Patent Application
20190002672
The present disclosure relates generally to an environment-friendly material and more particularly, to an environment-friendly material suitable for manufacturing window covering slat, a manufacturing method of window covering slat using the material, and a window covering slat manufactured by the method.
Conventionally, plastic window covering slats are usually made of polyvinylchloride (PVC). If the old window covering slats are discarded without recycling properly, the slats will be treated as regular trash so that Dioxin will be produced in incineration, thereby causing harm to human health and environment.
Taiwan Patent No. 379272 reveals a manufacturing method of environment-friendly paper made from a raw material, which is relatively friendly to the environment, containing inorganic mineral powder, polyethylene, and auxiliary agent. However, because the product obtained therefrom has considerably low toughness, it is not suitable for making window covering slats.
In addition, because a conventional elastic sheet manufactured by using a raw material comprising inorganic mineral powder that cannot be kneaded directly, the inorganic mineral powder has to be made into masterbatch before processing such as kneading and pelletizing, extruding, etc., thereby causing higher manufacturing cost and complicated process.
The present disclosure is accomplished in view of the above-noted circumstances. An objective of the present disclosure is to provide an environment-friendly material, which is suitable for manufacturing window covering slat. As such, the manufacturing cost can be reduced and the window covering slat manufactured therefrom is more environment-friendly in comparison with prior elastic window covering slat.
To attain the above objective, the present disclosure provides an environment-friendly material comprising 50 wt % to 70 wt % of inorganic mineral powder, 20 wt % to 45 wt % of polyolefin, and 5 wt % to 15 wt % of auxiliary agent. The inorganic mineral powder includes calcium carbonate; the polyolefin may be liner low density polyethylene (LLDPE), low density polyethylene (LDPE), medium density polyethylene (MDPE), high density polyethylene (HDPE), or polypropylene (PP); and the auxiliary agent may be polyolefin elastomer (POE), maleic anhydride grafted polyolefin elastomer (POE-g-MA), or maleic anhydride grafted polyethylene (PE-g-MA).
It is another objective of the present disclosure to provide a manufacturing method of window covering slat, which is capable of simplifying the manufacturing process and reducing the manufacturing cost.
To attain the above objective, the present disclosure provides a manufacturing method of window covering slat, comprising the steps of:
According to the manufacturing method of the present disclosure, the kneading and pelletizing in step a) may be implemented by, but not limited to, a planetary mixer, a Banbury mixer, a kneader, or a twin-screw mixer.
It is a further objective of the present disclosure to provide a window covering slat which is manufactured by the present manufacturing method.
Because the present material is not only polyvinylchloride-free but also comprises quite an amount of calcium carbonate, which is low cost and readily obtained, the present material is environment-friendly and the manufacturing cost can be effectively reduced. In addition, the present manufacturing method using the present material has advantages of environment-friendly, simplified manufacturing process and reduced manufacturing cost, inasmuch as the inorganic mineral powder contained in the environment-friendly material can be homogeneously mixed directly without being first processed into masterbatch.
The sole FIGURE is a flow chart illustrating the manufacturing method of the window covering slat of the present disclosure.
The present disclosure provides an environment-friendly material which can be used to manufacture environment-friendly window covering slat having appropriate mechanical strength. The window covering slat thus obtained is applicable to panel-type curtain, vertical louver or horizontal louver.
The environment-friendly material according to the present disclosure may comprise 50 wt % to 70 wt % of inorganic mineral powder, 20 wt % to 45 wt % of polyolefin, and 5 wt % to 15 wt % of auxiliary agent.
The inorganic mineral powder may be solid particles at room temperature and may comprise calcium carbonate, or may further comprise talcum powder.
The polyolefin may be liner low density polyethylene (LLDPE), low density polyethylene (LDPE), medium density polyethylene (MDPE), high density polyethylene (HDPE), or polypropylene (PP). In consideration of improving the toughness of the manufactured window covering slat, the polyolefin may preferably be LLDPE, HDPE or PP and more preferably be LLDPE.
The auxiliary agent may be polyolefin elastomer (POE), maleic anhydride grafted polyolefin elastomer (POE-g-MA), or maleic anhydride grafted polyethylene (PE-g-MA). In order to enhance the tear resistance of the manufactured window covering slat, the polyolefin may preferably be POE-g-MA.
According to the environment-friendly material of the present disclosure, in consideration of improving the hardness of the manufactured window covering slat, the present material may preferably comprise 60 wt % to 65 wt % of inorganic mineral powder, and more preferably comprise 65 wt % of inorganic mineral powder, 30 wt % of polyolefin, and 5 wt % of auxiliary agent.
