Patent Grant
10745837
Wet wipes cut from fibrous web structures formed in a co-forming process have been marketed for several years. The co-forming process involves melt spinning continuous filaments from polymer resin, and simultaneously, directing an air stream with entrained distributed cellulose fibers together with the filaments, typically into a co-forming box or similar blending apparatus, blending the filaments and fibers, and directing the blend along to a collecting/forming structure such as a moving forming belt. The filaments may be spun and introduced into the airstream carrying the cellulose fibers, or an airstream carrying the cellulose fibers may be introduced into the pathway of the filaments following spinning, the effect being the deposit of an entangled blend of filaments and fibers onto the moving forming structure and accumulation and formation of a batt thereof. Upon subsequent consolidation and bonding of the batt, a cohesive fibrous web structure may be formed. The co-forming process is, advantageously, typically dry, in contrast to wet forming techniques often used to make products such as paper towels from cellulose pulp. The co-formed fibrous web structure may be used, for example, as a wet wipe substrate. The entangled polymer filaments in the co-formed structure provide a matrix that holds the relatively short fibers, entangled therewithin, in place within the structure, and thereby help maintain structural integrity of the structure when it is wetted with an aqueous lotion.
The fibrous web structure from which wet wipes (for example, baby wipes) are made, should be strong enough when moistened with a lotion to maintain structural integrity in use, but also soft enough to give a pleasing and comfortable tactile sensation to the user. In addition, the structure should have suitable absorbency, porosity and surface texture to be effective in absorbing, retaining and carrying an aqueous lotion, releasing the lotion under pressure during use, and in cleaning soiled skin, while at the same time providing a reliable barrier between the user's hand and the soil (e.g., fecal matter).
In addition, cost and environmental sustainability concerns impose pressure to further improve the performance of wipes to enable better cleaning with less material, without compromising lotion carrying and release and other important properties such as tensile strength and protection.
Recently, improvements have been introduced to the co-forming process and resulting fibrous web structure. As described in U.S. application Ser. No. 13/076,492, a co-formed fibrous web structure with improved absorption properties is described.
In addition to the other improvements described in that application, it is briefly surmised that layers formed of meltblown polymer filaments alone can be formed on the outermost surfaces of the co-formed batt prior to bonding, to beneficial effect. It is surmised that the addition of the meltblown layer (called “scrim”) can help reduce release of lint (comprising fibers dislodged from the structure) during use by a consumer.
However, the ways in which inclusion of scrim layers, and the relative proportions of components of the scrim layers and intermediate or core layers, affect properties such as tensile strength, drape, surface friction, opacity, texture and feel of the web material, have not been apparent or predictable. Thus, it would be beneficial if the best proportions of components overall, together with their allocations among the various layers or substructures, of a fibrous web structure having scrim layers, and any other improvements making the structure desirable for use as wet wipe substrate, could be identified.
As used herein, the articles “a” and “an” when used herein, for example, “an anionic surfactant” or “a fiber” is understood to mean one or more of the material that is claimed or described.
“Basis Weight” is the weight per unit surface area (in a machine-direction/cross-direction plane) of a sample of web material (on one side), expressed in grams/meter2 (gsm). Basis weight may be specified in manufacturing specifications, and also may be measured, and reflects the weight of the material prior to addition of any liquid composition.
“Co-formed fibrous web structure” as used herein means that the fibrous web structure comprises an intermixed and/or entangled blend of at least two different materials wherein at least one of the materials comprises filaments, such as spun polymer filament (e.g., filaments spun from polypropylene resin), and at least one other material, different from the first material, comprises fibers. In one example, a co-formed fibrous web structure comprises fibers, such as cellulose or wood pulp fibers, and filaments, such as spun polypropylene filaments. A co-formed fibrous web structure may also comprise solid particulate additives such as but not limited to absorbent gel materials, filler particles, particulate spot bonding powders or clays.
“Cross Direction” or “CD” with respect to a fibrous web structure means the direction perpendicular to the predominant direction of movement of the fibrous web structure through its manufacturing line.
“Fiber” means an elongate particulate having a limited length exceeding its width or diameter, i.e. a length to width ratio of no more than 200. For purposes of the present disclosure, a “fiber” is an elongate particulate as described above that has a length of less than 3 cm. Fibers are typically considered discontinuous in nature. Non-limiting examples of fibers include hardwood and softwood pulp fibers; hemp bast; bagasse; bamboo; corn stalk; cotton; cotton stalk; cotton linters; esparto grass; flax tow; jute bast; kenaf bast; reed; rice straw, sisal; switch grass; wheat straw; and synthetic staple (i.e., cut or chopped) spun fibers made from polyester, nylons, rayon (including viscose and lyocell); polyolefins such as polypropylene and polyethylene, natural polymers, such as starch, starch derivatives, cellulose and cellulose derivatives, hemicellulose, hemicellulose derivatives, chitin, chitosan, polyisoprene (cis and trans), peptides, polyhydroxyalkanoates, copolymers of polyolefins such as polyethylene-octene, and biodegradable or compostable thermoplastics such as polylactic acid, polyvinyl alcohol, and polycaprolactone. Synthetic fibers may be monocomponent or multicomponent, e.g., bicomponent. For purposes herein, “long fibers” have an average length exceeding 10 mm; “medium length fibers” have an average length of from 2 mm and 10 mm; and “short fibers” have an average length less than 2 mm.
“Fibrous web structure” as used herein means a web or sheet structure formed of one or more types of filaments and/or fibers. The term “fibrous web structure” encompasses nonwovens.
A “filament” is an elongate particulate having a theoretically unlimited length, but at least a length-to-width and/or length-to-diameter ratio greater than 500 and a length greater than 5.08 cm. Filaments are typically spun in a continuous process, and are, therefore, considered substantially “continuous” in nature, having an indeterminate length. Non-limiting examples of filaments include meltspun/meltblown or spunbond filaments spun from polymer resin. Non-limiting examples of materials that can be spun into filaments include natural polymers, such as starch, starch derivatives, cellulose and cellulose derivatives, hemicellulose, hemicellulose derivatives, chitin, chitosan, polyisoprene (cis and trans), peptides, polyhydroxyalkanoates, and synthetic polymers including, but not limited to, thermoplastic polymers, such as polyesters, nylons, polyolefins such as polypropylene, polyethylene, polyvinyl alcohol and polyvinyl alcohol derivatives, sodium polyacrylate (absorbent gel material), and copolymers of polyolefins such as polyethylene-octene, and biodegradable or compostable thermoplastic fibers such as polylactic acid, polyvinyl alcohol, and polycaprolactone. Filaments may be monocomponent or multicomponent, e.g., bicomponent.
“Like chemistry,” with respect to two polymers, two blends of polymers, or a polymer and a blend of polymers, means that the two polymers, two blends of polymers, or a polymer and a blend of polymers, are capable of mixing at a temperature of 250° C. or lower, to form a single thermodynamic phase.
“Liquid composition” refers to any liquid, including, but not limited to a pure liquid such as water, an aqueous solution, a colloid, an emulsion (including oil-in-water and water-in-oil), a suspension, a solution and mixtures thereof. The term “aqueous solution” as used herein, refers to a solution that is at least about 20%, at least about 40%, or even at least about 50% water by weight, and is no more than about 95%, or no more than about 90% water by weight. The term “liquid composition” encompasses a lotion or other cleaning or skin conditioning formulation that may be included with wet wipes.
