Environmentally safe alkylation of aliphatic and aromatic hydrocarbons with olefins using solid HF-equivalent catalysts

Information

  • Patent Grant
  • 6677269
  • Patent Number
    6,677,269
  • Date Filed
    Thursday, May 17, 2001
    23 years ago
  • Date Issued
    Tuesday, January 13, 2004
    20 years ago
  • Inventors
  • Examiners
    • Bell; Mark L.
    • Pasterczyk; J.
    Agents
    • Pennie & Edmonds LLP
Abstract
Solid polymeric onium poly(hydrogen fluoride) complexes disclosed herein can be used for alkylating aliphatic or aromatic hydrocarbons with olefins. These solid polymeric complexes can be formed by a process of contacting a source of hydrogen fluoride with a homopolymer or copolymer containing in at least one repeat unit, a nitrogen, phosphorus, or sulfur atom, capable of forming an onium fluoride moiety upon reaction or complexation with the hydrogen fluoride source.
Description




FIELD OF THE INVENTION




The present invention relates to a method for alkylating aliphatic or aromatic hydrocarbons with olefins using solid hydrogen fluoride-equivalent catalysts. The process is environmentally safe and represents improved and simplified technology easily adaptable to presently operating commercial hydrogen fluoride alkylation plants.




BACKGROUND OF THE INVENTION




Anhydrous hydrogen fluoride is widely used as a catalyst in the petrochemical industry. It is particularly effective as alkylation catalyst, such as in the production of high-octane gasoline via isoalkane-olefin alkylation. Similarly, detergent alkylates are produced by alkylating aromatic compounds, such as benzene. These technologies have achieved significant application in industry. At the same time, because of the volatility of hydrogen fluoride (HF; boiling point of about 19.6° C.), the environmental and health dangers posed by accidental release from industrial reactors or storage tanks is increasingly unacceptable. To solve this problem, industry has reverted either to the use of sulfuric acid, a less suitable but also less volatile alkylation catalyst, or has operated in a manner that decreases or minimizes the volatility of hydrogen fluoride.




For example, U.S. Pat. No. 5,073,674 discloses the utility of liquid onium polyhydrogen fluoride complexes, containing about 70% to 95% by weight of hydrogen fluoride, as alkylation catalysts. These liquid catalysts, which are not polymer-based, typically have a relatively low molecular weight, optionally contain an additional Lewis acid halide or strong Bronstead acid co-catalyst.




Certain polyhydrogen fluoride complexes, such as polyhydrogen fluoride complexes of pyridine and its derivatives, are liquids which are used as fluorinating agents. For example, anhydrous hydrogen fluoride in the presence of pyridine has been used for fluorinating steroids (R. R. Hirschmann et al.,


J. Am. Chem. Soc.,


1956, 78, 4956). The 30% pyridine-70% hydrogen fluoride system (PPHF) was found to be particularly useful for this reaction (C. G. Bergstrom et al.,


J. Org. Chem.,


1963, 28, 2633) and subsequently was developed (Olah et al.,


J. Org. Chem.,


1979, 44, 3872, and references cited therein) as a general fluorinating agent. The PPHF reagent and subsequently developed related reagents (T. Fukuhara et al.,


Nippon Kagaku Kaish.,


1985, p. 1951) are, however, only suitable as convenient fluorinating agents and are not catalysts for alkylation.




Solid poly-4-vinylpyridinium polyhydrogen fluoride has also previously been utilized for fluorination (Olah et al.,


Synthesis,


1993, p. 693). This solid fluorination agent, which contains only 35% to 60% hydrogen fluoride by weight is not effective as an alkylation catalyst. Acidic metal hydrogen fluorides, such as those of the type M


+


HF


2







, as well as most other salts of hydrogen fluoride, also fail to catalyze the alkylation of hydrocarbons.




SUMMARY OF THE INVENTION




This invention is based, in part, on the discovery that certain solid polymeric onium polyhydrogen fluoride complexes can be used to catalyze or facilitate the alkylation of aliphatic or aromatic hydrocarbons with olefins.




One embodiment of the invention relates to a method of alkylating an aliphatic or aromatic hydrocarbon with an olefin, which comprises contacting the aliphatic or aromatic hydrocarbon with the olefin in the presence of a solid polymeric onium polyhydrogen fluoride complex under conditions sufficient for the alkylation of the aliphatic or aromatic hydrocarbon.




