Patent Application
20200176198
The present disclosure relates generally to electrochemistry, and, more specifically, zinc metal plating and stripping.
The following paragraphs are not an admission that anything discussed in them is prior art or part of the knowledge of persons skilled in the art.
Metallic zinc negative electrodes are used in many primary and secondary aqueous battery types. Zinc has a high abundance and large production which makes it inexpensive; it is non-toxic; has a low redox potential (−0.76 V vs. standard hydrogen electrode (SHE)) compared to other negative electrode materials used in aqueous batteries; and is stable in water due to a high overpotential for hydrogen evolution.
One drawback and challenge for secondary batteries using zinc negative electrodes is the formation of dendritic or mossy deposits which can build up during repeated cycling and cause premature cell failure by internal short circuits.
The deposition (plating) of zinc metal is an important industrial process. Zinc plating is used for corrosion protection and both aqueous and non-aqueous battery electrolytes (or plating baths) have been applied to this process, yet aqueous electrolytes can be more attractive due for practical and economic reasons. The smooth deposition of zinc is important for uniform coverage of metal substrates for good corrosion protection. Uniform deposition can be controlled not only by optimizing the plating bath composition, but also by controlling other parameters such as temperature, current density, and mechanical agitation (flow or stirring) of the bath.
The reversible zinc plating/stripping occurs in rechargeable batteries using zinc metal negative electrodes. Compared to the zinc plating process where only deposition occurs, volumetric changes during the plating/stripping cycling of zinc metal battery electrodes can lead to problems including internal short circuiting by penetration of zinc metal through the separator and contact with the positive electrode. In addition to the necessity to consider both plating and stripping mechanisms in a battery, during practical cycling, parameters such as current density and temperature cannot be controlled as easily and stirring the electrolyte is typically impossible. On the other hand, lessons can be learned from traditional zinc plating bath compositions to optimize for good cycling of the zinc electrode in rechargeable batteries.
Acidic sulfate and chloride plating baths have been historically used with the addition of so-called brighteners to provide a shiny finish of zinc metal on other metals. Chloride baths have the advantage of higher ionic conductivities and better dissolution of the zinc anode compared to their sulfate counterparts. However, the chloride anion should be avoided in batteries because it is quite corrosive and can dissolve other components of the battery during operation as well as lead to the risk of chlorine evolution at the positive electrode. For these reasons, the sulfate anion is preferred for acidic aqueous rechargeable zinc metal batteries. Zinc sulfate has the advantages of being relatively inexpensive, non-corrosive, and has a wide stability voltage window.
Many traditional aqueous batteries using zinc metal electrodes, such as alkaline batteries and zinc-carbon batteries, use alkaline electrolytes. Commonly, in alkaline electrolytes, a dendritic morphology of zinc deposits is observed. Dendrites are particularly problematic because of the high surface area and ease of penetration through separators. In addition to dendrite growth, the low coulombic efficiency (CE) of zinc metal plating/stripping is also a major challenge. This has inhibited these primary (non-rechargeable) battery types from being recharged. Many new battery chemistries including zinc-air batteries, zinc-ion batteries, zinc hybrid supercapacitors, zinc-bromide batteries, zinc-iodide batteries, zinc-iron redox flow batteries, and zinc-cerium redox flow batteries can use acidic electrolytes rather than alkaline electrolytes.
The following is intended to introduce the reader to the detailed description that follows and not to define or limit the claimed subject matter.
In an aspect of the present disclosure, an apparatus for a rechargeable battery can include: a negative electrode including zinc; and an electrolyte for transferring ions between the negative electrode and a positive electrode, the electrolyte including zinc sulfate dissolved in water with a pH in the range of 0-7, and at least one additive. The at least one additive can be selected to at least one of (i) increase ionic conductivity of the electrolyte, (ii) buffer the pH of the electrolyte, and (iii) control morphology of a stripped/plated surface of the negative electrode.
