Patent Application
20130320379
This application claims the benefit under 35 U.S.C. §119 of Korean Patent Application No. 10-2012-0058859, filed May 31, 2012, which is hereby incorporated by reference in its entirety.
The disclosure relates to an epoxy resin composition and light and light emitting apparatus.
The embodiment relates to an epoxy resin composition and a light emitting apparatus.
Recently, GaN white light emitting diodes (LED) have been extensively manufactured over the whole world. Methods for manufacturing the GaN white LED are mainly classified into two methods, one is a method using a single chip, in which a white LED is obtained by forming a phosphor layer on a blue LED or a UV LED, and the other is a method using a multi-chip, in which two or more LEDs are combined to obtain a white LED.
A representative method for manufacturing the white LED in the form of the multi-chip is to combine three R, G and B chips with each other. However, since operating voltage of each chip is not uniform, the output of each chip may vary depending on the surrounding temperature so that the color coordinate may be changed.
Due to the above problem, the multi-chip scheme is not suitable for implementing the white LED, but suitable for a special-purpose lighting that reproduces various colors by controlling the brightness of each LED using the circuit configuration.
For this reason, the binary system, which can be easily manufactured and obtained by combining a blue LED with a phosphor that is excited by the blue LED to generate yellow color, is representatively used to implement the white LED.
The binary system mainly employs a white LED, which uses the blue LED as an excitation light source and excites YAG (Yttrium Aluminum Garnet) phosphor using rare-earth 3-valent ion of Ce3+ as an activator, i.e., YAG:Ce phosphor using an excitation light emitted from the blue LED.
In addition, the white LED employs various packages according to applications, and representatively includes a surface mounting device (SMD) type ultra-miniaturized LED used in a backlight of a handheld terminal, and a vertical lamp type LED used for an electronic board, a solid display device or an image display.
Meanwhile, an index for analyzing the characteristics of white light includes a correlated color temperature (CCT) and a color rendering index (CRI).
The CCT indicates a temperature of an article when the article shines with emitting visible rays, it seems that a color of the article is identical to a color that a black body radiates at a temperature and it is assumed that the temperature of the black body is equal to that of the article. As the CCT becomes high, the light dazzles a human and becomes a bluish white.
Therefore, in spite of identical white lights, when the CCT is low, people feel warm, whereas when the CCT is high, people feel cold. Accordingly, it is possible to meet even the specification of a particular lighting requiring various color feelings by adjusting the CCT.
In a conventional white LED using the YAG:Ce phosphor, the CCT is fixed only to 6000 K-8000 K.
The CRI indicates a degree that the color of an article is changed when sun light or artificial light is irradiated onto the article. When the color of the article is identical to that under sun light, the CRI is defined as 100. In other words, the CRI is an index to show how the color of the article under the artificial lighting is close to that under sun light, and has a value of 0 to 100.
Accordingly, as the CRI approaches 100, i.e., white light, people can feel that the color of the article under the artificial lighting has no difference than that under sun light.
At present, an incandescent lamp has a CRI of 80 or more and a fluorescent lamp has a CRI of 75 or more, while a white LED using YAG:Ce phosphor has a CRI of approximately 70-75.
Accordingly, it is problematic that the white LED using the conventional YAG:Ce phosphor has the low CCT and low CRI.
In addition, since only the YAG:Ce phosphor is used, it is difficult to control the CCT, CRI and color temperature.
The LED using such a phosphor is disclosed in Korean Unexamined Patent Publication No. 10-2005-0098462.
The embodiment provides an epoxy resin composition and a light emitting apparatus having improved reliability, optical properties and heat-resistant property.
The epoxy resin composition according to the embodiment includes a triazine derivative epoxy resin and an alicyclic epoxy resin.
The light emitting apparatus according to the embodiment includes a light emitting chip, a body part to receive the light emitting chip and a filling part to cover the light emitting chip, wherein the body part or the filling part is formed by an epoxy resin composition comprising a triazine derivative epoxy resin and an alicyclic epoxy resin.
According to one embodiment, the alicyclic epoxy resin may be expressed as a following chemical formula 1:
(wherein, n is 1 to 1000, R1 is selected from hydrogen, a halogen group, an amino group, a C1-C30 alkyl group, an alkoxy group, a carboxyl group and a C5-C30 aryl group, R2 is selected from hydrogen, a halogen group, an amino group, a C1-C30 alkyl group, an alkoxy group, a carboxyl group and a C5-C30 aryl group, and R3 is expressed as a following chemical formula 2:)
(wherein, m is 0 to 3).
