The present invention relates to an enzyme electrode.
There is known an enzyme electrode including an electrode as a base material and a detection layer in which an enzyme and conductive particles are immobilized on the surface of the electrode using a crosslinking agent or a binder. The enzyme electrode has a structure that takes electrons generated by an enzyme reaction out of the electrode.
Generally, in order to properly hold an enzyme and conductive particles which are contained in the detection layer and to secure proper adhesion of the detection layer to a base material, it is conceived to increase the concentration of a crosslinking agent or a binder. However, when the concentration of the crosslinking agent or the binder is simply increased, the formation of a good electron transport pathway in the detection layer is prevented, and the response sensitivity of the enzyme electrode tends to decrease in proportion to the concentration of the crosslinking agent or the binder.
Further, in recent years, there has been a tendency that an enzyme electrode is reduced in size, and an enzyme electrode that maintains a proper immobilization state of a detection layer to a base material with a small amount of binder and also has good response sensitivity and reproducibility has been desired.
One aspect of the present invention has been made in view of the above circumstances, and is directed to provide an enzyme electrode having a detection layer which is properly immobilized to a base material and can obtain proper response sensitivity.
In order to achieve an object described above, the one aspect of the present invention applies configurations below. Namely, the one aspect of the present invention is an enzyme electrode. The enzyme electrode includes an electrode and a detection layer, the detection layer including an enzyme, conductive particles, and a non-conductive polymer, the non-conductive polymer being linked to at least one of at least a portion of the enzyme and at least a portion of the conductive particles by a linking chain containing nitrogen or oxygen, and the non-conductive polymer having a region of positive correlation between a concentration of the non-conductive polymer and a response sensitivity of the enzyme electrode.
In the one aspect, the linking chain containing nitrogen (N) or oxygen (O) is e.g. a covalent bond. The covalent bond is e.g. an amide ester bond. As the bond chain other than the amide ester bond, there are peptide bond, carbodiimide and azomethine. Further, the amide ester bond in the one aspect may be derived from an oxazoline group. The oxazoline group in the one aspect may be ontained in an amount of 4.5 mmol/g based on the non-conductive polymer.
In the one aspect, the conductive particles may be selected from at least one of carbon and metal. An average particle size of the conductive particles may be 100 nm or less. A specific surface area of the conductive particles may be 200 m2/g or more. The conductive particles may contain at least one of a carboxyl group, an amino group, an aldehyde group, a hydroxyl group, and a phenyl group. Further, the conductive particles may include one or both of fine particle types selected from carbon nanotube and fullerene.
In the one aspect, a weight ratio among the enzyme, the conductive particles, and the non-conductive polymer may be 0.023 to 2.0:0.1 to 1.0:2.5 to 10.0.
One of other aspects of the present invention is a biosensor including an enzyme electrode including an electrode and a detection layer, wherein the detection layer comprises an enzyme, conductive particles, and a non-conductive polymer, the non-conductive polymer is linked to at least one of at least a portion of the enzyme and at least a portion of the conductive particles by a linking chain containing nitrogen or oxygen, and the non-conductive polymer has a region of positive correlation between a concentration of the non-conductive polymer and a response sensitivity of the enzyme electrode.
One of other aspects of the present invention is an electronic apparatus including an enzyme electrode comprising an electrode and a detection layer, wherein the detection layer comprises an enzyme, conductive particles, and a non-conductive polymer, the non-conductive polymer is linked to at least one of at least a portion of the enzyme and at least a portion of the conductive particles by a linking chain containing nitrogen or oxygen, and the non-conductive polymer has a region of positive correlation between a concentration of the non-conductive polymer and a response sensitivity of the enzyme electrode.
One of other aspects of the present invention is an apparatus including an enzyme electrode and a feed section configured to supply, to a load, a current generated by an enzyme reaction by energization to the enzyme electrode, the enzyme electrode including an electrode and a detection layer, wherein the detection layer comprises an enzyme, conductive particles, and a non-conductive polymer, the non-conductive polymer is linked to at least one of at least a portion of the enzyme and at least a portion of the conductive particles by a linking chain containing nitrogen or oxygen, and the non-conductive polymer has a region of positive correlation between a concentration of the non-conductive polymer and a response sensitivity of the enzyme electrode. The other aspects of the present invention may include an electronic apparatus including the above-described biosensor and an electronic apparatus including the above-described apparatus.
