Patent Application
20200014078
This application claims priority to and the benefit of Korean Patent Application No. 10-2018-0077139 filed in the Korean Intellectual Property Office on Jul. 3, 2018, the entire content of which is incorporated herein by reference.
An electrode for a rechargeable lithium battery and a rechargeable lithium battery including the same are disclosed.
A portable information device such as a cell phone, a laptop, smart phone, and the like, or an electric vehicle, has used a rechargeable lithium battery having high energy density and easy portability as a driving power source. In addition, research on use of a rechargeable lithium battery as a power source for a hybrid or electric vehicle, or as a power storage device, by using high energy density characteristics has been actively conducted.
One of the main research tasks of such a rechargeable lithium battery is to improve the safety of the rechargeable battery. For example, if the rechargeable lithium battery is exothermic due to internal short circuit, overcharge and overdischarge, and/or the like, an electrolyte decomposition reaction and thermal runaway phenomenon may occur. As a result, an internal pressure inside the battery may rise rapidly to cause battery explosion. Among these, when the internal short circuit of the rechargeable lithium battery occurs, there is a high risk of explosion because the large amount of electrical energy stored in the battery is conducted between the shorted positive electrode and negative electrode.
Embodiments of the present disclosure are directed toward features capable of improving stability of a rechargeable lithium battery. An embodiment provides an electrode for a rechargeable lithium battery having improved stability.
Another embodiment provides a rechargeable lithium battery including the electrode.
According to an embodiment, an electrode for a rechargeable lithium battery includes a current collector and an active material layer on the current collector, wherein the active material layer includes flake-shaped polyethylene particles, and the flake-shaped polyethylene particles have an average particle size (D50) of about 1 μm to about 8 μm.
The flake-shaped polyethylene particles may have an average particle size (D50) of about 2 μm to about 6 μm.
The flake-shaped polyethylene particles may have a ratio of a major axis length to a minor axis length in a range from about 1 to about 5.
The flake-shaped polyethylene particles may have a thickness of about 0.2 μm to about 4 μm.
The active material layer may include an active material and may further include at least one selected from a conductive material and a binder.
The flake-shaped polyethylene particles may be included in an amount of about 0.1 wt % to about 5 wt % based on a total weight of the active material layer.
The active material layer may further include a coating layer and the flake-shaped polyethylene particles may be included in at least one selected from the active material layer and the coating layer.
The flake-shaped polyethylene particles may be included in the coating layer.
The coating layer may further include inorganic particles and a binder.
A weight ratio of the sum of the flake-shaped polyethylene particles and the inorganic particles to the binder may be about 80:20 to about 99:1.
A weight ratio of the flake-shaped polyethylene particles to the inorganic particles may be about 95:5 to about 10:90.
According to another embodiment, a rechargeable lithium battery including the aforementioned electrode for a rechargeable lithium battery is provided.
As the reaction rate according to the temperature is improved, an early shutdown function may be realized and stability of the rechargeable lithium battery may be secured.
The accompanying drawings, together with the specification, illustrate embodiments of the subject matter of the present disclosure, and, together with the description, serve to explain principles of embodiments of the subject matter of the present disclosure.
Hereinafter, referring to the drawings, embodiments of the present disclosure are described in more detail. In the following description, functions or constructions not described may be any suitable ones generally used in the art.
In order to clearly illustrate and describe the subject matter of the present disclosure, the description and relationships of certain features may be omitted. Throughout the disclosure, the same or similar configuration elements are designated by the same reference numerals. Also, because the size and thickness of each configuration shown in the drawing may be arbitrarily shown for better understanding and ease of description, the present disclosure is not necessarily limited thereto.
An electrode for a rechargeable lithium battery according to an embodiment of the present disclosure includes a current collector and an active material layer on the current collector, wherein the active material layer includes flake-shaped polyethylene particles.
The polyethylene particles according to embodiments of the present disclosure have a flake-shape as shown in
For example, as shown in
In general, polyethylene may be classified, according to the density of the polyethylene, into a high density polyethylene (HDPE) having a density of about 0.94 g/cc to about 0.965 g/cc, a medium density polyethylene (MDPE) having a density of about 0.925 g/cc to about 0.94 g/cc, a low density polyethylene (LDPE) having a density of about 0.91 g/cc to about 0.925 g/cc), or a very low density polyethylene (VLDPE) having a density of about 0.85 g/cc to about 0.91 g/cc.