According to one embodiment, the triazine derivative epoxy resin may include an isocyanurate epoxy resin.
According to one embodiment, the isocyanurate epoxy resin may be expressed as a following chemical formula 4:
(wherein, at least one of R4, R5 and R6 is expressed as the chemical formula 2 (m is 1 to 3) and a remaining of the R4, R5 and R6 is selected from hydrogen, a halogen group, an amino group, a C1-C30 alkyl group, an alkoxy group, a carboxyl group and a C5-C30 aryl group).
According to one embodiment, the isocyanurate epoxy resin may include triglycidylisocyanurate.
According to one embodiment, the alicyclic epoxy resin may be contained at a ratio of about 10 wt % to about 50 wt %.
According to one embodiment, the epoxy resin composition may further include a hardener, a catalyst and an additive.
The epoxy resin composition according to the embodiment includes the triazine derivative epoxy resin and the alicyclic epoxy resin. Thus, the epoxy resin composition according to the embodiment may have the improved moisture-resistant property, heat-resistant property and transmittance.
The epoxy resin composition according to the embodiment may have the improved reliability and optical properties by appropriately combining the triazine derivative epoxy resin, such as the isocyanurate epoxy resin, with the alicyclic epoxy resin.
The epoxy resin composition according to the embodiment can be used for the body part or the filling part of the light emitting apparatus, such as a light emitting diode package. Therefore, the light emitting apparatus according to the embodiment may have the improved reliability and optical properties.
Hereinafter, an epoxy resin composition according to the embodiment will be described in detail.
The epoxy resin composition according to one embodiment includes an epoxy resin, a hardener, a catalyst and an additive.
The epoxy resin may comprise the whole content of the epoxy resin composition according to the embodiment. The epoxy resin may be contained at a ratio of about 15 wt % to about 70 wt % based on the total content of the resin composition. In detail, the epoxy resin may be contained at a ratio of about 15 wt % to about 60 wt % based on the total content of the resin composition.
The epoxy resin may include an alicyclic epoxy resin and a triazine derivative epoxy resin. The alicyclic epoxy resin may be contained at a ratio of about 10 wt % to about 50 wt % based on the total content of the resin composition. In detail, the alicyclic epoxy resin may be contained at a ratio of about 15 wt % to about 35 wt % based on the total content of the resin composition.
If the epoxy resin composition according to the embodiment contains the alicyclic epoxy resin less than about 10 wt %, the optical property and moisture-resistant property of the epoxy resin composition may be deteriorated. In addition, if the epoxy resin composition according to the embodiment contains the alicyclic epoxy resin more than about 60 wt %, the heat-resistant property of the epoxy resin composition may be deteriorated.
In addition, the triazine derivative epoxy resin may be contained at a ratio of about 5 wt % to about 50 wt % based on the total content of the resin composition. In detail, the triazine derivative epoxy resin may be contained at a ratio of about 15 wt % to about 25 wt % based on the total content of the resin composition.
The alicyclic epoxy resin may be alicyclic hydrocarbon including at least one epoxy group. In detail, the alicyclic epoxy resin may include cyclohexane substituted with an epoxy group. In more detail, the alicyclic epoxy resin may include cyclohexane substituted with an epoxy group and an ether group. Further, the alicyclic epoxy resin may include at least two cyclohexane substituted with an epoxy group and linked with each other by an ether group.
The alicyclic epoxy resin may be expressed as a following chemical formula 1:
In the chemical formula 1, n may be 1 to 1000. R1 may be selected from hydrogen, a halogen group, an amino group, a C1-C30 alkyl group, an alkoxy group, a carboxyl group and a C5-C30 aryl group. R2 may be selected from hydrogen, a halogen group, an amino group, a C1-C30 alkyl group, an alkoxy group, a carboxyl group and a C5-C30 aryl group.
R3 may be a functional group including an epoxy group. That is, R3 may be an alkyl group substituted with an epoxy group. R3 may be an epoxy group. In detail, R3 may be expressed as a following chemical formula 2:
In the chemical formula 2, m may be 0 to 3, 0 or 1 to 3.
In particular, at least one of positions of 2, 3, 4 and 5 of cyclohexane may be substituted with R3 and the remaining may be substituted with R2.
