Patent Application
20160228851
N/A
The disclosure relates generally to metal oxide catalysts that are highly dispersed in a two-dimensional form on a silica support, as well as methods of making and using such catalysts.
Supported metal oxides are an important class of heterogeneous catalysts for a variety of chemical applications, including for use in biodiesel production, destructive adsorption of chlorocarbons and chemical warfare agents, and in natural gas upgrading processes such as alkane oxidation, olefin metathesis, and oxidative propane dehydrogenation (ODHP; see
Structurally, supported metal oxides include one or more metal oxide species loaded onto the surface of an inert support material, whereby the metal oxide species is bonded to the support material. Silica (SiO2), given its abundance and low cost, has traditionally been an important inert support material for such catalysts. Examples of commonly used metal oxides include group 3 metal oxides, such as aluminium oxide; group 4 metal oxides, such as titanium oxide; group 5 metal oxides, such as vanadium oxide, niobium oxide, and tantalum oxide; group 6 metal oxides, such as chromium oxide, molybdenum oxide, and tungsten oxide; and group 7 metal oxides, such as rhenium oxide.
At low metal oxide loadings (i.e, at loading levels insufficient to form a complete metal oxide monolayer on the support surface), the metal oxide species bonded to the support material surface are two-dimensional (typically monomeric, but in some case, oligomeric) species that are dispersed throughout the support material surface. As illustrated in
At sub-monolayer loadings, increased metal oxide loading generally results in increased dispersion (i.e., greater surface density) of the metal within the metal oxide catalyst. This increased dispersion generally increases the efficiency of the catalyst, because more catalytic sites are present within a given surface area of the support. However, at higher loading levels, metal oxide species in the form of three-dimensional nanoparticles begin to form on the support surface. As shown in
For example, referring now to
Metal oxides on silica, however, have only been able to form dispersed species without nanoparticle formation at very low metal loadings, as compared to other commonly used support materials. Specifically, the highest reported value for dispersion of vanadium on silica is only about 3 vanadium-atoms/nm2, while on other support materials (e.g., Al2O3, TiO2, and ZrO2), dispersed vanadium can exist at surface densities as high as 9 vanadium-atoms/nm2. Similarly, the highest reported value for dispersion of niobium on silica is only 1.1 niobium-atoms/nm2, and the highest reported value for dispersion of tantalum on silica is only 0.8 tantalum-atoms/nm2. These relatively low maximum dispersion densities using silica as a catalytic support have been attributed to the low reactivity of the surface hydroxyls of silica.
Accordingly, there is a need in the art for methods of increasing the low maximum dispersion thresholds for metal oxide catalysts supported on silica surfaces, and for substantially nanoparticle-free catalysts comprising highly dispersed metal oxides on silica supports.
As a result of the surprising discovery that sodium ion in low concentrations can be used to enhance dispersion of metal oxide catalysts on silica support surfaces, the inventors have developed improved metal oxide catalysts for use in a variety of processes, as well as methods of producing and using such catalysts.
Accordingly, in a first aspect, the disclosure encompasses a heterogeneous catalyst that includes one or more two-dimensional metal oxide species highly dispersed on the surface of a silica support that further comprises ions of one or more alkali metals, wherein the metal oxide is an oxide of a group 3, group 4, group 5, group 6 or group 7 metal, and wherein the catalyst is substantially free of metal oxide nanoparticles.
By “highly dispersed,” we mean that the one or more two-dimensional metal oxide species occur on the surface of the silica support at a dispersion density that is higher than the maximum dispersion density previously known for a specific metal oxide on the surface of a silica support. By “substantially free of nanoparticles,” we mean that any nanoparticles present are not detectable using conventional means of detection, including by Raman spectroscopy or UV-vis spectroscopy.
The enhanced dispersion of 2D metal oxides via sodium promotion is not exclusive to amorphous silica, but also includes application to mesoporous silica. Mesoporous silica is crystalline in structure and contains ordered pore structure. Exemplary mesoporous silica for use in the invention include SBA-15 and MCM-41 types.
In some embodiments, the mole ratio of the alkali metal ions present to the metal atoms of the metal oxide present is less than 0.25/1.
In some embodiments, the one or more two-dimensional metal oxide species are monomeric species.
In some embodiments, the one or more two-dimensional metal oxide species exhibit tetrahedral geometry around the metal atoms.
In some embodiments, the metal oxide is an oxide of a group 5, group 6 or group 7 metal. In some such embodiments, the metal oxide is an oxide of a group 5 or group 6 metal. In some such embodiments, the metal oxide is an oxide of a group 5 metal.
In some embodiments, the metal oxide is vanadium oxide, niobium oxide, tantalum oxide, chromium oxide, molybdenum oxide, tungsten oxide, rhenium oxide, titanium oxide, or mixtures thereof. In some such embodiments, the metal oxide is vanadium oxide, niobium oxide, tantalum oxide, titanium oxide; or mixtures thereof. If vanadium oxide is the metal oxide, it may optionally be dispersed on the surface of the silica support in the range of 3.2-10 V-atoms/nm2; 3.5-10 V-atoms/nm2; 4-10 V-atoms/nm2; 5-10 V-atoms/nm2; 6-10 V-atoms/nm2; 3.2-9 V-atoms/nm2; 3.5-9 V-atoms/nm2; 4-9 V-atoms/nm2; 5-9 V-atoms/nm2; or 6-9 V-atoms/nm2. If niobium oxide is selected, it may optionally be dispersed on the surface of the silica support in the range of 1.2-6 Nb-atoms/nm2; 1.5-6 Nb-atoms/nm2; 2-6 Nb-atoms/nm2; 1.2-5 Nb-atoms/nm2; 1.5-5 Nb-atoms/nm2; 2-5 Nb-atoms/nm2; 1.2-4 Nb-atoms/nm2; 1.5-4 Nb-atoms/nm2; 2-4 Nb-atoms/nm2; 1.2-3 Nb-atoms/nm2; 1.5-3 Nb-atoms/nm2; or 2-4 Nb-atoms/nm2. If tantalum oxide is selected, it may optionally be dispersed on the surface of the silica support in the range of 1-6 Ta-atoms/nm2; 1-5 Ta-atoms/nm2; 2-6 Ta-atoms/nm2; or 2-5 Ta-atoms/nm2.
In some embodiments, the ions of one or more alkali metals are sodium ions. In certain embodiments, the sodium ions are present in the silica support at a concentration of about 0.15-1.4 Na− ions/nm2, preferably 0.3-1.0 Na− ions/nm2, more preferably 0.4-0.8 Na− ions/nm2, or, most preferably, about 0.6 Na− ions/nm2.
In some embodiments, the silica support further comprises aluminum ions. In some such embodiments, the aluminum ions are optionally present in the silica support at a concentration of less than 1000 ppm. In some embodiments, the silica support does not comprise aluminum ions.
