Patent Grant
9972866
This application claims priority to and the benefit of Korean Patent Application No. 10-2014-0195962, filed on Dec. 31, 2014, in the Korean Intellectual Property Office, the content of which is incorporated herein in its entirety by reference.
1. Field
The present disclosure relates to an electrolyte for a lithium secondary battery and a lithium secondary battery including the electrolyte, and more particularly, to an electrolyte for a lithium secondary battery including an organic ester compound having a plurality of ester groups, and a lithium secondary battery including the electrolyte.
2. Description of the Related Art
Recently, lithium secondary batteries have drawn significant attention as power sources for small portable electronic devices. Lithium batteries using an organic electrolyte have greater energy density and a discharge voltage about twice that of batteries using an aqueous alkali electrolyte.
In lithium batteries, lithium-transition metal oxides, such as LiCoO2, LiMn2O4, LiNi1-xCoxO2 (wherein 0<x<1), which have a structure that allows intercalation of lithium ions, are mainly used as cathode active materials. Various forms of carbonaceous materials, including artificial graphite, natural graphite, hard carbon, or a combination thereof, which allow intercalation and deintercalation of lithium ions, have been used as anode active materials.
A carbonate-based solvent is widely used as an electrolyte solvent of a lithium secondary battery. However, the conventional carbonate-based solvent may degrade characteristics of the lithium secondary battery over its lifetime when used together with a high-voltage cathode.
Provided is an electrolyte for a lithium secondary battery, the electrolyte including an organic ester compound having a plurality of ester groups.
Provided is a lithium secondary battery including the electrolyte.
Additional aspects will be set forth in part in the description which follows and, in part, will be apparent from the description, or may be learned by practice of the presented exemplary embodiments.
According to an aspect of an exemplary embodiment, an electrolyte for a lithium secondary battery includes:
an organic ester compound represented by Formula 1;
an organic solvent; and
a lithium salt:
wherein, in Formula 1, R1, R2, and R3 are the same or different, and each independently a group represented by Formula 2:
wherein, in Formula 2, R′ is a C1-C10 alkyl group or a C3-C10 cycloalkyl group.
In Formula 2, R′ may be a branched C3-C10 alkyl group.
The organic ester compound may include triacetin, tripropionin, tributyrin, 3-(propionyloxy)propane-1,2-diyl diacetate, 3-(butyryloxy)propane-1,2-diyl diacetate, 3-(pentanoyloxy)propane-1,2-diyl diacetate, 3-(isobutyryloxy)propane-1,2-diyl diacetate, 3-((2-methylbutanoyl)oxy) propane-1,2-diyl diacetate, 3-((3-methylbutanoyl)oxy) propane-1,2-diyl diacetate, 3-acetoxypropane-1,2-diyl dipropionate, 3-(butyryloxy)propane-1,2-diyl dipropionate, 3-(isobutyryloxy)propane-1,2-diyl dipropionate, 3-((2-methylbutanoyl)oxy)propane-1,2-diyl dipropionate, 3-((3-methylbutanoyl)oxy)propane-1,2-diyl dipropionate, 3-acetoxy propane-1,2-diyl dibutyrate, 3-(propionyloxy)propane-1,2-diyl dibutyrate, 3-(pentanoyloxy)propane-1,2-diyl dibutyrate, 3-(isobutyryloxy)propane-1,2-diyl dibutyrate, 3-((2-methylbutanoyl)oxy)propane-1,2-diyl dibutyrate, 3-((3-methylbutanoyl)oxy)propane-1,2-diyl dibutyrate, 3-acetoxypropane-1,2-diyl dipentanoate, 3-(butyryloxy)propane-1,2-diyl dipentanoate, 3-(propionyloxy)propane-1,2-diyl dipentanoate, 3-(isobutyryloxy)propane-1,2-diyl dipentanoate, 3-((2-methylbutanoyl)oxy)propane-1,2-diyl