The at least one additive can include at least one salt that increases the ionic conductivity of the electrolyte. The at least one salt can include at least one of (i) a salt with zinc cations, (ii) a salt with sulfate anions, (iii) a salt with alkali metal, alkaline earth metal, magnesium, aluminum, tetra alkyl ammonium or ammonium cations, and (iv) a salt with perchlorate, chloride, nitrate, phosphate, acetate, or citrate anions. The at least one salt can be present in the electrolyte in a range from about 0.05 M to about 6 M.
The at least one additive can include at least one buffering agent that buffers the pH of the electrolyte. The at least one buffering agent can include at least one of borates, acetates, phosphates, citrates, phthalates, salicylic acid, and benzoic acid. The at least one buffering agent can be present in the electrolyte in a range from about 0.005 M to about 6 M.
The at least one additive can include at least one control additive that smooths the stripped/plated surface of the negative electrode. The at least one control additive can include at least one chemical functional group of alkyl, alkenyl, alkynyl, phenyl, amine, hydroxyl, ether, thiol, aldehyde, ketone, ester, carboxyl, amide, borate, carbonate, siloxyl, halo, imine, and imide. The at least one control additive can be present in the electrolyte in a range from about 10 ppm to about 50 percent.
The zinc sulfate can be dissolved so that Zn2+ ions are present in the electrolyte in a range from about 0.05 M to about 4 M. The pH of the electrolyte can be between about 4 and about 6.
The negative electrode can be formed substantially of zinc metal. The negative electrode can be formed substantially of a zinc alloy. The negative electrode can include a current collector, and the current collector can include an active surface that is formed substantially of a layer of zinc. The layer of zinc can include powdered zinc metal. The layer of zinc can include a sheet of zinc metal. The current collector can be formed substantially of a material selected from the group consisting of carbon, boron, lead, vanadium, chromium, manganese, iron, cobalt, nickel, cadmium, tungsten, bismuth, tin, indium, antimony, copper, titanium, zinc metal, and any combination thereof.
The apparatus can be used in the operation of an aqueous rechargeable battery, in which the electrolyte is static and contained between the positive and negative electrodes, or is flowed therebetween. The battery can take the form of a zinc-air battery, a zinc-ion battery, a zinc hybrid supercapacitor, a zinc-bromide battery, a zinc-iodide battery, a zinc-iron redox flow battery, or a zinc-cerium redox flow battery.
In an aspect of the present disclosure, a method can include: providing a negative electrode including zinc; dissolving zinc sulfate in water to provide an electrolyte with a pH in the range of 0-7 for transferring ions between the negative electrode and a positive electrode; and adding at least one additive to the electrolyte. The at least one additive can be selected to at least one of (i) increase ionic conductivity of the electrolyte, (ii) buffer the pH of the electrolyte, and (iii) control morphology of a stripped/plated surface of the negative electrode.
At least one salt can be added to increase the ionic conductivity of the electrolyte, the at least one salt including at least one of (i) a salt with zinc cations, (ii) a salt with sulfate anions, (iii) a salt with alkali metal, alkaline earth metal, magnesium, aluminum, tetra alkyl ammonium or ammonium cations, and (iv) a salt with perchlorate, chloride, nitrate, phosphate, acetate, or citrate anions. The at least one salt can be added to the electrolyte in a range from about 0.05 M to about 6 M.
At least one buffering agent can be added to buffer the pH of the electrolyte, the at least one buffering agent including at least one of borates, acetates, phosphates, citrates, phthalates, salicylic acid, and benzoic acid. The at least one buffering agent can be added to the electrolyte in a range from about 0.005 M to about 6 M.
At least one control additive can be added to smooth the stripped/plated surface of the negative electrode, the at least one control additive including at least one chemical functional group of alkyl, alkenyl, alkynyl, phenyl, amine, hydroxyl, ether, thiol, aldehyde, ketone, ester, carboxyl, amide, borate, carbonate, siloxyl, halo, imine, and imide. The at least one control additive can be added to the electrolyte in a range from about 10 ppm to about 50 percent.
The zinc sulfate can be dissolved so that Zn2+ ions are present in the electrolyte in a range from about 0.05 M to about 4 M. The pH of the electrolyte can be maintained between about 4 and about 6.