In a second aspect, the disclosure encompasses a method of making a desired chemical product. The method includes the step of contacting a liquid or gaseous reactant with the heterogeneous catalyst as described above, whereby the desired chemical product is formed by a process catalyzed by the heterogeneous catalyst.
In some embodiments, the liquid or gaseous reactant is an alkane, the process catalyzed by the heterogeneous catalyst is oxidative dehydrogenation, and the desired chemical product is an olefin. In some such embodiments, the metal oxide in the heterogeneous catalyst is selected from the group consisting of vanadium oxide, chromium oxide, molybdenum oxide, aluminum oxide, tantalum oxide, nobium oxide, titanium oxide, rhenium oxide, and mixtures thereof. In certain preferred embodiments, the metal oxide in the heterogeneous catalyst is vanadium oxide.
In some embodiments, the liquid or gaseous reactant is an alkane, the process catalyzed by the heterogeneous catalyst is non-oxidative dehydrogenation, and the desired chemical product is an olefin. In some such embodiments, the metal oxide in the heterogeneous catalyst is selected from the group consisting of vanadium oxide, chromium oxide, molybdenum oxide, aluminum oxide, tantalum oxide, nobium oxide, titanium oxide, rhenium oxide, and mixtures thereof. In certain embodiments, the metal oxide in the heterogeneous catalyst is chromium oxide, molybdenum oxide, vanadium oxide, or mixtures thereof.
In some embodiments, the liquid or gaseous reactant is an alkane, the process catalyzed by the heterogeneous catalyst is alkane oxidation, and the desired chemical product is an oxygenate. In some such embodiments, the metal oxide in the heterogeneous catalyst is selected from the group consisting of vanadium oxide, chromium oxide, molybdenum oxide, aluminum oxide, tantalum oxide, nobium oxide, titanium oxide, rhenium oxide, and mixtures thereof. In certain preferred embodiments, the metal oxide in the heterogeneous catalyst is molybdenum oxide.
In some embodiments, the liquid or gaseous reactant comprises one or more olefins, the process catalyzed by the heterogeneous catalyst is olefin metathesis, and the desired chemical product comprises one or more olefins that are different than the olefins of which the liquid or gaseous reactant is comprised. In some such embodiments, the metal oxide in the heterogeneous catalyst is selected from the group consisting of vanadium oxide, chromium oxide, molybdenum oxide, aluminum oxide, tantalum oxide, nobium oxide, titanium oxide, rhenium oxide, and mixtures thereof. In certain preferred embodiments, the metal oxide in the heterogeneous catalyst is tungsten oxide, molybdenum oxide, rhenium oxide, or mixtures thereof.
In some embodiments, the liquid or gaseous reactant is a chlorocarbon, the process catalyzed by the heterogeneous catalyst is chlorocarbon degradation, and the desired chemical product comprise products of chlorocarbon degradation. In some such embodiments, the metal oxide in the heterogeneous catalyst is selected from the group consisting of vanadium oxide, chromium oxide, molybdenum oxide, aluminum oxide, tantalum oxide, nobium oxide, titanium oxide, rhenium oxide, and mixtures thereof. In certain preferred embodiments, the metal oxide in the heterogeneous catalyst is niobium oxide.
In some embodiments, the liquid or gaseous reactant is glycerol, the process catalyzed by the heterogeneous catalyst is glycerol conversion, and the desired chemical product is acrolein. In some such embodiments, the metal oxide in the heterogeneous catalyst is selected from the group consisting of vanadium oxide, chromium oxide, molybdenum oxide, aluminum oxide, tantalum oxide, nobium oxide, titanium oxide, rhenium oxide, and mixtures thereof. In certain preferred embodiments, the metal oxide is niobium oxide, tungsten oxide, or mixtures thereof.
In a third aspect, the disclosure encompasses a method of making a heterogeneous catalyst including one or more two-dimensional metal oxide species highly dispersed on the surface of a silica support. The method includes the steps of (a) contacting a silica support with a solution containing one or more alkali metal ions, resulting in a silica support having an alkali metal promoter; and (b) contacting the silica support having an alkali metal promoter with a composition containing one or more metal oxides or metal oxide precursors, wherein the metal oxide is an oxide of a group 3, group 4, group 5, group 6 or group 7 metal. As a result of performing these steps, one or more two-dimensional metal oxide species are highly dispersed on the surface of the silica support.
In some embodiments, the mole ratio of the alkali metal ions in step (a) to the metal atoms of the metal oxide in step (b) is less than 0.25/1.
In some embodiments, the metal oxide is an oxide of a group 5, group 6 or group 7 metal. In some such embodiments, the metal oxide is an oxide of a group 5 or group 6 metal. In some such embodiments, the metal oxide is an oxide of a group 5 metal.
In some embodiments, the metal oxide is vanadium oxide, niobium oxide, tantalum oxide, chromium oxide, molybdenum oxide, tungsten oxide, rhenium oxide, titanium oxide, or mixtures thereof. In some such embodiments, the metal oxide is vanadium oxide, niobium oxide, tantalum oxide, titanium oxide, or mixtures thereof.
In some embodiments, the one or more alkali metal ions are potassium ions, sodium ions, rubidium ions, or combinations thereof. In some such embodiments, the one or more alkali metal ions are sodium ions. In some embodiments, the ions of one or more alkali metals are sodium ions. In certain embodiments, the sodium ions are present in the silica support at a concentration of about 0.15-1.4 Na− ions/nm2, preferably 0.3-1.0 Na− ions/nm2, more preferably 0.4-0.8 Na− ions/nm3, or, most preferably, about 0.6 Na− ions/nm2.
In some embodiments, the solution containing the one or more alkali metal ions also includes aluminum ions, which results in a silica support having an alkali metal promoter that also includes aluminum ions. In some such embodiments, the aluminum ions are present in the silica support having an alkali metal promoter at a concentration of less than 1000 ppm.
In some embodiments, the solution containing the one or more alkali metal ions does not include aluminum ions.
In some embodiments, either or both of the contacting steps further include calcining the resulting composition.
In some embodiments wherein metal oxide precursors are used, the metal oxide precursors may optionally be one or more metal alkoxides. In some such embodiments, the metal alkoxides are metal isopropoxides.
Further objects, features and advantages of the invention will be apparent from the following detailed description when taken in conjunction with the accompanying drawings.
The disclosure will be better understood and features, aspects and advantages other than those set forth above will become apparent when consideration is given to the following detailed description thereof. Such detailed description makes reference to the following drawings.
While the invention is susceptible to various modifications and alternative forms, specific embodiments thereof have been shown by way of example in the drawings and are herein described in detail. It should be understood, however, that the description herein of specific embodiments is not intended to limit the invention to the particular forms disclosed, but on the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the appended claims.
