Electrode having multi-modal distribution of zinc-based particles

Abstract
An electrode containing zinc-based particles suspended in a fluid medium is disclosed. The zinc-based particles have a multi-modal distribution, such as a bi-modal distribution, of particle sizes, particle morphologies and/or particle compositions. The electrode can be used as the anode in an alkaline battery, such as a primary alkaline battery.
Description




BACKGROUND OF THE INVENTION




The present invention relates to improvements in electrochemical cells, particularly cells having negative electrodes comprising zinc-based particles, such as in alkaline batteries.




An electrochemical cell (i.e., a galvanic cell or battery) has the following basic components: a negative electrode (sometimes called an anode), a positive electrode (sometimes called a cathode), and an ion-conductive solution (sometimes called an electrolyte) providing a path for the transfer of charged ions between the two electrodes when they are connected through an external load.




Some alkaline cells have anodes with zinc as an active element, and cathodes with manganese dioxide (MnO


2


) as an active element. Anodes do not have to be solid; in fact, conventional alkaline cells have a gelled zinc anode mixture. The mixture contains individual zinc-based particles suspended in a thickened liquid or gel containing a gelling agent, an alkaline electrolyte such as potassium hydroxide (KOH), and minor amounts of other additives, such as indium or bismuth (gassing inhibitors for reducing the undesirable tendency for hydrogen gas to build up inside the cell). The zinc-based particles are characterized by a specific size range, commonly indicated by the standard mesh size through which the particles pass. Typically, average anode particle sizes fall in the range of about −50/+200 mesh, indicating particles that pass through a 50 mesh screen and do not pass through a 200 mesh screen (the larger the screen number, the smaller the aperture size of the screen).




Common gelling agents used in anodes include carboxymethycellulose, polyacrylic acid (e.g., Carbopol 940™ from B. F. Goodrich in Brecksville, Ohio, or POLYGEL-4P™ from 3V in Bergamo, Italy), sodium polyacrylate (e.g., CL-15™ from Allied Colloids in Yorkshire, England), and salts. Non-limiting examples of gassing inhibitors include inorganic additives such as indium, bismuth, tin and lead and organic inhibitors such as phosphate esters and anionic and non-ionic surfactants. See U.S. Pat. Nos. 5,283,139, 5,168,018, 4,939,048, 4,500,614, 3,963,520, 4,963,447, 4,455,358, and 4,195,120 for examples of various anode mixtures.




The gel anode is typically separated from the cathode by a separator, such as a thin layer of non-woven material or paper, that prohibits electronic conduction between the anode and the cathode but allows ions to pass between them.




Alkaline Zn/MnO


2


cells have been commercially available for over 30 years, during which time their performance characteristics have been incrementally optimized by the industry in an attempt to provide the “longest lasting” battery (i.e., one with the greatest overall capacity, measured in ampere-hours) within the volume constraints imposed by the international size standards (e.g., AAAA, AAA, AA, C, D cylindrical and 9 volt prismatic sizes). The volume within such standard cells, into which the active materials are packed, is more or less fixed. The amount of energy available from any given cell size (which is a function of the total amount of the active elements in the cell) has a theoretical upper limit which is defined by the internal cell volume and the practical densities of the active components that are employed.




In addition to trying to produce the “longest-lasting” battery, battery manufacturers are also trying to increase the maximum instantaneous rate of electrical current that can be generated from a battery under a given load without the battery voltage dropping below a minimum value. The motivation for increasing this “maximum discharge rate” capability includes the ongoing development of electronic products, such as cellular phones, which require high currents from small packages. Some of these new devices automatically test the voltage levels of their batteries, and therefore may cause the premature disposal of batteries which have remaining overall capacity, if the sensed voltage dips excessively during a period of high current draw.




When a high current is being drawn from a battery, the voltage of the battery may drop due to zinc-based particle surface “passivation” or anode polarization which can indicate a localized lack of sufficient hydroxide ions to sustain the chemical reaction of the cell. It is believed that a certain amount of porosity is necessary for the free supply of OH





ions coming from the electrolyte and the free disposal of Zn(OH)


4




=


, Zn(OH)


2


or ZnO reaction products back into the electrolyte. If the zinc-based particles are too densely crowded, or if their surfaces are inaccessible due to accumulation of reaction products, the reaction cannot keep up with the rate of current draw. Batteries with densely packed zinc-based particles in their anodes may perform acceptably with very stable voltage levels while supplying low continuous currents, but drop to very low, unacceptable voltages when a high current is drawn due to zinc crowding (sometimes referred to as “choking” or being “electrolyte starved”).




In addition, too little electrolyte can starve the overall chemical reaction of the cell or cause the battery to “dry out”, as water from the electrolyte is continuously consumed during discharge. The net reaction inside the cell is:






Zn+2MnO


2


+H


2


O→ZnO+2MnOOH.






Thus, competing with the desire to pack as much zinc-based material as possible into the available anode volume to increase overall capacity for “long life” is the need to provide a sufficient amount of electrolyte to avoid “choking” during periods of high discharge rate.




SUMMARY OF THE INVENTION




The invention is based upon the discovery that including very small zinc-based particles (i.e., fines or dust) among the zinc-based particles of the anode of an alkaline electrochemical cell can provide good cell performance characteristics, especially those characteristics related to high discharge rate performance. The combination of smaller zinc-based particles and larger zinc-based particles can result in a multi-modal, such as a bi-modal distribution, of zinc-based particles in terms of particle size, particle morphology and/or particle composition.