The negative electrode and the electrolyte can be operated in an aqueous rechargeable battery, in which the electrolyte is static and contained between the positive and negative electrodes, or is flowed therebetween. The battery can take the form of a zinc-air battery, a zinc-ion battery, a zinc hybrid supercapacitor, a zinc-bromide battery, a zinc-iodide battery, a zinc-iron redox flow battery, or a zinc-cerium redox flow battery.
In an aspect of the present disclosure, an aqueous electrolyte for use in a rechargeable battery can include zinc sulfate dissolved in water with a pH in the range of 0-7, and at least one additive. The at least one additive can be selected to at least one of (i) increase ionic conductivity of the electrolyte, (ii) buffer the pH of the electrolyte, and (iii) control morphology of a stripped/plated surface of a negative electrode of the rechargeable battery.
The at least one additive can include at least one salt that increases the ionic conductivity of the electrolyte, the at least one salt including at least one of (i) a salt with zinc cations, (ii) a salt with sulfate anions, (iii) a salt with alkali metal, alkaline earth metal, magnesium, aluminum, tetra alkyl ammonium or ammonium cations, and (iv) a salt with perchlorate, chloride, nitrate, phosphate, acetate, or citrate anions. The at least one salt can be present in the electrolyte in a range from about 0.05 M to about 6 M.
The at least one additive can include at least one buffering agent that buffers the pH of the electrolyte, the at least one buffering agent including at least one of borates, acetates, phosphates, citrates, phthalates, salicylic acid, and benzoic acid. The at least one buffering agent can be present in the electrolyte in a range from about 0.005 M to about 6 M.
The at least one additive can include at least one control additive to smooth the stripped/plated surface of the negative electrode, the at least one control additive comprising at least one chemical functional group of alkyl, alkenyl, alkynyl, phenyl, amine, hydroxyl, ether, thiol, aldehyde, ketone, ester, carboxyl, amide, borate, carbonate, siloxyl, halo, imine, and imide. The at least one control additive can be present in the electrolyte in a range from about 10 ppm to about 50 percent.
The zinc sulfate can be dissolved so that Zn2+ ions are present in the electrolyte in a range from about 0.05 M to about 4 M. The pH of the electrolyte can be between about 4 and about 6.
Other aspects and features of the teachings disclosed herein will become apparent, to those ordinarily skilled in the art, upon review of the following description of the specific examples of the present disclosure.
The drawings included herewith are for illustrating various examples of apparatuses and methods of the present disclosure and are not intended to limit the scope of what is taught in any way. In the drawings:
Various apparatuses or methods will be described below to provide an example of an embodiment of each claimed invention. No embodiment described below limits any claimed invention and any claimed invention may cover apparatuses and methods that differ from those described below. The claimed inventions are not limited to apparatuses and methods having all of the features of any one apparatus or method described below, or to features common to multiple or all of the apparatuses or methods described below. It is possible that an apparatus or method described below is not an embodiment of any claimed invention. Any invention disclosed in an apparatus or method described below that is not claimed in this document may be the subject matter of another protective instrument, for example, a continuing patent application, and the applicant(s), inventor(s) and/or owner(s) do not intend to abandon, disclaim or dedicate to the public any such invention by its disclosure in this document.
The present disclosure relates generally to improving the cycle life of batteries having zinc metal negative electrodes. In particular, it has been determined that additives can be used to control the zinc morphology to extend the cycle life of secondary aqueous batteries by decreasing the likelihood of internal short circuits.
Additives to the base electrolyte were tested. Many were found to decrease the cycle life rather than increase it with a different mechanism than internal short-circuiting.