Before the present materials and methods are described, it is understood that this invention is not limited to the particular methodology, protocols, materials, and reagents described, as these may vary. It is also to be understood that the terminology used in this disclosure is for the purpose of describing particular embodiments only, and is not intended to limit the scope of the present invention, which will be limited only by the language of the appended claims.
As used in this disclosure and in the appended claims, the singular forms “a”, “an”, and “the” include plural reference unless the context clearly dictates otherwise. The terms “a” (or “an”). “one or more” and “at least one” can be used interchangeably. The terms “comprising”. “including”, and “having” can also be used interchangeably.
Unless defined otherwise, all technical and scientific terms used in this disclosure have the same meanings as commonly understood by one of ordinary skill in the art to which this disclosure belongs. All publications and patents specifically mentioned in this disclosure are incorporated by reference for all purposes, including for describing and disclosing the chemicals, instruments, statistical analysis and methodologies which are reported in the publications which might be used in connection with the disclosed methods and devices. All references cited in this disclosure are to be taken as indicative of the level of skill in the art.
This disclosure is based on the inventors' surprising discovery that the use of a sodium ion promoter (and optionally, an aluminum ion co-promoter) on a silica (SiO2) support facilitates the loading of highly dispersed two-dimensional metal oxide species onto the surface of the silica support, without the formation of undesirable nanoparticles. Specifically, we demonstrate in the Examples below that catalysts comprising Na+ promoted silica are capable of exhibiting metal oxide dispersion densities greater than the previously reported maximum dispersion densities for several different metal oxides, including vanadium oxide, niobium oxide, tantalum oxide, and titanium oxide. Given the data presented herein, similarly increased dispersion on Na+ promoted silica would be expected for other group 3, group 4, group 6, and group 7 metal oxides. The increased dispersion of the two-dimensional metal oxide species on the silica support results in a catalyst that can more efficiently catalyze one of the reactions of interest, because there are more active sites present in a given support surface area.
There are a number chemical processes for which the improved catalysts could be used. Examples of reactions of interest include, without limitation: (1) oxidative dehydrogenation of alkanes to olefins using, for example, supported V-oxides; (2) non-oxidative dehydrogenation of alkanes to olefins using, for example, supported Cr-, Mo-, V-, and/or Zn-oxides; (3) alkane oxidation to oxygenates, using, for example, supported Mo- and/or Fe-oxides; (4) olefin metathesis using, for example, supported W-, Mo-, and/or Re-oxides; (5) destruction of chlorocarbons and warfare agents using, for example, supported Nb-oxides; (6) glycerol conversion (to acrolein) using, for example, supported Nb- and/or W-oxides; (7) alkane metathesis using, for example, supported Ta-oxides; (8) ethanol dehydrogenation using, for example, supported Nb-oxides; (9) hydrotreating (a refinery process of reducing sulfur, nitrogen, and/or aromatics content) using, for example, supported Mo-oxides; and (10) partial oxidation using, for example, supported Mo-oxides.
The disclosed catalysts are not limited to the use of a single metal oxide, and encompass supported ternary metal systems as well. Non-limiting examples include the V/Ti/SiO2 or V/Ta/SiO2 systems commonly used to catalyze dehydrogenation of alkanes.
The following Examples are offered for illustrative purposes only, and are not intended to limit the scope of the invention in any way. Indeed, various modifications of the invention in addition to those shown and described herein will become apparent to those skilled in the art from the foregoing description and the following Examples and fall within the scope of the appended claims.
Promoted SiO2 was synthesized using incipient wetness impregnation and subsequent calcination, using Na(NO3) and Al(NO3)3 as metal precursor solutions. Appropriate amounts of Na(NO3) and Al(NO3)3 solutions, enough to support 0.40 wt % Na+ and 0.09 wt % Al3+ on the SiO2, were diluted in deionized water to equal the pore volume of the SiO2 support. Specifically, the metal precursor solution was prepared using 0.35 mL of 1M NaNO3, 0.33 mL of 0.2M Al(NO3)3, and 1.93 mL deionized H2O per 2 g of SiO2, culminating in 0.40 wt % Na+ and 0.09 wt % Al3+ in the final promoted-SiO2 sample. This solution was then dripped onto the SiO2, using a mortar and pestle to ensure proper contact between metal precursor solution and the oxide support. The resulting composition was then placed into a calcination furnace and heated to 700° C., ramping 1.5° C./min under flowing air, and holding at 700° C. for 4 hours, also under flowing air.
Vanadium oxide supported catalysts were made from the resulting Na-promoted SiO2 by a second incipient wetness impregnation and subsequent second calcination. Specifically, six different precursor solutions comprising the vanadium oxide precursor vanadium oxytriisopropoxide and isopropyl alcohol were prepared, using vanadium oxide precursor concentrations calculated to result in a wt % V on the SiO2 support of 1.8, 4.3, 6.3, 7.2, 11.1 and 12.3, respectively. These concentrations would result in a vanadium surface density of 1.3, 4.1, 7.2, 8.9, 13.4, and 15.4 Vatoms/nm2, respectively. Surface density is calculated using the following formula:
Surface density, (M)/nm2
Each of the precursor solutions were dripped onto the Na+-promoted SiO2, using a mortar and pestle to ensure proper contact between metal precursor solution and the oxide support. The resulting vanadium oxide catalyst compositions were then placed into a calcination furnace and heated to 700° C., ramping 1.5° C./min under flowing air, and holding at 700° C. for 3 hours, also under flowing air. The calcined supported vanadium oxide catalysts were then tested for enhanced metal oxide dispersion and catalytic activity.
Enhanced Dispersion of Vanadium Oxide Catalysts Supported on Na+-Promoted SiO2.
The enhanced dispersion of vanadium oxide on Na+-promoted SiO2 was demonstrated through Raman spectroscopy and UV-vis spectroscopy.
Analysis of UV-visible spectroscopy agrees with nanoparticle assignments of supported vanadium-oxide on promoted silica. The specific UV-vis edge energy shift of each supported vanadium-oxide catalyst is shown in Table 1. UV-vis edge energies of catalysts below monolayer vanadium-oxide coverage (<8.9V/nm2) show edge energies of ˜3.6 eV, corresponding to the support being entirely comprised of tetrahedral VO4 sites. Only the highest loadings of vanadium-oxide (13.4 and 15.4 V/nm2), meanwhile, show edge energies <3.0 eV, corresponding to the existence of nanoparticle V2O5 found on the SiO2 surface.
Catalytic Activity of Vanadium Oxide Catalyst Supported on Na+-Promoted SiO2.
The activity of the catalysts was assessed in an oxidative propane dehydrogenation reaction (ODHP; see
Notably, we have demonstrated enhanced dispersion of vanadium oxide on SiO2 resulting from the introduction of as little as 160 ppm Na+ to the silica support.
