Embossed monolayer particleboards and methods of preparation thereof

Information

  • Patent Grant
  • 9162369
  • Patent Number
    9,162,369
  • Date Filed
    Tuesday, October 20, 2009
    15 years ago
  • Date Issued
    Tuesday, October 20, 2015
    9 years ago
Abstract
There is provided an embossed particleboard, which can be used, for example, as a siding. The particleboard comprises a monolayer embossed particleboard including wood particles having an average size of less than 4 mm, a resin, and optionally a sizing agent. There is also provided a method of manufacturing a wood-based product such as a siding. The method comprises embossing and pressing in a single step a monolayer mat comprising wood particles having an average size of less than 4 mm and a resin, so as to obtain an embossed monolayer particleboard siding.
Description
FIELD OF THE DISCLOSURE

The present disclosure relates to the field of transformed wood-based materials. More specifically, the disclosure relates to embossed monolayer particleboards that can be used as siding.


BACKGROUND OF THE DISCLOSURE

Siding such as exterior siding of a building can be made of various materials. Many siding products encountered on the market are wood-based products. Such wood-based products include High Density Fiberboard (HDF) siding, Medium Density Fiberboard (MDF) siding, hardboard siding (Canaxel™) and Oriented Strand Board (OSB) siding. In order to provide these products with an interesting look such as a look that imitates natural wood, some manufacturers decided to emboss the siding so as to provide a wood grain embossing pattern to the siding.


However, the technologies that are available in order to prepare such products comprise important drawbacks. In a general manner, such products are prepared by using processes that comprise several steps and that are quite complicated. This also explains the relatively high price of the embossed siding.


Embossed MDF or HDF siding has interesting mechanical properties and it can be easily machined but its production costs are quite high since fibers must be refined.


It would thus be desirable to be provided with an alternative to the existing siding.


SUMMARY OF THE DISCLOSURE

In accordance with one aspect there is provided an embossed particleboard. The particleboard comprises a monolayer embossed particleboard including wood particles having an average size of less than about 4 mm, a resin, and optionally a sizing agent. Such a particleboard can be used for preparing various transformed wood-based materials such as siding, flooring material, outdoor furniture, outside moulding, road and commercial signs, and fencing etc.


In accordance with another aspect, there is provided an embossed particleboard. The particleboard is a monolayer embossed particleboard comprising wood particles having an average size of less than about 4 mm, a resin, and optionally a sizing agent.


In accordance with another aspect there is provided a method of manufacturing a wood-based siding. The method comprises embossing and pressing in a single step a monolayer mat comprising wood particles having an average size of less than about 4 mm and a resin, so as to obtain an embossed monolayer particleboard siding.


In accordance with another aspect there is provided a method of manufacturing a wood-based siding comprising:

    • obtaining wood particles having an average thickness of less than about 1 mm, an average length of less than about 40 mm, an average width of less than about 15 mm, and a moisture content of less than about 5%;
    • screening the wood particles through a 2 mm×2 mm square mesh so as to obtain screened wood particles;
    • mixing the screened wood particles with a resin and optionally with a sizing agent so as to obtain a mixture;
    • forming a monolayer mat with the mixture;
    • prepressing the monolayer mat so as to at least partially remove air therefrom; and
    • embossing and pressing under heat and pressure, in a single step, the monolayer mat so as to obtain an embossed monolayer particleboard siding.


In accordance with another aspect there is provided a method of manufacturing a wood-based siding comprising:

    • obtaining wood particles having an average thickness of less than about 1 mm, an average length of less than about 40 mm, an average width of less than about 15 mm, and a moisture content of less than about 5%;
    • screening the wood particles through a 2 mm×2 mm square mesh so as to obtain screened wood particles;
    • mixing the screened wood particles with a resin and optionally with a sizing agent so as to obtain a mixture;
    • forming a monolayer mat with the mixture by distributing the wood particles in the mat in such a manner that the smaller wood particles are mainly present at surfaces of the board and that larger particles are mainly present in a central portion of the board;
    • prepressing the monolayer mat so as to at least partially remove air therefrom; and
    • embossing and pressing under heat and pressure, in a single step, the monolayer mat so as to obtain an embossed monolayer particleboard siding.


