ENERGY COMPENSATED EQUIPOWER DENSITY OBLIQUE LASER SHOCK METHOD

Abstract

The present invention relates to the technical field of material surface peening, and more particularly to an energy compensated equipower density oblique laser shock method. The method includes: acquiring a radius of curvature of a peening region of a part to be processed, and judging a range of a laser incident angle; determining laser parameters, such as laser pulse width, a spot diameter, and required laser energy under a vertical incidence condition; calculating the required laser energy at the minimum incident angle, and judging whether the energy falls within the technical indexes of a laser; and performing laser shock peening on the part by pulse laser beams with different energies. According to the present invention, the laser power or energy is compensated according to changes in the incident angle and the radius of curvature of the part to be processed.

Description

TECHNICAL FIELD

The present invention relates to the technical field of material surface peening, and more particularly, to an energy compensated equipower density oblique laser shock method.

BACKGROUND OF THE PRESENT INVENTION

Laser shock, which is a technology of peening metal by shock waves inducted by strong laser, can substantially enhance the durability of metal materials. Laser has good reachability and accurate positioning; therefore, laser shock peening technology can be performed on some parts that cannot be processed by traditional surface peening. The laser shock peening technology is especially suitable for such parts as holes, chamfers, welds and grooves. However, the laser shock peening must be performed in an oblique incident angle when being performed on an impeller or an arc root of the whole blade. As the incident angle and an arc angle are changed, the shape and area of the projection plane of the laser beam on the surface are also changed, causing uneven laser shock peening effect.

SUMMARY OF THE PRESENT INVENTION

The purpose of the present invention is to overcome the shortcomings of the existing art, and provides an energy compensated equipower density oblique laser shock method based on an incident angle and a radius of curvature, to ensure the unchanged laser power density in the same region or on the same trajectory and improve the evenness of residual stress distribution.

To solve the technical problem, the present invention adopts the following technical solutions:

An energy compensated equipower density oblique laser shock method, including the following steps:

S1. acquiring a radius of curvature R of an arc peening region of a part to be processed and morphological characteristics thereof, judging a range of a laser incident angle α, and acquiring a minimum incident angle α_min;

S2: determining, according to a mechanical property of the part to be processed and a processing strength requirement thereof, laser parameters including laser pulse intensity, a spot diameter D, and required laser energy Eo under a vertical incidence condition;

S3. determining required laser energy E at the minimum incident angle α_min according to the minimum incident angle α_min determined in Step S1, the radius of curvature R and the spot diameter D determined in Step S2; and judging whether the laser energy E falls within the technical indexes of the laser, and proceeding to Step S4 if yes; and if no, returning to Step S2 to reselect the laser parameters;

S4. determining a peening path of the arc peening region of the part to be processed and a spot lapping rule; and

S5. performing laser shock peening to the part by pulse laser beams with different energies through the different incident angles.

According to the energy compensated equipower density oblique laser shock method, the laser power or energy is compensated according to changes in the incident angle and the radius of curvature of the part to be processed, thereby avoiding uneven peening effect arisen from changes in the shape and area of a projection plane of the laser beam on the surface of the part, achieving isointensity peening, ensuring unchanged laser power density in the same region or on the same trajectory, improving the evenness of residual stress distribution and the shock effect, and reducing roughness of the laser shock processed surface.

Preferably, the range of the laser incident angle α is α_min≤α<90°. The laser incident angle α is obtained according to the radius of curvature R of the arc peening region of the part to be processed and the influence of adjacent parts of the part to be processed to the regions to be processed.

Preferably, the part to be processed in Step S1 is an impeller including a bladed disk and a blade. The arc region is arranged at the joint of the bladed disk and the impeller. The laser shock peening is suitable for parts that cannot be processed by traditional surface peening, such as holes, chamfers, welds and grooves, and widely used in the arc peening region of the root of the impeller.

Preferably, the calculation of the required laser energy E at the minimum incident angle α_min in Step S3 includes the following steps:

S31. when the incident angle α is minimum, the spot area S is:

$S=\left(2R-\sqrt{4R^2-D^2}\right){\int }_0^{\frac{D}{2}}\sqrt{1+\frac{16R^2}{\left(D^2-4x^2\right){\cos }^2\alpha }}\mathrm{dx};$

S32. the required laser energy E during the oblique shock is:

$E=\frac{4E_0S}{\pi D^2}=\frac{4E_0(2R-\sqrt{4R^2-D^2)}}{\pi D^2}{\int }_0^{\frac{D}{2}}\sqrt{1+\frac{16R^2}{\left(D^2-4x^2\right){\cos }^2\alpha }}\mathrm{dx}.$

Preferably, in a peening path of the part to be processed in Step S4:

S41. the laser peening starts at an end face of the arc peening region;

S42. the part to be processed is moved to increase the incident angle gradually and uniformly, and the arc peening region is shocked at the minimum incident angle α_min or by the required laser energy E at the minimum incident angle α_min, till to the maximum incident angle;

S43. the part to be processed is rotated, shocked at the maximum incident angle, and moved to decrease the incident angle gradually and uniformly, till to the end face of the arc peening region; and

S44. reciprocating circulation is performed till the end face at one side of the arc peening region is peened.

