This application claims the benefit of priority based on Korean Patent Application No. 10-2016-0167794 filed on Dec. 9, 2016, the disclosure of which is incorporated herein by reference in its entirety.
The present application relates to an encapsulating composition, an organic electronic device comprising the same, and a method for manufacturing the organic electronic device.
An organic electronic device (OED) means a device comprising a layer of an organic material that generates an alternating current of electric charges using holes and electrons, and an example thereof may include a photovoltaic device, a rectifier, a transmitter and an organic light emitting diode (OLED), and the like.
The organic light emitting diode (OLED) among the organic electronic devices has lower power consumption and faster response speed, than conventional light sources, and is advantageous for thinning display devices or illuminations. In addition, the OLED has excellent space utilization, so that it is expected to be applied in various fields covering various portable devices, monitors, notebooks, and televisions.
In commercialization and application expansion of OLEDs, the most important problem is a durability problem. Organic materials and metal electrodes, and the like, contained in OLEDs are very easily oxidized by external factors such as moisture. Thus, products comprising OLEDs are highly sensitive to environmental factors. Accordingly, various methods have been proposed to effectively block penetration of oxygen or moisture from the outside into organic electronic devices such as OLEDs.
The present application provides an encapsulating composition which can effectively block moisture or oxygen introduced into an organic electronic device from the outside to secure the lifetime of the organic electronic device, is possible to realize a top emission type organic electronic device, is applicable to an inkjet method and can provide a thin display, and an organic electronic device comprising the same.
The present application relates to an encapsulating composition. The encapsulating composition may be a sealing material applied to sealing or encapsulating an organic electronic device such as, for example, an OLED. In one example, the encapsulating composition of the present application can be applied to sealing or encapsulating the entire surface of an organic electronic element. Thus, after the encapsulating composition is applied to the encapsulation, it may be present in an organic layer form sealing the entire surface of the organic electronic element. In addition, the organic layer may be laminated on the organic electronic element together with a protective layer and/or an inorganic layer, which is described below, to form a sealing structure.
In an embodiment of the present application, the present application relates to an encapsulating composition for sealing an organic electronic element which is applicable to an inkjet process, wherein the composition may be designed to have appropriate physical properties when it has been discharged onto a substrate using inkjet printing capable of non-contact patterning.
In this specification, the term “organic electronic device” means an article or device having a structure comprising an organic material layer that generates an alternating current of electric charges using holes and electrons between a pair of electrodes facing each other, and an example thereof may include a photovoltaic device, a rectifier, a transmitter and an organic light emitting diode (OLED), and the like, but is not limited thereto. In one example of the present application, the organic electronic device may be an OLED.
An exemplary encapsulating composition may comprise an epoxy compound and a compound having an oxetane group. The epoxy compound may be a photo-curable or thermosetting compound. The compound having an oxetane group may be comprised in an amount of 45 to 145 parts by weight, 48 to 144 parts by weight, 63 to 143 parts by weight or 68 to 142 parts by weight, relative to 100 parts by weight of the epoxy compound. In this specification, the term “part by weight” may mean a weight ratio between the respective components. By controlling the content ratio of the composition, the present application can form an organic layer on an organic electronic element by an ink jet method, and the applied encapsulating composition can provide an organic layer having excellent spreadability in a short time and excellent curing sensitivity after curing. In one example, the encapsulating composition of the present application may have a contact angle to glass of 15° or less, 12° or less, 10° or less, or 8° or less. The lower limit is not particularly limited, but may be 1° or 3° or more. By adjusting the contact angle to 15° or less, the present application can ensure spreadability in a short time in the inkjet coating, thereby forming an organic layer of a thin film. In the present application, the contact angle may be measured by applying a drop of the encapsulating composition onto glass using a sessile drop measurement method, which may be an average value measured after applying 5 times.
In one example, the epoxy compound may have at least monofunctionality or bifunctionality or more. That is, one or two or more epoxy functional groups may be present in the compound, and the upper limit is not particularly limited, but may be 10 or less. The epoxy compound realizes excellent heat resistance durability at high temperature and high humidity by realizing an appropriate cross-linking degree in an ink composition.
In an embodiment of the present application, the epoxy compound may comprise a compound having a cyclic structure in its molecular structure and/or a linear or branched aliphatic compound. That is, the encapsulating composition of the present application may comprise at least one of a compound having a cyclic structure in its molecular structure and a linear or branched aliphatic compound as the epoxy compound, and may also comprise them together. In one example, the compound having a cyclic structure in the molecular structure may have ring constituent atoms in the molecular structure in a range of 3 to 10, 4 to 8, or 5 to 7, and one or more, or two or more, or 10 or less of the cyclic structures may be present in the compound. When the compound having a cyclic structure and the linear or branched aliphatic compound are included together, the linear or branched aliphatic compound may be comprised in a range of 20 parts by weight or more, less than 205 parts by weight, 23 parts by weight to 204 parts by weight, 30 parts by weight to 203 parts by weight, 34 parts by weight to 202 parts by weight, 40 parts by weight to 201 parts by weight, 60 parts by weight to 200 parts by weight or 100 parts by weight to 173 parts by weight, relative to 100 parts by weight of the compound having a cyclic structure. By controlling the content range, the present application makes it possible to prevent element damage in top sealing the organic electronic element, to have appropriate physical properties that can be ink-jetted, to have excellent curing strength after curing, and also to realize excellent moisture barrier properties together.