dipentanoate, 3-((3-methylbutanoyl)oxy)propane-1,2-diyl dipentanoate, 2-(pentanoyloxy)propane-1,3-diyl diacetate, 2-(propionyloxy)propane-1,3-diyl diacetate, 2-(butyryloxy)propane-1,3-diyl diacetate, 2-(isobutyryloxy)propane-1,3-diyl diacetate, 2-((3-methylbutanoyl)oxy)propane-1,3-diyl diacetate, 2-((2-methylbutanoyl)oxy)propane-1,3-diyl diacetate, 2-acetoxypropane-1,3-diyl dipropionate, 2-(pentanoyloxy)propane-1,3-diyl dipropionate, 2-(butyryloxy)propane-1,3-diyl dipropionate, 2-(isobutyryloxy)propane-1,3-diyl dipropionate, 2-((3-methylbutanoyl)oxy)propane-1,3-diyl dipropionate, 2-((2-methylbutanoyl)oxy)propane-1,3-diyl dipropionate, 2-acetoxypropane-1,3-diyl dibutyrate, 2-(propionyloxy)propane-1,3-diyl dibutyrate, 2-(butyryloxy)propane-1,3-diyl dibutyrate, 2-(isobutyryloxy)propane-1,3-diyl dibutyrate, 2-((3-methylbutanoyl)oxy)propane-1,3-diyl dibutyrate, 2-((2-methylbutanoyl)oxy)propane-1,3-diyl dibutyrate, 2-acetoxypropane-1,3-diyl dipentanoate, 2-(propionyloxy)propane-1,3-diyl dipentanoate, 2-(butyryloxy)propane-1,3-diyl dipentanoate, 2-(isobutyryloxy)propane-1,3-diyl dipentanoate, 2-((3-methylbutanoyl)oxy)propane-1,3-diyl dipentanoate, 2-((2-methylbutanoyl)oxy)propane-1,3-diyl dipentanoate, or a combination thereof.
The organic ester compound may have a boiling point of about 150° C. or greater.
The amount of the organic ester compound may be from about 10 percent by weight (wt %) to about 70 wt % based on a total weight of the electrolyte. In some embodiments, the amount of the organic ester compound may be from about 12 wt % to about 45 wt % based on the total weight of the electrolyte.
An anion of the lithium salt may include F−, Cl−, Br−, I−, NO3−, N(CN)2−, BF4−, ClO4−, PF6−, (CF3)2PF4−, (CF3)3PF3−, (CF3)4PF2−, (CF3)5PF−, (CF3)6P−, CF3SO3−, CF3CF2SO3−, CF3SO2)2N−, (FSO2)2N−, CF3CF2(CF3)2CO−, (CF3SO2)2CH−, (SF5)3C−, (CF3SO2)3C−, CF3(CF2)7SO3−, CF3CO2−, CH3CO2−, SCN−, (CF3CF2SO2)2N−, or a combination thereof.
A concentration of the lithium salt may be from about 0.6 moles per liter of the solution (M) to about 2.0 M.
The organic solvent of the electrolyte may be any organic solvents in common use for electrolytes of lithium secondary batteries in the art. For example, the organic solvent may be an ether solvent, an ester solvent, an amide solvent, a linear carbonate solvent, or a cyclic carbonate solvent, which may be used alone or in combination of at least two thereof.
According to an aspect of another exemplary embodiment, a lithium secondary battery includes:
a cathode,
an anode, and
an electrolyte according to any one of the above-described embodiments, disposed between the cathode and the anode.
The anode may have a film formed on a surface thereof, wherein the film may be derived from an organic ester compound represented by Formula 1 as described above.
These and/or other aspects will become apparent and more readily appreciated from the following description of the exemplary embodiments, taken in conjunction with the accompanying drawings in which:
Reference will now be made in detail to exemplary embodiments, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to like elements throughout. In this regard, the present exemplary embodiments may have different forms and should not be construed as being limited to the descriptions set forth herein. Accordingly, the exemplary embodiments are merely described below, by referring to the figures, to explain aspects. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. Expressions such as “at least one of,” when preceding a list of elements, modify the entire list of elements and do not modify the individual elements of the list.
