Patent Application
20230160079
The present invention relates to an electrolysis cell unit including an electrolysis cell configured to include an electrode layer and a counter electrode layer with an electrolyte layer interposed therebetween, a method for producing or using the electrolysis cell unit, and an electrolysis cell device configured to include the electrolysis cell unit, and relates to a hydrocarbon production system configured to include this type of electrolysis cell device.
This type of hydrocarbon production system is configured as a system that produces hydrocarbons from at least water and carbon monoxide, and the electrolysis cell device including the electrolysis cell unit serves for electrolysis (electrolyzation) of a hydrogen source (typically water), and electrolysis (electrolyzation) of a carbon monoxide source (typically carbon dioxide).
This type of hydrocarbon production system is disclosed in JP-T-2016-522166 and JP-A-2019-112717.
The system disclosed in JP-T-2016-522166 includes a high temperature electrolyte (HTE) reactor (corresponding to electrolysis reaction unit of the present invention) including stacking of electrolysis single cells (corresponding to the electrolysis cell unit of the present invention) that generate either hydrogen or a synthetic raw material gas (“synthetic gas” representing a mixture of hydrogen and carbon monoxide) from steam and carbon dioxide, in which the synthetic gas obtained in this electrolysis single cell is converted into a desired combustible gas by a heterogeneous catalytic action.
Therefore, in the technique disclosed in JP-T-2016-522166, a hydrocarbon synthesis unit is provided on the downstream side of the electrolysis reaction unit, and hydrocarbons are produced using water and carbon dioxide as starting materials.
Referring to
Meanwhile, a technique disclosed in JP-A-2019-112717 relates to a power-to-gas unit that generates a useful gas (specifically, methane) from electric power, specifically, a technique is disclosed in which a methanation reaction catalyst material is contained in a cathode of a stack of a solid oxide (SOEC) basic electrolysis cell.
Also in the technique disclosed in JP-A-2019-112717, the electrolysis cell serves as the electrolysis reaction unit, and the methanation reaction catalyst material provided on the cathode constitutes the hydrocarbon synthesis unit.
In the related arts, in the electrolysis reaction unit, so-called “co-electrolysis” is carried out in which both water and carbon dioxide are electrolyzed together. A heterogeneous catalyst is used for synthesis (so-called methanation) of hydrocarbons.
However, the following problems regarding co-electrolysis in the electrolysis reaction unit and hydrocarbon synthesis in the hydrocarbon synthesis unit have been found.
Since an electrolysis voltage of water is around 1.23 V, while an electrolysis voltage of carbon dioxide is around 1.33 V, the electrolysis reaction of carbon dioxide is less likely to occur than the electrolysis reaction of water. As a result, even when the co-electrolysis reaction is attempted, the electrolysis reaction of carbon dioxide is unlikely to occur, and the concentration of carbon monoxide required for hydrocarbon synthesis cannot be sufficiently secured.
Although it is said that a heterogeneous catalyst is used, it is difficult to select this kind of catalyst, and a technique capable of stably synthesizing hydrocarbon has not yet been established.
3. Further, referring to the device described in JP-T-2016-522166, the device is large in size, and there is room for improvement in that hydrocarbon synthesis is efficiently performed without consuming special energy.
In view of this situation, a main object of the present invention is to obtain a hydrocarbon production system capable of appropriately securing hydrogen and carbon monoxide necessary for hydrocarbon synthesis, for example, in an electrolysis cell unit of a gas serving as a hydrogen source or a carbon monoxide source, and producing hydrocarbon using hydrogen and carbon monoxide generated in the above.
In a first characteristic configuration of an electrolysis cell unit according to the present invention,
there is provided an electrolysis cell unit including at least: an electrolysis cell in which an electrode layer and a counter electrode layer are formed with an electrolyte layer interposed therebetween; and a discharge path for discharging hydrogen generated in the electrode layer, in which the electrolysis cell is formed in a thin layer on a support and a reverse water-gas shift reaction unit that generates carbon monoxide using carbon dioxide and the hydrogen by a reverse water-gas shift reaction is provided in at least a portion of the discharge path.
This electrolysis cell unit includes the electrolysis cell, and when a current flows between the electrode layer and the counter electrode layer of the electrolysis cell, hydrogen is generated by an electrolysis reaction from a gas that is a hydrogen source. The generated hydrogen is released to the discharge path, but by making at least a portion of this discharge path the reverse water-gas shift reaction unit, it is possible to generate carbon monoxide using carbon dioxide flowing through the discharge path and hydrogen generated in the electrode layer. In this electrolysis cell unit, since a functional part as the electrolysis reaction unit and a functional part as the reverse water-gas shift reaction unit are configured as separate parts (the former is the electrolysis cell and the latter is the discharge path), by using an optimum material for each part and maintaining an appropriate temperature environment, as a result, carbon dioxide that cannot be sufficiently decomposed in the electrolysis reaction unit can be converted into carbon monoxide in the reverse water-gas shift reaction unit. Further, such an electrolysis reaction and a reverse water-gas shift reaction can be carried out in a single electrolysis cell unit. As will be described later, both reactions require relatively high temperatures, and thus, it is preferable to keep them in a single unit.
Further, the electrolysis cell according to the present invention is formed on the support in the form of a thin film, and thus, the electrolysis cell has a robust structure and yet exhibits sufficient capacity with high efficiency. In this respect, by making the electrolysis cell into a thin film, it is possible to suppress the internal resistance of the electrolysis cell and realize a high-performance electrolysis cell, and at the same time, reduce the amount of expensive cell material used and reduce the cost of the electrolysis cell.
In a second characteristic configuration of the present invention, the support is a metal.
By adopting a metal as the support, a material cost is suppressed by ensuring the strength with an inexpensive metal material, and workability is higher than that of ceramics, so that shape selectivity is high.
In a third characteristic configuration of the present invention,
a plurality of through holes penetrating the support are provided, the electrode layer is provided on one surface of the support, the discharge path is provided along the other surface thereof, and the reverse water-gas shift reaction unit is provided in at least a portion of an inner surface of the discharge path.
According to this characteristic configuration, the electrode layer can be provided on one surface of the support to realize hydrogen generation. The hydrogen generated in this way is guided from the electrode layer to the discharge path through the plurality of through holes and causes a good reaction in the reverse water-gas shift reaction unit provided in at least a portion of the discharge path, and when carbon dioxide is supplied, at least carbon monoxide can be generated.
In a fourth characteristic configuration of the present invention,
the reverse water-gas shift reaction unit is provided in at least a portion of an inside of the through hole.
According to this characteristic configuration, at least a portion of the through hole also functions as the reverse water-gas shift reaction unit.
In a fifth characteristic configuration of the present invention,
the reverse water-gas shift reaction unit is provided on a surface of the support different from a surface on which the electrolysis cell is formed.
According to this characteristic configuration, a function can be obtained as the reverse water-gas shift reaction unit on a different surface (for example, a surface opposite to the surface on which the electrolysis cell is formed) of the support.
In a sixth characteristic configuration of the present invention,
the electrolysis cell unit further includes a separator that separates hydrogen generated in the electrode layer and oxygen generated in the counter electrode layer, in which the reverse water-gas shift reaction unit is provided in at least a portion of the separator on a discharge path side of the hydrogen.
According to this characteristic configuration, when an electrolysis cell undergoes an electrolysis reaction, hydrogen is generated from the electrode layer and oxygen is generated from the counter electrode layer, but by providing the separator, the reverse water-gas shift reaction can be caused by using hydrogen and accompanying carbon dioxide in the reverse water-gas shift reaction unit.
In a seventh characteristic configuration of the present invention, the separator is a metal.
By adopting a metal as a separator, it is possible to suppress the material cost by ensuring gas separability with an inexpensive metal material. In addition, the metal is more workable than ceramics and has high shape selectivity.
