1. Field of the Invention
The present disclosure relates to plain bearings, and more particularly to plain bearings with electrodynamically finished bearing surfaces.
2. Description of Related Art
Plain bearings, such as thrust and journal bearings, are commonly used to support loads. Such bearings generally have a rotatable structure like a shaft that is rotatably supported relative to a bearing surface. When stationary and during rotation load is communicated through an interface located between the rotatable structure and the bearing surface. Bearings typically include lubricant which is carried into the interface during rotation to limit friction between the rotatable structure and the bearing surface in the interface.
During rotation the lubricant forms an elasto-hydrodynamic layer (EHD) within the interface between the rotatable element and the bearing surface. The EHD layer communicates the supported load between the rotatable structure and the bearing surface. In some bearings either or both the rotatable structure and bearing surface can have form error, i.e., deviation from an intended curvature and ideal surface condition, delaying formation of the EHD layer between the rotating structure and bearing surface during start of rotation, rotation stop, and during low speed rotation. Delay of EHD layer formation can increase wear due to friction between the contacting rotating structure and bearing surface, potentially reducing reliability and service life of the bearing.
Existing journal bearing and methods of making bearings have generally been considered satisfactory for their intended purpose. However, there is still a need in the art for improved bearing assemblies with improved surface finishes and methods of making bearing assemblies with improved surface finishes. The present disclosure provides a solution for this need.
A method of electrodynamically finishing a plain bearing includes electrically separating a bearing housing from a journal shaft with a lubricant disposed on a bearing surface of the bearing housing. The bearing housing or the bearing journal is rotated relative to the other and a voltage differential applied across the bearing housing and the journal shaft. A bearing surface asperity is eroded with electric discharge between the journal shaft and the bearing housing.
In certain embodiments, the method can include mechanically finishing the journal shaft with the bearing housing prior to electrically separating the bearing housing and member. A mechanical load can be communicated between the bearing housing and journal shaft through a lubricant film disposed in the gap. The minimum mechanical separation distance between the bearing housing and the journal shaft can be reduced.
In accordance with certain embodiments, the journal shaft can be translated relative to the bearing housing. The journal shaft can be rotated relative to the bearing housing. The bearing housing can be rotated relative to the journal shaft. A journal member or a thrust member can be rotated relative to the bearing housing. The bearing housing can be rotated relative to the journal member. The bearing housing can be rotated relative to the thrust member.
It is contemplated that an alternating current (AC) voltage differential can be applied across bearing housing and journal shaft. The voltage differential can be removed based upon a comparison of one or more of a lubricant property, load, temperature, and rotational speed with a selected value. The bearing surface can be smoothed by reduction of asperities disposed on the bearing surface. Carbide or metallic asperities disposed on the bearing surface can be vaporized.
A plain bearing assembly includes a bearing housing with a bearing surface and a journal shaft. The journal shaft is supported on the bearing surface with a lubricant disposed between the journal shaft and the bearing surface. The bearing surface has an electrodynamically eroded surface portion finished to the journal shaft.
In certain embodiments the plain bearing assembly can include a journal bearing or a thrust bearing. The bearing housing and/or the journal shaft can include a metallic material. The bearing housing and/or the journal shaft can include a carbide-containing material. A bearing housing lead can be electrically connected to the bearing housing. A journal shaft lead can be electrically connected to the journal shaft. Journal shaft and bearing housing leads can be connected to the bearing housing and journal shaft. A voltage source can be connected to the plain bearing assembly.
In accordance with certain embodiments, the voltage source can be an AC voltage source. A positive terminal of the voltage source can be connected to the journal shaft. A negative terminal of the voltage source can be connected to the bearing housing. A mechanical load can be coupled through the bearing assembly to a static structure. The mechanical load can include a rotor. A rotation source can be connected to the rotor.
A motor assembly includes a rotor and a stator. The bearing housing and the journal shaft include a carbide-containing metallic material. A minimum lubricant-film distance between the bearing surface and the journal is defined between an electrodynamically eroded asperity and the journal shaft.