It will be understood that when an element is referred to as being “on” another element, it can be directly in contact with the other element or intervening elements may be present therebetween. In contrast, when an element is referred to as being “directly on” another element, there are no intervening elements present.
It will be understood that, although the terms first, second, third etc. may be used herein to describe various elements, components, regions, layers, and/or sections, these elements, components, regions, layers, and/or sections should not be limited by these terms. These terms are only used to distinguish one element, component, region, layer, or section from another element, component, region, layer, or section. Thus, a first element, component, region, layer, or section discussed below could be termed a second element, component, region, layer, or section without departing from the teachings of the present embodiments.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting. As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise.
The term “or” means “and/or.” It will be further understood that the terms “comprises” and/or “comprising,” or “includes” and/or “including” when used in this specification, specify the presence of stated features, regions, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, regions, integers, steps, operations, elements, components, and/or groups thereof.
Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this general inventive concept belongs. It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and the present disclosure, and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.
Exemplary embodiments are described herein with reference to cross section illustrations that are schematic illustrations of idealized embodiments. As such, variations from the shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances, are to be expected. Thus, embodiments described herein should not be construed as limited to the particular shapes of regions as illustrated herein but are to include deviations in shapes that result, for example, from manufacturing. For example, a region illustrated or described as flat may, typically, have rough and/or nonlinear features. Moreover, sharp angles that are illustrated may be rounded. Thus, the regions illustrated in the figures are schematic in nature and their shapes are not intended to illustrate the precise shape of a region and are not intended to limit the scope of the present claims.
“About” or “approximately” as used herein is inclusive of the stated value and means within an acceptable range of deviation for the particular value as determined by one of ordinary skill in the art, considering the measurement in question and the error associated with measurement of the particular quantity (i.e., the limitations of the measurement system). For example, “about” can mean within one or more standard deviations, or within ±30%, 20%, 10%, 5% of the stated value.
As used herein, the term “alkyl group” refers to a completely saturated, branched or unbranched (or a straight or linear) hydrocarbon group.
Non-limiting examples of the “alkyl group” include a methyl group, an ethyl group, an n-propyl group, an iso-propyl group, an n-butyl group, an iso-butyl group, a sec-butyl group, an n-pentyl group, an iso-pentyl group, a neo-pentyl group, an iso-amyl group, an n-hexyl group, a 3-methylhexyl group, a 2,2-dimethylpentyl group, a 2,3-dimethylpentyl group, and an n-heptyl group.
As used herein, the term “substituted alkyl group” refers to an alkyl group in which a hydrogen atom is substituted with a non-hydrogen substituent (a halogen atom, a C1-C6 alkyl group, a C3-C6 cycloalkyl group, a C1-C6 alkoxy group, a C6-C10 aryl group, an oxygen atom, a sulfur atom, a nitrogen atom, and the like).
As used herein, the term “cycloalkyl group” refers to a monovalent group having one or more saturated or partially saturated rings in which all ring members are carbon.
Non-limiting examples of the “cycloalkyl group” include a cyclopropyl group, a cyclopropylmethyl group, a cyclobutyl group, a cyclobutyl group, a cyclopentyl group, a cyclopentenyl group, a cyclohexyl group, a cyclohexenyl group, a cycloheptyl group, a cycloheptenyl group, a cyclooctyl group, a cyclooctenyl group, and an adamantyl group.
As used herein, the term “substituted cycloalkyl group” refers to a cycloalkyl group in which a hydrogen atom is substituted with a non-hydrogen substituent (a halogen atom, a C1-C6 alkyl group, a C3-C6 cycloalkyl group, a C1-C6 alkoxy group, a C6-C10 aryl group, an oxygen atom, a sulfur atom, a nitrogen atom, and the like).
As used herein, the term “aryl group” refers to a group having at least one aromatic ring in which all ring members are carbon.
Non-limiting examples of the “aryl group” include a phenyl group and a naphthyl group.