As used herein, “fines” are particles small enough to pass through a standard 200 mesh screen in a normal sieving operation (i.e., with the sieve shaken by hand). “Dust” consists of particles small enough to pass through a standard 325 mesh screen in a normal sieving operation.




A zinc-based particle can be formed of, for example, zinc or a zinc alloy. Materials that can be alloyed with zinc to provide zinc-based particles include gassing inhibitors, such as indium and/or bismuth. Generally, a zinc-based particle formed of a zinc alloy will be mostly zinc. A zinc-based particle can be spun or air blown.




The zinc-based particles can include a plating material, such as indium and/or bismuth.




As used herein, a “zinc-based particle” refers to a singular or primary particle of zinc-based material rather than an agglomeration of more than one particle of zinc-based material. An anode can contain primary particles of zinc-based material and/or agglomerates of primary particles of zinc-based material.




According to one aspect of the invention, a negative electrode for an electrochemical cell contains zinc-based particles suspended in a fluid medium, with at least about 1 percent, by weight, of the zinc-based particles being of −200 mesh size or smaller. Even higher weight percentages (e.g., 6 percent, 10 percent, 25 percent, 50 percent, 80 percent, 90 percent or 100 percent) of zinc-based fines can be preferable.




In some embodiments, the zinc-based particles also include at least about 25 percent, by weight, (e.g., at least about 50 percent, 75 percent, 90 percent or 99 percent) of particles between about 20 and 200 mesh size or larger.




In certain embodiments, it is preferable that a substantial percentage (e.g., 10, 45, 80, 90 or 100 weight percent) of the zinc-based particles are dust (of −325 mesh size or smaller, as defined above). However, in other embodiments, less than 10 weight percent of the zinc-based particles may be of −325 mesh size or smaller (e.g., about 1 weight percent to about 10 weight percent, such as about 6 weight percent).




The negative electrode may include a surfactant. The fluid medium preferably includes both an electrolyte and a thickening agent.




The zinc-based particles can be spherical or nonspherical in shape. Nonspherical particles can be acicular in shape (having a length along a major axis at least two times a length along a minor axis) or of flake form (having a thickness of no more than about 20 percent of their maximum linear dimension).




According to another aspect, a negative electrode mixture for an electrochemical cell contains zinc-based particles suspended in a fluid medium with the zinc-based particles comprising less than about 68 percent (e.g., less than about 64 percent, 60 percent, 55 percent or even 45 percent) of the electrode mixture, by weight. The zinc-based particles include a sufficient proportion of particles of about −200 mesh size or smaller to provide an electrode resistivity of less than about 0.2 ohm-centimeters. Preferably, at least about 1 percent, by weight, of the zinc-based particles are of −200 mesh size (more preferably, of −325 mesh size) or smaller.




According to another aspect, the invention features a primary electrochemical cell having a cathode, an anode with zinc-based particles suspended in a fluid medium, at least 1 percent, by weight, of the zinc-based particles being of −200 mesh size or smaller, and a separator between the cathode and the anode.




The anode of the electrochemical cell may include other features, such as zinc-based particle sizes, mentioned above.




According to a further aspect, a negative electrode slurry for an electrochemical cell contains zinc-based particles suspended in a fluid medium including an electrolyte. The slurry has a resistivity of less than about 0.2 ohm-centimeters and the zinc-based particles comprise less than about 68 percent, by weight, of the slurry. The slurry can contain less than about 64 percent, 60 percent, 55 percent or even 45 percent, by weight, zinc-based particles.




According to another aspect of the invention, a method of generating an electric current includes accumulating ions on the surface of zinc-based particles suspended in a fluid medium containing an electrolyte, at least about 1 percent, by weight, of the zinc-based particles being of −200 mesh size or smaller.




In one aspect, the invention features a composition that includes a fluid medium and zinc-based particles contained in the fluid medium. The zinc-based particles have an average particle size of less than about 175 microns.




In another aspect, the invention features a battery that includes an anode, a cathode, and a separator disposed between the anode and the cathode. The anode includes a fluid medium and zinc-based particles contained in the fluid medium. The zinc-based particles have an average particle size of less than about 175 microns.




In a further aspect, the invention features a battery that includes an anode, a cathode, and a separator disposed between the anode and the cathode. The anode includes an active material in the form of zinc-based particles. All the zinc-based particles are of −200 mesh size or smaller.




In another aspect, the invention features an electrode including zinc-based particles in a fluid medium. The zinc-based particles have a multi-modal, such as a bi-modal, distribution of particle sizes.




In another aspect, the invention features an electrode including zinc-based particles in a fluid medium. The zinc-based particles have a multi-modal, such as a bi-modal, distribution of particle morphologies.




In another aspect, the invention features an electrode including zinc-based particles in a fluid medium. The zinc-based particles have a multi-modal, such as a bi-modal, distribution of particle compositions.




In another aspect, the invention features a battery including a cathode, an anode and a separator disposed between the cathode and the anode. The anode contains zinc-based particles in a fluid medium. The zinc-based particles can have a multi-modal, such as a bi-modal, distribution of particles sizes, particle morphologies and/or particle compositions. The battery can be a standard size battery, such as a AA battery, a AAA battery, a AAAA battery, a C battery, a D cylindrical battery or a 9 volt prismatic size battery.




Cells constructed according to the invention have displayed high tolerance for mechanical shock. They have also demonstrated high running voltages at high rate drains, low internal impedances under load, and good overall performance under various pulsed rate discharge loads.




In addition, the high proportion of zinc-based fines or dust can enable the total amount of zinc to be reduced (i.e., the cell can have a lower zinc “loading”) while maintaining overall capacity on practical drains and without the typical loss in mechanical stability normally associated with a reduction in zinc loading. This is believed to be due, in part, to a high efficiency of zinc usage and good particle-to-particle connectivity.




