Patent Application
20180332742
The present invention relates to an electromagnetic wave absorber for preventing electromagnetic interference, and a molded article equipped with the electromagnetic wave absorber.
In recent years, the use of electromagnetic waves in the range of millimeter waves (with a wavelength on the order of 1 to 10 mm and a frequency of 30 to 300 GHz) and submillimeter waves as an information communication medium has been on the increase. In the field of motor vehicle technology, the use of electromagnetic waves has been on the increase, for example, in collision avoidance systems which automatically apply brakes upon sensing obstacles and which measure the speed of a neighboring vehicle and a distance between a user's vehicle and the neighboring vehicle to control the speed of the user's vehicle and the distance between the vehicles. For normal operation of such systems, it is important to receive as little unwanted electromagnetic wave radiation as possible in order to prevent false recognition. It is hence desirable to use electromagnetic wave absorbers that absorb unwanted electromagnetic waves for the purpose of ensuring the performance of these systems.
The aforementioned electromagnetic wave absorbers are of various types according to the principles of the absorption of the electromagnetic waves. For example, it is known that an electromagnetic wave absorber of the type (referred to hereinafter as a “λ/4 type”) including an electromagnetic wave reflection layer, a dielectric layer having a thickness of λ/4 (where λ is an intended wavelength of an electromagnetic wave) and a resistive thin film layer is produced at low costs because of its relatively inexpensive materials and its easier designs. An electromagnetic wave absorber having an excellent property of functioning over a wide range of incident angles has been proposed in PTL 1, for example, as such a λ/4 type electromagnetic wave absorber.
PTL 1-JP-A-2003-198179
The electromagnetic wave absorber disclosed in PTL 1 has the excellent property over a wide range of incident angles. It has been strongly desired to hold this excellent performance of the electromagnetic wave absorber over a longer period of time because the technological development of fully autonomous driving has been promoted to involve the need for further increase in reliability of the collision avoidance systems.
In view of the foregoing, it is therefore an object to provide a λ/4 type electromagnetic wave absorber and a molded article equipped with the electromagnetic wave absorber which are capable of holding the performance thereof over a long period of time.
To accomplish the aforementioned object, a first aspect of the present invention is intended for an electromagnetic wave absorber comprising: a dielectric layer including a polymer film and having a first surface and a second surface; a resistive layer formed on the first surface of the dielectric layer and containing indium tin oxide (referred to hereinafter as “ITO”) as a main component; and an electrically conductive layer formed on the second surface of the dielectric layer and having a sheet resistance lower than that of the resistive layer, wherein the ITO in the resistive layer contains 20 to 40 wt. % of tin oxide (referred to hereinafter as “SnO2”) based on the total weight of the ITO.
In particular, a second aspect of the present invention is intended for the electromagnetic wave absorber of the first aspect, wherein the resistive layer contains a component other than the ITO. A third aspect of the present invention is intended for the electromagnetic wave absorber of the second aspect, wherein the component other than the ITO in the resistive layer is at least one selected from the group consisting of silicon oxide, magnesium oxide and zinc oxide. A fourth aspect of the present invention is intended for the electromagnetic wave absorber of the first to third aspects, wherein the electrically conductive layer is made of ITO. A fifth aspect of the present invention is intended for the electromagnetic wave absorber of the fourth aspect, wherein the ITO in the electrically conductive layer contains 5 to 15 wt. % of SnO2 based on the total weight of the ITO. A sixth aspect of the present invention is intended for the electromagnetic wave absorber of the first to third aspects, wherein the electrically conductive layer is made of at least one selected from the group consisting of aluminum (referred to hereinafter, as “Al”), copper (referred to hereinafter as “Cu”) and their alloys. A seventh aspect of the present invention is intended for the electromagnetic wave absorber, of the first to sixth aspects, wherein the resistive layer has a sheet resistance in the range of 300 to 500 Ω/□. An eighth aspect of the present invention is intended for the electromagnetic wave absorber of the first to seventh aspects, wherein the resistive layer has a thickness in the range of 20 to 100 nm. A ninth aspect of the present invention is intended for the electromagnetic wave absorber of the first to eighth aspects, wherein the dielectric layer includes a polymer film having a relative dielectric constant of 2.0 to 20.0. A tenth aspect of the present invention is intended for the electromagnetic wave absorber of the first to ninth aspects, wherein the polymer film of the dielectric layer is made of at least one selected from the group consisting of ethylene-vinyl acetate copolymer, vinyl chloride, urethane, acrylic, acrylic urethane, polyethylene, silicone and polyethylene terephthalate.