The alicyclic epoxy resin may be prepared through the condensation. In detail, the alicyclic epoxy resin may be synthesized by using cyclohexanediol having a following chemical formula 3 as a monomer. For instance, the alicyclic epoxy resin may be prepared through the condensation with cyclohexanediol expressed as a following chemical formula 3:
In the chemical formula 3, R1 may be selected from hydrogen, a halogen group, an amino group, a C1-C30 alkyl group, an alkoxy group, a carboxyl group and a C5-C30 aryl group. In addition, R2 may be selected from hydrogen, a halogen group, an amino group, a C1-C30 alkyl group, an alkoxy group, a carboxyl group and a C5-C30 aryl group.
R3 may be a functional group including an epoxy group. That is, R3 may be an alkyl group substituted with an epoxy group. R3 may be an epoxy group. In detail, R3 may be expressed as the above chemical formula 2.
The triazine derivative epoxy resin may be a triazine derivative including at least one epoxy group. In detail, the triazine derivative epoxy resin may be a triazine derivative including three epoxy groups.
The triazine derivative epoxy resin may be an isocyanurate epoxy resin. That is, the triazine derivative epoxy resin may be expressed as a following chemical formula 4:
In the chemical formula 4, at least one of R4, R5 and R6 may be a functional group including an epoxy group. In detail, at least one of R4, R5 and R6 may be an alkyl group substituted with an epoxy group. At least one of R4, R5 and R6 may be an epoxy group. In more detail, at least one of R4, R5 and R6 may be expressed as the chemical formula 2. In the chemical formula 2, m may be 1 to 3. In detail, m may be 1.
In addition, the remaining of the R4, R5 and R6 may be selected from hydrogen, a halogen group, an amino group, a C1-C30 alkyl group, an alkoxy group, a carboxyl group and a C5-C30 aryl group.
All of the R4, R5 and R6 may be functional groups including epoxy groups. In detail, the R4, R5 and R6 may be expressed as the above chemical formula 2.
In more detail, the isocyanurate epoxy resin may include triglycidylisocyanurate (TGIC).
In addition, the epoxy resin may further include other epoxy resins. In other words, the epoxy resin may further include typical epoxy resins having at least two epoxy groups in a molecule besides the triazine derivative epoxy resin and the alicyclic epoxy resin.
For instance, the epoxy resin may further include one or at least two of bisphenol A, 3,3′,5,5′-tetramethyl-4,4′-dihydroxydiphenylmethane, 4,4′-dihydroxydiphenylsulfone, 4,4′-dihydroxydephenylsulfide, 4,4′-dihydroxydiphenylketone, fluorenebisphenol, 4,4′-biphenol, 3,3′,5,5′-tetramethyl-4,4′-dihydroxybiphenyl, 2,2′-biphenol, resorcin, catechol, t-butylcatechol, hydroquinone, t-butylhydroquinone, 1,2-dihydroxynaphthalene, 1,3-dihydroxynaphthalene, 1,4-dihydroxynaphthalene, 1,5-dihydroxynaphthalene, 1,6-dihydroxynaphthalene, 1,7-dihydroxynaphthalene, 1,8-dihydroxynaphthalene, 2,3-dihydroxynaphthalene, 2,4-dihydroxynaphthalene, 2,5-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, 2,7-dihydroxynaphthalene, 2,8-dihydroxynaphthalene, allide or polyallide of dihydroxynaphthalene, allylbisphenol A, allylbisphenol F, divalent phenols such as allylphenolnovolac, or phenol novolac, bisphenolAnovolac, o-cresolnovolac, m-cresolnovolac, p-cresolnovolac, xylenolnovolac, poly-p-hydroxystyrene, tris-(4-hydroxyphenyl)methane, 1,1,2,2-tetrakis(4-hydroxyphenyl)ethane, fluoroglycinol, pyrogallol, t-butylpyrogallol, allidepyrogallol, polyallidepyrogallol, 1,2,4-benzenetriol, 2,3,4-trihydroxybenzophenone, phenolaralkyl resin, naphtholaralkyl resin, phenols of 3-valance or more such as dicyclopentadiene resin, and glycidylether derived from halogenated bisphenols such as tetrabromobisphenol.
Various types of hardeners generally known as epoxy resin hardeners may be used as the hardener for the epoxy resin composition according to the embodiment, preferably, a phenol hardener is used.