By reducing the total zinc loading needed to achieve a given performance level, water and alkaline electrolyte can be added which may reduce the risk of anode choking.




In some embodiments, it is desirable for the anode to have a relatively low resistivity. In these embodiments, the anode can have a resistivity of about 0.2 ohm-centimeters or less.




Other advantages and features will become apparent from the following description and claims.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is a cross sectional view through an alkaline cell.





FIG. 2

illustrates zinc-based particle size distributions.





FIG. 3

shows acicular particles.





FIG. 4

shows flake particles.





FIG. 5

shows the effect of anode solids loading on anode resistivity using different zinc-based particle size distributions.





FIGS. 6A and 6B

show battery voltage traces taken during pulse impedance tests of the cells of Example 1.











DESCRIPTION OF THE PREFERRED EMBODIMENTS




Referring to

FIG. 1

, cylindrical cell


10


has a casing


12


closed at its open end by seal member


14


being crimped in place. The cathode


16


is an annular structure with an outer surface in electrical contact with the inner surface of the casing, which serves as the positive external terminal of the cell. Cathode


16


is formed by stacking multiple cathode pellets


16




a,


as shown. Each cathode pellet is made from a mixture of MnO


2


, a conductive agent, and electrolyte. Alternatively, the cathode may be formed directly in the casing by pressure compaction, without stacking individual pellets.




A separator


18


lines the inner surfaces of annular cathode


16


and electronically separates the cathode from the anode


20


. Separator


18


can be any of a number of well known separator materials, such as cellulose or rayon.




Anode


20


is of gel form, having a desired amount of zinc-based material, in particulate form, suspended in a mixture of alkaline electrolyte and a gelling agent. Gassing inhibitors, such as those described above, are preferably added to the anode gel or as a coating on the zinc-based particles. Generally, the zinc-based particles and alkaline electrolyte together make up about 96%, and more preferably about 98%, by weight, of the anode.




Anode collector


22


passes through seal member


14


and extends into anode


20


. The upper end of anode collector


22


electrically contacts a negative end cap


24


, which serves as the negative external terminal of the cell. Upon assembly, additional liquid alkaline electrolyte is added to the cell and becomes distributed throughout the anode, cathode, and separator.




Anode


20


contains zinc-based particles having a multi-modal distribution, such as a bi-modal distribution, of zinc-based particles in terms of particle size, particle morphology and/or particle composition. A multi-modal distribution refers to a distribution having at least two distinct peaks. Thus, a plot of relative percent of particles as a function of particle size for zinc-based particles having a multi-modal distribution of particle sizes would have at least two distinct peaks. For example,

FIG. 2

, which is described below, shows several bi-modal particle size distributions. Similarly, a plot of relative percent of particles as a function of particle morphology for zinc-based particles having a multi-modal distribution of particle morphologies would have at least two distinct peaks, and a plot of relative percent of particles as a function of particle composition for zinc-based particles having a multi-modal distribution of particle compositions would have at least two distinct peaks.




For zinc-based particles having a multi-modal distribution of particle sizes, each mode has a different average particle size. For example, in a bi-modal distribution of particle sizes, one mode can have a relatively small average particle size (fines or dust), while the other mode can have a larger average particle size.




For zinc-based particles having a multi-modal distribution of particle sizes, one mode can have an average particle size of from about 15 microns to about 120 microns. For example, this mode can have an average particle size of from about 30 microns to about 40 microns, or this mode can have an average particle size of from about 95 microns to about 105 microns.




For zinc-based particles in a mode having an average particle size of from about 30 microns to about 40 microns, at least about 90 volume percent of the zinc-based particles can have a particle size of from about 5 microns to about 100 microns, and at least about 75 volume percent of the zinc-based particles can have a particle size of from about 15 microns to about 75 microns. The zinc-based particles in this mode can have a Scott density of about 53 grams per cubic inch as measured by ASTM B-417.




For zinc-based particles in a mode having an average particle size of from about 95 microns to about 105 microns, at least about 90 volume percent of the zinc-based particles can have a particle size of from about 15 microns to about 200 microns, and at least about 75 volume percent of the zinc-based particles can have a particle size of from about 25 microns to about 140 microns. The zinc-based particles in this mode can have a Scott density of about 53 grams per cubic inch as measured by ASTM B-417.




Another mode of the zinc-based particles can have an average particle size of from about 200 microns to about 330 microns. For example, the average particle size of this mode can be from about 290 microns to about 300 microns. For this mode, at least about 90 volume percent of the particles can have a particle size of from about 50 microns to about 850 microns, and at least about 75 volume percent of the particles can have a particle size of from about 100 microns to about 550 microns. For this mode, the zinc-based particles can have a Scott density of from about 50 grams per cubic inch to about 56 grams per cubic inch as measured by ASTM B-417.




For zinc-based particles having a multi-modal distribution of particle morphologies, more than one mode can be formed of nonspherical particles, with each mode being more or less nonspherical than other modes. Alternatively, one mode can be formed of spherical zinc-based particles, while another mode can be formed of nonspherical particles (e.g., flakes or acicular particles).




For zinc-based particles having a multi-modal distribution of particle compositions, one mode can be formed of zinc-based particles of one composition, while another mode can be formed of zinc-based particles of another composition. For example, one mode can include zinc-based particles formed of zinc and a certain amount of one or more gassing inhibitors (e.g., bismuth and/or indium), whereas another mode can include zinc-based particles formed of zinc and a different amount of one or more gassing inhibitors (e.g., bismuth and/or indium).