An eleventh aspect of the present invention is intended for the electromagnetic wave absorber of the first to tenth aspects, wherein a coating layer is provided in at least one of a location between the dielectric layer and the resistive layer and a location between the dielectric layer and the electrically conductive layer. A twelfth aspect of the present invention is intended for the electromagnetic wave absorber, of the eleventh aspect, wherein the coating layer is made of at least one selected from the group-consisting of silicon oxide (SiO2, SiO), silicon nitride (SiN), aluminum oxide (Al2O3), aluminum nitride (AlN), niobium oxide (Nb2O5), silicon tin oxide (STO) and aluminum-doped zinc oxide (AZO). A thirteenth aspect of the present invention is intended for the electromagnetic wave absorber of the eleventh and twelfth aspects, wherein the coating layer has a thickness in the range of 5 to 100 nm. A fourteenth aspect of the present invention is intended for the electromagnetic wave absorber of the first to thirteenth aspects which further comprises an adhesive layer provided outside the electrically conductive layer. A fifteenth aspect of the present invention is intended for a molded article equipped with an electromagnetic wave absorber as recited in the first to fourteenth aspects.
The present inventors have directed attention toward the problem of the need for further improvement in the reliability of the collision avoidance system, and have diligently made studies not only for the reduction in costs of the electromagnetic wave absorber but also for the holding of the excellent performance thereof over a long period of time. As a result, the present inventors have found that the aforementioned problem is solved by providing a λ/4 type electromagnetic wave absorber in the form of a laminate including: a dielectric layer including a polymer film and having a first surface and a second surface; a resistive layer formed on the first surface of the dielectric layer and containing ITO as a main component; and an electrically conductive layer formed on the second surface of the dielectric layer and having a sheet resistance lower than that of the resistive layer, wherein the ITO in the resistive layer contains 20 to 40 wt. % of SnO2. Thus, the present inventors have attained the present invention.
The SnO2 content of the resistive layer according to the present invention may be measured using X-ray photoelectron spectroscopy (XPS) or an electron probe microanalyzer (EPMA).
The sheet resistances of the resistive layer and the electrically conductive layer according to the present invention may be measured, for example, using resistance measurement methods of contact type (four-point probe method) or non-contact type (eddy current method).
The term “main component” as used in the present invention, means a component that influences the properties of the material. The “main component” refers to a component that generally makes up at least 50 wt. % of the whole material, and is to be interpreted as including meaning that the whole consists only of the main component.
The electromagnetic wave absorber according to the present invention is a λ/4 type electromagnetic wave absorber including: a dielectric layer including a polymer film and having a first surface and a second surface; a resistive layer formed on the first surface of the dielectric layer and containing ITO as a main component; and an electrically conductive layer formed on the second surface of the dielectric layer and having a sheet resistance lower than that of the resistive layer. This electromagnetic wave absorber is easily designed in accordance with an intended frequency, and is manufactured at low costs because relatively inexpensive materials may be used. Also, the ITO in the resistive layer contains 20 to 40 wt. % of SnO2 based on the total weight of the ITO. This provides an extremely stable amorphous structure, and allows variations in sheet resistance of the resistive layer to fall below approximately 15% if a change with time or an environmental change is effected, thereby producing the electromagnetic wave absorption effect over a long period of time.
In particular, in the case where the resistive layer contains a component other than the ITO in addition to the ITO that is a main component thereof, the durability of the resistive layer is increased, and the sheet resistance value of the resistive layer is held with accuracy over a longer period of time. The use of silicon oxide, magnesium oxide and zinc oxide as the component other than the ITO is preferable because the aforementioned effect is further improved.
In the case where the electrically conductive layer is made of ITO, a transparent electromagnetic wave absorber is provided, which not only becomes applicable to locations where transparency is required, but also allows a user to view a mounting location therethrough, thereby achieving improvements in positioning accuracy and in workability,
Further, in the case where the ITO in the electrically conductive layer contains 5 to 15 wt. % of SnO2 based on the total weight of the ITO, the ITO is easily formed into a stable polycrystalline structure by an annealing process. The electrically conductive layer has a low sheet resistance value that is not greater than one-fifth the sheet resistance value of the resistive layer, and the performance of the electromagnetic wave absorber is held over a longer period of time.