In accordance with another aspect there is provided a method of manufacturing a wood-based siding comprising:

    • obtaining wood particles having an average thickness of less than about 0.8 mm, an average length of less than about 30 mm, an average width of less than about 10 mm, and a moisture content of less than about 5%;
    • screening the wood particles through a 2 mm×2 mm square mesh so as to obtain screened wood particles;
    • mixing the screened wood particles with a resin and optionally with a sizing agent so as to obtain a mixture having a resin content of about 1% to about 15% by weight based on the dry wood particles weight, and a sizing agent content of about 0% to about 5% by weight based on the dry wood particles weight;
    • forming a monolayer mat with the mixture;
    • prepressing the monolayer mat so as to at least partially remove air therefrom; and
    • embossing and pressing under heat and pressure, in a single step, the monolayer mat so as to obtain an embossed monolayer particleboard siding.


It has been found that such methods allow for the production of a resistant siding at a low cost. It was also found that such a methods allow for the manufacture of siding that is suitable for use as exterior siding and that meet the standards of the industry (for example the CGSB 11.3 (87) standard). Such methods are particularly interesting since they are simple and they involve a limited number of steps since embossing and pressing can be carried out simultaneously using the same press. Moreover, since the wood particles used can be non-refined wood particles, the production costs are considerably lowered. Such a unique particleboard siding is also quite interesting in view of the fact that it includes only one layer of wood particles, that renders it more simple.







DETAILED DESCRIPTION OF THE DISCLOSURE

The following examples are presented in a non-limitative manner.


The expression “wood particles having an average size of less than about 4 mm” as used herein refers, for example, to wood particles that have been passed through a 4 mm×4 mm square mesh. For example, such wood particles can have an average length that is less than about 4 mm.


The expression “wood particles having an average size of less than about 2 mm” as used herein refers, for example, to wood particles that have been passed through a 2 mm×2 mm square mesh. For example, such wood particles can have an average length that is less than about 2 mm.


The expression “consisting essentially of” as used herein when referring to the particleboard means that such a particleboard can also comprise various components that do not materially affect or modify the mechanical and physical properties of the particleboard. Such components can be paint, protective layer(s), sealer, sizing agent, etc. Such components can also be, any components known to the person skilled in the art that when added in a certain quantity will not materially affect or modify the mechanical and physical properties of the particleboard.


The term “about” is intended to mean a reasonable amount of deviation of the modified term or expression such that the end result is not significantly changed. These terms of degree should be construed as including a deviation of at least ±5% of the modified term or expression if this deviation would not negate the meaning of the term or expression it modifies.


In the methods and particleboards disclosed in the present document, the mat can further comprise a sizing agent such as a wax. For example, the mat or board can comprise about 0.5% to about 7%, or about 1% to about 5% of wax by weight based on the dry wood particles weight. The mat or board can comprise about 0.5% to about 20%, about 0.9% to about 17%, about 1% to about 15%, about 8% to 20%, about 9 to 20% or about 10 to 15% of the resin by weight based on the dry wood particles weight. For example, the wood particles can be non-refined wood particles and they can exclude the presence of refined fibers. The wood particles can comprise saw dust, wood chips, wood flakes, wood flour, wood shavings, unrefined fibers, ground wood particles, cut wood particles, wood particles obtained from a dry process, or mixtures thereof. The particleboard can comprise a wood grain embossing pattern on at least one surface thereof. The particleboard can comprise a wood grain embossing pattern having an average relief depth of less than about 10 mm, less than about 5 mm, or less than about 3 mm, on at least one surface thereof. It can also be possible to provide a similar particleboard which is not embossed. The particleboard can have a bending strength of about 10 MPa to about 30 MPa, about 13 MPa to about 27 MPa, or about 20 MPa to about 25 MPa. The particleboard can have a bending strength of at least about 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, or 23 MPa. The particleboard can have an internal bond strength of about 0.2 to about 1.5 MPa, about 0.5 MPa to about 1.3 MPa, about 0.6 MPa to about 0.9 MPa, about 0.2 to about 0.8 MPa or about 0.4. to about 0.8 MPa. The particleboard can have an internal bond strength of at least about 0.2, 0.3, 0.4, 0.5, 0.6 or 0.7 MPa. The particleboard can have a density of about 500 kg/m3 to about 1000 kg/m3, of about 650 kg/m3 to about 950 kg/m3 or about 700 kg/m3 to about 900 kg/m3. The particleboard can have a thickness swelling of about 1% to about 4% about 2% to about 8% or about 3% to about 6%. The particleboard can have a thickness swelling of less than about 4, 3, 2.5 or 2%. The particleboard can have a hardness of at least about 2600, 2700, 2800, 2900, 3000, 3100 or 3200 N. The particleboard can have a hardness of about 2800 to about 4000 N or about 2800 to about 3800 N. The particleboard can have a lateral nail resistance of at least about 750, 850, 950, 1050 or 1150 N. The particleboard can have a lateral nail resistance of about 800 to about 1500 N, about 900 to about 1450 N, or about 1150 to about 1450 N. The particleboard can have an impact resistance of at least about 1000 mm, 1300 mm or 1600 mm. For example, the particleboard can be one that meets the requirements of the CGSB 11.3 (87) standard for a type 5 panel for an exterior wall application.


