Patent Application
20220250005
The present invention relates to an emission treatment catalysts and systems having a Diesel Oxidation Catalyst (DOC) positioned upstream from a Catalyzed Soot Filter (CSF), which is positioned upstream from a Selective Catalytic Reduction (SCR) catalyst. In one or more embodiments, the system provides an effective method of simultaneously remediating the nitrogen oxides (NOx), particulate matter, CO and gaseous hydrocarbons present in diesel engine exhaust streams.
Diesel engine exhaust is a heterogeneous mixture which contains not only gaseous emissions such as carbon monoxide (“CO”), unburned hydrocarbons (“HC”) and nitrogen oxides (“NOx”), but also condensed phase materials (liquids and solids) which constitute the so-called particulates or particulate matter. Often, catalyst compositions and substrates on which the compositions are disposed are provided in diesel engine exhaust systems to convert certain or all of these exhaust components to innocuous components. For example, diesel exhaust systems can contain one or more of a diesel oxidation catalyst, a soot filter and a catalyst for the reduction of NOR.
Oxidation catalysts that contain platinum group metals, base metals and combinations thereof are known to facilitate the treatment of diesel engine exhaust by promoting the conversion of both HC and CO gaseous pollutants and some proportion of the particulate matter through oxidation of these pollutants to carbon dioxide and water. Such catalysts have generally been contained in units called diesel oxidation catalysts (DOC's), which are placed in the exhaust of diesel engines to treat the exhaust before it vents to the atmosphere. In addition to the conversions of gaseous HC, CO and particulate matter, oxidation catalysts that contain platinum group metals (which are typically dispersed on a refractory oxide support) also promote the oxidation of nitric oxide (NO) to NO2.
The total particulate matter emissions of diesel exhaust are comprised of three main components. One component is the solid, dry, solid carbonaceous fraction or soot fraction. This dry carbonaceous matter contributes to the visible soot emissions commonly associated with diesel exhaust. A second component of the particulate matter is the soluble organic fraction (“SOF”). The soluble organic fraction is sometimes referred to as the volatile organic fraction (“VOF”), which terminology will be used herein. The VOF can exist in diesel exhaust either as a vapor or as an aerosol (fine droplets of liquid condensate) depending on the temperature of the diesel exhaust. It is generally present as condensed liquids at the standard particulate collection temperature of 52° C. in diluted exhaust, as prescribed by a standard measurement test, such as the U.S. Heavy Duty Transient Federal Test Procedure. These liquids arise from two sources: (1) lubricating oil swept from the cylinder walls of the engine each time the pistons go up and down; and (2) unburned or partially burned diesel fuel.
The third component of the particulate matter is the so-called sulfate fraction. The sulfate fraction is formed from small quantities of sulfur components present in the diesel fuel and oil. Small proportions of SO3 are formed during combustion of the diesel fuel, which in turn combines rapidly with water in the exhaust to form sulfuric acid. The sulfuric acid collects as a condensed phase with the particulates as an aerosol, or is adsorbed onto the other particulate components, and thereby adds to the mass of TPM.
One key aftertreatment technology in use for high particulate matter reduction is the diesel particulate filter. There are many known filter structures that are effective in removing particulate matter from diesel exhaust, such as honeycomb wall flow filters, wound or packed fiber filters, open cell foams, sintered metal filters, etc. However, ceramic wall flow filters, described below, receive the most attention. These filters are capable of removing over 90% of the particulate material from diesel exhaust. The filter is a physical structure for removing particles from exhaust, and the accumulating particles will increase the back pressure from the filter on the engine. Thus, the accumulating particles have to be continuously or periodically burned out of the filter to maintain an acceptable back pressure. Unfortunately, the carbon soot particles require temperatures in excess of 500° C. to burn under oxygen rich (lean) exhaust conditions. This temperature is higher than what is typically present in diesel exhaust.
Provisions are generally introduced to lower the soot burning temperature in order to provide for passive regeneration of the filter. The presence of a catalyst promotes soot combustion, thereby regenerating the filters at temperatures accessible within the diesel engine's exhaust under realistic duty cycles. In this way a catalyzed soot filter (CSF) or catalyzed diesel particulate filter (CDPF) is effective in providing for >80% particulate matter reduction along with passive burning of the accumulating soot, and thereby promoting filter regeneration.
Future emissions standards adopted throughout the world will also address NOx reductions from diesel exhaust. A proven NOx abatement technology applied to stationary sources with lean exhaust conditions is Selective Catalytic Reduction (SCR). In this process, NOx is reduced with ammonia (NH3) to nitrogen (N2) over a catalyst typically composed of base metals. The technology is capable of NOx reduction greater than 90%, and thus it represents one of the best approaches for achieving aggressive NOx reduction goals. SCR is under development for mobile applications, with urea (typically present in an aqueous solution) as the source of ammonia. SCR provides efficient conversions of NOx as long as the exhaust temperature is within the active temperature range of the catalyst, the operating window.