“Machine Direction” or “MD” with respect to a fibrous web structure means the direction parallel to the predominant direction of movement of the fibrous web structure through its manufacturing line.
“Meltblown” and forms thereof refer to a process of making filaments and webs thereof, in which filaments are spun by extruding streams of molten polymer resin under pressure through one or more spinnerets, and then substantially attenuating (elongating and reducing diameter and/or width of) the polymer streams following their exit from the spinnerets, with one or more high-velocity streams of heated air proximate the exits of the spinnerets. The air handling equipment (such as a manifold) may be a separate or integral part of the spinneret and is configured to direct the air stream(s) along path(s) at least partially parallel to the direction of extrusion of the polymer streams. Meltblown filaments are distinguished from polymer filaments made by other spunbond or melt-spinning processes by their comparatively very small diameter and/or very small width, imparted by the attenuating air streams, and typically have an average diameter or width of from 0.1 μm to 30 μm, 15 μm, 10 μm or even 5 μm. Following attenuation, the filaments may be air quenched with cooling air, or mist quenched with a mixture of cooling air and water droplets. The spun, attenuated and quenched fibers are then typically directed toward and accumulated in somewhat random, varying and entangled orientation on, a moving belt or rotating drum, to form a web.
“Nonwoven” for purposes herein means a consolidated web of fibers, continuous filaments, or chopped or staple fibers of any nature or origin, or any blend thereof, which have been formed into a web, and bonded together by any means, with the exception of weaving or knitting. A nonwoven is an example of a fibrous web structure. “Nonwoven” does not include nonfibrous skin-like or membrane-like materials with a continuous structure sometimes identified or described as “films”. “Nonwoven” does not include a product, such as paper, in which cellulose pulp fibers are distributed via a wetlaying process to form a sheet or web, without the need for any post-formation bonding processes to complete formation of the sheet or web.
“Particulate” as used herein means a granular substance or powder.
“Predominate” or a form thereof, with respect to a proportion of a component of a structure or composition, means that the component constitutes the majority of the weight of the structure or composition.
“Pre-moistened” and “wet” are used interchangeably herein and refer to fibrous web structures and/or wipes which are moistened with a liquid composition prior to packaging, and may be packaged in an effectively moisture impervious container or wrapper. Such pre-moistened wipes, which can also be referred to as “wet wipes,” may be suitable for use for cleaning a baby's skin (such, as, e.g., during a diaper change), as well the skin of older children and adults.
“Stack” refers to an orderly pile of individually cut portions of fibrous web structure, e.g., wipes. Based upon the assumption that there are at least three wipes in a stack, each wipe, except for the topmost and bottommost wipes in the stack, will be in direct contact with the wipe directly above and below itself in the stack. Moreover, when viewed from above, the wipes will be layered on top of each other, or superimposed, such that only the topmost wipe of the stack will be visible. The height of the stack is measured from the bottom of the bottommost wipe in the stack to the top of the topmost wipe in the stack and is provided in units of millimeters (mm).
“Surfactant” as used herein, refers to materials which preferably orient toward an interface. Surfactants include the various surfactants known in the art, including: nonionic surfactants; anionic surfactants; cationic surfactants; amphoteric surfactants, zwitterionic surfactants; and mixtures thereof.
Herein, where the quantity of a component of a fibrous web structure is expressed in “X weight percent” or “X percent by weight,” or an abbreviated or shortened form thereof, the quantity means that the component's weight constitutes X percent of the total weight of the fibrous web structure.
“z-direction” with respect to a web or a fibrous web structure means the direction orthogonal to the plane defined by the machine direction and cross direction of the web or fibrous web structure.
Unless otherwise noted, all component or composition levels are in reference to the active level of that component or composition, and are exclusive of impurities, for example, residual solvents or by-products, which may be present in commercially available sources.
Fibrous Web Structure
A fibrous web structure within the scope of the present invention may have a basis weight between about 10 gsm to about 120 gsm and/or from about 20 gsm to about 110 gsm and/or from about 30 gsm to about 100 gsm and/or from about 40 to 90 gsm. For purposes of use for making baby wipes, from product testing and consumer research it is believed that a fibrous web structure as disclosed herein having a basis weight from 40 gsm to 90 gsm and more preferably from 45 gsm to 85 gsm strikes the best balance between thickness/caliper, absorption capacity, opacity, drape and feel, and tensile strength, on one hand, and economy, on the other hand.
The fibrous web structure may include additives such as softening agents, temporary wet strength agents, permanent wet strength agents, bulk softening agents, silicones, wetting agents, latexes, especially surface-pattern-applied latexes, dry strength agents such as carboxymethylcellulose and starch, and other types of additives suitable for inclusion in and/or on fibrous web structures.
Fibrous web structures with the scope of the present invention may be formed of a plurality of filaments, a plurality of fibers, and a mixture of filaments and fibers.
Fibers useful as components of the fibrous web structure include cellulosic fibers commonly known as wood pulp fibers. Applicable wood pulps include chemical pulps, such as Kraft, sulfite, and sulfate pulps, as well as mechanical pulps including, for example, groundwood, thermomechanical pulp and chemically modified thermomechanical pulp. Chemical pulps, however, may be preferred since they impart a superior tactile sense of softness to tissue sheets made therefrom. Pulps derived from both angiosperm (flowering) trees (hereinafter, also referred to as “hardwood”) and gymnosperm (coniferous) trees (hereinafter, also referred to as “softwood”) may be utilized. The hardwood and softwood fibers can be blended, or alternatively, can be deposited in layers to provide a stratified web. U.S. Pat. Nos. 4,300,981 and 3,994,771 are incorporated herein by reference for the purpose of disclosing layering of hardwood and softwood fibers. Also applicable are fibers derived from recycled paper, which may contain any or all of the above categories as well as other non-fibrous materials such as fillers and adhesives used to facilitate the original papermaking.
A blend of long, or medium-length, pulp fibers, and short pulp fibers may be suitable for purposes herein. Generally, long and medium-length fibers tend to be larger and more coarse, providing desirable texture and absorption characteristics, while short fibers tend to be finer and softer, enhancing opacity of the structure and adding tactile softness. Including short pulp fibers as a portion of the fiber blend may be beneficial for controllably including consolidated masses of fibers in the blend.
In one example, a blend of softwood pulp fibers (medium-length) and hardwood pulp fibers (short) may be used. The softwood and hardwood pulp fibers, or medium-length and short fibers, may be included in a weight ratio of 20:80 to 90:10. For purposes herein, it may be desired that the weight ratio of softwood fibers to hardwood fibers, or weight ratio of medium-length fibers to short fibers, be from 60:40 to 90:10, more preferably 65:35 to 85:15, and still more preferably 70:30 to 80:20 in the structure. In a more particular example within these ranges, the softwood pulp fibers may be SSK (southern softwood kraft) pulp fibers. In another more particular example within these ranges, the hardwood pulp fibers may be birch, aspen or eucalyptus pulp fibers. In a still more particular example within these ranges, the softwood pulp fibers may be SSK pulp fibers and the hardwood pulp fibers may be birch, aspen or eucalyptus pulp fibers. Aspen, birch or eucalyptus pulp fibers may be desirable for their fineness, shortness, and softness, which contribute to enhancing opacity and softness of the fibrous web structure, and eucalyptus pulp may be particularly preferred for these characteristics.