In an eighth characteristic configuration of the present invention,
a reverse water-gas shift catalyst contained in the reverse water-gas shift reaction unit is a catalyst in which a metal or a metal oxide is supported on a carrier.
According to this characteristic configuration, the reverse water-gas shift reaction can be caused by the catalyst in which a metal or a metal oxide is supported on the carrier.
In a ninth characteristic configuration of the present invention,
a reverse water-gas shift catalyst contained in the reverse water-gas shift reaction unit is a catalyst containing at least one of platinum, nickel, and iron.
According to this characteristic configuration, it is possible to obtain a highly active reverse water-gas shift performance as described later.
In a tenth characteristic configuration of the present invention,
the carrier is a carrier containing a ceria-based metal oxide or a zirconia-based metal oxide as a main component.
According to this characteristic configuration, as will be described later, a highly active reverse water-gas shift performance can be obtained, and catalytic ability and durability can be obtained in a high-temperature environment required for a reverse water-gas shift reaction. Further, when the carrier is the carrier containing a ceria-based metal oxide or a zirconia-based metal oxide as a main component, a thermal expansion coefficient of the carrier can be close to that of a material used for a constituent material of the electrolysis cell or the support, so that the temperature is low. Accordingly, the electrolysis cell unit is not easily damaged even when a low temperature cycle and a high temperature cycle are repeated, and the electrolysis cell unit having excellent reliability and durability can be realized.
When obtaining the reverse water-gas shift catalyst, it is preferable to have at least a calcination step of performing calcination at a temperature of 450° C. or higher.
When the reverse water-gas shift catalyst is used, in order to cause a desired reverse water-gas shift reaction, it is necessary to set the reaction temperature range to a relatively high temperature range, but when the catalyst is obtained by calcination in this temperature range, the catalyst can be used stably. The temperature is preferably 450° C. or higher, but more preferably 600° C. or higher and 800° C. or higher because stability in a high temperature range can be improved. For example, the catalyst can be used stably even when combined with a solid oxide type electrolysis cell used in a relatively high temperature range (for example, 600° C. to 800° C.). Further, when the calcination temperature is set too high, a cost required for the calcination step becomes too high, and thus, an upper limit is about 1200° C.
When using a reverse water-gas shift catalyst, it is preferable that the reverse water-gas shift catalyst is subjected to a reduction pretreatment and then subjected to a reaction.
In many cases, at least a portion of the catalytically active component contained in the reverse water-gas shift catalyst is a metal oxide in the calcination step, but the reduction pretreatment (a treatment for performing a reduction treatment before use) is performed, and thus, the catalytically active component in an oxidized state is reduced and catalytic activity can be satisfactorily exhibited.
In a characteristic configuration of an electrolysis cell device according to the present invention,
there is provided an electrolysis cell device including at least: the electrolysis cell unit described above; an electrolysis raw material supply unit that supplies water and/or steam and carbon dioxide to the electrolysis cell unit; and a power supply unit that supplies electric power.
According to this characteristic configuration, an electrolysis raw material can be supplied from the electrolysis raw material supply unit to the electrolysis cell unit, electric power can be supplied from the power supply unit to the electrolysis cell, and thus, the electrolysis raw material can be electrolyzed by the electric power.
Here, for example, when the electrolysis raw material is water, hydrogen can be generated by the electrolysis, and when the electrolysis raw material is carbon dioxide, carbon monoxide is generated by the electrolysis. Further, in the electrolysis cell unit of the present invention, since the reverse water-gas shift reaction unit that generates carbon monoxide by using carbon dioxide and the hydrogen by the reverse water-gas shift reaction is provided in at least a portion of the discharge path, carbon monoxide can also be generated by the reaction in the discharge path.
In a characteristic configuration of a hydrocarbon production system according to the present invention,
there is provided a hydrocarbon production system including the electrolysis cell unit or the electrolysis cell device described above; and a hydrocarbon synthesis reaction unit that generates a hydrocarbon by at least reacting the hydrogen with the carbon monoxide.
According to this characteristic configuration, the electrolysis cell device described above can be used to synthesize hydrocarbons in the hydrocarbon synthesis reaction unit by receiving hydrogen and carbon monoxide from this device. Here, since the electrolysis cell unit or the electrolysis cell device according to the present invention is provided with at least the reverse water-gas shift reaction unit, carbon monoxide that may be insufficient in electrolysis in the electrolysis reaction unit can be supplemented by this reverse water-gas shift reaction unit, resulting in a compact and high-performance hydrocarbon production system.
In a characteristic configuration of a production method of an electrolysis cell unit according to the present invention,
the production method includes at least a calcination step of performing calcination at a temperature of 450° C. or higher in a step of forming the reverse water-gas shift reaction unit provided in this electrolysis cell unit.
The electrolysis cell unit according to the present invention includes an electrolysis cell in which an electrode layer, an electrolyte layer, and a counter electrode layer are formed, and is provided with the reverse water-gas shift reaction unit. A calcination operation is required to form the electrolysis cell and the reverse water-gas shift reaction unit, but the calcination steps required for the electrolysis cell and the reverse water-gas shift reaction unit can be performed at the same time. Further, it is preferable that the reverse water-gas shift reaction unit provided in the electrolysis cell unit operating in a relatively high temperature range includes a calcination step of performing calcination at a temperature of 450° C. or higher because the catalyst can be used stably. Further, it is more preferable that the calcination temperature is 600° C. or higher, and further preferably 800° C. or higher. In a case where such a calcination temperature is set, for example, even when the reverse water-gas shift reaction unit provided in the solid oxide type electrolysis cell unit operating in the temperature range of about 600° C. to 800° C. is used, in such a high temperature range, functions of the electrolysis cell and the reverse water-gas shift reaction unit can be stably operated for a long period of time. When the calcination temperature is too high, the cost of the calcination step becomes too high, and thus, an upper limit is about 1200° C.
In a characteristic configuration of a use method of an electrolysis cell unit according to the present invention,
the reverse water-gas shift reaction unit is used after being subjected to a reduction pretreatment.
As will be described later, in the catalyst suitable for the reverse water-gas shift reaction unit of the electrolysis cell unit according to the present invention, the active metal component thereof is an oxide in the state before use, and the reduction pretreatment is performed before use. Therefore, activity as the reverse water-gas shift catalyst can be enhanced.
An embodiment of the present invention will be described with reference to the drawings.
As illustrated in the figure, the hydrocarbon production system 100 includes an electrolysis reaction unit 10, a first catalytic reaction unit 20, a second catalytic reaction unit 30, a heavy hydrocarbon separation unit 35 (illustrated as a CnHm separation unit), a water separation unit 40 (illustrated as an H2O separation unit), and a carbon dioxide separation unit 50 (illustrated as a CO2 separation unit) in this order.
The electrolysis reaction unit 10 is a unit that electrolyzes at least a portion of an inflowing gas, the first catalytic reaction unit 20 is a reverse water-gas shift reaction unit that carries out a reverse water-gas shift reaction of at least a portion of the inflowing gas, and the second catalytic reaction unit 30 is configured to act as a hydrocarbon synthesis reaction unit that synthesizes at least a portion of the inflowing gas into hydrocarbon. Here, the hydrocarbon synthesized is mainly CH4 (hydrocarbon having one carbon atom), but also includes other lower saturated hydrocarbons having two to four carbon atoms and the like. Further, as will be illustrated later, by appropriately selecting a catalyst used for the second catalytic reaction unit 30, heavy hydrocarbons having a larger number of carbon atoms than the lower saturated hydrocarbons, unsaturated hydrocarbons, oxygen-containing hydrocarbons, or the like can also be synthesized. Therefore, in the present specification, the hydrocarbon is a concept including all of them, and is also collectively referred to as hydrocarbons.
The heavy hydrocarbon separation unit 35, the water separation unit 40, and the carbon dioxide separation unit 50 are units for removing at least a portion of predetermined components (CnHm, H2O, and CO2 in the order of description) from the gas flowing inside. As illustrated in
As a result, the hydrocarbon production system 100 is established as a carbon closed system that does not substantially release CO2 to the outside of the system.
