Patent Application
20170006957
The present invention relates to electrically conductive vulcanised-epoxidised natural rubber (ENR)-carbon black blend targeted for antistatic footwear application and method of preparation of the same.
Accumulated electrostatic charges on the high sensitive electronic components (e.g. computer integrated circuits, magnetic tape or disk and etc) are facing the difficulty of draining off to ground when they are placed on the surface of a good electrical insulator (such as wood, rubber and plastic). On the other hand, if these components are in contact with a good electrical conductor (i.e. metallic material), electrostatic will be discharged from them through the conductor in a very high rate and subsequently causes the unwanted current sparks. Both of these phenomenons can cause permanent damage to all these sensitive and expensive electronic components.
People manufacturing the sensitive electronic components are the most significant source of static electricity. As the result, it is essential to discharge static electricity from people who may come in contact with these sensitive electronic components. Working areas where which such sensitive electronic components are manufactured must have a grounded floor or grounded mats which are able to discharge the electrostatic from people walking on the floor or mats by conducting the static electricity from the people to the ground. The only contact people have with the floor is usually through their shoe soles. The conventional shoe soles (made from various types of electrical insulator) do not readily discharge static electricity from the body of the person to the floor. Therefore, it is necessary to have a pair of antistatic or electrically conductive shoes (which include their antistatic or electrically conductive soles) that can effectively discharge the accumulated static electricity from the person body (by creating an electrical conduit).
Technology of antistatic and electrically conductive footwear fabrication is well-established and it can be traced back to year 1941 [U.S. Pat. No. 2,261,072]. Majority of the antistatic, electrostatic dissipative and electrically conductive footwear available in the current market are produced with soles made from synthetic polymers or blends of synthetic and natural polymers.
U.S. Pat. Nos. 4,861,805 and 5,426,870 both disclosed antistatic shoe outer-soles could be made from polyurethane. Antistatic shoes with inner-soles and outer-soles made from vinyl chloride copolymer composition were reported respectively by U.S. Pat. Nos. 5,319,867 and 4,127,552. U.S. Pat. No. 5,426,870 also described antistatic shoe inner-sole that was made by using blend of natural rubber (non-chemically modified type) and styrene butadiene copolymer. Antistatic shoe soles (both outer and inner types) made from synthetic polymers were claimed to be lighter in weight, longer lasting and non-marking on floors if compared to natural rubber based shoe soles. However, it is also known that shoe soles made from all these synthetic polymers have shown some disadvantages, e.g. poor and inhomogeneous fillers dispersion for polyurethane based compositions, quick ageing problem for polyester based polyurethane due to hydrolysis (reaction with water) and also hard thermoplastic materials that reduce shoes wearers comfort.
All these synthetic polymers (i.e. polyurethane, vinyl chloride copolymer and styrene butadiene copolymer) used to manufacture antistatic and electrically conductive shoe soles are categorised as good electrical insulator in their virgin form. They could be turned into electrical conductors by addition of several types of conductive filler. The most common used electrically conductive fillers for antistatic, electrostatic dissipative and electrically conductive shoe soles manufacturing are carbon blacks [U.S. Pat. Nos. 5,233,769, 5,426,870, 5,319,867 and 7,424,782 B2].
It is according to one aspect of the present invention to provide an epoxidised natural rubber [ENR] based blend for antistatic footwear application comprising; epoxidised natural rubber [ENR], carbon blacks, antioxidants, processing oils, processing waxes and vulcanisation agents.
Vulcanisation accelerators, vulcanisation activators and vulcanisation coagents are selectively added to the ENR based blend in order to accelerate, activate and enhance the blend's vulcanisation process. Whitening agents are also selectively added for adjusting the level of black colour of the ENR based blend.
Accordingly, the present invention attempts to tackle one or more of the problems mentioned in the background section. The provision of the epoxidised natural rubber [ENR] is advantageous as it is environmentally friendly and sustainable since it is sourced from the Hevea Braziliensis trees. Several other advantages [as reported by I. R. Gelling, Journal of Natural Rubber Research, 1991] can also be obtained by using epoxidised natural rubber based compound, i.e. good dispersion level of fillers, high damping (i.e. increased shock absorption ability as an advantageous for shoe sole manufacturing), good tensile properties, good oil resistance, improved oxidation resistance and high abrasion resistance (an indication of good wear resistance). Reasonable light-weight antistatic footwear can be manufactured by adjusting the thickness of the epoxidised natural rubber based shoe sole (since the electrical conductivity of the shoe sole is not affected by its thickness).