In addition to the various wood pulp fibers, other cellulosic fibers such as cotton linters, rayon, lyocell, viscose and bagasse may be used. Other sources of cellulose in the form of fibers or materials capable of being spun into fibers include grasses and grain sources.
As shown in
As shown in
Further, the layered fibrous web structure 10b may comprise a third layer 22, as shown in
In yet another example, a fibrous web structure may include two outer layers consisting of 100% by weight filaments and an inner layer consisting of 100% by weight fibers.
In another example, instead of being layers of fibrous web structure 10c, the material forming layers 26, 28 and 30, may be in the form of layers wherein two or more of the layers may be combined to form a fibrous web structure. The layers may be bonded together, such as by thermal bonding and/or adhesive bonding, to form a multi-layer fibrous web structure.
Another example of a fibrous web structure is schematically illustrated in
In addition to layer 38, the fibrous web structure 10d may further comprise layer 40. Layer 40 may comprise a fibrous web structure comprising filaments 12, such as polypropylene filaments, and may be the same or different from the fibrous web structure of layer 38.
Two or more of the layers 36, 38 and 40 may be bonded together, such as by thermal bonding and/or adhesive bonding, to form a multi-layer fibrous web structure. After a bonding operation, especially a thermal bonding operation, it may be difficult to distinguish the layers of the fibrous web structure 10d and the fibrous web structure 10d may visually and/or physically be similar to a layered fibrous web structure in that one would have difficulty separating the once individual layers from each other. In one example, layer 36 may comprise a fibrous web structure that exhibits a basis weight of at least about 15 gsm and/or at least about 20 gsm and/or at least about 25 gsm and/or at least about 30 gsm up to about 120 gsm and/or 100 gsm and/or 80 gsm and/or 60 gsm and the layers 38 and 42, when present, independently and individually, may comprise fibrous web structures that exhibit basis weights of less than about 10 gsm and/or less than about 7 gsm and/or less than about 5 gsm and/or less than about 3 gsm and/or less than about 2.5 gsm, or from greater than 0 gsm to less than about 2.5 gsm, or from 0.5 gsm to 2.5 gsm.
Layers 38 and 40, when present, may help retain the fibers, in this case the wood pulp fibers 14, on and/or within the fibrous web structure of layer 36 thus reducing lint and/or dust (as compared to a single-layer fibrous web structure comprising the fibrous web structure of layer 36 without the layers 38 and 40) resulting from the wood pulp fibers 14 becoming free from the fibrous web structure of layer 36.
It should also be noted that the presence of polymer filaments in the core layer 36 together with the presence of polymer filaments of like chemistry in the two outer scrim layers, facilitate formation of a thermal bond 70 at which the polymer material in the three layers can be brought together under heat and compression so that they at least partially fuse, as may be observed in
As noted, it is believed that inclusion of meltspun, in one example meltspun and meltblown, polymer filaments in a co-formed fibrous web structure that is otherwise formed of cellulose or wood pulp fibers, as schematically illustrated in
However, adding polymer filaments to pulp fibers in a fibrous web structure of a given basis weight (as occurs with the addition of outer scrim layers of meltblown polymer filaments) may compromise the capacity of the structure to absorb aqueous liquids, for many types of polymers typically suitable and desirable for melt-spinning. This is due to the fact that, while pulp fibers are typically naturally hydrophilic, the preferred polymer filaments, such as polypropylene filaments, are typically naturally hydrophobic.
What remains to be decided, then, is an appropriate combination of weight percent pulp fiber content vs. filament content, with an appropriate allocation of meltspun/meltblown filament content to the scrim layers.
For the liquid absorbency performance desired for a wet wipe product it may be desired that the entire fibrous web structure be formed of at least 50 percent, more preferably at least 60 percent, and still more preferably at least 65 percent, by weight pulp fibers. Conversely, to achieve desired tensile strength and wet structural integrity, it may be desired that the entire fibrous web structure include at least 10 percent, at least 20 percent, or at least 25 percent, by weight polymer filaments. Thus, in some examples it may be preferred that the fibrous web structure be formed of 50 to 90 percent by weight pulp fibers, or 60 to 85 percent by weight pulp fibers, or even 65 to 85 percent by weight pulp fiber. Correspondingly, in such examples the fibrous web structure may comprise 10 to 50 percent by weight polymer filaments, or 15 to 40 percent by weight polymer filaments, or even 15 to 35 percent by weight polymer filaments, respectively.
Referring to
In an attempt to determine appropriate combinations of pulp content and allocation of filaments between core and scrim layers, however, seventeen variants of a three layer (scrim-core-scrim) fibrous nonwoven web structure such as schematically illustrated in
In a first assessment, wet cross direction and machine direction tensile strength of these seventeen variants was measured and recorded. A regression analysis was applied to the data and yielded a formula. The formula predicts that adding meltblown polypropylene filaments to the overall structure, enhances wet tensile strength. Surprisingly, however, the formula also predicts, generally, that increasing allocation of the added filaments from the core layer to the scrim layers by even a small amount appears to dramatically impact wet tensile strength of the fibrous nonwoven structure, with tensile strength increasing generally as more filaments are allocated from the core layer to the scrim layers—within the weight ratios of wood pulp fibers to polymer filaments contemplated. This effect is illustrated in
Since this effect was not predicted, the reasons for it are not currently well understood. Without intending to be bound by theory, it is hypothesized that higher numeric density of meltblown filaments (i.e., greater consolidation in the z-direction) may contribute to adding tensile strength to a structure formed of the filaments, while lower numeric density of meltblown filaments within the same space (such as when separated in the z-direction by interspersed fibers) may reduce tensile strength. Regardless, it was predicted that consumers of products made from the structure, such as baby wipes, would prefer comparatively greater tensile strength in the structure. This is due to the fact that comparatively greater tensile provides comparatively greater resistance to tearing and puncturing in dispensation and use, and the fact that tearing or puncturing during dispensation and/or use are undesirable failures for a baby wipe. This prediction is also supported by results of consumer research, which suggest that consumers tend to prefer comparatively more strength and tear resistance in a baby wipe.
In a second assessment, wet opacity of the seventeen variants was measured and recorded. Another regression analysis was applied to the data and yielded a formula. The formula predicted that opacity increases as basis weight of the fibrous web structure is increased; compare
Since the overall numbers of fibers and filaments present is generally not increased by a mere allocation of filaments from core to scrim layers, the reasons for this effect are not currently well understood. However, it was predicted that consumers of products made from the structure, such as baby wipes, would prefer comparatively greater opacity, since comparatively greater opacity equates with comparatively less translucency, making the wipe look more substantial and as if it better creates a physical barrier between the user's hand and soil (e.g. fecal matter) that the wipe is used to clean away from the baby's skin.
In another assessment, the seventeen variants were presented to a panel of human respondents, who were asked to evaluate the structure samples and rate them according to the extent to which they subjectively deemed them flexible. A subjective scoring system was used. Another regression analysis was applied to the data collected, and yielded a formula that is reflected in
Consumer preferences concerning flexibility are complex and not currently thoroughly understood. Without intending to be bound by theory, it is believed that some consumers may prefer a comparatively more flexible structure, perceiving it to be, for example, more soft and luxurious, while others may prefer a comparatively stiffer structure, perceiving it to be, for example, more robust and substantial.