New emission regulations for diesel engines around the world are forcing the use of more advanced emission controls systems. These systems will need to reduce both total particulate matter and NOx by about 90 percent. The engine manufacturers have multiple emission system options to meet the new regulations but one option is the combination of an active filter system for particulate reduction and a selective catalytic reduction system.
One system configuration that has been proposed in the literature involves a diesel oxidation catalyst (DOC) positioned downstream from the engine, a catalyzed soot filter (CSF) positioned downstream from the DOC, a reductant injection system position downstream from the CSF, a selective catalytic reduction (SCR) catalyst positioned downstream from the reductant injection system, and an optional ammonia oxidation (AMOX) catalyst positioned downstream from the SCR catalyst. The system also typically includes a hydrocarbon injection system located downstream from the engine and upstream from the DOC.
This system configuration offers several advantages for the overall system functionality. Having the DOC in the first position allows it to be placed as close as possible to the engine ensuring rapid heat up for cold start HC and CO emissions and the maximum DOC inlet temperature for active filter regeneration. The CSF being in front of the SCR will prevent particulate, oil ash and other undesirable materials from being deposited on the SCR catalyst thus improving its durability and performance. Having oxidation catalysts in front of the SCR allows for an increase in the NO2 to NO (or NO2 to NOx ratio entering the SCR which is known to increase the reaction rate of the NOx reduction occurring in the SCR if properly controlled. An example of such a system is described in United States Patent Application Publication Number 2005/0069476.
There is an ongoing need to investigate and provide alternative system strategies to improve the treatment of exhaust gas streams containing NOx and particulate matter.
Applicants have determined that in systems such as the type in which a DOC is located upstream from a CSF, which is located upstream from an SCR catalyst, the optimal control of the NO to NO2 ratio entering the filter can be an issue with the large volume of oxidation catalyst that is present in the DOC and CSF in front of the SCR. According to one or more embodiments of the invention, better control of the NO to NO2 ratio of the exhaust gas flowing into the SCR is provided by using a novel diesel oxidation catalyst.
Embodiments of the invention are directed to diesel oxidation catalysts comprising an inlet zone with an axial length and an outlet zone with an axial length. The inlet zone comprises at least one of platinum and palladium in a first loading. The outlet zone comprises palladium in a second loading. The outlet zone comprises substantially no platinum. The first loading being greater than the second loading and the axial length of the inlet zone being less than or equal to the axial length of the outlet zone.
In some embodiments, upon passing an exhaust stream through the catalyst, substantially no additional NO2 is produced over about 90% of the operating window of the catalyst.
In some embodiments, the axial length of the inlet zone is about half the axial length of the outlet zone. In other embodiments, the axial length of the inlet zone is about equal to the axial length of the outlet zone. In further embodiments, the axial length of inlet zone is at least about 10% of the total length of the catalyst. In additional embodiments, the axial length of the inlet zone is at least about 20% of the total length of the catalyst. In various embodiments, the total length of the inlet zone is at least about 40% of the total length of the catalyst. In other embodiments, the axial length of the inlet zone is less than about 35% of the total length of the catalyst.
According to one or more embodiments, the inlet zone has a platinum to palladium ratio equal to or greater than about 10:1.
In some embodiments, the first loading is greater than about 30 g/ft3. In some embodiments, the second loading is less than about 30 g/ft3.
The catalyst of one or more embodiments is disposed on a flow-through substrate.
In some embodiments, one or more of the inlet zone and the outlet zone further comprises a base metal oxide. In some embodiments, one or more of the inlet zone and the outlet zone further comprises ceria.
According to various embodiments, the inlet zone comprises platinum and palladium in a ratio of at least 2:1 and the outlet zone comprises substantially only palladium.
In detailed embodiments, the inlet zone comprises platinum and palladium in a ratio of about 10:1 with a loading of about 80 g/ft3 and the outlet zone comprises substantially only palladium with a loading of about 5 g/ft3.
In specific embodiments, the inlet zone and the outlet zone comprise substantially only palladium.
In detailed embodiments, one or more of the inlet zone and the outlet zone further comprises rhodium.
Additional embodiments of the invention are directed to methods of treating an exhaust stream from a diesel engine comprising NOx and particulate matter. The method comprising flowing the exhaust stream through the catalyst described herein. Briefly, a diesel oxidation catalysts comprising an inlet zone with an axial length and an outlet zone with an axial length. The inlet zone comprises at least one of platinum and palladium in a first loading. The outlet zone comprises palladium in a second loading. The outlet zone comprises substantially no platinum. The first loading being greater than the second loading and the axial length of the inlet zone being less than or equal to the axial length of the outlet zone. In detailed embodiments, the catalyst is effective to produce substantially no additional NO2 in the exhaust gas stream after passing through the catalyst over about 90% of the operating window of the catalyst.
Further embodiments of the invention are directed to methods of making a diesel oxidation catalyst. A first slurry comprising platinum and palladium is prepared. A second slurry comprising palladium is prepared. A inlet zone of a substrate is washcoated with the first slurry to a first loading, the inlet zone having an axial length. An outlet zone of the substrate is washcoated with the second slurry to a second loading, the outlet zone having an axial length. The first loading is greater than the second loading and the axial length of the inlet zone is less than or equal to the axial length of the outlet zone.