According to second aspect of the present invention, there is provided an internal mechanical mixing method for preparation of epoxidised natural rubber based blends by using internal mechanical mixing device and open milling device. This method comprising the steps of:
Accordingly, wherein step (b) further comprising the step of adding vulcanisation activators.
Accordingly, wherein step (d) further comprising the step of adding either vulcanisation accelerators or vulcanisation coagents or whitening agents or in any combination thereof.
According to third aspect of the present invention, there is provided an open milling method for preparation of epoxidised natural rubber based blends by using only open milling device. This method comprising the steps of:
Accordingly, wherein step (b) further comprising the step of adding vulcanisation activators to the masterbatch.
Accordingly, step (c) further comprising the step of adding either vulcanisation accelerators or vulcanisation coagents or whitening agents or in any combination thereof.
The present invention consists of several novel features and a combination of parts hereinafter fully described and illustrated in the accompanying description and drawings, it being understood that various changes in the details may be made without departing from the scope of the invention or sacrificing any of the advantages of the present invention.
The present invention will be fully understood from the detailed description given herein below and the accompanying drawings which are given by way of illustration only, and thus are not limitative of the present invention, wherein:
The present invention relates to an environmentally friendly and electrically conductive vulcanised epoxidised natural rubber (ENR) blend targeted for antistatic footwear (includes both inner- and outer-shoe soles) application and manufacturing. Hereinafter, this specification will describe the present invention according to the preferred embodiments of the present invention. However, it is to be understood that limiting the description to the preferred embodiments of the invention is merely to facilitate discussion of the present invention and it is envisioned that those skilled in the art may devise various modifications and equivalents without departing from the scope of the appended claims.
The present invention also describes two methods for preparation of vulcanised electrically conductive ENR based blend for antistatic footwear application, i.e. the internal mechanical mixing method and the open milling method. All vulcanised electrically conductive rubber blends in this present invention are based on ENR as the rubber host and carbon black as the only electrically conductive filler. These two major constituent materials in solid form are known to be highly processable with the help of some common mechanical mixing devices, such as internal mechanical mixing device (refer to
In view of problems such as material sustainability issue, poor fillers dispersion, low ageing resistance and also low comfort level due to hard materials for synthetic polymer based blends, it is now able to demonstrate that the very low electrical resistances of the vulcanised (at temperature 150±50° C.) epoxidised natural rubber-carbon black blends (reaching at the order of 101 ohms in term of volume resistance) can be produced directly by using either the internal mechanical mixing method or the open milling method, which are commercially friendly methods due to their practicability and high production rate. Processing aids such as oils and waxes are also introduced to the blends in order to enhance the processability and dispersion level of the carbon blacks within the solid ENR host matrixes.
Carbon blacks are common electrical conductive fillers and commercially available in different grades at reasonable market pricing. Potential commercial applications (such as for antistatic footwear products) with more interesting visual appearance (i.e. the adjustable level of black colour of the rubber blend due to the inclusion of whitening agent) can also be manufactured using this type of vulcanised ENR blend. Suitable methods for processing this type of vulcanised ENR based blend are including various types of rubber processing equipment, such as injection moulding, extrusion and hot press-moulding.
Masterbatches with different compositions of ENR, carbon black, antioxidants, processing oils, processing waxes and vulcanisation activators are prepared by using either an internal mechanical mixing device (at temperature of between 25 to 230° C., fill factor of between 0.60 to 0.90 and rotors speed of between 50-180 rounds per minute) or by using an open milling device (at temperature of between 25-230° C.) at the first stage of mixing process.
At the second stage of mixing, vulcanisation agents (either sulfur or peroxide), vulcanisation accelerators, vulcanisation coagents and whitening agents are added later (during the second stage of mixing process) to the masterbatch by using an open milling device (at temperature 30-70° C.) in order to avoid the premature vulcanisation problem that can cause hardening and reducing the processability of the produced ENR based blends.
The total mixing period to produce ENR based blend by using both types of methods is fallen between 3 to 60 minutes.
The vulcanisation process of all ENR based blends are performed at temperature ranges from 100-250° C. by either heating or microwave.