For zinc-based particles having a multi-modal distribution of particle compositions, one mode can include zinc-based particles formed of zinc, about 500 parts per million (ppm) indium relative to zinc and about 500 ppm bismuth relative zinc. Alternatively, this mode can include zinc-based particles formed of zinc, about 350 ppm indium relative to zinc and about 150 ppm bismuth relative zinc.




For zinc-based particles having a multi-modal distribution of particle compositions, another mode can include zinc-based particles formed of zinc, about 150 ppm indium relative to zinc and about 230 ppm bismuth relative to zinc.




The zinc-based particles in anode


20


can include as little as 1% by weight to 10% by weight of fines. Alternatively, the zinc-based particles in anode


20


can include at least 10% by weight, preferably at least 50% by weight, and more preferably at least 80% by weight. In some embodiments, 100% by weight of the zinc-based particles in anode


20


can be fines. High performance has also been noticed, as described more fully below, when there is a significant proportion of zinc-based particles in the form of dust in the anode.




The average size of the zinc-based particles can be relatively small. Preferably, the zinc-based particles have an average size of less than about 175 microns, more preferably less than about 150 microns, and most preferably less than about 120 microns. The manner in which the average particle size of the zinc-based particles is determined is discussed below.




The desired distribution of particle sizes can be produced by several processes. For instance, standard mesh sieves can be employed to sort zinc-based particles produced by centrifugal atomization, gas atomization, or any other known method. Once sorted, by sieving or air classification, for instance, various size ranges of particles can be mixed in proper proportions to produce the desired size distribution. Alternatively, the average size of the particles, as produced, can be controlled, along with the distribution of particle sizes about an average, to produce a statistical distribution having a significant proportion of fines and dust. Once formed, the particles can be mixed with surfactants, gassing inhibitors, gelling agents, electrolyte and other additives by standard processes.





FIG. 2

illustrates some of the distributions of zinc-based particles that have been tested in anode


20


. The distributions are shown as a function of effective particle diameter as measured with the particle diameter measurement technique described below. As a rough correspondence between mesh sizes and effective particle diameters, it should be noted that spherical particles with a diameter of 74 microns, for instance, will just sift through a 200 mesh screen, and spherical particles with a diameter of 44 microns will just sift through a 325 mesh screen. This correspondence is less accurate for particles of other shapes. Distribution


32


is of centrifugally atomized zinc-based particles that were sifted through a 325 mesh screen (i.e., dust), and has a peak at an effective particle diameter of about 57 microns. Distribution


34


is of gas atomized particles. Distributions


36


and


38


are of centrifugally atomized particles of −20/+200 and −200 mesh size, respectively. Distribution


40


is a combination of 50%, by weight, of the zinc-based dust of distribution


34


and 50%, by weight, of the particles of distribution


36


.




One of the effects of including significant proportions of very small zinc-based particles is an increase in the bulk surface area (i.e., the aggregate surface area) of the zinc-based particles in the anode. This is due to the inherent relationship between particle surface area and volume: namely that, for particles of similar shape, decreasing the particle size increases the surface area to volume ratio of the particle. High bulk surface area for a given particle mass is offered as a possible explanation of some of the high performance demonstrated by batteries with zinc-based particles in the form of fines.




Particle surface area can be further enhanced by controlling the production or subsequent processing of the zinc-based particles to produce particles with extended, nonspherical shapes, such as flakes or acicular particles. Acicular shapes (see particle


42


in

FIG. 3

, for instance) having a length L


1


along a major axis at least two times a length L


2


along a minor axis are considered to be appropriate. Flakes, such as particle


44


in

FIG. 4

, have a thin cross-section and two broad, opposite sides (such as a wafer or potato chip). Preferably, such a flake-form particle has an average thickness between its broad sides of no more than about 20% of the maximum dimension of the particle, to have a very low volume to surface area ratio.




One plausible theory for the mechanism that results in the good performance characteristics of batteries with anodes having high proportions of zinc-based dust or fines concerns particle-to-particle connectivity. This theory is only offered as a possible explanation of the observed results, and is not intended to limit the scope of the invention. In effect, it is believed that the additional fines form a mechanical network, particularly under electrical load and at low zinc loadings. This theory is supported by slurry resistivity measurements taken at various zinc loadings, as plotted in FIG.


5


. In this figure, the solid line is of an anode mixture with zinc-based particles of −20/+200 mesh size and the dashed line is of an anode mixture with zinc-based particles of −200 mesh size. It is believed that improved connectivity between large particles, fines and dust results in higher conductivity at loadings down to 50% or less. As a result, more electrolyte may be added to the mixture to increase zinc utilization (i.e., increase zinc volumetric usage efficiency) while maintaining low anode resistance. This improvement in connectivity, if the above theory is correct, would also tend to account for the high slurry viscosity, as well as good tolerance for mechanical shock (e.g., tap load voltage stability and drop voltage stability, as described below) of anodes with high proportions of fines and dust.




Continuous Load Test




This test simulates constant discharge in medium current draw applications, such as in some toys. A constant load (e.g., 30 ohms for a AAAA battery and 3.9 ohms for a AA battery) is applied across the battery terminals and the battery is continuously discharged through the load. The amount of time from the application of the load to when the battery voltage drops to a cut-off voltage is recorded.




Continuous Load Test




In this test power is discharged from the battery at a constant rate of (e.g., 0.25 watts for a AAAA battery or one watt for a AA battery), with the load automatically adjusted to account for changing battery voltage. This test is generally considered to be a more strenuous test than a continuous load (i.e., resistance) test, especially toward the end of the test as the battery voltage nears the cutoff value. The amount of time from the application of the load to when the battery voltage drops to a cut-off voltage is recorded.