One of other aspects of the present invention is a method of producing an enzyme electrode, comprising the steps of: preparing a reagent solution containing an enzyme, conductive particles, and a non-conductive polymer; applying the reagent solution to an electrode; and drying the applied reagent solution to thereby form a detection layer on the electrode, the detection layer comprising the enzyme, the conductive particles, and the non-conductive polymer, and the non-conductive polymer being linked to at least one of at least a portion of the enzyme and at least a portion of the conductive particles by a linking chain containing nitrogen or oxygen, wherein the non-conductive polymer has a region of positive correlation between a concentration of the non-conductive polymer and a response sensitivity of the enzyme electrode. A concentration of the non-conductive polymer added during the preparation of the reagent solution is 0.25% to 10%.
One of other aspects of the present invention is an enzyme electrode including an electrode and a detection layer, wherein the detection layer comprises an enzyme, conductive particles, and a polymer that forms an amide ester bond with at least one of at least a portion of the enzyme and at least a portion of the conductive particles.
According to one aspect of the present invention, an enzyme electrode having a detection layer which is properly immobilized to a base material and can obtain proper response sensitivity may be provided.
Hereinafter, an enzyme electrode as an embodiment of the present invention will be described with reference to drawings. Embodiments described below are for illustration purposes, and the present invention is not limited to the constitution of the following embodiments.
[Constitution of Enzyme Electrode]
<Electrode>
The electrode 1 is formed of a metallic material such as gold (Au), platinum (Pt), silver (Ag), and palladium, or a carbon material such as carbon. The electrode 1 is formed, for example, on an insulating substrate 3 as illustrated in
<Detection Layer>
That is, the detection layer 2 contains enzymes (enzyme molecules) 5, a plurality of conductive particles 6, and a plurality of non-conductive polymers (amide esters 9) that form an amide ester bond with at least one of at least a portion of enzymes 5 and at least a portion of the plurality of conductive particles 6.
The amide ester 9 is linked to the enzyme 5 or the conductive particles 6 to thereby result in a state where the enzyme 5 and the conductive particles 6 are strongly held or supported in the detection layer 2. Further, the amide ester bond leads to a state where the enzyme 5 and the conductive particles 6 are uniformly distributed in the detection layer 2. Thereby, a proper number of electron transport pathways are formed in which electrons generated by an enzyme reaction reach the electrode 1 through the conductive particles 6. Consequently, an improvement in the response sensitivity of an enzyme electrode is achieved. On the other hand, the detection layer 2 indicates proper adhesion to the electrode 1.
<<Enzyme>>
The enzyme 5 is, for example, an oxidoreductase. For example, the enzyme 5 is glucose dehydrogenase (GDH). As the GDH, it is preferred to apply flavin adenine dinucleotide-dependent glucose dehydrogenase (FADGDH) which does not need an electron-transfer mediator. Further, an oxidoreductase containing a cytochrome can be applied as the enzyme 5. Examples include glucose dehydrogenase containing cytochrome (Cy-GDH), D-fructose dehydrogenase, and cellobiose dehydrogenase.
<<Conductive Particles>>
Metal particles such as gold, platinum, silver, and palladium or a higher-order structure formed from carbon can be applied as the conductive particles 6. The higher-order structure can include one or more fine particle types (carbon fine particles) selected, for example, from conductive carbon black, Ketjen Black (registered trademark), carbon nanotube (CNT), and fullerene. One of the metals and carbons as described above can be selected as the conductive particles 6. Further, the conductive particles 6 can contain at least one of a carboxyl group, an amino group, an aldehyde group, a hydroxyl group, and a phenyl group as a functional group for crosslinking.
Note that the surface of the detection layer 2 may be covered with an outer-layer film made of cellulose acetate (CA) and the like.
<<Weight Ratio Among Enzyme, Conductive Particles, and Binder and the Like>>
The weight ratio among an enzyme, conductive particles, and a binder which constitute the detection layer 2 is preferably, for example, enzyme:conductive particles:binder=(0.023 to 2.0):(0.1 to 1.0):(2.5 to 10.0). Further, the conductive particles have an average particle size of, for example, 100 [nm] or less and a specific surface area of preferably, for example, 200 [m/g] or more.
[Method for Preparing Enzyme Electrode]
Hereinafter, the enzyme electrode 10 as described above is prepared, for example, as follows. Specifically, a metal layer which functions as an electrode 1 is formed on one side of an insulating substrate 3. For example, a metal layer having a desired thickness (for example, about 30 nm) is formed by depositing a metallic material by physical vapor deposition (PVD, for example, sputtering) or chemical vapor deposition (CVD) on one side of an insulating substrate 3 in a film form having a predetermined thickness (for example, about 100 μm). An electrode layer formed of a carbon material can also be formed instead of the metal layer.