Other embodiments of the invention are directed to systems for treating an exhaust stream comprising NOx from an engine. The system comprises the diesel oxidation catalyst described herein being disposed downstream of the engine.
In some detailed embodiments, the system further comprising a catalyzed soot filter disposed downstream of the diesel oxidation catalyst. The catalyzed soot filter having a plurality of longitudinally extending passages bounded by longitudinally extending walls. The passages comprising inlet passages having an open inlet end and a closed outlet end, and outlet passages having a closed inlet end and an open outlet end. The catalyzed soot filter comprising a catalyst composition on the walls. The catalyzed soot filter effective to optimize the ratio of NO to NO2 exiting the filter.
In some detailed embodiments, the system further comprises a selective catalytic reduction catalyst disposed downstream of the catalyzed soot filter.
Before describing several exemplary embodiments of the invention, it is to be understood that the invention is not limited to the details of construction or process steps set forth in the following description. The invention is capable of other embodiments and of being practiced or being carried out in various ways.
“Activated alumina” has its usual meaning of a high BET surface area alumina, comprising one or more of gamma-, theta- and delta aluminas.
“BET surface area” has its usual meaning of referring to the Brunauer, Emmett, Teller method for determining surface area by N2 absorption. Unless otherwise specifically stated, all references herein to the surface area of the catalyst support components or other catalyst components means the BET surface area.
“Bulk form,” when used to describe the physical form of a material (e.g., ceria), means the material is present as discrete particles that can be as small as 1 to 15 microns in diameter or smaller, as opposed to having been dispersed in solution onto another material such as gamma alumina. By way of example, in some embodiments of the invention, particles of ceria are admixed with particles of gamma alumina so that ceria is present in bulk form, as opposed to, for example, impregnating alumina particles with aqueous solutions of ceria precursors which upon calcination are converted to ceria disposed on the alumina particles.
When present in a catalyst, “cerium component” means one or more oxides of cerium (e.g., CeO2).
“Downstream” and “Upstream,” when used to describe an article, catalyst substrate or zone, refer to the relative positions in the exhaust system as sensed in the direction of the flow of the exhaust gas stream. When a catalyst or catalyst zone is “downstream” or “upstream” from another catalyst or zone, it may be on a different substrate or brick or on a different region of the same substrate or brick.
“High surface area support” means support materials with a BET surface area that is approximately greater than 10 m2/g, for example, greater than 150 m2/g.
“Platinum group metal component” or “PGM” refers to the platinum group metals or oxides thereof. Suitable platinum group metal components are platinum, palladium, rhodium iridium components, and combinations thereof.
“Diesel oxidation catalyst” or “DOC” refers to a catalyst promoting oxidation processes in diesel exhaust, to reduce emissions of the organic fraction of diesel particulates, gas-phase hydrocarbons, and/or carbon monoxide.
“Active regeneration” refers to the introduction of a combustible material (e.g., diesel fuel) into the exhaust and burning it across an oxidation catalyst to generate an exotherm from that provides heat (e.g. about 500-700° C.) needed to burn particulate matter such as soot from the filter
An ammonia destruction catalyst or AMOX refers to a catalyst that promotes the oxidation of NH3.
“Particulate filter” or “soot filter” is a filter designed to remove particulate matter from an exhaust gas stream such as soot, and particulate filters include, but are not limited to honeycomb wall flow filters, partial filtration filter, a wire mesh filter, wound fiber filters, sintered metal filters; and foam filters.
As used herein, “operating window” refers to the temperature and space velocity values encountered by the catalytic component during operation of the engine. The temperature of the operating window can vary between 0° C. and 800° C., and the space velocity can vary between 0 and 1,000,000/hour.
To meet future Heavy Duty emission regulations around the world it will be necessary to utilize particulate reduction and NOx reduction emission control system. One approach is the utilization of an active particulate filter system plus a Selective Catalytic Reduction system. This system can be configured in numerous ways but a configuration in the following order—Diesel Oxidation Catalyst (DOC)—Catalyzed Soot Filter (CSF)—Urea Injection—Selective Catalytic Reduction Catalyst (SCR)—with or without an Ammonia Oxidation Catalyst (AMOX) seems to offer attractive design benefits.
Embodiments of this invention utilize a DOC that is specifically designed to burn fuel for active regeneration of the filter by fuel injection either in-cylinder in the engine or post injection in the exhaust with minimal or no NO2 production across the DOC such that NO2 DOC out has negligible or no affect on particulate oxidation in the filter. The CSF can be designed to optimize the NO/NO2 ratio out of the filter to facilitate optimal NOx reduction across the SCR system.
According to one or more embodiments of the invention a diesel oxidation catalyst ix disposed on a flow through substrate.
