The present invention concerns an electromagnetic protection sheath made of textile.
It is generally concerned with the protection of electrical or other conductors from electromagnetic interference (EMI) by means of a sheath having shielding properties.
A textile sheath is proposed in the document U.S. Pat. No. 4,684,762.
That sheath consists of a textile woven or braided from filaments in which only a portion of the fibers is conductive.
Thus there is known a textile sheath comprising warp threads formed of filaments comprising at least 20% to 80% by weight of conductive fibers and weft threads formed of filaments comprising a proportion between 1% and 20% by weight inclusive of conductive fibers.
Thus a sheath of this kind has conductive filaments both in the longitudinal direction and in the transverse direction, thus enabling electrical connections to be made at the crossings of the filaments in the electromagnetic shielding textile structure.
However, these sheaths including a high proportion of conductive metal remain relatively heavy, which is a particular problem in aerospace applications.
An object of the present invention is to provide a solution to the aforementioned drawback and thus to propose a lightweight electromagnetic protection sheath structure.
To this end, the present invention is aimed at a textile electromagnetic protection sheath, characterized in that the textile is formed of conductive filaments extending in a first direction and non-conductive filaments interlaced with said conductive filaments.
The Applicant found that it was possible to obtain an effective electromagnetic protection sheath without conductive filaments crossing over in the textile structure.
The conductive filaments of the structure are therefore not electrically connected together by interlaced filaments.
This textile structure including conductor filaments in only one direction lightens the sheath and furthermore makes it easier to fit thanks to the flexibility of the textile used.
According to a preferred feature of the invention, the first direction corresponds to a longitudinal direction of the sheath.
The conductive filaments therefore extend in the longitudinal direction of the sheath to provide effective electromagnetic protection of the cables covered by the sheath.
The non-conductive filaments advantageously include at least one thermoformable thread.
Thanks to the presence of a thermoformable thread, it is possible to obtain a self-closing protection sheath by heat treatment of the textile.
The sheath can therefore be produced from a flat textile that is then itself thermoformed to produce a tubular sheath.
In one practical embodiment of the invention, the textile is woven, the conductive filaments constituting warp threads and the non-conductive filaments constituting weft threads.
In another embodiment, the textile is braided, the conductive filaments extending in a longitudinal direction of the textile and the non-conductive filaments being braided in directions intersecting the longitudinal direction of the textile.
According to another advantageous feature of the invention, the non-conductive filaments have a diameter greater than the diameter of the conductive filaments so that they provide mechanical protection for the conductive filaments.
Thus the shielding properties of the sheath are not degraded even in the event of wear by rubbing of the sheath, this rubbing being limited to the non-conductive filaments of larger diameter.
Other features and advantages of the invention will become more apparent in the course of the following description.
In the appended drawings, provided by way of nonlimiting example:
In this embodiment of the invention, the protection sheath is produced from a textile formed flat which is then transformed into a tubular sheath by a thermoforming process.
This produces a longitudinally slit and self-closing tubular electromagnetic protection sheath 10 the longitudinal edges 10a, 10b of which have a larger or smaller overlap portion according to the diameter of the bundle of cables to which this electromagnetic protection sheath 10 is fitted.
This self-closing structure of the sheath facilitates fitting and retaining the sheath around a bundle of cables even when the latter bundle is connected at its ends.
It suffices to separate the longitudinal edges 10a, 10b to pass the sheath around a bundle of cables.
This structure enables addition of cables to the bundle and viewing of the cables during maintenance operations.
This sheath 10 is then closed with the edges 10a, 10b one against the other automatically by virtue of shape memory.
The textile used to produce this protection sheath of the invention can be of different kinds, for example produced by a weaving, braiding or knitting process.
Generally speaking, this textile is formed of filaments of two types:
on the one hand, conductive filaments that extend in a first direction, for example in the longitudinal direction X of the sheath 10 in the embodiment shown in
on the other hand, non-conductive filaments interlaced with the conductive filaments.
These non-conductive filaments interlaced with the conductive filaments extend in directions intersecting (perpendicularly or otherwise) the conductive filaments that extend in the longitudinal direction X of the sheath.
In this embodiment, to provide the self-closing character of the sheath, these non-conductive filaments include at least one thermoformable thread.
More generally, the conductive filaments can consist of threads or fibers.
Any type of assembly of threads or fibers can be used, in particular in the form of a braid or woven or non-woven braided strip.
The conductive threads or fibers can be of metal or metalized.