The flake-shaped polyethylene particles may include for example polyethylene polymers such as HDPE, MDPE, and/or LDPE alone or in a mixture of two or more.
In the case of including the flake-shaped polyethylene particles, a reaction rate according to the temperature is increased under the same (or substantially the same) reaction conditions as compared with the case of including spherical-shaped polyethylene particles, and thus, a stability improvement effect of the rechargeable lithium battery may be further improved by including the flake-shaped polyethylene particles. For example, when the flake-shaped polyethylene particles are included, an area covering the surfaces of the electrode plate is thinner and wider, before melting, than is the case for the spherical-shaped polyethylene particles, before melting. If the polyethylene particles are melted at a temperature exceeding a set or certain temperature and ion channels are closed, an electrode plate area where the flake-shaped polyethylene particles are melted and closed is larger than an electrode plate area where the spherical-shaped polyethylene particles are melted and closed, and thus, the flake-shaped polyethylene particles may have a fast reaction rate as compared to the spherical-shaped polyethylene particles.
For example, during thermal runaway of a battery, the polyethylene particles are melted and the ion channel is closed, thereby limiting movement of ions through the ion channels and resulting in a shutdown function. Thus, additional electrical chemical reactions may be prevented or reduced by the shutdown function.
The flake-shaped polyethylene particles may have an average particle size (D50) of about 1 μm to about 8 μm, and, for example, about 2 μm to about 6 μm.
As used herein, when a definition is not otherwise provided, average particle size (D50) may be measured by any suitable method generally used in the art such as, for example, by utilizing a particle size analyzer, or transmission electron microscope (TEM) or scanning electron microscope (SEM) images (e.g., photographs). In some embodiments, a dynamic light-scattering measurement device may be used to perform a data analysis, and the number of particles may be counted for each particle size range. From this, the D50 value may be easily obtained through a calculation. For example, the D50 value may correspond to a particle size at which half of the mass (or volume) of the particles have a larger particle size and the other half of the mass (or volume) of the particles have a smaller particle size.
On the other hand, the flake-shaped polyethylene particles may have a ratio of a major axis length to a minor axis length ranging from about 1 to about 5, and specifically from about 1.1 to about 4.5 or from about 1.2 to about 3.5.
In addition, the flake-shaped polyethylene particles may have a thickness of about 0.2 μm to about 4 μm, and, for example, about 0.3 μm to about 2.5 μm, or about 0.3 μm to about 1.5 μm.
When the flake-shaped polyethylene particles have a size and/or thickness within the ranges described herein, ion channels may be effectively closed in a small amount (e.g., may be effectively closed rapidly or in a small amount of time).
The active material layer may include an active material and may further include at least one selected from a conductive material and a binder.
The flake-shaped polyethylene particles may be included in an amount of about 0.1 wt % to about 5 wt %, and, for example, about 0.2 wt % to about 3.0 wt % based on a total weight of the active material layer.
When the amount of the flake-shaped polyethylene particles are within the ranges described herein, cycle-life characteristics and output characteristics of a battery may be secured.
The electrode may further include a coating layer, and the flake-shaped polyethylene particles may be included in at least one selected from the active material layer and the coating layer.
For example, the flake-shaped polyethylene particles may be included in the coating layer.
When the flake-shaped polyethylene particles are included in the coating layer, the active material layer may be for example a negative active material layer.
The coating layer may further include inorganic particles and a binder.
A weight ratio of the sum of the flake-shaped polyethylene particles and the inorganic particles to the binder may be about 80:20 to about 99:1, and, for example, about 85:15 to about 97:3.
A weight ratio of the flake-shaped polyethylene particles to the inorganic particles may be about 95:5 to about 10:90, and, for example, about 30:70 to about 70:30.