Pulse Impedance Test




This test is a measure of the maximum dip in voltage that occurs when a fixed load is rapidly applied to the cell, and is an indication of the lag between voltage and current that can be exacerbated by the use of organic corrosion inhibitors to reduce gassing. Though of short duration, instantaneous drops in voltage can have significant consequences, as in devices which monitor instantaneous battery voltage and signal that the battery should be replaced if a low voltage is measured. A 3.9 ohm load is applied to the cell through a fast-acting relay, and the cell voltage is monitored on an oscilloscope. The load is maintained for 400 milliseconds. The minimum voltage during the test, which occurs upon application of the load, is measured.




High Current Pulse Test




AA battery




This test was designed to simulate the performance of a battery in a camera application. A controlled 1.1 amp current is intermittently drawn from the AA battery in a series of pulses, each of 10 seconds duration with a 50 second pause in between each pulse. The pulse series is continued for one hour each day until the AA battery voltage drops to a predetermined cut-off level, at which point the total number of pulses is recorded. This test is also performed on AA cells that have been stored for two weeks at 55° C. to determine how storage at elevated temperatures affects high discharge rate performance.




AAAA battery




This test was designed to simulate the performance of a flashlight. A 5.1 ohm resistance was intermittently applied to a AAAA battery in a series of pulses. The resistance was applied for four minutes per hour for eight hours in each day of service life until the AAAA battery voltage drops to a predetermined cut-off level, at which point the number of total service hours is recorded.




Anode AC Bulk Resistivity




This test measures how well the anode performs as an electrical conductor. A small alternating current, oscillating at about 1000 Hz, is applied to a volume of prepared anode mixture (with proper proportions of zinc-based particles, gelling agent, electrolyte and additives for use in an electrochemical cell), and the bulk resistivity of the mixture is measured.




Tap Load Voltage Instability




This test is a measure of the mechanical stability of the anode during a physical bump or shock. It is common for the voltage of batteries to dip under load during a bump (such as when they are tapped against a hard surface). This test measures the magnitude of such undesirable voltage dips. A constant 3.9 ohm load is applied to the battery, and the battery is struck once with an automated hammer (with a force of about 50-60 pounds, inducing an effective peak acceleration of about 20-50 kilometers/second/second with high attenuation) once every 60 seconds, while monitoring the battery voltage. Generally, when the battery reaches about a 25 percent discharge, the magnitude of the voltage dips reaches a maximum value, decreasing as the battery continues to discharge. The severity of the maximum voltage drop is used as a measure of cell performance.




Particle Diameter Measurement




The data in

FIG. 2

were generated by analyzing dry zinc-based particles, in bulk. A representative amount of sample powder to be analyzed was transferred into the funnel of a RODOS-VIBRI™ Sample Dispersion unit, available from Sympatec, which dispersed the powder into a stream of air to form an aerosol. The aerosol of the zinc-based particles in the form of powder is then passed through a HELOS™ Particle Size Analyzer, also available from Sympatec, which measures the intensity and distribution of light diffused through the aerosol of spinning particles. Various optical lenses with different focal lengths are used, in accordance with manufacturer's recommendations, with particles of different size ranges.




For a given sample of zinc-based particles, the average particle size is calculated using the following equation:







Average





particle





size

=




d
4





d
3













where d represents the diameter of a given zinc-based particle.




EXAMPLE 1




Cylindrical alkaline batteries of Type AA were built with gel anodes having the following two compositions to test the effect of zinc-based particles in the form of fines (the composition values listed are in percent by weight):




















Composition




1A




1B




























Zinc alloy particles




67.97




67.97







Indium acetate




0.03




0.03







(42% Indium)







Phosphate ester




0.06




0.06







(6% concentration)







Polyacrylic acid




0.53




0.53







Sodium polyacrylate




0.38




0.38







Acetic acid




0.09




0.09







(2.5% concentration)







Electrolyte solution




30.94




30.94







(2% ZnO, 35% KOH)









Total:




100.00




100.00







Particle sieve size




−20/+200




−200







Average particle size




335 microns




86 microns















The above compositions were prepared by first mixing the indium acetate powder with the dry zinc alloy particles. Next, the acetic acid and phosphate ester were applied, followed by the polyacrylic acid and sodium polyacrylate. After blending and crushing any lumps, the electrolyte solution was added and the mixture was blended until uniform. The zinc alloy particles in both 1A and 1B included 150 ppm In and 200 ppm Bi.




In each of the following tests, four individual batteries were tested.




















Example 1 test results:




1A




1B




























Continuous 3.9 ohm load test









Hours to 1.0 volts




1.51




1.57







Hours to 0.9 volts




1.70




1.86







Hours to 0.8 volts




1.73




2.01







One watt continuous load test







Hours to 1.0 volts




0.58




0.51







Hours to 0.9 volts




0.74




0.66







Hours to 0.8 volts




0.84




0.77







High current pulse test







Pulses to 1.0 volts




174




221







Pulses to 0.9 volts




233




337







Pulses to 0.8 volts




306




421







Pulse impedance test







Actual voltage trace





FIG. 6A





FIG. 6B















Note that in the pulse impedance tests the peak voltage dip 50 of 1A (

FIG. 6A

) is much more pronounced than the voltage dip 52 of 1B (FIG.


6


B).