Next, a detection layer 2 is formed on an electrode 1. Specifically, an electrode solution containing conductive particles 6, an enzyme 5, and a non-conductive high polymer containing an oxazoline group as a binder is prepared. The electrode solution is dropped on the surface of the electrode 1. The electrode solution is dried and solidified on the electrode 1, thereby capable of obtaining the enzyme electrode 10 in which the detection layer 2 is formed on the electrode 1.
Hereinafter, Examples of the enzyme electrode will be described.
<Formulation of Detection Layer>
First, electrode solutions (reagent solutions) according to Example 1, Example 2, and Comparative Example each containing conductive particles, an enzyme, and a binder were prepared. In each of Example 1, Example 2, and Comparative Example, Ketjen Black (registered trademark, hereinafter represented by “KJB”) was used as the conductive particles, and Cy-GDH was used as the enzyme.
On the other hand, in Example 1, EPOCROS ((registered trademark), hereinafter represented by “EPC”) which is one of highpolymers containing an oxazoline group which is a covalent linking chain containing nitrogen (N) or oxygen (O) was used as a binder. In Example 2, poly-(2-ethyl-2-oxazoline) (hereinafter represented by “PEO”) which is one of highpolymers containing an oxazoline group which is a covalent linking chain containing nitrogen (N) or oxygen (O) was used as a binder. Further, in Comparative Example, VYLONAL (registered trademark) was used as a binder. The final concentration of the electrode solution in Example 1, Example 2, and Comparative Example is as follows. The high polymer containing an oxazoline group which is a covalent linking chain containing nitrogen (N) or oxygen (O) is an example of “non-conductive polymers.”
As Example 1, four types of electrode solutions (samples) each having an EPC concentration of 0.25 [wt %], 0.5 [wt %], 1.0 [wt %], or 3.0 [wt %] were prepared.
As Example 2, four types of electrode solutions (samples) each having a PEO concentration of 0.25 [wt %], 0.5 [wt %], 1.0 [wt %], or 3.0 [wt %] were prepared.
As Comparative Example, four types of electrode solutions (samples) each having an MD-1200 concentration of 0.25 [wt %], 0.5 [wt %], 1.0 [wt %], or 3.0 [wt %] were prepared.
Note that the KJB used in Example 1, Example 2, and Comparative Example had an average particle size of 100 [nm] or less and a specific surface area of 200 [m2/g] or more. Further, the proportion of the oxazoline group in the molecule in Example 1 was 4.5 [mmol/g].
<A. Response Sensitivity Test>
<<Preparation of Enzyme Electrode>>
A base material having a gold (Au) metal layer (electrode) formed by sputtering on the surface of a polyether imide (PEI) as an insulating substrate was prepared, and an electrode solution (a sample, a reagent solution) was dropped on the surface of the electrode under a condition of 10.0 μL/cm2 per unit area (cm2) of the electrode. Then, the electrode solution on the surface of the electrode was air dried in an atmosphere of 23° C. and 40% RH. In this way, an enzyme electrode was obtained in which a detection layer in which an enzyme and conductive particles were immobilized with each binder as described above was formed on the surface of the electrode. The detection layer contains a non-conductive polymer having a covalent linking chain containing nitrogen (N) or oxygen (O).
<<Method for Measuring Response Sensitivity>>
Next, an example of a method for measuring the glucose concentration using an enzyme electrode will be described. The response sensitivity to glucose was measured by chronoamperometry in which a potential difference of 400 mV is applied to an electrode system, as a measuring method.
First, a 0.1 M phosphate buffer (pH 7.0) was prepared as a measuring liquid, and kept at 37° C. Next, an enzyme electrode, in which a platinum electrode is used as a counter electrode and an Ag/AgCl electrode is used as a reference electrode, was electrically connected to a potentiostat and immersed in a 0.1 M phosphate buffer. Then, constant voltage (400 mV vs Ag/AgCl) was applied to a working electrode.
For the measurement of glucose concentration, a current value (nA) at a final glucose concentration of 0 mg/dL was first measured, and current values at 25 mg/dL, 50 mg/dL, 150 mg/dL, and 250 mg/dL were then continuously measured while continuously dropping a 2 M glucose solution. A current value corresponds to response sensitivity.
<<Test Results>>
The results of the measurement of glucose concentration in Example 1, Example 2, and Comparative Example are as described in the following Table 1, Table 2, and Table 3, respectively. The values in each Table represent response sensitivity (nA).
