Patent Application
20200391265
The present disclosure relates generally to a system and method for an improved material flow through an extrusion machine by altering the material properties of an extrusion material in a magnetic field.
This section provides background information related to the present disclosure that is not necessarily prior art.
Extrusion is the processes of shaping material, such as plastic, metal, alloys, or billets, by pushing the material through a shaped opening in a die. Material pushed through the die exits the die as an elongated piece of material with the same shape as the die opening. The extrusion process for metal, such as an aluminum billet, is used to mass produce straight, semi-finished products. High-strength aluminum products are used, for example, in the automotive industry and must have consistent material properties (e.g., microstructural and mechanical properties) throughout its entirety. However, the material properties of the products can be affected by the extrusion process, resulting in an inferior product. For example, a solid cross section or a hollow cross section of an aluminum product can be produced by indirect extrusion; however, manufacturing conditions can cause recrystallization on a long side of a billet when homogenizing treatment temperature conditions or/and a high extrusion temperature allows for intermetallic compounds of these elements to grow. Additionally, the tooling itself can be damaged from the extrusion process.
It has been shown that an applied magnetic field can change the plastic behavior of crystalline materials, a phenomenon known as magnetoplasticity. The magnetoplasticity phenomenon has been explained by assuming that a dangling bond of a paramagnetic impurity forms a radical pair with a dangling bond of the dislocation core. It has been shown that an applied magnetic field can induce transitions between different spin states of such pairs characterized by different binding energies, and thus facilitate dislocation depinning from the impurity, which thereby enhances the crystal plasticity.
This section provides a general summary of the present disclosure and is not a comprehensive disclosure of its full scope or all of its features, aspects, and objectives. An electromagnetic extrusion system is provided for extruding a material. The electromagnetic extrusion system comprises a container defining a chamber for holding the extrusion material, and a die defining an opening in fluid communication with the chamber for the extrusion material to exit as an extrusion. The subject electromagnetic extrusion system also includes an electromagnetic winding disposed about the chamber, which is configured to carry an electrical current to generate a magnetic field to reduce flow stress of the extrusion material.
The electromagnetic extrusion system may also include a ram configured to push the extrusion material out of the opening.
According to an aspect of the disclosure, the electromagnetic extrusion system may be provided with the container having a cup shape with a tubular side wall defining an inner surface and extending in an axial direction from a solid base. The die may be configured to move with the ram through the chamber, and with the opening extending between an outer surface of the die and the inner surface of the tubular side wall of the chamber.
According to an aspect of the disclosure, the electromagnetic extrusion system may be provided with the container including a tubular side wall extending from a first end that is open to receive the ram, and with the die fixed relative to the container and disposed at a second end of the tubular side wall opposite first end.
According to an aspect of the disclosure, the electromagnetic winding may be helically wound about the chamber. According to another aspect, the electromagnetic winding may be configured to produce a magnetic flux density of at least 2 Tesla within the extrusion material. According to another aspect, the electrical current in the electromagnetic winding may be direct current.
According to an aspect of the disclosure, at least one of the container or the die may comprise a ferromagnetic material configured to intensify the magnetic flux within the extrusion material. According to another aspect of the disclosure a tool retainer block containing the electromagnetic winding may surround the container.
According to another aspect of the disclosure, the extrusion material is a metal. According to yet another aspect of the disclosure, the magnetic field dissipates a dislocation defect structure within the extrusion material using a magnetoplasticity effect.
A method of operating an extrusion system is also provided in the present disclosure. The method includes: forcing an extrusion material to exit a chamber through an opening; energizing an electromagnetic winding disposed about the chamber to produce a magnetic field in the extrusion material; and reducing flow stress in the extrusion material by the magnetic field in the extrusion material.
The step of energizing an electromagnetic winding disposed about the chamber includes may include passing a DC electrical current through the electromagnetic winding. According to an aspect of the disclosure, the magnetic field may have a magnetic flux density of at least 2 Tesla within the extrusion material. According to another aspect of the disclosure, the extrusion material is maintained in a solid state.
In summary, a system and method of extrusion that utilizes electromagnetic energy to improve material flow through an extrusion machine by altering material properties of an extrusion material being extruded.
The disclosure is best understood from the following detailed description when read in conjunction with the accompanying drawings. It is emphasized that, according to common practice, the various features of the drawings are not to-scale. On the contrary, the dimensions of the various features are arbitrarily expanded or reduced for clarity.
In general, extrusion systems, which may also be called extrusion machines, are used to produce semi-finished metal products. In particular, extrusion systems generally apply pressure to force an extrusion material through an opening 34 having a predetermined shape to create an extrusion 12 with a cross-sectional shape corresponding to the predetermined shape of the opening 34.
The electromagnetic extrusion system 20 includes a container 22 having a tubular side wall 24 extending between a first end 26 and a second end 28 and defining an inner surface 30 to enclose a chamber 25 for holding the billet 10 of the extrusion material. The extrusion system 20 also includes a die 32 defining an opening 34 in fluid communication with the chamber 25 for the extrusion material to exit therefrom as the extrusion 12.
As shown in
An electromagnetic winding 50 of electrically conductive material, is embedded within a tool retainer block 52 surrounding the container 22. The electromagnetic winding may be a traditional resistance-type electromagnet, such as a Bitter electromagnet or a helical coil of wire, such as copper. Alternatively, the electromagnetic winding 50 may be a superconducting magnet and which must be cryocooled to remain in a superconducting state with zero resistance.