In the methods and particleboards disclosed in the present document, the average size of the wood particles can be, for example, less than about 3 mm, less than about 2 mm, about 0.1 mm to about 2 mm, about 0.3 mm to about 0.7 mm, or about 0.4 mm to about 0.6 mm. For example, the average length of the wood particles can be less than about 3 mm, less than about 2 mm, about 0.1 mm to about 2 mm, about 0.3 mm to about 0.7 mm, or about 0.4 mm to about 0.6 mm. The wood particles in the particleboard can be distributed in such a manner that the smaller wood particles are mainly present at surfaces of the board and that larger particles are mainly present in a central portion of the board.


In the methods disclosed in the present document, embossing and pressing can be carried out simultaneously in a steel belt press, a single opening press or a multiopenings press. The press can be adapted to emboss the mat on at least one surface thereof. For example, the press can be adapted to emboss only the upper or lower surface or it can be adapted to emboss both of them. The mat can be pressed at a temperature of about 150° C. to about 300° C., about 160° C. to about 250° C., or about 170° C. to about 240° C. Before the embossing and pressing, the mat can be treated so as to at least partially remove air inside the mat. For example, the mat can be formed by distributing the wood particles in the mat in such a manner that the smaller particles are mainly present at surfaces of the mat and that larger particles are mainly present in a central portion of the mat. Such a distribution can be made by using wind and/or mechanical power. Before mixing the resin with the wood particles so as to form the mat, the wood particles can be at least partially dried. For example, before mixing the resin with the wood particles so as to form the mat, the wood particles can be heat dried at a temperature of about 100° C. to about 275° C. until the wood particles have a moisture content of less than about 5% or of about 125° C. to about 250° C. until the wood particles have a moisture content of less than about 3%.


In the methods disclosed in the present document, before being dried, the wood particles can be grinded or chipped by means of a flaking machine, a knife ring flakers, or a hammermill machine so as to obtain particles having an average thickness of less than about 0.8 mm, an average length of less than about 30 mm and an average width less than about 10 mm. The methods of the present document can further comprise cooling the particleboard and piling it on at least one another particleboard The methods can also further comprise cooling the particleboard at a temperature of about 60° C. to about 120° C. The methods can further comprise cutting and/or milling the so-obtained particleboard. The methods can further comprise cutting the particleboard to a desired size. The methods can further comprise applying at least one protective layer (for example a waterproof layer) on at least one surface of the particleboard. The methods can further comprise applying at least one layer of paint on at least one surface of the particleboard. The methods can also comprise applying a prepress sealer. For example, such a prepress sealer can be applied before embossing and pressing the mat under heat and pressure.


The particleboard can exclude the presence of a printed pattern.


Production Process of an Embossed Monolayer Particleboard Siding


For example, an embossed monolayer particleboard for use as a siding can be made as follows:

    • 1—Raw Material Handling
      • a. The raw material used can be, for example, a mix of spruce, pine, fir, maple, birch, aspen and other types of wood obtained from different sawmills or wood transformation facilities around Sayabec, Quebec, Canada. The size of the wood obtained depends on the supplier—a supplier may send anything from logs to chips, shavings or sawdust, etc.
      • b. The bigger pieces of wood can be grinded or chipped using wood flaking machine or knife ring flakers to make particles having a thickness of less than about 0.8 mm, a length of less than about 30 mm and a width of less than about 10 mm.
    • 2—Drying Operation
      • a. The wood particles can then be dried in a heated dryer at a temperature of about 150° C. to about 230° C. to remove the water and to bring the moisture content of the wood about 1% to about 3% based on dry weight in a rotating cylinder drying unit.
    • 3—Screening Operation
      • a. The dry material can then be screened. For the siding production, only particles passing through a screen with 2 mm square mesh or other configuration in view to reach an average size of 2 mm are kept. The bigger particles can be sent to a wood grinding machine to be reduced to have a width and thickness both less than about 2 mm.
    • 4—Resin Blending and Wax Addition
      • a. The particles can then be sent to a blending unit where the resin and the wax is mixed in with the wood. For siding products, a phenol-formaldehyde adhesive that is graded for exterior application can be used. Various other resins suitable for exterior applications can also be useda. Resin loading tests have been done by using about 10% to about 15% based on the dry wood weight and wax of about 0% to about 5%.
    • 5—Mat Forming
      • a. The resinated particles can then be assembled together in a forming machine to create the wood mat or the wood cake. The forming can be done by distributing the small particles on the faces and to gradually have the bigger pieces in the middle of the mat. Such a distribution can be made by using wind and/or mechanical power.
    • 6—Prepressing Operation
      • a. A prepressing operation can be made so as to allow for removal of part of the air inside the mat and to give better compaction before entering the press.
      • b. A prepress sealer (for example a chemical sealer such as F-610-002′ from Akzo Nobel) can be sprayed on the mat so as to facilitate paint process of the finished board.
    • 7—Hot Pressing
      • a. The wood mat can then be pressed at high temperature (about 170 to about 240° C.) in an embossed single opening press until the resin is fully polymerized or cured.
    • 8—Board Cooling and Stacking
      • a. The boards exiting the press can then be slightly cooled down to a temperature of about 60° C. to about 120° C. and piled together.
      • b. The boards can then be cut to size and shipped for milling and painting process of the siding panel.