In still another assessment, the seventeen variants were presented to the panel of human respondents, who were asked to evaluate the structure samples and rate them according to their perceptions of surface roughness. A subjective scoring system was used. Another regression analysis was applied to the data collected, and yielded a formula that is reflected in
Consumer preferences concerning surface roughness are also somewhat complex and not currently thoroughly understood. Without intending to be bound by theory, it is believed that some consumers may prefer a more rough-feeling structure (e.g., more like a paper towel), perceiving it to be, for example, more effective at sweeping, capturing and removing soil from skin, while others may prefer more smooth-feeling structure, perceiving it to be, for example, more gentle to skin and/or more soft and luxurious.
Although they provide some guidance concerning how to maximize particular properties such as tensile strength and opacity, the assessments described above do not appear to provide any certain guidance, prediction or expectation as to how to select a combination of weight percent pulp fiber content vs. meltblown filament content, and an allocation of meltblown filament content between the core layer and the scrim layers, that will be most pleasing to consumers of wet wipes such as baby wipes.
Samples of the seventeen variants that had been converted to wet wipes were presented to another panel of consumer respondents, who were asked to evaluate the wipes samples and rate them according to the extent to which they would prefer to purchase them as consumers. A subjective scoring system was used. Another regression analysis was applied to the data collected, and yielded a formula that, surprisingly, showed little correlation with the formulas for tensile strength and opacity. There was little correlation between the predicted most preferred higher tensile strength, the predicted most preferred higher opacity, and the most preferred consumer preference, for structures with varying allocations of meltblown polymer filaments to the scrim layers. Rather, as reflected by respective shaded bands 165-169 and 170-174 in
A model derived from the regression analysis enables a prediction of consumer preference from the ranges of the basis weights and proportions of pulp fibers of the samples tested. From the analysis, it is preferred that the Consumer Preference Indication for a fibrous nonwoven structure be greater than 0.0, more preferably 1.0 or more, still more preferably 1.75 or more, and still more preferably 2.25 or more, where Consumer preference Indication is calculated according to the following equation:
CPI=(BW×0.06232)−6.00192A−6.84371B−3.95686C+13.67992AB+7.12309BC+2,
Thus, as one example, according to the model described above and the description herein, a fibrous web structure having a basis weight of 60 gsm and the following composition will be a within the range of consumer preference indicated by CPI as set forth above:
From the values above, the example structure will have 65.0 percent by weight pulp fibers, 6.00 percent by weight meltblown polymer filaments in the two scrim layers together, and 29.0 percent by weight meltbown polymer filaments in the middle/core layer, and will have a CPI of 2.4071 according to the above model, indicating a consumer-preferred structure.
In contrast, if the above example is modified such that 3.00 gsm is additionally allocated from the core layer to each scrim layer (allocating a total of 9.60 gsm to the scrim layers together, or 4.80 gsm to each), the structure would have 16.0 percent by weight meltblown polymer filaments in the two scrim layers, and 19.0 percent by weight meltbown polymer filaments in the middle/core layer, and will have a CPI of about −0.1108, indicating a structure that is outside the consumer-preferred range in which the CPI is greater than 0.
It may be recognized that a web formed of meltblown polymer filaments to a basis weight of 4.8 gsm or less, by itself, is extremely thin and sheer, and barely tactilely perceptible when held in the hands. This illustrates the surprising sensitivity of consumer preference to allocation of meltblown filaments to the scrim layers, according to the model. It may be appreciated from the foregoing that consumer preferences are often elusive to prediction and that more than routine experimentation is necessary to discover them and then harmonize them with manufacturer preferences for features such as material strength, manufacturing cost and efficiency. The above-described formula for achieving a CPI greater than 0, more preferably 1, still more preferably 2, showed little correlation with the formulas that indicate maximization of properties such as tensile strength, opacity, surface roughness and flexibility with respect to choosing a combination of pulp fiber content, meltblown filament content and allocation of meltblown filaments between core and scrim layers.
Results of further consumer testing have suggested that extrapolation from the model above may yield ranges of consumer-preferred allocations of meltblown filaments for higher and lower proportionate pulp content structures than the variants made, tested and shown and plotted in the ternary plots of
Based on the foregoing, examples of a fibrous nonwoven structure are contemplated having a combination of the following features:
In hindsight of this research and analysis it appears that consumers will prefer a wet wipe cut from a fibrous web material having at least some of the total meltblown polymer fiber weight content allocated to scrim layers, but that that preference is very sensitive and falls off sharply when the allocation of meltblown filaments to the scrim layers strays above or below a relatively narrow band, as suggested in
The amount of meltblown polymer filaments allocated to the two scrim layers may be divided approximately equally, or may be divided unequally. For example, it may be desired that the two sides of the fibrous nonwoven structure have different feel or surface characteristics, for example, that one side have a more rough or higher-friction feel, and the other side have a more smooth or slick, lower-friction feel. To accomplish such difference, the scrim layer on one side may be imparted with a lower basis weight of, for example, from 0.1 gsm to 1.4 gsm, or to 1.0 gsm, or even to 0.6 gsm. Correspondingly, the scrim layer on the other side may be imparted with a higher basis weight of, for example, from 0.6 gsm to 3.0 gsm, or from 0.8 gsm to 2.8 gsm, or even from 1.0 gsm to 2.6 gsm. In order to provide the pulp fiber containment benefit of a scrim layer, however, as noted above, it may be desired that the basis weight of either scrim layer and preferably both scrim layers be at least 0.1 gsm, more preferably at least 0.2 gsm, or even more preferably at least 0.3 gsm. For example, for a fibrous nonwoven structure having a basis weight of, e.g., 60 gsm, this means that it may be desired that the weight percentage of either or preferably both scrim layers be at least 0.17%, or 0.34% combined.
The basis weight of the fibrous web structure, the overall weight percent pulp content vs. meltblown filament content, and the allocation of meltblown filaments between core layer(s) and scrim layers may be adjusted and regulated by design, adjustment and regulation of the speeds and/or feed rates to components that introduce the materials in the manufacturing line, including the components that separate and feed the pulp fibers and entrain them in airstream(s), the banks of filament spinnerets, the forming belt, etc.
The fibrous web structure and/or any product comprising such fibrous web structure may be subjected to any post-processing operations such as embossing operations, printing operations, tuft-generating operations, thermal bonding operations, ultrasonic bonding operations, perforating operations, surface treatment operations such as application of lotions, silicones and/or other materials, folding, and mixtures thereof.
Non-limiting examples of suitable polypropylenes for making the filaments are commercially available from Lyondell-Basell and Exxon-Mobil.
Any hydrophobic or non-hydrophilic materials within the fibrous web structure, such as polypropylene filaments, may be surface treated and/or melt treated with a hydrophilic modifier. Non-limiting examples of surface treating hydrophilic modifiers include surfactants, such as Triton X-100. Non-limiting examples of melt treating hydrophilic modifiers that are added to the melt, such as the polypropylene melt, prior to spinning filaments, include hydrophilic modifying melt additives such as VW351 and/or S-1416 commercially available from Polyvel, Inc. and Irgasurf commercially available from Ciba. The hydrophilic modifier may be associated with the hydrophobic or non-hydrophilic material at any suitable level known in the art. In one example, the hydrophilic modifier is associated with the hydrophobic or non-hydrophilic material at a level of less than about 20% and/or less than about 15% and/or less than about 10% and/or less than about 5% and/or less than about 3% to about 0% by dry weight of the hydrophobic or non-hydrophilic material.