Using similar procedures to those described in Example 1, we have demonstrated enhanced dispersion on silica surfaces comprising an Na+ promoter using metal oxides other than vanadium oxide, including niobium oxide, tantalum oxide, and titanium oxide. For each of these metal oxides, the alkoxide precursor was used to make the catalyst (see
As a prophetic extension of this Example, enhanced dispersion of W-oxide and Mo-oxide on SiO2 will be demonstrated. Dispersion of these oxides using Mo and W-alkoxide precursors (see
Further testing is planned to further demonstrate the catalytic activity of the disclosed catalysts. As a non-limiting example, an olefin metathesis reaction may be catalyzed, such as propylene metathesis to ethylene and butylene. Alternatively, the reverse reaction, metathesis of butylene and ethylene to form two equivalents of propylene, may be catalyzed.
Further extensions may also include developing “ternary catalysts” (multiple-supported metal oxide catalysts) for ODHP. In a non-limiting example, such ternary catalysts may include one or more group 5 metals, e.g., V/Nb/promoted-SiO2.
The catalytic performance of supported metal oxides is often controlled by their two- or three-dimensional dispersion. Silica, one of the popular inert supports, triggers the undesired formation of three-dimensional nanoparticles at significantly lower loadings than other conventional supports like Al2O3, TiO2, Nb2O5, or ZrO2. This observation has been ascribed to the lower reactivity of surface SiOH groups toward the precursor, compared to other metal hydroxyl groups on different supports. In this contribution, we show that by promoting amorphous silica with low amounts of sodium, the surface density of two-dimensional metal oxide species can be significantly enhanced to the same level as all other oxide supports previously reported in the literature. This effect is demonstrated for the case of supported vanadia using a variety of spectroscopic techniques (i.e., Raman, diffuse reflectance UV-vis, and 51V-MAS NMR), as well as a catalytic activity study for the oxidative dehydrogenation of propane (ODHP), a structure-sensitive probe reaction. The propane consumption rate was found to increase linearly with the vanadium surface density while the propylene selectivity was not affected until a monolayer coverage of ca. 9 vanadia per nm2 was surpassed. (
Supported metal oxides are an important class of catalytic materials, used for a variety of important reactions such as alkane oxidation and olefin metathesis, among others. (1,2) The surface structure of such materials is known to control the catalytic performance. (3) Previous work in this area classified supported metal oxide structures as being above or below “monolayer coverage” defined as the maximum amount of twodimensional (2D) metal oxide species that can exist on a support oxide surface before triggering the formation of threedimensional (3D) nanoparticles. (4) Metal oxides below the monolayer exist solely as 2D “dispersed” surface structures and may be present as isolated monomers and/or oligo- or polymeric species, featuring one or more bridging oxygen atoms between the metal centers (M-O-M).
The oxidative dehydrogenation of propane (ODHP) is a potential alternative for propane dehydrogenation (so-called “on-purpose” propylene production), due to its favorable thermodynamics and negligible coke formation. Yet, the low propylene selectivity restricts its industrial implementation, despite the potential for significant energy savings. Though varieties of catalysts have been explored for ODHP, supported vanadia catalysts have shown some of the most interesting results. While the desired dehydrogenation pathway is suggested to be structure-independent, the competing side-reactions, i.e. propylene (and to a lesser extent, propane) overoxidation to COx, becomes more favored over V2O5 nanoparticles. (15,35) Thus, in order to improve the propylene productivity, catalysts must maximize two-dimensional dispersion.
It is well established that the oxide support influences the catalytic activity, mainly due to intrinsic acid/base properties of the support. (35) Silica (SiO2) is one of the most utilized oxide supports, due to its low cost and inert properties. However, up until now, SiO2 only allows a low surface density of supported metal oxides to exist as 2D species compared to all other oxide supports, despite its high surface area. This is well documented in the case of supported vanadia (
In this study, we show that the optimal addition of sodium as a promoter can increase the level of dispersion of group V metal oxides on SiO2 to be equivalent to that of other oxide support materials. This is demonstrated by a variety of characterization techniques, including Raman spectroscopy, diffuse reflectance UV-vis, and 51V MAS NMR. Further, ODHP is utilized as a structure-sensitive probe reaction: increasing the 2D vanadia dispersion serves to linearly increase space-time yield while maintaining the same selectivity to propylene.
Catalyst Preparation.
Impure silica (im-SiO2) was used as provided by the supplier (Sigma-Aldrich; 165 m2 g−1; batch #MKBN2949 V) without any further treatment. Na+ promoted SiO2 (pro-SiO2) was prepared by incipient wetness impregnation of conventional amorphous silica (Aerosil200 from Evonik; 200 m2 g−1) by a sodium nitrate solution, followed by calcination under air. An appropriate amount of 1 M Na(NO3) solution was diluted in deionized H2O to equal the pore volume of the Aerosil200 (1.3 mL g−1). This sample was then calcined under air, ramping 1.5° C. min-1 to 700° C., and holding at 700° C. for 4 h. The optimal pro-SiO2 material contains 0.40 wt % Na+ and shows a surface area of 180±5 m2 g−1. Nitrate salts of alternative alkali or alkaline earth metals (Li-, K-, Rb-, Mg-nitrate) were used to attempt to substitute Na+. Their methods of preparation are identical to that described for pro-SiO2. The order of impregnation, whether it be V/alkali/support or alkali/V/support, and the consequences it may have on catalytic activity were previously studied. This work suggested stronger alkali-support interaction with an initial alkali impregnation in case of alumina support. This resulted in more active vanadia species but did not address the influence on the metal oxide dispersion.