Several tests have been made in order to evaluate the various properties of the siding products described in the present document.


Evaluation of the Physical and Mechanical Properties of the Siding in Accordance with the CGSB 11.3 (87) Standard


The purpose of such tests was to evaluate the physico-mechanical properties of particle panels with a nominal thickness of 12.5 mm according to the CGSB 11.3 (87) standard.


Procedure and Results


The results of the tests were measured using electronic equipment and thus include a certain percentage of uncertainty within the limits prescribed by the different test standards. A series of tests including bend, tensile, and dimensional stability tests, and tests for resistance to aging, resistance to tearing by nails, and impact resistance were performed according to the standards CGSB 11.3 (87) and ASTM D-1037 (06a).


Sampling of the panels was performed for the physico-mechanical evaluations. The panels were numbered 1 to 10. The panels bearing odd numbers, that is, 1, 3, 5, 7, and 9, were placed in reserve, while the five others, that is, those bearing the numbers 2, 4, 6, 8, and 10, were cut into test specimens according to the dimensions prescribed in the standard before placing them into the conditioning chamber at 20° C. and 50% relative humidity until equilibrium was attained, before proceeding with the performance measurements.









TABLE 1







Physico-Mechanical Tests Performed on the Panels












Number of test





specimens
Dimensions



Specifications
per panel
(mm)














Swelling
4
 150 × 150



Linear expansion
2
 75 × 305



Bending (normal)
12
150 × 75



Bending (6 cycles)
12
150 × 75



Resistance to aging
12
150 × 75



Lateral resistance to nails
6
150 × 75



Resistance to nailhead
6
150 × 75



passage





Impact resistance
6
 229 × 254



Tensile, perpendicular
18
 50 × 50



(Internal bond strength)





Tensile, parallel
8
 50 × 254



Hardness
6
150 × 75










Test Results


The summaries of results for physico-mechanical performance are presented in Tables 2 to 9. The values given in parentheses indicate the coefficient of variation for each of the mean values.


In summary, the results for the collection of tests demonstrate that the panels evaluated meet the requirements of the CGSB 11.3 (87) standard for Type 5 panels used for exterior wall applications. Performance, in terms of hardness, dimensional stability, resistance to nails tearing, tensile strength, stiffness, and impact resistance, exceeds to a large extent the minimum required by the standard.


The results of accelerated aging tests (6-cycle method), which are presented in Table 6, show that the panels numbered 8 and 10 do not meet the 50% requirements for residual modulus of rupture (MOR) after the aging cycles. Panels 8 and 10 attained an average of 47% and 49%, respectively, for residual MOR, while panels 2, 4, and 6 attained averages of 65%, 51%, and 66%, respectively, for the residual MOR.









TABLE 2







Summary of Results from Hardness Tests













Normative
Measured




Panel
value
value




number
(N)
(N)
Passed?















2
2600
2946 (12)
Yes



4

3579 (14)
Yes



6

3541 (14)
Yes



8

2906 (6) 
Yes



10

3412 (16)
Yes





*Average of 6 hardness-test specimens per panel


The values given in parentheses indicate the coefficient of variation for each of the mean values.













TABLE 3







Summary of Results from Swelling Tests










Swelling rate (%)




(thickness swelling)
Absorption rate (%)













Panel
Nor-


Nor-
Meas-



number
mative
Measured*
Passed?
mative
ured*
Passed?
