The inorganic particles may include, for example, Al2O3, SiO2, TiO2, SnO2, CeO2, MgO, NiO, CaO, GaO, ZnO, ZrO2, Y2O3, SrTiO3, BaTiO3, Mg(OH)2, boehmite, or a combination thereof, but the present disclosure is not limited thereto. Organic particles such as an acrylic compound, an imide compound, an amide compound, or a combination thereof may be further included in addition to the inorganic particles, but the present disclosure is not limited thereto.
The inorganic particles may be spherical, flake-shaped, cubic, or amorphous. The inorganic particles may have an average particle diameter (e.g., D50) of about 1 nm to about 2500 nm, for example, about 100 nm to about 2000 nm, or about 200 nm to about 1000 nm, or about 300 nm to about 800 nm.
In some embodiments, the electrode for a rechargeable lithium battery according to the present disclosure may be a positive electrode including a positive electrode current collector and a positive active material layer or a negative electrode including a negative electrode current collector and a negative active material layer.
The positive electrode according to an embodiment of the present disclosure includes a positive electrode current collector and a positive active material layer on the positive electrode current collector.
The positive electrode current collector may be aluminum or nickel, but the present disclosure is not limited thereto.
The positive active material may include lithiated intercalation compounds that reversibly intercalate and deintercalate lithium ions.
For example, the positive active material may include one or more composite oxides of lithium and a metal selected from cobalt, manganese, nickel, and a combination thereof.
Examples of the positive active material may include a compound represented by one of the following chemical formulae.
LiaA1-bXbD2 (0.90≤a≤1.8, 0≤b≤0.5); LiaA1-bXbO2-cDc (0.90≤a≤1.8, 0≤b≤0.5, 0≤c≤0.05); LiaE1-bXbO2-cDc (0.90≤a≤1.8, 0≤b≤0.5, 0≤c 0.05); LiaE2-bXbO4-cDc (0.90≤a≤1.8, 0≤b≤0.5, 0≤c≤0.05); LiaNi1-b-cCobXcDα (0.90≤a≤1.8, 0≤b≤0.5, 0≤c≤0.5, 0<α≤2); LiaNi1-b-cCobXcO2-αTα (0.90≤a≤1.8, 0≤b≤0.5, 0≤c≤0.05, 0<α<2); LiaNi1-b-cCObXcO2-αT2 (0.90≤a≤1.8, 0≤b≤0.5, 0≤c≤0.05, 0<α<2); LiaNi1-b-cMnbXcDα (0.90≤a≤1.8, 0≤b≤0.5, 0≤c≤0.05, 0<α≤2); LiaNi1-b-cMnbXcO2-αTα (0.90≤a≤1.8, 0≤b≤0.5, 0≤c≤0.05, 0<α<2); LiaNi1-b-cMnbXcO2-αT2 (0.90≤a≤1.8, 0≤b≤0.5, 0≤c≤0.05, 0<α<2); LiaNibEcGdO2 (0.90≤a≤1.8, 0≤b≤0.9, 0≤c≤0.5, 0.001≤d≤0.1); LiaNibCocMndGeO2 (0.90≤a≤1.8, 0≤b≤0.9, 0≤c≤0.5, 0≤d≤0.5, 0.001≤e≤0.1); LiaNiGbO2 (0.90≤a ≤1.8, 0.001≤b≤0.1); LiaCoGbO2 (0.90≤a≤1.8, 0.001≤b≤0.1); LiaMn1-bGbO2 (0.90≤a≤1.8, 0.001≤b≤0.1); LiaMn2GbO4 (0.90≤a≤1.8, 0.001≤b≤0.1); LiaMn1-gGgPO4 (0.90≤a≤1.8, 0≤g≤0.5); QO2; QS2; LiQS2; V2O5; LiV2O5; LiZO2; LiNiVO4; Li(3-f)J2(PO4)3 (0≤f≤2); Li(3-f)Fe2(PO4)3 (0≤f≤2); LiaFePO4 (0.90≤a≤1.8)
In the foregoing chemical formulae, A is selected from Ni, Co, Mn, and a combination thereof; X is selected from Al, Ni, Co, Mn, Cr, Fe, Mg, Sr, V, a rare earth element, and a combination thereof; D is selected from O, F, S, P, and a combination thereof; E is selected from Co, Mn, and a combination thereof; T is selected from F, S, P, and a combination thereof; G is selected from Al, Cr, Mn, Fe, Mg, La, Ce, Sr, V, and a combination thereof; Q is selected from Ti, Mo, Mn, and a combination thereof; Z is selected from Cr, V, Fe, Sc, Y, and a combination thereof; and J is selected from V, Cr, Mn, Co, Ni, Cu, and a combination thereof.