In the drawings, the gas flowing into each unit is illustrated in front of each unit, and the gas released from the unit is illustrated after each unit.
In the electrolysis reaction unit 10, H2O and CO2 as starting materials flow in and are electrolyzed internally, H2O is decomposed into H2 and O2, and some CO2 is decomposed into CO and O2 and released.
The reaction is described as follows.
The formulas 1 and 2 are also illustrated in a box illustrating the electrolysis reaction unit 10 of
In the first catalytic reaction unit 20 (reverse water-gas shift reaction unit), H2 and CO2 flow in, a reverse water-gas shift reaction occurs inside, CO2 becomes CO, H2 becomes H2O, and CO and H2O are released.
The reaction is described as the following equilibrium reaction, but the reverse water-gas shift reaction is a reaction (reaction proceeding in a direction in which CO2 and H2 react to generate CO and H2O) in which the reaction described by the following formula 3 proceeds to the right.
This formula 3 is also illustrated in a box illustrating the first catalytic reaction unit 20 (reverse water-gas shift reaction unit) in
In the second catalytic reaction unit 30 (hydrocarbon synthesis reaction unit), H2 and CO flow in, and hydrocarbon is synthesized by a catalytic reaction. For example, the reaction in which CH4 is synthesized from CO and H2 is described as the following equilibrium reaction, but the reaction in which CH4 is synthesized from CO and H2 is a reaction (reaction proceeding in a direction in which CO and H2 react to generate CH4 and H2O) in which the reaction described by the following formula 4 proceeds to the right.
This formula 4 is also illustrated in a box illustrating the second catalytic reaction unit 30 (hydrocarbon synthesis reaction unit) in
Furthermore, the equilibrium reaction of (Formula 3) also occurs at this unit.
Further, depending on the type of catalyst used in the second catalytic reaction unit 30, it is possible to proceed with a Fischer-Tropsch (FT) synthesis reaction or the like. Therefore, various hydrocarbons such as ethane, propane, butane, pentane, hexane, paraffin, and olefinic hydrocarbons can be synthesized from CO and H2.
As will be described later, the inventors have illustrated an example of a catalyst using ruthenium as a catalytically active component of the hydrocarbon synthesis catalyst cat2 disposed in the second catalytic reaction unit 30, but heavy hydrocarbons are also synthesized in a catalyst containing iron, cobalt, or the like as the catalytically active component, and this type of heavy hydrocarbon can be condensed and separated from a transport gas as the temperature decreases. Therefore, the above-mentioned heavy hydrocarbon separation unit 35 separates the hydrocarbon component separated in this manner.
The generated H2O is separated in the water separation unit 40 and returned to the upstream side of the electrolysis reaction unit 10 via the water return path 41 (water recycle line).
The generated CO2 is separated in the carbon dioxide separation unit 50 and returned to the upstream side of the electrolysis reaction unit 10 via the carbon dioxide return path 51 (carbon dioxide recycle line).
As a result, in this hydrocarbon production system 100, the hydrocarbon is finally synthesized and can be supplied to the outside.
The above is the outline of the above-mentioned hydrocarbon production system 100, and a configuration of each unit and a role thereof will be described below.
As illustrated above, the electrolysis reaction unit 10 decomposes H2O and CO2 that flow in by consuming electric power supplied according to the above formulas 1 and 2.
The electrolyte layer 1a can be formed in the state of a thin film having a thickness of 10 µm or less. As a constituent material of the electrolyte layer 1a, YSZ (yttria-stabilized zirconia), SSZ (scandia-stabilized zirconia), GDC (gadolinium-doped ceria), YDC (yttrium-doped ceria), SDC (samarium-doped ceria), and LSGM (strontium/magnesium-added lanthanum gallate), or the like can be used. In particular, zirconia-based ceramics are preferably used.
Preferably, the electrolyte layer 1a is formed by a low-temperature calcination method (for example, a wet method using a calcination treatment in a low temperature range that does not carry out a calcination treatment in a high temperature range exceeding 1100° C.), a spray coating method (thermal spraying method, aerosol deposition method, aerosol gas deposition method, a powder jet deposition method, particle jet deposition method, cold spray method, or the like), a PVD method (sputtering method, a pulse laser deposition method, or the like), a CVD method, or the like. These film forming processes that can be used in a low temperature range provide an electrolyte layer 1a that is dense and has high gastightness and gas barrier properties without using calcination in a high temperature range exceeding, for example, 1100° C. Therefore, damage to the metal support 4 can be suppressed, element mutual diffusion between the metal support 4 and the electrode layer 2 can be suppressed, and an electrolysis cell unit U having excellent performance and durability can be realized. In particular, it is preferable to use the low-temperature calcination method, the spray coating method, or the like because a low-cost element can be realized. Further, it is more preferable to use the spray coating method because the electrolyte layer 1a, which is dense and has high gastightness and gas barrier property, can be easily obtained in a low temperature range.
Further, the electrolyte layer 1a is densely configured in order to prevent the gas leak and exhibit high ionic conductivity. A density of the electrolyte layer 1a is preferably 90% or more, more preferably 95% or more, and further preferably 98% or more. When the electrolyte layer 1a is a uniform layer, the density is preferably 95% or more, and more preferably 98% or more. When the electrolyte layer 1a includes a plurality of layers, it is preferable that at least a portion of the electrolyte layer 1a includes a layer (dense electrolyte layer) having a density of 98% or more, and it is more preferable to include a layer (dense electrolyte layer) having a density of 99% or more. In a case where the dense electrolyte layer is included in a portion of the electrolyte layer 1a, even when the electrolyte layer 1a includes a plurality of layers, it is possible to easily form the electrolyte layer 1a that is dense and has high gastightness and gas barrier property.
The electrode layer 2 can be provided in a thin layer on the front surface of the metal support 4 and in a region larger than a region where holes 4a are provided. In the case of a thin layer, a thickness thereof can be, for example, about 1 µm to 100 µm, preferably 5 µm to 50 µm. With such a thickness, it is possible to secure sufficient electrode performance while reducing the amount of expensive electrode layer material used to reduce costs. The entire region provided with the holes (through holes) 4a is covered with the electrode layer 2. That is, the hole 4a is formed inside the region of the metal support 4 where the electrode layer 2 is formed. In other words, all the holes 4a are provided facing the electrode layer 2.
As the constituent material of the electrode layer 2, for example, a composite material such as NiO—GDC, Ni—GDC, NiO—YSZ, Ni—YSZ, CuO—CeO2, Cu—CeO2 can be used. In these examples, GDC, YSZ, and CeO2 can be referred to as aggregates of the composite material. Preferably, the electrode layer 2 is formed by a low-temperature calcination method (for example, a wet method using a calcination treatment in a low temperature range that does not carry out a calcination treatment in a high temperature range exceeding 1100° C.), a spray coating method (thermal spraying method, aerosol deposition method, aerosol gas deposition method, a powder jet deposition method, particle jet deposition method, cold spray method, or the like), a PVD method (sputtering method, a pulse laser deposition method, or the like), a CVD method, or the like. These processes that can be used in the low temperature range provide an improved electrode layer 2 without using, for example, calcination in a high temperature range higher than 1100° C. Therefore, the metal support 4 is not damaged, element mutual diffusion between the metal support 4 and the electrode layer 2 can be suppressed, and an electrochemical element having excellent durability can be realized. Further, it is more preferable to use the low-temperature calcination method because the handling of the raw material becomes easy.
