active material and Li as an alkali metal that is absorbed and released during charge and discharge will be mainly described below.
The electrode active material of the present invention is made of a layered composition including organic backbone layers containing an aromatic compound that is a dicarboxylic acid anion having a naphthalene backbone structure and alkali metal element layers containing an alkali metal element coordinated to oxygen contained in the carboxylic acid anion to form a backbone.
(wherein R is a naphthalene backbone structure, and A is an alkali metal element.)
The organic backbone layers contain an aromatic compound that is a dicarboxylic acid anion having a naphthalene backbone structure. The aromatic compound contained in the organic backbone layers preferably has the two carboxylic acid anions of the dicarboxylic acid anion attached to diagonally opposite positions of the aromatic ring structures. This facilitates formation of the layered structure of the organic backbone layers and the alkali metal element layers. The diagonally opposite positions to which the carboxylic acids are attached may be, for example, the 2- and 6-positions of naphthalene. The aromatic compound contained in the organic backbone layers may have a structure represented by general formula (2).
As shown in
The layered composition forming the electrode active material of the present invention has an interplanar spacing between (002) planes of 0.42400 to 0.42800 nm as measured by X-ray diffraction.
The layered composition preferably has an interplanar spacing between (200) planes of 0.50500 to 0.50950 nm as measured by X-ray diffraction.
Next, the nonaqueous secondary battery of the present invention will be described. The negative electrode of the nonaqueous secondary battery of the present invention may be formed by, for example, preparing a paste-like negative electrode mixture using a negative electrode active material made of a layered composition, a conductor, a binder, and a suitable solvent, applying the negative electrode mixture to a surface of a collector and drying it, and optionally compressing the coating for higher electrode density. The conductor may be any electron-conducting material that does not adversely affect the battery performance of the negative electrode, for example, one or a mixture of two or more of graphites such as natural graphite (flaky graphite and scaly graphite) and artificial graphite, acetylene black, carbon black, Ketjen black, carbon whisker, needle coke, carbon fiber, metals (e.g., copper, nickel, aluminum, silver, and gold), and the like. Among these conductors, carbon black and acetylene black are preferred for higher electron conductivity and coatability. Examples of binders, which function to bind active material particles with conductor particles, include fluorine-containing resins such as polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), and fluororubbers, thermoplastic resins such as polypropylene and polyethylene, ethylene-propylene-diene monomer (EPDM) rubber, sulfonated EPDM rubber, and natural butyl rubber (NBR), which can be used alone or as a mixture of two or more. Other examples include water-based binders such as cellulose binders and aqueous styrene-butadiene rubber (SBR) dispersions. Examples of solvents for dispersing the negative electrode active material, the conductor, and the binder include organic solvents such as N-methylpyrrolidone, dimethylformamide, dimethylacetoamide, methyl ethyl ketone, cyclohexanone, methyl acetate, methyl acrylate, diethylenetriamine, N,N-dimethylaminopropylamine, ethylene oxide, and tetrahydrofuran. The active material can also be slurried with, for example, a latex of SBR in water containing a dispersant and a thickener. Examples of thickeners include polysaccharides such as carboxymethyl cellulose and methyl cellulose, which can be used alone or as a mixture of two or more. Examples of coating techniques include roller coating using applicator rollers, screen coating, doctor blade coating, spin coating, and bar coating, any of which can be used to provide any thickness and shape. Examples of collectors include copper, nickel, stainless steel, titanium, aluminum, baked carbon, conductive polymer, conductive glass, and Al—Cd alloy collectors, as well as collectors formed of copper or the like and surface-treated with carbon, nickel, titanium, silver, or the like for improved adhesion, conductivity, and reduction resistance. The collector of the negative electrode is preferably formed of aluminum metal. That is, the layered composition is preferably provided on an aluminum metal collector. This is because aluminum is abundant and is highly resistant to corrosion. Such collectors can also be surface-treated by oxidation. Examples of shapes of collectors include foils, films, sheets, nets, punched or expanded shapes, laths, porous shapes, foams, and fiber bundles. The collector has a thickness of, for example, 1 to 500 μm.
