Patent Application
20160259276
1. Field of the Disclosure
The present disclosure relates to an electrophotographic member used in an electrophotographic image forming apparatus and a method for producing the electrophotographic member. Examples of the electrophotographic image forming apparatus include a copying machine, a printer, a facsimile, and a multifunction machine having functions of the foregoing machines.
2. Description of the Related Art
Electrophotographic image forming apparatuses include electrophotographic members such as a roller (e.g., fixing roller) and a belt (e.g., fixing belt) each obtained by coating a rubber layer with a fluorine-based resin.
To manage such an electrophotographic member, a marked portion (e.g., a character string such as a manufacturer's serial number) can be formed (hereafter also referred to as “marking”) in the electrophotographic member.
Japanese Patent Laid-Open No. 2005-338350 discloses a method in which marking is performed on a rubber layer and then the rubber layer is coated with a fluorine-based resin. Specifically, the marking is performed by irradiating a rubber layer with iron red with laser beams. Consequently, the marked portion turns black, and thus is easily recognized visually against the surrounding bright portion with iron red.
However, when a dark (e.g., black) rubber layer is used, it is difficult to visually recognize the marked portion 1f the method disclosed in Japanese Patent Laid-Open No. 2005-338350 is employed.
The present disclosure provides an electrophotographic member including a marked portion with good visibility and a method for producing the electrophotographic member.
Further features of the present disclosure will become apparent from the following description of exemplary embodiments with reference to the attached drawings.
Hereafter, an electrophotographic member according to an embodiment of the present disclosure and a method for producing the electrophotographic member will be described in detail.
Hereafter, a fixing belt used in a fixing device included in an electrophotographic image forming apparatus will be described in detail as an example of the electrophotographic member, but the electrophotographic member is not limited to such an example. For example, the electrophotographic member may be a fixing roller, a pressurizing belt, or a pressurizing roller, which are fixing members used in the fixing device. Furthermore, various structures can be replaced with other structures within the scope of the present disclosure.
First, the entire structure of the electrophotographic image forming apparatus (hereafter, simply referred to as an “image forming apparatus”) will be described.
Next, the flow of the electrophotographic process will be described. The photosensitive member 101 is uniformly charged by a charging roller 102 serving as a charging device so as to have a predetermined polarity (negative polarity in this embodiment). The charged photosensitive member 101 is then irradiated with laser beams 103 emitted from a laser beam source 110 through a laser optical system 110 in response to the input image information (information of original images) (image exposing treatment). The laser beam source 110 emits laser beams 103 modulated (on/off) on the basis of the image information, and the photosensitive member 101 is subjected to scanning exposure.
As a result, an electrostatic latent image corresponding to the image information is formed on the photosensitive member 101. The electrostatic latent image formed on the photosensitive member 101 is visualized by a developing device 104 using a toner. Specifically, a yellow toner image is formed by a developing device 104Y, and the yellow toner image is primarily transferred from the photosensitive member 101 to an intermediate transfer member 105 in a primary transfer portion T1. After the primary transfer, the toner left on the photosensitive member 101 is cleaned by a cleaning device 107.
The above-described process cycle including charging, exposure, development, primary transfer, and cleaning is repeatedly performed in the same manner to form a magenta toner image (a developing device 104M is operated), a cyan toner image (a developing device 104C is operated), and a black toner image (a developing device 104K is operated).
The four-color toner images sequentially superimposed on the intermediate transfer member 105 are secondarily transferred all together onto a recording material P in a secondary transfer portion T2. Herein, a voltage with a positive polarity is applied to a transfer roller 106 disposed so as to face the intermediate transfer member 105. After the secondary transfer, the toner left on the intermediate transfer member 105 is cleaned by a cleaning device 108.
The cleaning device 108 can be brought into contact with or separated from the intermediate transfer member 105. The cleaning device 108 is brought into contact with the intermediate transfer member 105 only when the intermediate transfer member 105 is cleaned. The transfer roller 106 can also be brought into contact with or separated from the intermediate transfer member 105. The transfer roller 106 is brought into contact with the intermediate transfer member 105 only during the secondary transfer.
The recording material P that has passed through the secondary transfer portion T2 is heated and pressurized by a fixing belt 1 and a pressurizing roller 6 of the fixing device (image heating device) 100 (
In this embodiment, the fixing belt 1 included in the fixing device 100 functions as an electrophotographic member.