EXAMPLE 2




Cylindrical alkaline batteries of Type AA were built with gel anodes having the following two compositions (the composition values listed are in percent by weight):





















Composition




2A




2B




2C





























Zinc alloy particles




69.80


1






69.80


2






69.80


3









Indium acetate




0.04




0.04




0.04







(42% Indium)







Phosphate ester




0.06




0.06




0.06







(6% concentration)







Polyacrylic acid




0.51




0.45




0.45







(Carbopol 940)







Acetic acid




1.12




1.12




1.12







(2.5% concentration)







Electrolyte solution




28.47




28.53




28.53







(2% ZnO, 35% KOH)










Total:




100.00




100.00




100.00















1


Alloy includes 150 ppm In, 200 ppm Bi; particles sieved to −20/+200 mesh size (average particle size of 354 micron; distribution 36,

FIG. 2

)













2


Alloy includes 150 ppm In, 200 ppm Bi; particles sieved to −325 mesh size (average particle size of 57 micron; distribution 32, FIG. 2).













3


An equal mixture, by weight, of particles as in 2A and gas atomized zinc particles alloyed with 500 ppm In and 500 ppm Bi. The gas atomized particles had a average particle size of about 41 micron (distribution 34, FIG. 2).













The particle mixture corresponds to distribution


40


. The average particle size of the mixture was 184 microns.




For each of the following tests, at least four individual batteries of each composition were tested. The results of the individual batteries are averaged.





















Example 2 test results:




2A




2B




2C













High current pulse test to 1.0 V










Pulses as built




226




293




299







Pulses after storage




217




278




244







Tap load voltage instability







(max voltage drop, mV)




374




112




 71















EXAMPLE 3




Cylindrical alkaline batteries of Type AA were built with gel anodes having the following two compositions to test the effect of zinc-based particles in the form of fines (the composition values listed are in percent by weight):




















Composition




3A




3B




























Zinc alloy particles




70.00




70.00







Indium acetate




0.03




0.03







(42% Indium)







Phosphate ester




0.06




0.06







(6% concentration)







Polyacrylic acid




0.51




0.48







(Carbopol 940)







Acetic acid




0.11




0.11







(2% concentration)







Electrolyte solution




29.29




29.32







(2% ZnO, 35% KOH)









Total:




100.00




100.00







Average particle size




298 microns




112 microns















The above compositions were prepared by first mixing the indium acetate powder with the dry zinc alloy particles. The electrolyte solution was mixed with the polyacrylic acid to form a gel. After blending and crushing any lumps, the gel was added to the indium acetate/zinc alloy combination and the resulting mixture was blended until uniform.




The zinc alloy in 3A included 150 ppm In and 200 ppm Bi.




3B was a mixture of 6 weight percent gas atomized zinc alloy particles (500 ppm In and 500 ppm Bi) of size −200 mesh or smaller, and 94 weight percent gas atomized zinc alloy particles (300 ppm In and 300 ppm Bi) between 150 and 200 mesh size.




In each of the following tests, four individual batteries were tested.




















Example 3 test results:




3A




3B




























Continuous 3.9 ohm load test









Hours to 1.0 volts




4.86




4.98







Hours to 0.8 volts




5.36




5.68







One watt continuous load test







Hours to 1.0 volts




0.75




0.79







Hours to 0.8 volts




1.03




1.063







High current pulse test







Pulses to 1.0 volts




188.8




235







Pulses to 0.8 volts




455




458















EXAMPLE 4




Cylindrical alkaline batteries of Type AAAA were built with gel anodes having the following two compositions to test the effect of zinc-based particles in the form of fines (the composition values listed are in percent by weight):




















Composition




4A




4B




























Zinc alloy particles




70.00




70.00







Indium acetate




0.04




0.04







(42% Indium)







Phosphate ester




0.06




0.06







(6% concentration)







Polyacrylic acid




0.51




0.51







Electrolyte solution




29.39




29.39







(2% ZnO, 35% KOH)









Total:




100.00




100.00







Particle sieve size




−20/+200




−200







Average particle size




335 microns




86 microns















The above compositions were prepared by first mixing the indium acetate powder with the dry zinc alloy particles. Next, phosphate ester was applied, followed by the polyacrylic acid. After blending and crushing any lumps, the electrolyte solution was added and the mixture was blended until uniform. The zinc alloy particles in both 4A and 4B included 150 ppm In and 200 ppm Bi.




In each of the following tests, four individual batteries were tested.




















Example 4 test results:




4A




4B




























Continuous 30 ohm load test









Hours to 1.0 volts




11.9




11.9







Hours to 0.9 volts




12.7




12.7







Hours to 0.8 volts




13.7




13.8







0.25 watt continuous load test







Hours to 1.0 volts




0.72




0.85







Hours to 0.9 volts




0.78




0.89







Hours to 0.8 volts




0.79




0.90







High current pulse test (hours)







Pulses to 1.0 volts




0.97




1.43







Pulses to 0.9 volts




1.66




1.90















Very small zinc-based particles, such as fines and dust, tend to be more unstable in oxygen-rich environments than larger particles and must therefore be processed with due care. Such issues, together with physical bulk handling issues of powders and fines, may need to be considered when determining the absolute minimum practical particle size for production anodes.




Other embodiments are also within the scope of the following claims.