Advantageously, polymeric onium polyhydrogen fluoride complexes used in the invention are solid. In a preferred embodiment, the polymeric onium polyhydrogen fluoride complex contains from about 70% to 95% by weight hydrogen fluoride. In another preferred embodiment, the polymeric onium polyhydrogen fluoride complex contains in some or all of its repeat units a nitrogen, phosphorus, or sulfur atom capable of forming an onium fluoride moiety upon reaction or complexation with hydrogen fluoride.




In another embodiment, the method may further comprise contacting the aliphatic or aromatic hydrocarbon and the olefin with a Lewis acid halide or a strong Bronstead acid. When added, the co-catalyst is preferably present in an amount from about 0.1% to 10% by weight of the polymeric onium polyhydrogen fluoride complex.




Another embodiment of the present invention relates to a process for forming a solid polymeric onium polyhydrogen fluoride complex, which comprises contacting a homopolymer or copolymer including, in at least one repeat unit, an atom, preferably nitrogen, phosphorus, or sulfur, capable of forming an onium fluoride moiety upon reaction or complexation with a source of hydrogen fluoride, preferably anhydrous hydrogen fluoride, under conditions sufficient to form the solid polymeric onium polyhydrogen fluoride complex.




Still another embodiment relates to a process for removing hydrogen fluoride from an alkylation product of the invention by contacting it with a solid homopolymer or copolymer including, in at least one repeat unit, an atom, preferably nitrogen, phosphorus, or sulfur, capable of forming an onium fluoride moiety upon reaction or complexation with a source of hydrogen fluoride, under conditions sufficient for the solid homopolymer or copolymer to complex hydrogen fluoride. In a preferred embodiment, the alkylation process does not necessitate any caustic or aqueous washing steps.




DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS




The invention is based on the unexpected discovery that certain environmentally-friendly, solid polymeric onium polyhydrogen fluoride complexes can, in fact, catalyze the alkylation of aliphatic or aromatic hydrocarbons with olefins.




As used herein, the term “solid polymeric onium polyhydrogen fluoride complex” refers to any solid polymeric or oligomeric material containing in some or all of its repeat units an atom, preferably nitrogen, phosphorus, or sulfur, more preferably nitrogen, capable of forming an onium (e.g., preferably ammonium, phosphonium, or sulfonium) fluoride moiety with hydrogen fluoride. Suitable solid polymeric onium polyhydrogen fluoride complexes include, but are not limited to, complexes and/or reaction products of hydrogen fluoride and polymers such as, but not limited to, poly(vinylpyridine) and poly(aminomethyl styrene), as shown below:











as well as mixtures or copolymers containing same, wherein “n” denotes the number of repeat units. With appropriate amounts of anhydrous hydrogen fluoride, the polymers or oligomers can form corresponding stable poly(hydrogen fluoride) salts. Examples of the prepared solid polyhydrogen fluoride complexes include, but are not limited to, polyvinylpyridinium polyhydrogen fluoride (PVPHF) or poly(4-aminomethyl)styryl polyhydrogen fluoride (PAMSHF), as shown below:











as well as mixtures or copolymers containing same, wherein m is such that the resultant polymeric onium polyhydrogen fluoride complex can catalyze an alkylation reaction. The range of values for m for each polymeric onium polyhydrogen fluoride complex may depend on the repeat unit weight of the non-complexed polymers, and is preferably such that the solid polymeric onium polyhydrogen fluoride complex contains from about 70 to about 95 weight percent hydrogen fluoride, with the polymeric component being present in an amount from about 30 to about 5 weight percent. For example, m can be from about 5 to about 200, or from about 10 to about 100. The solid polymeric onium polyhydrogen fluoride complexes thus formed can serve as solid equivalents of anhydrous hydrogen fluoride, facilitating alkylation reactions at their surfaces and/or providing hydrogen fluoride in low concentrations to hydrocarbons with which they come in contact.




The use of solid polymeric onium polyhydrogen fluoride complexes to effect alkylation has other significant advantages. For example, their reduced volatility reduces accidental atmospheric release of gaseous hydrogen fluoride. The polymeric onium polyhydrogen fluoride complexes can also be efficiently diluted with water and neutralized with caustic treatment, without forming dangerous aerosols characteristic of gaseous hydrogen fluoride release. Also, because of their low vapor pressure (e.g., below about 50° C.), the operating pressures in alkylation reactors and storage tanks can be substantially decreased.