The foregoing compounds may have a coating layer on the surface, or may be mixed with another compound having a coating layer. The coating layer may include at least one coating element compound selected from an oxide of the coating element, a hydroxide of the coating element, an oxyhydroxide of the coating element, an oxycarbonate of the coating element, and a hydroxy carbonate of the coating element. The compound for the coating layer may be amorphous or crystalline. The coating element included in the coating layer may include Mg, Al, Co, K, Na, Ca, Si, Ti, V, Sn, Ge, Ga, B, As, Zr, or a mixture thereof. The coating layer may be formed utilizing a method having no adverse influence (or substantially no adverse influence) on properties of a positive active material by using these elements in the compound. For example, the method may include any suitable coating method (e.g., spray coating, dipping, etc.), including those generally used in the art.
The positive active material may be included in an amount of about 90 wt % to about 98 wt % based on a total weight of the positive active material layer.
The positive active material layer may further include, optionally, a positive electrode conductive material and a positive electrode binder.
Each amount of the positive electrode conductive material and the positive electrode binder may be about 1 wt % to about 5 wt % based on a total weight of the positive active material layer.
The positive electrode conductive material is included to provide a positive electrode with conductivity (e.g., electrical conductivity). Any suitable electronically conductive material may be used as a conductive material unless it causes a chemical change in a battery (e.g., an undesirable change to any of the components of the rechargeable lithium battery). Examples thereof may include a carbon-based material such as natural graphite, artificial graphite, carbon black, acetylene black, ketjen black, carbon fiber, and the like; a metal-based material of a metal powder or a metal fiber including copper, nickel, aluminum silver, and the like; a conductive polymer such as a polyphenylene derivative; or a mixture thereof.
The positive electrode binder improves binding properties of positive active material particles with one another and with a current collector. Examples thereof may include polyvinyl alcohol, carboxylmethyl cellulose, hydroxypropyl cellulose, diacetyl cellulose, polyvinylchloride, carboxylated polyvinylchloride, polyvinylfluoride, an ethylene oxide-containing polymer, polyvinylpyrrolidone, polyurethane, polytetrafluoroethylene, polyvinylidene fluoride, polyethylene, polypropylene, a styrene-butadiene rubber, an acrylated styrene-butadiene rubber, an epoxy resin, nylon, and the like, but the present disclosure is not limited thereto.
In addition, the negative electrode according to another embodiment of the present disclosure may include a negative electrode current collector and a negative active material layer on the negative electrode current collector.
The negative electrode current collector may include one selected from a copper foil, a nickel foil, a stainless steel foil, a titanium foil, a nickel foam, a copper foam, a polymer substrate coated with a conductive metal, and a combination thereof.
The negative active material may include a material that reversibly intercalates/deintercalates lithium ions, a lithium metal, a lithium metal alloy, a material capable of doping/dedoping lithium, and/or transition metal oxide.
The material that reversibly intercalates/deintercalates lithium ions may include any suitable carbon material that is generally used in the art as a carbon-based negative active material in a rechargeable lithium battery. Examples of the carbon-based negative active material may be crystalline carbon, amorphous carbon, or a mixture thereof. The crystalline carbon may be non-shaped, sheet-shaped, flake-shaped, spherical-shaped, or fiber-shaped natural graphite or artificial graphite. The amorphous carbon may be a soft carbon, a hard carbon, a mesophase pitch carbonization product, fired coke, and/or the like.
The lithium metal alloy includes an alloy of lithium and a metal selected from Na, K, Rb, Cs, Fr, Be, Mg, Ca, Sr, Si, Sb, Pb, In, Zn, Ba, Ra, Ge, Al, and Sn.