An endless fixing belt (fixing rotary member) 1 is used as an electrophotographic member.
A pressurizing roller (pressurizing rotary member) 6 is used for forming a nip portion 14 between the pressurizing roller 6 and the fixing belt 1. The pressurizing roller 6 has a multilayer structure in which a silicone rubber elastic layer having a thickness of about 3 mm and a PFA resin tube having a thickness of about 40 μm are stacked on a metal core in this order. Both ends of the metal core of the pressurizing roller 6 in the longitudinal direction are rotatably supported by a device frame 13.
When the pressurizing roller 6 is rotated by a driving motor in a direction indicated by an arrow, the fixing belt 1 that is in pressure contact with the pressurizing roller 6 is a driven belt rotated by the pressurizing roller 6. Furthermore, the fixing belt 1 has an inner surface coated with a lubricant, and thus the slidability is ensured between the fixing belt 1 and a holder 4.
A fixing heater 2 is used for heating the recording material P through the fixing belt 1. The fixing heater 2 includes an alumina substrate and a resistance heating element formed on the alumina substrate in the form of a film having a thickness of about 10 μm by applying a conductive paste containing a silver-palladium alloy using a screen printing method. The resistance heating element is further coated with pressure glass, and thus the fixing heater 2 is a ceramic heater. The fixing heater 2 also has a function as a pressing member that presses the fixing belt 1 toward the pressurizing roller 6.
A holder 4 is used for holding the fixing heater and is formed of a liquid crystal polymer resin having high heat resistance. A metal stay 5 is used for supporting the holder 4. Both ends of the metal stay 5 in the longitudinal direction are urged toward the pressurizing roller 6 at a total pressure of 313.6 N (32 kgf) with a pressurizing mechanism.
A temperature sensor 3 is used for detecting the temperature of the fixing heater 2, and is connected to a control unit (CPU) 10 through an A/D converter 9. The temperature sensor 3 outputs a temperature detection signal to the control unit 10. The control unit 10 samples the output from the temperature sensor 3 at a predetermined interval to reflect the thus-obtained temperature information on the temperature control. That is, the control unit 10 controls the energization for the fixing heater 2 on the basis of the output from the temperature sensor 3 so that the temperature of the fixing heater 2 reaches a target temperature using a heater driving circuit 11.
A guide 7 is used for guiding the recording material P toward the nip portion 14. A pair of conveying rollers 8 are used for conveying the recording material P immediately after the fixing treatment.
The fixing belt 1 includes a cylindrical base member 1b and an inner sliding layer 1a disposed on the inner circumferential surface of the cylindrical base member 1b. Herein, the inner sliding layer 1a is disposed to improve the slidability with the fixing heater 2. If the slidability is not necessarily improved, the inner sliding layer may be omitted.
A silicone rubber elastic layer 1d (hereafter, simply referred to as a “rubber layer” or an “elastic layer”) is disposed so as to coat the outer circumferential surface of the cylindrical base member 1b, and a primer layer 1c is disposed between the cylindrical base member 1b and the silicone rubber elastic layer 1d. The rubber layer 1d includes a marked portion (also referred to as a “recessed portion”) 1L formed through a laser marking treatment (heat treatment). The marked portion indicates the letter/symbol for managing the fixing belt 1, such as a manufacturer's serial number (management number). In this embodiment, “Lot: ABCDE” is marked.
The marked portion 1L is not limited to the above example as long as the marked portion 1L is used to indicate some intention/instruction for operators/assemblers, such as an arrow that indicates an assembly direction or a picture that indicates an assembly procedure in the production/assembly.
A fluorine-based resin layer (release layer) 1f is disposed on the outer circumferential surface of the rubber layer 1d in which the marked portion 1L has been formed, with a whitish adhesive layer 1e disposed therebetween.
Hereafter, each layer of the fixing belt 1 will be described in detail.
Since the fixing belt 1 needs to have heat resistance, the cylindrical base member 1b is particularly a base member made of metal (also referred to as a “metal base member”) whose heat resistance and bending resistance are taken into consideration. The reason for which a base member made of metal but not resin is employed is to prevent formation of a through-hole in the fixing belt 1 when a marking treatment that uses laser beams described below is performed.