The fibrous web structure may include optional additives, each, when present, at individual levels of from about 0% and/or from about 0.01% and/or from about 0.1% and/or from about 1% and/or from about 2% to about 95% and/or to about 80% and/or to about 50% and/or to about 30% and/or to about 20% by dry weight of the fibrous web structure. Non-limiting examples of optional additives include permanent wet strength agents, temporary wet strength agents, dry strength agents such as carboxymethylcellulose and/or starch, softening agents, lint reducing agents, opacity increasing agents, wetting agents, odor absorbing agents, perfumes, temperature indicating agents, color agents, dyes, osmotic materials, microbial growth detection agents, antibacterial agents and mixtures thereof.
In addition to wipes, the fibrous web structure described herein may be converted to a sanitary tissue product or household cleaning product such as bath tissue or paper towels. It may be convolutedly wound about a core to form a roll. It may be combined with one or more other fibrous web structures as a layer to form a multi-layer product. In one example, a co-formed fibrous web structure may be convolutedly wound about a core to form a roll of co-formed product. A roll product may also be coreless.
Wipe
The fibrous web structure, as described above, may be utilized to form a wipe. “Wipe” is a general term to describe a sheet of material, typically cut from a non-woven web material, adapted for cleaning hard surfaces, food, inanimate objects, toys and body parts. In particular, many currently available wipes (including baby wipes) are adapted for use in cleaning of the perianal area of the body after defecation. Other wipes may be available for cleaning the face or other body parts. Multiple wipes may be attached together by any suitable method to form a mitt.
The material from which a wipe is made should be strong enough to resist tearing during normal use, yet still provide softness to the user's skin, such as a child's tender skin. Additionally, the material should be at least capable of retaining its form for the duration of the user's cleansing experience.
Wipes may be generally of sufficient dimension to allow for convenient handling. Typically, the wipe may be cut and/or folded to such dimensions as part of the manufacturing process. In some instances, the wipe may be cut into individual sheets so as to provide separate wipes which are often stacked, folded and interleaved in consumer packaging. In other embodiments, the wipes may be in a web form where the web has been slit and folded to a predetermined width and provided with means (e.g., perforations) to allow individual wipes to be separated from the web by a user. Wipes sheets divided by perforations may be gathered on a roll (in the manner of conventional dry bathroom tissue or paper towels).
Suitably, an individual wipe may have a length between about 100 mm and about 250 mm and a width between about 140 mm and about 250 mm. In one embodiment, the wipe may be about 200 mm long and about 180 mm wide and/or about 180 mm long and about 180 mm wide and/or about 170 mm long and about 180 mm wide and/or about 160 mm long and about 175 mm wide. The material of the wipe may generally be soft and flexible, potentially having a structured surface to enhance its cleaning performance.
In one example the surface of the fibrous web structure may be substantially, macroscopically flat. In another example the surface of the fibrous web structure may optionally contain raised and/or lowered portions. These can be in the form of logos, indicia, trademarks, geometric patterns, images of the surfaces that the substrate made from the structure is intended to clean (i.e., infant's body, face, etc.). They may be randomly arranged on the surface of the fibrous web structure or be in a repetitive pattern of some form.
In another example the fibrous web structure may be biodegradable. For example the fibrous web structure may be made from a biodegradable material such as a polyesteramide, or high wet strength cellulose.
In one example, the fibrous web structure is used to form a pre-moistened wipe, such as a baby wipe. A plurality of the pre-moistened wipes may be stacked one on top of the other and may be contained in a container, such as a plastic tub or a film wrapper. In one example, the stack of pre-moistened wipes (typically about 40 to 80 wipes/stack) may exhibit a height of from about 50 to about 300 mm and/or from about 75 to about 125 mm. The pre-moistened wipes may comprise a liquid composition, such as a lotion. The pre-moistened wipes may be stored long term in a stack in a liquid impervious container or film pouch without all of the lotion draining from the top of the stack to the bottom of the stack.
In one example, the pre-moistened wipes are present in a stack of pre-moistened wipes that exhibits a height of from about 50 to about 300 mm and/or from about 75 to about 200 mm and/or from about 75 to about 125 mm.
Wipes of the present invention may be saturation loaded with a liquid composition to form a pre-moistened wipe. The loading may occur individually, or after the fibrous web structures or wipes are place in a stack, such as within a liquid impervious container or packet. In one example, the pre-moistened wipes may be saturation loaded with from about 1.5 g to about 6.0 g and/or from about 2.5 g to about 4.0 g of liquid composition per gram of fibrous nonwoven structure.
In one example, the liquid composition comprises water or another liquid solvent. Generally the liquid composition is of sufficiently low viscosity to impregnate the entire structure of the fibrous web structure. In another example, the liquid composition may be primarily present at the fibrous web structure surface and to a lesser extent in the inner structure of the fibrous web structure. In a further example, the liquid composition is releasably carried by the fibrous web structure, that is the liquid composition is carried on or in the fibrous web structure and is readily releasable from the fibrous web structure by applying some force to the fibrous web structure, for example by wiping a surface with the fibrous web structure.
Liquid compositions useful in the present invention may be, but are not necessarily limited to, oil-in-water emulsions. In one example, the liquid composition may be at least 80% and/or at least 85% and/or at least 90% and/or at least 95% by weight water.
When present on or in the fibrous web structure, the liquid composition may be present at a level of from about 10% to about 1000% of the basis weight of the fibrous web structure and/or from about 100% to about 700% of the basis weight of the fibrous web structure and/or from about 200% to about 500% and/or from about 200% to about 400% of the basis weight of the fibrous web structure.
The liquid composition may comprise an acid. Non-limiting examples of acids that may be included in the liquid composition are adipic acid, tartaric acid, citric acid, maleic acid, malic acid, succinic acid, glycolic acid, glutaric acid, malonic acid, salicylic acid, gluconic acid, polymeric acids, phosphoric acid, carbonic acid, fumaric acid and phthalic acid and mixtures thereof. Suitable polymeric acids can include homopolymers, copolymers and terpolymers, and may contain at least 30 mole % carboxylic acid groups. Specific examples of suitable polymeric acids useful herein include straight-chain poly(acrylic) acid and its copolymers, both ionic and nonionic, (e.g., maleic-acrylic, sulfonic-acrylic, and styrene-acrylic copolymers), those cross-linked polyacrylic acids having a molecular weight of less than about 250,000, preferably less than about 100,000 poly (α-hydroxy) acids, poly (methacrylic) acid, and naturally occurring polymeric acids such as carageenic acid, carboxy methyl cellulose, and alginic acid. In one example, the liquid composition comprises citric acid and/or citric acid derivatives.
The liquid composition may also contain salts of the acid or acids used to lower the pH, or another weak base to impart buffering properties to the fibrous web structure. The buffering response is due to the equilibrium which is set up between the free acid and its salt. This allows the fibrous web structure to maintain its overall pH despite encountering a relatively high amount of bodily waste as would be found post urination or defecation in a baby or adult. In one embodiment the acid salt would be sodium citrate. The amount of sodium citrate present in the lotion would be between 0.01 and 2.0%, alternatively 0.1 and 1.25%, or alternatively 0.2 and 0.7% of the lotion.
In one example, the liquid composition does not contain any preservative compounds.