Preferably, the spot lapping rule in Step S4 includes that a spot lapping rate η is kept unchanged during the laser shock peening. The spot lapping rate η is a ratio between a length a′ of a curve connected at the intersection of the adjacent spots and a length a of a curve at two points which are farthest from the spot.

Preferably, steps of preprocessing a region to be peened, clamping the part to be processed and storing the peening path determined in Step S4 in the laser are included before Step S5. Preprocessing, clamping of the part to be processed, setting and storage of the peening path parameters are conventional operations of the laser, thus creating a precondition for shock peening of the part to be processed.

Compared with the existing art, the present invention has the following beneficial effects:

According to the energy compensated equipower density oblique laser shock method, the laser power or energy is compensated according to changes in the incident angle and the radius of curvature of the part to be processed, thereby avoiding uneven peening effect arisen from changes in the shape and area of a projection plane of the laser beam on the surface of the part, achieving isointensity peening, ensuring unchanged laser power density in the same region or on the same trajectory, improving the evenness of residual stress distribution and the shock effect, and reducing roughness of the laser shock processed surface.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flow chart of an energy compensated equipower density oblique laser shock method of the present invention;

FIG. 2 is a schematic diagram of an incident beam of an intermediate region peened at a minimum incident angle in Embodiment I;

FIG. 3 is a schematic diagram of a peening path of an arc peening region in Embodiment I; and

FIG. 4 is a schematic diagram of a spot lapping rate in Embodiment I.

DETAILED DESCRIPTION OF THE PRESENT INVENTION

The present invention is further described below in combination with the specific embodiments. Drawings are only used for exemplary description, and represent schematic diagrams only, rather than physical drawings, and thus, shall not be understood as the limitation to the present patent. To describe the embodiments of the present invention better, some components in the drawings may be omitted, amplified or reduced, and do not represent the dimensions of actual products. It could be understood for those skilled in the art that some known structures and description thereof in the drawings may be omitted.

The same or similar labels in the drawings of the embodiments of the present invention correspond to the same or similar components. In the description of the present invention, it should be understood that, if orientation or position relationships of terms “up”, “down”, “left” and “right” are the orientation or position relationships shown based on the drawings, such relationships only facilitate the description of the present invention and simplify the description, rather than indicating or implying that the indicated position or the components must have the specific orientation and constructed and operated in the specific orientation. Therefore, the terms for describing the position relationship in the drawings are only used for exemplary description, and shall not be understood as the limitation to the patent. Those ordinary skilled in the art could understand the specific meanings of the above terms according to the specific situations.

Embodiment 1

FIG. 1 to FIG. 4 show the first embodiment of an energy compensated equipower density oblique laser shock method, including the following steps:

S1. acquiring a radius of curvature R of an arc peening region of a part to be processed and morphological characteristics thereof, judging a range of a laser incident angle α, and acquiring a minimum incident angle α_min. In the present embodiment, the range of the laser incident angle α is α_min≤α<90°, the part to be processed in the present embodiment is an impeller including a bladed disk and a blade, and the arc region is arranged at the joint of the bladed disk and the impeller;

S2: determining, according to a mechanical property of the part to be processed and a processing strength requirement thereof, laser parameters including laser pulse intensity, a spot diameter D, and required laser energy Eo under a vertical incidence condition;

S3. determining required laser energy E at the minimum incident angle α_min according to the minimum incident angle α_min determined in Step S1, the radius of curvature R and the spot diameter D determined in Step S2; and judging whether the laser energy E falls within the technical indexes of the laser, and proceeding to Step S4 if yes; and if no, returning to Step S2 to reselect the laser parameters,

wherein the calculation of the required laser energy E at the minimum incident angle α_min in Step S3 includes the following steps:

S31. when the incident angle α is minimum, the spot area S is:

$S=\left(2R-\sqrt{4R^2-D^2}\right){\int }_0^{\frac{D}{2}}\sqrt{1+\frac{16R^2}{\left(D^2-4x^2\right){\cos }^2\alpha }}\mathrm{dx};$

S32. the required laser energy E during the oblique shock is:

$E=\frac{4E_0S}{\pi D^2}=\frac{4E_0(2R-\sqrt{4R^2-D^2)}}{\pi D^2}{\int }_0^{\frac{D}{2}}\sqrt{1+\frac{16R^2}{\left(D^2-4x^2\right){\cos }^2\alpha }}\mathrm{dx};$

S4. determining a peening path of the arc peening region of the part to be processed and a spot lapping rule, wherein in a peening path of the part to be processed in Step S4: S41. the laser peening starts at an end face of the arc peening region; S42. the part to be processed is moved to increase the incident angle gradually and uniformly, and the arc peening region is shocked at the minimum incident angle α_min or by the required laser energy E at the minimum incident angle α_min, till to the maximum incident angle;

S43. the part to be processed is rotated, shocked at the maximum incident angle, and moved to decrease the incident angle gradually and uniformly, till to the end face of the arc peening region; and

S44. reciprocating circulation is performed till the end face at one side of the arc peening region is peened.