According to one or more embodiments, the catalyst is effective to provide substantially no additional NO2 when an exhaust gas stream is passed through the catalyst. Substantially no NO2 is produced over about 90% of the operating window of the catalyst. In detailed embodiments, the catalyst is effective to provide substantially no additional NO2 when exhaust gas is passed through the catalyst over about 70%, 75% 80%, 85%, 90% or 95% of the operating window of the catalyst. According to one or more embodiments, as used in this specification, and the appended claims, “substantially no additional NO2” means that there is no more than a 25 ppm increase in the NO2 concentration.
In specific embodiments, the outlet zone 22 comprises substantially no platinum. As used in this specification, and the appended claims, “substantially no platinum” means that the platinum is not intentionally provided in the zone, for example, less than about 1 wt. % of the metal comprises platinum. In specific embodiments, the amount of platinum present is less than about 0.5 wt. % or less than about 0.1 wt. %.
The axial length of the inlet zone 20 can be adjusted as needed. In specific embodiments the axial length of the inlet zone 20 is less than about 45% of the total axial length of the catalyst. In other specific embodiments, the axial length of the inlet zone 20 is less than about 40%, 35%, 30%, 25%, 20%, 15%, 10%, 5% or 1%. In detailed embodiments, the axial length of the inlet zone is about half the axial length of the outlet zone; meaning the inlet axial length is about 33.3% of the total axial length of the catalyst 10 and the outlet axial length is about 66.7% of the total axial length. In other detailed embodiments, the axial length of the inlet zone 20 can be about 0%, or greater than about 5%, 10%, 15%, 20%, 25%, 30%, 33.3%, 35%, 40% or 45% of the total axial length.
In some specific embodiments, the inlet zone 20 has a platinum to palladium ratio equal to or greater than about 10:1. In another specific embodiment, the inlet zone 20 comprises substantially only palladium. As used in this specification, and the appended claims, the term “substantially only palladium” means that there is less than about 5% of other metals. In other detailed embodiments, the inlet zone 20 has a platinum to palladium ratio greater than or equal to about 1:1, 2:1, 3:1, 4:1, 5:1, 6:1, 7:1, 8:1, 9:1, 10:1, 15:1, 20:1, 30:1, 40:1 or 50:1.
In detailed embodiments, the loading of the inlet zone is high, compared to the loading of the outlet zone. In specific embodiments, the loading of the inlet zone is equal to or greater than about 30 g/ft3, 40 g/ft3, 50, g/ft3, 60 g/ft3, 70 g/ft3, 75 g/ft3, 80 g/ft3, 90 g/ft3, 100 g/ft3, 100 g/ft3, and 150 g/ft3.
In detailed embodiments, the loading of the outlet zone is low, compared to the loading of the inlet zone. In specific embodiments, the loading of the outlet zone is less than or equal to about 30 g/ft3, 20 g/ft3, 15 g/ft3, 10 g/ft3, 5 g/ft3, 4 g/ft3, 3 g/ft3, 2 g/ft3 or 1 g/ft3.
In specific embodiments, the diesel oxidation catalyst is disposed on a flow-through substrate like that depicted in
The diesel oxidation catalyst of some embodiments includes a base metal oxide in either or both of the inlet zone and the outlet zone. Suitable base metal oxides include, but are not limited to, oxides of rare earth metals such as ceria, praseodymia, neodymia and combinations thereof. These rare earth oxides may be stabilized by zirconia
In a specific embodiment, the inlet zone of the diesel oxidation catalyst comprises platinum and palladium in a ratio of at least 2:1 with a loading of at least about 75 g/ft3. The outlet zone comprises substantially only palladium with a loading of no greater than about 10 g/ft3.
In another specific embodiment, the inlet zone comprises platinum and palladium in a ratio of about 10:1 with a loading of about 80 g/ft3 and the outlet zone comprises substantially only palladium with a loading of about 5 g/ft3.
In a further specific embodiment, the inlet zone and the outlet zone comprise substantially only palladium. The loading of the inlet zone is greater than 30 g/ft3 and the loading of the outlet zone is less than 30 g/ft3.
Other metals may be included in either or both zones of the diesel oxidation catalyst. Suitable metals include, but are not limited to, rhodium and an alkaline earth metal oxides such as magnesium oxide, calcium oxide, strontium oxide, barium oxide and combinations thereof.
Other aspects of the invention are directed to methods of making a diesel oxidation catalyst. A first slurry is prepared comprising one or more of platinum and palladium. A second slurry is prepared comprising palladium. A substrate is washcoated with the first slurry over an inlet zone of the substrate to result in a first loading. The inlet zone has a first axial length. The outlet zone of the substrate is washcoated with the second slurry to a second loading. The outlet zone having a second axial length. The first loading is greater than the second loading and the axial length of the inlet zone is not greater than about the axial length of the outlet zone.
In detailed embodiments, the axial length of the inlet zone is about half the axial length of the outlet zone. In other detailed embodiments the axial length of the inlet zone is about equal to the axial length of the outlet zone. The axial length of the inlet zone can be any percentage of the length of the substrate up to a length of about 50%. For example, the axial length of the inlet zone can be 5%, 10%, 20, 30%, 33.3%, 35%, 40%, 45% or 50%. These are merely examples and should not be taken as limiting the scope of the invention.