In one example, the epoxy compound may have an epoxy equivalent in a range of 50 to 350 g/eq, 73 to 332 g/eq, 94 to 318 g/eq or 123 to 298 g/eq. In addition, the compound having an oxetane group may have a weight average molecular weight in a range of 150 to 1,000 g/mol, 173 to 980 g/mol, 188 to 860 g/mol, 210 to 823 g/mol or 330 to 780 g/mol. By controlling the epoxy equivalent of the epoxy compound to be low or controlling the weight average molecular weight of the compound having an oxetane group to be low, the present application can prevent the viscosity of the composition from becoming excessively high to render the inkjet process impossible, while improving the curing completion degree after curing of the sealing material, and simultaneously provide moisture barrier properties and excellent curing sensitivity. In this specification, the weight average molecular weight means a value converted to standard polystyrene measured by GPC (gel permeation chromatograph). In one example, a column made of a metal tube having a length of 250 to 300 mm and an inner diameter of 4.5 to 7.5 mm is filled with 3 to 20 mm polystyrene beads. When a solution diluted by dissolving a substance to be measured in a THF solvent is passed through the column, the weight average molecular weight can be indirectly measured according to a flowing time. It can be detected by plotting amounts separated from the column by size for each time. Also, the epoxy equivalent herein is grams (g/eq) of a resin comprising one gram equivalent of epoxy group, which can be measured according to the method defined in JIS K 7236.
Also, the compound having an oxetane group may have a boiling point in a range of 90 to 300° C., 98 to 270° C., 110 to 258° C., or 138 to 237° C. By controlling the boiling point of the compound to the above range, the present application can provide a sealing material which can have excellent moisture barrier properties from the outside while realizing excellent printability even at a high temperature in an inkjet process, and prevent damage applied to the element due to suppressed outgas. In this specification, the boiling point may be measured at 1 atm, unless otherwise specified.
In one example, the compound having a cyclic structure in its molecular structure may be exemplified by 3,4-epoxycyclohexylmethyl 3′,4′-epoxycyclohexanecarboxylate (EEC) and derivatives, dicyclopentadiene dioxide and derivatives, vinylcyclohexene dioxide and derivatives, or 1,4-cyclohexanedimethanol bis(3,4-epoxycyclohexanecarboxylate) and derivatives, but is not limited thereto.
In one example, the structure of the compound comprising the oxetane group is not limited as long as it has the functional group, and for example, OXT-221, CHOX, OX-SC, OXT101, OXT121 or OXT212 from TOAGOSEI, or EHO, OXBP, OXTP or OXMA from ETERNACOLL may be exemplified. Also, the linear or branched aliphatic epoxy compound may include aliphatic glycidyl ether, 1,4-butanediol diglycidyl ether, ethylene glycol diglycidyl ether, 1,6-hexanediol diglycidyl ether, propylene glycol diglycidyl ether, diethylene glycol diglycidyl ether, butyl glycidyl ether, 2-ethylhexyl glycidyl ether or neopentyl glycol diglycidyl ether, but is not limited thereto.
In an embodiment of the present application, the encapsulating composition may further comprise a photoinitiator. The photoinitiator may be an ionic photoinitiator. Also, the photoinitiator may be a compound absorbing a wavelength in a range of 180 nm to 400 nm. By using the photoinitiator, the present application can realize excellent curing properties in a specific composition of the present application.
In one example, the photoinitiator may be a cationic photopolymerization initiator. As the cationic photopolymerization initiator, a known material in the art can be used and for example, it may include a compound having a cation moiety comprising aromatic sulfonium, aromatic iodonium, aromatic diazonium or aromatic ammonium and an anion moiety comprising AsF6-, SbF6-, PF6-, or tetrakis(pentafluorophenyl) borate. Furthermore, as the cationic photopolymerization initiator, an ionized cationic initiator of onium salt or organometallic salt series or a non-ionized cationic photopolymerization initiator of organic silane or latent sulfonic acid series can be exemplified. Diaryliodonium salt, triarylsulfonium salt or aryldiazonium salt and the like can be exemplified as the initiator of the onium salt series, iron arene or the like can be exemplified as the initiator of the organometallic salt series, o-nitrobenzyl triaryl silyl ether, triaryl silyl peroxide or an acyl silane and the like can be exemplified as the initiator of the organosilane series, and α-sulfonyloxy ketone or α-hydroxymethylbenzoin sulfonate and the like can be exemplified as the initiator of the latent sulfuric acid series, without being limited thereto.
In one example, the encapsulating composition of the present application may comprise a photoinitiator comprising a sulfonium salt as the photoinitiator in the above-mentioned specific composition, so as to be suitable for a use sealing an organic electronic element by an inkjet method. Even if the encapsulating composition according to the above composition is directly sealed on the organic electronic element, it can prevent chemical damage from being applied to the element due to a small amount of generated outgas. Furthermore, the photoinitiator comprising a sulfonium salt may also have excellent solubility, thereby being suitably applied to an inkjet process.