All vulcanised (at temperature 150±50° C.) ENR based blends (including 5.0 to 60.0 p.p.h.r. of carbon blacks) prepared by using either internal mechanical mixing method or open milling method exhibit low electrical resistances (with the range of order from 101-1010 ohms in term of volume resistances) and other good physical properties (with tensile strengths equal 16.0 to 26.0 MPa, elongations at break equal 140.0 to 680.0%, tear strengths equal 10.0 to 38.0 N/mm, hardness equals of Shore A 30.0 to 90.0, compression sets equal 8.0 to 65.0%, Dunlop rebound resiliencies equal 14.0 to 56.0% and Akron abrasions equal 4.0 to 50.0 mm3/500 rev).
Mixing proportions and function of each of the raw materials, chemicals and processing devices used to produce the electrical conductive vulcanised ENR based blends are listed as following:
From hereinbelow, the preferred embodiments of the present invention will be discussed in relation to the accompanying
50.0 to 150.0 parts per hundred rubber (p.p.h.r.) of solid epoxidised natural rubber [ENR]—with refer to
5.0 to 60.0 p.p.h.r. of carbon blacks (include grades of either reinforcing or semi-reinforcing or non-reinforcing or conductive blacks, all in either single or combination form of application) are used as the only electrically conductive fillers.
0.1 p.p.h.r to 10.0 p.p.h.r. of vulcanisation agents (selected from either sulfur or peroxide), 0 to 10.0 p.p.h.r. of vulcanisation accelerators, 0 to 12.5 p.p.h.r. of vulcanisation activators and 0 p.p.h.r. to 20.0 p.p.h.r. of vulcanisation coagents are used as the ingredients for all solid ENR based blends vulcanisation purpose.
0.1 to 20.0 p.p.h.r. of antioxidants (either staining or non-staining grades, all in either single or combination form of application) are included into all blends in the hope to enhance their oxidation resistance.
1.0 p.p.h.r. to 60.0 p.p.h.r. of processing oils (include types of either natural or synthetic oil, in either single or combination form of application) are added into all blends as processing aid in order to enhance the processability.
0.05 to 20.0 p.p.h.r. of processing waxes (include types of either natural or synthetic wax, in either single or combination form of application) are also added into all blends as processing aid in order to enhance the processability and dispersion level of the carbon blacks within the solid ENR host matrixes.
0 to 35.0 p.p.h.r. of whitening agents (either in solid or liquid form) are added for adjusting the level of black colour of the ENR based blend.
Internal mechanical mixing device (with refer to
Open milling device (with refer to
Both open milling device and internal mechanical mixing device may be used independently or in any combination thereof.
The invention now being generally described, the same will be better understood by reference to the following detailed examples which are provided for purposes of illustration only and are not to be limiting of the invention unless so specified.
Vulcanised ENR-carbon black blend with various compositions of carbon black filler are prepared for the antistatic footwear application feasibility study (based on their selected electrical and physical properties). Examples of formulation for preparing the vulcanised ENR-carbon black blends are shown in Table 1.
100.0 p.p.h.r of solid epoxidised natural rubbers (i.e. ENR 50 grade with 50.0±3.0 mole % of epoxide contents) are used as the only rubber host.
5.0 to 60.0 p.p.h.r. of carbon blacks, include grades of reinforcing [N330] and conductive black [XC 72] in either single or combination form of application are used as the only electrically conductive fillers.
2.0 p.p.h.r. of sulfurs are used as the vulcanising agent and 1.6 p.p.h.r. of Santocure NS (N-t-butyl-2-benzothiazole sulfenamide) as the favourable vulcanisation accelerators. Both 5.0 p.p.h.r. of zinc oxide and 2.5 p.p.h.r. of stearic acid are added as the vulcanisation activators.
1.0 p.p.h.r. of Permanax WSL (alpha-1-methyl cyclohexyl derivative of selected xylenols) is added as the antioxidant (a non-staining grade).
5.0 p.p.h.r. of Nytex 840 processing oil (a type of naphthenic synthetic processing oil) and 0.5 p.p.h.r. of paraffin wax are added as the processing aids.
5.0 p.p.h.r. of titanium dioxides are added as the whitening agent. The titanium dioxides used are in solid powder form.