These and other features of the systems and methods of the subject disclosure will become more readily apparent to those skilled in the art from the following detailed description of the preferred embodiments taken in conjunction with the drawings.
So that those skilled in the art to which the subject disclosure appertains will readily understand how to make and use the devices and methods of the subject disclosure without undue experimentation, embodiments thereof will be described in detail herein below with reference to certain figures, wherein:
Reference will now be made to the drawings wherein like reference numerals identify similar structural features or aspects of the subject disclosure. For purposes of explanation and illustration, and not limitation, a partial view of an exemplary embodiment of a plain bearing assembly in accordance with the disclosure is shown in
Referring to
Plain bearing assembly 100 includes a bearing housing 102 with a bearing surface 104 and a journal shaft 106. Journal shaft 106 is supported on bearing surface 104 with a lubricant 108 disposed between journal shaft 106 and bearing surface 104. Bearing surface 104 has an electrodynamically eroded surface portion 110 finished such that surface portion 110 is matched to journal shaft 106. In this respect surface portion 110 has one or more electrodynamically eroded asperity 122 (shown in
Lubricant-film gap 112 is occupied at least in part by lubricant 108. A portion of lubricant 108 is disposed between rotating journal shaft 106 and electrodynamically surface portion 110. Examples of suitable lubricants include hydrodynamic oils with viscosities dependent upon bearing rotational speed, oil temperature, and load, having dielectric breakdown strength suitable for controlled erosion of race surfaces at relative low voltages at lubricant-film thicknesses present in mechanically matched bearing assemblies.
In the illustrated exemplary embodiment journal shaft 106 be formed from a metallic material 114 and that bearing housing 102 be formed from metallic material 116. It is contemplated that one or more of metallic material 114 and metallic material 116 can a carbide-containing metallic material. In accordance with certain embodiments, metallic material 114 and metallic material 116 can be formed from similar or substantially equivalent metallic alloy compositions. Examples of suitable metallic materials include carbon martensitic stainless steels and austenitic stainless steels.
Rotor 14 is fixed relative to journal shaft 106 and bearing housing 102, and is fixed relative to stator 17. Rotation source 16 is operably connected to rotor 14 for applying rotational energy to rotor 14. As will be appreciated by those of skill in the art in view of the present disclosure, rotor 14 can be fixed to bearing housing 102 and journal shaft 106 fixed relative to stator 17, as suitable for an intended application.
In the illustrated exemplary embodiment plain bearing assembly 100 supports rotor 14 within motor assembly 22 with lubricant 108 disposed between bearing housing 102 and journal shaft 106. As will also be appreciated by those of skill in the art in view of the present disclosure, vibration V associated with rotation of rotor 14 about rotation axis 20 couples to stator 17, and therethrough to static structure 12 through plain bearing assembly 100 and can influence performance of devices carried by vehicle 10, such as an exemplary imaging device 24. Asperities, e.g., electrodynamically eroded asperity 122 (shown in
With reference to
A voltage source 216 for forming electrodynamically finished bearing surface portion 212 is connected to journal bearing assembly 200. In this respect voltage source 216 is connected to journal bearing assembly 200 through a finishing circuit 218. Finishing circuit 218 includes a journal shaft lead 220 and a bearing housing lead 222. Journal shaft lead 220 is connected to a positive terminal of voltage source 216 and bearing housing lead 222 is connected to a negative terminal of voltage source 216 to apply a voltage differential (illustrated with positive and negative symbols at voltage source 216) across sleeve 204 and journal 214. The voltage differential can be an AC voltage differential 224. The voltage differential can be a DC voltage differential 226. AC voltage differentials can reduce asperities on both journal land 208 and bearing surface 206. DC voltage differentials can reduce asperities on bearing surface 206 relative rapidly due to the constant polarity of the voltage differential.