When a group containing a specified number of carbon atoms is substituted with any of the groups listed in the preceding paragraphs, the number of carbon atoms in the resulting “substituted” group is defined as the sum of the carbon atoms contained in the original (unsubstituted) group and the carbon atoms (if any) contained in the substituent. For example, when the term “substituted C1-C10 alkyl” refers to a C1-C10 alkyl group substituted with C6-C10 aryl group, the total number of carbon atoms in the resulting aryl substituted alkyl group is C7-C20.
As used herein, the term “halogen atom” refers to a fluorine atom, a bromine atom, a chlorine atom, or an iodine atom.
As used herein, the term “discharging” refers to a deintercalation process of lithium ions from an anode, and the term “charging” refers to an intercalation process of lithium ions into the anode.
Hereinafter, embodiments of an electrolyte for a lithium battery and a lithium secondary battery including the electrolyte will be described in greater detail.
According to an aspect of the present disclosure, an electrolyte for a lithium secondary battery includes:
an organic ester compound represented by Formula 1,
an organic solvent, and
a lithium salt.
In Formula 1, R1, R2, and R3 may be the same or different (i.e., any two or three of R1, R2, and R3 may be the same or different), and may be each independently a group represented by Formula 2:
In Formula 2, R′ may be a substituted or unsubstituted C1-C10 alkyl group or a substituted or unsubstituted C1-C10 cycloalkyl group.
For example, in Formula 2, R′ may be a substituted or unsubstituted branched C3-C10 alkyl group.
The organic ester compound may have a smaller viscosity and a lower melting point compared to a conventional carbonate-based solvent, and is suitable for use as an electrolyte solvent. The organic ester compound may have a higher dielectric constant compared to the conventional carbonate-based solvent. The organic ester compound is added to the electrolyte to be subjected to decomposition reaction on a surface of the anode and form a stable solid electrolyte interface (SEI) membrane with low resistance at an interface between the anode and the electrolyte, and thus may improve stability of the lithium secondary battery.
The organic ester compound may include triacetin, tripropionin, tributyrin, 3-(propionyloxy)propane-1,2-diyl diacetate, 3-(butyryloxy)propane-1,2-diyl diacetate, 3-(pentanoyloxy)propane-1,2-diyl diacetate, 3-(isobutyryloxy)propane-1,2-diyl diacetate, 3-((2-methylbutanoyl)oxy) propane-1,2-diyl diacetate, 3-((3-methylbutanoyl)oxy) propane-1,2-diyl diacetate, 3-acetoxypropane-1,2-diyl dipropionate, 3-(butyryloxy)propane-1,2-diyl dipropionate, 3-(isobutyryloxy)propane-1,2-diyl dipropionate, 3-((2-methylbutanoyl)oxy)propane-1,2-diyl dipropionate, 3-((3-methylbutanoyl)oxy)propane-1,2-diyl dipropionate, 3-acetoxy propane-1,2-diyl dibutyrate, 3-(propionyloxy)propane-1,2-diyl dibutyrate, 3-(pentanoyloxy)propane-1,2-diyl dibutyrate, 3-(isobutyryloxy)propane-1,2-diyl dibutyrate, 3-((2-methylbutanoyl)oxy)propane-1,2-diyl dibutyrate, 3-((3-methylbutanoyl)oxy)propane-1,2-diyl dibutyrate, 3-acetoxypropane-1,2-diyl dipentanoate, 3-(butyryloxy)propane-1,2-diyl dipentanoate, 3-(propionyloxy)propane-1,2-diyl dipentanoate, 3-(isobutyryloxy)propane-1,2-diyl dipentanoate, 3-((2-methylbutanoyl)oxy)propane-1,2-diyl dipentanoate, 3-((3-methylbutanoyl)oxy)propane-1,2-diyl dipentanoate, 2-(pentanoyloxy)propane-1,3-diyl diacetate, 2-(propionyloxy)propane-1,3-diyl diacetate, 2-(butyryloxy)propane-1,3-diyl diacetate, 2-(isobutyryloxy)propane-1,3-diyl diacetate, 2-((3-methylbutanoyl)oxy)propane-1,3-diyl diacetate, 