Patent Application
20200032512
The invention relates to environmentally responsible insulating construction blocks and structures constructed primarily of recycled materials. The environmentally responsible insulating construction blocks and structures comprise shredded rubber tire pieces coated with silica fume, slag cement and cement, which are then mixed with water and formed in a mold. In one embodiment, a layer of grout is disposed on one side of the environmentally responsible insulating construction block for use in a roofing system. In one embodiment, a permeable layer of a fireproof material is disposed on one side of the environmentally responsible insulating construction block. In one embodiment, the environmentally responsible insulating construction blocks are used in the absence of grout or permeable fireproof material layers. In one embodiment, environmentally responsible insulating construction blocks are used in place of wood blocking for roof assembly applications such as installation of a drip edge or wall coping; or in expansion joints. The environmentally responsible insulating construction blocks provide high insulation as well as strength for applications such as green roofing deck construction. Environmentally friendly structures can be built by pouring the coated shredded rubber tire pieces into molds to form walls, and then to pour a layer of the coated shredded rubber tire pieces as a roof deck, therefore forming an entire structure in one single monolithic pour.
In many developed countries the construction and use of buildings is a leading consumer of energy and producer of greenhouse gas emissions. Sustainable architecture seeks to minimize the negative environmental impact of buildings by efficiency and moderation in the use of materials, energy, and development space. Sustainable architecture uses a conscious approach to energy and ecological conservation in the design of the built environment
Green building (also known as green construction or sustainable building) refers to both a structure and the using of processes that are environmentally responsible and resource-efficient throughout a building's life-cycle, from siting to design, construction, operation, maintenance, renovation, and demolition. Green building rating systems such as BREEAM (United Kingdom), LEED® (United States and Canada), DGNB (Germany), CASBEE (Japan), and VERDEGBCe (Spain) help consumers determine a structure's level of environmental performance. These systems award credits for building features that support green design in categories such as location and maintenance of building site, conservation of water, energy, and building materials, and occupant comfort and health. The number of credits generally determines the level of achievement. Additionally, green building codes and standards, such as the International Code Council's draft International Green Construction Code, are rules created by standards development organizations that establish minimum requirements for elements of green building such as materials or heating and cooling.
Leadership in Energy and Environmental Design (LEED®) is a set of rating systems for the design, construction, operation, and maintenance of green buildings in the United States and Canada which was developed by the U.S. Green Building Council (USGBC). LEED® certification of a building is recognized across the globe as the premier mark of achievement in green building. LEED®-certified buildings cost less to operate, reducing energy and water bills by as much as 40%. Businesses and organizations across the globe use LEED® to increase the efficiency of their buildings, freeing up valuable resources that can be used to create new jobs, attract and retain top talent, expand operations and invest in emerging technologies.
The intent of LEED® is to provide a standard certification process that registers buildings constructed with environmental performance, efficiency, and occupant health and well-being as primary goals. Buildings receive points towards varying levels of certification based on the set of categories established by the USGBC. For example, points are awarded with respect to the following features:
Green roofing systems installed on 50% of more of a roof surface virtually guarantees 2 point toward LEED® certification, and can contribute an additional 7+ points. This is almost 20% of the total number of points needed for a building to be LEED®-certified.
Low slope roofing systems have been developed for use with buildings. Low slope roofing systems commonly include a structural deck made of metal or concrete that is covered with a layer of insulation, and the insulation is then covered with a waterproof membrane. A commercial low slope roof system may use single-ply membranes of pre-fabricated sheets rolled onto the roof and attached with mechanical fasteners, adhered with chemical adhesives, or held in place with ballast such as gravel, stones, or pavers; built-up roofs consisting of a base sheet, fabric reinforcement layers, and a dark protective surface layer; modified bitumen sheet membranes having one or more layers of plastic or rubber material with reinforcing fabrics, and surfaced with mineral granules or a smooth finish; and spray polyurethane foam roofs constructed by mixing two liquid chemicals together that react and expand to form one solid piece that adheres to the roof then having a protective coating such as metal or tile placed over the polyurethane.
