Claims
- 1. In a method of electrolyzing alkali metal chlorides in an electrodic gap between an anode and a cathode provided with a diaphragm, the improvement comprising the diaphragm being made of a composition comprising an inert fibrous material impregnated with a copolymer of styrene and divinyl benzene copolymerized directly on the material in the absence of a solvent and there sulfonated and halogenated.
- 2. The method of claim 1 wherein the fiber material is asbestos and the halogen is chlorine.
- 3. In a diaphragm cell comprising a cell can and a cell base provided with a plurality of cathodes provided with a diaphragm and a plurality of anodes, the improvement comprising forming the diaphragm from a composition comprising an inert fibrous material impregnated with a copolymer of styrene and divinyl benzene copolymerized directly on the material in the absence of a solvent and there sulfonated and halogenated.
- 4. The cell of claim 3 wherein the fibers are asbestos.
- 5. A cathode structure provided with a diaphragm of a composition comprising an inert fibrous material impregnated with a copolymer of styrene and divinyl benzene copolymerized directly on the material in the absence of a solvent and there sulfonated and halogenated which has been formed by pulling a liquid suspension of said fibers under vacuum through perforations in the cathode.
- 6. A cathode structure provided with an asbestos paper diaphragm formed by compacting the fibers of a composition comprising an inert fibrous material impregnated with a copolymer of styrene and divinyl benzene copolymerized directly on the material in the absence of a solvent and there sulfonated and halogenated into paper.
- 7. A cathode structure of claim 5 wherein the said fibers are pulled into a diaphragm before impregnation.
- 8. A method of producing a composition comprising an inert fibrous material impregnated with a copolymer of styrene and divinyl benzene copolymerized directly on the material in the absence of a solvent and there sulfonated and halogenated comprising impregnating the inert fibrous material with styrene, divinyl benzene and polymerization initator, heating the impregnated fibrous material to effect copolymerization of the styrene and divinyl benzene, sulfonating the resulting fibrous material with sulfur trioxide to introduce sulfonic acid groups in the styrene - divinyl benzene copolymer and halogenating the resulting fibrous material to introduce halogen into the sulfonated divinyl benzene - styrene copolymer.
- 9. The method of claim 8 wherein the fibrous material is asbestos.
- 10. The method of claim 9 wherein the asbestos is impregnated with an organic solution of divinyl benzene and styrene and benzoyl peroxide and the solvent is evaporated.
- 11. The method of claim 9 wherein the impregnated asbestos is heated to 80.degree. to 100.degree. C to copolymerize divinyl benzene and styrene.
- 12. The method of claim 9 wherein the halogenation is effected with chlorine in the presence of water containing ferric chloride.
- 13. The method of claim 9 wherein the asbestos is in fiber form.
- 14. The method of claim 8 wherein the sulfonation is effected by treating the material with a solution of SO.sub.3 in liquid SO.sub.2 at -10.degree. to -40.degree. C and a small amount of water is then added to stabilize the introduced sulfonic groups before removal of SO.sub.2.
- 15. The method of claim 8 wherein sulfonation is effected by passing a flow of anhydrous nitrogen containing SO.sub.3 through the fibrous material and successively passing through the material a flow of nitrogen saturated with water vapor to stabilize the sulfonic groups introduced into the copolymer.
- 16. A method of producing an asbestos material suitable for diaphragms for diaphragm cells comprising impregnating an asbestos material with an organic aromatic solution of divinyl benzene, styrene and benzoyl peroxide, evaporating the organic aromatic solvent, heating the impregnated asbestos material to 80.degree. to 100.degree. C to effect copolymerization of the monomers, sulfonating the resulting copolymer-asbestos material with sulfur trioxide in liquid sulfur dioxide to introduce sulfonic acid groups in the copolymer, washing the sulfonated material with water and chlorinating the asbestos material to introduce chlorine into the sulfonated divinyl benzene-styrene copolymer.
- 17. The method of claim 16 wherein the asbestos material contains 5 to 50% by weight of the copolymer.
Priority Claims (1)
Number |
Date |
Country |
Kind |
20989 |
Mar 1975 |
IT |
|
Parent Case Info
This is a division of Ser. No. 575,415, filed May 7, 1975; now U.S. Pat. No. 4,020,235.
US Referenced Citations (6)
Divisions (1)
|
Number |
Date |
Country |
Parent |
575415 |
May 1975 |
|