Patent Application
20220205128
This non-provisional application claims priority under 35 U.S.C. § 119(a) on Patent Application No(s).109146382 filed in Taiwan, R.O.C. on Dec. 28, 2020, the entire contents of which are hereby incorporated by reference.
The present disclosure relates to an electropolishing treatment method, and in particular to an electropolishing treatment method for a stainless steel workpiece.
Metal additive manufacturing is one of the key technologies in the current manufacture of ultra-precision metal components, which can effectively meet the processing needs of high-value molds, special specification metal components and complex structural morphologies and internal flow channels, and is the developmental trend of the metal precision processing industry in the future. Among them, the metal additive manufacturing 17-4PH® stainless steel workpiece has become one of the main application materials of national defense, aerospace and medical industry in the future because of its high strength, hardness, ductility and corrosion resistance. However, the above-mentioned industries have a considerably high requirement for the dimensional accuracy of the metal additive manufacturing 17-4PH® stainless steel workpiece, and have a higher requirement for the flatness and roughness of the workpiece surface, especially in the complex twisting surface and sheet characteristics of the blade workpiece, it has a deeper technical difficulty. The reason is that improving the surface roughness of the material can not only prevent the stress concentration caused by material surface defects, but also reduce mechanical vibration and wear, and can further increase the service life of the workpiece material.
Although the metal additive manufacturing can produce metal products that have complex morphologies, complex flow channels and internal structure, the products have the disadvantage of excessive surface roughness, so it is necessary to carry out the subsequent processing to meet the needs of commercialization. Current precision grinding and polishing processes such as grinding, lapping, mechano-chemical polishing, chemo-mechanical polishing, all have shape and precision limitations, and the phenomenon of processing deterioration layers and residual stresses will occur. Although the electropolishing surface treatment process has the advantages of no processing deterioration layer produced on the polishing surface, no additional stress and capable of processing complex shape and small workpieces, it is important that electropolishing technology is also affected by metal surface structure, electrolyte formulation, temperature, current density and voltage, etc. All the above parameters may easily cause the uneven dissolution of the anode in the electropolishing process, which causes that the polishing workpiece fails to achieve the expected roughness and gloss. In other words, there is no good electropolishing treatment method for the 17-4PH® stainless steel produced by the additive manufacturing and the flatness and roughness of the surface of the stainless objects.
In view of the disadvantages of the above-mentioned prior art, a main object of the present disclosure is to provide an electropolishing treatment method for a stainless steel workpiece, so that the average surface roughness of the stainless steel workpiece can reach a level <1.6 μm.
Another object of the present disclosure is to provide a two-stage electropolishing treatment method for a stainless steel workpiece, which can solve the problems of residual stress and processing direction produced by traditional machining, so that the surface properties of the whole workpiece are homogeneous.
A further object of the present disclosure is to provide a two-stage electropolishing treatment method for a stainless steel workpiece, the electrolyte formulation is mainly composed of acidic solution and ethanol solution, the operation is simple and the solution formulation is easy to obtain, and automatic electropolishing processes can be introduced in the future, a number of workpieces can be simultaneously polished and leveled in a short period of time, in order to achieve the purpose of high efficient production.
To achieve the above objects, an electropolishing treatment method for a stainless steel workpiece provided according to the present disclosure comprises the following steps: placing the stainless steel workpiece in an oxalic acid solution and performing supersonic oscillation; performing a first electropolishing treatment to the stainless steel workpiece, wherein the first electropolishing treatment uses the stainless steel workpiece as an anode and 10% to 15% perchloric acid as an electrolyte, and when a constant voltage is set as 12V to 15V, the first electropolishing treatment procedure is performed; and performing a second electropolishing treatment to the stainless steel workpiece, wherein the second electropolishing treatment uses the stainless steel workpiece after the first electropolishing treatment as an anode, and an electrolyte consists of ethanol, sulfuric acid and perchloric acid, and when a constant voltage is set as 12V to 15V, the second electropolishing treatment is performed to obtain the stainless steel workpiece after the second electropolishing treatment.
In the above description, the electrolyte of the second electropolishing treatment consists of 90% to 93% ethanol, 4% to 7% sulfuric acid and 2% to 3% perchloric acid.