The counter electrode layer 3 can be formed in a thin layer on the surface of the electrolyte layer 1a opposite to the electrode layer 2. In the case of a thin layer, a thickness thereof can be, for example, about 1 µm to 100 µm, preferably 5 µm to 50 µm. With such a thickness, it is possible to secure sufficient electrode performance while reducing the amount of expensive counter electrode layer material used to reduce costs. As the material of the counter electrode layer 3, for example, a composite oxide such as LSCF or LSM, a ceria-based oxide, or a mixture thereof can be used. In particular, it is preferable that the counter electrode layer 3 contains a perovskite-type oxide containing two or more kinds of elements selected from the group consisting of La, Sr, Sm, Mn, Co, and Fe.
The electrolyte layer 1a, the electrode layer 2, and the counter electrode layer 3 are formed as a thin film as described later, and the inventor calls this thin layer forming.
As illustrated above, the electrolysis cell unit U has a metal support type, includes a metal support 4 as a support for the electrode layer 2, and a supply path forming member 5 for forming a U-shaped electrode layer-side gas supply path 5a is provided on a side opposite to the electrode layer 2 in a state where the metal support 4 is interposed therebetween. Further, the metal support 4 is provided with a large number of holes 4a penetrating the front and back surfaces. The gas (H2O and CO2) supplied through the electrode layer-side gas supply path 5a is subject to electrolysis and is supplied to the electrode layer 2 through a large number of holes 4a. Further, the generated gas (H2, CO) is discharged from the hole 4a.
Meanwhile, also on the counter electrode layer 3 side, a supply path forming member 6 for forming a counter electrode layer-side gas supply path 6a is provided. As illustrated in
The metal support 4 supports the electrode layer 2, the electrolyte layer 1a, and the counter electrode layer 3 and serves as a support for maintaining the strength of the electrolysis cell 1 and the electrolysis cell unit U as a whole. In this example, the plate-shaped metal support 4 is used as the metal support, but other shapes such as a box shape and a cylindrical shape are also possible.
The metal support 4 may have sufficient strength to form the electrolysis cell unit U as a support, and for example, can use a support having a thickness of about 0.1 mm to 2 mm, preferably about 0.1 mm to 1 mm, and more preferably about 0.1 mm to 0.5 mm. In the present embodiment, the support is made of metal, but ceramics can also be used, for example.
The metal support 4 has, for example, the plurality of holes 4a provided so as to penetrate the front surface and the back surface of the metal plate. For example, the hole 4a can be provided in the metal support 4 by mechanical, chemical, or optical drilling. The hole 4a has a function of allowing gas to pass from the back surface to the front surface of the metal support 4. The hole 4a may be provided so as to be inclined in a gas flow direction (the front and back directions of the paper surface in
By using a ferrite-based stainless steel material (an example of an Fe-Cr-based alloy) as a material of a base material of the metal support 4, a thermal expansion coefficient of the metal support 4 can be made close to those of YSZ (yttria-stabilized zirconia), GDC (gadolinium-doped ceria, also referred to as CGO), and the like used as materials for the electrode layer 2 and the electrolyte layer 1a. Therefore, the electrolysis cell unit U is less likely to be damaged even when the low temperature and high temperature cycles are repeated. Therefore, it is preferable because the electrolysis cell unit U having excellent long-term durability can be realized.
The same material as that of the metal support 4 can be used for the supply path forming members 5 and 6 of the electrolysis cell unit U, and the thickness thereof can be substantially the same.
Although the metal support 4 and both supply path forming members 5 and 6 have conductivity, they are gastightly configured to function as a separator for separating the supply paths 5a and 6a.
In the electrolysis cell unit U having the above configuration, in an electrolysis operation, DC power is supplied between the pair of electrode layers 2 and 3 provided with the electrolyte layer 1a interposed therebetween from a power supply unit (illustrated by a battery in
Then, H2O and CO2, which are gases to be electrolyzed, are supplied to the electrode layer 2 from an electrolysis raw material supply unit (upstream portion of the electrolysis reaction unit 10 in
The supplied gas (H2O, CO2) and the released gas (H2O, H2, CO, O2, CO2) in the electrolysis reaction are illustrated above and below the electrolysis cell unit U in
When H2O and CO2 are supplied to the electrolysis reaction unit 10 to carry out the electrolysis, H2O has a lower electrolysis voltage than CO2 and is easily electrolyzed. Therefore, when H2O and CO2 having the same amount are temporarily supplied to the electrolysis reaction unit 10 and the electrolysis reaction is carried out, the H2 concentration tends to be higher than the CO concentration at the outlet of the electrolysis reaction unit 10, and unreacted CO2 tends to remain.
As illustrated above, the first catalytic reaction unit 20 (reverse water-gas shift reaction unit) causes a reverse water-gas shift reaction, converts CO2 into CO using the supplied H2, and converts H2 into H2O. That is, in the electrolysis reaction unit 10 that supplies H2O and CO2 to electrolyze, the remaining CO2 that is not decomposed is converted into CO.
The reaction here is as illustrated by the formula 3, but this reaction is an endothermic reaction and is an equilibrium reaction according to the reaction temperature conditions. As a result, as described above, it is preferable that the catalyst is capable of causing the reaction represented by the formula 3 on the high temperature side (for example, 600° C. to 800° C.) as much as possible.
In the description of the catalyst in the present specification, a component having activity as a catalyst may be referred to as a “catalytically active component”, and a carrying body carrying the catalytically active component may be referred to as a “carrier (catalyst support)”.
The inventors examined various combinations of catalytically active components and carriers as described later, and found that a specific combination was suitable.
In a production of this type of catalyst, by executing an impregnation-supporting step of immersing the carrier in a solution containing a catalytically active component (metal), taking out the carrier, drying and heat-treating the carrier, it is possible to easily obtain a carrier-support catalyst (impregnated supported product) in which the catalytically active component is distributed on the surface of the carrier. This heat treatment is a calcination treatment. The preparation and use of the catalyst will be described with reference to
A preparation method described here is the same except that the starting material is different in the combination of various catalytically active components and carriers.
As illustrated in
In this case, as illustrated in the example of the reverse water-gas shift catalyst cat1 in
When the calcination treatment is carried out in air, the supported catalytically active components ca1 and ca2 are in a state where a part or all of them are oxidized. Before using the catalyst, a so-called reduction pretreatment may be carried out to reduce the catalytically active component in an oxidized state to sufficiently enhance the activity.
As the reverse water-gas shift catalyst cat1 used for the first catalytic reaction unit 20, the inventors have selected a catalyst that satisfies the following requirements.
A catalyst composed by supporting at least one or two of platinum, nickel, and iron as the catalytically active component ca1 on the carrier cb1 containing a ceria-based metal oxide or a zirconia-based metal oxide as a main component. Here, since the strength of the catalyst cat1 can be increased, a ratio of the carrier cb1 to the entire catalyst is preferably 55% by weight or more, more preferably 60% by weight or more, and further preferably 65% by weight or more. Further, an upper limit of this ratio can be, for example, 99.5% by weight, but when the upper limit is more than this, the catalytically active component ca1 cannot be sufficiently supported, and it may be difficult to obtain the effect as the reverse water-gas shift catalyst cat1.
Further, as the ceria-based metal oxide, ceria doped with at least one of gadolinium, samarium, and yttrium can also be used.
Further, as the zirconia-based metal oxide, zirconia stabilized by at least one of yttria and scandia can also be used.
Since the reverse water-gas shift reaction can proceed satisfactorily, a supported amount of the catalytically active component ca1 is preferably 0.5% by weight or more, more preferably 1% by weight or more, and further preferably 5% by weight or more. Further, when the supported amount of the catalytically active component ca1 is increased too much, it becomes difficult to support the catalytically active component ca1 in a high dispersion, it is difficult to obtain a significant improvement in the catalytic activity, and the catalyst cost also increases. Accordingly, the supported amount of the catalytically active component ca1 is preferably 35% by weight or less, more preferably 30% by weight or less, and further preferably 25% by weight or less.