A first embodiment of the invention encompasses a method of alkylating an aliphatic or aromatic hydrocarbon which includes contacting the aliphatic or aromatic hydrocarbon with an olefin in the presence of a solid polymeric onium polyhydrogen fluoride complex under conditions sufficient for the alkylation of the aliphatic or aromatic hydrocarbon. As used herein, the term “aliphatic hydrocarbon” encompasses saturated hydrocarbons, preferably isoalkanes. Isoalkanes according to the invention preferably contain from about 4 to about 10 carbon atoms (C


4


-C


10


). As used herein, the term “aromatic hydrocarbon” encompasses poly-and mono-cyclic aromatic hydrocarbons, such as benzene. Aromatic hydrocarbons according to the invention preferably contain from about 6 to about 20 carbon atoms (C


6


-C


20


). In one method of this embodiment, the reaction product is a high-octane alkylate. In another method, the reaction product is a detergent alkylate.




Examples of olefins used in alkylating aliphatic hydrocarbons include, but are not limited to, ones that contain from three to eight carbon atoms (C


3


-C


8


), and preferentially ones that contain from four to six carbon atoms (C


4


-C


6


). Examples of olefins used in alkylating aromatic hydrocarbons include, but are not limited to, ones that contain from about two to about twenty carbon atoms (C


2


-C


20


).




In a preferred method, the alkylation reaction is conducted at a temperature of from about 0° C. to about 50° C. and at a pressure of from about atmospheric to about 800 psi. Advantageously, the alkylation reaction can be conducted batchwise or under continuous flow conditions, with an aliphatic or aromatic hydrocarbon to olefin molar ratio of from about 2:1 to about 20:1. Under batchwise conditions, higher yields can be obtained by adding the olefin in portions to the aliphatic or aromatic hydrocarbon to be alkylated and the solid polymeric onium polyhydrogen fluoride complex. Under flow conditions, the olefin and the aliphatic or aromatic hydrocarbon to be alkylated, in the proper ratios, are passed through solid polymeric onium polyhydrogen fluoride resins.




In specific methods of the invention, improved yields can be obtained by adding a co-catalyst to the reaction mixture in an amount of about 0.1 to about 10 weight percent of the hydrogen fluoride contained in the solid polymeric onium polyhydrogen fluoride complex being used. Examples of co-catalysts include, but are not limited to, Lewis acid halides such as boron tristriflate, strong Bronstead acids such as fluorosulfuric or perfluoroalkanesulfonic acid, and mixtures thereof.




In a preferred method of the invention, a saturated, branched, aliphatic hydrocarbon, e.g., isobutane, is alkylated with an olefin, e.g., isobutylene, in the presence of a solid polymeric onium polyhydrogen fluoride complex at a temperature of from about 0° C. to about 50° C. and a pressure of from about atmospheric to about 800 psi for a time sufficient to form a high-octane alkylate. In another preferred method, an aromatic hydrocarbon, e.g., benzene, is alkylated with an olefin, e.g., dodecene, to form a detergent alkylate, e.g., dodecylbenzene, which upon sulfonation under sufficient conditions can yield a widely used detergent.




Preferably, alkylation reactions according to the invention include reaction of an isoalkane with an olefin to give high-octane alkylate products. Examples of high-octane alkylate products have from about 6 to about 12 carbons (C


6


-C


12


) and can be useful or present in gasoline. In a particularly preferred method, isobutane or isopentane is reacted with a C


4


-C


5


olefin, such as isobutylene. Alkylation of aromatic hydrocarbons, such as benzene, with liquid olefins having about 10 to about 20 carbon atoms (C


10


-C


20


) can result in detergent alkylates. Whereas these reactions are presently practiced commercially using anhydrous hydrogen fluoride, the present invention can particularly minimize or eliminate environmental and health hazards associated with the use of volatile and toxic anhydrous hydrogen fluoride in industrial alkylation plants. The polymers used in the invention can immobilize volatile anhydrous hydrogen fluoride by reacting therewith to form solid polymeric onium polyhydrogen fluoride complexes. Thus the resulting complexes exhibit substantially decreased volatility and aerosol formation compared to highly toxic hydrogen fluoride in case of accidental release to the atmosphere.