In addition to Zn∥Zn symmetric cells, Zn∥Ti cells were also used to test the cycle life of zinc metal in different electrolytes and determine the coulombic efficiency (CE). An example of the cycling a Zn∥Ti cell is displayed in
During charge of a battery at the negative electrode, the desired zinc deposition reaction is shown below in reactions 1 and 2/3, depending on the pH. In the acidic pH range (pH<7, reaction 1), the oxidation (dissolution) product is soluble Zn2+. In alkaline electrolytes (pH>7, reactions 2 and 3), Zn2+ precipitates in the form of insulating ZnO. The zincate ion (Zn(OH)42−) is slightly soluble in high concentrations of hydroxide (OH−) and is in equilibrium with ZnO. This dissolution/precipitation mechanism in alkaline electrolytes leads to passivation of active zinc metal in the electrode, decreasing the CE and exacerbating dendrite growth. The simple mechanism in acidic electrolytes is preferred for reversibility of the zinc electrode and high CE. High CE is important for long-term cycling of batteries with a low excess of zinc metal. Inactive zinc (low CE) results in the need to use a large excess of zinc metal in order to ensure that there is enough active zinc to be cycled. The hydrogen evolution reaction (HER) is competitive to zinc deposition during charge and is also pH dependent (see reactions 4 and 5 below) and catalytic in nature, the precise potential at which they occur is sensitive to the electrolyte composition and electrode or current collector material. HER is more severe at low pH than high pH according to reactions 4 and 5 and this can also lead to lower CE.
Cathodic Reactions:
Zinc Deposition:
Zn2++2e−→Zn E°=−0.76V vs. SHE (1)
Zn(OH)42−+2e−→Zn+4OH− (2)
ZnO+H2O+2OH−↔Zn(OH)42− (3)
Hydrogen Evolution Reaction (HER):
2H++2e−→H2E°=0.00V vs. SHE (4)
2H2O+2e−→H2+2OH−E°=0.00V vs. SHE (5)
The pH dependence on the reversibility of the zinc electrode was examined using Zn∥Ti cells. Zinc metal was deposited onto the Ti electrode substrate at 1 mA/cm2 to a capacity of 1 mAh/cm2, then stripped to an upper voltage cut-off of 0.7 V. The electrolytes examined were [1 M ZnSO4+1 M H2SO4] in water (acidic, pH=0), [1 M ZnSO4+0.1 M H2SO4] in water (acidic, pH=3), 1 M ZnSO4 in water (slightly acidic, pH=5), and [6 M KOH saturated with ZnO] in water (alkaline, pH=14).
Moving forward with the preferred pH electrolyte containing only ZnSO4, different concentrations of the sulfate salt were tested (
Rather than relying only on the base salt of ZnSO4 to reach maximum ionic conductivity, additional salts can be added. In example 2, a small amount of ammonium sulfate (0.1 M) to 1 M ZnSO4 increased the ionic conductivity from 44.8 mS/cm for 1 M ZnSO4 only to 57.1 mS/cm. This increase in ionic conductivity led to an increase in the number of cycles achieved in Zn∥Ti cells from 59 to 93.
In example 3, the effect of a buffering agent (boric acid) and a brightener (ethylene glycol) were examined. When 90 vol. % water and 10 vol. % ethylene glycol was used as the solvent for 1 M ZnSO4 instead of pure water, the number of cycles increased to 82. When using H3BO3 in addition to ethylene glycol, the number of cycles was increased to 351. This suggests that ethylene glycol breaks down during cycling and changes the pH. The buffer agent can prevent the detrimental pH change.
Other brighteners for sulfate plating baths were tested as control additives in example 4. Nicotinamide, SDS, and ethylvanillin all improved the cycling performance of the cells. However, it can be seen that not all of these compounds increased the cycle life. Some (CTAB and furfural) were actually detrimental and decreased the number of cycles (similar to PVP in
More examples of selected beneficial additives which can extend the cycle life of the 1 M ZnSO4/H2O electrolyte are shown in
In summary, electrolyte formulas were examined for batteries using zinc metal negative electrolytes. The Coulombic efficiency of zinc plating/stripping can be highest and the cycling can be most stable for electrolytes which have a near neutral pH. In electrolytes with a near neutral pH, the zinc metal electrode undergoes morphology changes and volumetric expansion after repeated cycling which can lead to internal short-circuits of battery cells. The likelihood of cell failure by internal short circuits was examined using accelerated lifetime tests of Zn∥Zn symmetric cells at high current densities (10 mA/cm2 or 50 mA/cm2) and/or high cycling capacities (5 mAh/cm2) and also using Zn∥Ti cells by plating zinc onto a Ti and subsequently stripping it from the Ti. Additives to ZnSO4/H2O electrolytes which increase the ionic conductivity and/or buffer the pH and/or act as brighteners to smooth the zinc surface were found to be effective in extending the number of cycles before internal short-circuits occurred.