2
8
2.3 (29)
Yes
20
12.6 (11)
Yes


4

2.3 (35)
Yes

11.4 (19)
Yes


6

2.3 (35)
Yes

11.5 (7) 
Yes


8

1.6 (16)
Yes

12.6 (1) 
Yes


10

1.9 (20)
Yes

10.9 (18)
Yes





*Average of 4 swelling-test specimens per panel


The values given in parentheses indicate the coefficient of variation for each of the mean values.













TABLE 4







Summary of Results from Nail-Tearing Tests










Lateral resistance (N)
Head passage (N)













Panel
Nor-


Nor-
Meas-



number
mative
Measured*
Passed?
mative
ured*
Passed?
















2
750
1404 (10)
Yes
750
1263 (10)
Yes


4

1276 (12)
Yes

1211 (15)
Yes


6

1301 (8) 
Yes

1226 (15)
Yes


8

1379 (15)
Yes

1196 (11)
Yes


10

1222 (21)
Yes

1153 (19)
Yes





*Average of 6 lateral-resistance test specimens and 6 head-passage test specimens for each panel


The values given in parentheses indicate the coefficient of variation for each of the mean values.













TABLE 5







Summary of Results from Tensile-Strength Tests










Perpendicular to the surface




(MPa)
Parallel to the surface



(internal bond strength)
(MPa)













Panel
Nor-


Nor-
Meas-



number
mative
Measured*
Passed?
mative
ured*
Passed?
















2
0.17
0.71 (10)
Yes
7.0
 9.1 (10)
Yes


4

0.64 (13)
Yes

12.5 (8)
Yes


6

0.75 (14)
Yes

 11.1 (13)
Yes


8

0.55 (17)
Yes

 9.1 (9)
Yes


10

0.62 (17)
Yes

12.0 (5)
Yes





*Average of 18 perpendicular tensile-test specimens and 7 tensile-test specimens parallel to the surface


The values given in parentheses indicate the coefficient of variation for each of the mean values.













TABLE 6







Summary of Results from Tests for Resistance to Aging (Bending)









Modulus of rupture after 6-cycle treatment












Modulus of rupture in dry state
Modulus of rupture




Panel
(MPa)
(MPa)
Loading (%)















number
Normative
Measured*
Passed
Normative
Measured
Normative
Calculated
Passed?


















2
13.0
23.0 (12)
Yes
N/A
14.9 (22)
50
65
Yes


4

22.8 (30)
Yes

11.6 (34)

51
Yes


6

22.7 (23)
Yes

15.0 (41)

66
Yes


8

23.6 (8) 
Yes

11.1 (13)

47
No


10

22.7 (20)
Yes

11.1 (41)

49
No





*Average of 12 test specimens per panel


The values given in parentheses indicate the coefficient of variation for each of the mean values.













TABLE 7







Summary of Results from Residual Swelling after Aging Tests










Panel
Residual swelling (%)












number
Normative
Measured*
Passed?















2
15
2.90 (36)
Yes



4

3.94 (23)
Yes



6

3.53 (23)
Yes



8

3.34 (27)
Yes



10

4.31 (41)
Yes





*Average of 12 test specimens per panel


The values given in parentheses indicate the coefficient of variation for each of the mean values.













TABLE 8







Summary of Results from Impact-Resistance Tests










Panel
Impact resistance (%)












number
Normative
Measured*
Passed?















2
350
Greater than
Yes



4

1680 mm
Yes



6

(maximum
Yes



8

capability of
Yes



10

equipment)
Yes





*Average of 6 test specimens per panel













TABLE 9







Summary of Results from Linear-Expansion Tests, 50-90% RH










Panel
Linear expansion (%)












number
Normative
Measured*
Passed?















2
0.30
0.21
Yes



4

0.18
Yes



6

0.22
Yes



8

0.17
Yes



10

0.17
Yes





*Average of 2 test specimens per panel






Table 10 presents a summary of results representing the average of 5 evaluated panels. In considering the results for the collection of tests performed, it can be concludes that the panels evaluated meet all the requirements of the CGSB 11.3 (87) standard for Type 5 panels used for exterior wall applications.