Further, it is also preferable to add either one or two of platinum, nickel, and iron to the catalytically active component ca1 to support copper as a further catalytically active component ca1. In this configuration, the supported amount of copper is equal to or less than the supported amount of the catalytically active component ca1 with either one or both of nickel and iron as a main catalytically active component ca1.
Hereinafter, test results of Examples in the case where the catalytically active component ca1 and the carrier cb1 are variously changed as the reverse water-gas shift catalyst cat1 used for the first catalytic reaction unit 20 will be described.
As catalytically active components ca1, Ni and Fe were examined, and Pt (platinum) was also examined.
As the carrier cb1, Al2O3 (alumina) was also examined using ZrO2 (zirconia), YSZ (yttria-stabilized zirconia), GDC (gadolinium-doped ceria), and CeO2 (ceria) as examples.
In the following description, Test 1 and Test 2 will be introduced, but a difference between the two tests is that in the calcination of the reverse water-gas shift catalyst cat1, the calcination temperature of Test 1 is set to 450° C., and the calcination temperature of Test 2 is set to a high temperature side of 600° C. to 1000° C.
The test results of Examples (1 to 19) when the carrier is variously changed as the catalyst used for the first catalytic reaction unit 20 will be described.
As catalytically active components, Ni and Fe were examined, and Pt (platinum) was also examined.
As the carrier, ZrO2 (zirconia), YSZ (yttria-stabilized zirconia), GDC (gadolinium-doped ceria), and CeO2 (ceria) were used as examples, and Al2O3 (alumina) was also examined.
In preparing the reverse water-gas shift catalyst cat1, an aqueous solution is obtained by quantifying and dissolving any one or both of a water-soluble nickel compound (nickel nitrate, nickel chloride, nickel sulfate, nickel ammonium sulfate, nickel acetate, nickel oxalate, nickel citrate, or the like) and a water-soluble iron compound (iron nitrate, iron chloride, iron sulfate, ammonium iron sulfate, iron acetate, iron oxalate, iron citrate, or the like) according to the composition of the target catalyst. Further, when supporting copper as another catalytically active component ca1, an aqueous solution is obtained by similarly quantifying and dissolving a water-soluble copper compound (copper nitrate, copper chloride, copper sulfate, ammonium copper sulfate, copper acetate, copper oxalate, copper citrate, or the like). A predetermined amount of carrier powder (ceria, zirconia, GDC, YSZ, Al2O3) is added to the aqueous solution, stirred and impregnated, then evaporated to dryness, dried, then crushed and molded, and then calcinated in air. This impregnation is the “impregnation-supporting step” referred to in the present invention, and the result is the “impregnated supported product”.
The catalysts of the following examples were prepared using nickel nitrate hexahydrate, iron nitrate nonahydrate, and copper nitrate trihydrate, respectively. The catalyst using Pt was prepared using tetraammine platinum hydroxide.
In the above catalyst preparation, temperatures of evaporation to dryness, drying, and calcination could be carried out in a generally used temperature range, but in Test 1, the catalysts of the following examples were each at 80° C., 80° C., and 450° C.
Table 1 illustrates Examples 1 to 19 of the reverse water-gas shift catalyst cat1 in the present invention.
A horizontal axis represents the type of carrier cb1, a metal supported amount (% by weight; expressed as wt.% in the table) as the catalytically active component, a CO adsorption amount (ml/g), and a BET surface area (m2/g).
Regarding the CO adsorption amount, the CO adsorption amount was measured after the catalyst was subjected to a reduction pretreatment at 350° C. for 1 hour under a hydrogen atmosphere.
In the catalytic activity test, a mixed gas of 50% H2-50% CO2 (a mixed gas containing H2 and CO2 in a ratio of 1:1 (volume ratio)) was used as a reaction gas, and the reaction temperature was changed from 600° C. to 800° C. in increments of 50° C. under the conditions in which a Gas Hourly Space Velocity (GHSV) was 10000/h.
Before conducting the catalytic activity test, the reduction pretreatment of the catalyst was carried out at 600° C. while flowing a hydrogen gas through the catalyst layer.
As the test results, a CO2 conversion rate (%), a CO concentration (%) at the outlet of the reaction unit, and a CH4 concentration (%) are illustrated in Table 2.
The CO2 conversion rate (%) was calculated according to the following formula based on a gas analysis result at the outlet of the catalyst layer.
[CH4 concentration] + [CO concentration]/([CH4 concentration] + [CO concentration] + [CO2 concentration])
As illustrated above, in the reverse water-gas shift catalyst cat1 used in the first catalytic reaction unit 20 (reverse water-gas shift reaction unit), it is desirable that the CO2 conversion rate (%) on the high temperature side (for example, around 600 to 800° C.) is high.
Hereinafter, the test results of Examples (20 to 29) of Test 2 will be described. Even in this test,
Ni and Fe were examined as catalytically active components, and the addition of Cu was also examined.
As the carrier, CeO2 (ceria) and ZrO2 (zirconia) are used as examples, and Al2O3 (alumina) is also examined.
The reverse water-gas shift catalyst cat1 used in Test 2 was prepared in the same manner as in Test 1 except that the calcination temperatures were changed to 600° C., 800° C., and 1000° C.
Table 3 illustrates the catalyst of each of Examples (20 to 29) prepared.
In the catalytic activity test, a mixed gas containing H2 and CO2 in a ratio of 1:1 (volume ratio) was used as a reaction gas, and the reaction temperature was changed from 600° C. to 800° C. in increments of 50° C. under the conditions in which GHSV was 10000/h.
Before conducting the catalytic activity test, the reduction pretreatment of the catalyst was carried out at 600° C. while flowing a hydrogen gas through the catalyst layer.
As the test results, the CO2 conversion rate (%), the CO concentration (%) at the outlet of the reaction unit, and the CH4 concentration (%) are illustrated in Table 4.
For reference, an equilibrium value (calculated value) of the CO2 conversion rate under the experimental conditions is illustrated in Table 4.
For the iron/zirconia catalyst, the test results when the calcination temperatures are 450° C., 600° C., 800° C., and 1000° C. are illustrated in Example 8, Example 22, Example 26, and Example 29, respectively. Meanwhile, for the iron/alumina catalyst, the test results when the calcination temperatures are 450° C., 600° C., and 800° C. are illustrated in Example 14, Example 23, and Example 27, respectively. As can be seen from these results, although the metal supported amount is slightly different, the iron/zirconia catalyst is superior to the iron/alumina catalyst in the activity in carrying out the reverse water-gas shift reaction. Further, the iron/zirconia catalyst has extremely high catalytic activity not only when the calcination temperature is 450° C. but also when the calcination temperature is as high as 600° C., 800° C., and 1000° C., and regardless of the calcination temperature, the CO2 conversion rate of the iron/zirconia catalyst reaches the vicinity of the equilibrium value.
The test results when the calcination temperatures are 450° C., 600° C., 800° C., and 1000° C. are illustrated in Example 4, Example 20, Example 24, and Example 28, respectively. As can be seen from these results, the nickel/ceria catalyst has extremely high catalytic activity not only when the calcination temperature is 450° C. but also when the calcination temperature is as high as 600° C., 800° C., and 1000° C., and regardless of the calcination temperature, the CO2 conversion rate of nickel/ceria catalyst reaches the vicinity of the equilibrium value.
Example 7 illustrates the test results when the calcination temperature is 450° C. As a result, the nickel/alumina catalyst had a lower CO2 conversion rate than the nickel/ceria catalyst described above.
The test results when the calcination temperatures are 450° C., 600° C., and 800° C. are illustrated in Example 6, Example 21, and Example 25, respectively. From these results, it can be seen that the CO2 conversion rate of the nickel/copper/ceria catalysts tends to decrease slightly when the calcination temperature thereof is as high as 600° C. or 800° C., but the calcination temperature conditions described above are superior to those of the similar iron/alumina catalyst. Further, in the nickel/copper/ceria catalyst having the calcination temperature of 450° C., the CO2 conversion rate reaches the vicinity of the equilibrium value.
