Patent Grant
10763068
The present invention relates to an electron emitting device and a method of producing the same.
The applicant has developed electron emitting devices having a novel structure, which are capable of operating in the atmospheric air (see, for example, Patent Documents 1 and 2).
The electron emitting device which is described in Patent Document 2 includes a semi-conductive layer which is interposed between a pair of electrodes (i.e., a substrate electrode and a surface electrode), the semi-conductive layer being composed of a dielectric material with electrically conductive nanoparticles dispersed therein. By applying a voltage on the order of several dozen volts to the semi-conductive layer, electrons can be emitted from the surface electrode (field electron emission). Therefore, unlike any conventional electron emitting device (e.g., a corona discharger) that utilizes a discharge phenomenon under a strong field, this electron emitting device has an advantage in that ozone will not be generated.
This electron emitting device can be suitably used as a charger device for charging a photosensitive drum of an image forming apparatus (e.g., a copier machine), for example. According to Non-Patent Document 1, an electron emitting device that includes a surface electrode of the layered structure described in Patent Document 2 may have a lifetime of about 300 hours (equivalent to approximately 300,000 sheets in the case of a medium-fast copier machine) or more.
[Patent Document 1] Japanese Laid-Open Patent Publication No. 2009-146891 (Japanese Patent No. 4303308)
[Patent Document 2]Japanese Laid-Open Patent Publication No. 2016-136485
[Non-Patent Document 1]Tadashi IWAMATSU et al., NIHON GAZO GAKKAISHI (Journal of the Imaging Society of Japan), Vol. 56, No. 1, pp. 16-23, (2017)
However, there is a desire to improve the characteristics and/or prolong the lifetime of the aforementioned electron emitting device. Accordingly, an objective of the present invention is to provide: an electron emitting device having a novel structure, such that the characteristics of the electron emitting device can be improved and/or its lifetime can be prolonged; and a method of producing the same.
An electron emitting device according to an embodiment of the present invention comprises a first electrode, a second electrode, and a semi-conductive layer provided between the first electrode and the second electrode, wherein the semi-conductive layer includes a porous alumina layer having a plurality of pores and silver supported in the plurality of pores of the porous alumina layer.
In one embodiment, the first electrode is formed of an aluminum substrate or an aluminum layer, and the porous alumina layer is an anodized layer formed at a surface of the aluminum substrate or at a surface of the aluminum layer.
In one embodiment, the first electrode is formed of an aluminum substrate containing aluminum in an amount of not less than 99.00 mass % but less than 99.99 mass %, and the porous alumina layer is an anodized layer formed at a surface of the aluminum substrate.
In one embodiment, aluminum is contained in an amount of 99.98 mass % or less in the aluminum substrate.
In one embodiment, the porous alumina layer has a thickness which is not less than 10 nm and not more than 5 μm.
In one embodiment, the plurality of pores have an opening having a two-dimensional size which is not less than 50 nm and not more than 3 μm as viewed from a normal direction of a surface thereof.
In one embodiment, the plurality of pores of the porous alumina layer have a depth which is not less than 10 nm and not more than 5 μm. The plurality of pores of the porous alumina layer may have a depth which is not less than 50 nm and not more than 500 nm.
In one embodiment, a barrier layer included in the porous alumina layer has a thickness which is not less than 1 nm and not more than 1 μm. A barrier layer included in the porous alumina layer may have a thickness of 100 nm or less.
In one embodiment, the plurality of pores of the porous alumina layer have a stepped side surface. The plurality of pores have, along a depth direction, two or more pore subportions with mutually differing pore diameters, such that any pore subportion at a deeper position has a smaller pore diameter.
In one embodiment, the silver contains silver nanoparticles having an average particle size which is not less than 1 nm and not more than 50 nm. The silver may contain silver nanoparticles with an average particle size which is not less than 3 nm and not more than 10 nm.
In one embodiment, the second electrode includes a gold layer. The second electrode has the layered structure described in Patent Document 2.
A method of producing of an electron emitting device according to an embodiment of the present invention is a method of producing any of the above electron emitting devices, comprising: a step of providing an aluminum substrate or an aluminum layer supported by a substrate; a step of anodizing a surface of the aluminum substrate or the aluminum layer to form a porous alumina layer; and a step of applying silver nanoparticles in a plurality of pores of the porous alumina layer.