In addition to the above ingredients, the liquid composition may comprise additional ingredients. Non-limiting examples of additional ingredients that may be included in the liquid composition include: skin conditioning agents (emollients, humectants) including waxes such as petrolatum, cholesterol and cholesterol derivatives; di- and tri-glycerides including sunflower oil and sesame oil; silicone oils such as dimethicone copolyol, caprylyl glycol; and acetoglycerides such as lanolin and its derivatives; emulsifiers; stabilizers; surfactants including anionic, amphoteric, cationic and nonionic surfactants; colorants; chelating agents including EDTA; sun screen agents; solubilizing agents; perfumes; opacifying agents; vitamins; viscosity modifiers such as xanthan gum; astringents; and external analgesics.
The liquid composition also may be formulated as described in any of, for example, U.S. Pat. Nos. 8,221,774 and 8,899,003; and U.S. patent application Ser. Nos. 11/717,928; 11/807,139; 12/105,654; 12/611,310; 12/771,391; 12/976,180; 13/220,982; 13/752,639; 14/330,171; 14/493,469; 14/602,692; and 62/057,297. An opacifying lotion formulation such as described in, for example, U.S. patent application Ser. No. 13/220,982, may be particularly useful for imparting opacity to, or enhancing opacity of, a fibrous web structure, particularly one with a lower basis weight, e.g., from 40-80 gsm, 40-70 gsm, or even 40-60 gsm, having the effect of interacting with the pulp fibers (including the relatively fine hardwood pulp fibers, when included) in a synergistic way to increase opacity of the structure and thereby enhance an appearance of robustness and barrier functionality of a wet wipe made from the fibrous nonwoven structure.
Wipes of the present invention may be placed in the interior of a container, which may be liquid impervious, such as a plastic tub or a sealable packet, for storage and eventual sale to the consumer. The wipes may be folded and stacked. The wipes of the present invention may be folded in any of various known folding patterns, such as C-folding, Z-folding and quarter-folding. Use of a Z-fold pattern may enable a folded stack of wipes to be interleaved with overlapping portions. Alternatively, the wipes may include a continuous strip of material which has perforations between each wipe and which may be arranged in a stack or wound into a roll for dispensing, one after the other, from a container, which may be liquid impervious.
The fibrous web structure or wipes of the present invention may further include prints, which may provide aesthetic appeal. Non-limiting examples of prints include figures, patterns, letters, pictures and combinations thereof.
Method for Making a Co-Formed Fibrous Web Structure
A non-limiting example of a method for making a co-formed fibrous web structure or a core layer thereof according to the present invention is schematically illustrated in
In another example schematically illustrated in
In a single-pass, direct forming process, a first meltblowing spinneret 46a may be used to spin a plurality of first meltblown filaments 12a that may be accumulated on a moving forming surface, such as the surface of a moving forming belt 48, to form a first scrim layer.
Downstream in the process, a configuration of co-forming equipment that may include co-form meltblowing spinneret 46b, a fiber spreader 44, and a mixing box such as co-form box 47, may be arranged and configured to deliver meltblown filaments and air-entrained pulp fibers, respectively to the mixing box such as co-form box 47. In the co-form box the filaments and fibers may be blended, entangled and entrained in an air stream to form a co-form stream 14a, which may then be directed to a moving forming surface (such as belt 48) to accumulate and form a co-form layer. In the example illustrated in
Further downstream in the process, a second meltblowing spinneret 46b may be used to spin a plurality of second meltblown filaments 12b that may be accumulated on a moving forming surface, such as the surface of moving forming belt 48, to form a second scrim layer. In the example illustrated in
The fiber spreader(s) 44 may be configured, and may comprise equipment including an educator, as described in, for example, U.S. Patent App. Ser. No. 62/094,087. The co-form box may be configured as described in, for example, U.S. Patent App. Ser. No. 62/094,089.
As reflected in
Referring to
As shown in
Following attenuation, the filaments may be air quenched with cooling air. The filaments forming the scrim layers (e.g., those from spinnerets 46a and 46c, as shown in the example of
Following quenching the filaments may be directed directly at a moving collecting and/or forming surface such as a forming belt 48 (e.g., as shown in
After the layers have been formed or deposited on the collecting surface, such as a belt 48, they may be calendered, for example, while the deposited layers of filaments and fibers are still on the collection device, or downstream thereof. In one example as shown in
The surface area occupied by the bonds 70 relative to the total surface area of the fibrous web structure may be expressed as bond area percentage, and is calculated as the total surface area occupied by the bonds 70, divided by the overall surface area of a side of the fibrous web structure 50 on which the bonds appear, ×100%. Bond area percentage on a fibrous web structure approximately reflects bonding area percentage of the raised (bonding) surfaces of the bonding protrusions on a calender bonding roller, divided by the total surface area of the circumscribing cylindrical shape of the portion of the calender bonding roller that contacts the web structure in the nip. Bond area percentage may be increased or decreased by altering the design of the pattern of bonding protrusions on the calendar bonding roller. Bonding protrusions having larger bonding surface area and/or more dense spacing impart comparatively greater bond area percentage to the web structure, while bonding protrusions having smaller bonding surface area and/or less dense spacing impart comparatively lesser bond area percentage to the web structure. Generally, it is believed that, within the practical operating ranges contemplated herein, greater bond area percentage may impart comparatively greater machine and cross direction tensile strength, but also comparatively greater stiffness, in the web structure. Conversely, comparatively lesser bond area percentage may impart comparatively less machine and cross direction tensile strength, and comparatively less stiffness (i.e., greater flexibility), in the web structure. For purposes of the present disclosure and of striking the best balance between strength and consumer preferences in the fibrous web structure, it may be desired that thermal bond area percentage be in a range of from 2% to 12%, more preferably from 3% to 10%, even more preferably from 4% to 8%, and still more preferably from 5% to 7%.
In addition, the fibrous web structure 50 may be subjected to other post-processing operations such as embossing, tuft-generating operations, moisture-imparting operations, and surface treating operations to form the finished fibrous web structure. One example of a surface treating operation that the fibrous web structure may be subjected to is the surface application of an elastomeric binder, such as ethylene vinyl acetate (EVA), latexes, and other elastomeric binders. Such an elastomeric binder may aid in reducing the lint created from the fibrous web structure during use by consumers. The elastomeric binder may be applied to one or more surfaces of the fibrous web structure in a pattern, especially a non-random, repeating pattern of microregions, or in a manner that covers or substantially covers the entire surface(s) of the fibrous web structure.
In one example, the fibrous web structure 50 and/or the finished fibrous web structure may be combined with one or more other fibrous web structures. For example, another fibrous web structure, such as a filament-containing fibrous web structure, such as a polypropylene filament fibrous web structure may be associated with a surface of the fibrous web structure 50 and/or the finished fibrous web structure. The polypropylene filament fibrous web structure may be formed by meltblowing polypropylene filaments (filaments that comprise a second polymer that may be the same or different from the polymer of the filaments in the fibrous web structure 50) onto a surface of the fibrous web structure 50 and/or finished fibrous web structure. In another example, the polypropylene filament fibrous web structure may be formed by meltblowing filaments comprising a second polymer that may be the same or different from the polymer of the filaments in the fibrous web structure 50 onto a collection device to form the polypropylene filament fibrous web structure. The polypropylene filament fibrous web structure may then be combined with the fibrous web structure 50 or the finished fibrous web structure to make a two-layer fibrous web structure—three-layer if the fibrous web structure 50 or the finished fibrous web structure is positioned between two layers of the polypropylene filament fibrous web structure like that shown in
In yet another example, the fibrous web structure 50 and/or finished fibrous web structure may be combined with a filament-containing fibrous web structure such that the filament-containing fibrous web structure, such as a polysaccharide filament fibrous web structure, such as a starch filament fibrous web structure, is positioned between two fibrous web structures 50 or two finished fibrous web structures like that shown in
In one example, the method for making a fibrous web structure comprises the step of combining a plurality of filaments and optionally, a plurality of fibers to form a fibrous web structure that exhibits the properties of the fibrous web structures described herein. In one example, the filaments comprise thermoplastic filaments. In one example, the filaments comprise polypropylene filaments. In still another example, the filaments comprise natural polymer filaments. The method may further comprise subjecting the fibrous web structure to one or more processing operations, such as calendaring the fibrous web structure. In yet another example, the method further comprises the step of depositing the filaments onto a patterned belt that creates a non-random, repeating pattern of micro regions.