As illustrated above, the iron/zirconia-based catalysts and the nickel/ceria-based catalysts exhibit extremely high reverse water-gas shift catalytic activity even when the calcination temperature is variously changed to 450° C. to 1000° C., and thus, for example, even when used in combination with a solid oxide type electrolysis cell used in a high temperature range of around 600° C. to 800° C., it is easy to secure high performance and durability, which is useful.
From the above results, as illustrated above, as the reverse water-gas shift catalyst cat1 used for the first catalytic reaction unit 20, the catalyst obtained by supporting at least one or both of nickel and iron as the catalytically active component ca1 on the carrier cb1 containing the ceria-based metal oxide or the zirconia-based metal oxide as a main component can be used. Furthermore, platinum can also be used when the cost is acceptable.
Further, as the ceria-based metal oxide as the carrier cb1, ceria doped with at least one of gadolinium, samarium, and yttrium can also be used.
Further, the zirconia-based metal oxide as the carrier cb1 can be zirconia stabilized by at least one of yttria and scandia.
Further, it is also preferable to add either one or both of nickel and iron to the catalytically active component ca1 to support copper as a further catalytically active component ca1.
By using the reverse water-gas shift catalyst cat1 in the first catalytic reaction unit 20 (reverse water-gas shift reaction unit), the reverse water-gas shift reaction can be carried out at around 600 to 1000° C. with the CO2 conversion rate (%) equal to or higher than that of the Pt catalyst, which is highly active but very expensive.
Since the test of this example was carried out under a very high GHSV condition of 10000/h, by reducing the GHSV to less than 10000/h, that is, by increasing the amount of catalyst used with respect to the amount of gas to be treated, it is possible to carry out the reverse water-gas shift reaction at a higher CO2 conversion rate (%).
In the description so far, according to the system configuration illustrated in
The reaction of the electrolysis reaction unit 10 is an exothermic reaction depending on the reaction conditions, and the reaction of the reverse water-gas shift reaction unit 20 is an endothermic reaction. Therefore, thermal efficiency of the system can be improved by integrating the two reaction units 10 and 20. In this way,
Based on the above concept, it is preferable to provide the reverse water-gas shift reaction unit 20 in the electrolysis cell unit U which is the electrolysis reaction unit 10. This is because when a solid oxide type electrolysis cell that operates at around 600 to 800° C. is used as the electrolysis cell 1, in the reverse water-gas shift catalyst cat1 of the present application which can obtain high activity at around 600 to 800° C., the electrolysis reaction unit 10 and the reverse water-gas shift reaction unit 20 can be used in the same temperature range.
In this case as well, it is sufficient that the gas that has passed through the electrolysis reaction unit 10 is guided to the reverse water-gas shift reaction unit 20 to generate the reverse water-gas shift reaction.
As illustrated in
That is, the electrolysis cell unit U also includes the electrolysis cell 1 in which the electrode layer 2 and the counter electrode layer 3 are formed with the electrolyte layer 1a interposed therebetween, the metal support 4 which functions as a support thereof and also acts as a separator, and the supply path forming members 5 and 6, and the electrode layer-side gas supply path 5a and the counter electrode layer-side gas supply path 6a are formed in the electrolysis cell unit U. More specifically, as can be seen from
However, in this example, the reverse water-gas shift catalyst cat1 described above is applied to an inner surface (supply path-side inner surface of supply path forming member 5, surface of the metal support 4 opposite to surface on which electrode layer 2 is formed, and surfaces of the plurality of holes 4a) of the electrode layer-side gas supply path 5a. A coating layer 20a is illustrated by a thick solid line.
Further, the electrode layer-side gas supply path 5a extends beyond the electrolysis reaction unit 10, and the coating layer 20a is also provided on the extension side.
As a result, the electrode layer-side gas supply path 5a of the electrolysis cell unit U is a discharge path for discharging at least H2 generated in the electrode layer 2, and the electrolysis cell unit U is integrally provided with the electrolysis reaction unit 10 and the reverse water-gas shift reaction unit 20.
In this configuration, the metal support 4 acts as a separator that separates H2 generated in the electrode layer 2 and O2 generated in the counter electrode layer 3, and at least a portion of the separator on the discharge path side of H2 is reverse water-gas shift reaction unit 20.
By stacking the electrolysis cell units U configured in this way in a right-left direction of
The inventors have stored a granular reverse water-gas shift catalyst cat1 in the electrode layer-side gas supply path 5a and conducted an experiment under a concept in which the electrolysis reaction unit 10 and the reverse water-gas shift reaction unit 20 are combined with each other (the electrode layer-side gas supply path 5a of the electrolysis reaction unit 10 is the reverse water-gas shift reaction unit 20).
Hereinafter, a specific description will be given with reference to
Here, as the electrolysis cell 1, a metal-supported solid oxide type electrolysis cell was used. As the metal support 4, a metal substrate was prepared by providing a plurality of through holes (which become holes 4a) by applying laser processing to a ferritic stainless steel metal plate having a thickness of 0.3 mm. The electrode layer 2 and an intermediate layer 2a were laminated in this order on the metal substrate, and the electrolyte layer 1a was laminated on the intermediate layer 2a of the metal substrate so as to cover the intermediate layer 2a. Further, a reaction prevention layer 7 and the counter electrode layer 3 were sequentially laminated on the electrolyte layer 1a to prepare the electrolysis cell 1. A mixture of NiO powder and GDC powder was used as the material for forming the electrode layer 2, GDC powder was used as the material for forming the intermediate layer 2a, 8YSZ (8 mol% yttria-stabilized zirconia) powder was used as the material for forming the electrolyte layer 1a, GDC powder was used as the material for forming the reaction prevention layer 7, and a mixture of and GDC powder and LSCF powder was used as the material for forming the counter electrode layer 3. Further, the thicknesses of the electrode layer 2, the intermediate layer 2a, the electrolyte layer 1a, the reaction prevention layer 7, and the counter electrode layer 3 were about 25 µm, about 10 µm, about 5 µm, about 5 µm, and about 20 µm, respectively. By providing the intermediate layer 2a between the electrode layer 2 and the electrolyte layer 1a and providing the reaction prevention layer 7 between the electrolyte layer 1a and the counter electrode layer 3, the performance and durability of the electrolysis cell 1 can be improved. Moreover, preferably, the intermediate layer 2a and the reaction prevention layer 7 are formed by a low-temperature calcination method (for example, a wet method using a calcination treatment in a low temperature range that does not carry out a calcination treatment in a high temperature range exceeding 1100° C.), a spray coating method (thermal spraying method, aerosol deposition method, aerosol gas deposition method, a powder jet deposition method, particle jet deposition method, cold spray method, or the like), a PVD method (sputtering method, a pulse laser deposition method, or the like), a CVD method, or the like. These processes that can be used in the low temperature range provide the improved intermediate layer 2a and reaction prevention layer 7 without using, for example, calcination in a high temperature range higher than 1100° C. Therefore, it is preferable because the electrolysis cell 1 having excellent performance and durability can be realized without damaging the metal support 4. Further, it is more preferable to use the low-temperature calcination method because the handling of the raw material becomes easy.
Regarding the electrolysis cell unit U obtained as described above, the performance improvement in the case where the reverse water-gas shift catalyst cat1 formed in the form of particles was stored in the electrode layer-side gas supply path 5a (which also serves as the discharge path of the gas electrolyzed by the electrolysis reaction unit 10) was examined.
An electrolysis reaction was carried out while supplying a gas containing H2O and CO2 to the electrolysis cell unit U, and a ratio of H2 to CO of an outlet gas of the electrolysis cell unit U was measured using a gas chromatograph. The results are illustrated in Table 5 below. The experimental results are described as Comparative Examples A1 and A2.