In one embodiment, the step of forming the porous alumina layer comprises an anodization step and an etching step to be performed after the anodization step.
In one embodiment, the step of forming the porous alumina layer comprises a further anodization step after the etching step.
According to an embodiment of the present invention, there is provided: an electron emitting device having an a novel structure such that its characteristics can be improved and/or its lifetime can be prolonged as compared to the aforementioned conventional technique; and a method of producing the same.
Hereinafter, with reference to the drawings, electron emitting devices according to embodiments of the present invention and methods of producing the same will be described. Embodiments of the present invention are not to be limited to the illustrated embodiments. In the following description, constituent elements with like functions are denoted by like reference numerals, and redundant description will be avoided.
The electron emitting device 100 includes a first electrode 12, a second electrode 52, and a semi-conductive layer 30 provided between the first electrode 12 and the second electrode 52. The first electrode 12 is composed of an aluminum substrate 12 (e.g., a thickness of 0.5 mm), for example, whereas the second electrode 52 is composed of a gold (Au) layer (e.g., 40 nm thick), for example. The dielectric layer 22 may function as a device separation layer when a plurality of electron emitting devices 100 are to be produced on an aluminum substrate. The size of a single electron emitting device 100 (i.e., the size of a region surrounded by the dielectric layer 22) may be e.g., about 5 mm×about 5 mm (5 mm□), and the dielectric layer 22 has a width of about 5 mm. The dielectric layer 22 may be omitted when just forming a single electron emitting device 100. However, providing the dielectric layer 22 may result in the advantages of an ability to restrain a concentrated electric field and a leakage current from occurring between the first electrode 12 and the second electrode 52.
The semi-conductive layer 30 includes a porous alumina layer 32 having a plurality of pores 34 and silver (Ag) 42 that is supported in the plurality of pores 34 of the porous alumina layer 32.
The plurality of pores 34 have an opening whose two-dimensional size (Dp) as viewed from the normal direction of its surface is not less than about 50 nm and not more than about 3 μm, for example. The plurality of pores 34 may have an opening whose two-dimensional size (Dp) as viewed from the normal direction of its surface is less than about 500 nm. In the present specification, an “opening” refers to an uppermost portion of a pore 34. If a pore 34 has two or more pore subportions with mutually differing pore diameters along the depth direction, regarding the pore diameter, the pore diameter of the uppermost portion is referred to as the opening diameter. The “two-dimensional size” means an area equivalent circle diameter of the opening (pore 34) as viewed from the normal direction of its surface. In the following description, any reference to “two-dimensional size”, “opening diameter”, or “pore diameter” is intended to be an area equivalent circle diameter. Details of the porous alumina layer 32 will be described later with reference to
The silver supported in the pores 34 may be, for example, nanoparticles of silver (hereinafter denoted as “Ag nanoparticles”). The Ag nanoparticles preferably have an average particle size of not less than 1 nm and not more than 50 nm, for example. More preferably, the Ag nanoparticles have an average particle size of not less than 3 nm and not more than 10 nm, for example. The Ag nanoparticles may be coated with an organic compound (e.g., an alcohol derivative and/or surfactant).
The first electrode 12 is composed of an aluminum substrate (e.g., 0.5 mm thick), for example, whereas the porous alumina layer 32 is an anodized layer formed on the surface of the aluminum substrate. Instead of an aluminum substrate, an aluminum layer which is formed on a substrate (e.g., a glass substrate) may be used. In other words, the porous alumina layer 32 may be an anodized layer which is formed at the surface of an aluminum layer that is supported by a substrate. In this case, if the substrate is a dielectric substrate such as a glass substrate, an electrically conductive layer may be formed between the aluminum layer and the substrate, and the aluminum layer and the electrically conductive layer may be utilized as electrodes. Any aluminum layer (i.e., a portion remaining after anodization) functioning as an electrode preferably has a thickness of e.g. 10 μm or more.
The second electrode 52 is composed of a gold (Au) layer, for example. The Au layer preferably has a thickness of not less than 10 nm and not more than 100 nm, e.g. 40 nm. Otherwise, platinum (Pt) may be used. Furthermore, as described in Patent Document 2, a layered structure of an Au layer and a Pt layer may be adopted; in this case, preferably the Au layer serves as a lower layer and the Pt layer serves as an upper layer in the layered structure (Pt layer/Au layer). In the layered structure, the Pt layer preferably has a thickness of not less than 10 nm and not more than 100 nm, e.g. 20 nm, and the Au layer preferably has a thickness of not less than 10 nm and not more than 100 nm, e.g. 20 nm. As compared to forming the second electrode 52 with an Au layer alone, the Pt layer/Au layer layered structure can provide a lifetime which is about 5 times longer.