2-((2-methylbutanoyl)oxy)propane-1,3-diyl diacetate, 2-acetoxypropane-1,3-diyl dipropionate, 2-(pentanoyloxy)propane-1,3-diyl dipropionate, 2-(butyryloxy)propane-1,3-diyl dipropionate, 2-(isobutyryloxy)propane-1,3-diyl dipropionate, 2-((3-methylbutanoyl)oxy)propane-1,3-diyl dipropionate, 2-((2-methylbutanoyl)oxy)propane-1,3-diyl dipropionate, 2-acetoxypropane-1,3-diyl dibutyrate, 2-(propionyloxy)propane-1,3-diyl dibutyrate, 2-(butyryloxy)propane-1,3-diyl dibutyrate, 2-(isobutyryloxy)propane-1,3-diyl dibutyrate, 2-((3-methylbutanoyl)oxy)propane-1,3-diyl dibutyrate, 2-((2-methylbutanoyl)oxy)propane-1,3-diyl dibutyrate, 2-acetoxypropane-1,3-diyl dipentanoate, 2-(propionyloxy)propane-1,3-diyl dipentanoate, 2-(butyryloxy)propane-1,3-diyl dipentanoate, 2-(isobutyryloxy)propane-1,3-diyl dipentanoate, 2-((3-methylbutanoyl)oxy)propane-1,3-diyl dipentanoate, 2-((2-methylbutanoyl)oxy)propane-1,3-diyl dipentanoate, or a combination thereof.
The organic ester compound may have a boiling point of about 150° C. or greater. While not wishing to be bound by theory, it is understood that when the organic ester compound has a boiling point within this range, gasification of the organic ester compound during operation of the lithium secondary battery may be prevented.
The amount of the organic ester compound may be from about 10 percent by weight (wt %) to about 70 wt % based on a total weight of the electrolyte. While not wishing to be bound by theory, it is understood that when the amount of the organic ester compound is within this range, a lithium secondary battery with improved capacity and lifetime characteristics may be obtained. For example, the amount of the organic ester compound may be about 12 wt % to about 45 wt % based on the total weight of the electrolyte.
A concentration of the lithium salt may be from about 0.6 molar (M) to about 2.0 M, and in some embodiments, from about 0.7 M to about 1.6 M. While not wishing to be bound by theory, it is understood that when the concentration of the lithium salt is within these ranges (0.6 M-2.0 M), the electrolyte may have improved performance due to high conductivity and may have improved mobility of lithium ions due to an appropriate viscosity. The lithium salt may be any lithium salts in common use for electrolytes of lithium secondary batteries in the art. For example, an anion of the lithium salt may be F−, Cl−, Br−, I−, NO3−, N(CN)2−, BF4−, ClO4−, PF6−, (CF3)2PF4−, (CF3)3PF3−, (CF3)4PF2−, (CF3)5PF−, (CF3)6P−, CF3SO3−, CF3CF2SO3−, (CF3SO2)2N−, (FSO2)2N−, CF3CF2(CF3)2CO−, (CF3SO2)2CH−, (SF5)3C−, (CF3SO2)3C−, CF3(CF2)7SO3−, CF3CO2−, CH3CO2−, SCN−, (CF3CF2SO2)2N−, or a combination thereof.
The organic solvent of the electrolyte may be any organic solvents in common use for electrolytes of lithium secondary batteries in the art. For example, the organic solvent may be an ether solvent, an ester solvent, an amide solvent, a linear carbonate solvent, or a cyclic carbonate solvent, which may be used alone or in combination of at least two thereof.
A representative example of the organic solvent of the electrolyte may include a cyclic carbonate solvent, a linear carbonate solvent, or a combination thereof. Non-limiting examples of the cyclic carbonate include ethylene carbonate (EC), propylene carbonate (PC), 1,2-butylene carbonate, 2,3-butylene carbonate, 1,2-pentylene carbonate, 2,3-pentylene carbonate, vinylene carbonate, a halide thereof, or a combination thereof. Non-limiting examples of the linear carbonate include dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropyl carbonate, ethyl methyl carbonate (EMC), methyl propyl carbonate, ethyl propyl carbonate, or a combination thereof.