TABLE 10







Summary of Test Results











Properties

Normative

CGSB


evaluated
Description
value
Result
11.3-87















Nail tearing
Lateral resistance to
750
1316
(14)
Passed



nails (N)







Head passage (N)
750
1210
(14)
Passed


Dimensional
Resistance to water:
8.0
2.1
(28)
Passed


stability
swelling; 24 hr in







water (%)







Resistance to water:
20.0
11.8
(13)
Passed



absorption; 24 hr in







water (%)







Linear expansion (%),
0.30
0.19
(25)
Passed



50-90% RH






Bending
Resistance to aging:
15.0
3.6
(34)
Passed



residual swelling (%)







Modulus of rupture
13.0
23.0
(19)
Passed



(MPa)







Modulus of rupture: 6
N/A
12.7
(35)
N/A



cycles (MPa)







MOR*/MOR (%)
50
55
(25)
Passed


Tensile
Perpendicular (MPa)
0.17
0.65
(21)
Passed


strength
Parallel (MPa)
7.0
10.7
(16)
Passed


Hardness (N)
Textured surface
2600
3384
(14)
Passed



Smooth surface

3169
(17)
Passed











Impact resistance (mm)
350 mm
1680

Passed





*MOR Modulus of rupture for test specimens subjected to six aging cycles


The values given in parentheses indicate the coefficient of variation for each of the mean values.


The values given in parentheses indicate the coefficient of variation for each of the mean values.






In general, the samples of evaluated panels demonstrated that the physico-mechanical performance meets the requirements prescribed in the CGSB 11.3 standard for Type 5 (exterior covering).


REFERENCES



  • ASTM D-1037-06a. Annual book of ASTM standards; Section 4: Construction, 2008. West Conshohocken, Pa.: American Society for Testing and Materials, p. 120.

  • CGSB 11.3, Hard-fiber panels. Publications of the Government of Canada (May 1976), Canadian General Standards Board, Gatineau, Quebec.



Therefore, as demonstrated above, the particleboard siding as described in the present document meet all the requirements of the CGSB 11.3 (87) standard related to panels (type 5) for use as exterior siding. It has thus been shown that such exterior siding can be easily prepared, at low cost, in a single step. In terms of physical and mechanical properties, the siding of the present document has the same advantages than MDF or HDF panels (very resistant and easily machined) but such a siding also has the advantages of particleboards, they can be prepared at low costs. In other words, the siding of the present document possesses the advantages of MDF or HDF panels and particleboards (as indicated above) without having their disadvantages (high cost of MDF and HDF; and low resistance of particleboard).


The present disclosure has been described with regard to specific examples. The description was intended to help the understanding of the disclosure, rather than to limit its scope. It will be apparent to one skilled in the art that various modifications may be made to the disclosure without departing from the scope of the disclosure as described herein, and such modifications are intended to be covered by the present document.