In other detailed embodiments, the first loading is greater than about 40 g/ft3. The first loading can be greater than other amounts, including, but not limited to, 50 g/ft3, 60 g/ft3, 70 g/ft3, 80 g/ft3, 90 g/ft3, 100 g/ft3, 110 g/ft3, 120 g/ft3, 130 g/ft3, 140 g/ft3, 150 g/ft3, 160 g/ft3, 170 g/ft3, 180 g/ft3, 190 g/ft3 and 200 g/ft3. These are merely examples and should not be taken as limiting the scope of the invention.
In further detailed embodiments, the second loading is less than about 20 g/ft3. The second loading can also be less than about 15 g/ft3, 10 g/ft3, 9 g/ft3, 8 g/ft3, 7 g/ft3, 6 g/ft3, 5 g/ft3, 4 g/ft3, 3 g/ft3, 2 g/ft3 and 1 g/ft3. These are merely examples and should not be taken as limiting the scope of the invention.
Further embodiments of the invention relate to an emission treatment system that effectively provides simultaneous treatment of the particulate matter, the NOx and other gaseous components of diesel engine exhaust. Due to the choice of catalytic compositions implemented in the system, effective pollutant abatement is provided for exhaust streams of varying temperatures. This feature is advantageous for operating diesel vehicles under varying loads and vehicle speeds which significantly impact exhaust temperatures emitted from the engines of such vehicles.
One embodiment of the inventive emission treatment system is schematically depicted in
Accordingly, one or more embodiments are directed to a system for treating an exhaust stream comprising NOR from an engine. The system comprises a diesel oxidation catalyst, as previously described, disposed downstream of the engine. Briefly, a diesel oxidation catalyst having an inlet zone with a first loading of at least one of palladium and platinum and an outlet zone with a second loading comprising palladium. The first loading is greater than the second loading and the length of the first zone is no greater than the length of the second zone.
The exact catalyst composition and loading providing that regulates the amount of NO2 exiting the oxidation catalyst will depend on the particular application and factors such as whether the engine is a heavy duty diesel engine, a light duty diesel engine, the operating temperature, space velocity and other factors. Suitable catalysts for the oxidation include platinum group metal- and base metal-based compositions. The catalyst compositions can be coated onto honeycomb flow-through monolith substrates formed of refractory metallic or ceramic (e.g., cordierite) materials. Alternatively, oxidation catalysts may be formed on to metallic or ceramic foam substrates which are well-known in the art. These oxidation catalysts, by virtue of the substrate on which they are coated (e.g., open cell ceramic foam), and/or by virtue of their intrinsic oxidation catalytic activity provide some level of particulate removal. The oxidation catalyst may remove some of the particulate matter from the exhaust stream upstream of the wall flow filter, since the reduction in the particulate mass on the filter potentially extends the time before forced regenerations.
One suitable oxidation catalyst composition that may be used in the emission treatment system contains a platinum group metal (PGM) component (e.g., platinum, palladium or rhodium components) dispersed on a high surface area, refractory oxide support (e.g., γ-alumina) which is combined with a zeolite component (for example, a beta zeolite).
Zeolites used in such compositions are resistant to sulfur poisoning, sustain a high level of activity for the SCR process, and are capable of oxidation of excess ammonia with oxygen. Specific, non-limiting examples of such zeolites include USY, Beta and ZSM-20. Additional examples of suitable SCR catalysts include zeolite having the CHA structure, for example SSZ-13, and non-zeolitic molecular sieves having the CHA structure, for example silicoaluminophosphates such as SAPO-34, SAPO-18, SAPO-44. Particular, non-limiting examples are materials having the CHA structure that are promoted with Cu and/or Fe, for example Cu/SSZ-13 and Cu/SAPO-34, Cu/SAPO-18 and CuSAPO-44.
Platinum group metal-based compositions suitable for use in forming the oxidation catalyst are also described in U.S. Pat. No. 5,100,632 (the '632 patent) hereby incorporated by reference. The '632 patent describes compositions that have a mixture of platinum, palladium, rhodium, and ruthenium and an alkaline earth metal oxide such as magnesium oxide, calcium oxide, strontium oxide, or barium oxide.
Catalyst compositions suitable for the oxidation catalyst may also be formed using base metals as catalytic agents. For example, U.S. Pat. No. 5,491,120 (the disclosure of which is hereby incorporated by reference) discloses oxidation catalyst compositions that include a catalytic material having a BET surface area of at least about 10 m2/g and consist essentially of a bulk second metal oxide which may be one or more of titania, zirconia, ceria-zirconia, silica, alumina-silica, and α-alumina.
In specific embodiments, the outlet zone of the catalyst comprises substantially no platinum. In other specific embodiments, the axial length of the inlet zone is less than about 35% of the total length of the catalyst. In other embodiments, the emission treatment system further comprises a catalyzed soot filter 42 disposed downstream of the diesel oxidation catalyst 41. In specific embodiments, the catalyzed soot filter 42 may have a plurality of longitudinally extending passages bounded by longitudinally extending walls. The passages comprise inlet passages having an open inlet end and a closed outlet end, and outlet passages having a closed inlet end and an open outlet end. The catalyzed soot filter 42 comprises a catalyst composition on the walls and is effective to optimize the ratio of NO to NO2 exiting the filter.