Methods of the invention are readily adaptable to use in existing plant equipment. Their industrial use should not involve costly process changes or major changes in operating technology. One particular further practical advantage of the invention is that the processing of the alkylate reaction products can be performed in a greatly simplified and low cost way.




The invention optionally provides that the alkylates can be treated without any washing or caustic solution, e.g., by passing the alkylates through a bed or column filled with a fresh basic polymer, e.g., PVP or PAMS. These basic polymers can remove hydrogen fluoride from the alkylates through complexation to form the corresponding solid polymeric onium polyhydrogen fluoride salts. In this way, hydrogen fluoride removal and solid polymeric onium polyhydrogen fluoride complex regeneration can be achieved simultaneously.











EXAMPLES




The following are examples of methods and materials which can be used according to the present invention, and are not to be construed as limiting the scope of the invention in any way.




Example 1




A solid polymeric polyhydrogen fluoride catalyst was prepared by placing 19.5 g of poly (4-vinylpyridine) (PVP, approximately 2% crosslinked) into a polyethylene bottle, cooling it to about −78° C., and adding about 80.5 g of anhydrous hydrogen fluoride in small portions, thus forming the poly (4-vinylpyridinium) polyhydrogen fluoride (PVPHF) catalyst.




After warming to room temperature, the PVPHF catalyst was then added into a 600 mL, mechanically stirred stainless steel or Monel autoclave, to which then about 220 mL of liquid isobutane and about 20 mL of isobutylene was fed. The reactor was stirred while keeping the temperature at about 35° C. to 40° C. for about 30 minutes. The reactor was cooled with ice water and depressurized by venting of excess isobutane. The alkylate product of the isobutane-isobutylene reaction was then passed through a column containing fresh PVP to absorb any excess HF. The alkylate product was distilled and analyzed by GC-MS (a gas chromatography apparatus coupled to a mass spectrometer). It gave approximately a 70% yield with a research octane number (RON) of about 90. Of that yield, the alkylate product was found to contain about 63% of octane isomers, with 2,2,4-trimethylpentane (TMP) amounting to 36% of the alkylate product. The C


9


and higher alkylate fractions amounted to about 10-14% of the product.




Example 2




The isobutane-isobutylene alkylation reaction was carried out as in Example 1, but poly (4-aminomethyl styrene) (PAMS) was substituted for PVP. The catalyst reaction of Example 2 involved a similar ratio of amino groups to anhydrous hydrogen fluoride added as in Example 1. A 65% yield of alkylate product was obtained with a RON of about 91.5. Of that yield, the alkylate product was found to contain about 42% 2,2,4-TMP. The C


9


and higher alkylate fractions amounted to about 10-16% of the product.




Example 3




The isobutane-isobutylene alkylation reaction was carried out as in Example 2, except that the isobutylene was incrementally fed in small portions to the reactor containing the isobutane and the polymeric onium polyhydrogen fluoride catalyst. The alkylate product obtained in this manner generally contained less than about 10% of C


9


and higher alkylate fractions.




Examples 4-5




For Examples 4-5, each polymeric onium polyhydrogen fluoride catalyst, as prepared in Examples 1-2, respectively, was loaded in to a reaction vessel, along with about 200 mL benzene and about 40 mL of a liquid olefin having from about 12 to 18 carbons (or a mixture of olefins obtained by dehydrogenation of a corresponding C


12


to C


18


alkane mixture). The reaction vessel was stirred at about 60° C. to 70° C. for about 1 hour. After removal of hydrogen fluoride from the alkylate by treatment with the corresponding fresh basic polymer, the corresponding detergent alkylates were obtained in approximately 85% to 90% yield.




The embodiments of the invention described above are intended to be merely exemplary, and those skilled in the art will recognize, or will be able to ascertain using no more than routine experimentation, numerous equivalents of the specific materials and procedures described herein. All such equivalents are considered to be within the scope of the invention and are encompassed by the appended claims.