In an embodiment of the present invention, the photoinitiator may be comprised in an amount of 1 to 15 parts by weight, 3 to 14 parts by weight, or 7 to 13.5 parts by weight relative to 100 parts by weight of the epoxy compound. By controlling the photoinitiator content range, the present application can minimize physical and chemical damage of an organic electronic element due to the nature of an encapsulating composition of the present application that is directly applied in the element.
In an embodiment of the present application, the encapsulating composition may further comprise a surfactant. In one example, the surfactant may comprise a polar functional group. The polar functional group may include, for example, a carboxyl group, a hydroxyl group, a phosphate, an ammonium salt, a carboxylate group, a sulfate or a sulfonate. Furthermore, in an embodiment of the present application, the surfactant may be a non-silicone-based surfactant or a fluorine-based surfactant. The non-silicone-based surfactant or the fluorine-based surfactant may be applied together with the above-mentioned epoxy compound and the compound having an oxetane group to provide excellent coating properties on the organic electronic element. On the other hand, in the case of a surfactant comprising a polar reactive group, it may have high affinity with the other components of the encapsulating composition, and thus realize an excellent effect in terms of adhesion. In an embodiment of the present application, a hydrophilic fluorine-based surfactant or non-silicone-based surfactant may be used to improve inkjet coating properties of a base material.
Specifically, the surfactant may be a polymer type or oligomer type fluorine-based surfactant. As the surfactant, a commercially available product may be used, which may be selected from the group consisting of Glide 100, Glide 110, Glide 130, Glide 460, Glide 440, Glide 450 or RAD 2500 from TEGO, Megaface F-251, F-281, F554, F-560, F-561, F-562, F-563, F-565, F-568, F-570 and F-571 from DIC (DaiNippon Ink Chemicals), or Surflon S-111, S-112, S-113, S-121, S-131, S-132, S-141 and S-145 from Asahi Glass Co., Fluorad FC-93, FC-95, FC-98, FC-129, FC-135, FC-170C, FC-430 and FC-4430 from Sumitomo 3M Ltd., or Zonyl FS-300, FSN, FSN-100 and FSO from DuPont and BYK-350, BYK-354, BYK-355, BYK-356, BYK-358N, BYK-359, BYK-361N, BYK-381, BYK-388, BYK-392, BYK-394, BYK-399, BYK-3440, BYK-3441, BYKETOL-AQ, BYK-DYNWET 800 from BYK, and the like.
The surfactant may be comprised in an amount of 0.1 to 10 parts by weight, 0.05 to 10 parts by weight, 0.1 to 10 parts by weight, 0.5 to 8 parts by weight or 1 to 4 parts by weight, relative to 100 parts by weight of the epoxy compound. Within the content range, the present application makes it possible that the encapsulating composition is applied to an inkjet method to form an organic layer of a thin film.
In an embodiment of the present application, the encapsulating composition may further comprise a photosensitizer in order to complement the curing property at a long wavelength activation energy beam of 300 nm or more. The photosensitizer may be a compound that absorbs a wavelength in a range of 200 nm to 400 nm.
The photosensitizer may be one or more selected from the group consisting of an anthracene-based compound such as anthracene, 9,10-dibutoxyanthracene, 9,10-dimethoxyanthracene, 9,10-diethoxyanthracene and 2-ethyl-9,10-dimethoxyanthracene; a benzophenone-based compound such as benzophenone, 4,4-bis(dimethylamino)benzophenone, 4,4-bis(diethylamino)benzophenone, 2,4,6-trimethylaminobenzophenone, methyl-o-benzolybenzoate, 3,3 -dimethyl-4-methoxybenzophenone and 3,3,4,4-tetra(t-butylperoxycarbonyl)benzophenone; a ketone-based compound such as acetophenone, dimethoxyacetophenone, diethoxyacetophenone, 2-hydroxy-2-methyl-1-phenylpropan-1-one and propanone; perylene; a fluorene-based compound such as 9-fluorenone, 2-chloro-9-proprenone and 2-methyl-9-fluorenone; a thioxanthone-based compound such as thioxanthone, 2,4-diethylthioxanthone, 2-chlorothioxanthone, 1-chloro-4-propyloxythioxanthone, isopropylthioxanthone (ITX) and diisopropylthioxanthone; a xanthone-based compound such as xanthone and 2-methylxanthone; an anthraquinone-based compound such as anthraquinone, 2-methylanthraquinone, 2-ethylanthraquinone, t-butylanthraquinone and 2,6-dichloro-9,10-anthraquinone; an acridine-based compound such as 9-phenylacridine, 1,7-bis(9-acridinyl)heptane, 1, 5-bis(9-acridinylpentane) and 1, 3-bis(9-acridinyl)propane; a dicarbonyl compound such as benzyl, 1,7,7-trimethyl-bicyclo[2,2,1]heptane-2,3-dione and 9,10-phenanthrenequinone; a phosphine oxide-based compound such as 2,4,6-trimethylbenzoyldiphenylphosphine oxide and bis(2,6-dimethoxybenzoyl)-2,4,4-trimethylpentylphosphine oxide; a benzoate-based compound such as methyl-4-(dimethylamino) benzoate, ethyl-4-(dimethylamino) benzoate and 2-n-butoxyethyl-4-(dimethylamino) benzoate; an amino synergist such as 2,5-bis(4-diethylaminobenzal)cyclopentanone, 2,6-bis(4-diethylaminobenzal)cyclohexanone and 2,6-bis(4-diethylaminobenzal)-4-methyl-cyclopentanone; a coumarin-based compound such as 3,3 -carbonylvinyl-7-(diethylamino)coumarin, 3-(2-benzothiazolyl)-7-(diethylamino)coumarin, 3 -benzoyl-7-(diethylamino)coumarin, 3-benzoyl-7-methoxy-coumarin and 10,10-carbonylbis[1,1,7,7-tetramethyl-2,3,6,7-tetrahydro-1H,5H,11H-C1]-[6,7,8-ij]-quinolizin-11-one; a chalcone compound such as 4-diethylaminochalcone and 4-azidobenzalacetophenone; 2-benzoylmethylene; and 3-methyl-b-naphthothiazoline.