Once finishing circuit 218 is established and voltage differential applied, one of journal 214 and bearing housing 202 is rotated relative to the other. For example, journal 214 can be rotated relative to bearing housing 202 as shown with arrow 228. This concentrates finishing locally at a region of bearing housing when journal 214 is proximate to bearing surface 206. Bearing housing 202 can be rotated relative to journal 214 as shown with arrow 230. This uniformly finishes bearing surface 206 to journal land 208 about substantially the entire circumference of bearing surface 206. In certain embodiments a load 232 can be applied to between journal 214 and bearing housing 202, affecting the time required for finishing by reducing the radial distance occupied by lubricant-film gap 112 (shown in
In certain embodiments, the voltage differential between bearing surface 206 and journal surface 215 can be applied statically. In this respect it is contemplated that the electrical isolation of journal 214 and/or bearing housing 202 can be interrupted. Interruption of the electrical isolation, such as by grounding only one of journal 214 and bearing housing 202, allows the element with the interrupted electrical isolation to develop a static charge from flow of lubricant 213 across the element. When static charge builds up sufficient to overcome the dielectric breakdown strength of lubricant between journal surface 215 and an asperity on bearing surface 206 an electrical discharge event occurs, reducing the asperity by vaporizing material forming the asperity, thereby smoothing bearing surface 206.
With reference to
When the potential difference exceeds the dielectric breakdown strength associated with a minimum width of lubricant-film gap 112 an electrical discharge event 120 occurs between an asperity 122 bounding the lubricant-film gap 112, as shown in
As shown in
Referring now to
In certain embodiments, the journal shaft and bearing housing are mechanically matched to one another and assembled into the plain bearing assembly prior to electrically separating the bearing housing and journal shaft, as shown with box 350. A mechanical load, e.g., load 232 (shown in
It is contemplated that the voltage differential can be removed based upon a comparison of one or more of a lubricant property, load, temperature, and rotational speed with a selected value, as shown by box 390. When the comparison indicates that the selected value has not been reached application of the voltage differential continues, as shown with arrow 392. When the comparison indicates that the selected value has been reached the voltage differential is removed, as shown with box 394 and arrow 396. The plain bearing assembly is thereafter considered ‘run-in’ such that the leads can physically be removed and the assembly incorporating the plain bearing assembly fully employed in its intended use.
With reference to
With reference to
Plain bearings generally include a shaft or journal that rotates freely in a supporting metal sleeve or shell, or a movable plate supported on a guide plate. Some plain bearings can include form or finish errors in the raceway due to machining process limitations. The form errors can cause in undesirable lubricant whirl and/or retarded EHD layer development, potentially causing excessive wear during startup and/or shutdown. Some of the raceway form or finish errors are the result of high-hardness inclusions in the race material, such as carbides, which are harder than the surrounding bearing material, like steel. Such inclusions can be smeared during honing or polishing of the bearing surface, resulting in bearing surface artifacts like “honing lines” and roughness.
In embodiments described herein, electrical discharge across the EHD between the bearing housing and bearing housing is used to improve smoothness of the bearing surface by reducing (or removing entirely) form error and improving the bearing surface finish. The improved smoothness reduces oil whirl potential and allows for lower hydrodynamic speeds during startup and shutdown, reducing metal-to-metal wear that can occur during star-up and shutdown. It is contemplated that the smoothing process be controlled using one or more of lubricant properties, load, temperature, rotational speed, voltage magnitude, and voltage rise time during the electrical discharge smoothing process.
Electrical discharge erosion is a phenomenon in bearings where a voltage across a journal shaft and bearing housing discharges when the film thickness between the journal shaft and bearing housing is less than the corresponding discharge gap based on the lubricant dielectric constant. At high voltages electrical discharge can have magnitude sufficient to destructively pit, crater, erode, and potentially reduce the reliability of the plain bearing assembly by making the bearing surface less smooth. Plain bearing assemblies are therefore generally electrically grounded, the shaft fixed to the journal shaft being electrically or the bearing housing being electrically isolated.