In the case where the electrically conductive layer is made of at least one selected from the group-consisting of aluminum, copper and their alloys, the sheet resistance value is easily decreased. This achieves reflection close to total reflection to improve the absorption performance of the electromagnetic wave absorber.
In the case where the resistive layer has a sheet resistance in the range of 300 to 500 Ω/□, electromagnetic waves are attenuated effectively.
In the case where the resistive layer has a thickness in the range of 20 to 100 nm, the resistive layer having a desired sheet resistance is formed with high thickness accuracy. This provides the electromagnetic wave absorber having a more uniform electromagnetic wave absorption effect.
In the case where the dielectric layer includes a polymer film having a relative dielectric constant of 2.0 to 20.0, the thickness of the dielectric layer is easy to control. This provides the electromagnetic wave absorber having a more uniform electromagnetic wave absorption effect.
In the case where the polymer film of the dielectric layer is made of at least, one selected from the group consisting of ethylene-vinyl acetate copolymer, vinyl chloride, urethane, acrylic, acrylic urethane, polyethylene, silicone and polyethylene terephthalate, the electromagnetic wave absorber having good balance between dimensional stability and costs and having good usability is provided.
In the case where a coating layer is provided in at least one of a location between the dielectric layer and the resistive layer and a location between the dielectric layer and the electrically conductive layer, a component in the dielectric layer is prevented from diffusing into the resistive layer or the electrically conductive layer. This prevents the sheet resistance of the resistive layer or the electrically conductive layer from being influenced by the component in the dielectric layer to achieve a stable sheet resistance value held over a long period of time.
In particular, in the case where the coating layer is made of at least one selected from the group consisting of SiO2, SiN, Al2O3, AlN, Nb2O5, STO and AZO, a component in the dielectric layer is prevented from diffusing into the resistive layer or the electrically conductive layer with higher reliability. This achieves high absorption performance held over a long period of time.
In the case where the coating layer has a thickness in the range of 5 to 100 nm, the stability of the sheet resistance of the resistive layer or the electrically conductive layer and the durability of the resistive layer or the electrically conductive layer are especially excellent.
The electromagnetic wave absorber further comprising an adhesive layer provided outside the electrically conductive layer is easily attached to another member (to-be-attached member). In addition, the position of attachment of the electromagnetic wave absorber is fixed. This achieves the stable maintenance of excellent electromagnetic wave absorption performance.
Also, a molded article equipped with any one of these electromagnetic wave absorbers is capable of exhibiting excellent electromagnetic wave absorption performance with higher stability because the electromagnetic wave absorber is always disposed in position precisely.
Next, embodiments according to the present disclosure will now be described in detail with reference to the drawings. It should be noted that the present disclosure is not limited to the embodiments.
An electromagnetic wave absorber according to the present disclosure includes a laminate having a resistive layer A, a dielectric layer B and an electrically conductive layer C which are arranged in the order named, for example, as shown in
This electromagnetic wave absorber is a λ/4 type electromagnetic wave absorber configured such that, when an electromagnetic wave (λo) having a wavelength (cycle) intended to be absorbed enters the λ/4 type electromagnetic wave absorber, an electromagnetic wave obtained by the reflection (front surface reflection) from a surface of the resistive layer A and an electromagnetic wave obtained by the reflection (back surface reflection) from a surface of the electrically conductive layer C interfere with each other. In the λ/4 type electromagnetic wave absorber, it is known that the thickness (t) and relative dielectric constant (εr) of the dielectric layer B determine the wavelength (cycle) of the electromagnetic wave (λo) intended to be absorbed, as represented by Equation (1) below. That is, the electromagnetic wave having the wavelength (cycle) intended to be absorbed is set by appropriately setting the material and thickness of the dielectric layer B. The components of the electromagnetic wave absorber will be described in order hereinafter.