Next, with reference to
First, as shown in
As necessary, the surface of the aluminum substrate may be subjected to a pretreatment. For example, a microblasting treatment may be performed. Alternatively, after a porous alumina layer is formed through anodization, the porous alumina layer may be removed by etching. The pores in the porous alumina layer to be first formed are likely to be distributed irregularly (randomly). Therefore, in order to form a porous alumina layer with a regular array of pores, it is preferable to remove the porous alumina layer that was formed first.
Next, as shown in
Next, as shown in
Next, with reference to
The porous alumina layer is formed by, for example, allowing the surface of an aluminum substrate (within which portions that were not anodically oxidized will become the first electrode 12) to undergo anodization in an acidic electrolytic solution. The electrolytic solution to be used in the step of forming the porous alumina layer may be, for example, an aqueous solution that contains an acid which is selected from the group consisting of oxalic acid, tartaric acid, phosphoric acid, chromic acid, citric acid, and malic acid. By adjusting the conditions of anodization (e.g., the kind of electrolytic solution, applied voltage), it is possible to control the opening diameter Dp, the interpore distance Dint, the pore depth Dd, the thickness tp of the porous alumina layer, and the thickness tb of the barrier layer. A porous alumina layer which is obtained through anodization may have, for example, cylindrical pores 34B as in the porous alumina layer 32B shown in
After the anodization, the porous alumina layer may be placed in contact with an etchant for alumina and subjected to a predetermined amount of etching so as to enlarge the pore diameter. With wet etching, the pore wall and the barrier layer can be etched substantially isotropically. By adjusting the kind of etchant and its concentration, as well as the etching time, it is possible to control the etching amount (that is, the opening diameter Dp, interpore distance Dint, pore depth Dd, the barrier layer thickness tb, etc.). Examples of etchants that may be used are: an aqueous solution of phosphoric acid; an aqueous solution of an organic acid, e.g., formic acid, acetic acid, or citric acid; or a chromic and phosphoric acid mixture aqueous solution. A porous alumina layer which is obtained by performing etching only once after the anodization will have cylindrical pores 34B, as in the porous alumina layer 32B illustrated in
For example, an anodization may be performed with oxalic acid (0.05 M, 5° C.) and a formation voltage of 80 V for about 25 minutes; thereafter, 20 minutes of etching may be performed with phosphoric acid (0.1 M, 25° C.); as a result, a porous alumina layer 32B having a depth Dd of about 2000 nm, an opening diameter Dp of 100 nm, an interpore distance Dint of 200 nm, and a barrier layer thickness tb of about 30 nm can be obtained.
In another example, for example, an anodization may be performed with oxalic acid (0.05 M, 5° C.) and a formation voltage of 80 V for about 10 minutes; thereafter, 20 minutes of etching may be performed with phosphoric acid (0.1 M, 25° C.); as a result, a porous alumina layer 32B having a depth Dd of about 700 nm, an opening diameter Dp of 100 nm, an interpore distance Dint of 200 nm, and a barrier layer thickness tb of 50 nm can be obtained.
After the etching step, a further anodization may be performed to grow the pores in the depth direction, and also to thicken the porous alumina layer. Since the pore growth begins from the bottoms of the pores that have already been formed, each pore will have a stepped side surface. As a result, pores 34A having a stepped side surface are obtained, as in the pores 34A illustrated in
The porous alumina layer 32A may be formed in the following manner, for example. An anodization may be performed with oxalic acid (0.05 M, 5° C.) and a formation voltage of 80 V for about 10 minutes; thereafter, 20 minutes of etching with phosphoric acid (0.1 M, 25° C.) is performed; thereafter again, an anodization may be performed with oxalic acid (0.05 M, 5° C.) and a formation voltage of 80 V for about 20 minutes; as a result, a porous alumina layer 32A having a depth Dd of about 1500 nm, an opening diameter Dp of 100 nm, an interpore distance Dint of 200 nm, and a barrier layer thickness tb of 50 nm can be obtained. Herein, along the depth direction, each pore 34A has two pore subportions with mutually differing pore diameters, such that it has a pore subportion with a depth Dd1 of 500 nm and a pore diameter Dp1 of about 20 nm at a deeper position.