The material capable of doping/dedoping lithium may be a silicon-based material, for example, Si, SiOx (0<x<2), a Si-Q alloy (wherein Q is an element selected from an alkali metal, an alkaline-earth metal, a Group 13 element, a Group 14 element, a Group 15 element, a Group 16 element, a transition metal, a rare earth element, and a combination thereof, and not Si), a Si-carbon composite, Sn, SnO2, a Sn—R alloy (wherein R is an element selected from an alkali metal, an alkaline-earth metal, a
Group 13 element, a Group 14 element, a Group 15 element, a Group 16 element, a transition metal, a rare earth element, and a combination thereof, and not Sn), a Sn-carbon composite, and/or the like. At least one of the foregoing materials may be mixed with SiO2. The elements Q and R may be selected from Mg, Ca, Sr, Ba, Ra, Sc, Y, Ti, Zr, Hf, Rf, V, Nb, Ta, Db, Cr, Mo, W, Sg, Tc, Re, Bh, Fe, Pb, Ru, Os, Hs, Rh, Ir, Pd, Pt, Cu, Ag, Au, Zn, Cd, B, Al, Ga, Sn, In, Ge, P, As, Sb, Bi, S, Se, Te, Po, and a combination thereof.
The transition metal oxide may include lithium titanium oxide.
In the negative active material layer, the negative active material may be included in an amount of about 95 wt % to about 99 wt % based on the total weight of the negative active material layer.
The negative active material layer may further include, optionally, a negative electrode conductive material and a negative electrode binder.
Each amount of the negative electrode conductive material and negative electrode binder may be about 1 wt % to about 5 wt % based on a total weight of the negative active material layer.
The negative electrode conductive material may provide negative electrode with electrical conductivity. The negative electrode conductive material may be the same as described herein with respect to the aforementioned positive electrode conductive material.
The negative electrode binder acts to adhere negative active material particles to each other and to adhere the negative active material to the current collector. The negative electrode binder may be a non-aqueous binder, an aqueous binder, an amphiphilic binder (aqueous/non-aqueous binder), or a combination thereof.
The non-aqueous binder may be polyvinylchloride, carboxylated polyvinylchloride, polyvinylfluoride, an ethylene oxide-containing polymer, polyvinylpyrrolidone, polyurethane, polytetrafluoroethylene, polyvinylidene fluoride, polyethylene, polypropylene, polyamideimide, polyimide, or a combination thereof.
The aqueous binder may be a styrene-butadiene rubber, an acrylated styrene-butadiene rubber, polyvinyl alcohol, sodium polyacrylate, a copolymer of propylene and a C2 to C8 olefin, a copolymer of (meth)acrylic acid and (meth)acrylic acid alkyl ester, or a combination thereof.
The amphiphilic binder may be an acrylated styrene-based rubber, and/or the like.
When the negative electrode binder is an aqueous binder, a cellulose-based compound may be further used to provide viscosity as a thickener. The cellulose-based compound may include one or more of carboxylmethyl cellulose, hydroxypropylmethyl cellulose, methyl cellulose, or alkali metal salts thereof. The alkali metals may be Na, K, and/or Li. The thickener may be included in an amount of about 0.1 to about 3 parts by weight based on 100 parts by weight of the negative active material.
Hereinafter, a rechargeable lithium battery according to another embodiment of the present disclosure is described with reference to
Referring to
In some embodiments, a lithium salt is included in the electrolyte and is dissolved in a solvent to act as a source of lithium ions in a battery in order to enable the operation of the basic rechargeable lithium battery and to promote transportation of lithium ion between the positive electrode and the negative electrode
The lithium salt may include LiPF6, LiSbF6, LiAsF6, LiN(SO2C2F5)2, Li(CF3SO2)2N, LiN(SO3C2F5)2, LiC4F9SO3, LiClO4, LiAlO2, LiAlCl4, LiN(CxF2x+1SO2)(CyF2y+2SO2) (wherein, x and y are natural numbers, for example an integer ranging from 1 to 20), LiCl, Lil, LiB(C2O4)2 (lithium bis(oxalato) borate, LiBOB), or a combination thereof.