The electrode of the nonaqueous secondary battery of the present invention may be formed by providing an electrode mixture containing a layered composition and a conductor on a collector and baking the electrode mixture in a temperature range of 250° C. to 450° C. in an inert atmosphere. The layered composition includes organic backbone layers containing an aromatic compound that is a dicarboxylic acid anion having a naphthalene backbone and alkali metal element layers containing an alkali metal element coordinated to oxygen contained in the carboxylic acid anion to form a backbone. In this manner, the interplanar spacings between (002) planes, (102) planes, (211) planes, (112) planes, and (200) planes in the layered composition can be relatively easily controlled within the above ranges. In baking, a baking temperature of 250° C. or higher is preferred for improved charge-discharge properties, and a baking temperature of 450° C. or lower is preferred for reduced structural damage to the layered composition. Preferably, the baking temperature is 275° C. to 350° C., more preferably about 300° C. The baking time is selected depending on the baking temperature and is preferably, for example, 2 to 24 hours. In addition, the inert atmosphere may be, for example, an inert gas such as nitrogen gas, He, or Ar, preferably Ar. The conductor and the collector may be those described above, and as described above, the electrode mixture may contain a binder and a solvent.
The positive electrode of the nonaqueous secondary battery of the present invention may be formed by, for example, preparing a paste-like positive electrode mixture using a positive electrode active material, a conductor, a binder, and a suitable solvent, applying the positive electrode mixture to a surface of a collector and drying it, and optionally compressing the coating for higher electrode density. Examples of positive electrode active materials include sulfides containing a transition metal element and oxides containing lithium and a transition metal element. Specific examples include transition metal sulfides such as TiS2, TiS3, MoS3, and FeS2; lithium manganese multiple oxides such as Li(1-a)MnO2 (e.g., 0<a<1, which applies hereinafter) and Li(1-a)Mn2O4; lithium cobalt multiple oxides such as Li(1-a)CoO2; lithium nickel multiple oxides such as Li(1-a)NiO2; lithium vanadium multiple oxides such as LiV2O3; and transition metal oxides such as V2O5. Particularly preferred are transition metal multiple oxides of lithium, including LiCoO2, LiNiO2, LiMnO2, and LiV2O3. Examples of conductors, binders, and solvents used for the positive electrode include those illustrated for the negative electrode. Examples of collectors for the positive electrode include aluminum, titanium, stainless steel, nickel, iron, baked carbon, conductive polymer, and conductive glass collectors, as well as collectors formed of aluminum, copper, or the like and surface-treated with carbon, nickel, titanium, silver, or the like for improved adhesion, conductivity, and oxidation resistance. Such collectors can also be surface-treated by oxidation. The shape of the collector may be similar to that of the collector for the negative electrode.
The ion-conducting medium of the nonaqueous secondary battery of the present invention may be, for example, a nonaqueous electrolyte solution or nonaqueous gel electrolyte solution containing a support salt. Examples of solvents for nonaqueous electrolyte solutions include carbonates, esters, ethers, nitriles, furans, sulfolanes, and dioxolanes, which can be used alone or as a mixture. Specific examples include, as carbonates, cyclic carbonates such as ethylene carbonate, propylene carbonate, vinylene carbonate, butylene carbonate, and chloroethylene carbonate and linear carbonates such as dimethyl carbonate, ethyl methyl carbonate, diethyl carbonate, ethyl-n-butyl carbonate, methyl-t-butyl carbonate, di-1-propyl carbonate, and t-butyl-1-propyl carbonate; cyclic esters such as γ-butyrolactone and γ-valerolactone; linear esters such as methyl formate, methyl acetate, ethyl acetate, and methyl lactate; ethers such as dimethoxyethane, ethoxymethoxyethane, and diethoxyethane; nitriles such as acetonitrile and benzonitrile; furans such as tetrahydrofuran and methyltetrahydrofuran; sulfolanes such as sulfolane and tetramethylsulfolane; and dioxolanes such as 1,3-dioxolane and methyldioxolane. Particularly preferred are combinations of a cyclic carbonate and a linear carbonate. Such combinations are advantageous not only in terms of cyclability, which indicates battery properties after repeated charge and discharge, but also in terms of the balance of the properties such as the viscosity of the electrolyte solution, the electrical capacity of the resulting battery, and the output of the battery. The cyclic carbonate probably increases the dielectric constant of the electrolyte solution because of its relatively high dielectric constant, whereas the linear carbonate probably reduces the viscosity of the electrolyte solution.