Further thereafter, as necessary, the porous alumina layer may be placed in contact with an etchant for alumina in order to perform further etching, thus further enlarging the pore diameter. As the etchant, the aforementioned etchants are preferable here also.
By repeating anodization steps and etching steps, pores can be formed each having two or more pore subportions with mutually differing pore diameters along the depth direction, such that any pore subportion at a deeper position has a smaller pore diameter, for example. Furthermore, as in the porous alumina layer 32C illustrated in
As described above, the porous alumina layer 32 may be any of the porous alumina layers 32A, 32B and 32C shown in
The depth Dd of the plurality of pores 34 in the porous alumina layer 32 may be e.g. not less than 10 nm and not more than 5 μm. The depth Dd of the plurality of pores 34 may be e.g. not less than 50 nm and not more than 500 nm. The depth Dd of the plurality of pores 34 may be set as appropriate, depending on the thickness of the porous alumina layer 32.
The thickness tb of the barrier layer 32b of the porous alumina layer 32 is preferably not less than 1 nm and not more than 1 μm. More preferably, the thickness tb of the barrier layer 32b is 100 nm or less. The barrier layer 32b is a layer constituting the bottom of the porous alumina layer 32. If the barrier layer 32b is thinner than 1 nm, short-circuiting may occur upon voltage application; on the other hand, if it is thicker than 1 μm, a sufficient voltage may not be applied to the semi-conductive layer 30. Generally speaking, the thickness tb of the barrier layer 32b of the porous alumina layer 32 depends on the interpore distance Dint and the opening diameter (two-dimensional size) Dp of the pores 34 and the conditions of anodization.
Hereinafter, by way of experimental examples, the electron emitting device 100 according to an embodiment of the present invention will be described in more detail.
The semi-conductive layer 30A is obtained by allowing Ag nanoparticles 42n to be supported in the porous alumina layer 32A which has been formed as described above, for example.
For the Ag nanoparticles, for example, an Ag nanoparticle dispersion obtained by dispersing alcohol derivative-coated Ag nanoparticles in an organic solvent (an average particle size of the alcohol derivative-coated Ag nanoparticles: 6 nm, dispersion solvent: toluene, Ag concentration: 1.3 mass %) can be used. For example, on a porous alumina layer 32A that is formed in a region of about 5 mm×about 5 mm, 200 μL (microliters) of the aforementioned Ag nanoparticle dispersion is added dropwise; and spin coating is performed under conditions of: e.g. 500 rpm for 5 seconds and thereafter 1500 rpm for 10 seconds. Thereafter, baking is performed at 150° C. for 1 hour, for example. For enhanced dispersibility, the Ag nanoparticles are coated with an organic substance having e.g. alkoxide and/or carboxylic acid, or a derivative thereof at its terminal end. The baking step is able to remove or reduce the organic substance.
The semi-conductive layer 30A which has just been formed, the Ag nanoparticles 42n abound in lower portions of the pores 34A, as shown in
Once the “forming” treatment is performed, as shown in
While electrons are being stably emitted, as shown in
Thereafter, a phenomenon occurs such that the porous alumina layer 32 is locally destroyed. This is presumably because of heat generation that is caused by electron emission.
As can be seen from
With reference to
As shown in
In
The construction of the electron emitting device 100 produced is as follows.
first electrode 12: a portion of JIS A1050 (thickness 0.5 mm) excluding any anodically oxidized portion
porous alumina layer (32A): opening diameter Dp of about 100 nm, depth Dd of about 2200 nm, interpore distance Dint of 200 nm, porous alumina layer thickness tp of 2200 nm, barrier layer thickness tb of about 50 nm
Ag nanoparticles 42n: alcohol derivative-coated Ag nanoparticles contained in the aforementioned Ag nanoparticle dispersion, having an average particle size of 6 nm
second electrode 52: Au layer (thickness 40 nm)
device size (size of the second electrode 52): 5 mm×5 mm
The porous alumina layer 32A shown in
After carrying out the aforementioned “forming” treatment, an energization test for the electron emitting device 100 was performed through an intermittent driving with ON periods of 16 seconds and OFF periods of 4 seconds. The driving conditions are as follows. The driving voltage Vd (pulse voltage) applied between the first electrode 12 and the second electrode 52 was a rectangular wave having a frequency of 2 kHz and a duty ratio of 0.5, and the driving voltage Vd was increased at a rate of 0.1 V/sec, until the emission current Ie reached a predefined value (which herein was 4.8 μA/cm2) or greater. Thereafter, a feedback control of adjusting the driving voltage Vd was performed so that the emission current Ie as monitored with the counter electrode 110 remained constant. The driving environment was 25° C., with a relative humidity RH of 30% to 40%.