The photosensitizer may be included in a range of 28 to 40 parts by weight, 31 to 38 parts by weight or 32 to 36 parts by weight, relative to 100 parts by weight of the photoinitiator. By controlling the content of the photosensitizer, the present invention can realize a synergistic action of curing sensitivity at a desired wavelength, and also prevent the photosensitizer from lowering the adhesive force by not dissolving in the inkjet coating.
The encapsulating composition of the present application may further comprise a coupling agent. The present application can improve adhesiveness of a cured product of the encapsulating composition to an adherend or moisture transmission resistance of the cured product. The coupling agent may include, for example, a titanium-based coupling agent, an aluminum-based coupling agent, or a silane coupling agent.
In an embodiment of the present application, the silane coupling agent may include, specifically, an epoxy-based silane coupling agent such as 3-glycidyloxypropyltrimethoxysilane, 3-glycidyloxypropyltriethoxysilane, 3-glycidyloxypropyl (dimethoxy)methylsilane and 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane; a mercapto-based silane coupling agent such as 3-mercaptopropyltrimethoxysilane, 3-mercaptopropyltriethoxysilane, 3 -mercaptopropylmethyldimethoxysilane and 11-mercaptoundecyltrimethoxysilane; an amino-based silane coupling agent such as 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, 3-aminopropyldimethoxymethylsilane, N-phenyl-3-aminopropyltrimethoxysilane, N-methylaminopropyltrimethoxysilane, N-(2-aminoethyl)-3-aminopropyltrimethoxysilane and N-(2-aminoethyl)-3-aminopropyldimethoxymethylsilane; a ureide-based silane coupling agent such as 3-ureidepropyltriethoxysilane; a vinyl-based silane coupling agent such as vinyltrimethoxysilane, vinyltriethoxysilane and vinylmethyldiethoxysilane; a styryl-based silane coupling agent such as p-styryltrimethoxysilane; an acrylate-based silane coupling agent such as 3-acryloxypropyltrimethoxysilane and 3-methacryloxypropyltrimethoxysilane; an isocyanate-based silane coupling agent such as 3-isocyanatopropyltrimethoxysilane; a sulfide-based silane coupling agent such as bis(triethoxysilylpropyl)disulfide and bis(triethoxysilylpropyl)tetrasulfide; phenyltrimethoxysilane, methacryloxypropyltrimethoxysilane, imidazolesilane, triazinesilane, and the like.
In the present application, the coupling agent may be included in an amount of 0.1 to 10 parts by weight or 0.5 to 5 parts by weight, relative to 100 parts by weight of the epoxy compound. Within the above range, the present application can realize an effect of improving the adhesiveness by the addition of the coupling agent.
The encapsulating composition of the present application may comprise, if necessary, a moisture adsorbent. The term “moisture adsorbent” can be used to generically mean a component capable of adsorbing or removing moisture or humidity introduced from the outside through a physical or chemical reaction or the like. That is, it means a moisture-reactive adsorbent or a physical adsorbent, and a mixture thereof is also usable.
A specific kind of the usable moisture adsorbent in the present application is not particularly limited, which may include, for example, one or a mixture of two or more of a metal oxide, a metal salt or phosphorus pentoxide (P2O5), and the like, in the case of a moisture-reactive adsorbent, and may include zeolite, zirconia or montmorillonite, and the like, in the case of the physical adsorbent.
The encapsulating composition of the present application may comprise the moisture adsorbent in an amount of 5 parts by weight to 100 parts by weight, 5 to 80 parts by weight, 5 parts by weight to 70 parts by weight or 10 to 30 parts by weight, relative to 100 parts by weight of the epoxy compound. As the encapsulating composition of the present application preferably controls the content of the moisture adsorbent to 5 parts by weight or more, the present application can make the encapsulating composition or the cured product thereof exhibit excellent moisture and humidity barrier properties. In addition, by controlling the content of the moisture adsorbent to 100 parts by weight or less, the present application can provide a thin film sealing structure.