[MATH. 1]
λo=4 t√{square root over (εr)} (1)
<Resistive Layer A>
The resistive layer A is disposed in order to reflect the electromagnetic wave having the intended wavelength (cycle) near the front surface of the electromagnetic wave absorber. The resistive layer A contains ITO as a main component. The concentration expressed in percentage by weight of SnO2 in the ITO is in the range of 20 to 40 wt. %. More preferably, the ITO contains 25 to 35 wt. % of SnOs. The resistive layer A,
in which the amount of SnO2 in the ITO is in the aforementioned range, has an extremely stable amorphous structure to suppress variations in sheet resistance of the resistive layer A under high-temperature and high-humidity environments. It should be noted that widely used ITO generally contains 5 to 15 wt. % of Sn02, and is different from the ITO for use in the resistive layer A according to the present disclosure. The ITO containing 5 to 15 wt. % of SnO2 can easily provide a resistive layer having a sheet resistance of 300 to 500 Ω/□ when formed as an amorphous film without performing an annealing process. This resistive layer, however, is crystallized by an environmental change such as heating or humidified heat to significantly vary in resistance value. For this reason, this resistive layer cannot be used as a resistive layer for a radio wave absorber. When the ITO containing 5 to 15 wt. % of SnO2 is formed into a polycrystalline structure by an annealing process, the polycrystalline structure has long-term stability but has too high electrical conductivity. For the provision of the resistive layer A having a sheet resistance of 300 to 500 Ω/□ by forming the widely used ITO into a polycrystalline structure, it is hence necessary that the resistive layer A is an extremely thin film, having a thickness of not greater than 10 nm. It is very difficult for an extremely thin film having a thickness of not greater than 10 nm to have a uniform thickness as designed. The control of the resistance value of such an extremely thin film is accordingly very difficult.
The resistive layer A may further contain a component other than ITO. Examples of such a component include silicon oxide, magnesium oxide and sine oxide. Such a component other than ITO is preferably in trace amounts when contained in the resistive layer A. For example, the component other than ITO is preferably contained in an amount of 0.5 to 10 parts by weight, and more preferably in an amount of 1 to 5 parts by weight, per 100 parts by weight of ITO. When the resistive layer A contains such a component other than ITO, the thickness of the resistive layer A can be increased without any change in sheet resistance value. This increases the durability of the resistive layer A to thereby allow the sheet resistance value of the resistive layer A to be held with accuracy over a longer period of time.
The sheet resistance of the resistive layer A is preferably in the range of 300 to 500 Ω/□, and more preferably in the range of 350 to 450 Ω/□. When the sheet resistance of the resistive layer A is in the aforementioned range, the electromagnetic waves are attenuated effectively.
The thickness of the resistive layer A is preferably in the range of 20 to 100 nm, and more preferably in the range of 25 to 60 nm. If the resistive layer A is too thick or too thin, the reliability of the sheet resistance value tends to decrease when a change with time or an environmental change is effected.
<Dielectric Layer B>
The dielectric layer B includes the laminated film having the resin layer b2, the resin layer b1 and the resin layer b2 which are laminated together in the order named (with reference to
[Resin Layer b1]
The resin layer b1 serves an important function in determining the wavelength (cycle) of the electromagnetic wave (λo) intended to be absorbed, and is obtained by forming a resin composition having a predetermined relative dielectric constant (εr) so that the resin composition will have a predetermined thickness (t) after being cured in accordance with the wavelength (cycle) of the electromagnetic wave (λo) intended to be absorbed, and then curing the resin composition. Preferable examples of the resin composition used for the resin layer b1 include: synthetic resins such as ethylene-vinyl acetate copolymer (EVA), vinyl chloride, urethane, acrylic, acrylic urethane, polyethylene, silicone, polyethylene terephthalate, polyester, polystyrene, polyimide, polycarbonate, polyamide, polysulfone, polyether sulfone and epoxy; and synthetic rubbers such as polyisoprene rubber, polystyrene-butadiene rubber, polybutadiene rubber, chloroprene rubber, acrylonitrile-butadiene rubber, butyl rubber, acrylic rubber, ethylene propylene rubber and silicone rubber which are used as resin components. In particular, EVA is preferably used from the viewpoints of moldability and relative dielectric, constant. The use of urethane, acrylic and acrylic urethane achieves a further reduction in the thickness of the resin layer b1 to thereby achieve the thinning of the entire electromagnetic wave absorber. These resin compositions may be used either alone or in combination.