In still another example, two layers of fibrous web structure 50 comprising a non-random, repeating pattern of microregions may be associated with one another such that protruding microregions, such as pillows, face inward into the two-layer fibrous web structure formed.
The process for making a fibrous web structure 50 may be close coupled (where the fibrous web structure is convolutedly wound into a roll prior to proceeding to a converting operation) or directly coupled (where the fibrous web structure is not convolutedly wound into a roll prior to proceeding to a converting operation) with a converting operation to emboss, print, deform, surface treat, thermal bond, cut, stack or other post-forming operation known to those in the art. For purposes of the present invention, direct coupling means that the fibrous web structure 50 can proceed directly into a converting operation rather than, for example, being convolutedly wound into a roll and then unwound to proceed through a converting operation.
In one example, the fibrous web structure is embossed, cut into sheets, and collected in stacks of fibrous web structures.
A process according the present disclosure may include preparing individual rolls and/or sheets and/or stacks of sheets of fibrous web structure and/or sanitary tissue product comprising such fibrous web structure(s) that are suitable for consumer use.
The following non-limiting examples of methods are contemplated within this description:
1. A method for manufacturing a fibrous web structure, comprising the steps of:
melt spinning first polymer filaments and directing the first polymer filaments to a moving belt, thereby forming a first scrim layer of polymer filaments on the belt;
downstream of the first scrim layer forming step, melt spinning second polymer filaments, blending the second polymer filaments with cellulose pulp fibers in a configuration of co-forming equipment, and directing the blend of second polymer filaments and cellulose pulp fibers at the belt and the first scrim layer to form a core layer overlying the first scrim layer;
downstream of the core layer forming step, melt spinning third polymer filaments and directing the third polymer filaments at the belt and the core layer, thereby forming a second scrim layer overlying the core layer;
conveying the first scrim layer, overlying core layer, and overlying second scrim layer into the nip between a pair of calender rollers, at least one of the rollers having thereon a pattern of bonding protrusions, the rollers having a source of heating energy supplied at the nip; and
compressing the layers in the nip and beneath the bonding protrusions to form a pattern of thermal bonds bonding the scrim layers to and thereby complete the fibrous web structure.
2. A method for manufacturing a fibrous web structure, comprising the steps of:
melt spinning first polymer filaments, blending the first polymer filaments with cellulose pulp fibers in a configuration of co-forming equipment, and directing the blend of first polymer filaments and cellulose pulp fibers at a first moving belt to form a core layer;
melt spinning second polymer filaments and directing the second polymer filaments toward the first moving belt or a second moving belt, the first moving belt or the second moving belt carrying the core layer, and directly forming a scrim layer of melt spun polymer filaments directly over the core layer, on one side of the core layer;
bringing a second scrim layer comprising third melt spun polymer filaments into facing contact with the core layer on another side of the core layer;
conveying the first scrim layer, core layer, and second scrim layer together into the nip between a pair of calender rollers, at least one of the calender rollers having thereon a pattern of bonding protrusions, with a source of heat energy supplied at the nip; and
compressing the layers in the nip and beneath the bonding protrusions to form a pattern of thermal bonds bonding the scrim layers to, and thereby complete, the fibrous web structure.
3. The method of example 2 wherein the second scrim layer is formed by melt spinning the third melt spun polymer filaments and directing the third melt spun polymer filaments toward the first moving belt, the second moving belt, or a third moving belt, with the first, second or third moving belt carrying the core layer and first scrim layer, and directly forming the second scrim layer directly over the core layer, on the other side of the core layer.
4. The method of either of examples 2 or 3 wherein the core layer, the first scrim layer and the second scrim layer are formed in a single pass.
5. The method of any of the preceding examples wherein the core layer forming step is repeated in successive configurations of co-forming equipment wherein the successive configurations increase the basis weight of the core layer.
6. The method of any of the preceding examples wherein the one or more of the first, second or third polymer melt spun filaments comprise meltblown filaments.
7. The method of example 5 wherein one or both of the first and second scrim layers comprise meltblown polymer filaments.
8. The method of any of the preceding examples wherein one or both of the second melt spun polymer filaments and third melt spun polymer filaments are mist quenched following spinning and prior to formation of the respective scrim layer(s).
9. The method of any of the preceding examples wherein the cellulose pulp fibers comprise softwood pulp fibers, preferably SSK pulp fibers.
10. The method of any of the preceding examples wherein the cellulose pulp fibers comprise hardwood pulp fibers, preferably aspen, birch or eucalyptus fibers.
11. The method of any of the preceding examples wherein any or all of the first, second and third meltspun polymer filaments comprise polyolefin, preferably polypropylene, and more preferably predominately polypropylene.
12. The method of any of the preceding examples wherein the bonding protrusions have a bonding area percentage of from 2% to 12%, more preferably from 3% to 10%, even more preferably from 4% to 8%, and still more preferably from 5% to 7%.
13. The method of any of the preceding examples further comprising the steps of dividing the fibrous nonwoven structure into sheets, gathering the sheets into a supply of wipes, and wetting the wipes with a liquid composition to form a supply of wet wipes.
14. The method of example 12 wherein the dividing step comprises cutting the fibrous nonwoven structure into individual sheets.
15. The method of either of examples 12 or 13 further comprising the step of folding and/or stacking the sheets to form a stack supply of wipes having a rectangular cuboid form.
16. The method of example 12 further comprising the step of gathering the divided sheets on a roll to form a roll supply of wipes having a cylindrical form.
The following example was manufactured on a pilot line in a two-pass, direct forming process as follows:
Co-Formed Core Layer
A 21%:27.5%47.5%:4% blend, respectively, of PH835 polypropylene (LyondellBasell, London, UK):Metocene MF650W polypropylene (LyondellBasell, London, UK):Metocene MF650X (LyondellBasell, London, UK):White 412951 (Ampacet Corporation, Tarrytown, N.Y.) whitening agent/opacifier is dry blended, to form a melt blend. The melt blend is heated to about 400° F.-405° F. through a melt extruder. A 15.5 inch wide Biax 12 row spinnerette with 192 nozzles per cross-direction inch, commercially available from Biax Fiberfilm Corporation, is utilized. 40 nozzles per cross-direction inch of the 192 nozzles have a 0.018 inch inside diameter melt outlet hole while the remaining nozzles are plugged, i.e., there is no opening in the nozzle. Approximately 0.18 grams per (open) hole per minute (ghm) of the melt blend is extruded from the open nozzles to form meltblown filaments from the melt blend.