Ethylene carbonate (EC) and propylene carbonate (PC) as cyclic carbonates available as the organic solvent of the electrolyte are high-viscosity organic solvents with a high dielectric constant and thus may facilitate dissociation of the lithium salt in the electrolyte. Such a cyclic carbonate may be mixed with a linear carbonate, such as dimethyl carbonate (DMC) and diethyl carbonate (DEC), having low viscosity and low dielectric constant in an appropriate ratio to prepare an electrolyte having high electric conductivity.
Non-limiting examples of the ether solvent available as the organic solvent include dimethyl ether, diethyl ether, dipropyl ether, methyl ethyl ether, methyl propyl ether, ethyl propyl ether, or a combination thereof.
Non-limiting examples of the ester solvent available as the organic solvent include methyl acetate, ethyl acetate, propyl acetate, methyl propionate, ethyl propionate, propyl propionate, γ-butyrolactone, γ-valerolactone, γ-caprolactone, σ-valerolactone, ε-caprolactone, or a combination thereof.
Non-limiting examples of the amide solvent available as the organic solvent include N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMA), N-methyl-2-pyrrolidone (NMP), or a combination thereof.
The electrolyte for a lithium secondary battery may further include a conventional additive to form a solid electrolyte interface (SEI) membrane within the scope of the objective of the present inventive concept. Non-limiting examples of the additive to form the SEI membrane include vinylene carbonate, vinyl ethylene carbonate, fluoroethylene carbonate, a cyclic sulfite, a saturated sultone, an unsaturated sultone, an acyclic sulfone, or a combination thereof.
Non-limiting examples of the cyclic sulfite may include ethylene sulfite, methyl ethylene sulfite, ethyl ethylene sulfite, 4,5-dimethyl ethylene sulfite, 4,5-diethyl ethylene sulfite, propylene sulfite, 4,5-dimethyl propylene sulfite, 4,5-diethyl propylene sulfite, 4,6-dimethyl propylene sulfite, 4,6-diethyl propylene sulfite, 1,3-butylene glycol sulfite, or a combination thereof. Non-limiting examples of the saturated sultone may include 1,3-propane sultone, 1,4-butane sultone, or a mixture thereof. Non-limiting examples of the unsaturated sultone may include ethene sultone, 1,3-propene sultone, 1,4-butene sultone, 1-methyl-1,3-propene sultone, or a combination thereof. Non-limiting examples of the acyclic sulfone may include divinyl sulfone, dimethyl sulfone, diethyl sulfone, methylethyl sulfone, methylvinyl sulfone, or a combination thereof.
The amount of the additive to form an SEI membrane may be appropriately chosen according to a type of the additive. For example, the amount of the additive to form an SEI membrane may be from about 0.01 parts by weight to about 10 parts by weight based on a total weight of the electrolyte for a lithium secondary battery.
According to another aspect of the present disclosure, a lithium secondary battery includes an electrolyte according to any of the above-described embodiments.
For example, the lithium secondary battery may be manufactured by injecting an electrolyte according to any of the above-described embodiments into an electrode assembly including a cathode, an anode, and a separator disposed between the cathode and the anode. The cathode and the anode may be each manufactured by mixing an active material, a binder, and a conducting agent with a solvent to prepare a slurry, coating the slurry on a current collector such as aluminum, and drying and pressing the resulting product.