The metal base member can be prepared by nickel electroforming as described in Japanese Patent Laid-Open No. 2002-258648 and Japanese Patent Laid-Open No. 2005-121825. The resin base member having heat resistance can be made of a polyimide resin, a polyamide-imide resin, or a polyether ether ketone resin as described in Japanese Patent Laid-Open No. 2005-300915 and Japanese Patent Laid-Open No. 2010-134094.
In this embodiment, a metal base member made of a nickel-iron alloy and having an inside diameter of φ30 mm, a thickness of 40 μm, and a length of 400 mm is used as the cylindrical base member.
The inner sliding layer 1a is suitably made of a resin having high durability and high heat resistance, such as a polyimide resin, a polyamide-imide resin, or a polyether ether ketone resin. In particular, a polyimide resin is used in terms of ease of production, heat resistance, modulus of elasticity, strength, and the like. The polyimide resin is formed from a polyimide precursor solution obtained by reacting an aromatic tetracarboxylic dianhydride or a derivative thereof and an aromatic diamine in a substantially equimolar amount in an organic polar solvent. Specifically, the polyimide resin can be formed by coating the inner surface of the cylindrical base member 1b with the polyimide precursor solution and performing drying and heating to cause a dehydration ring closure reaction.
The coating method is a ring coating method. The cylindrical base member 1b whose inner surface has been coated is dried for 30 minutes in, for example, a hot-air circulating oven at 60° C. and then fired for 10 to 60 minutes in a hot-air circulating oven at 200° C. to 240° C., which is a temperature range in which the fatigue strength of the cylindrical base member does not decrease. As a result, a polyimide inner sliding layer can be formed by the dehydration ring closure reaction.
The silicone rubber elastic layer 1d is disposed to impart flexibility so that the fixing belt 1 can follow the projections and depressions of paper fibers constituting the recording material. Furthermore, the fixing belt 1 needs to have a function of supplying a sufficient amount of heat without delay to the recording material (toner image) in the nip portion 14. Therefore, the thermal effusivity (b=(λ·Cp·ρ)0.5) of the elastic layer is improved by increasing the thermal conductivity and the volumetric heat capacity.
In this embodiment, as illustrated in
The addition-curable silicone rubber serving as the base material 1da contains an organopolysiloxane having an unsaturated aliphatic group, an organopolysiloxane having active hydrogen bonded to silicon, and a platinum compound serving as a cross-linking catalyst. The organopolysiloxane having active hydrogen bonded to silicon reacts with an alkenyl group in the organopolysiloxane having an unsaturated aliphatic group through the catalysis of the platinum compound to form a cross-linking structure.
The carbon fiber 1dc and the inorganic filler 1db are added in consideration of the balance between thermal conductivity, heat capacity, flexibility, and the like. When the amount of the inorganic filler 1db added is increased, the thermal conductivity and the heat capacity improve, but the flexibility tends to degrade. Therefore, a heat transfer path is formed between particles of the inorganic filler 1db using the carbon fiber 1dc to prevent loss of flexibility, and the ratio of the amount of the base material 1da to the total amount of the carbon fiber 1dc and the inorganic filler 1db is increased. Consequently, a rubber layer 1d having good balance with flexibility can be formed.
The carbon fiber 1dc is, for example, carbon fiber or carbon nanotube. In this embodiment, carbon fiber is used.
When the carbon fiber 1dc is added in such a manner, the lightness (L*) of the rubber layer is 15 or less. The lightness (L*) is defined in the CIE Lab (L*ab* colorimetric system) color space. When the differences in L (lightness), a* (hue of red-green axis), and b* (hue of yellow-blue axis) between targets are assumed to be ΔL*, Δa*, and Δb*, the color difference is defined as (ΔL*2+Δa*2+Δb*2)1/2. The visibility tends to improve as the color difference increases. The lightness (L*) can be measured with PIAS manufactured by Quality Engineering Associates, Inc. (QEA).
The inorganic filler 1db is, for example, silicon carbide (SiC), silicon nitride (Si3N4), boron nitride (BN), aluminum nitride (AlN), alumina (Al2O3), zinc oxide (ZnO), magnesium oxide (MgO), silica (SiO2), copper (Cu), aluminum (Al), silver (Ag), iron (Fe), or nickel (Ni). In this embodiment, aluminum (Al) is used.