The electromagnetic winding 50 may be a different material or construction, such as a hollow tube configured to carry a cooling fluid. As shown in the examples of
One or both of the container 22 and/or the die 32 may comprise a ferromagnetic material, such as Fe, Ni, or Co alloys, which function to intensify the magnetic field within the extrusion material. The magnetic flux density B of a solenoid in free space is described by equation 1:
where μ0 is the magnetic constant, 1.25663706×10−6 m kg s−2 A−2, N is the number of turns, I is the electrical current (in Amps), and l is the length of the loop. For a solenoid immersed in a material with relative permeability μr, such as the in the electromagnetic extrusion system 20 disclosed herein, the magnetic flux density B is described by equation 2:
In other words, the magnetic field generated by the solenoid is intensified by the ferromagnetic material, which has a high relative permeability. For example, a magnet design that normally provides a magnetic flux density B of 0.2 T could potentially achieve a magnetic field density B of 1.2 T by saturating the ferromagnetic material within the electromagnetic winding 50. In other words, by making the tooling, such as the container 22, and/or the die 32 of ferromagnetic material, the magnetic field in the extrusion material may be intensified.
In the example configuration shown in
In summary, the system of the present disclosure provides for flow stress of the extrusion material to be reduced because the magnetic field allows the extrusion material to recrystallize with an improved dynamic recovery rate. The dynamic recovery rate is improved because the magnetic field dissipates the dislocation defect structure via the magnetoplasticity effect. In other words, the flow stress on tooling, such as the chamber 22 and the die 32 and the ram 36, is reduced because the alteration of the material properties in the magnetic field improves the flow of the extrusion material through the electromagnetic extrusion system 20, which reduces pressure on the tooling. In other words, the net effect of the magnetoplasticity effect in the is the enablement of more uniform deformation to produce more complex extrusion shapes or a reduction in the material flow stress allowing for lower extrusion press loads which can increase tooling life or facilitate making extrusions using existing, lower tonnage forming presses for a particular application.
Because the billet 10 remains stationary in relation to the container 22, friction loss and resulting heat is kept to a minimum. The temperature required for operation of the extrusion system 20 is low enough to suppress surface coarsening of crystal grains on the extrusion 12, which results in the finished product having fewer impurities. Additionally, the processing time using this process is faster than other extrusion processes, and therefore, allows for increased production.
As described in the flow chart of
The method 200 also includes energizing an electromagnetic winding 50 disposed about the chamber 25 to produce a magnetic field in the extrusion material at step 204. The electromagnetic winding 50 is preferably formed as a solenoid including an electrical conductor helically wound about the chamber 25. This step 204 may include passing a DC electrical current through the electromagnetic winding 50 at substep 204A. A DC electrical current is preferred, although an AC current may be used provided that the frequency of the AC current is chosen to minimize induction heating and to avoid melting the extrusion material. Also, DC magnetic fields resulting from the DC electrical current are more effective because they are able to penetrate the entire conductive extrusion material. AC fields, on the other hand, have a rather shallow skin depth, limiting the penetration depth into the surface of the extrusion material.
The method 200 also includes reducing flow stress in the extrusion material by the magnetic field in the material at step 206. This step utilizes the magnetoplasticity effect, by which a material is altered by dissipating dislocation defect structures by a strong magnetic field. The magnetic field preferably has a magnetic flux density of at least 2 Tesla in the extrusion material, although the reduction in the flow stress may depend on other factors such as, for example, the composition of the extrusion material, the temperature, and the pressure applied to the extrusion material.
The method 200 also includes cooling the extrusion material to maintain the extrusion material in a solid state at step 208. In order to take full advantage of the magnetoplasticity effect, the extrusion material is preferably maintained at a temperature where in remains a solid. The electromagnetic winding 50 will generate heat through joule heating, which is described by the equation P=I2R, where P is the power dissipated as heat (in Watts), I is the electrical current (in Amps), and R is the resistance of the electromagnetic winding 50 (in Ohms). Because the electromagnetic winding 50 may carry a substantial amount of electrical current, the joule heating may also be substantial. Step 208 may include circulating a cooling fluid into heat conductive communication with the electromagnetic winding 50 to remove heat generated in the electromagnetic winding 50 at sub-step 208A. The cooling fluid may be a liquid or a gas and may be, for example, a coolant that is circulated through passages in the tool retainer block 52 and/or through the electromagnetic winding 50 itself. The cooling fluid may be cooled to remove the excess heat by traditional means, such as an evaporative cooling system, one or more heat exchangers, and/or using one or more chillers to transfer heat using phase changes of a refrigerant.
The foregoing description of the embodiments has been provided for purposes of illustration and description. It is not intended to be exhaustive or to limit the disclosure. Individual elements or features of a particular embodiment are generally not limited to that particular embodiment, but, where applicable, are interchangeable and can be used in a selected embodiment, even if not specifically shown or described. The same may also be varied in many ways. Such variations are not to be regarded as a departure from the disclosure, and all such modifications are intended to be included within the scope of the disclosure.
This PCT International Patent Application claims the benefit of U.S. Provisional Patent Application Ser. No. 62/552,893 filed Dec. 15, 2017 entitled “Electromagnetic Extrusion,” the entire disclosure of the application being considered part of the disclosure of this application and hereby incorporated by reference.
This invention was made under Department of Energy (DOE) Contract No. DE-AC05-00OR22725 between Magna International Inc. and UT-Battelle, LLC, operating and management Contractor for the Oak Ridge National Laboratory for the United States Department of Energy. The Government has certain rights in this invention.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2018/049087 | 8/31/2018 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62552893 | Dec 2017 | US |