All supported metal oxide catalysts were synthesized via incipient wetness impregnation, following previously reported synthesis procedures for analogous materials. Prior to impregnation, im-SiO2, pro-SiO2, or conventional-SiO2 was dried under static conditions overnight at 120° C. Impregnation was performed inside a glovebox under a dry N2 atmosphere. Metal alkoxide solutions, i.e., vanadium oxytriisopropoxide (VTI; Sigma-Aldrich), niobium ethoxide (Sigma-Aldrich, 99.95%), and tantalum ethoxide (Sigma-Aldrich, 99.98%), were used as the metal oxide precursors. Those alkoxide precursors were previously shown to be superior to other precursors like sodium metavanadate and the like. The alkoxides were diluted with dry isopropanol (Sigma-Aldrich, 99.5%) or dry ethanol (Sigma-Aldrich, 99.5%) prior to impregnation to form a solution equal in volume to the pore volume of the support. The ratio of metal-to-isopropanol was altered to create a variety of metal oxide loadings. Impregnated samples were vacuum-dried inside the glovebox and transferred to a calcination oven where they were dried under a flow of N2 at 120° C. for 3 h, ramped to 550° C. at 1° C. min-1 under dry air, and calcined at 550° C. for 3 h. Catalyst Characterization. Raman measurements were carried out with a Renishaw InVia Raman Spectrometer with a 785 nm excitation laser. All measurements used a 1200 L mm−1 grating and were taken with a range of 250-1200 cm−1 and a dispersion of 1.36565 cm−1 pixel−1. The experiments were performed in a high-temperature Linkam CCR1000 cell. Samples were dehydrated by heating to 500° C. (10° C. min−1 ramp) under 16 and 4 mL min−1 He and O2, respectively, for 1 h before measurement. Solid-state 51V MAS NMR spectra were acquired on an Avance NMR spectrometer (Bruker, Karlsruhe, Germany) operating at a 1H Larmor frequency of 400 MHz. The samples were spun around the magic angle with a rate of 18 kHz at room temperature using a double resonance 3.2 mm probe (containing ca. 15 mg sample). The probe was tuned to the resonance frequencies of 51V (105.246 MHz). The parts per million scale of the spectra was calibrated using the 13C signal of adamantane as an external secondary reference. Samples were dehydrated under a flow of dry air at 500° C. for 3 h prior to the NMR measurements. Infrared spectra were recorded on a self-supporting wafer using a Bruker Alpha spectrometer in transmission mode (resolution of 2 cm−1). The intensities were normalized to the Si—O—Si overtones of the silica framework. Diffuse reflectance UV-vis spectra were recorded with a Maya 200 spectrometer (Ocean Optics) equipped with a UV-vis deuterium/halogen light source (DH-2000-BAL from Mikropack) using BaSO4 as a background. Both FT-IR and UV-vis analysis were carried out inside a glovebox (<1 ppm of H2O and O2).
The point of zero charge (PZC) was determined according to a well-described method: titration of 0.1 M HNO3 to a blank reference solution (3 mL 0.1 M KNO3, 2 mL 0.01 M KOH, 5 mL DI H2O) and reference solution plus conventional- (or pro-) SiO2 gradually lowered the pH of the solution. Intersection of the titration curves of the blank solution with that of the solution plus conventional- (or pro-)SiO2 indicated the pH at which the quantity of Si—OH2+ sites was equivalent to that of Si—O− sites, defined as the PZC. The titration curves are provided in the figures herein.
Vanadium loadings were determined using induced coupled plasma optical emission spectroscopy (ICP-OES) after complete acid digestion. Surface area and pore volume calculations were performed using Micromeritics 3-Flex instrumentation (t-plot analysis). Bulk analysis was repeated three times to accurately determine the metal oxide surface density.
ODHP Catalytic Activity. Catalytic activity measurements were performed using a Microactivity-Effi reactor. A total of 60-150 mg of catalyst (particle size of 600-710 μm) was mixed with inert SiC particles of equal size in a ratio of 2:1 (SiC-to-catalyst) and packed inside a quartz reactor tube (9 mm ID). Reactions were carried out at 490° C. with inlet flow ratios of 3:6:11 O2/C3H8/N2. Exhaust streams were analyzed using a Shimadzu 2010 GC equipped with three Restek columns (Rtx-1, Rt-Q-Bond, and RT-Msieve 5A) and a thermal conductivity detector (TCD) and flame ionization detector (FID). The catalysts were investigated under different contact times to monitor product selectivity at varying propane conversions (inverse weight-hour-space-velocity (WHSV−1) of 20-140 [kg-cat s m−3]). The carbon balance of each data point closes within 5%.
Surface density, (M) mn−2
From Serendipity to a Reproducible Synthesis Procedure.
Use of impure SiO2 (im-SiO2) delivered directly from Sigma-Aldrich (batch #MKBN2949 V) allowed for a significantly better dispersion of vanadia than ever observed before. Indeed, V2O5 nanoparticles could not be detected up until a surface coverage as high as 8.9 V nm−2 (see below). Systematic addition of the various metal impurities found in im-SiO2 (determined by ICP-OES) to conventional SiO2 via incipient wetness impregnation (see Experimental section) revealed Na+ to be the responsible promoter. The enhanced dispersion properties of im-SiO2 could be reproduced by adding 0.40 wt % Na+ using a 1 M Na(NO3) solution via incipient wetness impregnation to conventional-SiO2 to create Na+− promoted material (pro-SiO2). Impregnation of vanadia to a SiO2 support containing <0.40 wt % Na+ did not show the enhanced dispersion effect (viz. formation of V2O5 particles), while impregnation of vanadia to SiO2 material containing Na+ loadings of ≧1.0 wt % revealed the formation of sodium metavanadate (
Surprisingly, when substituting sodium with other alkali or alkaline earth metals (Li+, K+, Rb+, Mg2+) with comparable promoter/V molar ratios, no enhanced 2D vanadia dispersion could be observed. Indeed, Raman spectroscopy reveals the formation of 3D V2O5 in almost all prepared samples (
Previous studies explored alkali-metal promoters for supported vanadium catalysts to neutralize acidic sites on various supports, and investigated its effect on the redox behavior. It is worth emphasizing that in one study, the authors varied the molar ratio of Na/V between 0:1 and 1:1 for V/CeO2 catalysts and monitored the effect on reducibility and activity for ODH of methanol. At Na/V ratios <0.25, sodium addition only marginally decreased redox ability and showed no negative effect on catalytic activity, while the opposite is true with Na/V ratios >0.25.
In this example, we focus on the effect of the Na+-promoter on the structural properties of supported metal oxides on SiO2 and couple this to the reactivity of the material using ODHP as a structure-sensitive probe reaction.
Enhancing 2D Dispersion.
Raman spectra of the prepared materials are displayed in
It is important to note that the V═O stretching vibration of 2D vanadia at 1035 cm−1 does not shift to lower wavenumbers upon the addition of Na+. This suggests that the V═O bond does not weaken upon Na+ promotion as was observed in earlier work for higher Na+ loadings.
In addition to the Raman spectra, diffuse reflectance UV-vis (DRUV-vis) edge energy shifts of dehydrated vanadia catalysts supported on im-SiO2 were determined (
Solid-state 51V MAS NMR spectra of dehydrated vanadia supported im-SiO2 samples are displayed in
The enhanced dispersion when using im-SiO2 is not exclusive to supported vanadia but is also observed with the other group V metal oxides (i.e., niobium and tantalum oxides; see Raman spectra in
Catalytic Activity.
The strong structure-sensitivity of ODHP can be conveniently used to characterize supported vanadium materials. When plotting the propylene selectivity as a function of propane conversion for the various catalysts (
In
Catalysts with high vanadia surface density remain stable for at least 4.5 days on stream, despite the high temperature and the formation of water as a reaction product. This is illustrated in
Hypothesis for the Potential Role of Sodium as a Promoter.