A concentration of the lithium salt may be about 0.1 M to about 2.0 M. When the lithium salt is included at the above concentration range, an electrolyte may have excellent performance and lithium ion mobility due to improved or optimal electrolyte conductivity and viscosity.
In some embodiments, the electrolyte may further include an organic solvent to dissolve the lithium salt. The organic solvent may be a non-aqueous organic solvent having high ion conductivity, a high dielectric constant, and a low viscosity. The non-aqueous organic solvent serves as a medium for transporting ions taking part in the electrochemical reaction of a battery.
Such a non-aqueous organic solvent may be, for example, a carbonate-based, ester-based, ether-based, ketone-based, alcohol-based, and/or aprotic solvent.
The carbonate-based solvent may include dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropyl carbonate (DPC), methylpropyl carbonate (MPC), ethylpropyl carbonate (EPC), methylethyl carbonate (MEC), ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), and/or the like. The ester-based solvent may include methyl acetate, ethyl acetate, n-propyl acetate, dimethylacetate, methyl propionate, ethyl propionate, propyl propionate, y-butyrolactone, decanolide, valerolactone, mevalonolactone, caprolactone, and/or the like
The ether-based solvent may include dibutyl ether, tetraglyme, diglyme, dimethoxyethane, 2-methyltetrahydrofuran, tetrahydrofuran, and/or the like, and the ketone-based solvent may be cyclohexanone, and/or the like.
The alcohol based solvent may include ethanol, isopropyl alcohol, and/or the like, and the aprotic solvent may include nitriles such as T-CN (wherein T is a C2 to C20 linear, branched, or cyclic hydrocarbon group, a double bond, an aromatic ring, or an ether bond), and/or the like, amides such as dimethyl formamide, and/or the like, dioxolanes such as 1,3-dioxolane, and/or the like, sulfolanes, and/or the like.
The non-aqueous organic solvent may be used alone or in a mixture. When the organic solvent is used in a mixture, the mixture ratio may be controlled in accordance with a desirable battery performance.
The carbonate-based solvent is prepared by mixing a cyclic carbonate and a chain-type carbonate. In this case, when the cyclic carbonate and the chain-type carbonate are mixed together to a volume ratio of about 1:1 to about 1:9, performance of an electrolyte may be enhanced.
The non-aqueous organic solvent may further include an aromatic hydrocarbon-based organic solvent in addition to the carbonate-based solvent. Herein, the carbonate-based solvent and the aromatic hydrocarbon-based organic solvent may be mixed to a volume ratio of about 1:1 to about 30:1.
The aromatic hydrocarbon-based organic solvent may be an aromatic hydrocarbon-based compound of Chemical Formula 1.
In Chemical Formula 1, R3 to R8 are the same or different and are selected from hydrogen, a halogen, a C1 to C10 alkyl group, a haloalkyl group, and a combination thereof.
Examples of the aromatic hydrocarbon-based organic solvent may be selected from benzene, fluorobenzene, 1,2-difluorobenzene, 1,3-difluorobenzene, 1,4-difluorobenzene, 1,2,3-trifluorobenzene, 1,2,4-trifluorobenzene, chlorobenzene, 1,2-dichlorobenzene, 1,3-dichlorobenzene, 1,4-dichlorobenzene, 1,2,3-trichlorobenzene, 1,2,4-trichlorobenzene, iodobenzene, 1,2-diiodobenzene, 1,3-diiodobenzene, 1,4-diiodobenzene, 1,2,3-triiodobenzene, 1,2,4-triiodobenzene, toluene, fluorotoluene, 2,3-difluorotoluene, 2,4-difluorotoluene, 2,5-difluorotoluene, 2,3,4-trifluorotoluene, 2,3,5-trifluorotoluene, chlorotoluene, 2,3-dichlorotoluene, 2,4-dichlorotoluene, 2,5-dichlorotoluene, 2,3,4-trichlorotoluene, 2,3,5-trichlorotoluene, iodotoluene, 2,3-diiodotoluene, 2,4-diiodotoluene, 2,5-diiodotoluene, 2,3,4-triiodotoluene, 2,3,5-triiodotoluene, xylene, and a combination thereof.