Examples of support salts contained in the nonaqueous secondary battery of the present invention include LiPF6, LiBF4, LiAsF6, LiCF3SO3, LiN(CF3SO2)2, LiC(CF3SO2)3, LiSbF6, LiSiF6, LiAlF4, LiSCN, LiClO4, LiCl, LiF, LiBr, LiI, and LiAlCl4. In particular, one or a combination of two or more salts selected from the group consisting of inorganic salts such as LiPF6, LiBF4, LiAsF6, and LiClO4 and organic salts such as LiCF3SO3, LiN(CF3SO2)2, and LiC(CF3SO2)3 is preferably used for improved electrical properties. The concentration of the support salt in the nonaqueous electrolyte solution is preferably 0.1 to 5 mol/L, more preferably 0.5 to 2 mol/L. A support salt concentration of 0.1 mol/L or more provides sufficient current density, whereas a support salt concentration of 5 mol/L or less improves the stability of the electrolyte solution. The nonaqueous electrolyte solution may contain a flame retardant such as a phosphorus- or halogen-containing flame retardant.
Instead of a liquid ion-conducting medium, the ion-conducting medium may be a solid ion-conducting polymer. The ion-conducting polymer may be a polymer gel containing a polymer, such as acrylonitrile, ethylene oxide, propylene oxide, methyl methacrylate, vinyl acetate, vinylpyrrolidone, or polyvinylidene fluoride, and a support salt. The ion-conducting polymer may also be used in combination with a nonaqueous electrolyte solution. In addition to ion-conducting polymers, examples of available ion-conducting media include inorganic solid electrolytes, mixtures of organic polymer electrolytes and inorganic solid electrolytes, and inorganic solid powders bound by organic binders.
The nonaqueous secondary battery of the present invention may include a separator between the positive electrode and the negative electrode. The separator may be formed of any composition that can be used in the operating range of the nonaqueous secondary battery, including polymer nonwoven fabrics such as polypropylene and polyphenylene sulfide nonwoven fabrics and thin macroporous films of olefin resins such as polyethylene and polypropylene. They may be used alone or as a mixture thereof.
Examples of shapes of the nonaqueous secondary battery of the present invention include, but not limited to, coins, buttons, sheets, laminates, cylinders, flat shapes, and rectangles. The nonaqueous secondary battery is also applicable to large batteries for use with, for example, electric cars.
In the nonaqueous secondary battery of the present invention described in detail above, the layered composition, serving as an active material, has four coordination bonds between Li and the oxygen in the dicarboxylic acid, which presumably makes it insoluble in the nonaqueous electrolyte solution to maintain its crystal structure, thus improving the stability of the charge-discharge cyclability. In the layered composition, the organic backbone layers presumably function as redox sites, whereas the Li layers presumably function as Li-ion absorbing sites. In addition, the negative electrode has a charge-discharge potential of 0.5 to 1.0 V with respect to lithium metal, which prevents a significant decrease in energy density due to a decrease in the operating voltage of the battery and also prevents precipitation of lithium metal. This novel layered composition (crystalline organic-inorganic composite material) presumably improves the charge-discharge properties. Furthermore, because the layered composition has a structure whose interplanar spacings, measured by X-ray diffraction, between planes such as (002) planes, (102) planes, (211) planes, and (112) planes fall within the preferred ranges, it increases the n-electron interaction of the aromatic compound, thus allowing exchange of more electrons. In addition, particularly if the layered composition has a structure whose interplanar spacing between (200) planes falls within the preferred range, the layered composition has fewer defects in the alkali metal element layers, which are made of an alkali metal and oxygen, and thus allows exchange of more ions, which increases the performance as an electrode active material. This presumably improves the capacity density and the cycling stability and thus improves the charge-discharge properties.
It should be understood that the present invention is not limited to the above embodiment but can be practiced in various embodiments within the technical scope of the present invention.
For example, although the interplanar spacings, measured by X-ray diffraction, between planes such as (002) planes, (102) planes, (211) planes, (112) planes, and (200) planes in the layered composition are controlled within the preferred ranges for improved charge-discharge properties by baking the nonaqueous secondary battery electrode containing the layered composition in the embodiment described above, the interplanar spacings may be controlled within the preferred ranges in other manners. For example, the interplanar spacings between (002) planes, (102) planes, (211) planes, (112) planes, and (200) planes may be controlled within the preferred ranges by setting conditions preferred for preparation of the layered composition. Alternatively, the layered composition may be formed by allowing an alkali metal element to coordinate to naphthalenedicarboxylic acid, be baked as a mixture with a carbon material (e.g., a conductor) to achieve the preferred interplanar spacings, and be applied as a paste-like electrode mixture to a collector.