Metal oxide nanoparticles are formed when it becomes more favorable to anchor to supported metal oxide species rather than support-oxide anchoring sites during the impregnation and/or calcination. As a working hypothesis, we propose that Na+ enhances 2D metal oxide dispersion on SiO2 by exchanging with surface silanol groups, making these anchoring sites more reactive. This hypothesis is supported by IR spectroscopy (
The highly nucleophilic ≡SiONa sites can more readily react with the VO(OiPr)3 precursor, yielding a surface bound ≡SiO—V(O)(OiPr)2 species plus NaOiPr. The basic sodium isopropoxide could react with a less reactive silanol group, regenerating the more favorable ≡SiONa anchoring site. Our proposed (catalytic) mechanism for Na+-assisted vanadiumoxide anchoring is displayed in Scheme 1. We envision that this mechanism could help in preferential multipodal bonding of the vanadium to the silica surface rather than atop surfacebound vanadium sites.
This proposed mechanism could also explain the necessity for an optimal amount of sodium to be present to observe enhanced 2D dispersion. It is indeed plausible that each silanol activating This proposed mechanism could also explain the necessity for an optimal amount of sodium to be present to observe enhanced 2D dispersion. It is indeed plausible that each silanol activating silanol activating Na+ species can only migrate a limited distance before becoming surrounded by anchored vanadia species. No longer able to migrate via the proposed ion-exchange mechanism, vanadium-surrounded Na+ species cannot activate the remaining unreactive silanol groups, leaving any unanchored VO(OiPr)3 precursor to anchor to already surface-bound vanadia during the calcination step, thus forming 3D V2O5. No evidence for the formation of VONa bonds could be found in the calcined materials, and 51V NMR indicates only a slight downfield shift of the (SiO)3V≡O vanadia centers upon the addition of sodium. Attempts to capture this effect using 23Na MAS NMR with pro-SiO2 catalysts have been unsuccessful to date due to the low signal-to-noise ratio, likely caused by (1) the low sodium content and, more importantly, (2) the amorphous nature of the support leading to peak broadening. The proposed hypothesis will be further investigated, also to explore why it is that other alkali and alkali-Earth metal ions (Li+, K+, Rb+, Mg2+) do not display the same enhanced 2D dispersion effect that Na+-promoted SiO2 offers. Most likely, sodium ions present an optimal balance between charge density and solvation by the isopropanol solvent used during the impregnation.
Structural properties of supported metal oxides, particularly the presence of 2D or 3D metal oxide species, control their catalytic performance. Out of all traditional oxide supports, SiO2 has historically allowed the lowest 2D metal oxide dispersion, despite its high surface area. Using Raman and DRUV-vis spectroscopy, 51V-NMR, and catalytic activity data with ODHP as a probe reaction, we now show that the promotion of conventional silica with 0.40 wt % Na+ can significantly enhance the dispersion of vanadia on SiO2 to levels equivalent to that of other common oxide supports (i.e., up to 8.9 V nm−2). Increasing the quantity of 2D vanadia serves to proportionally increase the rate of propane ODH while maintaining high propylene selectivity. Raman spectroscopy further confirms enhanced dispersion of the other group V metal oxides (Nb, Ta oxide) on Na+-promoted SiO2. It is hypothesized that the role of Na+ is to ion-exchange with surface silanols to form more-reactive Si—O—Na+ anchoring sites. The silanol groups that would normally remain unreactive toward the metal oxide precursor now have the ability to function as an anchoring site. From the optimal Na/V ratio of 0.2, and the fact that the sodium promotion nearly triples the amount of dispersed vanadia, we propose a catalytic mechanism in which one sodium ion is able to facilitate the anchoring of several vanadia species. The enhanced metal oxide dispersion effect is displayed here for the case of group V metal oxides but likely includes other metal oxides as well. This finding presents exciting new opportunities for metal oxide catalysts supported on SiO2.
The oxidative dehydrogenation of propane (ODHP) is a highly attractive reaction for the on-purpose production of propylene. Unfortunately, rapid consecutive over-oxidation of the desired olefin limits the selectivity and hampers the industrial feasibility. Supported metal oxides, and in particular dispersed vanadium containing materials, have shown promising results. Yet one has to improve both the selectivity and activity (space-time-yield) to make this reaction economically attractive. In this contribution we build upon our previous work that allowed us to increase the dispersion of group V metal oxides on silica to prepare a ternary metal oxide catalyst based on vanadium and tantalum that shows superior selectivity and productivity.
Introduction
The great abundance of shale gas has initiated a renaissance in the chemical industry [1]. One of the effects is a shift from naphtha to ethane cracking at the heart of the chemical value chain. As a consequence, the United States is now one of the low cost producers of ethylene. Indeed, the ethylene production costs dropped from close to $0.6/pound in 2005 to below $0.3/pounds currently, causing an expected growth in the production of polyethylene by more than 50% by 2020 [2]. However, this feedstock shift also brings about challenges for the production of other olefins, in particular propylene. As an example, steam cracking of naphtha typically produces 31% ethane, 16% propylene and 8% crude C4s (plus pyrolysis gasoline and hydrogen). With ethane as a feedstock, steam cracking produces close to 80% ethylene but only 3% propylene and 3% crude C4s. As a consequence, the demand for propylene is growing far more rapidly than can be satisfied by steam cracking (
One of the already implemented technologies to fill the demand gap is DeHydrogenation (DH) of propane (equation 1), obtained from the “wet fraction” of shale/natural gas. The three most important DH technologies are: (1) Oleflex (UOP), (2) Catofin (Lummus), and (3) STAR (Uhde) [4]. In order to drive this endothermic reaction (□H°298=+124 kJ mol-1), high reaction temperatures are required (550-750° C.), causing rapid catalyst deactivation due to coking. Various technological solutions have been engineered to handle this problem, such as Continuous Catalyst Regeneration (CCR by UOP), or the use of parallel fixed bed reactors that alternate between catalyst regeneration and on-stream operation (e.g. Catofin process).
C3H8→C3H6+H2 (1)
The endothermicity of this process makes this technology rather energy intensive. Co-feeding of oxygen and propane could result in the Oxidative DeHydrogenation of propane (ODHP), making the reaction exothermic (ΔH°298=−117 kJ mol−1) and prevents the formation of carbon deposition. Unfortunately this approach leads to problems of rapid consecutive over-oxidation, a general problem for partial oxidations [5].