Claims
  • 1. A process for forming a solid polymeric onium poly(hydrogen fluoride) complex, which comprises contacting a homopolymer or copolymer with a source of hydrogen fluoride under conditions sufficient to form poly(vinylpyridinium) poly(hydrogen fluoride) or poly(ammoniomethyl)styrl poly(hydrogen fluoride), wherein the poly(vinylpyridinium) poly(hydrogen fluoride) or poly(ammoniomethyl)styrl poly(hydrogen fluoride) comprises a plurality of onium fluoride moieties and comprises from about 70 to about 95 weight percent hydrogen fluoride.
  • 2. A solid polymeric onium poly(hydrogen fluoride) complex formed by the process of claim 1 that is capable of facilitating alkylation of an aliphatic or aromatic hydrocarbon with an olefin.
  • 3. The solid polymeric onium poly(hydrogen fluoride) complex of claim 2, wherein the number of hydrogen fluoride groups complexed to each onium fluoride moiety is from about 5 to about 200.
  • 4. The solid polymeric onium poly(hydrogen fluoride) complex of claim 2, wherein the number of hydrogen fluoride groups complexed to each onium fluoride moiety is from about 10 to about 100.
  • 5. The process of claim 1, wherein the source of hydrogen fluoride is anhydrous hydrogen fluoride.
  • 6. The solid polymeric onium poly(hydrogen fluoride) complex formed by the process of claim 1, wherein the number of hydrogen fluoride groups complexed to each onium fluoride moiety is from about 5 to about 200.
  • 7. The solid polymeric onium poly(hydrogen fluoride) complex formed by the process of claim 1, wherein the number of hydrogen fluoride groups complexed to each onium fluoride moiety is from about 10 to about 100.
  • 8. A solid polymeric onium poly(hydrogen fluoride) complex comprising poly(vinylpyridinium) poly(hydrogen fluoride) or poly(ammoniomethyl)stylrl poly(hydrogen fluoride) which is capable of facilitating alkylation of an aliphatic or aromatic hydrocarbon with an olefin, wherein the solid polymeric onium poly(hydrogen fluoride) complex comprises from about 70 to about 95 weight percent hydrogen fluoride.
  • 9. The solid polymeric onium poly(hydrogen fluoride) complex of claim 8, wherein the number of hydrogen fluoride groups complexed to each onium moiety is from about 5 to about 200.
  • 10. The solid polymeric onium poly(hydrogen fluoride) complex of claim 8, wherein the number of hydrogen fluoride groups complexed to each onium moiety is from about 10 to about 100.
  • 11. The solid polymeric onium poly(hydrogen fluoride) complex of claim 8, consisting essentially of poly(ammoniomethyl)styryl poly(hydrogen fluoride) that comprises a plurality of ammoniomethylstyryl fluoride moieties.
  • 12. The solid polymeric onium poly(hydrogen fluoride) complex of claim 11, wherein the number of hydrogen fluoride groups complexed to each ammoniomethylstyryl fluoride moiety is from about 5 to about 200.
  • 13. The solid polymeric onium poly(hydrogen fluoride) complex of claim 11, wherein the number of hydrogen fluoride groups complexed to each ammoniomethylstyryl fluoride moiety is from about 10 to about 100.
US Referenced Citations (7)
Number Name Date Kind
5073674 Olah Dec 1991 A
5118804 Defaye et al. Jun 1992 A
5663474 Pham et al. Sep 1997 A
6177058 Singh et al. Jan 2001 B1
6200924 Lloyd et al. Mar 2001 B1
6281309 Babcock et al. Aug 2001 B1
6395673 Harmer et al. May 2002 B1
Non-Patent Literature Citations (6)
Entry
US 2002/0137626 A1, U.S. Pre-Grant publication to Harmer et al., published Sep. 2002.*
R. Hirschmann et al., “The Reaction of Epoxides with Anhydrous Hydrogen Fluoride in the Presence of Organic Bases. The Preparation of 9α-Fluoro-4-pregnene-11β,17α,21-Triol 3,20-Dione 21-Acetate and Its 1-Dehydro Analog”, J. Am. Chem. Soc., 1956, 78, 4956.
C.G. Bergstrom et al., “9α-Fluoro-11-deoxy Steroids”, J. Org. Chem., 1963, 28, 2633.
Olah et al., “Synthetic Methods and Reactions. 63. Pyridinium Poly (hydrogren fluoride) (30% Pyridine-70% Hydrogen Fluoride): A Convenient Reagent for Organic Fluorination Reactions”, J. Org. Chem., 1979, 44, 3872.
T. Fukuhara et al., Nippon Kagaku Kaish., 1985, p. 1951.
G. Olah et al., “Poly-4-vinylpyridinium Poly (Hydrogen Fluroide): A Solid Hydrogen Fluoride Equivalent Reagent”, Synthesis, 1993, 693.