Low slope roofing insulation became more prevalent during the 1960's and forward as increasingly more buildings became air conditioned and as the cost of energy, both for heating and cooling rose dramatically. Currently insulation levels may exceed R30 as specified by code or because of the building's use and geographic location.
Insulated panels are known to be used on wall and roof building applications to form part or all of the building envelope. An insulation panel typically has opposing inside and outside surfaces with an insulating foam core adhered between the surfaces. The panel can then be mounted onto support structures to form the wall or roof application in a building.
In the luxury real estate market, buyers in high rise structures seek living spaces on the roof of the structure for providing such amenities as gardens and pools. A green roof, or living roof, is a roof of a building that is partially or completely covered with vegetation and a growing medium, planted over a waterproofing membrane. It may also include additional layers such as a root barrier and drainage and irrigation systems.
One disadvantage of green roofs is the additional mass of soil and retained water that can place a large strain on the structural support of a building. Some types of green roofs also have more demanding structural standards such as in seismic and hurricane-prone regions of the world. Some existing buildings cannot be retrofitted with certain kinds of green roofing because of the weight load of the substrate and vegetation exceeds permitted static loading. For example, the weight of a green roof caused the collapse of a large sports hall roof in Hong Kong in 2016.
One known way to provide rooftop green spaces for high rises is through the use of Inverted Roof Membrane Assemblies (IRMA), also called a Protected Membrane Roof system (PMR) or a Built-up-Roof (BUR) system. In IMRAs, typically a waterproofing membrane is adhered to the roof structure of the building, then a protective moisture resistant insulation layer is laid to protect the membrane from atmospheric degradation such as sun, wind and rain, and also foot traffic. A layer of mesh may be laid to filter for debris, and the insulation layer is held down with a form of ballast such as gravel wooden decking or paving stones. A camber, or slope, of the roof is created during construction to carry water to a roof drain. An example of a IRMA is shown in
Tire recycling or rubber recycling is the process of recycling vehicles' tires that are no longer suitable for use on vehicles due to wear or irreparable damage. These tires are a large and difficult source of waste due to the large volume produced, and the fact they contain a number of components that are ecologically problematic. In the United States alone the Environmental Protection Agency (EPA) estimates that roughly 300 million scrap tires are generated annually. Over 60 million of these tires end up in landfills, ocean, lakes, greatly harming our environment. Local recycling facilities are having a very difficult time dealing with this problem because of the enormous quantities of tires being generated each year and with only so many limited re-use options available to them.
The same characteristics that make waste tires problematic—cheap availability, bulk, and resilience—also make them attractive targets for recycling. Tires are known to be recycled for use on basketball courts, in hot melt asphalt, for increasing burning value of RDF in incineration plants and new shoe products.
In roofing, the most critical point is the roof edge, which area is susceptible to wind uplift failures and moisture infiltration. Eave flashing, or drip edge flashing, is installed at the edge of the roof to ensure proper water run-off. Coping is a protective cap or cover on a wall to protect the wall from water infiltration. Expansion joints are used in roofing where plan dimensions are large to accommodate such situations as change of direction of steel framing or decking; where separate wings of buildings exist; where the type of decking exists; where additions are connected to existing buildings; at junctions where interior heating conditions change; and where movement between walls and the roof deck may occur. Typically, wood blocking is used as a substrate for metal edge components such as flashing, coping and expansion joints.
The invention relates to an environmentally responsible insulating construction block for green roofing and decking applications as well as environmentally friendly substitutes for wood blocking in roofing systems and in structures. The environmentally responsible construction blocks provide high insulation as well as strength for applications such as green roofing and decking construction. Additionally, environmentally friendly structures can be built in one single monolithic pour.
In one embodiment of the invention, the environmentally responsible insulating construction blocks are adhered to a waterproof membrane that is adhered to the top layer of an insulating layer of a roofing system that is adhered to a roof substrate of a building to provide a green roofing application.