The inorganic fillers 1db may be used alone or in combination of two or more. The average diameter of the inorganic filler 1db is, for example, 1 μm or more and 50 μm or less in terms of ease of handling and dispersibility. The inorganic filler 1db may be a spherical inorganic filler, a pulverized inorganic filler, a plate-shaped inorganic filler, or a whisker-shaped inorganic filler. In particular, the inorganic filler 1db is a spherical inorganic filler in terms of dispersibility.
For this reason, the thickness of the silicone rubber elastic layer 1d is preferably 100 μm or more and 500 μm or less and more preferably 200 μm or more and 400 μm or less.
An addition-curable silicone rubber composition containing an addition-curable silicone rubber and an inorganic filler is charged into a cylinder pump 57 by turning a motor on. The addition-curable silicone rubber composition charged into the pump 57 is pressure-fed to a coating head 54 through a pressure feed tube 56. The addition-curable silicone rubber composition is then applied onto the outer circumferential surface of the cylindrical base member 1b from a coating liquid supply nozzle 53 located inside the coating head 54.
The cylindrical base member 1b is integrated with a cylindrical metal core 51 inserted into the cylindrical base member 1b. That is, the cylindrical base member 1b is rotated by rotating the cylindrical metal core 51 with a motor while the coating liquid is supplied. Furthermore, the cylindrical base member 1b is slid together with the cylindrical metal core 51 at a constant speed in the right direction (
The thickness of the coating film can be controlled by the clearance between the coating liquid supply nozzle and the cylindrical base member 1b, the supply rate of the silicone rubber composition, and the moving speed of the cylindrical base member 1b. In this embodiment, the clearance between the coating liquid supply nozzle and the cylindrical base member 1b is set to be 400 μm, the supply rate of the silicone rubber composition is set to be 2.8 mm/s, and the moving speed of the cylindrical base member 1b is set to be 30 mm/s. Thus, a silicone rubber composition layer 55 having a thickness of 300 μm is formed.
The addition-curable silicone rubber composition layer 55 formed on the cylindrical base member 1b is heated in an electric furnace for a predetermined time to cause a cross-linking reaction (curing) to proceed. Thus, the silicone rubber elastic layer 1d can be formed.
To improve the adhesiveness between the cylindrical base member 1b and the silicone rubber elastic layer 1d, the cylindrical base member 1b is desirably subjected to a primer treatment (application of an adhesive) in advance. The primer (adhesive) 1c used needs to have better wettability with the cylindrical base member 1b than the silicone rubber elastic layer 1d. Examples of the primer 1c include hydrosilyl (SiH) silicone primers, vinyl silicone primers, and alkoxy silicone primers. In this embodiment, a silicone primer is used. The thickness of the primer layer 1c is, for example, 0.5 to 5.0 μm for the purpose of suppressing unevenness and producing adhesiveness.
In this embodiment, a visible marked portion (recessed portion) 1L is formed in the rubber layer 1d to, for example, manage the fixing belt 1. Therefore, a marking treatment that uses laser beams is performed in this embodiment. This corresponds to a second step in
The marking treatment that uses laser beams provides higher productivity than a marking treatment that uses a cutting tool or the like because there is no need to replace consumable parts. The marking treatment that uses laser beams is also advantageous in that an object subjected to the marking treatment does not deform due to pressing because the object can be processed without contact. Examples of the laser include a YAG laser, a YAVO4 laser, and a CO2 laser.
By irradiating the circumferential surface of the silicone rubber elastic layer 1d with laser beams, the depth of the marked portion 1L is preferably set to be 35 μm or more and 100 μm or less. The depth of the marked portion 1L is more preferably set to be 50 μm or more.
This is because, if the depth of the marked portion 1L is less than 35 μm, a whitish adhesive described below substantially does not enter the marked portion 1L, which degrades the visibility of the marked portion 1L. Furthermore, if the depth of the marked portion (recessed portion) 1L is more than 100 μm, air left in the recessed portion cannot be completely squeezed out because of the step height between the recessed portion and its surrounding portion in a step of squeezing the adhesive disposed between the fluorine-based resin layer 1f and the silicone rubber elastic layer 1d. Consequently, air bubbles may be left between the rubber layer 1d and the fluorine-based resin layer 1f.
