Patent Grant
7241932
The present invention relates to an immobilising medium for the encapsulation of radioactive waste.
Nuclear plants generate numerous types of radioactive waste which must be encapsulated for long-term storage. A current scheme for treating waste liquors, for example which arise from decontamination of plants by spraying them with nitric acid, comprises precipitating waste in a flocculent form by adding sodium hydroxide, separating the precipitated floc using ultrafiltration and encapsulating the floc in cement. However, the cemented waste form may not be as leach resistant and the waste loading may not be as high as it would be liked.
It is therefore an object of the invention to provide a waste form which is more leach resistant and/or provides a higher waste loading than the current waste forms.
According to a first aspect of the present invention there is provided a waste immobilising medium having a sodium silicate based glass matrix in which there is contained radioactive waste wherein the waste comprises one or more inert metal components and one or more fission products.
The term inert metal components as used herein means metal components not derived from the irradiated nuclear fuel, i.e. it does not include fission products or actinides. The inert metal components may be metal components derived from the plant. The inert metal components may, for example, originate from the dissolution of stainless steel in the plant as a result of spraying the plant with nitric acid.
The invention is therefore effective for treating waste streams from decontamination of plants rich in inert metal components.
At least a portion of the inert metal components are dissolved in the glass matrix and increase its durability. These inert metal components may be dissolved in the glass matrix up to their solubility limits to impart durability to the glass. As a result, the waste immobilising medium is highly durable and leach resistant and is suitable for long term storage of radioactive waste. It has been found that the leach resistance of the waste immobilising medium according to the present invention is better than for borosilicate glasses currently in use.
The inert metal components preferably comprise iron, nickel and chromium. The inert metal components may also comprise other metals e.g. zinc.
The waste may also comprise one or more phosphates. The waste may also comprise one or more other anions; e.g. it may comprise one or more sulphates.
Preferably, the waste comprises up to 10% fission products and at least 90% inert metal components calculated using the masses of the oxides of the fission products and the inert metal components.
Typically, the amount of fission products will be much less than 10%.
Preferably, at least 90% of the waste calculated as above comprises iron, nickel, chromium and, optionally, zinc.
Further preferably at least 90% of the waste calculated as above comprises iron, nickel and chromium.
The waste immobilising medium has a waste loading of up to about 90 weight %. Preferably, the waste loading is from about 80 weight % to about 90 weight %. Waste loading is defined as the mass of waste/total mass of waste immobilising medium, which is the same as mass of waste/(mass of waste+ mass of additives). Maximising the waste loading thereby minimises the final volume of the waste form.
The sodium silicate glass matrix efficiently acts as a host for the fission products and any actinide elements which are present in the waste. For example, caesium, barium and strontium may be dissolved in the glass.
The glass preferably comprises a weight ratio of silica to soda of between about 4.5–2.5:1. More preferably the weight ratio is about 4:1.
If a high phosphate level is present in the waste, a rare earth element may be incorporated into the immobilising medium in order to precipitate monazite. Typical rare earth elements which may be used include lanthanum, neodymium or cerium. Lanthanum is preferred. The function of the monazite phase is to immobilise phosphate which would otherwise cause phase separation in the sodium silicate glass.
The immobilising medium may use sodium which may be in the waste to provide at least some of the sodium used to form the sodium silicate glass.
According to a second aspect of the present invention there is provided a method of preparing the waste immobilising medium according to the first aspect of the invention, the method including the steps of
The amounts of the sodium containing precursor and silica are adjusted so that a sodium silicate glass is formed in the final waste immobilising medium.
The radioactive waste is typically provided in the form of a waste liquor.
The waste liquor may contain a sodium-containing component. Thus, the waste liquor may provide at least some of the sodium for forming the sodium silicate glass matrix.
The sodium containing precursor may be sodium oxide (Na2O) or, preferably, sodium silicate.
A preferred precursor composition which is added to the waste to form the mixture comprises a glass frit of about 20 weight % soda (Na2O) and about 80 weight % silica (SiO2)
A rare earth element e.g. lanthanum may be include in the mixture to enable formation of the monazite where there is phosphate in the waste. The rare earth element may be added in the form of the oxide, e.g. La2O3.
Because of the use of nitric acid in nuclear plants, many of the waste components in the waste may be present in the form of nitrates.
Preferably, such waste liquor is denitrated before or whilst forming the mixture. This makes further processing easier. If the liquor is not denitrated, an undesirable sludge or paste may be formed in the mixture which may be difficult to dry effectively.
The denitration may be performed in one of many ways. A preferred method of denitration comprises reacting the liquor with formaldehyde. After denitration, the liquor remains as a substantially liquid phase.
Mixing of the components in the mixture is effected typically by stirring. Stirring ensures homogeneity in the mixture. Other methods of homogeneously mixing may be used.
After the mixture has been formed and sufficiently mixed, the mixture is dried. The drying may be carried out by one of many methods known to the skilled person in the art.
After the mixture has been dried, it is calcined to form a powder. The calcination may be carried out in a neutral (e.g. with N2 gas) or reducing atmosphere. The reducing atmosphere may comprise an Ar/H2 mixture or a N2/H2 mixture. The hydrogen is typically diluted to 10% or less in the inert gas. For example, a 5% mixture of H2 in N2 may be used.
The calcination may be carried out between 650–800° C. Typically, about 750° C. may be used.
Optionally, the calcined powder, particularly powder calcined in an N2/H2 mixture, may be mixed with an oxygen getter prior to compaction and sintering. The oxygen getter may be a metal. For example, metallic titanium is an effective getter.
Where a metal getter is used, e.g. titanium, it may be present in the powder in an amount of, for example, about 2 wt %.
Finally, the calcined powder is compacted and sintered to produce the final immobilising medium suitable for long term storage.
The compaction and sintering may be carried out according to known methods such as Hot Uniaxial Pressing or Hot Isostatic Pressing (HIP). HIP is preferred. Preferably the temperature for HIP is 1000–1400° C. More preferably the temperature for HIP is 1100–1300° C.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0118945.5 | Aug 2001 | GB | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/GB02/03322 | 7/22/2002 | WO | 00 | 8/3/2004 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO03/015106 | 2/20/2003 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3849330 | Isaacson et al. | Nov 1974 | A |
| 4234449 | Wolson et al. | Nov 1980 | A |
| 4404129 | Penberthy et al. | Sep 1983 | A |
| 4726916 | Aubert et al. | Feb 1988 | A |
| 5774815 | Christian et al. | Jun 1998 | A |
| 6023006 | Fiquet et al. | Feb 2000 | A |
| Number | Date | Country |
|---|---|---|
| 0 043 643 | Jan 1982 | EP |
| 1 588 350 | Apr 1981 | GB |
| WO 9801867 | Jan 1998 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20040267080 A1 | Dec 2004 | US |