Claims
  • 1. A method of manufacturing a wood-based siding, comprising: prepressing a material that consists of a monolayer mat consisting essentially of wood particles having an average size that is the same size or less than wood particles that have been pressed through a 4 mm×4 mm square mesh and a resin, the prepressing at least partially removing air therefrom; andembossing and pressing under heat and pressure in a press adapted to impart an embossing pattern to at least one surface of said siding, in a single step, the material that consists of the prepressed monolayer mat so as to obtain an embossed monolayer particleboard siding consisting essentially of said resin and wood particles and having said embossing pattern on at least one surface, wherein said wood particles exclude the presence of refined wood fibers and wherein said mat comprises about 0.5% to about 20% of the resin, based on the dry wood particles weight.
  • 2. The method of claim 1, wherein said embossing and pressing is carried out simultaneously in a single opening press.
  • 3. The method of claim 1, wherein said mat consists of said wood particles, said resin, and a sizing agent.
  • 4. The method of claim 1, wherein said mat is pressed at a temperature of about 170° C. to about 240° C.
  • 5. The method of claim 1, wherein said mat has about 0.5% to about 20% of said resin by weight based on the dry wood particles weight.
  • 6. The method of claim 1, wherein a sizing agent is present in said mat.
  • 7. The method of claim 1, wherein said mat is formed by distributing said wood particles in said mat in such a manner that the smaller particles are mainly present at surfaces of said mat and that larger particles are mainly present in a central portion of said mat.
  • 8. The method of claim 1, wherein the average size of said wood particles is the same size or less than wood particles that have been passed through a 2 mm×2 mm square mesh.
  • 9. The method of claim 1, wherein said method further comprises at least one of cutting and milling the so-obtained embossed monolayer particleboard siding, or said method further comprises applying at least one protective layer on at least one surface of said embossed monolayer particleboard siding.
  • 10. A method of manufacturing a wood-based siding comprising: obtaining wood particles having an average thickness of less than about 1 mm, an average length of less than about 40 mm, an average width of less than about 15 mm, and a moisture content of less than about 5%;screening said wood particles through a 2 mm×2 mm square mesh so as to obtain screened wood particles;mixing said screened wood particles with a resin so as to obtain a mixture;forming a monolayer mat with said mixture by distributing said wood particles in said mat in such a manner that the smaller wood particles are mainly present at surfaces of said board and that larger particles are mainly present in a central portion of said board;prepressing said monolayer mat so as to at least partially remove air therefrom;applying a prepress sealer to the prepressed monolayer mat; andembossing and pressing, in a single step, in a press adapted to impart an embossing pattern to at least one surface of said siding, a material that consists of said monolayer mat so as to obtain an embossed monolayer particleboard siding consisting essentially of said resin and wood particles and having an embossing pattern on at least one surface, wherein said wood particles exclude the presence of refined wood fibers and wherein said mat comprises about 0.5% to about 20% of the resin, based on the dry wood particles weight.
  • 11. The method of claim 1, wherein said embossing pattern is a wood grain embossing pattern.
  • 12. The method of claim 2, wherein said embossing pattern is a wood grain embossing pattern.
  • 13. The method of claim 10, wherein said embossing pattern is a wood grain embossing pattern.
  • 14. The method of claim 1, wherein said embossing pattern is a wood grain embossing pattern.
  • 15. The method of claim 10, wherein said method further comprises at least one of cutting and milling the so-obtained embossed monolayer particleboard siding, or said method further comprises applying at least one protective layer on at least one surface of said embossed monolayer particleboard siding.
  • 16. The method of claim 1, wherein said mat comprises about 8% to about 20% of the resin, based on the dry wood particles weight.
  • 17. The method of claim 1, wherein said mat comprises about 1% to about 15% of the resin, based on the dry wood particles weight.
  • 18. The method of claim 1, wherein said mat comprises about 10% to about 15% of the resin, based on the dry wood particles weight.
  • 19. The method of claim 10, wherein said mat comprises about 8% to about 20% of the resin, based on the dry wood particles weight.
  • 20. The method of claim 10, wherein said mat comprises about 10% to about 15% of the resin, based on the dry wood particles weight.
  • 21. The method of claim 1, further comprising before the embossing and pressing, applying a prepress sealer to the prepressed monolayer mat.
CROSS-REFERENCE TO RELATED APPLICATION

This application claims the benefit of U.S. provisional application No. 61/136,999 filed on Oct. 21, 2008 which is hereby incorporated by reference in its entirety.