Thus, in this embodiment, a CO2 laser having a wavelength of 10.6 μm, an output of 20 W, and an oscillation frequency of 25 kHz is used. The depth of letters constituting the marked portion 1L is 50 μm and the font size is 3×3 mm (one letter).
The adhesive layer 1e is disposed between the silicone rubber elastic layer 1d and a fluorine-based resin tube serving as the fluorine-based resin layer 1f so as to fix the silicone rubber elastic layer 1d and the fluorine-based resin layer 1f.
The adhesive layer 1e is formed by applying an adhesive to the cured silicone rubber elastic layer 1d. This corresponds to a third step in
The rubber layer 1d on which the adhesive layer 1e has been formed is then coated with the fluorine-based resin tube 1f. By squeezing the adhesive present between the rubber layer 1d and the fluorine-based resin tube 1f, the thickness of the adhesive layer 1e is made substantially uniform over the entire region. This squeezing step corresponds to a seventh step in
As illustrated in
Herein, when the marked portion 1L is constituted by letters, the region that surrounds the marked portion 1L, which is a region where the adhesive layer 1e needs to have the thickness X, at least includes a square region on which one letter is circumscribed (e.g., a region that surrounds the letter “C” indicated by a dotted line in
The adhesive constituting the adhesive layer 1e is an addition-curable silicone rubber adhesive, which is a whitish adhesive. Specifically, the addition-curable silicone rubber adhesive contains an organopolysiloxane having an unsaturated hydrocarbon group such as a vinyl group, an organohydrogenpolysiloxane, and a platinum compound serving as a cross-linking catalyst. The addition-curable silicone rubber adhesive is cured by an addition reaction.
The adhesive constituting the adhesive layer 1e is a whitish adhesive to achieve the visibility against the black silicone rubber elastic layer 1d containing carbon by causing the adhesive to enter the recessed portion 1L formed through the laser marking treatment. Specifically, the lightness (L*) is 60 or more. The lightness (L*) is the same index as the lightness (L*) of the rubber layer 1d, and can be measured with the same instrument.
In this embodiment, the silicone rubber elastic layer 1d containing carbon has a dark color such as black compared with the intrinsic color of silicone rubber (iron red), and thus the lightness (L*) is low (lightness (L*): 15 or less). Therefore, in the case where the background color is a color of the silicone rubber elastic layer 1d, when the marked portion (letter portion) 1L is a white letter portion whose lightness (L*) of the L*ab color space is large (lightness (L*): 60 or more), the color difference (dE) increases and the visibility of the marked portion 1L considerably improves.
In this embodiment, for the purpose of achieving good visibility of the marked portion 1L, the difference in lightness (L*) between the rubber layer 1d and the adhesive layer 1e is, for example, 45 or more.
The coloring agent contained in the adhesive is a white pigment such as titanium oxide (titanium white), flowers of zinc (zinc white), lithopone, and white lead.
In this embodiment, an addition-curable silicone rubber adhesive “DOW CORNING (R) SE 1819 CV A/B (manufactured by Dow Corning Toray Co., Ltd.)” is used as the adhesive that satisfies above conditions.
In this embodiment, a fluorine-based resin tube is used as the fluorine-based resin layer (release layer) 1f. The fluorine-based resin tube is made of, for example, a tetrafluoroethylene-perfluoro(alkyl vinyl ether) copolymer (PFA), polytetrafluoroethylene (PTFE), or a tetrafluoroethylene-hexafluoropropylene copolymer (FEP). In this embodiment, PFA is used in view of moldability and toner releasability.
The thickness of the fluorine-based resin layer 1f is, for example, 50 μm or less. This is because, when the fluorine-based resin layer 1f is stacked on the rubber layer 1d, the elasticity of the rubber layer 1d serving as a lower layer can be maintained and an excess increase in the surface hardness of the fixing belt 1 can be suppressed. The inner surface of the fluorine-based resin tube 1f can be subjected to a sodium treatment, an excimer laser treatment, an ammonia treatment, or the like in advance to improve the adhesiveness.
The light transmittance (visible light transmittance) of the fluorine-based resin layer 1f is, for example, 60% or more. This is because the visibility of the marked portion 1L located below the fluorine-based resin layer 1f is prevented from being degraded. The light transmittance can be measured with an ultraviolet-visible-near infrared (UV-Vis-NIR) spectrophotometer. The phrase “the light transmittance (visible light transmittance) is 60% or more” means that the transmittance in the entire wavelength region of 380 nm to 750 nm is 60% or more in the obtained spectrum data.
