Patent Application
20080101080
Applicant claims priority under 35 U.S.C. §119 of German Application No. 10 2006 050 327.9 filed Oct. 25, 2006.
1. Field of the Invention
The present invention relates to an electroluminescent film composite. In particular, the invention relates to an electroluminescent film composite for attachment in the entry region of a motor vehicle to decorate the entry and facilitate entering the vehicle in the dark. The electroluminescent film composite has an upper electrode layer, a lower electrode layer, a luminescence layer disposed between the upper and the lower electrode layer, and an adhesive layer on the underside. Furthermore, the invention relates to a motor vehicle equipped with such a film composite.
2. The Prior Art
Electroluminescent film composites, referred to by the abbreviation EL films in the following, are design elements in automobile construction that are used in many different ways. For example, they serve for backlighting of the car roof lining, or of dashboards. For some years now, they have also been affixed in the entry region of automobiles, particularly on thresholds, running boards, and doorsills, in order to decorate the entry and facilitate entering the car in the dark.
In this connection, film composites of the type stated initially are integrated into the entry region, for example as described in the German utility model DE 201 03 133 U1 or in the German Offenlegungsschrift DE 103 20 467 A1, in such a manner that they are either completely recessed into the entry threshold, or are covered on the top with a metal or plastic shutter. Such a shutter is required in order to protect the EL film from scratches and impact stresses, such as those that unavoidably occur due to contact with the shoes of car passengers who are getting in or out. Entry strips lighted with EL films, which strips have a simple structure, as they are already available in the discount trade, also cannot make do without separate protective covers, such as injection-molded plastic parts or metal strips.
The separate covers make lighting the entry region more expensive, and they cause significant effort in installation. EL films in the entry region that are provided as standard equipment require a suitably designed environment, in order to guarantee sufficient scratch and impact protection. After-market film composites of the type stated initially require a clearly elevated structure, as compared with the surroundings. This structure can result in fit problems, for one thing, and there is the risk of getting caught on them when getting in and out.
With the background of the set of problems described, it is an object of the present invention to provide the lighting of a vehicle entry using electroluminescence in a simpler and more cost-advantageous manner, and, in this connection, to particularly reduce the installation effort, without having to do without sufficient friction wear protection.
These and other objects are achieved, according to one aspect of the present invention, by an electroluminescent film composite for attachment in the entry region of a motor vehicle having an upper electrode layer, a lower electrode layer, a luminescence layer disposed between the upper and the lower electrode layer and an adhesive layer on the underside. The film composite has a friction-wear-resistant, at least partially transparent protective layer as the uppermost layer, which is connected with the remainder of the composite over its entire area.
Preferred embodiments are discussed below.
Instead of a separate shutter, the friction wear protection is rigidly integrated into the film composite, i.e. connected with the other layers of the composite in planar manner, for example in that a friction-wear-resistant protective film is already applied during production of the composite, via gluing, hot-lamination, or a similar method. Alternatively or additionally, a friction-wear-resistant coating layer can be applied, also already during production of the composite. A coating layer is understood to be a layer that is applied in the flowable or pourable state, and not in the form of a film body, for example by imprinting, spraying, spreading, powder-coating or casting.
The film composite may be configured as an entry strip. A carrier film may be disposed underneath the lower electrode layer. The carrier film may be made predominantly of poly(ethylene terephthalate)(PET).
The protective layer may be structured as a protective film made predominantly of polyvinyl chloride material or polyurethane material having a thickness of at least 75 μm.
The protective layer may be a coating layer. The coating layer may be cast, spread on or sprayed on, or printed on. The coating layer may consist of a polyurethane material, such as a polyurethane resin, or a texture or relief varnish.
The coating layer may be produced from an application agent that has a flow limit of more than 50 Pa when it is applied to the surface. The coating layer may have a thickness of at least 50 μm and may be enriched with solid particles such as rubber particles, glass particles, or support pigments.
The free surface of the protective layer may be hardened with electron beams or textured. At least one decorative element may be integrated into the film composite underneath the protective layer. The decorative layer may have a metallic effect.
The decorative element may represent a mask for the formation of graphic and/or alphanumeric symbols and may be translucent or printed.
The upper electrode layer, lower electrode layer, and luminescence layer may be structured over only part of the area or spaced apart from an edge of the film composite by at least one millimeter, all around.
It is surprising for a person skilled in the art that a protective layer having a thickness of less than 100 micrometers, preferably less than 40 micrometers, is alone able to offer sufficient friction wear protection. This protection can be further improved by electron-beam hardening of the surface or nanoparticle coatings. As compared with commercially available plastic covers, there is furthermore a clearly increased impact resistance; in particular, the risk of splintering due to brittleness caused by cold in winter no longer exists. The surface can be kept permanently dirt-free by means of nanotexturing.