The exhaust stream is conveyed to the soot filter 42. On passing through the soot filter 42, particulate matter is filtered and the gas contains approximately equal ratios of NO to NO2.
The particulate matter including the soot fraction and the VOF are also largely removed (greater than 80%) by the soot filter 42. The particulate matter deposited on the soot filter 42 is combusted through the regeneration of the filter, the temperature at which the soot fraction of the particulate matter combusts is lowered by the presence of the catalyst composition disposed on the soot filter.
In the embodiment show in
Downstream of the soot filter 42 is a selective catalytic reduction catalyst (SCR) 43. The exhaust gas containing NO and NO2 is reduced to N2 in the SCR 43.
The emission treatment system may optionally be equipped with a slip oxidation catalyst 44 downstream of the SCR catalyst 43. The slip oxidation catalyst can be coated, for example, with a composition containing base metals and less than 0.5 wt % of platinum. This provision can be used to oxidize any excess NH3 before it is vented to the atmosphere.
The configuration shown in
Second, the CSF 42 being in front of the SCR 43 will prevent particulate, oil ash and other undesirable materials from being deposited on the SCR catalyst thus improving its durability and performance.
Third, having oxidation catalysts 41 in front of the SCR 43 allows for an increase in the NO2 to NO ratio entering the SCR 43 which is known to increase the reaction rate of the NOx reduction occurring in the SCR 43, if properly controlled.
However, the optimal control of the NO to NO2 ratio entering the filter 42 can be an issue with the large volume of oxidation catalyst that is present in the DOC 41 and CSF in front of the SCR 43. According to one or more embodiments, proper system design provides for the control of the NO to NO2 ratio into the SCR 43 using a novel combination of DOC 41 and diesel filter catalysts 42.
Selective Catalytic Reduction Catalysts
Suitable SCR catalyst compositions for use in the system are able to effectively catalyze the reduction of the NOx component, so that adequate NOx levels can be treated even under conditions of low load which typically are associated with lower exhaust temperatures. In one or more embodiments, the catalyst article is capable of converting at least 50% of the NOx component to N2, depending on the amount of reductant added to the system. In addition, SCR catalyst compositions for use in the system are also ideally able to aid in the regeneration of the filter by lowering the temperature at which the soot fraction of the particulate matter is combusted. Another desirable attribute for the composition is that it possesses the ability to catalyze the reaction of O2 with any excess NH3 to N2 and H2O, so that NH3 is not emitted to the atmosphere.
Useful SCR catalyst compositions used in the system also have thermal resistance to temperatures greater than 650° C. Such high temperatures are often encountered during the regeneration of soot filters. Additionally, SCR catalyst compositions should resist degradation upon exposure to sulfur components, which are often present in diesel exhaust gas compositions.
Suitable SCR catalyst compositions are described, for instance, in U.S. Pat. No. 4,961,917 (the '917 patent) and U.S. Pat. No. 5,516,497, which are both hereby incorporated by reference in their entirety. Compositions disclosed in the '917 patent include one or both of an iron and a copper promoter present in a zeolite in an amount of from about 0.1 to 30 percent by weight, a specific example being from about 1 to 5 percent by weight, of the total weight of promoter plus zeolite. In addition to their ability to catalyze the reduction of NOx with NH3 to N2, the disclosed compositions can also promote the oxidation of excess NH3 with O2, especially for those compositions having higher promoter concentrations.
Substrates
Substrates of particular use with the diesel oxidation catalysts and optional exhaust components described are of the flow-through type, open-cell foam filters and the wall flow type. The flow-through type substrate has been previously described with respect to
An alternate substrate is an open cell foam substrate that contains a plurality of pores.
The foam substrate may be composed of metallic or ceramic materials. Examples of ceramic foams are disclosed in U.S. Pat. No. 6,077,600, which is herein incorporated by reference in its entirety. Ceramic foam carriers have walls formed from fibers coated with ceramic materials. Substrates in the form of metal foams are well known in the prior art, e.g., see U.S. Pat. No. 3,111,396, which is herein incorporated by reference in its entirety.
Other alternate substrate are wall flow substrates useful for supporting the catalyst compositions have a plurality of fine, substantially parallel gas flow passages extending along the longitudinal axis of the substrate. Typically, each passage is blocked at one end of the substrate body, with alternate passages blocked at opposite end-faces. Such monolithic carriers may contain up to about 700 or more flow passages (or “cells”) per square inch of cross section, although far fewer may be used. For example, the carrier may have from about 7 to 600, more usually from about 100 to 400, cells per square inch (“cpsi”). The cells can have cross sections that are rectangular, square, circular, oval, triangular, hexagonal, or are of other polygonal shapes. Wall flow substrates typically have a wall thickness between 0.002 and 0.1 inches. An example of a suitable wall flow substrate has a wall thickness of between about 0.002 and 0.015 inches.
