ENVIRONMENT-FRIENDLY CEMENT SELF-REPAIRING SYSTEM, ITS PREPARATION METHOD AND APPLICATION

Abstract

The invention discloses an environment-friendly cement self-repairing system, and its preparation method and application. The preparation method comprises the following steps: adding a shell curing agent into deionized water to prepare solution 1, adding an inorganic nano emulsifier into deionized water, ultrasonically dispersing, then adding polysaccharide-shell, and uniformly stirring to obtain emulsion polymerization aqueous phase; adding epoxy diluent into epoxy resin, and uniformly stirring; obtaining an emulsion polymerization oil phase; mixing the emulsion polymerization aqueous phase and emulsion polymerization oil phase, and stirring to obtain uniform emulsion; dropping the uniform emulsion into solution drop by drop by using pendant drop method, stirring until the droplets are shaped, then filtering, washing with deionized water, and drying to obtain self-repairing capsules; next, mixing with an environment-friendly curing agent to obtain an environment-friendly cement self-repairing system. The environment-friendly cement self-repairing system is green, nontoxic and harmless, has strong water absorption, can block tiny cracks by volume expansion when contacts with water, thus further enhances the cement self-repairing effect.

Description

Claims

1. A preparation method of environment-friendly cement self-repairing system, comprising steps as follows: step 1, preparation of a self-repairing capsule, comprising the following substeps: sub-step 1, preparation of solution 1: adding an amount of deionized water into a shell curing agent, and uniformly stirring to obtain the solution 1 with the mass fraction of the shell curing agent of 2.22%-2.72%;sub-step 2, preparation of an emulsion polymerization aqueous phase: adding an inorganic nano-emulsifier into the deionized water, ultrasonically dispersing for 5-15 min at 20 kHZ, adding a polysaccharide shell, and uniformly stirring to obtain an emulsion polymerization aqueous phase with the mass fraction of inorganic nano-emulsifier of 0.5%-1.5% and the mass fraction of polysaccharide shell of 1%-2.5%;sub-step 3, preparation of an emulsion polymerization oil phase: adding an epoxy diluent into an epoxy resin, and stirring evenly, obtaining the emulsion polymerization oil phase with the mass fraction of the epoxy diluent of 10%-20%;sub-step 4, preparation of an emulsion: mixing the emulsion polymerization aqueous phase obtained in sub-step 2 with the emulsion polymerization oil obtained in sub-step 3 according to the mass ratio of 75-50:25-50, and stirring at 10,000-12,000 rpm to obtain a uniform emulsion;sub-step 5, preparation of a self-repairing capsule: dropping the homogeneous emulsion obtained in sub-step 4 into the solution 1 obtained in sub-step 1 by pendant drop method, stirring until the droplets are shaped, and filtering, washing with the deionized water, then drying to obtain self-repairing capsules;step 2, mixing the self-repairing capsule and an environment-friendly curing agent according to the mass ratio of (2.15-2.54):1 to obtain the environment-friendly cement self-repairing system, the inorganic nano-emulsifier is nano silicon dioxide, bentonite or nano calcium carbonate, and the environment-friendly curing agent is chitosan, dopamine or lysine.

2. The preparation method of environment-friendly cement self-repairing system as claimed in claim 1, wherein, the shell curing agent is calcium chloride, calcium sulfate or aluminum chloride.

3. (canceled)

4. The preparation method of environment-friendly cement self-repairing system as claimed in claim 1, the polysaccharide shell material is sodium alginate or xanthan gum.

5. The preparation method of environment-friendly cement self-repairing system as claimed in claim 1, the epoxy diluent is benzyl glycidyl ether, phenyl glycidyl ether or butyl glycidyl ether.

6-7. (canceled)

8. An environmentally-friendly cement self-repairing system prepared by the preparation method as claimed in claim 1.

9. An application of the environment-friendly cement self-repairing system as claimed in claim 8 in cement self-repair.