The following paragraphs describe the experimental methods used herein.
The morphologies of the zinc electrodes were examined by field-emission scanning electron microscopy (FE-SEM, LEO 1530).
The cycling behavior of Zn∥Zn symmetric cells were investigated in PFA based Swagelok® type cell using titanium rods as the current collectors. For all cells, two pieces of glass fiber membranes (Millipore, AP-40, 475 μm thick) were used as the separator. Zinc foil (250 μm thick, 99%, McMaster Carr) was punched into 1 cm2 disks and served as the zinc electrodes for the symmetric cells. Galvanostatic cycling studies were performed using multichannel biologic VMP3 potentiostat/galvanostat at room temperature (22±3° C.).
Test cells of Zn∥Ti format were constructed from titanium plates sandwiched between acrylic plates with a rubber gasket for sealing. For all cells, one piece of glass fiber membrane (Whatman glass microfiber filter) was used as the separator. Zinc foil (250 μm thick, 99%, McMaster Carr) was cut into 5.5 cm×5.5 cm squares (30.25 cm2) and served as the negative electrodes. A square plate of Ti (McMaster Carr) cut to 4 cm×4 cm (16 cm2) served as the positive electrode substrate for zinc deposition and dissolution. Zinc was deposited onto the Ti plate at 1 mA/cm2 to a capacity of 1 mAh/cm2, then it was stripped to an upper voltage cut-off of 0.7 V. The coulombic efficiency (CE) was calculated as the charge passed for stripping over the charge passed for deposition (1 mAh/cm2). Galvanostatic cycling studies were performed using Landt battery testing station (CT2001A) at room temperature (22±3° C.).
The standard electrolyte consisted of 1 M ZnSO4 (in the form of ZnSO4.7H2O) dissolved in deionized water. All chemicals were purchased from Sigma-Aldrich and used as received. The various additives tested were boric acid (H3BO3), ethylene glycol, ethyl vanillin, polyvinylpyrrolidone (PVP, Avg. Mn=8000 g/mol), Pluronic P-123 surfactant, polyethylene glycol (PEG-4600, Avg. Mn=4600 g/mol), polyethylene glycol (PEG-600, Avg. Mn=600 g/mol), potassium pyrophosphate (K2P4O7), Triton X-100 surfactant, 2-chlorobenzaldehyde, dodecylamine, tetrabutylammonium sulfate, jeffamine M-600, jeffamine ED-600, glycine, thiourea, polyvinylalcohol (PVA), polyethyleneimine (PEI), zinc citrate, dextrin, cetyltrimethylammonium bromide (CTAB), sodium dodecyl sulfate (SDS), nicotinamide, ammonium sulfate ((NH4)2SO4), and furfural. The additives were dissolved in the 1 M ZnSO4 electrolyte in various quantities.
For the pH studies, potassium hydroxide (KOH), zinc oxide (ZnO), and sulfuric acid (H2SO4) were purchased from Sigma-Aldrich and used to prepare the electrolytes in addition to ZnSO4.7H2O. The pH was roughly measured with pH paper only.
Ionic conductivities were measured using an Oakton PC 700 conductivity meter.
While the above description provides examples of one or more apparatuses or methods, it will be appreciated that other apparatuses or methods may be within the scope of the accompanying claims.
This application claims priority to U.S. Provisional Application No. 62/492,446 filed on May 1, 2017, the entire contents of which are hereby incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CA2018/050510 | 5/1/2018 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62492446 | May 2017 | US |