The thickness of the resin layer b1 is preferably in the range of 50 to 2000 μm, and more preferably in the range of 100 to 1000 μm. If the resin layer b1 is too thin, it is difficult to ensure the dimensional accuracy of the thickness thereof. If the resin layer b1 is too thick, material costs are increased.
[Resin Layers b2]
The resin layers b2 are substrates for the formation of the resistive layer A or the electrically conductive layer C by sputtering or the like, and are used as an ancillary material for precisely controlling the thickness of the resin layer b1 during the formation of the resin layer b1. The resin layers b2 are preferably made of a material resistant to high temperatures of evaporation, sputtering and the like for use in the formation of the resistive layer A or the electrically conductive layer C. Examples of the material of the resin layers b2 include polyethylene terephthalate (PET), polyethylene naphthalate (PEN), acrylic (PMMA) polycarbonate (PC) and cycloolefin polymer (COP). In particular, PET is preferably used, because of its excellent heat resistance and its good balance between dimensional stability and costs. The resin layers b2 on opposite sides of the resin layer b1 may be made of the same material or different materials.
The thickness of the resin layers b2 is preferably in the range of 10 to 125 μm, and more preferably in the range of 20 to 50 μm. If the resin layers b2 are too thin, wrinkles or deformation is prone to occur in the resin layers b2 during the formation of the resistive layer A. If the resin layers b2 are too thick, the bendability of the electromagnetic wave absorber is decreased. The resin layers b2 on opposite sides of the resin layer b1 may have the same thickness or different thicknesses.
<Electrically Conductive Layer C>
The electrically conductive layer C is disposed in order to reflect the electromagnetic wave having the intended wavelength (cycle) near the back surface of the electromagnetic wave absorber. The electrically conductive layer C has a sheet resistance sufficiently lower than that of the resistive layer A. Based on these facts, examples of the material of the electrically conductive layer C include ITO, Al, Cu, nickel (Ni), chromium (Cr), molybdenum (Mo) and alloys of these metals. In particular, ITO is preferably used from the viewpoints of not only providing a transparent electromagnetic wave absorber to become applicable to locations where transparency is required but also achieving improvements in workability. In particular, ITO containing 5 to 15 wt. % of SnO2 based on the total weight of the ITO is preferably used. On the other hand, Al, Cu or alloys of these metals are preferably used from the viewpoints of easily lowering the sheet resistance value and further reducing noise. The thickness of the electrically conductive layer C is preferably in the range of 20 to 200 nm, and more preferably in the range of 50 to 150 nm. If the electrically conductive layer C is too thick, the electrically conductive layer C is prone to suffer stresses and cracks. If the electrically conductive layer C. is too thin, a desired low resistance value cannot be obtained. The sheet resistance of the electrically conductive layer C is preferably 1/500 to 1/5, and further preferably 1/200 to 1/15, of the sheet resistance of the resistive layer A.
With this configuration, the resistive layer A contains, as a main component, ITO containing 20 to 40 wt. % of SnO2 based on the total weight, of the ITO. If a change with time or an environmental change is effected in the electromagnetic wave absorber, this configuration allows variations in the sheet resistance of the resistive layer A to fall below approximately 15%, thereby achieving the absorption of the electromagnetic wave having the target wavelength (cycle) over a long period of time.
The electromagnetic wave absorber according to the first embodiment includes the laminate comprised of the resistive layer A, the dielectric layer B and the electrically conductive layer C. However, an additional layer other than these layers A, B and C may be provided in the electromagnetic wave absorber. Specifically, additional layers may be provided outside the resistive layer A, outside the electrically conductive layer C, between the resistive layer A and the dielectric layer B, and between the dielectric layer B and the electrically conductive layer C.
For example, the provision of a coating layer outside the resistive layer A increases the durability and weather resistance of the resistive layer A. As shown in
Examples of the material of the coating layers E and E′ include SiO2, SiN, Al2O3, AlN, Nb2O5, STO and AZO. In particular, AlN and AZO, which further increase the durability of the resistive layer A or the electrically conductive layer C, are preferably used.
The thickness of the coating layers E and E′ is preferably in the range of 5 to 100 nm, and more preferably in the range of 10 to 50 nm. If the coating layers E and E′ are too thin, there is apprehension that the effect of increasing the durability of the resistive layer A or the electrically conductive layer C becomes poor. If the coating layers E and E′ are too thick, the coating layers E and E′ are prone to become cracked, so that there is tendency to fail to produce the stable effect of increasing the durability.