Claims
  • 1. An electrode, comprising:zinc alloy particles in a fluid medium, the particles having a multi-modal distribution of particle sizes including a first mode and a second mode, wherein the particles in the second mode of the multi-modal distribution have an average particle size of less than about 120 microns wherein the second mode is different than the first mode, and wherein the electrode comprises at least 10% of the particles in the second mode by weight.
  • 2. The electrode of claim 1, wherein the zinc alloy particles in the second mode have an average particle size of less than about 44 microns.
  • 3. A battery, comprising:an anode; a cathode; and a separator disposed between the anode and the cathode, wherein the anode comprises zinc alloy particles in a fluid medium, the zinc alloy particles having a multi-modal distribution of particle sizes including a first mode and a second mode, wherein the particles in the second mode of the multi-modal distribution have an average particle size less than about 120 microns, wherein the second mode is different than the first mode, and wherein the anode comprises at least 10% of the particles in the second mode by weight.
  • 4. The electrode of claim 3, wherein the battery is a AA battery.
  • 5. The electrode of claim 3, wherein the battery is a AAA battery.
  • 6. The electrode of claim 3, wherein the battery is a AAAA battery.
  • 7. The battery of claim 3, wherein the zinc alloy particles in the second mode have an average particle size of 44 microns or less.
  • 8. The electrode of claim 1, wherein the zinc alloy particles include a material selected from the group consisting of indium and bismuth.
  • 9. The electrode of claim 2, wherein the zinc alloy particles include a material selected from the group consisting of indium and bismuth.
  • 10. The battery of claim 3, wherein the zinc alloy particles include a material selected from the group consisting of indium and bismuth.
  • 11. The battery of claim 7, wherein the zinc alloy particles include a material selected from the group consisting of indium and bismuth.
  • 12. The electrode of claim 1, wherein the zinc alloy particles in the second mode have an average diameter of 86 microns is or less.
  • 13. The battery of claim 3, wherein the zinc alloy particles in the second mode have an average diameter of 86 microns or less.
CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation-in-part of U.S. Ser. No. 08/905,254, filed Aug. 1, 1997, and entitled “Zinc Electrode Particle Form”, now U.S. Pat. No. 6,284,410 and a continuation-in-part of U.S. Ser. No. 09/115,867, filed Jul. 15, 1998, and entitled “Zinc-Based Electrode Particle Form”, now abandoned.