In one example, the encapsulating composition may further comprise an inorganic filler, if necessary. The specific type of the usable filler in the present application is not particularly limited, and for example, one or a mixture of two or more of clay, talc, alumina, calcium carbonate, silica, and the like may be used.
The encapsulating composition of the present application may comprise 0 to 50 parts by weight, 1 to 40 parts by weight, 1 to 20 parts by weight, or 1 to 10 parts by weight of inorganic filler, relative to 100 parts by weight of the epoxy compound. The present application can provide a sealing structure having excellent moisture or humidity barrier properties and mechanical properties by controlling the inorganic filler, preferably, to 1 part by weight or more. Furthermore, by controlling the content of the inorganic filler to 50 parts by weight or less, the present invention can provide a cured product exhibiting excellent moisture barrier properties even when formed into a thin film.
In addition to the above-mentioned constitutions, the encapsulating composition according to the present application may comprise various additives in the range without affecting the above-described effects of invention. For example, the encapsulating composition may comprise a defoamer, a tackifier, an ultraviolet stabilizer or an antioxidant and the like in an appropriate range of content depending on the desired physical properties.
In one example, the encapsulating composition may be in a liquid phase at room temperature, for example, at 25° C. In an embodiment of the present application, the encapsulating composition may be in a solventless type liquid phase. The encapsulating composition may be applied to sealing an organic electronic element, and specifically, may be applied to sealing the entire surface of the organic electronic element. As the encapsulating composition has a liquid form at room temperature, the present application can seal the organic electronic element by a method of applying the composition to the side of the element.
Also, the encapsulating composition of the present application may be an ink composition. The encapsulating composition of the present application may be an ink composition capable of an inkjet process. The encapsulating composition of the present application may have a specific composition and physical properties so that ink-jetting can be performed.
Furthermore, in an embodiment of the present application, the encapsulating composition may have a viscosity in a range of 50 cPs or less, 1 to 46 cPs or 5 to 44 cPs, as measured by Brookfield's DV-3 at a temperature of 25° C., a torque of 90% and a shear rate of 100rpm. By controlling the viscosity of the composition within the above range, the present application can realize physical properties that can be performed and increase coating properties, at the time of being applied to an organic electronic element, to provide a sealing material of a thin film.
In one example, the encapsulating composition may have a surface energy of the cured product after curing in a range of 5 mN/m to 45 mN/m, 10 mN/m to 40 mN/m, 15 mN/m to 35 mN/m, or 20 mN/m to 30 mN/m. The surface energy can be measured by a method known in the art, and for example, can be measured by a ring method. The present application can realize excellent coating properties in the above surface energy range.
In an embodiment of the present application, the surface energy (γsurface, mN/m) can be calculated as γsurface=γdispersion+γpolar. In one example, the surface energy can be measured using a drop shape analyzer (DSA100 product from KRUSS). For example, after an encapsulating composition for measuring the surface energy is applied on a SiNx substrate to a thickness of about 50 μm and a coating area of 4 cm2 (width: 2 cm, height: 2 cm) to form a sealing layer (spincoater), it is dried at room temperature for about 10 minutes under a nitrogen atmosphere and then UV-cured with an intensity of 1000 mW/cm2 through a light quantity of 4000 mJ/cm2. The process of dropping the deionized water whose surface tension is known on the film after curing, and obtaining the contact angle thereof is repeated five times to obtain an average value of the obtained five contact angle values, and identically, the process of dropping the diiodomethane whose surface tension is known thereon and obtaining the contact angle thereof is repeated five times to obtain an average value of the obtained five contact angle values. Then, the surface energy can be obtained by substituting the value (Strom value) regarding the solvent surface tension by the Owens-Wendt-Rabel-Kaelble method using the obtained average values of the contact angles for the deionized water and diiodomethane.
Also, in an embodiment of the present application, the encapsulating composition may have a light transmittance of 90% or more, 92% or more, or 95% or more in the visible light region after curing. Within the above range, the present application provides an organic electronic device having high-resolution, low power consumption and long-life by applying the encapsulating composition to a top emission type organic electronic device. Furthermore, the encapsulating composition of the present application may have a haze of 3% or less, 2% or less or 1% or less according to JIS K7105 standard test after curing, and the lower limit is not particularly limited, but may be 0%. Within the haze range, the encapsulating composition may have excellent optical properties after curing. In this specification, the above-mentioned light transmittance or haze may be measured in a state where the encapsulating composition is cured to an organic layer, and may be optical characteristics measured when the thickness of the organic layer is any one thickness of 2 μm to 50 μm. In an embodiment of the present application, in order to realize the optical characteristics, the above-mentioned moisture adsorbent or inorganic filler may not be included.
In one example, the encapsulating composition of the present application may have an amount of volatile organic compounds measured after curing of less than 50 ppm. In this specification, the volatile organic compound can be represented as outgas. The volatile organic compounds may be measured after curing the encapsulating composition and then holding a sample of the cured product at 110° C. for 30 minutes using Purge & Trap-gas chromatography/mass spectrometry. The measurement may be performed using a Purge & Trap sampler (JAI JTD-505 III)-GC/MS (Agilent 7890b/5977a) instrument.