As described herein above, the separator 113 may be between the positive electrode 114 and the negative electrode 112. The separator 113 may include polyethylene, polypropylene, polyvinylidene fluoride, or a multi-layer thereof and may be a mixed multilayer such as a polyethylene/polypropylene double-layered separator, a polyethylene/polypropylene/polyethylene triple-layered separator, a polypropylene/polyethylene/polypropylene triple-layered separator, or the like.
Hereinafter, the above aspects of the present disclosure are illustrated in more detail with reference to examples. However, these examples are exemplary, and the present disclosure is not limited thereto.
95 wt % of a positive active material in which LiCoO2/LiFePO4“LCO/LFP” were mixed to a weight ratio of 9:1, 3 wt % of a polyvinylidene fluoride binder, and 2 wt % of a ketjen black conductive material were mixed in a N-methyl pyrrolidone solvent to provide a positive active material slurry. The positive active material slurry was coated on both surfaces of an aluminum current collector, dried and compressed to provide a positive electrode formed with a positive active material layer.
98 wt % of graphite, 0.8 wt % of carboxylmethyl cellulose, and 1.2 wt % of styrene-butadiene rubber were mixed in pure water to provide a negative active material slurry. The negative active material slurry was coated on both surfaces of a copper current collector, dried, and compressed to provide a negative electrode formed with a negative active material layer.
48 wt % of flake-shaped polyethylene (PE) particles having an average particle size of 2 μm (major axis length/minor axis length ratio=about 2, thickness=about 0.6 μm, D50=2 μm), 47 wt % of alumina (average particle diameter (D50)=0.7 μm), and 5 wt % of an acrylated styrene-based rubber binder were mixed in an alcohol-based solvent to provide a PE/alumina slurry.
The PE/alumina slurry was coated on both surfaces of the negative electrode, dried, and compressed to provide a negative electrode formed with a coating layer including flake-shaped PE particles.
The positive electrode, a separator including a PE/polypropylene (PP) multi-layer substrate, the negative electrode formed with the coating layer including the flake-shaped PE particles were sequentially stacked to provide an electrode assembly having a structure shown in
A rechargeable battery cell was manufactured in accordance with substantially the same procedure as in Example 1, except that the negative electrode was prepared using flake-shaped PE particles having an average particle size of 4 μm (major axis length/minor axis length ratio=about 2.4, thickness=about 0.6 μm, D50=4 μm).
A rechargeable battery cell was manufactured in accordance with the same procedure as in Example 1, except that the negative electrode was prepared using flake-shaped PE particles having an average particle size of 6 μm (major axis length/minor axis length ratio=about 2.4, thickness=about 0.6 μm, D50=6 μm).
The results of particle distributions of flake-shaped polyethylene particles included in the electrode according to Examples 1 to 3 are shown in
A rechargeable battery cell was manufactured in accordance with substantially the same procedure as in Example 1, except that the negative electrode was prepared using a dispersion in which spherical-shaped PE particles having an average particle size of 4 μm were dispersed in an alcohol-based solvent instead of the flake-shaped PE particles having an average particle size of 2 μm.
A negative electrode formed with a coating layer including flake-shaped PE particles according to Example 1, a separator including a PE/PP multi-layer substrate, and a negative electrode formed with a coating layer including flake-shaped PE particles according to Example 1 were sequentially stacked, and an electrolyte including 1M LiBF4 dissolved in propylene carbonate was injected thereto to provide a coin symmetric cell shown in
The obtained coin symmetric cell was introduced into a temperature changeable chamber after mounting a temperature sensor and a resistance measurer (a resistance meter) and evaluated. Changes in temperature and resistance of the coin symmetric cell were measured while increasing the temperature at a rate of 10° C./minute, and the results of evaluating the resistance increase rate of an electrode plate according to a temperature are shown in
Referring to
From this, it can be seen that in a case of a battery cell including an electrode according to an embodiment, ion channels are effectively suppressed (or the availability and/or functionality of the ion channels may be reduced) during thermal runaway by the thermal/physical impact, so the shut-down function may be expressed or initiated at an early stage.