In one embodiment, the environmentally responsible insulating construction blocks are provided in side by side relation to similar environmentally responsible insulating construction blocks and adhered to a roof substrate to provide an insulating layer for a membrane roofing system. A waterproof membrane is glued to the top of the environmentally responsible insulating construction blocks, and the environmentally responsible insulated construction blocks are then adhered to the waterproof membrane for use as a green roofing application.
In one embodiment, environmentally responsible insulating construction blocks are layered with a top layer of permeable fireproof material for use as a green decking application.
In one embodiment, environmentally responsible insulating construction blocks are used as a green decking application without a layer of permeable fireproof material.
In one embodiment, a plurality of environmentally responsible insulating construction blocks is adhered to a waterproof membrane that is adhered to the top layer of an insulating layer of a roofing system that is adhered to a roof substrate of a building to provide a green roofing application. In one embodiment, a second layer of environmentally responsible insulating construction blocks having no grout layer or permeable fireproof material layer is adhered to the top layer of the green roofing application for use as a green decking application. In one embodiment, a second layer of environmentally responsible insulating construction blocks having a top layer of a permeable fireproof material is adhered to the top layer of the green roofing application for use as a green decking application. In one embodiment, the tops of the environmentally responsible insulating construction blocks that form the green roofing application are tapered to create a “slope to drain” roofing system. The bottom surfaces of the environmentally responsible insulated construction blocks for green decking application are tapered to correspond to the tapering of the tops of the environmentally responsible insulated construction blocks for green roofing application. The slope of the tops and bottoms of the environmentally responsible insulating construction blocks direct liquids to a roof drain. The permeability of the environmentally responsible insulating construction blocks for green decking application allows for water to pass through and be directed to the roof drain.
In one embodiment, environmentally responsible insulated construction blocks are used as the substrate for installation of flashing, coping and expansion joints in roofing applications in place of wood blocking.
The environmentally responsible insulating construction blocks for green decking application comprise a plurality of shredded rubber tire pieces dry mixed with silica fume, slag cement and cement until the shredded rubber tire pieces are coated. Water is then added to the dry coated shredded rubber mixture. In one embodiment, the wetted shredded rubber tire mixture is placed in the mold whereupon it dries into an environmentally responsible insulating construction block for green decking application. In one embodiment, a layer of a permeable fireproof material is placed in the mold and the wetted shredded rubber tire mixture is placed in the mold on top of the layer of permeable fireproof material whereupon it dries into an environmentally responsible insulating construction block for green decking application. The dried environmentally responsible insulating construction block for green decking application comprises an open matrix from the top through which liquids such as water can freely pass.
In one embodiment, the permeable fireproof material comprises expanded slate.
The environmentally responsible insulating construction blocks for green roofing application comprise a plurality of shredded rubber tire pieces dry mixed with silica fume, slag cement and cement until the shredded rubber tire pieces are coated. Water is then added to the dry coated shredded rubber mixture. A layer of grout may be placed in the mold and the wetted shredded rubber tire mixture is placed in the mold on top of the layer of grout whereupon it dries into an environmentally responsible insulating construction block for green roofing application. The dried environmentally responsible insulating construction block for green roofing application comprises an open matrix. In one embodiment, the environmentally responsible insulating construction blocks can further comprise insulation foam disposed in the interior open matrix of the blocks.
In one embodiment, the coated shredded rubber tire mixture is poured into molds to form walls for a structure. In one embodiment, the coated shredded rubber tire mixture is poured directly onto a scarified concrete slab. In one embodiment, the coated shredded rubber tire mixture is poured on top of a layer of grout that has been placed on top of a scarified concrete slab. Rods are inserted through the length of the molds so that a top can be placed on the poured coated shredded rubber tire mixture for compression while it dries. The top may be a plywood sheet.
In one embodiment, a layer of coated shredded rubber tire mixture is poured on a plywood layer to form a roof covering. A plurality of rods extends upward from the plywood layer to allow for a top to be placed over the poured coated shredded rubber tire mixture to compress it while it dries.
The invention will now be described, by way of example, with reference to the accompanying drawings, in which like numerals refer to like elements.