According to the results of measurement described in Table 1, Table 2, and Table 3, in Example 1 and Example 2, it has been found that although a variation in measurement data is partly observed, positive correlation is observed in Examples when measurement data is seized as a whole, and there is a region where a retention or an improvement in response sensitivity is observed relative to an increase in the amount of a binder added. Specifically, Example 1 and Example 2 each have a region of positive correlation between the concentration of a binder (non-conductive polymer) added and the response sensitivity of an enzyme electrode. On the other hand, in Comparative Example, it has been found that although a variation in data is partly observed, negative correlation is observed when measurement data is seized as a whole, and there is a tendency that a reduction in response sensitivity is observed relative to an increase in the amount of a binder added. When a non-conductive polymer is added to an enzyme electrode, response sensitivity generally tends to be reduced as described in Comparative Example, but in Example 1 and Example 2, when a non-conductive polymer was added, an improvement in response sensitivity was observed. From Example 1 and Example 2, it has been found that when a high polymer containing an oxazoline group is used as a binder, an improvement in response sensitivity can be obtained irrespective of an increase in the amount of the binder added.
<B. Adhesion (or strength) test method>
Next, enzyme electrodes prepared using the electrode solutions in Example 1, Example 2, and Comparative Example were each tested for the adhesion of the detection layer to the electrode (strength of the detection layer).
<<Preparation of Enzyme Electrode>>
The same base material (base material in which an electrode is formed on an insulating substrate) as that used in the response sensitivity test was prepared, and each of the electrode solutions in Example 1, Example 2, and Comparative Example was dropped (applied) on the surface of an electrode under a condition of 10.0 μL/cm2 per unit area (cm2) of the electrode. Then, the electrode solution on the surface of the electrode was air dried in an atmosphere of 23° C. and 40% RH. In this way, a detection layer (enzyme electrode) formed on the electrode which is to be used for the adhesion (or strength) test was prepared.
<<Adhesion (or Strength) Test>>
The adhesion of the detection layer to an electrode was tested according to JISK5600-5-6 Adhesion (Crosscut method).
<<Test Results>>
The test results by the crosscut method are described in Table 4 below. The test results are classified into 0 to 5, in which a numerical value of 0 represents the best adhesion, and a numerical value of 5 represents the poorest adhesion.
From the above test results, in Example 1 and Example 2, it has been found that an improvement in adhesion is observed with an increase in the amount of a binder (high polymer containing an oxazoline group) added. On the other hand, in Comparative Example, it has been found that the relationship between the amount of a binder added and the adhesion is not observed, and the adhesion tends to be poor as a whole.
<C. Relationship between Response Sensitivity Test Results and Adhesion (or Strength)>
Further, black circle plots in
Further, triangular plots in
The axis of ordinates of the graph indicates a current value (response sensitivity) (nA) and represents test results when the glucose concentration is 150 mg/dL. On the other hand, the axis of abscissas of the graph represents adhesion (or strength). However, the numerical values in the graph represent the opposite of the numerical values for the classification used in the crosscut method described in Table 4. Specifically, a numerical value of 5 represents the best adhesion, and a numerical value of 0 represents the poorest adhesion.
As illustrated in
Thus, an enzyme electrode having high adhesion to a base material (electrode) and high response sensitivity, which has not been achieved by using an existing crosslinking agent and binder, can be prepared by preparing a detection layer containing a polymer containing an oxazoline group which is a covalent linking chain containing nitrogen (N) or oxygen (O). From Examples as described above, the concentration of the non-conductive polymer is, for example, 0.25% to 10%, preferably 0.5% to 5%, more preferably 1% to 3%.
[Operations and Effects of the Embodiment]
According to the enzyme electrode 10 as described above, good response sensitivity can be obtained by immobilization of a proper enzyme 5 and conductive particles 6, and proper adhesion to a base material can be obtained. Particularly, since the concentration or the amount needed for proper immobilization can be reduced compared with an existing binder, it is expected to contribute to the reduction in size of the enzyme electrode 10.
Note that the enzyme electrode 10 can be applied, for example, to a biosensor which are applied to glucose measurement as described above, or an electronic apparatus (for example, measuring device). Alternatively, the enzyme electrode 10 can also be applied as a part of a power supply unit that supplies, to a load, response current generated by an enzyme reaction (current caused by electrons transferred to an electrode) as electric power through a feed section that connects the electrode and the load. The electronic equipment can include an electronic equipment including a biosensor to which the enzyme electrode according to the embodiment is applied and an electronic equipment including the above apparatus (power supply unit) to which the enzyme electrode according to the embodiment is applied.
1: substrate (electrode), 2: detection layer, 3: insulating substrate, 5: enzyme, 6: conductive polymer, 7: oxazoline group, 8: acrylic/styrene chain, 9 amide ester
Number | Date | Country | Kind |
---|---|---|---|
2012-142375 | Jun 2012 | JP | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/JP2013/067381 | 6/25/2013 | WO | 00 |