Applicants have come to appreciate that, at relatively low voltages and with suitable control, electrical discharge can constructively smooth the bearing surface. In particular, the bearing surface can be gently eroded at localized high spots in a compensatory manner, thereby reducing (or eliminating entirely) form error and artifacts in the bearing surface from the surface honing and polishing processes typically used to define the bearing surface finish. This results in a smoother bearing surface that otherwise possible with conventional honing techniques, allowing the lubricant-film in the bearing assembly to be established at lower rotational speeds, reducing (or eliminating) startup and shutdown wear. The in-situ finishing and/or matching can also compensate for some amounts of alignment and/or installation error in bearing assembly and/or end item housing the bearing assembly.
Without wishing to be bound to a specific theory, it is understood that the electrical discharge process is compensatory because erosion occurs preferentially in high stress regions of the bearing surface that in low stress regions of the bearing surface. The smoothing arises out of low voltage electrical discharge events occurring between the highest asperities of the bearing surface and journal shaft, the localized nature of a given asperity causing a given electrical discharge event to generate heat sufficient to vaporizes asperity peak, thereby smoothing the bearing surface. Advantageously, carbides in the bearing surface material are affected at nearly the same rate as the steel material, which prevents the smearing that can accompany removal of such carbides in conventional abrasive honing processes.
In accordance with certain embodiments, the smoothing can be done in-situ. In this respect the journal shaft and bearing housing can be finished and/or matching to more closely conform to one another subsequent to assembly. Finishing and/or matching can be done, for example, by varying the rotation speeds and temperatures during the initial run-in of the bearing—either on a test stand or subsequent to installation into an end item—thereby affecting the lubricant film thickness and material erosion rates. In further embodiments, AC voltage magnitude and frequency can be varied to control the material erosion rate to improve (or optimize) the geometric precision and surface finish in the final product. Once the smoothing process is complete and suitable finishing achieved, erosion can be halted by removal of the voltage source and electrically isolating the bearing assembly in the end item housing the bearing assembly to eliminate any further erosion which could otherwise be possible from any induced voltages from the end item or end item environment.
The methods and systems of the present disclosure, as described above and shown in the drawings, provide for bearing assemblies with low disturbances, greater load-carrying capacity, improved fatigue life, and/or smoother bearing surfaces for lower EHD liftoff speeds to reduce metal-to-metal wear at low operating speeds. While the apparatus and methods of the subject disclosure have been shown and described with reference to preferred embodiments, those skilled in the art will readily appreciate that change and/or modifications may be made thereto without departing from the scope of the subject disclosure.
Number | Name | Date | Kind |
---|---|---|---|
2782160 | Treuhaft et al. | Feb 1957 | A |
3547796 | Randall | Dec 1970 | A |
3900374 | Haggerty | Aug 1975 | A |
4601801 | Fukuda et al. | Jul 1986 | A |
5906535 | Tonooka et al. | May 1999 | A |
6176998 | Wardle | Jan 2001 | B1 |
6461486 | Lorincz et al. | Oct 2002 | B2 |
6896416 | Matsuzaki | May 2005 | B2 |
7255778 | Mori | Aug 2007 | B2 |
7374644 | Butterfield et al. | May 2008 | B2 |
9322109 | Langlais | Apr 2016 | B2 |
20090321274 | Comaty | Dec 2009 | A1 |
20100043742 | Erdmann | Feb 2010 | A1 |
Number | Date | Country |
---|---|---|
2017015228 | Jan 2017 | JP |
20170009072 | Jan 2017 | KR |
2017034788 | Mar 2017 | WO |
Entry |
---|
Extended European Search Report, prepared by Examiner, of the European Patent Office, dated Oct. 19, 2018, issued in corresponding European Patent Application No. 18186854.8. |
Number | Date | Country | |
---|---|---|---|
20190040907 A1 | Feb 2019 | US |