The invention relates to environmentally responsible insulating construction blocks for green roofing and green decking applications, and as a substitute for wood blocking for attachment of drip edge flashing, coping and expansion joints in roofing systems. The environmentally responsible insulating construction blocks provide high insulation as well as strength. Additionally, environmentally friendly structures can be built in one single monolithic pour.
In one embodiment of the invention, an environmentally responsible insulating construction block is provided for use for green roofing applications. In this embodiment, the environmentally responsible insulating construction block is adhered to a waterproof membrane that is adhered to the top layer of an insulating layer of a membrane roofing system that is adhered to a roof substrate of a building.
Environmentally responsible insulated construction blocks used for green roofing applications comprise coated shredded rubber pieces having a top layer of dried grout that is dried into a block comprising a bottom surface, a top surface, the top surface comprising the grout layer, and four side surfaces substantially perpendicular to the top surface and the bottom surface, wherein the environmentally responsible insulating construction blocks have a thickness defined by the distance between the top surface and the bottom surface. The environmentally responsible insulated construction blocks comprising the coated shredded rubber mixture and dried grout are glued or otherwise adhered to a roof substrate of a building to provide an insulating layer for a membrane roofing system. A waterproof membrane is glued or otherwise adhered to the grout layer of the environmentally responsible insulated construction blocks. The environmentally responsible insulating construction blocks of the invention comprising the coated shredded rubber mixture and a top layer of dried grout are adhered to the waterproof membrane. In one embodiment, the tops of the environmentally responsible insulated construction blocks may be shaped in a manner to induce liquid flow toward a desired direction, for example to a drain.
In one embodiment, the environmentally responsible insulating construction blocks for green roofing application are provided in side by side relation to substantially similar environmentally responsible insulating construction blocks and adhered to a roof substrate to provide an insulating layer for a membrane roofing system. A waterproof membrane is glued to the top of the environmentally responsible insulating construction blocks for green roofing application, and the environmentally responsible insulated construction blocks for green roofing application are then adhered to the waterproof membrane to form a green roof.
In one embodiment of the invention, an environmentally responsible insulating construction block is provided for use for green decking applications. In this embodiment, the environmentally responsible insulating construction block is adhered to a surface to provide a green deck to which growing media or tiles may be adhered. The environmentally responsible insulating construction blocks for green decking application comprise a porous matrix through which water can flow freely.
Environmentally responsible insulated construction blocks used for green decking applications comprise coated shredded rubber pieces that are dried into a block comprising a bottom surface, a top surface, and four side surfaces substantially perpendicular to the top surface and the bottom surface, wherein the environmentally responsible insulating construction blocks for decking application have a thickness defined by the distance between the top surface and the bottom surface. In one embodiment, the top surface comprises a permeable fireproof material. The environmentally responsible insulated construction blocks for decking application comprising the coated shredded rubber mixture and permeable waterproof material, if any, are glued or otherwise adhered to a substrate of the roof of a building to provide a porous deck to which growing media and/or pavers and tiles can be adhered.
In one embodiment, the permeable fireproof material comprises expanded slate.
In one embodiment, a plurality of environmentally responsible insulating construction blocks for roofing application is adhered to a waterproof membrane that is adhered to the top layer of an insulating layer of a roofing system that is adhered to a roof substrate of a building to provide a green roof. In one embodiment, a second layer of environmentally responsible insulating construction blocks are adhered to the top layer of the green roof to form a green deck. In one embodiment, a second layer of environmentally responsible insulating construction blocks having a top layer of a permeable fireproof material are adhered to the top layer of the green roof to form a green deck. In one embodiment, the tops of the environmentally responsible insulating construction blocks for green roofing application are tapered to create a “slope to drain” roofing system. The bottom surfaces of the environmentally responsible insulated construction blocks for green decking application are tapered to correspond to the tapering of the tops of the environmentally responsible insulated construction blocks for green roofing application. The slope of the tops and bottoms of the environmentally responsible insulating construction blocks for roofing application and decking application direct liquids to a roof drain. The permeability of the environmentally responsible insulating construction blocks for green decking application allows for water to pass through and be directed to the roof drain.