For the first stage of mixing, ENR-carbon black masterbatches with different proportions [in p.p.h.r.] of carbon blacks, Nytex 840, paraffin wax, Permanax WSL, zinc oxide and stearic acid (accordingly to the formulation as shown in Table 1 of Example 1) are prepared by using an internal mechanical mixing device (with refer to
For the second stage of mixing, 2.0 p.p.h.r. of sulfurs, 1.6 p.p.h.r. of Santocure NS and 5.0 p.p.h.r. of titanium dioxides are added to each of the ENR-carbon black masterbatches (with 5.0 to 60.0 p.p.h.r. of total carbon black) on a two-roll open milling device (with refer to
ENR-carbon black blends with different proportions [in p.p.h.r.] of carbon blacks, Nytex 840, paraffin wax, Permanax WSL, zinc oxide, stearic acid, sulfur, Santocure NS and titanium dioxide (accordingly to the formulation as shown in Table 1 of Example 1) are prepared directly by using a two-roll open milling device (with refer to
Each of the sulfur-vulcanisation system containing ENR-carbon black blends is then removed from the two-roll open milling device after 16 minutes of total mixing period. Prolonged mixing shall be avoided in order to prevent premature vulcanisation.
Each of the sulfur-vulcanisation system containing ENR-carbon black blends is prepared accordingly to Examples 1, 2 and 3. Appropriate amounts (varied with the targeted application and testing) of each of the sulfur-vulcanisation system containing ENR-carbon black blends are cut and fed into a mould (dimension of the mould is also varied with the type of targeted application and testing). The mould together with the sulfur-vulcanisation system containing ENR-carbon black blend are sent for vulcanisation by using an electrical hot press machine with heating temperature 150±2° C., pressure 60 psi and duration based on the Tc90 (curing time to at least 90% of curing level) of each blend (as measured by a Monsanto's moving die typed rheometer). The Tc90 values of blends prepared by using the internal mechanical mixing method and open milling method are reported in Table 4 and 5 respectively.
Sulfur-vulcanised ENR-carbon black blends prepared by using either the internal mechanical mixing method (as described in Examples 2 and 4) or open milling method (as described in Examples 3 and 4) have the orders of electrical volume resistance (measured using 2-probe technique with a Keithley 6157A Electrometer) as summarised in Table 6 and 7 respectively, which rendered the material suitable for antistatic footwear application and manufacturing.
Sulfur-vulcanised ENR-carbon black blends prepared by using either the internal mechanical mixing method (described in Examples 2 and 4) or open milling method (described in Examples 3 and 4) exhibit Shore A hardness values as shown in Table 8 and 9 respectively.
Sulfur-vulcanised ENR-carbon black blends prepared by using either the internal mechanical mixing method (as described in Examples 2 and 4) or open milling method (as described in Examples 3 and 4) have some main non-aged tensile properties (measured according to the standard, i.e. ISO 37) as shown in Table 10 and 11 respectively.
Sulfur-vulcanised ENR-carbon black blends prepared by using either the internal mechanical mixing method (as described in Examples 2 and 4) or open milling method (as described in Examples 3 and 4) show crescent tear strength values (measured according to the standard, i.e. ISO 34) as reported in Table 12 and 13 respectively.
Sulfur-vulcanised ENR-carbon black blends prepared by using either the internal mechanical mixing method (as described in Examples 2 and 4) or open milling method (as described in Examples 3 and 4) also show compression set values (measured according to Standard ISO 815 at 30 min) as reported in Table 14 and 15 respectively.
Sulfur-vulcanised ENR-carbon black blends prepared by using either the internal mechanical mixing method (as described in Examples 2 and 4) or open milling method (as described in Example 3 and 4) also exhibit Dunlop rebound resilience values (measured according to Standard BS 903 Part A8) as reported in Table 16 and 17 respectively. Damping properties of the ENR-carbon black blends always enhanced with their decreasing rebound resilience values.
Sulfur-vulcanised ENR-carbon black blends prepared by using either the internal mechanical mixing method (as described in Examples 2 and 4) or open milling method (as described in Examples 3 and 4) show Akron abrasion values (measured according to Standard BS 903 Part A9) as reported in Table 18 and 19 respectively.
The invention being thus described, it will be apparent that the same may be varied in many ways. Such variations are to be regarded as within the scope of the invention, and all such modifications as would be apparent to one skilled in the art are intended to be within the scope of the following claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| PI2011700024 | Mar 2011 | MY | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14004147 | Dec 2013 | US |
| Child | 15272423 | US |