As shown in
Examples of the material of the adhesive layer E used herein include pressure sensitive adhesives such as rubber pressure sensitive adhesives, acrylic pressure sensitive adhesives, silicone pressure sensitive adhesives and urethane pressure sensitive adhesives. Also, adhesive agents such as emulsion adhesive agents, rubber adhesive agents, epoxy adhesive agents, cyanoacrylate adhesive agents, vinyl adhesive agents and silicone adhesive agents may foe used as the material of the adhesive layer F. These examples of the material of the adhesive layer F may be selected as appropriate depending on the material and shape of the to-foe-attached member. In particular, acrylic pressure sensitive adhesives are preferably used from the viewpoints of their long-term adhesive strength and their high reliability of attachment.
The electromagnetic wave absorber (with reference to
First, as shown in
Next, as shown in
This provides the electromagnetic wave absorber capable of effectively absorbing the electromagnetic wave having the intended wavelength (cycle) because of the ease of control of the thickness of the resin layer b1. Also, the resistive layer A and the electrically conductive layer C may be formed Separately. This shortens the time regal red for the manufacture of the electromagnetic wave absorber to achieve the manufacture of the electromagnetic wave absorber at low costs.
The process for forming the dielectric layer B comprised of only the resin layer b1 may be performed, for example, by initially preparing the resin layer b1 in film form having a predetermined thickness, forming the resistive layer A on a first surface of the resin layer b1 in film form, and then forming the electrically conductive layer C on a second surface thereof.
The process for providing the coating layer E between the resistive layer A and the dielectric layer B as shown in
The process for providing the adhesive layer F as shown in
Next, a second embodiment of the present disclosure will be described.
As in the aforementioned first embodiment, additional layers may also be provided between the layers in the electromagnetic wave absorber of the second embodiment shown in
The electromagnetic wave absorber according to the second embodiment shown in
First, as shown in
Next, as shown in
The process for providing the coating layer E between the resistive layer A and the dielectric layer B as shown in
The process for further providing the coating layer E between the one resin layer D and the resistive layer A as shown in
The present disclosure will be described hereinafter in further detail using inventive examples and comparative examples. The present disclosure is not limited to the inventive examples to be described below within the scope of the present disclosure.
Prior to description on Inventive Examples and Comparative Examples of the present disclosure, the reliability of the resistive layer A in the electromagnetic wave absorber according to the present disclosure, was evaluated in accordance with indices described below in [Reliability Evaluation 1] and [Reliability Evaluation 2]. These evaluations were performed using n=5 for each test, example, and the average was defined as an evaluation for each test example. The evaluations (Reliability Evaluation 1 and Reliability Evaluation 2) in each test, example are listed in TABLE 1 below.
[Reliability Evaluation 1]
In Test Examples 1 to 6 out of Test Examples 1 to 10, a resistive layer was formed on a base material in film form (PET available from Mitsubishi Chemical Polyester Film Co. and known under the trade name of Mitsubishi Diafoil) by sputtering using materials listed in TABLE 1. In Test Examples 7 to 10, the resistive layer was formed on the base material in film form by the use of materials listed in TABLE 1, and a coating layer was further formed on the resistive layer by the use of materials listed in TABLE 1. These test specimens were heated under an atmosphere having a temperature of 120° C for predetermined time periods (24 hours, 100 hours and 1000 hours). A change in the sheet resistance of the resistive layer, after the heating with respect to the sheet resistance of the resistive layer before the heating was Calculated as a sheet resistance variation percentage (%), and was evaluated in accordance with the following indices.
∘: The sheet resistance variation, percentage is less than 10%.
Δ: The sheet resistance variation percentage is not less than 10% and less than 15%.
×: The sheet resistance variation, percentage is not less than 15%.
[Reliability Evaluation 2]
Test specimens for evaluation of the resistive layer were produced in the same manner as the test specimens of Reliability Evaluation 1. These test specimens were placed under an atmosphere having a temperature of 85° C and a humidity of 35% for predetermined time periods (24 hours, 100 hours and 1000 hours). A change in the sheet resistance of the resistive layer after the placement for the predetermined time periods with respect to the sheet resistance of the resistive layer before the placement for the predetermined time periods was calculated as a sheet resistance variation percentage (%), and was evaluated in accordance with the following indices.