Approximately 415 SCFM of compressed air is heated such that the air has a temperature of about 395° F. at the spinnerette. Approximately 420 g/minute of Golden Isle (from Georgia Pacific) 4825 semi-treated SSK pulp (Georgia-Pacific, Atlanta, Ga.) is defibrated through a hammermill to form SSK wood pulp fibers. Approximately 2100 SCFM Air at a temperature of about 80° F. and about 75% relative humidity (RH) is drawn into the hammermill. The pulp is conveyed as described in U.S. Pat. App. No. 62/170,176 using a motive air mass flow of approximately 1200 SCFM via two fiber spreaders. The solid additive spreaders turns the pulp fibers and distributes the pulp fibers in the cross-direction such that the pulp fibers are injected into the stream of meltblown filaments at a 45° angle through two 4 inch×15 inch cross-direction (CD) slots. The pulp conveying ductwork and geometry are as described in U.S. Pat. App. Ser. No. 62/170,169 and 62/170,172. A forming box surrounds the area where the meltblown filaments and pulp fibers are commingled. This forming box is designed to reduce the amount of air allowed to enter or escape from this commingling area. The forming box is as described in U.S. Pat. App. Ser. No. 62/170,179. A forming vacuum pulls air through a moving collection surface, such as a non-patterned forming belt or through-air-drying fabric, thus collecting and accumulating the commingled meltblown filaments and pulp fibers to form a fibrous structure batt. An example of such a fabric is Albany International Electrotech F541-28I. The forming vacuum level is adjusted to prevent excessive air from escaping from the forming box. The fibrous structure batt formed by this process comprises about 78% by dry fibrous structure weight of pulp and about 22% by dry fibrous structure weight of meltblown filaments. The line speed is adjusted (in the present example, to approximately 69 feet/min.) to accumulate the fiber/filament blend to reach the desired basis weight. The batt is then gathered on a storage roll.
First Scrim Layer
The dimensions and values disclosed herein are not to be understood as being strictly limited to the exact numerical values recited. Instead, unless otherwise specified, each such dimension is intended to mean both the recited value and a functionally equivalent range surrounding that value. For example, a dimension disclosed as “40 mm” is intended to mean “about 40 mm.”
All documents cited in the Background and Detailed Description are incorporated herein by reference to the extent not inconsistent with the specific disclosure herein; but the citation of any document is not to be construed as an admission that it is prior art with respect to the present invention. To the extent that any meaning or definition of a term in this document conflicts with any meaning or definition of the same term in a document incorporated by reference, the meaning or definition assigned to that term in this document shall govern.
While particular embodiments of the present invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the invention. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of this invention.
This application claims the benefit of U.S. Provisional Application No. 62/186,544, filed Jun. 30, 2015, the substance of which is incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4100324 | Anderson | Jul 1978 | A |
| 4355066 | Newman | Oct 1982 | A |
| 4370289 | Sorenson | Jan 1983 | A |
| 4436780 | Hotchkiss | Mar 1984 | A |
| 4604313 | McFarland et al. | Aug 1986 | A |
| 4623576 | Lloyd | Nov 1986 | A |
| 4675226 | Ott | Jun 1987 | A |
| 4774125 | McAmish | Sep 1988 | A |
| 4784892 | Storey | Nov 1988 | A |
| 4885202 | Lloyd | Dec 1989 | A |
| 4906513 | Kebbell | Mar 1990 | A |
| 4931201 | Julemont | Jun 1990 | A |
| 5204165 | Schortmann | Apr 1993 | A |
| 5316601 | Hebbard | May 1994 | A |
| 5350624 | Georger et al. | Sep 1994 | A |
| 5441550 | Hassenboehler, Jr. | Aug 1995 | A |
| 5455110 | Connor | Oct 1995 | A |
| 5683794 | Wadsworth | Nov 1997 | A |
| 5834385 | Blaney | Nov 1998 | A |
| 5914084 | Benson | Jun 1999 | A |
| 5948710 | Pomplum | Sep 1999 | A |
| 5962112 | Haynes | Oct 1999 | A |
| 6013223 | Schwarz | Jan 2000 | A |
| 6028018 | Amundson | Feb 2000 | A |
| 6183684 | Lu | Feb 2001 | B1 |
| 6194974 | Craig et al. | Feb 2001 | B1 |
| 6177370 | Skoog | Jun 2001 | B1 |
| 6361784 | Brennan et al. | Mar 2002 | B1 |
| 6488801 | Bodaghi | Dec 2002 | B1 |
| 6494974 | Riddell | Dec 2002 | B2 |
| 6589892 | Smith | Jul 2003 | B1 |
| 6861380 | Garnier | Mar 2005 | B2 |
| 6926931 | Qashou | Aug 2005 | B2 |
| 7278187 | Petersen | Oct 2007 | B2 |
| 7381299 | Shannon | Jun 2008 | B2 |
| 7425517 | Deka | Sep 2008 | B2 |
| 7645353 | Thomaschefsky | Jan 2010 | B2 |
| 7879191 | Dyer | Feb 2011 | B2 |
| 9408761 | Xu et al. | Aug 2016 | B2 |
| 9944047 | Burt et al. | Apr 2018 | B2 |
| 20030010091 | Tungare | Jan 2003 | A1 |
| 20030211802 | Keck | Nov 2003 | A1 |
| 20030224686 | Anderson | Dec 2003 | A1 |
| 20050130536 | Siebers | Jun 2005 | A1 |
| 20050136772 | Chen | Jun 2005 | A1 |
| 20050148261 | Close et al. | Jul 2005 | A1 |
| 20050148262 | Verona | Jul 2005 | A1 |
| 20050245159 | Chmeilewski | Nov 2005 | A1 |
| 20080248239 | Pomeroy | Oct 2008 | A1 |
| 20090023839 | Barnholtz | Jan 2009 | A1 |
| 20090084513 | Barnholtz et al. | Apr 2009 | A1 |
| 20090151748 | Ridenhour | Jun 2009 | A1 |
| 20100048082 | Topolkaroev | Feb 2010 | A1 |
| 20110045261 | Sellars | Feb 2011 | A1 |
| 20110104970 | Barnholtz et al. | May 2011 | A1 |
| 20110244199 | Brennan | Oct 2011 | A1 |
| 20120177888 | Escafere et al. | Jul 2012 | A1 |
| 20140039434 | Xu et al. | Feb 2014 | A1 |
| 20150086760 | Castillo | Mar 2015 | A1 |
| 20150322601 | Satpal | Nov 2015 | A1 |
| 20170000695 | Castillo et al. | Jan 2017 | A1 |
| 20170002486 | Castillo et al. | Jan 2017 | A1 |
| 20180002848 | Burt et al. | Jan 2018 | A1 |
| Number | Date | Country |
|---|---|---|
| 1 156 147 | Nov 2001 | EP |
| 2 456 585 | Jul 2013 | EP |
| 4641340 | Mar 2011 | JP |
| Entry |
|---|
| PCT International Search Report dated Sep. 28, 2016 (12 pages). |
| U.S. Appl. No. 115/197,842, filed Jun. 30, 2016, Castillo et al. |
| U.S. Appl. No. 15/197,878, filed Jun. 30, 2016, Castillo et al. |
| U.S. Appl. No. 15/197,895, filed Jun. 30, 2016, Burt et al. |
| All Office Actions, U.S. Appl. No. 15/197,842. |
| All Office Actions, U.S. Appl. No. 15/197,878. |
| All Office Actions, U.S. Appl. No. 15/197,895. |
| Number | Date | Country | |
|---|---|---|---|
| 20170022643 A1 | Jan 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62186544 | Jun 2015 | US |