In one embodiment, the shredded rubber tire pieces comprise shredded tires. In one embodiment, the shredded rubber tire pieces are shredded to a size such that the steel from the tires is removed but nylon remains in the shredded rubber tire pieces. In one embodiment, the shredded rubber tire pieces are approximately 2 inches nominal size. In one embodiment, the shredded rubber tire pieces have a size greater than approximately ½ inch but smaller than approximately 2 inches. In one embodiment, the shredded rubber tire pieces have a size greater than approximately 1 inch but smaller than approximately 2 inches.
In one embodiment of the invention, the environmentally responsible insulating construction blocks have a thickness (measured from the bottom surface to the top surface) ranging from around 2 inches to around 20 inches, with length and width (measured along the side surfaces) of around 12 inches square. Other dimensions of the environmentally responsible insulating construction blocks may be constructed in accordance with the principles of the invention and these preceding dimensions are listed as examples only and are not intended in any way to limit the invention.
In one embodiment, the green roof and green deck made from the environmentally responsible insulated construction blocks meet building codes designed to withstand severe weather conditions, such as strong winds. 101.4.2 Florida Building Code (FBC), for example, applies to “the construction, erection, alteration, modification, repair, equipment, use and occupancy, location, maintenance, removal and demolition of every public and private building, structure . . . ” and sets forth requirements for buildings to withstand wind forces resulting from design wind speeds. In Broward County, Fla., buildings must withstand wind forces of 140 mph, and in Miami-Dade County, Fla., buildings must withstand wind forces of 146 mph. Other standards exist, for example ASCE (American Society of Civil Engineers)-7 and Florida Statute 553.844 setting forth Building Construction Standards titled “Windstorm loss mitigation; requirements for roofs and opening protection.” These standards may also apply to roof and deck replacement.
In one embodiment, the coated shredded rubber tire mixture is poured into molds in a monolithic pour to form walls for a structure. In one embodiment, the coated shredded rubber tire mixture is poured directly onto a scarified concrete slab. In one embodiment, the coated shredded rubber tire mixture is poured on top of a layer of grout that has been placed on top of a scarified concrete slab. Rods are inserted through the length of the molds so that a top can be placed on the poured coated shredded rubber tire mixture for compression while it dries. The top may be a plywood sheet.
In one embodiment, a layer of coated shredded rubber tire mixture is poured on a plywood layer to form a roof covering. A plurality of rods extends upward from the plywood layer to allow for a top to be placed over the poured coated shredded rubber tire mixture to compress it while it dries.
Turning to the figures,
In
In
In
In
In
In
In
In
In
In
The order of mixing of ingredients may be altered as desired by the operator. For example, the shredded rubber tire pieces or waterproof material, such as expanded slate, expanded slate may be placed in the mixer, then the dry mixture of silica fume, slag cement and cement may be added prior to mixing.
In
In
In
In
In
In
Environmentally responsible insulated construction blocks 610 are attached to the metal or concrete deck 630 using high strength self-setting grout 640, and a waterproof membrane 650 is disposed on an adhesive or glue layer 625 that is disposed on the top surfaces 615 of the environmentally responsible insulated construction blocks 610.
In one embodiment, waterproof membrane 650 comprises any membrane known today or later developed for roofing or other construction purposes. Waterproof membrane 650 may vary according to the use and the climate of the construction.
In
In
In
In
In
In
In
As seen in
In other embodiments, environmentally responsible insulating construction blocks of other dimensions as needed can be installed as described above. In other embodiments, environmentally responsible insulating construction blocks as prepared for green decking applications, with or without a layer of permeable fireproof material, may be installed directly on the roof deck 810 and the plurality of environmentally responsible insulation construction blocks 800 may be adhered to the top surface thereof to provide additional height, if needed.
As seen in
As seen in
As seen in
In both applications, environmentally responsible insulating construction blocks as prepared for green decking applications may be installed directly on the roof deck 1010 and the plurality of environmentally responsible insulation construction blocks 1000 may be adhered to the top surface thereof to provide additional height, if needed.
The following examples illustrate the manufacture and characteristics of environmentally responsible insulated construction blocks in further detail. These examples are exemplary only and in no way limit or are intended to limit the scope of this invention.