The assembly of threads or fibers can therefore include metal threads or fibers, metalized threads or fibers or a mixture of metal and metalized threads or fibers.
The assemblies of threads or fibers include at least one portion of conductive threads or fibers.
The conductive filaments can therefore consist only of conductive threads or fibers or include only a portion of non-conductive threads or fibers.
For example, the conductive metal threads or fibers can be produced in copper or in any other conductive metal material.
The conductive threads or fibers can equally be produced from metalized non-conductive threads, i.e. threads coated with a conductive coating, for example of copper or silver.
ARACON® metalized polymer from du Pont de Nemours can be used, for example.
The conductive threads or fibers can equally be produced from polymer or elastomer material charged with conductive material particles or fibers.
The X-STATIC® material from Nobbelfiber can be used, for example.
Similarly, the non-conductive filaments can consist of thread or fiber, or an assembly, for example a braid or a braided woven or nonwoven strip, of non-conductive threads or fibers.
These non-conductive threads or fibers consist of mineral or synthetic fibers, for example, or a mixture of mineral and synthetic fibers.
The mineral fibers can be glass fibers, for example.
The non-conductive synthetic fibers can be formed in polyester, PPS (polyphenylenesulfide), PEEK (polyetheretherketone), polyamide, polyethylene, polypropylene, PEI (polyethyleneimine), PEK (polyetherketone) or PEKK (polyetherketoneketone).
These fibers have the advantage of being thermoformable.
Moreover, it is equally possible to use NOMEX® meta-aramide fibers or TEFLON® PTFE (polytetrafluoroethylene) fibers from du Pont de Nemours.
As shown in
The conductive filaments 11 constitute the warp threads of the weave and extend in a longitudinal direction X.
The non-conductive filaments 12 constitute the weft threads of the weave and thus extend in a transverse direction substantially perpendicular to the longitudinal direction X.
In this example, the conductive filaments 11 can be produced from braided copper wire, for example, and the non-conductive filaments can be thermoformable PPS monofilaments.
The non-conductive filaments 12 preferably have a diameter greater than the diameter of the conductive filaments 11.
Thus wear of the sheath by rubbing or abrasion can be limited to the non-conductive filaments 12.
The shielding properties of the sheath can therefore be preserved even in the event of wear of the sheath by rubbing.
The textile is produced by braiding.
The conductive filaments 11′ extend in a longitudinal direction X of the braided textile.
The non-conductive filaments 12′ are braided in directions intersecting the longitudinal direction X of the textile.
They are therefore braided around the conductive filaments 11′ and produce the interlaced structure of the textile.
In this embodiment, and in a manner that is in no way limiting on the invention, the conductive filaments 11′ consist of braided copper wire.
The non-conductive filaments 12′ consist of a thermoformable PPS thread.
Of course other types of conductive and non-conductive materials or filaments can be used.
It will be noted that in the two embodiments described above the textile structure does not have crossing conductive filaments where the filaments cross.
The electromagnetic protection nevertheless remains effective provided that the conductive filaments extend parallel to each other in a first direction, in this embodiment in the longitudinal direction of the sheath.
Thanks to the use of non-conductive filaments in the other directions of the sheath, it is possible to limit the weight of the sheath and to give it satisfactory flexibility.
This type of electromagnetic protection sheath, being relatively light in weight, is particularly well suited to aerospace applications, for protecting bundles of cables in aircraft.
Thanks to the use of a thermoformable thread, the textile structure can be produced flat, by weaving or braiding, and then subjected to heat treatment at a temperature of more than 200° C. to deform the thermoformable thread in the substantially transverse direction of the sheath, which thus becomes self-closing.
Of course, the sheath 10 need not be self-closing and could instead include closure means on its longitudinal edges 10a, 10b.
As shown in
The sheath 10 can also have self-closing properties thanks to a different thermoforming treatment.
For example, cold pressing of a sheath woven flat and folded in half can impart a shape memory structure to the sheath.
Such a sheath can therefore return to its closed shape to cover a bundle of cables after it is placed around the bundle of cables.
Of course, the present invention is not limited to the embodiments described above.
In particular, the electromagnetic protection sheath could equally be produced by knitting it.
Similarly, the electromagnetic protection sheath could be produced directly in the form of a closed tubular sheath by an appropriate weaving, braiding or knitting technique.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0754917 | May 2007 | FR | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12599099 | Nov 2009 | US |
| Child | 16794569 | US |