Suitable wall flow filter substrates are composed of ceramic-like materials such as cordierite, α-alumina, silicon carbide, silicon nitride, zirconia, mullite, spodumene, alumina-silica-magnesia, aluminum titanate or zirconium silicate, or of any other suitable porous, refractory metal. Wall flow substrates may also be formed of ceramic fiber composite materials. Suitable wall flow substrates are formed from cordierite and silicon carbide. Such materials are able to withstand the environment, particularly high temperatures, encountered in treating the exhaust streams.
Suitable wall flow substrates for use in the inventive system include thin porous walled honeycombs (monoliths) through which the fluid stream passes without causing too great an increase in back pressure or pressure across the article. Normally, the presence of a clean wall flow article will create a back pressure of 1 inch water column to 10 psig. Ceramic wall flow substrates used in the system may be formed of a material having a porosity of at least 50% (e.g., from 50 to 75%) having a mean pore size of at least 5 microns (e.g., from 5 to 30 microns). When substrates with these porosities and these mean pore sizes are coated with the techniques described below, adequate levels of SCR catalyst compositions can be loaded onto the substrates to achieve excellent NOx conversion efficiency. These substrates are still able retain adequate exhaust flow characteristics, i.e., acceptable back pressures, despite the SCR catalyst loading. U.S. Pat. No. 4,329,162 is herein incorporated by reference with respect to the disclosure of suitable wall flow substrates.
Suitable wall flow filters may be formed with lower wall porosities, e.g., from about 35% to 50%, than the wall flow filters utilized in the invention. In general, the pore size distribution of a suitable commercial wall flow filter is very broad with a mean pore size smaller than 17 microns.
The porous wall flow filter used according to embodiments of this invention is catalyzed in that the wall of said element has thereon or contained therein one or more catalytic materials. Catalytic materials may be present on the inlet side of the element wall alone, the outlet side alone, both the inlet and outlet sides, or the wall itself may consist all, or in part, of the catalytic material. This invention includes the use of one or more layers of catalytic materials and combinations of one or more layers of catalytic materials on the inlet and/or outlet walls of the element.
To coat the wall flow substrates with a catalyst composition, the substrates are immersed vertically in a portion of the catalyst slurry such that the top of the substrate is located just above the surface of the slurry. In this manner, slurry contacts the inlet face of each honeycomb wall, but is prevented from contacting the outlet face of each wall. The sample is left in the slurry for about 30 seconds. The substrate is removed from the slurry, and excess slurry is removed from the wall flow substrate first by allowing it to drain from the channels, then by blowing with compressed air (against the direction of slurry penetration), and then by pulling a vacuum from the direction of slurry penetration. By using this technique, the catalyst slurry typically permeates the walls of the substrate, yet the pores are not occluded to the extent that undue back pressure will build up in the finished substrate. As used herein, the term “permeate” when used to describe the dispersion of the catalyst slurry on the substrate, means that the catalyst composition is dispersed throughout the wall of the substrate.
The coated substrates are dried typically at about 100° C. and calcined at a higher temperature (e.g., 300 to 450° C.). After calcining, the catalyst loading can determined be through calculation of the coated and uncoated weights of the substrate. As will be apparent to those of skill in the art, the catalyst loading can be modified by altering the solids content of the coating slurry. Alternatively, repeated immersions of the substrate in the coating slurry can be conducted, followed by removal of the excess slurry as described above.
Reductant Injector
A reductant dosing system is optionally provided downstream of the soot filter and upstream of the SCR catalyst to inject a NOx reductant into the exhaust stream. As disclosed in U.S. Pat. No. 4,963,332, NOx upstream and downstream of the catalytic converter can be sensed, and a pulsed dosing valve can be controlled by the upstream and downstream signals. In alternative configurations, the systems disclosed in U.S. Pat. No. 5,522,218, where the pulse width of the reductant injector is controlled from maps of exhaust gas temperature and engine operating conditions such as engine rpm, transmission gear and engine speed. Reference is also made to the discussion of reductant pulse metering systems in U.S. Pat. No. 6,415,602, the discussion of which is hereby incorporated by reference.
In the embodiment of
This invention is not limited to the aqueous urea metering arrangement shown in
In addition to urea and cyanuric acid, other nitrogen based reducing reagents or reductants especially suitable for use in the control system of the present invention includes ammelide, ammeline, ammonium cyanate, biuret, cyanuric acid, ammonium carbamate, melamine, tricyanourea, and mixtures of any number of these. However, the invention in a broader sense is not limited to nitrogen based reductants but can include any reductant containing hydrocarbons such as distillate fuels including alcohols, ethers, organo-nitro compounds and the like (e.g., methanol, ethanol, diethyl ether, etc.) and various amines and their salts (especially their carbonates), including guanidine, methyl amine carbonate, hexamethylamine, etc.