Manufacture of an Environmentally Responsible Insulated Construction Block for Green Decking Application.
Approximately 1 gallon of silica fume weighing 6.4 lbs., approximately 1 gallon of slag cement weighing 9.2 lbs. and approximately 1.5 gallons of Portland cement weighing 15.3 lbs. were mixed together for at least 2 minutes. Rubber tires were shredded to a size range of approximately ½″ to 2 inches wherein the steel from the tires was removed but nylon from the tires remained in the shredded rubber tire pieces. Seventy-five (75) lbs. of the shredded tire pieces were added to the mix, and the resulting mixture was mixed for another five (5) minutes. Thereafter, 2 gallons of water were added to wet the dry shredded rubber tire mixture.
Separately, 3 gallons of expanded slate was mixed with 25.6 oz. slag cement, 25.6 oz. silica fume and 38.4 oz. Portland cement were mixed together for at least five (5) minutes. Thereafter, 51.2 oz. water were added to wet the dry expanded slate mixture.
A layer of the wetted shredded rubber tire mixture was poured into molds sized 12 inches by 12 inches by 4 inches deep to which approximately 1 inch of the wetted expanded slate mixture had previously been added. The molds were filled and a lid closed over the mold and left to dry for 5 days at room temperature in the ambient environment. Once the mixture was dry in each mold, the resulting environmentally responsible insulated construction blocks were removed and were ready for use in green decking applications.
Environmentally responsible insulated construction blocks for green decking application were prepared as in Example 1 except that the bottom of the mold is sloped. The dried environmentally responsible insulated construction blocks have a sloped top surface comprising expanded slate.
Environmentally responsible insulated construction blocks for green decking application were prepared as in Example 1 except that no expanded slate mixture was used in the preparation of the blocks and the resulting blocks did not include a permeable fireproof material layer.
Manufacture of an Environmentally Responsible Insulated Construction Block for Green Roofing Application.
Environmentally responsible insulated construction blocks for green roofing applications were prepared by mixing together 1 gallon of silica fume weighing 6.4 lbs., approximately 1 gallon of slag cement weighing 9.2 lbs. and approximately 1.5 gallons of Portland cement weighing 15.3 lbs. for at least 2 minutes. Rubber tires were shredded to a size range of approximately ½″ to 2 inches wherein the steel from the tires was removed but nylon from the tires remained in the shredded rubber tire pieces. Seventy-five (75) lbs. of the shredded tire pieces were added to the mix, and the resulting mixture was mixed for another five (5) minutes. Thereafter, 2 gallons of water were added to wet the dry shredded rubber tire mixture. When the mixture was fully wetted, the mixture was poured into molds sized 12 inches by 12 inches and having a thickness of around 4 inches to which ½ inch of grout had previously been added. The molds were filled and a lid closed over the mold and left to dry for 5 days at room temperature in the ambient environment. Once the mixture was dry in each mold, the resulting environmentally responsible insulated construction blocks were removed and then attached to the metal or concrete deck of the top of a building using high strength self-setting grout. A waterproof membrane was disposed on an adhesive or glue layer that was disposed on the top surfaces of the environmentally responsible insulated construction blocks. Thereafter a plurality of the environmentally responsible insulated construction blocks prepared as in Example 2 were adhered to the waterproof membrane in a green roofing application.
The environmentally responsible insulated construction blocks for green decking application as prepared in EXAMPLE 1 were tested alone and as attached to various roofing systems, and also environmentally responsible insulated construction blocks for green roofing application as described in Example 4 for the following: wind uplift testing; Class A fire rating; field withdrawal resistance testing; metal edge attachment testing; sound transmission loss; compression testing; steady-state thermal transmission properties; flow of water; age testing; and recycled content, as well as physical properties testing. The results are presented below.
TAS 114-95 Wind Uplift Testing.
UL 790 Class a Fire Rating.
TAS-105 Field Withdrawal Resistance Testing.
TAS-111(B)-95 Metal Edge Attachment Testing.
ASTM E90-09 Sound Transmission Loss.