The present application also relates to an organic electronic device. As shown in
In an embodiment of the present application, the organic electronic element may comprise a first electrode layer, an organic layer formed on the first electrode layer and comprising at least a light emitting layer, and a second electrode layer formed on the organic layer. The first electrode layer may be a transparent electrode layer or a reflective electrode layer, and the second electrode layer may also be a transparent electrode layer or a reflective electrode layer. More specifically, the organic electronic element may comprise a reflective electrode layer formed on a substrate, an organic layer formed on the reflective electrode layer and comprising at least a light emitting layer, and a transparent electrode layer formed on the organic layer.
In the present application, the organic electronic element (23) may be an organic light emitting diode.
In one example, the organic electronic device according to the present application may be a top emission type, but is not limited thereto, and may be applied to a bottom emission type.
The organic electronic device may further comprise a protective layer (35) for protecting the electrodes and the light emitting layer of the element. The protective layer may be an inorganic protective layer (35). The protective layer may be a protective layer by chemical vapor deposition (CVD), and the material may be the same as or different from the following inorganic layer, where a known inorganic material may be used. For example, as the protective layer, silicon nitride (SiNx) may be used. In one example, silicon nitride (SiNx) used as the protective layer can be deposited to a thickness of 0.01 μm to 50 μm.
In an embodiment of the present application, the organic electronic device (3) may further comprise an inorganic layer (34) formed on the organic layer (33). The material of the inorganic layer (34) is not limited, which may be the same as or different from the above-described protective layer. In addition, the inorganic layer (34) may be formed in the same manner as the protective layer (35). In one example, the inorganic layer may be one or more metal oxides or nitrides selected from the group consisting of Al, Zr, Ti, Hf, Ta, In, Sn, Zn and Si. The inorganic layer may have a thickness of 0.01 μm to 50 μm or 0.1 μm to 20 μm or 1 μm to 10 μm. In one example, the inorganic layer of the present application may be an inorganic material without any dopant, or may be an inorganic material comprising a dopant. The dopant which may be doped may be one or more elements selected from the group consisting of Ga, Si, Ge, Al, Sn, Ge, B, In, Tl, Sc, V, Cr, Mn, Fe, Co and Ni, or an oxide of the element, but is not limited thereto.
In one example, the organic layer may have a thickness in a range of 2 μm to 20 μm, 2.5 μm to 15 μm, and 2.8 μm to 9 μm. The present application may provide a thin-film organic electronic device by providing a thin organic layer.
The organic electronic device (3) of the present application may comprise a sealing structure comprising the organic layer (33) and the inorganic layer (34), as described above, where the sealing structure may comprise at least one or more organic layers and at least one or more inorganic layers, and the organic layer and the inorganic layer may be repeatedly laminated. For example, the organic electronic device may have a structure of substrate/organic electronic element/protective layer/(organic layer/inorganic layer)n, where n may be a number in a range of 1 to 100.
In one example, the organic electronic device (3) of the present application may further comprise a cover substrate present on the organic layer (33). The material of the substrate and/or the cover substrate is not particularly limited, and a known material in the art may be used. For example, the substrate or the cover substrate may be glass, a metal base material or a polymer film. As the polymer film, for example, a polyethylene terephthalate film, a polytetrafluoroethylene film, a polyethylene film, a polypropylene film, a polybutene film, a polybutadiene film, a vinyl chloride copolymer film, a polyurethane film, an ethylene-vinyl acetate film, an ethylene-propylene copolymer film, an ethylene-ethyl acrylate copolymer film, an ethylene-methyl acrylate copolymer film or a polyimide film and the like may be used.
Also, as shown in
The present application also relates to a method for manufacturing an organic electronic device.
In one example, the manufacturing method may comprise a step of forming an organic layer (33) on a substrate (31) in which an organic electronic element (32) is formed on its upper part, so that the above-described encapsulating composition seals the entire surface of the organic electronic element (32).
Here, the organic electronic element (32) may be produced by forming a reflective electrode or a transparent electrode on a substrate (31) such as glass or a polymer film, as a substrate (31), by a method such as vacuum deposition or sputtering, and forming an organic material layer on the reflective electrode. The organic material layer may comprise a hole injecting layer, a hole transporting layer, a light emitting layer, an electron injecting layer, and/or an electron transporting layer. Subsequently, a second electrode is further formed on the organic material layer. The second electrode may be a transparent electrode or a reflective electrode.
The manufacturing method of the present application may further comprise a step of forming a protective layer (35) on the first electrode, the organic material layer and the second electrode, formed on the substrate (31). Then, the above-described organic layer (33) is applied to cover the entire surface of the organic electronic element (32) on the substrate (31). Here, the step of forming the organic layer (33) is not particularly limited and the above-described encapsulating composition may be applied to the entire surface of the substrate (31) using a process such as inkjet printing, gravure coating, spin coating, screen printing or reverse offset coating.