Additional embodiments of the invention are directed to methods method of treating an exhaust stream from a diesel engine comprising NOx and particulate matter. The method comprises flowing the exhaust stream through the catalyst compositions previously described. Briefly, a diesel oxidation catalyst having an inlet zone with a first loading of at least one of palladium and platinum and an outlet zone with a second loading comprising palladium. The first loading is greater than the second loading and the length of the first zone is no greater than the length of the second zone.
In specific embodiments, the exhaust gas is passed through a catalyst as previously described where the outlet zone contains substantially no platinum. The catalyst of detailed embodiments is effective to produce substantially no additional NO2 in the exhaust gas stream after passing through the catalyst over about 90% of the operating window of the catalyst. In other detailed embodiments, the catalyst is effective to produce substantially no additional NO2 in the exhaust gas stream after passing through the catalyst over about 70%, 75% 80%, 85%, 90% or 95% of the operating window of the catalyst. In some specific embodiments, the axial length of the inlet zone is about half the axial length of the outlet zone and the first loading is greater than about 60 g/ft3 and the second loading is less than about 6 g/ft3.
Data shows that the engine out NO2 percentage of NOx can vary depending on the engine design, the exhaust temperature and the load. See
Additionally, data has shown that the majority of NO2 available at the inlet of the SCR catalyst is produced in the CSF. See
Since the NO2 produced in the DOC must pass through the CSF and as the CSF builds a soot layer on the inlet channel walls, the NO2 generated by the DOC will react with the soot and revert back to NO. The extent of this reaction will be dependent on the thickness of the soot layer thus it will be variable. Therefore, the amount of NO2 generated by the DOC that actually makes it to the SCR is variable and unreliable. However, the generation of NO2 over the CSF is much more controllable because the DOC will have oxidized almost all of the HC and CO coming from the engine and the CSF PGM loading will drive the NO to NO2 toward equilibrium for the given conditions regardless of the amount of soot in the filter. See
Embodiments of the invention are able to utilize a DOC that makes little or no NO2 compared to engine out in combination with an optimized CSF designed to provide the proper NO to NO2 ratio for optimal SCR operation. See
A properly designed DOC can be configured to contain a catalyst that is effective produce little or no NO2 compared to the engine out emissions. See Table 1 and
The optimization of the DOC according to one or more embodiments includes the utilization of platinum group metals such as platinum and palladium in appropriate ratios, loadings and distribution on the substrate to optimize HC and CO conversion and active regeneration of the filter while making little or no NO2. This optimization will allow the removal of Platinum (the primary catalyst for making NO2) from the DOC thus reducing the overall cost of the DOC. This allows more platinum to be utilized on the CSF where it will give the most benefit for generating NO2 for the SCR.
This design offers many benefits, including the opportunity for lower Pt loading on the DOC, reducing the cost. The opportunity to increase the use of Pd on the DOC, increasing the Pd to Pt ratio, improving the thermal durability of the DOC. Allowing a more stable NO to NO2 ratio into the filter. Allowing better utilization of the system PGM by placing more PGM and more Pt on the filter. Allowing for the optimization of the filter for NO2 production for the SCR which creates a system that is amore able to provide the optimal NO to NO2 ratio for proper SCR operation.
A standard diesel oxidation catalyst was prepared using a 10.5″×6.0″ cylindrically shaped substrate with 300 cells per square inch and 5 mil wall thickness. The substrate was coated with a 10:1 platinum to palladium washcoat with a loading of 40 g/ft3. The substrate was zoned 50:50 over the axial length of the substrate. The loading in the inlet zone was 55 g/ft3 and the outlet zone loading was 25 g/ft3.
Low NO2 Example
A substrate identical to that of the Comparative Example was zone washcoated. The inlet zone was 2″ long and contained platinum and palladium at a ratio of 10:1 with a loading of 80 g/ft3. The outlet zone was the remaining 4″ of the substrate and was washcoated with substantially only palladium with a loading of 5 g/ft3. The total loading for the Low NO2 sample was 30 g/ft3 with an overall platinum to palladium ratio of 4.2:1.
Reference throughout this specification to “one embodiment,” “certain embodiments,” “one or more embodiments” or “an embodiment” means that a particular feature, structure, material, or characteristic described in connection with the embodiment is included in at least one embodiment of the invention. Thus, the appearances of the phrases such as “in one or more embodiments,” “in certain embodiments,” “in one embodiment” or “in an embodiment” in various places throughout this specification are not necessarily referring to the same embodiment of the invention. Furthermore, the particular features, structures, materials, or characteristics may be combined in any suitable manner in one or more embodiments.
While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.
This application is a continuation-in-part under 35 U.S.C. § 120 of U.S. patent application Ser. No. 12/330,663, filed Dec. 9, 2008, which claims the benefit of priority under 35 U.S.C. § 119(e) to U.S. Patent Application No. 61/012,947, filed Dec. 12, 2007, the teachings of which are hereby incorporated by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61012947 | Dec 2007 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15995316 | Jun 2018 | US |
| Child | 17661058 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12484710 | Jun 2009 | US |
| Child | 15995316 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12330663 | Dec 2008 | US |
| Child | 12484710 | US |