The cathode active material may include a lithium-containing transition metal oxide. Non-limiting examples of the cathode active material may include LixCoO2 (wherein 0.5<x<1.3), LixNiO2 (wherein 0.5<x<1.3), LixMnO2 (wherein 0.5<x<1.3), LixMn2O4 (wherein 0.5<x<1.3), Lix(NiaCobMnc)O2 (wherein 0.5<x<1.3, 0<a<1, 0<b<1, 0<c<1, and a+b+c=1), LixNi1-yCoyO2 (wherein 0.5<x<1.3 and 0<y<1), LixCo1-yMnyO2 (wherein 0.5<x<1.3 and 0≤y<1), LixNi1-yMnyO2 (wherein 0.5<x<1.3 and O≤y<1), Lix(NiaCobMnc)O4 (wherein 0.5<x<1.3, 0<a<2, 0<b<2, 0<c<2, and a+b+c=2), LixMn2-zNizO4 (wherein 0.5<x<1.3, 0<z<2), LixMn2-zCozO4 (wherein 0.5<x<1.3 and 0<z<2), LixCoPO4 (wherein 0.5<x<1.3), LixFePO4 (wherein 0.5<x<1.3), or a combination thereof. The lithium-containing transition metal oxide may be coated with a metal such as aluminum (Al) or a metal oxide. Alternatively, the cathode active material may include a lithium-containing transition metal sulfide, a lithium-containing transition metal selenide, a lithium-containing transition metal halide, or a combination thereof, in addition to or in place of the lithium-containing metal oxide.
Typical examples of the anode active material may include a carbonaceous material, a lithium metal, silicon, or tin that allows intercalation and deintercalation of lithium ions. For example, a metal oxide such as TiO2, SnO2, or the like having a potential of less than 2 Volts (V) with respect to lithium may also be used as the anode active material. For example, the anode active material may be a carbonaceous material, including a low-crystalline carbon and a high-crystalline carbon. Representative examples of the low-crystalline carbon are soft carbon and hard carbon. Representative examples of the high-crystalline carbon are high-temperature sintered carbon, such as natural graphite, artificial graphite, kish graphite, pyrolytic carbon, mesophase pitch based carbon fiber, meso-carbon microbeads, mesophase pitches, and petroleum or coal tar pitch derived cokes.
The binder may bind the active material and a conducting agent together to fix them to a current collector. The binder may be any binders in common use for lithium secondary batteries, for example, polyvinylidene fluoride, polypropylene, carboxymethylcellulose, polyvinylpyrrolidone, tetrafluoroethylene, polyethylene, polyvinyl alcohol, or styrene butadiene rubber.
Non-limiting examples of the conducting agent may include artificial graphite; natural graphite; acetylene black; ketjen black; channel black; lamp black; thermal black; conductive fibers such as carbon fibers and metallic fibers; conductive metal oxides such as titanium oxide; and metal powders such as aluminum or nickel.
Non-limiting examples of the separator may include a single olefin such as polyethylene (PE) and polypropylene (PP), an olefin composite, polyamide (PA), polyacrylonitrile (PAN), polyethylene oxide (PEO), polypropylene oxide (PPO), polyethylene glycol diacrylate (PEGA), polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVdF), or polyvinyl chloride (PVC).
The lithium secondary battery according to an embodiment may have any shape, for example, a cylindrical type using a can, a rectangular type, a pouch type, or a coin type.
Referring to
The cathode 13, the anode 11, and the separator 12 may be rolled or folded and then be accommodated in a battery case 14, followed by injecting an electrolyte (not shown) into the battery case 14 and sealing with a cap assembly 15, thereby completing manufacture of the lithium secondary battery 10. The battery case 14 may be a cylindrical, rectangular, or thin-film type. For example, the lithium secondary battery 10 may be a large thin-film battery.
One or more embodiments of the present disclosure will now be described in detail with reference to the following examples. However, these examples are only for illustrative purposes and are not intended to limit the scope of the one or more embodiments of the present disclosure.
After an organic ester compound and an organic solvent were mixed to obtain an electrolyte solvent, LiPF6 as a lithium salt was added thereto to obtain an electrolyte containing 1.3 molar (M) solution of LiPF6. The types and amounts of organic ester compounds, organic solvents, and lithium salts used in Examples 1 to 4 are represented in Table 1.