As shown in FIG. 4, the spot lapping rule in Step S4 includes that a spot lapping rate η is kept unchanged during the laser shock peening. The spot lapping rate η is a ratio between a length a′ of a curve connected at the intersection of the adjacent spots and a length a of a curve at two points which are farthest from the spot.

S5. Performing laser shock peening to the part by pulse laser beams with different energies through the different incident angles. Steps of preprocessing a region to be peened, clamping the part to be processed and storing the peening path determined in Step S4 in the laser are included before Step S5.

Through the above steps, the laser power or energy is compensated according to changes in the incident angle and the radius of curvature of the part to be processed, thereby avoiding uneven peening effect arisen from changes in the shape and area of a projection plane of the laser beam on the surface of the part, achieving isointensity peening, ensuring unchanged laser power density in the same region or on the same trajectory, improving the evenness of residual stress distribution and the shock effect, and reducing roughness of the laser shock processed surface.

Apparently, the above embodiments of the present invention are only examples taken for clearly describing the present invention, rather than limiting the embodiments of the present invention. Those ordinary skilled in the art can also make other different forms of changes or vibrations based on the above description. All embodiments need not and cannot be illustrated herein. Any modification, equivalent replacement and improvement made within the spirit and principle of the present invention shall fall within the protection scope of claims of the present invention.

Claims

1. An energy compensated equipower density oblique laser shock method, comprising the following steps: S1. acquiring a radius of curvature R of an arc peening region of a part to be processed and morphological characteristics thereof, judging a range of a laser incident angle α, and acquiring a minimum incident angle αmin;S2: determining, according to a mechanical property of the part to be processed and a processing strength requirement thereof, laser parameters comprising laser pulse intensity, a spot diameter D, and required laser energy Eo under a vertical incidence condition;S3. determining required laser energy E at the minimum incident angle αmin according to the minimum incident angle αmin determined in Step S1, the radius of curvature R and the spot diameter D determined in Step S2; and judging whether the laser energy E falls within the technical indexes of the laser, and proceeding to Step S4 if yes; and if no, returning to Step S2 to reselect the laser parameters;S4. determining a peening path of the arc peening region of the part to be processed and a spot lapping rule, wherein the spot lapping rule in Step S4 comprises that a spot lapping rate η is kept unchanged during the laser shock peening;S5. performing laser shock peening to the part by pulse laser beams with different energies through the different incident angles,wherein a peening path of the part to be processed in Step S4 is determined according to the following steps:S41. the laser peening starts at an end face of the arc peening region;S42. the part to be processed is moved to increase the incident angle gradually and uniformly, and the arc peening region is shocked at the minimum incident angle αmin or by the required laser energy E at the minimum incident angle αmin, till to the maximum incident angle;S43. the part to be processed is rotated, shocked at the maximum incident angle, and moved to decrease the incident angle gradually and uniformly, till to the end face of the arc peening region; andS44. reciprocating circulation is performed till the end face at one side of the arc peening region is peened.

2. The energy compensated equipower density oblique laser shock method according to claim 1, wherein the range of the laser incident angle α is αmin≤α<90°.

3. The energy compensated equipower density oblique laser shock method according to claim 1, wherein the part to be processed in Step S1 is an impeller comprising a bladed disk and a blade; and the arc region is arranged at the joint of the bladed disk and the impeller.

4. The energy compensated equipower density oblique laser shock method according to claim 1, wherein the calculation of the required laser energy E at the minimum incident angle αmin in Step S3 comprises the following steps: S31. when the incident angle α is minimum, the spot area S is:

5. The energy compensated equipower density oblique laser shock method according to claim 1, wherein in step S4, the spot lapping rate η is a ratio between a length a′ of a curve connected at the intersection of the adjacent spots and a length a of a curve at two points which are farthest from the spot.

6. The energy compensated equipower density oblique laser shock method according to claim 1, wherein steps of preprocessing a region to be peened, clamping the part to be processed and storing the peening path determined in Step S4 in the laser are comprised before Step S5.

7. The energy compensated equipower density oblique laser shock method according to claim 2, wherein steps of preprocessing a region to be peened, clamping the part to be processed and storing the peening path determined in Step S4 in the laser are comprised before Step S5.

8. The energy compensated equipower density oblique laser shock method according to claim 3, wherein steps of preprocessing a region to be peened, clamping the part to be processed and storing the peening path determined in Step S4 in the laser are comprised before Step S5.

9. The energy compensated equipower density oblique laser shock method according to claim 4, wherein steps of preprocessing a region to be peened, clamping the part to be processed and storing the peening path determined in Step S4 in the laser are comprised before Step S5.

10. The energy compensated equipower density oblique laser shock method according to claim 5, wherein steps of preprocessing a region to be peened, clamping the part to be processed and storing the peening path determined in Step S4 in the laser are comprised before Step S5.