ASTM C39 Compression Testing.
Environmentally responsible insulated construction block for green roofing application
ASTM C-518 Standard Test Method of Steady-State Thermal Transmission Properties by Means of Heat Flow Meter Apparatus.
UL Flow Rate of Water Passing Thru Environmentally Responsible Insulated Construction Blocks for Green Decking Application.
Age Testing.
Physical Properties Testing.
Recycled Content.
Maximum Design Pressure (Steel Deck).
A plurality of environmentally responsible insulated construction blocks for green roofing application having a ¼″ slope was adhered using AH-160 propack adhesive continuous 1½ inch beads spaced 6″ O.C. to min. 22 GA 1.5″ Type B galvanized steel deck. An 8000 psi structural concrete surface was adhered to the top surface of the plurality of environmentally responsible insulated construction blocks for green roofing application to which was applied a NOA-approved fully adhered roofing system. The maximum design pressure measured was −292.5 psf.
The environmentally responsible insulated construction blocks for green decking application as prepared in Example 3 were tested for Class A fire rating. The results are presented below.
UL 790 Class a Fire Rating.
A structure having four walls and a roof was built using the coated shredded rubber tire mixture of EXAMPLE 4. A scarified concrete slab was poured as the base of the structure. Molds for walls of about twelve (12) inches thickness were constructed and a layer of grout was placed over the scarified concrete slab at the base of the molds. Metal rods were inserted from the base to extend beyond the tops of the molds. A plywood sheet was placed on top of the poured coated shredded rubber tire mixture to provide compression to the mixture while it dried. A roof structure was built on the top of the walls using plywood. A layer of the coated shredded rubber tire mixture twelve (12) inches thick was poured on the plywood layer to form the roof. The roof was thereafter coated with stucco and roof paint. A plurality of rods extended upward from the plywood layer to allow for a top to be placed over the poured coated shredded rubber tire mixture to compress it while it dried.
The structure comprising was tested and found to have a load bearing capacity of 20,106 lbs. During testing, the structure sagged ¼ inch due to weight load but the sag decreased to ⅛ inch when the weight was removed. The structure was measured to have an R-value of 15.72 with a recycled content of about 93.83%.
Environmentally responsible insulated construction blocks manufactured for green roofing application as described in Example 4 were tested, accepted and approved by the Miami-Dade County (Florida) Dept. of Regulatory and Economic Resources (RER), Board and Code Administration as Roof Edge Termination Systems in compliance with the Florida Building Code including the High Velocity Hurricane Zone of the Florida Building Code where the pressure requirements as determined by applicable building code do not exceed the design pressure values listed. Blocks 2 ft. by 2 ft. by 2 in. and 2 ft. by 1 ft. by 2 in. in size were tested as a substrate for a Grade 40, 24 gauge continuous galvanized steel cleat with a Grade 40, 24 gauge galvanized steel continuous drip edge/gravel stop both installed with OMG Headlock SP #14×1⅝ or 3½ in. length fasteners at 9 in. on center into the blocks. The blocks were to be installed onto concrete or steel deck using 1½ in. continuous beads of ICP Adhesives Polyset AH-160 spaced 6 in. apart. Under these conditions, the maximum design pressure was found to be −300 psf (horizontal).
In the foregoing description, the invention has been described with reference to specific exemplary embodiments thereof. It will be apparent to those skilled in the art that a person understanding this invention may conceive of changes or other embodiments or variations, which utilize the principles of this invention without departing from the broader spirit and scope of the invention. The specification and drawings are, therefore, to be regarded in an illustrative rather than a restrictive sense.
| Number | Date | Country | |
|---|---|---|---|
| 62506849 | May 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16059573 | Aug 2018 | US |
| Child | 16221687 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15981189 | May 2018 | US |
| Child | 16059573 | US | |
| Parent | PCT/US2018/032905 | May 2018 | US |
| Child | PCT/US2015/061055 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16221687 | Dec 2018 | US |
| Child | 16594909 | US | |
| Parent | PCT/US2015/061055 | Nov 2015 | US |
| Child | 15981189 | US |