The three steps in
In the first step in
In the second step, a vacuum (negative pressure relative to atmospheric pressure) is formed in a gap portion between the outer surface of the fluorine-based resin tube 1f and the inner surface of the expansion mold K. In the vacuum (5 kPa), the fluorine-based resin tube 1f is expanded in the radial direction and thus the outer surface of the fluorine-based resin tube 1f is brought into close contact with the inner surface of the expansion mold K.
In the third step, the intermediate product formed through the three steps in
In the fourth step, after the cylindrical base member 1b on which the rubber layer 1d has been stacked is placed inside the expanded fluorine-based resin tube 1f, the vacuum (negative pressure relative to atmospheric pressure) in the gap portion between the outer surface of the fluorine-based resin tube 1f and the inner surface of the expansion mold K is released.
When the vacuum is released, the increased diameter of the fluorine-based resin tube 1f decreases to a diameter substantially equal to the outside diameter of the cylindrical base member 1b on which the rubber layer 1d has been stacked. Thus, the fluorine-based resin tube 1f and the rubber layer 1d are brought into close contact with each other.
In the fifth step, the fluorine-based resin tube 1f is stretched in the longitudinal direction to a predetermined stretching ratio. When the fluorine-based resin tube 1f is stretched, the adhesive present between the fluorine-based resin tube 1f and the rubber layer 1d serves as a lubricant, and thus the fluorine-based resin tube 1f can be smoothly stretched. In this embodiment, the stretching ratio of the fluorine-based resin tube 1f in the longitudinal direction is 8%. As a result of stretching the fluorine-based resin tube 1f in the longitudinal direction in such a manner, creases are not easily formed on the fluorine-based resin tube 1f while the fixing device is operated. Consequently, a fixing belt having high durability can be produced.
In the sixth step, since a force is exerted on the fluorine-based resin tube 1f so that the length of the fluorine-based resin tube 1f returns to the original length, the fluorine-based resin tube 1f is temporarily fixed by being pressed and heated from the outside using a metal piece M including a heater. The temperature of the metal peace M during the pressing/heating is 200° C. and the pressing/heating time is 20 seconds.
In the seventh step, an excess amount of the adhesive present between the rubber layer 1d and the fluorine-based resin layer 1f is squeezed out. Through the squeezing step, the thickness X (
In the eighth step, a heat treatment is performed in an electric furnace for a predetermined time. As a result, the adhesive is cured to form an adhesive layer 1e.
In the final step, the fixing belt 1 is cut into a desired length.
Through the above steps, the fixing belt 1 is produced.
Hereafter, the effects of this embodiment will be investigated based on Examples 1 and 2 and Comparative Example.
An N-methyl-2-pyrrolidone solution of a polyimide precursor made of 3,3′,4,4′-biphenyltetracarboxylic dianhydride and p-phenylenediamine was prepared as a polyimide precursor solution. The precursor solution was applied onto an inner surface of a cylindrical base member 1b made of a nickel-iron alloy and having an inside diameter of φ30 mm, a thickness of 40 μm, and a length of 400 mm, and fired at 200° C. for 20 minutes to perform imidation. Thus, an inner sliding layer 1a having a thickness of 20 μm was formed.
A hydrosilyl-based silicone primer (DY39-051 A/B manufactured by Shin-Etsu Chemical Co., Ltd.) was applied onto the surface of the cylindrical base member 1b and fired at 200° C. for 5 minutes.
An addition-curable silicone rubber (rubber layer 1d) was applied onto the silicone primer so as to have a thickness of 300 μm and fired at 200° C. for 30 minutes. The addition-curable silicone rubber is obtained by adding an inorganic filler and a carbon fiber to an undiluted addition-curable silicone rubber liquid (a liquid prepared by equally mixing an “A liquid” and a “B liquid” of SE1886 (trade name) manufactured by Dow Corning Toray Co., Ltd.). Specifically, high-purity spherical alumina (trade name: “Alunabeads CB-A25BC” manufactured by Showa Titanium Co., Ltd.) was added as the inorganic filler so that the volume ratio of the spherical alumina was 25% relative to the cured rubber layer 1d. Subsequently, a carbon fiber (trade name: “VGCF-S” manufactured by SHOWA DENKO K.K.) produced by a vapor deposition method was further added so as to have a volume ratio of 2.0%, and kneading was performed. The lightness (L*) of the rubber layer 1d was 5 because of the addition of the carbon fiber.