The hardener may be contained at a ratio of about 5 wt % to about 50 wt % based on the total content of the epoxy resin composition.
The phenol hardener is a single phenol compound and may include a phenol resin in addition to the phenol compound.
In detail, the phenol hardener may include bisphenol A, bisphenol F, 4,4′-dihydroxydiphenylmethane, 4,4′-dihydroxydiphenylether, 1,4-bis(4-hydroxyphenoxy)benzene, 1,3-bis(4-hydroxyphenoxy)benzene, 4,4′-dihydroxyphenylsulfide, 4,4′-dihydroxyldiphenylketone, 4,4′-dihydroxydiphenylsulfone, 4,4′-di hydroxydiphenyl, 2,2′-dihydroxydiphenyl, 10-(2,5-dihydroxyphenyl)-10H-9-oxa-10-phosphaphenanthrene-10-oxide, phenolnovolac, bisphenolAnovolac, o-cresolnovolac, m-cresolnovolac, p-cresolnovolac, xylenolnovolac, poly-p-hydroxystyrene, hydroquinone, resorcin, catechol, t-butylcatechol, t-butylhydroquinone, fluoroglycinol, pyrogallol, t-butylpyrogallol, allylpyrogallol, polyallylpyrogallol, 1,2,4-benzenetriol, 2,3,4-trihydroxybenzophenone, 1,2-dihydroxynaphthalene, 1,3-dihydroxynaphthalene, 1,4-dihydroxynaphthalene, 1,5-dihydroxynaphthalene, 1,6-dihydroxynaphthalene, 1,7-dihydroxynaphthalene, 1,8-dihydroxynaphthalene, 2,3-dihydroxynaphthalene, 2,4-dihydroxynaphthalene, 2,5-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, 2,7-dihydroxynaphthalene, 2,8-dihydroxynaphthalene, allide or polyallide of the dihydroxynaphthalene, allylbisphenolA, allylbisphenolF, allylphenolnovolac, and allylpyrogallol.
The hardener may be prepared by mixing at least two types of hardeners.
Meanwhile, the hardener generally known in the art can be used instead of the phenol hardener. For instance, the hardener may include an amine hardener, an acid anhydride hardener, a phenol hardener, a polymercaptan hardener, a polyaminoamide hardener, an isocyanate hardener or a blocked isocyanate hardener. The content of the hardener may be appropriately set by taking into consideration the type of the hardener and the property of the thermal conductive epoxy resin to be obtained.
In detail, the amine hardener may include aliphatic amines, polyether polyamines, alicyclic amines, aromatic amines, and the like. The aliphatic amines may include ethylenediamine, 1,3-diaminopropane, 1,4-diaminopropane, hexamethylenediamine, 2,5-dimethylhexamethylenediamine, trimethylhexamethylenediamine, diethylenetriamine, iminobispropylamine, bis(hexamethylene)triamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, N-hydroxyethylethylenediamine, tetra(hydroxyethyl)ethylenediamine, and the like. The polyether polyamines may include triethyleneglycolamine, tetraethyleneglycoldiamine, diethyleneglycolbis(propylamine), polyoxypropylenediamine, polyoxypropyleneamines, and the like. The alicyclic amines may include isophoronediamine, methendiamine, N-aminoethylpiperazine, bis(4-amino-3-methyldicyclohexyl)methane, bis(aminomethyl)cyclohexane, 3,9-bis(3-aminopropyl)2,4,8,10-tetra-oxaspiro(5,5)undecan, norbornenediamine and the like. The aromatic amines may include tetra-chloro-p-xylenediamine, m-xylenediamine, p-xylenediamine, m-phenylenediamine, o-phenylenediamine, p-phenylenediamine, 2,4-diaminoanisole, 2,4-toluenediamine, 2,4-diaminodiphenylmethane, 4,4′-diaminodiphenylmethane, 4,4′-diamino-1,2-diphenylethane, 2,4-diaminodiphenylsulfone, 4,4′-diaminodiphenylsulfone, m-aminophenol, m-aminobenzylamine, benzyldimethylamine, 2-(dimethylamino-methyl)phenol, triethanolamine, methylbenzylamine, α-(m-aminophenyl)ethylamine, α-(p-amino-phenyl)ethylamine, diaminodiethyldimethyldiphenylmethane, α,α′-bis(4-aminophenyl)-p-diisopropylbenzene and the like.