(Manufacture of Cylindrical Cell)
Li1.2Ni0.13CO0.13Mn0.53O2 (OLO) as a cathode active material, polyvinylidene fluoride (PVDF) as a binder, and Denka black as a conducting agent were mixed in a weight ratio of about 92:4:4 to obtain a solid mixture. This solid mixture was dispersed in N-methyl-2-pyrrolidone to prepare a cathode active material layer composition. The cathode active material layer composition was coated on an aluminum foil having a thickness of about 15 micrometers (μm), dried in an oven set at about 90° C. for about 2 hours, and then further dried in a vacuum oven at about 120° C. for about 2 hours to completely evaporate a solvent. The resulting product was then pressed and punched, thereby manufacturing a cathode.
The cathode, a silicon anode (available from Samsung Fine Chemicals Co. Ltd.), a polyethylene separator, and the electrolyte prepared in Example 1 as described above were used to manufacture a 18650 cylindrical cell.
20 wt % of ethylene carbonate (EC), 43 wt % of diethyl carbonate (DEC), 22 wt % of fluoroethylene carbonate (FEC), and 15 wt % of LiPF6 as a lithium salt were mixed to prepare an electrolyte containing 1.3 M solution of LiPF6.
Manufacture of Cylindrical Cell
A cylindrical cell was manufactured in the same manner as in Examples 1 to 4, except that the electrolyte prepared in Comparative Example 1 as described above, instead of the electrolytes of Examples 1 to 4, was used.
A charge-discharge test was performed using the cylindrical cells of Examples 1 to 4 and Comparative Example 1 in the following manner.
First, each of the cylindrical cells was charged at about 25° C. with a constant current of about 0.05 Coulomb (C) to a voltage of about 4.55 V, and then discharged with a constant current of about 0.05 C to a discharge voltage of about 2.0 V (First cycle of formation process).
Next, each of the cylindrical cells was charged at about 25° C. with a constant current of about 0.1 C to a voltage of about 4.55 V, and then discharged with a constant current of about 0.1 C to a discharge voltage of about 2.0 V (Second cycle of formation process). This cycle was repeated one more (Third cycle of formation process).
The cylindrical cell after the formation process was charged at about 25° C. with a constant current of about 1 C to a voltage of about 4.55 V, and then discharged with a constant current of about 1 C to a discharge voltage of about 2.0 V, followed by discharge capacity measurement. This discharge capacity was recorded as a 1st cycle discharge capacity or an initial capacity. This charge and discharge cycle was repeated to the 53th cycle.
A discharge capacity measured at every cycle was recorded as a specific capacity. The results are shown in
Referring to
A capacity retention of each cylindrical cell was calculated based on the discharge capacity measured at each cycle using Equation 1. The discharge capacities and capacity retentions at the 53th cycle of the cylindrical cells of Examples 1 to 4 and Comparative Example 1 are represented in Table 2. Also, the capacity retentions at the 53th cycle of the cylindrical cells of Examples 1 to 4 and Comparative Example 1 are shown in
Capacity retention (%)=(53th-cycle discharge capacity/1st-cycle discharge capacity)×100 Equation 1
Referring to Table 2 and
As described above, according to the one or more embodiments, an electrolyte for a lithium secondary battery, including an organic ether compound of Formula 1, may form a stable film on a surface of the anode, and thus provide a lithium secondary battery with improved capacity and lifetime characteristics.
It should be understood that exemplary embodiments described herein should be considered in a descriptive sense only and not for purposes of limitation. Descriptions of features or aspects within each exemplary embodiment should typically be considered as available for other similar features or aspects in other exemplary embodiments.
While one or more exemplary embodiments have been described with reference to the figures, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present inventive concept as defined by the following claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2014-0195962 | Dec 2014 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20130230781 | Yu et al. | Sep 2013 | A1 |
| 20130260229 | Uzun et al. | Oct 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 2007-250424 | Sep 2007 | JP |
| 2012082760 | Jun 2012 | WO |
| WO-2016084704 | Jun 2016 | WO |
| Entry |
|---|
| M.C. Smart et al. “Use of Organic Esters as Cosolvents in Electrolytes for Lithium-Ion Batteries with Improved Low Temperature Performance”, Journal of the Electrochemical Society, 149 (4), A361-A370 (2002). |
| Number | Date | Country | |
|---|---|---|---|
| 20160190649 A1 | Jun 2016 | US |