As can be seen from
From the study so far, it has been found that the lifetime can be made about 5 times longer (about 160 hours) by replacing the second electrode 74 (a single Au layer with a thickness of 40 nm) of an electron emitting device 200 of Comparative Example, which will be described later with reference to
For comparison sake, a reference electron emitting device 200 was produced as shown in
The construction of the electron emitting device produced is as follows.
first electrode 71: JIS A1050 (thickness: 0.5 mm)
dielectric layer 72: an anodic oxidized alumina layer (a porous alumina layer subjected to a sealing treatment), having a thickness of 4 μm
semi-conductive layer 73: thickness of 1 μm to 2 μm
insulator 73m: silicone resin
Ag nanoparticles 73n: alcohol derivative-coated Ag nanoparticles contained in the aforementioned Ag nanoparticle dispersion, having an average particle size of 6 nm and accounting for 1.5 mass % with respect to silicone resin
second electrode 74: an Au layer (thickness 40 nm)
device size (size of the second electrode 74): 5 mm×5 mm
The dielectric layer 72 was formed by a method similar to that of the dielectric layer 22 of the electron emitting device 100 described with reference to
As can be seen from
As can be seen from
Presumably, the distribution of Ag nanoparticles (including also a migration that may occur upon electric field application) may be somehow related to the electron emission characteristics and/or the device lifetime; however, no specific correlation has been established yet. However still, the electron emitting device according to an embodiment of the present invention allows Ag nanoparticles to be supported in the pores of the porous alumina layer, and the Ag nanoparticle distribution can be controlled by controlling the opening diameter, depth, interpore distance, etc., of the pores. Therefore, the characteristics of the electron emitting device can be improved and/or a long lifetime can be achieved.
Next, three kinds of electron emitting devices (test samples Nos. 1 to 3) as shown in Table 1 below were evaluated.
As illustrated herein, when the first electrode is formed by using a relatively rigid aluminum substrate (thickness 0.2 mm or more) containing aluminum with a purity of not less than 99.00 mass % and not more than 99.99 mass %, the aluminum substrate can be utilized as a support substrate, so that the electron emitting device can be efficiently produced.
Test samples Nos. 1 to 3 differ from one another with respect to the composition (e.g., aluminum content) of the aluminum substrate 12 used in forming the first electrode 12. The construction of test sample No. 1 (thickness: 0.5 mm) and the method of production it are basically identical with those of the electron emitting device 100 described with reference to
Table 1 shows the main component in the composition of the respective aluminum substrate constituting the first electrode 12 of test samples Nos. 1 to 3.
Test sample No. 1 was produced by using JIS A1050 as the aluminum substrate 12. JIS A1050 has the following composition (mass %).
Si: 0.25% or less, Fe: 0.40% or less, Cu: 0.05% or less, Mn: 0.05% or less, Mg: 0.05% or less, Zn: 0.05% or less, V: 0.05% or less, Ti: 0.03% or less, others: each 0.03% or less, Al: 99.50% or more
Test sample No. 2 was produced by using JIS A1100 as the aluminum substrate 12. JIS A1100 has the following composition (mass %).
Si+Fe: 0.95% or less, Cu: 0.05% to 0.20%, Mn: 0.05% or less, Zn: 0.10% or less, others: each 0.05% or less and altogether 0.15% or less, Al: 99.00% or more
Test sample No. 3 was produced by using an aluminum base material containing aluminum in an amount of 99.98 mass % or more as the aluminum substrate 12. The aluminum substrate of test sample No. 3 had the following composition (mass %).
Si: 0.05% or less, Fe: 0.03% or less, Cu: 0.05% or less, Al: 99.98% or more
The energization test for test samples Nos. 1 to 3 was performed basically similarly to the energization test described with reference to
In any of test samples Nos. 1 to 3, when the driving voltage Vd was about 10 V or more, the emission current Ie gradually increased. By confirming that the emission current Ie increased with an increasing driving voltage Vd, it was determined that it was operating as an electron emitting device. Thus, it was confirmed that each of test samples Nos. 1 to 3 was operating as an electron emitting device.