US Referenced Citations (75)
Number Name Date Kind
3983307 Power et al. Sep 1976 A
4004767 Chilton Jan 1977 A
4007076 Clarke et al. Feb 1977 A
4112169 Huffman et al. Sep 1978 A
4236365 Wheeler Dec 1980 A
4955169 Shisko Sep 1990 A
5000673 Bach et al. Mar 1991 A
5008057 Risius et al. Apr 1991 A
5016416 Munk May 1991 A
5045262 Munk Sep 1991 A
5170603 Barlett Dec 1992 A
5213821 Munk May 1993 A
5217665 Lim et al. Jun 1993 A
5275682 Götz Jan 1994 A
5290621 Bach et al. Mar 1994 A
5344704 O'Dell et al. Sep 1994 A
5391340 Mirous et al. Feb 1995 A
5647934 Vaders et al. Jul 1997 A
5695875 Larsson et al. Dec 1997 A
5744079 Kimura et al. Apr 1998 A
5869138 Nishibori et al. Feb 1999 A
5908496 Singule et al. Jun 1999 A
5980798 Bonomo et al. Nov 1999 A
5989468 Lundgren et al. Nov 1999 A
5993709 Bonomo et al. Nov 1999 A
6007320 Froese et al. Dec 1999 A
6113729 Chiu Sep 2000 A
6132503 Singule et al. Oct 2000 A
6132656 Dodd Oct 2000 A
6187234 Bonomo et al. Feb 2001 B1
6197235 Miller et al. Mar 2001 B1
6312632 Graf Nov 2001 B1
6344101 Graf Feb 2002 B1
6364982 Lynch et al. Apr 2002 B1
6479128 Schafernak et al. Nov 2002 B1
6541097 Lynch et al. Apr 2003 B2
6569540 Preston et al. May 2003 B1
6579483 Vaders Jun 2003 B1
6605245 Dubelsten et al. Aug 2003 B1
6638459 Mente et al. Oct 2003 B2
6649098 Mente et al. Nov 2003 B2
6696167 Sean et al. Feb 2004 B2
6743318 Vaders Jun 2004 B2
6841231 Liang et al. Jan 2005 B1
6866740 Vaders Mar 2005 B2
6881771 Haas et al. Apr 2005 B2
6923999 Graf Aug 2005 B2
6972150 Vaders Dec 2005 B2
7077988 Gosselin Jul 2006 B2
7096916 Vaders Aug 2006 B2
7108031 Secrest Sep 2006 B1
7314585 Vaders Jan 2008 B2
7393480 Haas Jul 2008 B2
20010032432 Paxton et al. Oct 2001 A1
20040086678 Chen et al. May 2004 A1
20060264519 Eckert et al. Nov 2006 A1
20070175041 Hardwick et al. Aug 2007 A1
20070207296 Eisermann Sep 2007 A1
20100247943 Demeyere et al. Sep 2010 A1
20100310838 Ketzer et al. Dec 2010 A1
20100326583 Korai Dec 2010 A1
20110014414 Senior Jan 2011 A1
20110052905 Smith Mar 2011 A1
20110104431 Niedermaier May 2011 A1
20110104483 Shinozaki et al. May 2011 A1
20110117340 Oldorff May 2011 A1
20110139356 Pohe Jun 2011 A1
20110167744 Whispell et al. Jul 2011 A1
20110175251 Ziegler et al. Jul 2011 A1
20110177319 Ziegler et al. Jul 2011 A1
20110189448 Lindgren et al. Aug 2011 A1
20110217463 Oldorff Sep 2011 A1
20110217562 Peretolchin et al. Sep 2011 A1
20110220271 Fyie et al. Sep 2011 A1
20110223411 Pfau et al. Sep 2011 A1
Foreign Referenced Citations (64)
Number Date Country
1319883 Oct 1985 CA
2004182 May 1990 CA
2036584 Aug 1991 CA
2049396 Feb 1992 CA
2049397 Feb 1992 CA
1301618 May 1992 CA
2057476 Jun 1992 CA
1310801 Dec 1992 CA
2085175 Jun 1993 CA
2117529 Sep 1993 CA
2138546 Jan 1994 CA
1329872 May 1994 CA
2102959 Aug 1994 CA
2186264 Dec 1995 CA
2244005 Feb 1997 CA
2197696 Aug 1997 CA
2245946 Aug 1997 CA
2250161 Aug 1997 CA
2255894 Jan 1998 CA
2199463 Mar 1998 CA
2279852 Jul 1998 CA
2255784 Oct 1998 CA
2236633 Nov 1998 CA
2210125 Jan 1999 CA
2315008 Jun 1999 CA
2266246 Sep 1999 CA
2335204 Dec 1999 CA
2336649 Jan 2000 CA
2279808 Feb 2000 CA
2344041 Mar 2000 CA
2350526 May 2000 CA
2356893 Aug 2000 CA
2368091 Nov 2000 CA
2317281 Feb 2001 CA
2402003 Sep 2001 CA
2405674 Oct 2001 CA
2406170 Oct 2001 CA
2421037 Feb 2002 CA
2368328 Jul 2002 CA
2400836 Feb 2003 CA
2484852 Nov 2003 CA
2431292 Dec 2003 CA
2432881 Dec 2003 CA
2503553 May 2004 CA
2545008 May 2005 CA
2519489 Sep 2005 CA
2508148 Nov 2005 CA
102069523 May 2011 CN
2305462 Apr 2011 EP
2308678 Apr 2011 EP
2319688 May 2011 EP
939863 Oct 1963 GB
965108 Jul 1964 GB
1443194 Jul 1976 GB
2002086421 Mar 2002 JP
2010280152 Dec 2010 JP
2011062424 Jun 2011 KR
9928102 Jun 1999 WO
9967069 Dec 1999 WO
WO 2007061201 May 2007 WO
2009141743 Nov 2009 WO
2010055429 May 2010 WO
2011077518 Jun 2011 WO
2011082491 Jul 2011 WO
Non-Patent Literature Citations (3)
Entry
From Wikipedia, the free encyclopedia, “Particle board” [online], [retrieved on Aug. 10, 2012]. Retrieved from the Internet <URL: http://en.wikipedia.org/wiki/Particle—board>.
Berglung et al., Handbook of Wood Chemistry and Wood Composites, 2005, p. 279-301.
English Abstract of DE 19956765(A1), Nickel, E., May 31, 2000.
Related Publications (1)
Number Date Country
20100104813 A1 Apr 2010 US