∘: The sheet resistance variation percentage is less than 10%.
Δ: The sheet resistance variation percentage is not less than 10% and less than 15%.
×: The sheet resistance variation percentage is not less than 15%.
The results in TABLE 1 show that Test Example 2 which uses ITO containing 20 wt. % of SnO2 for the resistive layer and Test Example 3 which uses ITO containing 30 wt. % of SnO2 for the resistive layer are highly evaluated in Reliability Evaluation 1 and Reliability Evaluation 2 to exhibit excellent durability. The results in TABLE 1 also show that Test Example 7 which uses ITO containing 20 wt. % of SnO2 for the resistive layer and which has an undercoating layer provided on the resistive layer similarly exhibits excellent durability.
Next, Inventive Examples 1 to 14 and Comparative Examples 1 to 4 were produced pursuant to the first embodiment shown in
[Return Losses]
Return losses (dB) for a millimeter wave of 76 GHz were measured pursuant to JIS R 1679 (Measurement methods for reflectivity of electromagnetic wave absorber in millimetre wave frequency), and were evaluated in accordance with indices to foe described below. The aforementioned measurements were made using n=5 for each of Inventive Examples and Comparative Examples, and the average was applied to the following indices and defined as an evaluation for each of Inventive Examples and Comparative Examples.
∘∘: The return loss is not less than 30 dB.
∘: The return loss is not less than 20 dB and less than 30 dB.
Δ: The return loss is not less than 10 dB and less than 20 dB.
×: The return loss is less than 10 dB.
[Evaluation of Electromagnetic Wave Absorption Performance]
∘∘: Both of the return losses in the initial stage and after a lapse of 1000 hours under an atmosphere having a temperature of 120° C are evaluated as “∘∘”, and the electromagnetic wave absorption, performance is very excellent.
∘: One of the return losses in the initial, stage and after a lapse of 1000 hours under an atmosphere having a temperature of 120° C is evaluated as “∘∘” and the other return loss is evaluated as “∘”; or both of the return losses are evaluated as “∘”, and the electromagnetic wave absorption performance is excellent.
Δ: One of the return losses in the initial stage and after a lapse of 1000 hours under an atmosphere having a temperature of 120° C is evaluated as “∘∘” or “∘” and the other return loss is evaluated as “Δ”; or both of the return losses are evaluated as “Δ” and the electromagnetic wave absorption performance is moderate.
×: At least one of the return losses in the initial stage and after a lapse of 1000 hours under an atmosphere having a temperature of 120° C is evaluated as “×”, and the electromagnetic wave absorption performance or the reliability thereof is poor.
Pursuant to the method of the first embodiment-shown in
An intended electromagnetic wave absorber in each of Inventive Examples 2 and 3 and comparative Examples 1 and 2 was provided in substantially the same manner as in Inventive Example 1 except that the resistive layer A was formed using the blending amount of SnO2 changed to that in percent by weight listed in TABLE 2.
An intended electromagnetic wave absorber in Inventive Example 4 was provided in substantially the same manner as in Inventive Example 1 except that the electrically conductive layer C was formed using Al so as to provide a sheet resistance of 2 Ω/□ and that the resistive layer A was formed so as to have a sheet resistance of 380 Ω/□.
An intended electromagnetic wave absorber in each of Inventive Examples 5 to 8 was provided in substantially the same manner as in Inventive Example 1 except that the resistive layer A was formed so as to have a sheet resistance listed in TABLE 2.
An intended electromagnetic wave absorber in each of Inventive Examples 9 to 11 was provided in substantially the same manner as in Inventive Example 1 except that the dielectric layer B was formed by the use of the material listed in TABLE 2. At this time, the dielectric lever B had a relative dielectric constant of 2.45 in Inventive Example 9, a relative dielectric constant of 2.7 in Inventive Example 10 and a relative dielectric constant of 2.55 in Inventive Example of 11.
An intended electromagnetic wave absorber in each of Inventive Examples 12 to 15 was provided in substantially the same manner as in Inventive Example 1 except that the thickness of the resistive layer A was changed to that listed in TABLE 2.