Table 2 shows results of determining an average value of emission current Ie for each test sample. In Table 2, “Δ” indicates that an average value of emission current Ie was not less than 0.001 μA/cm2 but less than 0.01 μA/cm2; “∘” indicates that an average value of emission current Ie was not less than 0.01 μA/cm2 but less than 0.1 μA/cm2; and “⊚” indicates that an average value of emission current Ie was not less than 0.1 μA/cm2 but less than 4.8 μA/cm2.
Test sample No. 2, in which the purity (i.e., ratio of aluminum content of the aluminum substrate) was lower than that of test sample No. 1, had an average value of emission current Ie which was greater than that of test sample No. 1. On the other hand, test sample No. 3, in which the purity (ratio of aluminum content) of the aluminum substrate was higher than that of test sample No. 1, had an average value of emission current Ie which was smaller than that of test sample No. 1. Thus, as the purity (ratio of aluminum content) of the aluminum substrate decreased, the average value of emission current Ie increased.
However, the aforementioned energization test only illustrates exemplary driving conditions. Depending on the driving conditions of the electron emitting device, the value of emission current Ie may vary. Under operation with a large average value of emission current Ie (i.e., amount of electron emission per unit time), the duration in which operation as an electron emitting device is possible may decrease. As used herein, “the duration in which operation as an electron emitting device is possible” means the period from the moment at which operation as an electron emitting device is confirmed to the moment at which the value of emission current Ie decreases for the same driving voltage Vd; note that this definition differs from that of “lifetime” (i.e., the length of time during which the emission current Ie maintained a certain value) which was described with reference to
The value of emission current and the duration of operation that is expected of an electron emitting device may vary depending on the application (i.e., driving conditions). However, in applications where large emission current values are required, for example, it is preferable to use an aluminum base material with a relatively low aluminum purity (not less than 99.00 mass % and not more than 99.50 mass %). In applications where long hours of operation is highly regarded, for example, it is preferable to use an aluminum base material having a relatively high aluminum purity (not less than 99.50 mass % and not more than 99.98 mass %).
The exact mechanism by which the aluminum purity affects the characteristics of the electron emitting device is not clear as yet. However, as seen from Table 1, any element that is contained as an impurity in the aluminum substrate used herein, except for Mg, is an element which has a high standard electrode potential (i.e., so-called “noble”) as compared to aluminum. Therefore, an impurity element(s) (e.g., iron) that is more noble than aluminum may possibly be affecting the characteristics of the electron emitting device.
Embodiments of the present invention may be suitable as an electron emitting device for use in a charger device of an image forming apparatus, or a method of producing the same, for example.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017-098997 | May 2017 | JP | national |
| 2017-119726 | Jun 2017 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2018/018713 | 5/15/2018 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2018/212166 | 11/22/2018 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20060138664 | Ito et al. | Jun 2006 | A1 |
| 20100278561 | Kanda et al. | Nov 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| 2001-143600 | May 2001 | JP |
| 2003-229045 | Aug 2003 | JP |
| 2004-014406 | Jan 2004 | JP |
| 2004-178863 | Jun 2004 | JP |
| 2009-146891 | Jul 2009 | JP |
| 2016-136485 | Jul 2016 | JP |
| Entry |
|---|
| English translation of JP 2004-014406 (Year: 2004). |
| Iwamatsu et al., “Novel Charging System by Electron Emission Device in the Atmosphere”, Journal of the Imaging Society of Japan, vol. 56, No. 1, 2017, 5 pages. |
| Nakamatsu et al., “Electron Emission Device, Method for Manufacturing Same, and Method for Manufacturing Electronic Device”, U.S. Appl. No. 16/127,670, filed Sep. 11, 2018. |
| Nakamatsu et al., “Electron Emission Device and Method for Manufacturing the Same”, U.S. Appl. No. 16/369,004, filed Mar. 29, 2019. |
| Official Communication issued in International Patent Application No. PCT/JP2018/018713, dated Aug. 14, 2018. |
| Number | Date | Country | |
|---|---|---|---|
| 20200075285 A1 | Mar 2020 | US |