US Referenced Citations (98)
Number Name Date Kind
552709 Huber Jan 1896 A
3661645 Strier et al. May 1972 A
3784506 Vasta Jan 1974 A
3884722 Tucholski May 1975 A
3923544 Berchielli Dec 1975 A
3953242 Hoffman Apr 1976 A
3954506 Sullivan May 1976 A
4104188 Nicaise Aug 1978 A
4112205 Charkoudian et al. Sep 1978 A
4144382 Takeda et al. Mar 1979 A
4175052 Norteman, Jr. Nov 1979 A
4195120 Rossler et al. Mar 1980 A
4197635 Bilhorn Apr 1980 A
4209577 Clash Jun 1980 A
4242424 Buckler et al. Dec 1980 A
4247606 Uetani et al. Jan 1981 A
4260669 Kerg Apr 1981 A
4288913 Parsen et al. Sep 1981 A
4328297 Bilhorn May 1982 A
4332870 Parsen et al. Jun 1982 A
4361633 Nel et al. Nov 1982 A
4372823 Church et al. Feb 1983 A
4380578 Bahary Apr 1983 A
4404117 Gugenberger Sep 1983 A
4427751 Furukawa et al. Jan 1984 A
4435488 Bahary et al. Mar 1984 A
4455358 Graham et al. Jun 1984 A
4460543 Glaeser Jul 1984 A
4464446 Berger et al. Aug 1984 A
4487651 Wang Dec 1984 A
4500614 Nagamine et al. Feb 1985 A
4514473 Atkin et al. Apr 1985 A
4548642 Glaeser Oct 1985 A
4563404 Bahary Jan 1986 A
4579791 Wang Apr 1986 A
4585716 Chalilpoyil et al. Apr 1986 A
4592974 Takeda et al. Jun 1986 A
4604335 Johnson Aug 1986 A
4606869 Showak Aug 1986 A
4619845 Ayers et al. Oct 1986 A
4631013 Miller Dec 1986 A
4632699 Meeus et al. Dec 1986 A
4649093 Vu et al. Mar 1987 A
4681698 Graham et al. Jul 1987 A
4722763 Pa et al. Feb 1988 A
4735876 Miura et al. Apr 1988 A
4743185 Vu et al. May 1988 A
4778516 Raman Oct 1988 A
4812374 Kagawa et al. Mar 1989 A
4861688 Miura et al. Aug 1989 A
4920020 Strauven et al. Apr 1990 A
4957827 Kordesch et al. Sep 1990 A
4994333 Jose et al. Feb 1991 A
4996129 Tuck Feb 1991 A
5082622 Meeus et al. Jan 1992 A
5108494 Uemura et al. Apr 1992 A
5139900 Tada et al. Aug 1992 A
5147739 Beard Sep 1992 A
5162169 Tomantschger et al. Nov 1992 A
5164274 Kordesch et al. Nov 1992 A
5168018 Yoshizawa et al. Dec 1992 A
5183481 Felder Feb 1993 A
5198315 Tada et al. Mar 1993 A
5206096 Goldstein et al. Apr 1993 A
5209995 Tada et al. May 1993 A
5228958 Goldstein et al. Jul 1993 A
5232798 Goldstein et al. Aug 1993 A
5240793 Glaeser Aug 1993 A
5278005 Yamauchi et al. Jan 1994 A
5283139 Newman et al. Feb 1994 A
5296267 Tada et al. Mar 1994 A
5312476 Uemura et al. May 1994 A
5340666 Tomantschger et al. Aug 1994 A
5346781 Yuasa et al. Sep 1994 A
5348816 Shinoda et al. Sep 1994 A
5368958 Hirai et al. Nov 1994 A
5376480 Shinoda et al. Dec 1994 A
5389468 Fujiwara et al. Feb 1995 A
5419987 Goldstein et al. May 1995 A
5424145 Tomantschger et al. Jun 1995 A
5425798 Sasaki et al. Jun 1995 A
5432031 Teraoka et al. Jul 1995 A
5434023 Teraoka et al. Jul 1995 A
5445908 Inoue et al. Aug 1995 A
5482798 Mototani et al. Jan 1996 A
5514496 Mishima et al. May 1996 A
5532087 Nerz et al. Jul 1996 A
5541021 Watanabe et al. Jul 1996 A
5587254 Kojima et al. Dec 1996 A
5626988 Daniel-Ivad et al. May 1997 A
5652043 Nitzan Jul 1997 A
5712060 Grigorieva et al. Jan 1998 A
5741609 Chen et al. Apr 1998 A
5750288 Xie et al. May 1998 A
5780186 Casey, Jr. Jul 1998 A
6015636 Goldstein et al. Jan 2000 A
6022639 Urry Feb 2000 A
6284410 Durkot et al. Sep 2001 B1
Foreign Referenced Citations (60)
Number Date Country
2077796 Sep 1992 CA
23 45 514 Sep 1973 DE
2347273 Mar 1974 DE
2441356 Mar 1975 DE
2345514 Apr 1975 DE
2364203 Jun 1975 DE
3605718 Aug 1987 DE
0 161 701 Nov 1985 EP
0 162 411 Nov 1985 EP
0 328 131 Aug 1989 EP
0 497 074 Jan 1991 EP
0 377 106 Mar 1995 EP
0 762 521 Dec 1997 EP
0 817 294 Jul 1998 EP
2 276 699 Jun 1974 FR
47-43896 Nov 1968 JP
51 104533 Sep 1976 JP
46445 Apr 1977 JP
54-99945 Jan 1978 JP
55-117869 Sep 1980 JP
56-145669 Nov 1981 JP
57182972 Nov 1982 JP
58-158867 Sep 1983 JP
58218760 Dec 1983 JP
59-66061 Apr 1984 JP
59-167961 Sep 1984 JP
60-97581 May 1985 JP
61-64974 Apr 1986 JP
61-77264 Apr 1986 JP
61.78067 Apr 1986 JP
61.79789 Apr 1986 JP
61-131363 Jun 1986 JP
61-133560 Jun 1986 JP
61.140066 Jun 1986 JP
61.140067 Jun 1986 JP
61.140068 Jun 1986 JP
61.140464 Jun 1986 JP
61-193362 Aug 1986 JP
61-203564 Sep 1986 JP
61.153948 Dec 1986 JP
62-31951 Feb 1987 JP
62-040162 Feb 1987 JP
62-105365 May 1987 JP
62-123658 Jun 1987 JP
09-235636 Sep 1987 JP
62-225164 Oct 1987 JP
63-006747 Jan 1988 JP
63-195975 Aug 1988 JP
3-33014 Feb 1991 JP
30 071559 Mar 1991 JP
3-272563 Dec 1991 JP
92-08897 Feb 1992 JP
5-101824 Apr 1993 JP
7-105948 Apr 1995 JP
60-91562 May 1995 JP
498667 Jan 1974 RU
399942 Feb 1974 RU
586516 Dec 1977 RU
WO 9820569 May 1998 WO
WO 9113924 Nov 1998 WO
Non-Patent Literature Citations (13)
Entry
NJZ Metal Powder Data Sheet, Horse Head Zinc Powders, The New Jersey Zinc Company, Inc., Pre-1996.
Daniel-Ivad et al., “Mercury and lead free Zn/MnO2 cells”, Electrochemical Society Proceedings, vol. 95-14, 1995.
Commercial Battery (Date Unknown).
Huot et al., “Electrochemical Performance of Gelled Zinc Alloy Powders in Alkaline Solutions”, pp. 81-85, Journal of Power Sources, vol. 65, Nos. 1-2, Mar.-Apr. 1997.
Ozbilen et al., “Influence of Liquid Metal Properties on Particle Size of Inert Gas Atomised Powders”, pp. 44-52, Power Metallurgy, vol. 39, No. 1, 1996.
Hani Henein, “Process Diagnostics to Monitor and Control Gas Atomization Operations”, pp. 1-199-1-219, Metal Powder Industries Foundation, 1996.
Boyko et al., “Ensemble Laser Probe Sizing Results for Gas Atomized Zinc Powders”, pp. 655-658, First International Conference on Processing Materials for Properties, 1993.
Ali Unal, “Gas Atomization of Fine Zinc Powder”, pp. 11-21, The International Journal of Powder Metallurgy, vol. 26, No. 1, 1990.
Dunkley et al., “Evaluating the Performance of Atomizers for Producing Metal Powers”, pp. 26-31, Industrial Heating, Oct. 1989.
Lavernia et al., “Powder Size and Distribution in Ultrasonic Gas Atomization”, pp. 22-26, Journal of Metals, Aug. 1985.
“Gas Atomisation of High Temperature Alloy Powders”, pp. 563-566, MPR, Oct. 1983.
J.J. Dunkley, “Properties and Applications of Atomised Metal Powders”, pp. 520-525, Assoc. Italiana di Metallurgia, 1982.
Daniel-Ivad et al., “Mercury and lead free Zn/MnO2 cells”, Extended Abstracts, vol. 95-2, 1995.
Continuation in Parts (2)
Number Date Country
Parent 09/115867 Jul 1998 US
Child 09/156915 US
Parent 08/905254 Aug 1997 US
Child 09/115867 US