After the temperature was decreased to room temperature, a portion (near one end of the rubber layer in the longitudinal direction) to be a non-image-forming region of the formed rubber layer 1d was irradiated with laser beams using ML-G9300 manufactured by KEYENCE CORPORATION to form a marked portion 1L. As a result, the depth of the marked portion 1L was 50 μm.
An addition-curable silicone rubber adhesive (obtained by equally mixing an “A liquid” and a “B liquid” of SE1819CV (trade name) manufactured by Dow Corning Toray Co., Ltd.) containing a white pigment and thus having a lightness (L*) of about 80 to 95 was prepared and applied.
The adhesive constituting an adhesive layer 1e was substantially uniformly applied so as to have a thickness of about 10 μm.
Subsequently, a fluorine-based resin tube having a length of 400 mm, an inside diameter of 29 mm, and a thickness of 25 μm was prepared as a fluorine-based resin layer 1f and stacked thereon. The fluorine-based resin tube used was obtained by extruding a fluorine-based resin pellet (trade name: Teflon PFA451HPJ manufactured by Du Pont-Mitsui Fluorochemicals Company, Ltd.). The light transmittance (visible light transmittance) of the fluorine-based resin layer 1f was 70%.
An excess amount of the adhesive was then removed by uniformly squeezing the fluorine-based resin tube 1f to sufficiently decrease the thickness of the adhesive layer 1e. Subsequently, heating was performed for one hour in an electric furnace whose temperature was set to 200° C. to cure the adhesive. Thus, the fluorine-based resin tube 1f was adhered to the rubber layer 1d.
Consequently, the difference in lightness (L*) between the rubber layer 1d and the adhesive was 75 or more. Since the marked portion 1L had a white color as opposed to a black color of the background and the light transmittance of the fluorine-based resin layer 1f was high, a fixing belt 1 having a marked portion 1L with excellent visibility could be produced.
Example 2 was the same as Example 1, except that the adhesive used was prepared by adding 5 wt % of alumina serving as a pigment to a transparent addition-curable silicone rubber adhesive (obtained by equally mixing an “A liquid” and a “B liquid” of SE1740 (trade name) manufactured by Dow Corning Toray Co., Ltd.).
When alumina was added in such a manner, the adhesive turned pink and the lightness (L*) of the adhesive was about 60 to 75. That is, the difference in lightness (L*) between the rubber layer 1d and the adhesive was 55 or more. Even if such an adhesive was used, the marked portion 1L had a pink color as opposed to a black color of the background and furthermore the light transmittance of the fluorine-based resin layer 1f was high. Therefore, a fixing belt 1 having a marked portion 1L with good visibility could be produced.
Comparative Example will be described with reference to
Comparative Example was the same as Example 1, except that the adhesive used was prepared by adding 5 wt % of iron red serving as a pigment to a transparent addition-curable silicone rubber adhesive (obtained by equally mixing an “A liquid” and a “B liquid” of SE1740 (trade name) manufactured by Dow Corning Toray Co., Ltd.).
When iron red was added in such a manner, the adhesive turned reddish brown and the lightness (L*) of the adhesive was about 25 to 40. Consequently, the difference in lightness (L*) between the rubber layer 1d and the adhesive was 20 to 35.
In Comparative Example, as illustrated in
Table collectively shows the investigation results of Examples 1 and 2 and Comparative Example.
In Examples 1 and 2, when a dark (black) rubber layer 1d is used, the marked portion 1L is brightly viewed compared with the surrounding portion (high contrast), and thus the visibility is improved. In contrast, in Comparative Example, when a dark (black) rubber layer 1d is used, the marked portion 1L is not brightly viewed compared with the surrounding portion (low contrast), and thus the visibility is poor.
While the present disclosure has been described with reference to exemplary embodiments, it is to be understood that the disclosure is not limited to the disclosed exemplary embodiments. The scope of the following claims is to be accorded the broadest interpretation so as to encompass all such modifications and equivalent structures and functions.
This application claims the benefit of Japanese Patent Application No. 2015-044051, filed Mar. 5, 2015, which is hereby incorporated by reference herein in its entirety.