As the reverse water-gas shift catalyst cat1, a granular catalyst obtained by supporting about 10% of Ni on the 8YSZ carrier similar to in Example 2 was stored, an electrolysis reaction was carried out while supplying a gas containing H2O and CO2 to the electrolysis cell unit U, and the ratio of H2 to CO of the outlet gas of the electrolysis cell unit U was measured using a gas chromatograph. The results are illustrated in Table 6. The experimental result is described as Example A1.
By the above comparative experiment, in the electrolysis cell unit U in which the electrolysis cell 1 was formed in a thin layer on the metal support 4, and the reverse water-gas shift reaction unit 20 generating CO by using CO2 and H2 by the reverse water-gas shift reaction was provided in the electrode layer-side gas supply path 5a which was the discharge path of the electrolyzed gas, it was possible to increase a composition ratio of CO to H2 generated by electrolysis.
In the comparison between the electrolysis cell unit U in which the reverse water-gas shift catalyst cat1 is not stored in the electrode layer-side gas supply path 5a (which is the discharge path for the electrolyzed gas) and the electrolysis cell unit U in which the reverse water-gas shift catalyst cat1 is stored, the hydrogen/carbon monoxide ([H2/CO]) ratio changes from about 10 or more to about 5 at the outlet, and by combining the reaction of the electrolysis reaction unit 10 and the reaction of the reverse water-gas shift reaction unit 20, the amount of CO that is advantageous for various hydrocarbon syntheses can be secured, which is preferable. In addition, since thermal efficiency of the hydrocarbon production system 100 can be improved by adopting a methanation reaction of CO rather than a methanation reaction of CO2, by combining the reaction of the electrolysis reaction unit 10 and the reaction of the reverse water-gas shift reaction unit 20, the amount of CO can be secured, which is preferable. This is because 2 mol of H2O is generated when 1 mol of CO2 is methanized, whereas 1 mol of H2O is generated when 1 mol of CO is methanized, and thus, the hydrocarbon production system 100 that employs the methanation reaction of CO can suppress latent heat and sensible heat loss of 1 mol of H2O as a whole system.
By appropriately adjusting the ratio of H2O and CO2 introduced into the electrolysis reaction unit 10, the reaction conditions (electrolysis voltage, reaction temperature, or the like) of the electrolysis reaction unit 10, the reaction conditions (amount of catalyst used, GHSV, reaction temperature, or the like) of the reverse water-gas shift reaction unit 20, or the like, the hydrogen/carbon monoxide ([H2/CO]) ratio at the outlet of the reverse water-gas shift reaction unit 20 can be adjusted to a value (for example, H2/CO = 3 which is the equivalent ratio of the methanation reaction of CO, or the like) suitable for the second catalytic reaction unit 30 (hydrocarbon synthesis reaction unit) in the subsequent stage.
In the descriptions so far, the example in which the electrolysis reaction unit 10 and the first catalytic reaction unit (reverse water-gas shift reaction unit) 20 are integrated has been mainly described, however, it is possible to adopt a configuration in which heat exchanger 11 is provided between both units 10 and 20 so that heat can be exchanged between both units. For example, in the structure of
The inventors have called the system including the electrolysis reaction unit 10 and the reverse water-gas shift reaction unit 20 described so far as an “electrolysis reaction system”.
At least H2 and CO flow into the second catalytic reaction unit 30 (hydrocarbon synthesis reaction unit), and hydrocarbons (methane and various hydrocarbons having two or more carbon atoms) and the like are generated by the catalytic reaction.
As an activity test of the catalyst (hydrocarbon synthesis catalyst cat2) used in the second catalytic reaction unit 30, the inventors conducted the following evaluation test 1, evaluation test 2, and evaluation test 3.
As an example of the hydrocarbon synthesis catalyst cat2, a catalyst was prepared by variously changing the carrier and the catalytically active component. As the catalytically active component ca2, those obtained by adding Mo, V, Fe, Co, and the like to Ru and Ru, and Ni were examined. As the carrier cb2, ZrO2, Al2O3, SiO2, MgO, and TiO2 were examined.
The preparation of the hydrocarbon synthesis catalyst cat2 is also the method adopted as described with reference to
That is, a water-soluble ruthenium compound (ruthenium nitrate, ruthenium chloride, ruthenium sulfate, ruthenium ammonium sulfate, ruthenium acetate, ruthenium oxalate, ruthenium citrate, or the like) is quantified and dissolved according to the composition of the target catalyst to obtain an aqueous solution. Further, when molybdenum, vanadium, iron, and cobalt are supported as further catalytically active components, these water-soluble metal compounds are similarly quantified to obtain a dissolved aqueous solution. Using the aqueous solution, for example, by impregnating and supporting the catalytically active component on carrier particles (ZrO2, Al2O3, SiO2, MgO, TiO2) having a predetermined amount, and carrying out necessary treatment steps such as a drying treatment, a calcination treatment, and a reduction treatment, the hydrocarbon synthesis catalyst cat2 can be obtained.
Using ruthenium chloride aqueous solution, ammonium molybdate aqueous solution, vanadyl oxalate aqueous solution, iron nitrate aqueous solution, and cobalt nitrate aqueous solution, respectively, and when both ruthenium and catalytically active components other than ruthenium are supported, the catalysts of the following examples were prepared using a sequential carrier method (a two-step carrier method in which a catalytically active component other than ruthenium is first supported on a carrier and then ruthenium is supported).
In the evaluation test 1, a mixed gas containing 12.4% CO, 24.8% CO2, 37.2% H2, 12.4% H2O and the balance being N2 was used as the reaction gas, GHSV was set to 4000/h (WET base), and the activity test of the hydrocarbon synthesis catalyst cat2 was carried out at a reaction temperature of 275° C. to 360° C. In this case, the reaction gas is an example obtained by assuming a model in which a co-electrolysis reaction between water and carbon dioxide in the electrolysis reaction unit 10 is carried out under the conditions that an electrolysis reaction rate of carbon dioxide is low, and a mixed gas of CO, CO2, H2, and H2O after the reverse water-gas shift reaction of carbon dioxide is carried out in the reverse water-gas shift reaction unit 20 installed in the subsequent stage is introduced into the hydrocarbon synthesis reaction unit 30 to carry out the hydrocarbon synthesis reaction.
The following two indicators were adopted when organizing the test results.
1. CO2 removal assumed hydrocarbon conversion rate = [number of carbons in hydrocarbons in outlet gas]/[number of carbons in outlet gas - number of carbons in outlet CO2]
This indicator is an indicator illustrating the conversion rate to hydrocarbons when CO2 is removed from the outlet gas of the hydrocarbon synthesis reaction unit 30 obtained by the catalytic reaction, and it is preferable that this indicator is high.
2. C1-C4 calorific value (MJ/Nm3) = ∑(Nn × HN)/∑Nn
This indicator is an indicator illustrating amounts of C1 to C4 components contained in the outlet gas of the hydrocarbon synthesis reaction unit 30 obtained by the catalytic reaction, and when this value exceeds 39.8, it can be confirmed that hydrocarbons such as ethane, propane, and butane are generated in addition to methane.
Regarding the evaluation test 1, Tables 7 and 8 illustrated below illustrate Examples B1 to B3 of the hydrocarbon synthesis catalyst cat2 in the present invention.
As illustrated in Tables 7 and 8, it was confirmed that hydrocarbons could be synthesized using a catalyst in which ruthenium was supported on an alumina carrier or a catalyst in which molybdenum or vanadium was supported in addition to ruthenium as a hydrocarbon synthesis catalyst cat2 from the mixed gas of CO, CO2, H2, and H2O.
From the above results, it was confirmed that the above-mentioned hydrocarbon production system 100 could generate a high-calorie gas having a C1-C4 calorific value of 39 MJ/Nm3 or more.