An intended electromagnetic wave absorber in Inventive Example 16 was provided in substantially the same manner as in Inventive Example 1 except that the resistive layer A having a thickness of 50 nm was formed by the use of 2.5 wt. % of SiO2 and ITO containing 30 wt. % of SnO2 and that the dielectric layer B was formed by the use of acrylic.
An intended electromagnetic wave absorber in Comparative Example 3 was provided in substantially the same manner as in Inventive Example 1 except that the electrically conductive layer C was formed by the use of ITO containing 30 wt. % of SnO2 so as to have a sheet resistance of 430 Ω/□ (equal to the sheet resistance of the resistive layer A).
Ad intended electromagnetic wave absorber in Comparative Example 4 was provided, in substantially the same manner as in Inventive Example 1 except that the electrically conductive layer C was formed by the use of aluminum-doped zinc oxide (AZO) so as to have a sheet resistance of 600 Ω/□.
Pursuant to the method of the second embodiment shown in
The resistive layer A, the dielectric layer B, the electrically conductive layer C and the coating layers E and E′ were formed pursuant to Inventive Example 17 so as to have configurations listed in TABLE 3. An intended electromagnetic wave absorber in each of Inventive Examples 18 to 36 was thus provided. The dielectric layer B had a relative dielectric constant of 2.55 when acrylic was used, a relative dielectric constant of 2.7 when urethane was used, a relative dielectric constant of 2.4 when SEPS was used, a relative dielectric constant of 2.3 when EPT was used, and a relative dielectric constant of 2.7 when silicone was used. In Inventive Example 26, the coating layer E′ was not formed, but Al was directly laminated onto the other resin layer D.
The results in TABLES 2 and 3 showed that each of Inventive Examples 1 to 36 had excellent electromagnetic wave absorption performance to maintain the performance thereof over a long period of time even in the ease of a change in surrounding environment. This is because the resistive layer A in each of Inventive Examples 1 to 36 holds a set sheet resistance over a long period of time under heated environments as shown in the aforementioned results in TABLE 1. In particular, it is found that each of Inventive Examples 17 to 36 including at least one of the coating layer E and the coating layer E′ has very excellent electromagnetic wave absorption performance. On the other hand, Comparative Examples 1 and 2, in which the resistance value of the resistive layer A changed with time in the case of a change in surrounding environment due to a smaller or larger amount of SnO2 added to ITO in the material of the resistive layer A, could not maintain the initial excellent electromagnetic wave absorption performance over a long period of time. Comparative Examples 3 and 4, in which the sheet resistance of the electrically conductive layer C was equal to or higher than that of the resistive layer A, could not obtain sufficient electromagnetic wave absorption performance.
The electromagnetic wave absorber in each Inventive Example described above, may not only be attached to any location of a member in which it is desired to absorb unwanted, electromagnetic waves but also be previously installed on a member, e.g. a vehicle body member, which might receive unwanted electromagnetic waves. In this case, the electromagnetic wave absorber is always disposed in position to exhibit, more stable electromagnetic wave absorption performance. Examples of such a member include resin molded articles or metal molded articles such as bumpers, grilles, fenders, spoilers, emblems, brackets and bumper beams. Thus, a molded article including the electromagnetic wave absorber according to the present disclosure is capable of exhibiting excellent electromagnetic wave absorption performance with higher stability.
Although specific forms in the present disclosure have been described in the aforementioned examples, the aforementioned examples should be considered as merely illustrative and not restrictive. It is contemplated that various modifications evident to those skilled in the art could be made without departing from the scope of the present disclosure.
The present, disclosure, which is capable of holding the performance capability of absorbing unwanted electromagnetic waves over a long period of time, is preferably used for an electromagnetic wave absorber for a millimeter-wave radar for use in a vehicle collision avoidance system. The present disclosure may be used for other purposes of suppressing radio wave interference and reducing noises in an intelligent transport system (ITS) that performs information communications between vehicles, roads and persons and in a next generation mobile communication system (5G) using millimeter waves.
A Resistive layer
B Dielectric layer
C Electrically conductive layer
| Number | Date | Country | Kind |
|---|---|---|---|
| 2015-243395 | Dec 2015 | JP | national |
| 2016-241156 | Dec 2016 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2016/087247 | 12/14/2016 | WO | 00 |