The anhydride hardener may include dodecenylsuccinicanhydride, polyadipicacidanhydride, polyazelaicacidanhydride, polysebacicacidanhydride, poly(ethyloctadecanedoicacid)anhydride, poly(phenylhexadecanedoicacid)anhydride, methyltetrahydrophthalicanhydride, methylhexahydrophthalicanhydride, hexahydrophthalicanhydride, anhydrousmethylhimicacid, tetrahydrophthalicanhydride, trialkyltetrahydrophthalicanhydride, methylcyclohexenedicarboxylicacidanhydride, methylcyclohexenetetracarboxylicacidanhydride, phthalicanhydride, trimelliticanhydride, pyromelliticacidanhydride, benzophenonetetracarboxylicacidanhydride, ethyleneglycolbistrimellitate, anhydrousheticacid, anhydrousnadicacid, anhydrousmethylnadicacid, 5-(2,5-dioxotetrahydro-3-furanyl)-3-methyl-3-cyclohexane-1,2-dicarboxylicacidanhydride, 3,4-dicarboxy-1,2,3,4-tetrahydro-1-naphthalenesuccinicanhydride, 1-methyl-dicarboxy-1,2,3,4-tetrahydro-1-naphthalenesuccinicanhydride and the like.
The catalyst may promote the curing reaction of the epoxy resin composition according to the embodiment. The catalyst may be contained in the epoxy resin composition according to the embodiment at a ratio of about 0.1 wt % to about 2 wt %. The catalyst may include a metal, such as Pb, Pt or Ti. In addition, triphenylphospin (TPP) may be used as the catalyst. Further, the catalyst may include amidazole type tertiary amine, quaternary ammonium salt, amidines and its derivatives, phosphine or phosphonium. Various materials having superior curability with no color may be used as the catalyst.
The additive may be contained in the epoxy resin composition according to the embodiment at a ratio of about 0.1 wt % to about 10 wt %. The additive may include a dispersing agent, a leveling agent, and an antioxidant. The dispersing agent may include a silicon type dispersing agent.
In addition, the leveling agent may include a sulfonic compound or an ester compound. Further, the antioxidant may include phenyl-β-naphthylamine, aromatic amines or hydroquinone.
Furthermore, the dispersing agent, leveling agent and antioxidant generally known in the art can be used as the additive for the epoxy resin according to the embodiment.
Hereinafter, a light emitting diode package will be described in detail with reference to
In the description of the embodiments, it will be understood that when each substrate, layer, film or electrode is referred to as being “on” or “under” another substrate, layer, film or electrode, it can be “directly” or “indirectly” on or under another element or the other constituent elements may also be present. Such a position of the elements will be determined based on the drawings. The size of the elements shown in the drawings may be exaggerated for the purpose of explanation and may not utterly reflect the actual size.
Referring to
The body part 100 includes a cavity having an open top surface. The cavity C may be formed by punching, cutting or etching the body part 100. In addition, the cavity C may be simultaneously formed with the body part 100 by using a metal mold having the internal structure identical to the cavity C.
The cavity C may have a cup shape or a concave container shape and a surface of the cavity C may have a circular shape, a polygonal shape or a random shape, but the embodiment is not limited thereto.
A sidewall of the cavity C may be vertical or inclined with respect to a bottom surface of the cavity C by taking a light distribution angle of the light emitting diode package according to the embodiment into consideration.
The lead electrodes 210 and 220 may be integrally formed with the body member 100. In detail, two lead electrodes 210 and 220 may be provided in one body part 100. The lead electrodes 210 and 220 may constitute a lead frame, but the embodiment is not limited thereto.
The lead electrodes 210 and 220 are disposed in the body part 100 such that the lead electrodes 210 and 220 can be electrically isolated from the bottom surface of the cavity C. Outer portions of the lead electrodes 210 and 220 may be exposed out of the body part 100.
End portions of the lead electrodes 210 and 220 may be disposed on one side of the cavity C or may be disposed opposite to the cavity C.
The lead electrodes 210 and 220 may be prepared in the form of a lead frame and the lead frame may be formed when the body part 100 is injection-molded. For instance, the lead electrodes 210 and 220 may include a first lead electrode 210 and a second lead electrode 220.
The first and second electrodes 210 and 220 are spaced apart from each other. The first and second lead electrodes 210 and 220 are electrically connected to the light emitting chip 300.