Although the above embodiment illustrates a nonaqueous secondary battery, a nonaqueous secondary battery electrode and an electrode active material may also be provided.
Specific examples of fabrication of nonaqueous secondary batteries of the present invention will be described below as the Examples. First, results of research on layered compositions will be described below as the Experimental Examples.
Lithium 2,6-naphthalenedicarboxylate was synthesized as a layered composition shown in
Fabrication of Coated Electrode
A nonaqueous secondary battery electrode was fabricated using the active material powder of Experimental Example 1. A slurried mixture was prepared by mixing 60% by mass of the lithium 2,6-naphthaleledicarboxylate of Experimental Example 1, 30% by mass of carbon black as a conductor, and 10% by mass of polyvinylidene fluoride as a binder and dispersing the mixture using an appropriate amount of N-methyl-2-pyrrolidone as a dispersant. The slurried mixture was uniformly applied to a 10 μm thick copper foil collector and was dried by heating to fabricate a coated sheet. The coated sheet was then pressed and punched to prepare a circular electrode having an area of 2.05 cm2.
Fabrication of Bipolar Test Cell
A nonaqueous electrolyte solution was prepared by adding lithium hexafluorophosphate to a concentration of 1 mol/L in a nonaqueous solvent containing ethylene carbonate, dimethyl carbonate, and ethyl methyl carbonate in a volume ratio of 30:40:30. A bipolar test cell was fabricated by holding a separator (Tonen Tapyrus Co., Ltd.) impregnated with the above nonaqueous electrolyte solution between the above electrode, serving as a working electrode, and a lithium metal foil (300 μm thick), serving as a counter electrode. The resulting cell is referred to as a bipolar test cell of Experimental Example 1.
A white powder sample was yielded as an active material powder of Experimental Example 2 by repeating the procedure of Experimental Example 1 except that lithium terephthalate was synthesized instead of the lithium 2,6-naphthalenedicarboxylate of Experimental. Example 1. This active material was a layered composition including organic backbone layers having the basic structure represented by formula (5) below. Also, a nonaqueous secondary battery electrode of Experimental Example 2 was fabricated by repeating the procedure of Experimental Example 1 using the active material powder of Experimental Example 2, and a bipolar test cell was fabricated using the nonaqueous secondary battery electrode of Experimental Example 2.
A white powder sample was yielded as an active material powder of Experimental Example 3 by repeating the procedure of Experimental Example 1 except that lithium 2,3-naphthalenedicarboxylate was synthesized instead of the lithium 2,6-naphthalenedicarboxylate of Experimental Example 1. This active material, described in detail later, did not form a layered composition and was a compound having formula (6) below. Also, a nonaqueous secondary battery electrode of Experimental Example 3 was fabricated by repeating the procedure of Experimental Example 1 using the active material powder of Experimental Example 3, and a bipolar test cell was fabricated using the nonaqueous secondary battery electrode of Experimental Example 3.
(X-Ray Diffraction Measurement)
Powdered X-ray diffraction measurement was performed on the active material powders of Experimental Examples 1 to 3. In the measurement, the Cu—Kα line (wavelength: 1.54051 Å) was used as radiation, and an X-ray diffractometer (Rigaku RINT-2200) was used. In the measurement, additionally, a single-crystal graphite monochromator was used as a monochromatic X-ray source, the applied voltage was set to 40 kV, the current was set to 30 mA, the scan rate was set to 4°/min, and the angular range was set to 2θ=10° to 90°.
(Simultaneous Thermogravimetry and Differential Calorimetry)
Simultaneous thermogravimetry and differential calorimetry was performed on the active material powders of Experimental Examples 1 to 3. In the measurement, a simultaneous thermogravimeter-differential calorimeter (Rigaku Thermo Mass) was used. In the measurement, the measurement temperature range was set to room temperature to 750° C., and the heating rate was set to 10° C./min.
(Charge-Discharge Test)
In an environment with a temperature of 20° C., the bipolar test cells of Experimental Examples 1 to 3 were reduced (charged) to 0.5 V at 0.02 mA and were then oxidized (discharged) to 3.0 V at 0.02 mA.
Next, results of research on layered compositions whose interplanar spacings, measured by X-ray diffraction, between (002) planes, (102) planes, (211) planes, (112) planes, and (200) planes fall within the preferred ranges will be described as the Examples.