A widely investigated class of catalysts for ODHP are supported vanadium oxide materials [6-16]. Strong structure-dependent performance has been reported: the presence of site-isolated, or highly dispersed, vanadia species was shown to be key to obtain high selectivity [6]. The presence of V2O5 nanoparticles results in the acceleration of the undesired propylene combustion. Even for well-dispersed systems, it is well established that the support plays an important role in controlling the activity and selectivity [6]. For instance, V/TiO2 materials are more active but also less selective than V/SiO2. Aiming for synergetic effects, Schlögl and coworkers prepared a V/Ti/SBA-15 material [17]. This system indeed showed an enhancement of the catalyst's productivity (kg-C3H6 kg-cat−1 hr−1) by a factor of ˜7, compared to a V/SBA-15 catalyst. While the V/Ti/SBA-15 catalyst shows enhanced productivity, its selectivity to propylene remains equivalent to (or slightly below) that of V/SBA-15. Thus, catalysts showing superior selectivity under ODH conditions are still highly sought after.
Recently, our group reported on a method to enhance the two-dimensional dispersion of Group V metal oxides on silica by promoting the support with small amounts of sodium [18]. Grant J T, et al. (2015) ACS Catal 5:5787-5793 is incorporated herein by reference in its entirety. This allowed us to increase the monolayer coverage from ˜3 V nm−2 to ˜9 V nm−2, avoiding the formation of V2O5 nanoparticles. In the present contribution we aim to investigate this system in more detail and use this technique to add an additional metal oxide to enhance the performance of the vanadium at high surface coverage.
Experimental
Material synthesis Sodium-promoted SiO2 (pro-SiO2) was prepared by incipient wetness impregnation (IWI) of a 1M NaNO3 solution to conventional amorphous silica (Aerosil200 from Evonik; 200 m2 g−1). An appropriate amount of 1M NaNO3 solution was diluted in deionized H2O to roughly equal the pore volume of Aerosil200 (1.3 mL g−1). The Na-impregnated sample was then calcined under air, ramping 1.5° C. min−1 to 700° C., holding at 700° C. for 4 h. Sodium loading of pro-SiO2 is equal to 0.4 wt % Na+.
All supported vanadium-oxide and tantalum-oxide catalysts were synthesized using IWI inside a glovebox under a dry N2 atmosphere. All samples were dried overnight in static conditions at 120° C. prior to metal impregnation. Metal alkoxide solutions were used as precursors, as these were previously shown to be superior to other precursors [8]. Supported vanadium oxide catalysts were synthesized by IWI of vanadium oxytriisopropoxide (VTI; Sigma-Aldrich) diluted in dry isopropanol (Sigma-Aldrich, 99.5%) onto pro-SiO2. The ratio of vanadium-to-isopropanol was altered to create a variety of vanadium oxide loadings. Impregnated samples were vacuum-dried inside the glovebox and transferred to a calcination oven where they were dried under a flow of N2 at 120° C. for 3 h, ramped to 550° C. at 1° C. min−1 under dry air, and calcined at 550° C. for 3 h. Only a minor (i.e. 10%) decrease in specific surface area could be observed.
The ternary catalyst 4V/18Ta/pro-SiO2 was prepared in a two steps procedure. An initial IWI treatment of tantalum ethoxide (Sigma-Aldrich, 99.98%) diluted in dry ethanol (Sigma-Aldrich, 99.5%) was made to pro-SiO2. The tanatalum-to-ethanol ratio was adjusted to create a final tantalum metal loading of 18 wt %. This sample was vacuum-dried inside the glovebox and transferred to a calcination oven to undergo the calcination procedure detailed above for supported vanadium oxide catalysts. The 18Ta/pro-SiO2 catalyst was then dried overnight at 120° C. before transferring to a glovebox to undergo impregnation of VTI to allow for a vanadium loading of 4 wt % followed by vacuum-dry and calcination.
Characterization
Raman characterization was performed using a Renishaw InVia Raman Spectrometer using a 785 nm excitation laser. The analysis was done in a high-temperature Linkam CCR1000 cell. Samples were dehydrated by ramping 10° C. min−1 and holding at 500° C. under 20 mL min−1 of a 80% He, 20% O2 gas mixture for 1 h before measurement. All measurements used a 1200 L mm−1 grating and were taken with a range of 250-1100 cm−1 and a dispersion of 1.36565 cm−1 pixel−1.
Solid-state 51V-NMR spectra were acquired on an Avance NMR spectrometer (Bruker) operating at a 1H Larmor frequency of 400 MHz. The samples were spun around the Magic Angle with a rate of 18 kHz at room temperature using a double resonance 3.2 mm probe (containing ca. 15 mg sample). The probe was tuned to the resonance frequencies of 13C (176.06 MHz). The ppm scale of the spectra was calibrated using the 13C signal of adamantane as an external secondary reference.
Diffuse Reflectance UV-Vis spectra were measured using a Maya 200 spectrometer (Ocean Optics) equipped with a UV-vis deuterium/halogen light source (DH-2000-BAL from Mikropack) using BaSO4 as a background matrix. All measurements were recorded inside a glove box (<1 ppm H2O and O2). Infrared spectra were measured on a self-supporting wafer using a Bruker Alpha spectrometer in transmission mode (resolution of 2 cm−1). The intensities were normalized to the Si—O—Si overtones of the silica framework.
Metal loadings were determined using induced coupled plasma optical emission spectroscopy (ICP-OES) after complete acid digestion. Pore volumes and surface areas were performed using Micromeritics 3-Flex instrumentation (t-plot analysis).
Catalytic Testing
Catalytic measurement was performed using a Microactivity-Effi reactor. Reactions were carried out at 490° C. and ambient pressure with inlet flow ratios of 15% O2 and 30% C3H8 (balance N2). Total inlet flowrate was varied between 40-160 mL min−1 to monitor product selectivity at varying propylene yields. The reactor bed contained 40-150 mg of catalyst particles (size 600-710 μm) diluted with inert SiC particles to ensure uniform catalyst bed temperature. These particles were packed inside a quartz reactor tube (9 mm ID). We carefully verified that there was negligible thermal background reactivity occurring under our experimental conditions (viz, homogeneous gas phase chemistry). Exhaust streams were analyzed using a Shimadzu 2010 GC equipped with three Restek columns (RTX-1, RT-Q-Bond, and RT-Msieve 5A), a flame ionization detector (FID) and a thermal conductivity detector (TCD). The carbon balance of each data point closes within ±5%.