The manufacturing method may further comprise a step of irradiating the organic layer with light. In the present invention, a curing process may also be performed on an organic layer sealing an organic electronic device, and such a curing process may be performed, for example, in a heating chamber or a UV chamber, and preferably, may be performed in a UV chamber.
In one example, after the above-described encapsulating composition is applied to form a top side organic layer, the composition can be irradiated with light to induce cross-linking. The irradiation of light may comprise irradiating with light having a wavelength range of 250 nm to 450 nm or 300 nm to 450 nm region bands at a light quantity of 0.3 to 6 J/cm2 or a light quantity of 0.5 to 5 J/cm2.
In addition, the manufacturing method of the present application may further comprise a step of forming an inorganic layer (34) on the organic layer (33). As the step of forming an inorganic material layer, a known method in the art may be used, which may be the same as or different from the above-described method of forming a protective layer.
The present application provides an encapsulating composition which can effectively block moisture or oxygen introduced into an organic electronic device from the outside to secure the lifetime of the organic electronic device, is possible to realize a top emission type organic electronic device, is applicable to an inkjet method and can provide a thin display, and an organic electronic device comprising the same.
3: organic electronic device
31: substrate
32: organic electronic element
33: organic layer
34: inorganic layer
35: protective layer
36: sealing structure
37: encapsulation film
38: cover substrate
Hereinafter, the present invention will be described in more detail through Examples according to the present invention and Comparative Examples not complying with the present invention, but the scope of the present invention is not limited by the following examples.
An alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (Irgacure PAG 290 from BASF, hereinafter, I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 23.8:28.7:37.5:5.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:F552) at room temperature.
In the mixing vessel, a uniform encapsulating composition ink was prepared using a planetary mixer (Kurabo, KK-250s).
An encapsulating composition was prepared in the same manner as in Example 1, except that an alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (FC-4430 from 3M) were each introduced into a mixing vessel in a weight ratio of 29.4:10.2:50.4:5.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:FC-4430) at room temperature.
An encapsulating composition was prepared in the same manner as in Example 1, except that an alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator comprising a sulfonium salt (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 12.4:24.8:46.8:10.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:F552) at room temperature.
An encapsulating composition was prepared in the same manner as in Example 1, except that an alicyclic epoxy compound (Celloxide 2081P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 24.8:24.3:40.9:5.0:1.0 (Celloxide 2081P:DE203:OXT-221:I290:F552) at room temperature.
An encapsulating composition was prepared in the same manner as in Example 1, except that an alicyclic epoxy compound (Celloxide 3000, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 30.0:7.2:52.8:5.0:1.0 (Celloxide 3000:DE203:OXT-221:I290:F552) at room temperature.
An alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator comprising a sulfonium salt (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 12.4:24.8:52.8:5.0:1.0 (Celloxide2021P:DE203:OXT-221:1290:F552) at room temperature.
In the mixing vessel, a uniform encapsulating composition ink was prepared using a planetary mixer (Kurabo, KK-250s).
An encapsulating composition was prepared in the same manner as in Example 6, except that GSID26-1 from BASF was used as a photoinitiator comprising a sulfonium salt instead of I290 as a photoinitiator.
An encapsulating composition was prepared in the same manner as in Example 6, except that CPI210S, a photoinitiator from San-apro Co., was used as a photoinitiator comprising a sulfonium salt instead of I290 as a photoinitiator.
An encapsulating composition was prepared in the same manner as in Example 6, except that UV 692 (active contents 50 wt %, solvent (propylene carbonate) 50 wt %) from Tetrachem was used as a photoinitiator comprising a sulfonium salt instead of I290 as a photoinitiator.
An encapsulating composition was prepared in the same manner as in Example 6, except that UV693 from Tetrachem was used as a photoinitiator comprising a sulfonium salt instead of I290 as a photoinitiator.
An encapsulating composition was prepared in the same manner as in Example 6, except that Irgacure PAG 103, a non-ionic photoinitiator from BASF, was used instead of I290 as a photoinitiator.
An encapsulating composition was prepared in the same manner as in Example 6, except that CGI725, a non-ionic photoinitiator from BASF, was used instead of I290 as a photoinitiator.
An encapsulating composition was prepared in the same manner as in Example 1, except that an alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) as an epoxy compound, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator comprising a sulfonium salt (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 37.5:52.5:5.0:1.0 (Celloxide2021P:OXT-221:I290:F552) at room temperature.
An encapsulating composition was prepared in the same manner as in Example 1, except that an alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 37.5:7.0:45.5:5.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:F552) at room temperature.
An encapsulating composition was prepared in the same manner as in Example 1, except that an alicyclic epoxy compound (Celloxide 2081P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 20.0:41.0:29.0:5.0:1.0 (Celloxide 2081P:DE203:OXT-221:I290:F552) at room temperature.
An encapsulating composition was prepared in the same manner as in Example 1 except that Irgacure 250 (active contents 75 wt %, solvent (propylene carbonate) 25 wt %), an iodonium photoinitiator from BASF, was used instead of I290 as a photoinitiator.
An alicyclic epoxy compound (Celloxide 2021P, Daicel) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 2.3:23.4:64.3:5.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:F552) at room temperature.