In addition to the components mentioned above, additional additives may optionally be added to the present material, without changing the physical/chemical properties of the present material, to provide corresponding functions or properties according to an actual need. For example, a bleaching agent, a toner or a pigment may be used to change the color of the manufactured window covering slat. Or, an antioxidant or an anti-ultraviolet agent may be used to prolong the lifetime of the manufactured window covering slat. Or, a UV absorber may be used to increase the ultraviolet absorption capacity of the manufactured window covering slat. In addition, a lubricant, an elastic auxiliary agent or an antistatic agent may also be used.
The present disclosure also provides a manufacturing method of window covering slat, which can be used to manufacture environment-friendly window covering slat having appropriate mechanical strength, and thus the obtained window covering slat is applicable to panel-type curtain, vertical louver or horizontal louver.
Referring to the sole FIGURE, the manufacturing method according to the present disclosure comprises step S1 of kneading and pelletizing an environment-friendly material to obtain a composite material. Then, in step S2, the obtained composite material is extruded to form a sheet. Finally, the obtained sheet is further processed, in step S3, to produce a window covering slat.
In step S1, the environment-friendly material mainly includes 50 wt % to 70 wt % of inorganic mineral powder, 20 wt % to 45 wt % of polyolefin, and 5 wt % to 15 wt % of auxiliary agent.
Detailed descriptions of the inorganic mineral powder, polyolefin and auxiliary agent, which are identical to those described above, are omitted for simplicity.
In step S1, in consideration of improvement in the hardness of the manufactured window covering slat, the environment-friendly material used in the present manufacturing method may preferably comprise 60 wt % to 65 wt % of inorganic mineral powder, and more preferably comprise 65 wt % of inorganic mineral powder, 30 wt % of polyolefin, and 5 wt % of auxiliary agent.
Further, as described above, one or more additional additives may optionally be added to the environment-friendly material used in step S1, without changing the physical/chemical properties thereof, according to an actual requirement. The additional additive may be, but not limited to, a bleaching agent, a toner, a pigment, an antioxidant, an anti-ultraviolet agent, a UV absorber, a lubricant, an elastic auxiliary agent and an antistatic agent, and may be added in a small amount in addition to the components contained in the environment-friendly material.
In step S1, the kneading and pelletizing of the environment-friendly material may be implemented by, but not limited to, a planetary mixer, a Banbury mixer, a kneader, or a twin-screw mixer, to obtain the composite material to be used in the following step S2.
In step S2, the extrusion of the composite material to form the sheet may be accomplished by any type of applicable extruder known in the art, such as, but not limited to, a hot-press extruder.
Finally, in step S3, the sheet thus obtained in step S2 is further processed to produce a window covering slat.
Hereinafter, a preferred embodiment of the manufacturing method according to the present disclosure is utilized to produce a slat sample. The physical property, such as impact-resistance of the slat sample, is tested.
The materials of examples and comparative examples shown in the following Table 1 are respectively kneaded and pelletized by a planetary mixer under 170° C. to 210° C. to obtain composite materials. The composite materials are then extruded respectively by a hot-press extruder under 180° C. to form sheets. The sheets thus obtained are respectively cut into slat samples having dimensions of 90 mm×12 mm×1 mm. The impact-resistance test (mechanical strength) of the slat samples manufactured from the materials of examples and comparative examples are tested at room temperature and the test results are shown in the following Table 2.
On the basis that a window covering slat applicable for vertical louver should in general have an impact resistance of at least about 7 pounds, because each of the slat samples made of the materials of examples by the present manufacturing method has an impact resistance larger than 7 pounds, it is proven that the material and the manufacturing method of the present disclosure are suitable for manufacturing window covering slat having superior mechanical strength.
In addition, in comparison with the material including HDPE and PE-g-MA of example 3, the material including LLDPE and POE-g-MA of example 4 can be used to manufacture a window covering slat having more superior impact resistance.
In conclusion, the material of the present disclosure is suitable for producing window covering slat having superior mechanical property. And, because the present material is polyvinylchloride-free and includes quite an amount of calcium carbonate, the present material is environment-friendly and the manufacturing cost can be effectively reduced. Further, the manufacturing method of the present disclosure utilizing the present material has advantages of environment-friendly, simplified manufacturing process and reduced manufacturing cost, inasmuch as the inorganic mineral powder contained in a specific amount in the present material can be homogeneously mixed directly without being first processed into masterbatch. Furthermore, the window covering slat produced from the present manufacturing method is not only environment-friendly but also has superior mechanical property.