Results and Discussion
Evidence for the Enhanced 2D Dispersion at Optimal Na/V Ratio
Diffuse Reflectance UV-Vis (DRUV-Vis) spectroscopy is widely used to conveniently differentiate between monomeric, polymeric and nanoparticles of vanadium oxide at the surface of catalytic materials [19]. The spectra in
We emphasize that these unprecedented vanadium dispersion levels (up to ˜9 V nm−2) were only obtained when the amorphous silica support was promoted with 0.4 wt % of sodium (
As previously reported [18], the enhanced 2D metal oxide dispersion afforded by pro-SiO2 is not exclusive to supported vanadia but applies to the other Group V metal oxides as well, e.g. supported Nb-oxide and Ta-oxide. Raman spectroscopy was used to show that use of pro-SiO2 as a support could increase the maximum supported 2D Nb-oxide and Ta-oxide species to at least 5.5 wt % Nb and 18 wt % Ta. We now show, for the case of the 4V/18Ta/pro-SiO2 material (containing 4 wt % V and 18 wt % Ta), that also combinations of Group V metals can be anchored together on a surface, allowing for enhanced 2D dispersion of multiple metal oxides. Indeed, no Raman bands associated with 3D V2O5 or Ta2O5 nanoparticles are detected for the 4V/18Ta/pro-SiO2 catalyst (
Working Hypothesis Behind the Enhanced Dispersion
The addition of sodium was found to reduce both the isolated SiOH stretching vibrations (appearing at 3745 cm−1) and H-bonded silanol groups (broad signal at 3660 cm−1; see
Insights from Solid State 51V NMR
The absence of a sharp isotropic shift at −614 ppm in the V/pro-SiO2 51V MAS spectra up to vanadia coverages of 8.9 V nm−2 (corresponding to 7.2 wt % V) confirms the absence of V2O5 particles [22,23]. The isotropic shift for V/SiO2 is at −695 ppm, whereas the isotropic shift for all of the dispersed V/pro-SiO2 samples is at −675 ppm. The subtle deshielding of the vanadium when the support is sodium-promoted points towards a slightly lower electron density at the vanadium nucleus. This could in principle cause an increase in the V═O bond strength, which is however not observed with Raman spectroscopy. Indeed, we observe a slightly lower V═O stretching frequency for the sodium-promoted material (viz. 1035 versus 1043 cm−1). Based on these observations, we hypothesize that sodium could be interacting with the vanadyl oxygen atom (
The 51V MAS NMR spectrum for the ternary V/Ta/pro-SiO2 system shows a single isotropic shift at −685 ppm. It appears to experience the same subtle deshielding of the 51V nuclei compared to the V/SiO2 system, although not to the same extent as the V/pro-SiO2 materials. More importantly, this result indicates that the vanadium is still bound to the silica and not on top of the tantalum.
Catalytic ODHP Results
Catalysts with vanadium loadings above and below monolayer coverage were tested for differences in propylene selectivity and yield. All catalysts containing less than 7.2 wt % V (corresponding to 8.9 V nm−2) supported on pro-SiO2 show higher selectivity to propylene than those with higher vanadium loadings at comparable propylene yields (see
Close evaluation of the kinetic data reveals that the turnover frequency (TOF), i.e. mol C3H8 reacted per mol V per s, is reduced by approximately a factor of 1.7 in the case of the V/pro-SiO2, compared to supported vanadia materials on un-promoted SiO2. Assuming a constant pre-exponential factor, this corresponds to a subtle difference in activation energy of ≈0.7 kcal mol−1. This decrease in TOF upon sodium promotion could be due to the generation of slightly less-reactive V═O sites, caused by the interaction of the vanadyl oxygen atom with the sodium promoter (vide supra). We emphasize that there is a significant spread in the reported literature for TOF values for V/SiO2 catalysts for ODHP, varying between almost three orders of magnitude (10−4-6×10−2 s−1) [6]. Based on the results shown here, this spread could be due to varying levels of impurities found in the silica and warrants caution when comparing literature data [6]. In any case, this minor decrease in TOF caused by the sodium promoter is more than compensated by a nearly three-fold enhancement of the monolayer coverage, leading to an overall increase in space-time-yield for V/pro-SiO2 materials.
Following our earlier observation that also other Group V metal oxides show enhanced 2D dispersion when supported on Na+-promoted SiO2 [18], we attempted to co-immobilize a second metal oxide, approaching a combined monolayer. As Ta/SiO2 has been reported in the literature as a very active [24], but less selective ODHP catalyst, we focused our attention on the preparation of a V/Ta/SiO2 catalyst (containing 4 wt % V and 18 wt % Ta), featuring a surface coverage of ≈8 (V+Ta) per nm2. Remarkably, this ternary metal oxide catalyst shows a significantly improved catalytic performance over the V/pro-SiO2 material. Indeed, the 4V/18Ta/pro-SiO2 catalyst shows substantially higher selectivity to propylene than all other supported catalysts, maintaining close to 80% propylene selectivity at 5.4% propylene yield (
Importantly, these results suggest that an optimal amount of a third transition metal oxide at sub-monolayer coverage significantly improves the productivity toward propylene. However, fundamental insights will continue to be explored to explain the increased selectivity and productivity of ternary (VOx)m/(MOy)n/pro-SiO2 type catalysts.
Promotion of amorphous silica with small amounts of sodium (pro-SiO2) allows for a greater dispersion of Group V metal oxides. In this contribution we report on Raman and 51V MAS NMR spectroscopic data, in conjugation with catalytic activity data to further explore this effect. A change in the isotropic 51V shift from −695 to −675 ppm upon Na+-promotion indicates subtle deshielding of the vanadium center, due to a more positive vanadium site. However, Raman spectroscopy indicates that this does not lead to a stronger V═O bond as one might expect. Indeed, the vanadyl stretch shifts from 1043 to 1038 cm−1, indicating that the V═O bond actually weakens. These observations lead to the hypothesis that the Na+ ions weakly interacts with the vanadyl oxygen atom, removing electron density from the V═O bond. This hypothesis is in line with a minor decrease in the turnover frequency (TOF) for the oxidative dehydrogenation of propane reaction (ODHP) for V/pro-SiO2 compared to V/SiO2. Indeed, the rate-determining step in this reaction has been proposed to be the H-abstraction from propane by the vanadyl oxygen atom. Removing electron density from the vanadyl bond would hence lower the reactivity. Nevertheless, the TOF of V/pro-SiO2 still falls well within the range of literature reported TOF of V/SiO2 catalysts for ODHP, which varies by almost three orders of magnitude. This large deviation in reported TOF data might be explained by the potential presence of various impurities for the SiO2 support materials using in the various studies. Successful 2D co-dispersion of both V- and Ta-oxide on pro-SiO2 demonstrates that combinations of supported Group V metal oxides can coexist on the pro-SiO2 surface. This V/Ta/pro-SiO2 ternary catalyst shows improved productivity as well as higher selectivity to propylene for ODHP than 2D V/pro-SiO2 catalysts.
The invention is not limited to the embodiments set forth in this disclosure for illustration, but includes everything that is within the scope of the claims. Furthermore, all documents cited in this disclosure are hereby incorporated by reference in their entirety and for all purposes as if fully set forth in this disclosure.
This application claims the benefit of U.S. Provisional Patent Application Ser. No. 62/112,689, filed Feb. 6, 2015, which is incorporated by reference herein as if set forth in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62112689 | Feb 2015 | US |