In the mixing vessel, a uniform encapsulating composition ink was prepared using a planetary mixer (Kurabo, KK-250s).
An encapsulating composition was prepared in the same manner as in Comparative Example 1, except that an alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 12.5:7.3:66.7:5.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:F552) at room temperature.
An encapsulating composition was prepared in the same manner as in Comparative Example 1, except that an alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 8.3:11.5:70.2:5.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:F552) at room temperature.
An encapsulating composition was prepared in the same manner as in Comparative Example 1, except that an alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 23.8:30.0:36.2:5.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:F552) at room temperature.
An encapsulating composition was prepared in the same manner as in Comparative Example 1, except that an alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 37.8:17.6:34.6:5.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:F552) at room temperature.
An encapsulating composition was prepared in the same manner as in Comparative Example 1, except that an alicyclic epoxy compound (Celloxide 2081P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a silicone-based surfactant (BYK1798 from BYK Co., Ltd.) were each introduced into a mixing vessel in a weight ratio of 24.8:24.3:40.9:5.0:1.0 (Celloxide 2081P:DE203:OXT-221:I290:BYK1798) at room temperature.
An encapsulating composition was prepared in the same manner as in Comparative Example 1, except that an alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a silicone-based surfactant (BYK3455 from BYK Co., Ltd.) were each introduced into a mixing vessel in a weight ratio of 30.0:7.2:52.8:5.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:BYK3455) at room temperature.
An encapsulating composition was prepared in the same manner as Example 6, except that an alicyclic epoxy compound (Celloxide 2021P, Daicel Corp.) and an aliphatic epoxy compound (DE203, HAJIN CHEM TECH) as epoxy compounds, an oxetane group-containing compound (OXT-221 from TOAGOSEI), a photoinitiator (I290) and a fluorine-based surfactant (F552 from DIC) were each introduced into a mixing vessel in a weight ratio of 12.4:24.8:55.8:1.0:1.0 (Celloxide2021P:DE203:OXT-221:I290:F552) at room temperature.
Physical properties in Examples and Comparative Examples were evaluated in the following manner.
1. Viscosity Measurement
Each viscosity of the encapsulating compositions prepared in Examples and Comparative Examples was measured using DV-3 as a Brookfield viscometer as follows.
For the prepared encapsulating composition, it was measured under conditions of a temperature of 25° C., a torque of 90% and a shear rate of 100 rpm. Specifically, 0.5 ml of a sample was injected using a cone/plate method of the Brookfield viscometer to measure the viscosity.
2. Curing Sensitivity Measurement
The encapsulating compositions prepared in Examples and Comparative Examples were each irradiated with UV of 1 J/cm2 at an intensity of 1000 mW/cm2 and then the tack free time of each adhesive was measured. First, the encapsulating composition is applied by spin coating to a thickness of 10 μm and cured. A time until a tacky feeling disappears and there is no leakage of the sealing material when the surface of the sealing material has been touched immediately after curing, is defined as a tack free time and measured. It was classified as ⊚ in the case where the tack free time was less than 1 second, as O in the case where it was less than 1 minute, as Δ in the case where it was 5 minutes or more and as X in the case where it was 30 minutes or more.
3. Contact Angle Measurement
For the encapsulating compositions prepared in Examples and Comparative Examples, each contact angle to glass at 25° C. was measured. It is measured by injecting the encapsulating composition into a syringe, dropping one droplet to a volume of 5 μl and then photographing it with CCD camera. The mean value of 5 times was used and the used equipment was DSA100 from KRUSS. It was classified as O in the case where the contact angle was less than 15° because the spreadability was excellent, as Δ in the case where the contact angle was 15° to 30°, and as X in the case where the contact angle was more than 30°.
4. Surface Hardness Measurement
The encapsulating compositions prepared in Examples and Comparative Examples were each applied on an LCD glass base material of 50 mm×50 mm to a thickness of 5 μm through spin coating. The applied composition was cured at a light quantity of 1000 mJ/cm2 through an LED UV lamp. The cured product was subjected to a surface hardness test at a speed of 273 mm/min under a weight of 500 g using a pencil hardness tester from H to 5 H.
5. Solubility Measurement
When the encapsulating compositions prepared in Examples and Comparative Examples were observed with naked eyes after they were stirred for 3 hours, it was classified as X in the case of no dissolution, as Δ in the case of partial dissolution and as O in the case of complete dissolution.
6. Outgas Measurement
The encapsulating compositions prepared in Examples and Comparative Examples were each cured by irradiation with UV of 1 J/cm2 at an intensity of 1000 mW/cm2, and 50 mg of each sample of the cured products was maintained at 110° C. for 30 minutes using Purge & Trap-gas chromatography/mass spectrometry and then the amount of volatile organic compounds was measured. The measurement was performed using a Purge & Trap sampler (JAI JTD-505 III)-GC/MS (Agilent 7890b/5977a) instrument. It was represented as O in the case where the measured amount was 50 ppm or less, as A in the case where it was 100 ppm or less and as X in the case where it was more than 100 ppm.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2016-0167794 | Dec 2016 | KR | national |