Lithium 2,6-naphthalenedicarboxylate was synthesized by repeating the procedure of Experimental Example 1. The starting materials used were 2,6-naphthalenedicarboxylic acid and lithium hydroxide monohydrate (LiOH.H2O). Methanol (100 mL) was added to lithium hydroxide monohydrate (0.556 g), and it was stirred. After the lithium hydroxide monohydrate was dissolved, 2,6-naphthalenedicarboxylic acid (1.0 g) was added, and it was stirred for one hour. After stirring, the solvent was removed, and the residue was dried in vacuo at 150° C. for 16 hours to yield a white powder sample.
[Fabrication of Coated Electrode]
A slurried electrode mixture was prepared by mixing 66.7% by mass of the electrode active material (lithium 2,6-naphthalenedicarboxylate) of Example 1 prepared as above, 11.1% by mass of carbon black as a conductor, 11.1% by mass of fibrous carbon (vapor-grown carbon fiber (VGCF)) as a conductor, and 10% by mass of polyvinylidene fluoride as a binder and dispersing the mixture using an appropriate amount of N-methyl-2-pyrrolidone as a dispersant. The slurried electrode mixture was uniformly applied to a 10 μm thick copper foil collector and was dried by heating to fabricate a coated sheet. The coated sheet was then pressed and punched to prepare a circular electrode having an area of 2.05 cm2. The circular electrode was then baked at 300° C. in an argon inert atmosphere for 12 hours.
[Fabrication of Bipolar Test Cell]
A nonaqueous electrolyte solution was prepared by adding lithium hexafluorophosphate to a concentration of 1 mol/L in a nonaqueous solvent containing ethylene carbonate, dimethyl carbonate, and ethyl methyl carbonate in a volume ratio of 30:40:30. A bipolar test cell was fabricated by holding a separator (Tonen Tapyrus Co., Ltd.) impregnated with the above nonaqueous electrolyte solution between the above electrode, serving as a working electrode, and a lithium metal foil (300 μm thick), serving as a counter electrode. The resulting cell is referred to as a bipolar test cell of Example 1.
(Charge-Discharge Test)
In an environment with a temperature of 20° C., the above bipolar test cell was reduced (charged) to 0.5 V at 0.03 mA and was then oxidized (discharged) to 2.0 V at 0.03 mA. The capacity retention (%) after ten cycles was determined as Q(10th)/Q(1st)×100, where Q(1st) is the discharge capacity for the first charge-discharge operation, and Q(10th) is the discharge capacity for the tenth charge-discharge operation.
(X-Ray Diffraction Measurement)
An X-ray diffraction measurement was performed on the nonaqueous secondary battery electrode (dilithium 2,6-naphthalenedicarboxylate electrode) of Example 1. In the measurement, an X-ray diffractometer (Rigaku RINT-2200) that used the Cu—Kα line (wavelength: 1.54051 Å) as radiation was used. In the measurement, a single-crystal graphite monochromator was used as a monochromatic X-ray source, the applied voltage was set to 40 kV, and the current was set to 30 mA. In the measurement, recording was performed at a scan rate of 4°/min over an angular range of 2θ=15° to 30°.
To examine reproducibility, lithium 2,6-naphthalenedicarboxylate was synthesized in different batches (on different dates). Electrodes were fabricated by repeating the procedure of Example 1. The resulting electrodes are referred to as Examples 2 and 3.
An electrode that was the same as the electrode of Example 1 and that underwent one charge-discharge cycle described above is referred to as Example 4. An X-ray diffraction measurement was performed on the electrode of Example 4.
An electrode that was the same as the electrode of Example 1 and that underwent ten charge-discharge cycles described above is referred to as Example 5. An X-ray diffraction measurement was performed on the electrode of Example 5.
An electrode was fabricated as Comparative Example 1 by repeating the procedure of Example 1 except that the electrode was not baked after fabrication.
(Results and Discussions)
An electrode baked at 200° C. did not achieve the above interplanar spacings. In addition, the results of the simultaneous thermogravimetry and differential calorimetry in
1)Q(1st)oxi: Oxidation capacity for the first charge-discharge operation
2)Q(10th)oxi: Oxidation capacity for the tenth charge-discharge operation
3)Capacity retention (%) = (Q10th)/(Q1st) × 100
1)Electrode of Example 1 that underwent one charge- discharge cycle
2)Electrode of Example 1 that underwent ten charge- discharge cycles
The present application claims priority on the basis of the Japanese Patent Application No. 2012-96854 filed on Apr. 20, 2012, the entire contents of which are incorporated herein by reference.