Rechargeable lithium battery cells obtained from Examples 1 to 3 were charged at a rate of 0.5C/0.5C and at 4.4V and then discharged until 3.0V, and the cell capacity decrease rate after 150 cycles was measured. The results thereof are shown in
Referring to
Resultantly, the rechargeable lithium battery cell according to an embodiment may have effective shut-down functions while maintaining excellent battery characteristics.
It will be understood that, although the terms “first,” “second,” “third,” etc., may be used herein to describe various elements, components, regions, layers and/or sections, these elements, components, regions, layers and/or sections should not be limited by these terms. These terms are used to distinguish one element, component, region, layer or section from another element, component, region, layer or section. Thus, a first element, component, region, layer or section described below could be termed a second element, component, region, layer or section, without departing from the spirit and scope of the present disclosure.
Spatially relative terms, such as “beneath,” “below,” “lower,” “under,” “above,” “upper,” and the like, may be used herein for ease of explanation to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. It will be understood that the spatially relative terms are intended to encompass different orientations of the device in use or in operation, in addition to the orientation depicted in the figures. For example, if the device in the figures is turned over, elements described as “below” or “beneath” or “under” other elements or features would then be oriented “above” the other elements or features. Thus, the example terms “below” and “under” can encompass both an orientation of above and below. The device may be otherwise oriented (e.g., rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein should be interpreted accordingly.
It will be understood that when an element or layer is referred to as being “on,” “connected to,” or “coupled to” another element or layer, it can be directly on, connected to, or coupled to the other element or layer, or one or more intervening elements or layers may be present. In addition, it will also be understood that when an element or layer is referred to as being “between” two elements or layers, it can be the only element or layer between the two elements or layers, or one or more intervening elements or layers may also be present.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the present disclosure. As used herein, the singular forms “a” and “an” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises,” “comprising,” “includes,” and “including,” when used in this specification, specify the presence of the stated features, integers, acts, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, acts, operations, elements, components, and/or groups thereof. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. Expressions such as “at least one of,” when preceding a list of elements, modify the entire list of elements and do not modify the individual elements of the list.
As used herein, the terms “substantially,” “about,” and similar terms are used as terms of approximation and not as terms of degree, and are intended to account for the inherent deviations in measured or calculated values that would be recognized by those of ordinary skill in the art. Further, the use of “may” when describing embodiments of the present disclosure refers to “one or more embodiments of the present disclosure.” As used herein, the terms “use,” “using,” and “used” may be considered synonymous with the terms “utilize,” “utilizing,” and “utilized,” respectively. Also, the term “exemplary” is intended to refer to an example or illustration.
Also, any numerical range recited herein is intended to include all sub-ranges of the same numerical precision subsumed within the recited range. For example, a range of “1.0 to 10.0” is intended to include all subranges between (and including) the recited minimum value of 1.0 and the recited maximum value of 10.0, that is, having a minimum value equal to or greater than 1.0 and a maximum value equal to or less than 10.0, such as, for example, 2.4 to 7.6. Any maximum numerical limitation recited herein is intended to include all lower numerical limitations subsumed therein, and any minimum numerical limitation recited in this specification is intended to include all higher numerical limitations subsumed therein. Accordingly, Applicant reserves the right to amend this specification, including the claims, to expressly recite any sub-range subsumed within the ranges expressly recited herein.
Hereinbefore, certain embodiments of the present disclosure have been described and illustrated. It should be apparent to a person having ordinary skill in the art, however, that the subject matter of the present disclosure is not limited to the embodiments as described herein, and may be variously modified and transformed without departing from the spirit and scope of the present disclosure. Accordingly, the modified or transformed embodiments as such may not be understood separately from the technical ideas and aspects of the present disclosure, and the modified embodiments are within the scope of the claims of the present disclosure, and equivalents thereof.
100: rechargeable lithium battery
112: negative electrode
113: separator
114: positive electrode
120: battery case
140: sealing member
200: coin symmetric cell
210: spring
212: negative electrode
214: positive electrode
216: first spacer
218: separator
220: bottom case
222: second spacer
224: top case
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2018-0077139 | Jul 2018 | KR | national |