The light emitting chip 300 is disposed in the cavity C. The light emitting chip 300 is a light emitting unit that generates light. In detail, the light emitting chip 300 may be a light emitting diode chip that generates the light. For instance, the light emitting chip 300 may include a colored light emitting diode chip or a UV light emitting diode chip. One light emitting chip 300 may be disposed in one cavity C.
The filling part 400 is disposed in the cavity C. The filling part 400 is filled in the cavity C. The filling part 400 covers the light emitting chip 300. The filling part 400 may seal the light emitting chip 300 against external environment. In addition, the filling part 400 may have a convex shape to serve as a lens. In addition, phosphors may be distributed in the filling part 400.
The body part 100 and/or the filling part 400 may be formed by using the epoxy resin composition according to the embodiment. That is, the body part 100 and/or the filling part 400 can be formed by curing the epoxy resin composition according to the embodiment through a thermal curing process.
Accordingly, the body part 100 and/or the filling part 400 may include polymer including isocyanurate and alicyclic hydrocarbon linked with each other through an ether group. In detail, the body part 100 and/or the filling part 400 may include polymer having a net structure which is prepared by linking isocyanurate and cyclohexane with each other through an ether group.
Therefore, the body part 100 and/or the filling part 400 may have the improved moisture-resistant property, heat-resistant property and transmittance.
As described above, the epoxy resin composition according to the embodiment includes a triazine derivative epoxy resin and an alicyclic epoxy resin. Thus, the epoxy resin composition according to the embodiment may have the improved moisture-resistant property, heat-resistant property and transmittance.
In other words, the epoxy resin composition according to the embodiment can be formed by appropriately combining a triazine derivative epoxy resin, such as isocyanurate epoxy resin, and an alicyclic epoxy resin so that the epoxy resin composition may have the improved reliability and optical property.
In addition, the epoxy resin composition according to the embodiment can be used for the body part 100 and/or the filling part 400. Thus, the light emitting diode package according to the embodiment can inhibit the body part 100 and/or the filling part 400 from being thermally deformed and inhibit the moisture from penetrating into the light emitting chip 300. Therefore, the light emitting diode package according to the embodiment may have the improved reliability and optical property.
Any reference in this specification to “one embodiment,” “an embodiment,” “example embodiment,” etc., means that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment of the invention. The appearances of such phrases in various places in the specification are not necessarily all referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with any embodiment, it is submitted that it is within the purview of one skilled in the art to effects such feature, structure, or characteristic in connection with other ones of the embodiments.
Although embodiments have been described with reference to a number of illustrative embodiments thereof, it should be understood that numerous other modifications and embodiments can be devised by those skilled in the art that will fall within the spirit and scope of the principles of this disclosure. More particularly, various variations and modifications are possible in the component parts and/or arrangements of the subject combination arrangement within the scope of the disclosure, the drawings and the appended claims. In addition to variations and modifications in the component parts and/or arrangements, alternative uses will also be apparent to those skilled in the art.
Triglycidylisocyanurate (hereinafter referred to as epoxy resin 1), an alicyclic epoxy resin (hereinafter referred to as epoxy resin 2) expressed as the chemical formula 1 wherein n is 1 to 5, R1 and R2 are hydrogen and R3 is an epoxy group, a hardener (MeHHPA (Methylhexahydrophthalic anhydride) or HHPA (Hexahydrophthalic anhydride)), a catalyst (Triphenylphosphine) and an additive (phenyl-β-naphthylamine) were mixed as shown in Table 1 to prepare an epoxy resin composition.
Then, the thermal curing process was performed for about 2 hours at the temperature of about 100° C. to prepare a specimen having a thickness of about 2 mm. After that, the moisture absorption (humidity permeated at 100% humidity was measured for 24 hours at the temperature of 121° C.), the heat-resistant property (reduction of transmittance was measured with respect to a light having a wavelength band of 450 nm after leaving the specimen for 1000 hours at the temperature of 120° C.), the initial transmittance (measured with respect to a light having a wavelength band of 450 nm) and the transmittance retention (reduction of transmittance in comparison with the initial transmittance was measured with respect to a light having a wavelength band of 450 nm after leaving the specimen for 24 hours at the temperature of 175° C.) were measured, respectively.
Result
As can be understood from Table 1, experimental examples 1 to 6 represent the improved moisture-resistant property, heat-resistant property and optical property as compared with those of comparative examples 1 and 2.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2012-0058859 | May 2012 | KR | national |