As compared with the state of the art described above, there is the advantage that the film composite can be glued on at the desired application location in one working step, and, at the same time, the material expenditure is slight. The film composite according to the invention is generally more flexible and clearly thinner than a metal or plastic shutter (according to an advantageous embodiment, having a bending resistance of less than 20 mNm, preferably less than 10 mNm, according to DIN 53 121, and a total thickness of less than 3 m, preferably less than 1.5 mm). As a result, the application flexibility is greater, particularly for after-market sets.
Depending on the desired place of application, the film composite is preferably designed to be as step-resistant as possible. In particular, preferably the film composite is designed so that a pressure stress of 7 newtons per square centimeter, preferably 10 newtons per square centimeter, can be absorbed without permanent damage.
According to another aspect, the invention provides a motor vehicle that has an entry region having a film composite as discussed above affixed at step height. The top of the film composite may be free of a separately affixed protective cover. The film composite may be attached to the motor vehicle solely via its underside adhesive layer.
Fundamentally, any variant of the invention described or indicated in the present application can be particularly advantageous, depending on the economic and technical conditions in an individual case. Unless something is stated to the contrary, and to the extent that it is fundamentally technically possible, individual characteristics of the embodiments described can be interchanged or combined with one another, as well as with measures known from the state of the art.
Other objects and features of the present invention will become apparent from the following detailed description considered in connection with the accompanying drawings. It should be understood, however, that the drawings are designed for the purpose of illustration only and not as a definition of the limits of the invention.
In the following, examples of preferred embodiments of the present invention will be explained in greater detail, using the related drawings. In this connection, the drawings are purely schematic, and are not representations to scale, for reasons of better illustration. In particular, relationships of the dimensions relative to one another can deviate from actual embodiments. For example, the thickness of film layers is represented in greatly exaggerated manner.
Elements that correspond to one another are provided with the same reference symbol in the individual figures, to the extent that doing so makes sense.
Individually, the drawings show:
a shows an example of a film composite according to the invention, disposed on a carrier material, in a cross-sectional representation similar to
b shows the film composite from
Turning now in detail to the drawings,
In place of separate electrode layers 5, 7 of a transparent conductive varnish, silver paste, or carbon paste, or the like, for example, electrically conductive sputter or vapor-deposited films 4, 8 can also be used. Contacting of electrode layers 5, 7 can take place, for example, by so-called bus bars of suitable conductive pastes or metal films. Insulation of electrode layer 5, 7 on the film edge, with regard to the surroundings, is not shown but is necessary.
In addition to the layers listed, various other film layers such as dielectrics, vapor barriers, optical filters, and the like can also supplement the structure, if necessary, in advantageous manner, and might even be necessary for special application cases.
Insulating film 8 on the top also fulfills the task of a protective film 8. It is characterized in that it has sufficient step resistance and friction wear resistance to withstand constant stress caused by people stepping on it. Suitable materials for protective film 8 are, in particular, films made from polyvinyl chloride (PVC) or polyurethane (PU). Preferably, a protective film 8 having a thickness of at least 75 μm, particularly preferably at least 100 μm, is used. A double-layer or multi-layer protective film 8 is also possible.
Materials that are particularly suitable for the formation of the protective film, depending on the application case, are, for example, a highly transparent polyurethane (PU) film with a thickness of 100-300 μm available under the name Schreiner ProTech 3S film or a PVC-film, black/shagreened with a thickness of 145 μm available under the name Schreiner No. 47 001269—01. A partially transparent PVC material, scarred with black, available from RITRAMA S.p.A., for example, with acrylate permanent adhesive as the connection layer, is also well suited.
A second preferred embodiment of the invention is shown in
A material that is particularly suitable for forming coating layer 10, depending on the application case, is a so-called step protection varnish, particularly a step protection varnish that is a colorless (transparent) UV-lacquer available under the name Nori Cure UVL 3. Transparent casting masses available under the name Plastoclear are also particularly well suited.
Furthermore, the application agents that form coating layer 10 can be enriched with additional solids, for example with rubber particles, glass particles, or other so-called support pigments, whereby these preferably have a Mohs hardness of 6 or greater, in order to produce a stable layer that is particularly step-resistant and friction-wear-resistant. The surface of coating layer 10 is preferably not smooth, but rather textured, and prevents uncontrolled slipping on it.
a and 3b show a film composite 1 extensively structured as in
The combination of a suitable top-side protective layer 8, 10 and an adhesive 3 applied on the underside leads to a lighting element that is easy to apply but nevertheless stable and robust. Furthermore, an optically attractive component can be produced via graphic effects such as an imprint of a translucent metal effect layer that has an opaque effect towards the outside (not shown) underneath the top-side protective layer 8, 10, which component demonstrates high product quality, despite a clearly reduced cost expenditure.
Although only a few embodiments of the present invention have been shown and described, it is apparent that many changes and modifications may be made thereunto without departing from the spirit and scope of the invention.