In the evaluation test 2, a mixed gas containing 0.45% CO, 18.0% CO2, 71.55% H2, and 10.0% H2O was used as the reaction gas, GHSV was set to 5000/h (DRY base), and the activity test of the hydrocarbon synthesis catalyst cat2 was carried out at a reaction temperature of about 230° C. to about 330° C. In this case, the reaction gas is an example obtained by assuming a model in which the mixed gas obtained when the co-electrolysis reaction of water and carbon dioxide is carried out in the electrolysis reaction unit 10 under the conditions that the electrolysis reaction rate of carbon dioxide is low is introduced into the hydrocarbon synthesis reaction unit 30 to carry out a hydrocarbon synthesis reaction.
The following two indicators were adopted when organizing the test results.
1. hydrocarbon conversion rate = [number of carbons in hydrocarbons in outlet gas]/[number of carbons in outlet gas]
This indicator is an indicator illustrating the ratio of the number of carbons converted into hydrocarbons without being converted into CO2 among the total carbons flowing in, and it is preferable that this indicator is high.
2. CO2 removal assumed hydrocarbon conversion rate = [number of carbons in hydrocarbons in outlet gas]/[number of carbons in outlet gas - number of carbons in outlet CO2]
This indicator is an indicator illustrating the conversion rate to hydrocarbons when CO2 is removed from the outlet gas of the hydrocarbon synthesis reaction unit obtained by the catalytic reaction, and it is preferable that this indicator is also high.
For the evaluation test 2, the used catalysts (Examples B4 to B16) are illustrated in Table 9, and the test results are illustrated in Table 10.
In the evaluation test 3, a mixed gas (H2/CO = 3) containing H2 and CO in a ratio of 3:1 (volume ratio) was used as the reaction gas, the GHSV was set to 4000/h, and the activity test of the hydrocarbon synthesis catalyst cat2 was carried out at the reaction temperature of 235° C. to about 330° C. In this activity test, a catalyst (Examples B17 and B18) in which iron or cobalt was supported on a titania carrier in addition to ruthenium was used. In this case, the reaction gas is an example obtained by assuming a model in which a mixed gas obtained by adding carbon monoxide to hydrogen obtained by electrolyzing water in the electrolysis reaction unit 10, and a mixed gas of hydrogen and carbon monoxide obtained by separating water and carbon dioxide as needed from the gas obtained by carrying out a co-electrolysis reaction of water and carbon dioxide are introduced into the hydrocarbon synthesis reaction unit 30 to carry out the hydrocarbon synthesis reaction.
The results of the evaluation test 3 are illustrated in Table 11.
As illustrated in Table 11, it was confirmed that hydrocarbons can be synthesized from a mixed gas containing H2 and CO using a catalyst in which ruthenium and iron or cobalt are supported on a titania carrier as a hydrocarbon synthesis catalyst cat2.
It was confirmed that the above-mentioned hydrocarbon production system 100 can generate a high-calorie gas having a C1-C4 calorific value of 39 MJ/Nm3 or more.
From the above results, as illustrated above, a catalyst in which at least ruthenium is supported as the catalytically active component ca2 on the metal oxide carrier cb2 can be used in the second catalytic reaction unit 30 (hydrocarbon synthesis reaction unit). Further, it is preferable to support at least one of molybdenum, vanadium, iron, and cobalt as the catalytically active component ca2.
It was found that, preferably, the hydrocarbon synthesis catalyst cat2 was a catalyst in which at least ruthenium was supported on the metal oxide carrier cb2, the supported amount of ruthenium was 0.1% by weight or more and 5% by weight or less, and at least one of molybdenum, vanadium, iron, and cobalt as the catalytically active component ca2 was supported on the metal oxide carrier cb2 in addition to ruthenium.
Here, the supported amount of at least one of the molybdenum, vanadium, iron, and cobalt can be 0.2% by weight or more and 6% by weight or less.
Further, in hydrocarbon synthesis catalysts cat2, the adsorption amount of carbon monoxide of the highly active catalyst was 0.4 ml/g or more.
When the gas reaching the heavy hydrocarbon separation unit 35 is cooled, the heavy hydrocarbons contained in the gas released from the hydrocarbon synthesis reaction unit 30 are condensed and the heavy hydrocarbons can be taken out to the outside. For example, in the hydrocarbon synthesis reaction unit 30 using the 2 wt.% Ru/2 wt.% Fe/TiO2 catalyst illustrated in Example B17, when a mixed gas (H2/CO = 3) containing H2 and CO in a ratio of 3:1 (volume ratio) was introduced and the reaction was carried out at 275° C., a linear higher aliphatic hydrocarbon having an average chain length of 26 carbon atoms could be extracted from the heavy hydrocarbon separation unit 35. Moreover, when the reaction was carried out at 325° C., a linear higher aliphatic hydrocarbon having an average chain length of 18 carbon atoms could be extracted from the heavy hydrocarbon separation unit 35.
A condenser is arranged in the water separation unit 40, and the gas containing H2O flowing in is adjusted to a predetermined temperature and pressure to be condensed and water is taken out to the outside.
For example, PSA is arranged in this unit 50, and the gas containing CO2 flowing in is adsorbed to the adsorbent under a predetermined temperature and pressure to separate CO2, the separated CO2 is separated from the adsorbent, and thus, CO2 is favorably separated. The separated CO2 can be returned to the front of the electrolysis reaction unit 10 and reused via the carbon dioxide return path 51.
It is also possible to use PSA or the like to make the carbon dioxide separation unit and the water separation unit the same separation unit.
(1) In the above embodiment, CO2 separated in the carbon dioxide separation unit 50 is returned to the front of the electrolysis reaction unit 10. However, in the hydrocarbon production system 100 according to the present invention, since the conversion of CO2 to CO is mainly performed by the reverse water-gas shift reaction unit 20, a return destination of CO2 may be in front of the reverse water-gas shift reaction unit 20. This configuration is illustrated in
(2) In the above embodiment, H2 in the gas obtained from the hydrocarbon synthesis reaction unit 30 is not particularly described. However, a hydrogen separation unit (described as H2 separation unit in the drawing) 60 that separates H2 using a hydrogen separation membrane or the like may be provided to separate H2 and use H2 separately. This configuration is illustrated in
(3) In the above embodiment, the water separation unit 40 is provided on the lower side of the hydrocarbon synthesis reaction unit 30. However, as illustrated in
(4) In the above embodiment, an example in which both H2O and CO2 are supplied to the electrolysis reaction unit 10 and subjected to the electrolysis reaction is illustrated. However, as illustrated in
(5) In the above embodiment, an example in which a solid oxide type electrolysis cell is used as the electrolysis cell 1 in the electrolysis reaction unit 10 is illustrated. However, as the electrolysis cell 1, an alkaline type electrolysis cell, a polymer film type electrolysis cell, or the like may be used.
(6) In the above embodiment, the electrolysis reaction unit 10 and the first catalytic reaction unit 20 are integrated. However, in addition to the reaction units 10.20, the second catalytic reaction unit 30 may be integrated. A configuration example in this case is illustrated in
Also, in the case of this configuration, each of the reaction units 10, 20, and 30 can be configured on the metal support 4 and the supply path forming member 5, and the metal support 4 is supposed to act as a separator for separating the generated hydrocarbon and oxygen.
(7) In the above embodiment, an example of synthesizing a hydrocarbon such as methane in the hydrocarbon synthesis reaction unit 30 is illustrated. However, depending on how the hydrocarbon synthesis catalyst used in the hydrocarbon synthesis reaction unit 30 is selected, it is also possible to synthesize a chemical raw material from hydrogen and carbon monoxide introduced into the hydrocarbon synthesis reaction unit 30.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2020-065258 | Mar 2020 | JP | national |
This application is the U.S. National Phase of International Application No. PCT/JP2021/014084 filed Mar. 31, 2021, and claims priority to Japanese Patent Application No. 2021-065258 filed Mar. 31, 2020, the disclosures of which are hereby incorporated by reference in their entirety.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2021/014084 | 3/31/2021 | WO |