In the above description, the time of the first electropolishing treatment is between 5 and 10 minutes.
In the above description, the time of the second electropolishing treatment is between 15 and 20 minutes.
In the above description, the stainless steel workpiece is a workpiece produced by an additive manufacturing equipment.
In the above description, the stainless steel workpiece is a 17-4PH® stainless steel workpiece.
In the above description, the stainless steel workpiece is a stainless steel workpiece of heat treatment state or additive manufacturing state.
In the above description, the time of the supersonic oscillation is between 60 and 70 minutes.
The above summary description and the following detailed description and the accompanying drawings are the way, means and effect made for further describing the disclosure which can achieve a predetermined object. Other objects and advantages of the disclosure will become apparent from the following description and the drawings.
The implementation of the disclosure is further described by the specific embodiments as below, and a person having ordinary skill in the art can easily understand other advantages and effects of the present disclosure by the content of the specification. Furthermore, unless otherwise specified, the concentration “%” indicated in the present specification is “volume percentage concentration %”.
The disclosure provides an electropolishing treatment method for a stainless steel workpiece, referring to
As shown in
First, the additive manufacturing 17-4PH® stainless steel workpiece is placed in 10% oxalic acid solution to perform supersonic acid cleaning for 1 hour, and then the workpiece is used as an anode, placed in an electrolyte of 10% to 15% perchloric acid to perform electropolishing at a constant voltage of 12V for 10 minutes.
The additive manufacturing 17-4PH® stainless steel workpiece that is finished through the first electropolishing is placed in an electrolyte (electrolyte consists of 90% to 93% ethanol, 4% to 7% sulfuric acid and 2% to 3% perchloric acid) to perform electropolishing at a constant voltage of 12V for 20 minutes.
The cathode in the embodiment, for example, may be but not limited to a platinum electrode, graphite electrode, titanium electrode or tungsten gold electrode.
Referring
As shown in
The electropolishing working steps of the disclosure can be divided into three steps, the workpiece sample is placed at the anode, when electropolishing, the workpiece sample at the anode produces a dissolution reaction to perform steps of leveling, smoothing and glossing, in order to achieve the polishing effect, and the principle of each step is described below.
At the beginning of the reaction, the surface of the test plate is rough, at this time the electric field intensity at the high point of the metal surface is large, the high point of the surface occurs dissolved phenomenon, on the contrary, the low point is less affected by the dissolution speed because of the low electric field intensity, the de-leveling effect of this stage is the largest in the overall process. After a period of reaction, the initial leveling effect can be achieved, and this step also removes surface impurities.
When the reaction enters this stage, metal ions are released from the surface of the object at the time of electrolysis, dissolved into the electrolyte, combined to acid group ions in the electrolyte to form a film (barrier layer) of the reaction product on the anode surface, which will vary depending on the electrolyte. Although the thickness of the barrier layer is thin, the resistance caused by the barrier layer is very high, the same a height difference is formed on the surface as treated, resulting in the dissolution at the high point, a small electric field concentration at the low point because of a protective effect. After the high point of the substrate surface is dissolved for a long time, the height difference of the surface is gradually shortened, so as to achieve the smoothing effect of the surface.
The step is used to eliminate the microroughness surface of the surface. In this stage, the viscous layer distributed on the substrate surface is the site where trace polishing occurs. At this time, the anode current density becomes very small, resulting in a trace amount of removal at the microscopic high point, while a protective effect is formed at the low point, it does not produce dissolution, so that the substrate achieves a brightening effect.
As one of the key materials for national defense, aviation and medical industry in the future, that is, the additive manufacturing 17-4PH® stainless steel, and the present disclosure was carried out based on the needs of the above-mentioned precision processing industry. Therefore, an additive manufacturing plant or precision parts processing plant can adopt the present disclosure, the product is widely used and has a great prospect of economic profit.
The above embodiments of the disclosure made only by way of example to describe the feature and effect of the disclosure, and it should not be considered as the scope of substantial technical content is limited thereby. Various possible modifications and alternations of the embodiments could be carried out by the those of ordinary skill in the art without departing from the spirit and scope of the disclosure. Therefore, the scope of the disclosure is based on the appended claims.